TY - CONF A1 - Kianinejad, kaveh A1 - Fedelich, Bernard A1 - Darvishi Kamachali, Reza A1 - Schriever, Sina A1 - Manzoni, Anna Maria A1 - Agudo Jacome, Leonardo A1 - Megahed, Sandra A1 - Kamrani, Sepideh A1 - Saliwan-Neumann, Romeo T1 - Experimentally informed multiscale creep modelling of additive manufactured Ni-based superalloys N2 - Excellent creep resistance at elevated temperatures, i.e. T / T_m> 0.5, due to γ-γ’ microstructure is one of the main properties of nickel-based superalloys. Due to its great importance for industrial applications, a remarkable amount of research has been devoted to understanding the underlying deformation mechanism in a wide spectrum of temperature and loading conditions. Additive manufactured (AM) nickel-based superalloys while being governed by similar γ-γ’ microstructure, exhibit AM-process specific microstructural characteristics, such as columnar grains, strong crystallographic texture (typically <001> fiber texture parallel to build direction) and compositional inhomogeneity, which in turn leads to anisotropic creep response in both stationary and tertiary phases. Despite the deep insights achieved recently on the correlation between process parameters and the resulting microstructure, the anisotropic creep behavior and corresponding deformation mechanism of these materials are insufficiently understood so far. One reason for this is the lack of capable material models that can link the microstructure to the mechanical behavior. To overcome this challenge, a multiscale microstructure-based approach has been applied by coupling crystal plasticity (CP) and polycrystal model which enables the inclusion of different deformation mechanisms and microstructural characteristics such as crystallographic texture and grain morphology. The method has been applied to experimental data for AM-manufactured INCONEL-738LC (IN738). The effect of different slip systems, texture, and morphology on creep anisotropy at 850°C has been investigated. Results suggest a strong correlation between superlattice extrinsic stacking fault (SESF) and microtwinning and observed creep anisotropy. T2 - EUROMAT 23 CY - Frankfurt a. M., Germany DA - 04.09.2023 KW - IN738LC KW - Creep anisotropy KW - Crystal plasticity PY - 2023 AN - OPUS4-58263 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ávila Calderón, Luis Alexander A1 - Rehmer, Birgit A1 - Schriever, Sina A1 - Ulbricht, Alexander A1 - Agudo Jácome, Leonardo A1 - Sommer, Konstantin A1 - Mohr, Gunther A1 - Skrotzki, Birgit A1 - Evans, Alexander T1 - Creep and creep damage behavior of stainless steel 316L manufactured by laser powder bed fusion N2 - This study presents a thorough characterization of the creep properties of austenitic stainless steel 316L produced by laser powder bed fusion (LPBF 316L) contributing to the sparse available data to date. Experimental results (mechanical tests, microscopy, X-ray computed tomography) concerning the creep deformation and damage mechanisms are presented and discussed. The tested LPBF material exhibits a low defect population, which allows for the isolation and improved understanding of the effect of other typical aspects of an LPBF microstructure on the creep behavior. As a benchmark to assess the material properties of the LPBF 316L, a conventionally manufactured variant of 316L was also tested. To characterize the creep properties, hot tensile tests and constant force creep tests at 600 °C and 650 °C are performed. The creep stress exponents of the LPBF material are smaller than that of the conventional variant. The primary and secondary creep stages and the times to rupture of the LPBF material are shorter than the hot rolled 316L. Overall the creep damage is more extensive in the LPBF material. The creep damage of the LPBF material is overall mainly intergranular. It is presumably caused and accelerated by both the appearance of precipitates at the grain boundaries and the unfavorable orientation of the grain boundaries. Neither the melt pool boundaries nor entrapped gas pores show a significant influence on the creep damage mechanism. KW - 316L KW - Laser Powder Bed Fusion (LPBF) KW - Creep behavior KW - Additive Manufacturing KW - AGIL PY - 2022 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-539373 SN - 0921-5093 VL - 830 SP - 142223 PB - Elsevier B.V. AN - OPUS4-53937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Skrotzki, Birgit A1 - Schriever, Sina T1 - BAM reference data - Results of ASTM E139-11 creep tests on a reference material of Nimonic 75 nickel-base alloy N2 - Results of creep tests on a certified reference material at T = 600°C and a tensile creep load of 160 MPa are provided. The evaluated results include the times to reach 2% and 4% creep strain, respectively, and the creep rate after 400 h. The data were audited and are BAM reference data. KW - Reference data KW - Creep KW - Nickel-base alloy KW - Nimonic 75 KW - Reference material BCR-425 PY - 2021 U6 - https://doi.org/10.5281/zenodo.5106606 PB - Zenodo CY - Geneva AN - OPUS4-52970 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Epishin, A. I. A1 - Fedelich, Bernard A1 - Viguier, B. A1 - Schriever, Sina A1 - Svetlov, I. L. A1 - Petrushin, N. V. A1 - Saillard, R. A1 - Proietti, A. A1 - Poquillon, D. A1 - Chyrkin, A. T1 - Creep of single-crystals of nickel-base γ-alloy at temperatures between 1150 °C and 1288 °C N2 - A γ-analogue of the superalloy CMSX-4 that does not contain the strengthening γ′ -phase and only consists of the γ-solid solution of nickel has been designed, solidified as single-crystals of different orientations, and tested under creep conditions in the temperature range between 1150 and 1288 °C. The tests have revealed a very high creep anisotropy of this alloy, as was previously found for CMSX-4 at supersolvus temperature of 1288 °C. This creep anisotropy could be explained by the dominance of 〈011〉{111} octahedral slip. Furthermore, the analysis of the creep data has yielded a high value of the creep activation energy, Qc≈442 kJ/mol, which correlates with the high activation energy of Re diffusion in Ni. This supports the hypothesis that dislocation motion in the γ-matrix of Re-containing superalloys is controlled by the diffusion of the Re atoms segregating at the dislocation core. The Norton stress exponent n is close to 5, which is a typical value for pure metals and their alloys. The absence of γ′ -reprecipitation after high-temperature creep tests facilitates microstructural investigations. It has been shown by EBSD that creep deformation results in an increasing misorientation of the existing low angle boundaries. In addition, according to TEM, new low angle boundaries appear due to reactions of the a/2 〈011〉 mobile dislocations and knitting of new networks. KW - Nickel alloys KW - Single-crystals KW - Creep KW - Electron microscopy KW - Deformation mechanisms PY - 2021 U6 - https://doi.org/10.1016/j.msea.2021.141880 SN - 0921-5093 VL - 825 SP - 1 EP - 13 PB - Elsevier CY - Amsterdam AN - OPUS4-53132 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Fedelich, Bernard A1 - Feldmann, Titus A1 - Haftaoglu, Cetin A1 - Nolze, Gert A1 - Schriever, Sina A1 - Epishin, A. A1 - Camin, B. A1 - Lopez-Galilea, I. A1 - Ruttert, B. A1 - Theisen, W. T1 - Untersuchung des Kriechverhaltens einer Nickelbasis-Superlegierung bei ultrahohen homologen Temperaturen und Anwendung auf das heiß-isostatische Pressen (HIP) N2 - Mit Hilfe des HIP-Verfahrens („Hot Isostatic Pressing“) werden Poren in der einkristallinen Nickel-Basis Superlegierung CMSX-4 kontinuierlich geschrumpft und dadurch die nach der Erstarrung und der Wärmebehandlung vorhandene Porosität stark reduziert. In diesem Beitrag werden experimentelle und numerische Untersuchungen zu den Mechanismen der Porenschrumpfung zusammengefasst. Es zeigt sich, dass das Verformungsverhalten während Kriechversuchen bei der HIP-Temperatur durch Versetzungsgleitung auf oktaedrischen Ebenen dominiert wird. Dagegen zeigen Messungen der Porositätsabnahme und Simulationen des Porenschließens, dass die Kinetik der Porenschrumpfung durch das Phänomen der Leerstellendiffusion zwischen Poren und Kleinwinkelkorngrenzen („Low Angle Boundary“, LAB) bestimmt wird. Im Gegensatz führt die klassische Kristallviskoplastizität zu einer systematischen Überschätzung dieser Kinetik. Der scheinbare Widerspruch lässt sich auflösen, wenn man bedenkt, dass auf der Skala der Poren Versetzungsquellen nicht gleichmäßig verteilt sind, wie in der konventionellen Kristallplastizität implizit angenommen wird. Stattdessen wird in einem weiterführenden Modell davon ausgegangen, das Kleinwinkelkorngrenzen (LABs) als Versetzungsquellen fungieren, während die Scherspannungen sehr stark in der Nähe der Poren lokalisiert sind, was die Emission von Versetzungen deutlich reduziert. T2 - Langzeitverhalten warmfester Stähle und Hochtemperaturwerkstoffe CY - Online meeting DA - 27.11.2020 KW - HIP KW - Superlegierung KW - Kriechen PY - 2020 SN - 978-3-946885-95-5 VL - 2020 SP - 28 EP - 39 PB - Forschungsvereinigung Warmfeste Stähle und Hochtemperaturwerkstoffe AN - OPUS4-51796 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rockenhäuser, Christian A1 - von Hartrott, P. A1 - Metzger, M. A1 - Schriever, Sina A1 - Augenstein, E. A1 - Karlin, J. A1 - Piesker, Benjamin A1 - Schweizer, Ch. A1 - Skrotzki, Birgit T1 - Lebensdauerberechnung von Aluminium-Radialverdichterrädern unter Berücksichtigung der Werkstoffalterung N2 - In this project, a procedure was developed to improve the lifetime assessment precision of exhaust turbo charger radial compressor wheels made from the age hardenable aluminum alloy EN AW-2618A. This comprises particularly the consideration of material aging, which has to be anticipated during operation of such components under relevant service conditions (temperature, time, stress). First of all, a solid experimental database was established for the investigated material. This includes a mechanical as well as a microstructural characterization of the as-received state (T61) and after aging up to 25,000 h at relevant service temperatures (160 °C, 180 °C, 190 °C). The microstructural investigations focused on the development of the radii of the cylindrical hardening phase, which coarsens during aging. The relation between aging temperature, time and mechanical load (if applicable) was established for the first time to this extent. An interrelationship to describe the coarsening was established. The effect of aging on hardness, strength, creep behavior and fatigue lifetime (LCF, TMF) was studied and a correlation to the microstructure was established. The results of the creep tests were used to calibrate a modified hyperbolic sine creep model. A time and temperature dependent deformation model according to Chaboche, which describes the relevant phenomena of high temperature deformation and cyclic plasticity, was extended. It now considers material aging by describing the strength not only as a function of temperature but also as a function of aging, i.e. of the mean radius of the precipitates. A similar procedure was applied to extend the model in order to assess the fatigue lifetime. The calculated lifetimes of LCF and TMF tests completed during this project match well with the experimental results. Only one LCF test with a hold time of 900 s in tension deviates clearly from the mean value and shows the limits of the time independent damage model. Tests with shorter hold times of 60 s are within the scatter band, likewise the different aging conditions. A damage accumulation model additionally describing the progressive aging during lifetime was developed and implemented. Besides considering aging in the deformation and lifetime assessment, it is also possible to judge complex loading cycles in a postprocessing by rain flow classification of typical complex loading cycles. The methodology and the models were implemented into the Finite-Element software Abaqus and Ansys and are available for numerical assessment of components. N2 - In diesem Forschungsvorhaben wurde ein Verfahren entwickelt, um die Genauigkeit der Lebensdauerbewertung für Abgasturbolader (ATL)-Verdichterräder aus der ausscheidungs-härtbaren Aluminiumlegierung EN AW-2618A zu verbessern. Dies umfasst insbesondere die Berücksichtigung der Werkstoffalterung, mit der beim Einsatz dieser Bauteile unter entsprechender Betriebsbeanspruchung (Temperatur, Zeit, Spannung) gerechnet werden muss. Zunächst wurde eine solide experimentelle Datenbasis für den untersuchten Werkstoff geschaffen. Dies umfasste sowohl eine mechanische als auch eine mikrostrukturelle Charakterisierung des Ausgangszustands (T61) sowie von ausgelagerten Zuständen bis zu 25.000 h bei betriebsrelevanten Temperaturen (160 °C, 180 °C, 190 °C). Bei den Untersuchungen zur Mikrostruktur wurde der Fokus auf die Entwicklung der Radien der stäbchen-förmigen aushärtenden Phase gelegt, die während der Alterung vergröbern. Der Zusammenhang zwischen Auslagerungstemperatur, -zeit und ggfs. mechanischer Belastung wurde erstmals in diesem Umfang quantifiziert und entsprechende Gesetzmäßigkeiten zur Beschreibung der Vergröberung ermittelt. Vergleichend dazu wurde der Einfluss der Alterung auf die Härte, die Festigkeit, das Kriechverhalten und die Ermüdungslebensdauer (LCF, TMF) bestimmt, so dass eine Korrelation zur Mikrostruktur vorliegt. Die Ergebnisse der Kriechversuche wurden zur Kalibrierung eines modifizierten Sinus-hyperbolicus-Kriechmodells verwendet. Ein zeit- und temperaturabhängiges Verformungsmodell nach Chaboche, welches die wesentlichen Phänomene der Hochtemperaturverformung und der Wechselplastizität beschreibt, wurde erweitert und berücksichtigt nun die Werkstoffalterung, indem die Festigkeit nicht nur als Funktion der Temperatur, sondern auch des Alterungszustands (d. h. des mittleren Radius der Ausscheidungen) dargestellt wird. Für die Erweiterung des Modells zur Bewertung der Ermüdungslebensdauer wurde analog verfahren. Die berechnete Lebensdauer der im Verlauf des Vorhabens durchgeführten LCF- und TMF-Versuche stimmt gut mit den experimentellen Ergebnissen überein. Lediglich ein LCF-Versuch mit einer Haltezeit von 900 s im Zug weicht deutlich vom Mittelwert ab und zeigt die Grenzen des zeitunabhängigen Schädigungsmodells auf. Versuche mit kürzeren Haltezeiten bis zu 60 s liegen im Streuband, ebenso die verschiedenen Alterungszustände. Eine Schädigungsakkumulation unter Berücksichtigung der fortschreitenden Alterung über der Lebensdauer wurde entwickelt und implementiert. Neben der Berücksichtigung der Alterung in der Verformungs- und Lebensdaueranalyse besteht auch die Möglichkeit, komplexe Belastungszyklen in einem Postprozessing zu bewerten, indem Rainflow-Klassierungen typischer komplexer Belastungszyklen vorgenommen werden. Die Methodik und die Modelle wurden in die Finite-Elemente-Programme Abaqus und Ansys implementiert und stehen für die rechnerische Bewertung von Bauteilen zur Verfügung. T2 - FVV Frühjahrstagung 2018 CY - Bad Neuenahr, Germany DA - 22.03.2018 KW - Aluminium KW - Centrifugal compressor wheel KW - Dark-field transmission electron microscopy (DFTEM) KW - Degradation KW - S-phase PY - 2018 SP - 97 EP - 130 AN - OPUS4-44604 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - von Hartrott, P. A1 - Rockenhäuser, Christian A1 - Schriever, Sina A1 - Skrotzki, Birgit T1 - Correlation of the precipitate size evolution and the creep rate of the aluminium alloy EN AW 2618A at 190 °C N2 - A short description of the work done on the topic "Correlation of the precipitate size evolution and the creep rate of the aluminium alloy EN AW 2618A at 190 °C" is given. T2 - International Conference on Aluminium Alloys 16 CY - Montreal, Canada DA - 17.06.2018 KW - Alloy 2618A KW - Degradation KW - Aluminium KW - Creep KW - Coarsening PY - 2018 SN - 978-1-926872-41-4 SP - 99 AN - OPUS4-45284 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rockenhäuser, Christian A1 - Schriever, Sina A1 - von Hartrott, P. A1 - Piesker, Benjamin A1 - Skrotzki, Birgit T1 - Comparison of long-term radii evolution of the S-phase in aluminum alloy 2618A during ageing and creep N2 - A study was made on the effect of creep loading on the precipitate radii evolution of the aluminum alloy 2618A. The overageing process of the alloy was investigated under load at a temperature of 190 °C with stresses between 79 and 181 MPa and compared to stress free isothermal ageing. The precipitates responsible for strength were characterized using dark-field transmission electron microscopy (DFTEM). This allows the experimental Determination of radii distributions of the rod-shaped Al2CuMg precipitates and the evaluation regarding their mean precipitate radius. It was found that the mean precipitate radius enables the comparison of the different microstructural conditions of crept and uncrept samples. The mean precipitate radii of the samples experiencing creep are significantly higher than those of undeformed samples. It was shown that the acquired radii distributions are viable to determine averaged particle radii for comparison of the aged samples. A ripening process including pipe diffusion along dislocations describes the data on coarsening very well for the creep samples. KW - Aluminum alloys KW - Electron microscopy KW - Aging KW - Creep KW - Microstructure KW - S-Phase PY - 2018 U6 - https://doi.org/10.1016/j.msea.2018.01.033 SN - 0921-5093 VL - 716 SP - 78 EP - 86 PB - Elsevier B. V. AN - OPUS4-44090 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Epishin, A. A1 - Fedelich, Bernard A1 - Nolze, Gert A1 - Schriever, Sina A1 - Feldmann, Titus A1 - Farzik Ijaz, M. A1 - Viguier, B. A1 - Poquillon, D. A1 - Le Bouar, Y. A1 - Ruffini, A. A1 - Finel, A. T1 - Creep of single crystals of nickel-based superalloys at ultra-high homologous temperature N2 - The creep behavior of single crystals of the nickel-based superalloy CMSX-4 was investigated at 1288 °C, which is the temperature of the hot isostatic pressing treatment applied to this superalloy in the industry. It was found that at this super-solvus temperature, where no gammaPrime-strengthening occurs, the superalloy is very soft and rapidly deforms under stresses between 4 and 16 MPa. The creep resistance was found to be very anisotropic, e.g., the creep rate of [001] crystals was about 11 times higher than that of a [111] crystal. The specimens of different orientations also showed a very different necking behavior. The reduction of the cross-sectional area psi of [001] crystals reached nearly 100 pct, while for a [111] crystal psi = 62 pct. The EBSD analysis of deformed specimens showed that despite such a large local strain the [001] crystals did not recrystallize, while a less deformed [111] crystal totally recrystallized within the necking zone. The recrystallization degree was found to be correlated with deformation behavior as well as with dwell time at high temperature. From the analysis of the obtained results (creep anisotropy, stress dependence of the creep rate, traces of shear deformation, and TEM observations), it was concluded that the main strain contribution resulted from <01-1>{111} octahedral slip. T2 - 3rd European Conference on Superalloys (‘Eurosuperalloys 2018’) CY - Oxford, UK DA - 9.9.2018 KW - Single-crystal KW - Superalloy KW - Creep KW - Isostatic hot pressing (HIP) PY - 2018 U6 - https://doi.org/10.1007/s11661-018-4729-6 SN - 1073-5623 SN - 1543-1940 VL - 49A IS - 9 SP - 3973 EP - 3987 PB - Springer Sciences & Business Media CY - New York, NY AN - OPUS4-45660 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -