TY - JOUR A1 - Blaeß, Carsten A1 - Boccaccini, A. R. A1 - Müller, Ralf T1 - Sintering and Crystallization of Fluoride-Containing Bioactive Glass F3 N2 - The fluoride-containing bioactive glass F3 with nominal composition (mol%) 44.8 SiO2 - 2.5 P2O3 - 36.5 CaO - 6.6 Na2O - 6.6 K2O - 3.0 CaF2 is a highly promising candidate for bone replacement applications. Its strong crystallization tendency, however, requires a thorough understanding of the interplay between glass powder particle size, surface crystallization, and sintering. Therefore, this study characterizes the sintering and crystallization of bulk specimens and various particle size fractions by differential thermal-analysis, laser scanning, electron microscopy, X-ray diffraction, and Infrared spectroscopy. Particle size fractions < 56 µm were found to fully densify, while crystals growing from the glass particle surface retard sintering of coarser fractions. Small amounts of a non-stoichiometrically calcium phosphosilicate (Ca14.92(PO4)2.35(SiO4)5.65) occurs as the primary crystal phase followed by combeite (Na4Ca4[Si6O18]) as a temporarily dominating phase. The surface crystallization of both pha­ses was found to be mainly responsible for sinter retardation. During later stages of crystallization, additional phases such as cuspidine (Ca4F2Si2O7) and silicorhenanite (Na2Ca4(PO4)2SiO4) occur, but finally monoclinic wollastonite (CaSiO3) forms as the dominant phase. KW - Bioactive Glass KW - Sintering KW - Crystallization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632482 DO - https://doi.org/10.52825/glass-europe.v3i.2564 SN - 2940-8830 VL - 3 SP - 105 EP - 124 AN - OPUS4-63248 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Waurischk, Tina A1 - Deubener, J. A1 - Müller, Ralf T1 - Internal friction and energy dissipation during fracture in silicate glasses N2 - To obtain a deeper insight into the nature of energy dissipation during fracture, the internal friction of 13 borosilicate, aluminosilicate, soda-lime, and lead-containing glasses, for which inert crack growth data are known, was measured using dynamic mechanical thermal analysis. For asymmetrically bent glass beams, the loss tangent, tan δ, was determined between 0.2 and 50 Hz at temperatures between 273 K and the glass transition temperature, Tg. It was found that the area under the tan δ vs T·Tg−1 curve correlates with the crack growth exponent, n, in the empirical v = v0·KIn relation between crack growth velocity, v, and stress intensity, KI, which indicates that n correlates with the degree of energy dissipation of sub-Tg relaxation phenomena. KW - Glass KW - Internal friction KW - Crack growth PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-631582 DO - https://doi.org/10.1063/5.0255432 SN - 0021-9606 VL - 162 IS - 19 SP - 1 EP - 9 PB - AIP Publishing AN - OPUS4-63158 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pan, Z. A1 - Waurischk, Tina A1 - Duval, A. A1 - Müller, Ralf A1 - Deubener, J. A1 - Krishnan, N. M. A. A1 - Wondraczek, K. A1 - Wondraczek, L. T1 - Precise Real‐Time Measurement of Liquid Viscosity Using Digital Video Data N2 - Quantitative knowledge of liquid viscosity is of fundamental importance in many areas of materials synthesis and processing. However, the determination of viscosity often relies on specialized experimental equipment, offline experimentation, or invasive procedures, in particular when required in extreme conditions such as at high temperature, high pressure, and in confined or corrosive environments. Here, this study proposes and validates a fast and simple method that mimics the intuitive perception of liquid flow within a quantitative framework. For this, this study employs digital video observation to derive quantitative values of the shear viscosity of liquids, with high precision and rapid acquisition rates. The technique involves capturing liquid dynamics after minor mechanical stimulation. Processed imaging data are indexed by similarity and referenced to a digital database generated with a finite element model, from which values of viscosity are obtained in line. The approach is tested on water at room temperature and on a high‐temperature glass melt. Covering a viscosity range of four orders of magnitude, both yield convincing agreement with tabulated reference data at low computational cost. KW - Image analyses KW - Liquids KW - Materials discovery KW - Similarity analyses KW - Viscosities PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-634606 DO - https://doi.org/10.1002/aisy.202500297 SN - 2640-4567 SP - 1 EP - 12 PB - Wiley AN - OPUS4-63460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Chen, Ya‐Fan A1 - Arendt, Felix A1 - Bornhöft, Hansjörg A1 - de Camargo, Andréa S. S. A1 - Deubener, Joachim A1 - Diegeler, Andreas A1 - Gogula, Shravya A1 - Contreras Jaimes, Altair T. A1 - Kempf, Sebastian A1 - Kilo, Martin A1 - Limbach, René A1 - Müller, Ralf A1 - Niebergall, Rick A1 - Pan, Zhiwen A1 - Puppe, Frank A1 - Reinsch, Stefan A1 - Schottner, Gerhard A1 - Stier, Simon A1 - Waurischk, Tina A1 - Wondraczek, Lothar A1 - Sierka, Marek T1 - Ontology‐Based Digital Infrastructure for Data‐Driven Glass Development N2 - The development of new glasses is often hampered by inefficient trial‐and‐error approaches. The traditional glass manufacturing process is not only time‐consuming, but also difficult to reproduce with inevitable variations in process parameters. These challenges are addressed by implementing an ontology‐based digital infrastructure coupled with a robotic melting system. This system facilitates high‐throughput glass synthesis and ensures the collection of consistent process data. In addition, the digital infrastructure includes machine learning models for predicting glass properties and a tool for extracting patent information. Current glass databases have significant gaps in the relationships between compositions, process parameters, and properties due to inconsistent studies and nonconforming units. In addition, process parameters are often omitted, and even original literature references provide limited information. By continuously expanding the database with consistent, high‐quality data, it is aimed to fill these gaps and accelerate the glass development process. KW - Digitalisation KW - Data-driven glass development KW - Ontology PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625844 DO - https://doi.org/10.1002/adem.202401560 SN - 1527-2648 SP - 1 EP - 12 PB - Wiley VHC-Verlag AN - OPUS4-62584 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blaeß, Carsten A1 - Müller, Ralf T1 - Fast crack healing in glass-matrix composites with rigid filler percolation frameworks N2 - To ensure the durability of solid oxide fuel cell sealants, the understanding of the microstructural influence on viscous crack healing is essential. To this end, the effect of microstructure with respect to the spatial distribution of filler particles on viscous crack healing was studied with confocal laser scanning microscopy in glass-matrix composites (GMCs) made by mix-milling and sintering of sodalime magnesium silicate glass and Φ ≈ 6 vol% ZrO2 chemically inert rigid filler particles. This way, no change in Φ occurred during the crack healing treatments studied on Vickers indentation-induced radial cracks in polished GMC surfaces. Different microstructures were mimicked using different ZrO2 particle sizes for mix-milling. Unlike coarse ZrO2 particles, similar in size to the glass particle, fine ZrO2 particles, much smaller than the glass particles, form a rigid percolation framework (RPF) of ZrO2 filler particles around the former glass particles or glass particle agglomerates. For this RPF microstructure, crack healing was observed more readily as crack healing retardation phenomena like large-scale crack widening and crack tip rounding were strongly reduced, whereas narrow cracks could still heal locally within the glassy regions. KW - Crack healing KW - Glass matrix composite KW - Rigid percolation frameworks KW - Vickers indentation PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625921 DO - https://doi.org/10.1111/jace.20386 SN - 0002-7820 SP - 1 EP - 10 PB - Wiley AN - OPUS4-62592 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zaiser, E. A1 - Fantin, Andrea A1 - Manzoni, Anna Maria A1 - Hesse, René A1 - Többens, D. M. A1 - Hsu, W.-C. A1 - Murakami, H. A1 - Yeh, A.-C. A1 - Pavel, M. J. A1 - Weaver, M. L. A1 - Zhu, H. A1 - Wu, Y. A1 - Vogel, F. T1 - Elucidating hierarchical microstructures in high entropy superalloys: An integrated multiscale study N2 - In this study, we examine a high entropy superalloy (HESA-Y1: Ni49.37Co20Cr7Fe4Al11.6Ti6Re1Mo0.5W0.5Hf0.03 at%), focusing on hierarchical microstructure formation and its effects on mechanical properties. Thermodynamic modeling using Thermo-Calc predicts equilibrium phase fractions, compositions, and transition temperatures,which are validated by experimental data from differential scanning calorimetry (DSC). Transmission electronmicroscopy (TEM) reveals that secondary aging induces nanometer-sized γ particles within γ’ precipitates, forming a hierarchical γ/γ’ microstructure. Atom probe tomography (APT) confirms supersaturation of γ’ precipitates with γ-forming elements (Co, Cr, Fe), driving γ particle formation, and measures interfacial widths between γ’ and γ phases. Partitioning coefficients derived from APT align with Thermo-Calc predictions for most elements. Vickers microhardness testing shows an increase of about 50 HV in the hierarchical microstructure compared to the conventional one. In situ synchrotron X-ray diffraction (XRD) from 25 to 750 ◦C determines a small, negative lattice misfit δ between γ and γ’ phases, suggesting enhanced microstructural stability, consistent with Thermo-Calc calculations. Our methodological approach enables measurement of the unconstrained lattice parameter of phase-extracted γ’ in a single-crystal XRD setup. Due to their small size and low volume fraction, γ particles do not produce distinct reflections in the X-ray diffractogram. Elucidating hierarchical microstructures across multiple scales, we establish that the presence of Re and Hf and controlled aging processes lead to enhanced mechanical properties, offering valuable insights for the design of advanced high entropy superalloys. KW - High entropy alloys KW - Transmission electron microscopy KW - X-ray diffraction KW - Superalloy PY - 2025 DO - https://doi.org/10.1016/j.matchar.2024.114642 VL - 220 SP - 1 EP - 13 PB - Elsevier Inc. AN - OPUS4-62348 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Manzoni, Anna Maria A1 - Mohring, Wencke A1 - Schneider, Mike A1 - Laplanche, Guillaume A1 - Hagen, Sebastian Peter A1 - Stephan‐Scherb, Christiane T1 - High‐Temperature Oxidation of the CrFeNi Medium‐Entropy Alloy N2 - The isothermal high‐temperature oxidation behavior of the equiatomic CrFeNi medium‐entropy alloy is a key issue that determines whether this material is suited for high‐temperature application. In this view, the understanding of the long‐term behavior is even more crucial than short‐term corrosion effects. Herein, a single‐phase CrFeNi alloy of the face‐centered‐cubic structure is exposed to synthetic air at 1000, 1050, and 1100 °C for 24, 100, and 1000 h and its oxidation behavior is systematically compared to that of 316L steel, which shows a surprising initial oxidation stabilization during early stages. The oxidation rate of CrFeNi is parabolic at 1000 °C (with a parabolic constant kp = 1.4·10−5 mg−2 cm−4 s−1) and 1050 °C (kp = 2.7·10−5 mg−2 cm−4 s−1), but breakaway oxidation occurs at 1100 °C after 4 h of exposure. In all cases, the oxide scales are found to (at least) partially spall off. Chromium diffuses outward to form a Cr2O3 layer at the gas/oxide interface, and a thin layer of (Cr, Fe, Ni)3O4 is identified at the oxide/alloy interface. Unlike the 316L alloy, which contains more Mn and Fe, the CrFeNi alloy does not show any catastrophic oxidation behavior at the investigated conditions. KW - Corrosion KW - Medium-entropy alloy KW - Scanning electron microscopy PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-636672 DO - https://doi.org/10.1002/adem.202500400 SN - 1438-1656 SP - 1 EP - 14 PB - Wiley VHC-Verlag AN - OPUS4-63667 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Serrano-Munoz, Itziar A1 - Agudo Jácome, Leonardo A1 - Thompsom, Sean A1 - Schneider, Judy T1 - On the transferability of post-processing heat treatments designed for PBF-LB IN718 alloys to directed energy deposition specimens N2 - Many processes are being developed for metal additive manufacturing (AM) which vary by their heat source and feedstock. The use of directed energy deposition (DED) is growing due to its ability to build larger structures outside of a contained powder bed chamber. However, the only standard exclusively for post-build heat treatment of AM IN718 is ASTM standard F3055-14a, developed for powder bed fusion (PBF). This study evaluates the applicability of this current heat treatment standard to AM IN718 specimens produced using two methods of DED: laser-blown powder (LP)-DED and arc-wire (AW)-DED. Electron microscopy and X-ray diffraction techniques were used to characterize the specimens in the as-built condition and after the full heat treatment (FHT) specified in F3055. No evidence of remaining Laves phase was observed in the two DED specimens after the FHT. Yield strengths for the DED specimens were 1049 MPa for FHT AW-DED and 1096 MPa for LP-DED, higher than the minimum stated for PBF-LB IN718 of 920 MPa. The size, morphology, inter-spacing, and diffraction patterns of the γ´ and γ´´ strengthening precipitates are found to be similar for both DED processes. Differences were observed in the microstructure evolution where the F3055 heat treatments resulted in partial recrystallization of the grain structure, with a higher content of annealing twins observed in the AW-DED. These microstructural differences correlate with differences in the resulting elongation to failure. Thus, it is proposed that variations in heat treatments are needed for optimizing IN718 produced by different AM processes. KW - Additive manufacturing variants KW - Directed energy deposition (DED) KW - Post-process heat treatments KW - SEM-EBSD and TEM microscopy KW - XRD phase analysis PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-628165 DO - https://doi.org/10.1007/s00170-025-15386-1 SN - 1433-3015 VL - 137 IS - 7-8 SP - 3949 EP - 3965 PB - Springer Science and Business Media LLC AN - OPUS4-62816 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weinel, Kristina A1 - Hahn, Marc Benjamin A1 - Lubk, Axel A1 - González Martínez, Ignacio Guillermo A1 - Büchner, Bernd A1 - Agudo Jácome, Leonardo T1 - Nanoparticle Synthesis by Precursor Irradiation with Low-Energy Electrons N2 - Nanoparticles (NPs) and their fabrication routes are intensely studied for their wide range of application in optics, chemistry, and medicine. Γ-ray and ion irradiation of precursor matter are established methods that facilitate tailored NP synthesis without complicated chemistry. Here, we develop and explore NP synthesis based on irradiating precursor microparticles with low-energy electron beams. We specifically demonstrate the fabrication of plasmonic gold nanoparticles of sizes between 3 and 350 nm on an amorphous SiOx substrate using a 30 kV electron beam. By detailed comparison with electron scattering simulations and thermodynamic modeling, we reveal the dominant role of inelastic electron–matter interaction and subsequent localized heating for the observed vaporization of the precursor gold microparticles. This general principle suggests the suitability of electron-beam irradiation for synthesizing NPs of a wide class of materials. KW - Gold Nanoparticle KW - Scanning Electron Microscopy KW - In situ irradiation KW - Thermodynamic modelling KW - Heat Transfer PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-627609 DO - https://doi.org/10.1021/acsanm.4c06033 SN - 2574-0970 VL - 8 IS - 10 SP - 4980 EP - 4988 PB - ACS Publications CY - Washington, DC AN - OPUS4-62760 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Feng, Wen A1 - Schulz, Johannes A1 - Wolf, Daniel A1 - Pylypenko, Sergii A1 - Gemming, Thomas A1 - Weinel, Kristina A1 - Agudo Jácome, Leonardo A1 - Büchner, Bernd A1 - Lubk, Axel T1 - Secondary electron emission from gold microparticles in a transmission electron microscope: comparison of Monte Carlo simulations with experimental results N2 - We measure the electron beam-induced current to analyze the electron-induced secondary electron (SE) emission from micron-sized gold particles illuminated by 80 and 300 keV electrons in a transmission electron microscope. A direct comparison of the experimental and simulated SE emission (SEE) employing Monte Carlo scattering simulations based on the GEANT4 toolkit yields overall good agreement with a noticeable discrepancy arising from the shortcoming of the GEANT4 scattering cross sections in the low-loss regime. Thus, the electron beam-induced current analysis allows to quantify the inelastic scattering including SEE in the transmission electron microscope and provides further insight into the charging mechanisms. KW - Electron beam-induced current KW - Transmission electron microscopy KW - Secondary electron emission KW - Secondary electron yield KW - Gold micronoparticle PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-622557 DO - https://doi.org/10.1088/1361-6463/ad9840 VL - 58 IS - 8 SP - 1 EP - 7 PB - IOP Publishing CY - Bristol, GB AN - OPUS4-62255 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -