TY - CONF A1 - Heuser, Lina T1 - Composition-structure-property relationships of ternary borate glasses N2 - Since the pioneer work of Krogh-Moe [1] in the 1960’s the structure clarification of borate glasses is of interest for many generations. In the present contribution the composition–structure–property relationships of Me2O–ZnO–B2O3, Me = Li (LZB), Na (NZB), K (KZB), Rb (RZB), CaO–ZnO–B2O3 (CaZB), and Li2O–PbO–B2O3 (LPbB) glasses are investigated. Non-toxic, highly polarizable zinc oxide potentially substitutes harmful lead oxide in glasses for applications e.g., in photovoltaics and microelectronics. Glass structure was analyzed using Raman and infrared spectroscopy, and the glass properties were measured using dilatometry (Tg, viscosity data, coefficient of thermal expansion) and rotational viscometry (high-temperature viscosity) [2,3]. The spectroscopic results show that alkali and calcium ions largely balance out the negative charges of BO4-units, while zinc and lead ions mainly stabilize the non-bridging oxygen atoms (NBO). The type of network modifier ion directs formation of the BO4-containing groups and the number of BO4-units (N4). Thus, i.) BO4-containing pentaborate was assigned in LZB, NZB and CaZB glasses, and ii.) diborate in KZB and RZB glasses. Simultaneous presence of pentaborate and diborate was only detected in LPbB. The combination of modifier’s properties, i.e., lower Lewis’s basicity (Rb+ > Li+), higher field strength (Rb+ < Li+), lower polarizability (Rb+ > Li+), and steric effects with increasing size (Rb+ > Li+) [4], leads to slightly increasing N4 in the series RZB (0.36) ≈ KZB < NZB (0.37) < LZB ≈ CaZB (0.39). This increase in N4 results in an increase in the atomic packing density 0.519 (RZB) – 0.584 (LZB) and thus in the Young’s Modulus 38.1 GPa (RZB) – 92.5 GPa (LZB) and in the glass transition temperature (Tg) 444 °C (RZB) – 467 °C (LZB) in the alkali series. In reverse order the coefficient of thermal expansion decreases from 12·10-6 K-1 (RZB) – 8.54·10-6 K-1 (LZB) with increasing N4. Ca2+ in CaZB enhances the viscosity (Tg: 580 °C) compared to Li+ in isocompositional LZB due to higher coordination. On the other hand, Pb2+ in LPbB decreases the viscosity (Tg: 399 °C) compared to Zn2+ in LZB with similar molar fractions. T2 - 98th Glass-Technology Conference of the German Society of Glass Technology (DGG) CY - Goslar, Germany DA - 26.05.2025 KW - Borate glasses KW - Structure-property relationship PY - 2025 AN - OPUS4-63771 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina T1 - An overview of structural, physical and thermal properties of low melting zinc and lead borate glasses N2 - Low melting zinc borate glasses awake interest to replace lead borate glasses in the silver metallization pastes for solar cells or microelectronics. In the current study, characteristic properties of alkali zinc borate glasses (X2O-ZnO-B2O3, X = Li, Na, K, Rb) were compared to an earth alkali zinc borate glass (CaO-ZnO-B2O3). Additionally, zinc oxide is partially substituted by lead oxide or cooper oxide in the borate glasses (Li2O-PbO-B2O3, Na2O ZnO CuO-B2O3). The alkali zinc borate glasses indicate less differences in Raman spectra, and thus in structural properties, in comparison to the Ca and Pb ions influence. LPbB (Tg = 401 °C) has a lower viscosity than LZB (Tg = 468 °C) and CaZB has the highest glass transition temperature (Tg = 580 °C). The Angell plot for the alkali zinc borate glasses shows a high fragility m = 80. Besides Tg, the density measured by means of the Archimedean principle, molar volume, and coefficient of thermal expansion (CTE) of the glasses were investigated. Trends could be found according to alkali ions or intermediate oxides. The density increases with decreasing alkali ion size from KZB (2.632 g/cm3) to LZB (2.829 g/cm3) and increases from LZB to LPbB (3.764 g/cm3). CTE ranges between 7.09 10-6 K-1 for CaZB and 11.5 10 6 K 1 for KZB and RZB. The differential thermal analysis (DTA) and X ray diffraction (XRD) indicate crystallization of various crystalline phases during heating with 5 K/min in most cases. T2 - 94. Glastechnische Tagung CY - Online meeting DA - 10.05.2021 KW - Borate glasses KW - Glass structure KW - Viscosity KW - Young´s Modulus KW - Alkali ions PY - 2021 AN - OPUS4-52867 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -