TY - CONF A1 - Mieller, Björn A1 - Schulz, Bärbel A1 - Mrkwitschka, Paul A1 - Rabe, Torsten T1 - Influence of surface treatment on the strength of a dental zirconia for implants N2 - Roughening of zirconia dental implants is a common clinical practice to improve ingrowth behavior. It depends on the manufacturer of the implant at which stage of the manufacturing process and by which method the surface is roughened. Systematic studies on this topic are rarely found in the literature. Therefore, the influence of surface treatment on the strength of a dental zirconia was investigated as part of a research project on the development of ceramic implants. The material under test was a commercial zirconia consisting of a Y-TZP matrix and Ce-TZP inclusions in the sintered state. This material is characterized by a slightly higher fracture toughness and slightly reduced strength compared to typical 3Y-TZP. Sets of samples were sandblasted in the white-fired or sintered condition. The ball-on-three-ball-strength of these samples was measured and compared to the strength of as-fired samples and polished samples. The complete study was performed two times for validation of the results. It is found that the average strength of TZP ceramics differs by almost 500 MPa depending on the surface treatment. Conventionally sintered specimens with as-fired surface exhibit a strength of 880 MPa. Sandblasting in the white fired state reduces the strength to 690 MPa. Both polishing and sandblasting in the sintered condition result in an increase in strength to about 1180 MPa. Comparative microstructural investigations, roughness measurements and X-ray phase analyses were carried out to determine the causes of these huge differences in strength. These findings may challenge the practice of white body surface treatment and give reason for further investigations on other commercial dental TZP materials. T2 - 97th DKG Annual Meeting - CERAMICS 2022 CY - Online meeting DA - 07.03.2022 KW - Ceramics KW - Implants KW - Biaxial strength PY - 2022 AN - OPUS4-54453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -