TY - CONF A1 - Bayerlein, Bernd T1 - Transforming Materials Science with Concepts for a Semantically Accessible Data Space N2 - The digital transformation in materials science enables more efficient and sustainable processes. Through technological adaptations and a commitment to the FAIR principles, materials and processes are holistically addressed across entire value chains. The Platform MaterialDigital (PMD) and related initiatives are developing innovative solutions to the challenges of digitalization. The focus is on the interoperable integration of heterogeneous materials and processes data in semantically accessible data spaces. An ontological framework, based on the PMD Core Ontology and application-specific ontologies, promotes semantic interoperability of cross-domain and multi-scale (meta)data. This framework can be extended through natural language processing in a script-supported manner, as demonstrated with the Microscopy Ontology. The presentation further highlights how freely available mechanical and microstructural datasets of various aging stages of an aluminum alloy can be semantically integrated and flexibly searched. Graph-based operations enable links between processing and microstructural properties to be established, facilitating enhanced correlation analysis and pattern recognition. T2 - TMS Specialty Congress 2025 CY - Anaheim, CA, USA DA - 15.06.2025 KW - FAIR Data KW - Semanitc Interoperability KW - Community KW - Reproducibility PY - 2025 AN - OPUS4-63474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bayerlein, Bernd T1 - Data-Driven Materials Science Supported by Community, Reproducibility, and Standardization N2 - Reproducible research in materials science demands a strong community and shared semantic standards. The interdisciplinary nature of the field has led to fragmented data practices, hampering collaboration and integration. Digitalisation initatives such as the German MaterialDigital Initiative addresses this by fostering a community-driven approach to FAIR data management, using ontologies to build consensus and semantic interoperability. Through interactive events like the Ontology Playground, a unified data culture that accelerates innovation and ensures reproducibility across materials research is supported. T2 - Seminar of the Person Group CY - Berkeley, CA, USA DA - 23.06.2025 KW - FAIR Data KW - Semantic Interoperability KW - Community KW - Reproducibility PY - 2025 AN - OPUS4-63475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Franchin, G. A1 - Zocca, Andrea A1 - Karl, D. A1 - Yun, H. A1 - Tian, X. T1 - Editorial: Advances in additive manufacturing of ceramics N2 - Recently, additive manufacturing of ceramics has achieved the maturity to be transferred from scientific laboratories to industrial applications. At the same time, research is progressing to expand the boundaries of this field into the territory of novel materials and applications. This feature issue addresses current progress in all aspects of additive manufacturing of ceramics, from parts design to feedstock selection, from technological development to characterization of printed components. KW - Additive manufacturing KW - Ceramic PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-549361 DO - https://doi.org/10.1016/j.oceram.2022.100277 SN - 2666-5395 VL - 10 SP - 1 EP - 2 PB - Elsevier CY - Amsterdam AN - OPUS4-54936 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina T1 - Sintering of silver‑alkali zinc borate glass‑composites N2 - Since decades electric contacts based on silver metallization pastes are key components of photovoltaics and advanced microelectronics. For the metallization of commercial Si solar cells, high conductive silver glass pastes are cost effectively applicated by screen printing. Nevertheless, silver pastes are still one of the most crucial and expensive none Si materials in solar cells. Ever shorter time to market as well as increasing demands on reduced Ag consumption and line width require the targeted development of silver-glass-pastes with increased sinter ability and electrical conductivity. As a main difficulty, however, the liquid phase sintering of silver glass pastes is poorly understood so far. In the present study, the influence of different network modifier in alkali-zinc-borate paste glasses on liquid phase sintering of silver-glass-pastes was investigated. Low melting X2O-ZnO-B2O3 glasses with X = Na, Li and Rb (abbr. LZB, NZB, and RZB) were utilized to prepare silver-glass-composites containing 30 %Vol glass. Shrinkage behavior of the silver-glass-composites compared with that of pure silver and pure glass powder compacts was studied with heating microscopy. The powder compacts were uniaxially pressed and heated at 5 K/min to the glass softening temperature. Glass transformation temperature and viscosity of the glasses were respectively measured with dilatometry and rotational viscometry. The thermal behavior of the pure glasses was analyzed with thermal analysis. Additionally, the contact angle of glass on pure silver foil was determined by means of heating microscopy between room temperature and 830 °C. Thermal analysis of the alkali-zinc-borate-glasses under study has shown transformation temperatures between 450 °C (RZB), 460 °C (LZB) and 465 °C (NZB). For all glasses crystallization was found to start approximately at about 550 °C. However, different peak areas hint on a different degree of crystallization. Conformingly, the sintering behavior, measured in terms of area shrinkage, significantly differed for the silver-pastes under study. For silver-pastes with NZB or LZB-glass, sintering starts at 464 °C for NZB Ag pastes and at 451 °C for LZB Ag pastes and ends at 597 °C for NZB Ag paste and at 594 °C for LZB Ag paste. The sintering of the RZB Ag paste proceeds between 426 °C and 703 °C. The final densification was retarded possibly due to crystallization or swelling. The low sinter onset at 426 °C seems to correlate with the good wetting behavior of the RZB glass. Thus, the lowest apparent contact angle between the just densified powder compact sintered at a silver substrate was found for this glass. Moreover, microstructure analyses of the various composites indicate differences in silver dissolution and reprecipitation. T2 - Technology Crossover Extravaganza, HiTEC/CICMT/APEPS CY - Online meeting DA - 26.04.2021 KW - Silver-glass-metallization-paste KW - Sintering KW - Crystallization KW - Alkali ions KW - Sintering atmosphere PY - 2021 AN - OPUS4-52872 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Ralf T1 - Sintering and Foaming of Silicate Glass Powders N2 - The lecture focuses on the mechanisms of non-desired gas bubble formation and foaming during the sintering of glass powder compacts. It is shown that foaming is driven by carbon gases and that carbonates, encapsulated in micropores or mechaniacally dissolved beneath the glass surface, provide the major foaming source. T2 - Sandanski Workshop Sinter crystallization 27th-29th September 2021 PROJECT “THEORY AND APPLICATIONS OF SINTER-CYSTALLIZATION” DN 19/7 CY - Online meeting DA - 27.10. 2021 KW - Sintering KW - Non-desired foaming PY - 2021 AN - OPUS4-53772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Blaeß, Carsten T1 - 3D printing of crystallizing bioactive glasses N2 - Artificial bone replacement by individual customized three-dimensional resorbable bioactive glass has not yet been widely established in the clinical use. This is mainly due to the antagonism of sintering ability and suitable bioactivity. Competitive crystallization often prevents the generation of dense sintered bodies, especially for additive manufactured 3D structures. Previous studies of the fluoride-containing glass F3 have shown its potential to combine both sintering ability and suitable bioactivity. Furthermore, the occurring sintering blockade by surface crystallization of Na2CaSi2O6 was tunable by glass particle size. In this study the glasses F3, F3-Cu with 1 mol% CuO added at the expense of CaO and the well-known 13-93 were chosen to determine the influence of surface crystallization on 3D printed sinter bodies. For this purpose, grain size fractions in range of smaller 32 µm to 315 µm in fraction size of 6-20 µm were sieved from jaw crushed glass frit as well as glass cubes were cut from casted blocks for all glasses. Sintering behavior of both pressed and printed powder compacts was observed via heating microscopy. Crystallization was determined by DTA and crystallization progress was monitored on fractured sinter bodies and polished cubes via electron and laser scanning microscopy as well as with diffractometry. Depending on grain size the formation of crystalline support framework along former grain boundaries shows the capability to stabilize fully densified sinter bodies before softening. Beside of this, the generation of complex hierarchic porosity was possible as well. T2 - ICG Berlin 2022 CY - Berlin, Germany DA - 03.07.2022 KW - Bioactive Glass KW - Crystallization KW - Sintering KW - 3D printing PY - 2022 AN - OPUS4-55253 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina T1 - Flüssigphasensinterung von Silber-Glas Dispersionen N2 - Silber-Glas Wechselwirkungen spielen eine wichtige Rolle zum Beispiel in Glas-haltigen Silberpasten, die in der Photovoltaik oder Mikroelektronik verwendet werden. Um ein besseres Verständnis der Vorgänge zu erhalten, werden niedrig-schmelzende, bleifreie X2O ZnO B2O3 Gläser (X = Li, Na, K und Rb, Abk.: LZB, NZB, KZB and RZB) zur Untersuchung der Pasten verwendet. Raman und Infrarot Spektroskopie zeigen, dass die Glasstruktur weitgehend vergleichbar ist, aber Unterschiede in der Bildung von Pentaboratgruppen in LZB und NZB oder Diboratgruppen in KZB und RZB auftreten. Die Anzahl an vierfach koordinierten Bor-Ionen (N4) sinkt mit zunehmendem Alkaliionenradius. Die Verringerung von N4 führt zu einer niedrigeren Glasübergangstemperatur in der Reihe LZB (472 °C) < NZB (465 °C) < KZB (460 °C) < RZB (449 °C). Zur Herstellung der Pasten wurde kommerzielles Silber-Pulver mit 30 Vol.-% Glas und Organik gemischt. Das Sinterverhalten der gepressten Pulver wurde mittels Erhitzungsmikrospie untersucht. Der Sinterbeginn der Pasten ist vergleichbar und korrespondiert mit den geringen Unterschieden der Viskosität bei vergleichbarer Partikelgröße der Gläser. In den Ag-KZB- und Ag-RZB-Pasten ist die Schwindung durch die stärker einsetzende Kristallisation im Vergleich zu LZB und NZB verzögert. T2 - AK Glasig-kristalline Multifunktionswerkstoffe CY - Aachen, Germany DA - 17.02.2022 KW - Sintern KW - Silber KW - Glas KW - Diffusion KW - Gefüge PY - 2022 AN - OPUS4-55735 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina T1 - Liquid phase sintering of alkali zinc borate glass-bearing silver pastes for applications in photovoltaics and microelectronics N2 - Liquid phase sintering of glass bearing silver pastes used in photovoltaics and microelectronics is poorly understood. In particular, the role of different network modifiers acting in the glass component and the question of the most suitable atmospheric oxygen level during sintering are still under considerable debate. To tackle these issues, low-melting and lead-free X2O-ZnO-B2O3 glasses with X = Li, Na, K and Rb (LZB, NZB, KZB and RZB) were prepared. Infrared spectroscopy showed that the glass structure was similar to each other, while an increase of tetrahedrally coordinated boron with increasing field strength of the alkali was evident. In turn, the glass transition temperature (from differential thermal analysis) increased in the order: RZB (449 °C) < KZB (460 °C) < NZB (465 °C) < LZB (472 °C). Powders of each glass were mixed with organics to receive silver-glass-pastes containing 30 vol% glass and these were subjected to heating microscopy in air. Although similar onset temperatures of sintering were recorded for Ag-NZB and Ag-LZB glass pastes, and for Ag-RZB paste and KZB-Ag-paste, respectively, differences in the crystallization behavior and final densification were observed between the former and the latter group. These were translated in terms of differences in silver dissolution and reprecipitation among the two groups. Further, running the experiments in nitrogen gas showed that sintering of all pastes was considerably hampered. The slow-down of the sinter kinetics was found to be in line with the assumed lower oxidation and dissolution of silver ions into the glass-forming liquid. T2 - 26th International Congress on Glass CY - Berlin, Germany DA - 03.07.2022 KW - Silver metallization paste KW - Sintering KW - Glass KW - Alkali zinc borate glasses KW - Viscosity KW - Structure PY - 2022 AN - OPUS4-55728 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Heuser, Lina T1 - In situ observation of silver precipitation in sodium zinc borate glass-forming melts N2 - Melting of Na2CO3-ZnO-B2O3 batches containing up to 16.8 wt% AgNO3 (5 mol% Ag2O in the target glass composition) was observed in situ by means of hot stage microscopy. In all batches metallic silver precipitation took place as most of the silver nitrate was reduced to metallic silver before Ag+ ions could be dissolved in the evolving borate melts. In turn, only traces of Ag+ (<300 ppmw) were dissolved in the sodium zinc borate glass melts under study. It is assumed that the oxidation to Ag+ was limited due to poor availability of reducible oxygen in the glass melts and presence of Na2O being a stronger base than Ag2O. Thus, the precipitated metallic silver formed droplets of different sizes. The larger droplets (d > 20 µm) were already settled at the bottom of the container and remained constant in size upon dwelling for 1 h at 1050 °C of about one hour and the subsequent cooling (45 K/min) to room temperature, whereas the smaller droplets (d < 20 µm) were mobile in the borate melt due to Marangoni and Stokes motion. For the latter droplets, coalescence was observed in situ. A growth of larger droplets at the expense of smaller ones, i.e., Ostwald ripening was also expected but could not be studied with the used experimental equipment. T2 - 26th International Congress on Glass CY - Berlin, Germany DA - 03.07.2022 KW - Glass melt KW - Silver KW - Sodium zinc borate glass KW - Hot stage microscopy KW - Precipitation PY - 2022 AN - OPUS4-55732 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Reinsch, Stefan T1 - Surface-Initiated Microstructure Formation in Glass Ceramics N2 - Up to now, oriented surface crystallization phenomena are discussed controversially, and related studies are restricted to few glasses. For silicate glasses we found a good correlation between the calculated surface energy of crystal faces and oriented surface nucleation. Surface energies were estimated assuming that crystal surfaces resemble minimum energy crack paths along the given crystal plane. This concept was successfully applied by Rouxel in calculating fracture surface energies of glasses. Several oriented nucleation phenomena can be herby explained assuming that high energy crystal surfaces tend to be wetted by the melt. This would minimize the total interfacial energy of the nucleus. Furthermore, we will discuss the evolution of the microstructure and its effect on the preferred crystal orientation. T2 - 26th International Congress on Glass CY - Berlin, Germany DA - 03.07.2022 KW - Glass KW - Oriented surface crystallization KW - Surface energy KW - Bond energy KW - Nucleation mode PY - 2022 AN - OPUS4-56070 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -