TY - JOUR A1 - Holzer, Marco A1 - Johansen, Sidsel M. A1 - Christensen, Johan F.S. A1 - Smedskjaer, Morten M. A1 - Cicconi, Maria Rita A1 - de Ligny, Dominique A1 - Müller, Ralf A1 - de Camargo, Andrea S.S. A1 - Maaß, Robert T1 - Direct connection between secondary relaxation mode and fracture toughness in alkali-aluminosilicate glasses N2 - Oxide glasses are intrinsically brittle, lacking sufficient atomic-scale mechanisms that can relax mechanical stresses in the vicinity of a propagating crack. As a result, fracture is typically well-captured by considering local bond rupture at the crack tip. Here we demonstrate that barrier energies related to the low-temperature 𝛾-relaxation mode in alkali-aluminosilicate glasses are inversely related to the fracture toughness measured via standardized three-point bending fracture experiments. This holds true for both a series with varying cations (Li, Na, K) and one with varying Li concentration. The structural rationale for this finding is gained via Raman spectroscopy. The findings suggest that a fundamental structural relaxation mode measured on bulk specimens can serve as an effective guideline for fracture toughness of oxide glasses. Data for additional silicate glasses support this conclusion. KW - Fracture toughness KW - Oxide glass KW - Mechanical properties KW - Alkali-aluminosilicate glasses KW - Internal friction PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-651540 DO - https://doi.org/10.1016/j.mtadv.2025.100669 SN - 2590-0498 VL - 29 SP - 1 EP - 10 PB - Elsevier Ltd. CY - Amsterdam, Niederlande AN - OPUS4-65154 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hickel, Tilmann A1 - Waske, Anja A1 - Tehranchi, Ali A1 - Bhattacharya, Biswajit A1 - Stawski, Tomasz M. A1 - Fellinger, Tim-Patrick A1 - Mehmood, Asad A1 - Witt, Julia A1 - Ozcan, Ozlem A1 - Guilherme Buzanich, Ana A1 - Kumar, Sourabh A1 - Mishra, Rajesh Kumar A1 - Holzer, Marco A1 - Stucchi de Camargo, Andrea Simone A1 - Agudo Jácome, Leonardo A1 - Manzoni, Anna A1 - Fantin, Andrea A1 - John, Elisabeth A1 - Hodoroaba, Vasile-Dan A1 - Bührig, Sophia A1 - Murugan, Jegatheesan A1 - Marschall, Niklas A1 - George, Janine A1 - Darvishi Kamachali, Reza A1 - Maaß, Robert A1 - Emmerling, Franziska T1 - Chemically complex materials enable sustainable high-performance materials N2 - Chemically complex materials (CCMats) 􀀀 including high-entropy alloys, oxides, and related multi-principal element systems 􀀀 offer a paradigm shift in materials design by leveraging chemical diversity to simultaneously optimize functional, structural, and sustainability criteria. The vastness of the compositional and structural space in CCMats propels the field into an expanding exploratory state. To reconcile functional and structural performance across this immense parameter space remains an open challenge. This Perspective evaluates the opportunities and challenges associated with harnessing chemical complexity across a broad spectrum of applications, such as hydrogen storage, ionic conductors, catalysis, magnetics, dielectrics, semiconductors, optical materials, and multifunctional structural systems. It is delineated how three central design strategies: targeted substitution (SUB), defect engineering (DEF), and diversity management (DIV) enable the reconciliation of high functional performance with long-term structural stability and environmental responsibility. Advances in computational thermodynamics, microstructure simulations, machine learning, and multimodal characterization are accelerating the exploration and optimization of CCMats, while robust data infrastructures and automated synthesis workflows are emerging as essential tools for navigating their complex compositional space. By fostering cross-disciplinary knowledge transfer and embracing data-driven design, CCMats are poised to deliver next-generation materials solutions that address urgent technological, energy, and environmental demands. KW - Chemically complex materials KW - Structural stability KW - Functional performance KW - Design strategies KW - Sustainability PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-655598 UR - https://www.sciencedirect.com/science/article/pii/S1359028626000033?via%3Dihub DO - https://doi.org/10.1016/j.cossms.2026.101256 SN - 1359-0286 VL - 42 SP - 1 EP - 26 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-65559 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kärcher, Victor A1 - Reiker, Tobias A1 - da Costa, Pedro F.G.M. A1 - de Camargo, Andrea S.S. A1 - Zacharias, Helmut T1 - Quantum control in size selected semiconductor quantum dot thin films N2 - We introduce a novel technique for coherent control that employs resonant internally generated fields in CdTe quantum dot (QD) thin films at the L-point. The bulk band gap of CdTe at the L-point amounts to 3.6 eV, with the transition marked by strong Coulomb coupling. Third harmonic generation (λ3 = 343 nm, hν = 3.61 eV) for a fundamental wavelength of λ 1 = 1,030 nm is used to control quantum interference of three-photon resonant paths between the valence and conduction bands. Different thicknesses of the CdTe QDs are used to manipulate the phase relationship between the external fundamental and the internally generated third harmonic, resulting in either suppression or strong enhancement of the resonant third harmonic, while the nonresonant components remain nearly constant. This development could pave the way for new quantum interference–based applications in ultrafast switching of nanophotonic devices. KW - Nonlinear nanophotonics KW - Quantum interference KW - Third harmonic KW - Coherent control KW - Thin films KW - Quantum dots PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625859 DO - https://doi.org/10.1515/nanoph-2024-0529 VL - 14 IS - 2 SP - 229 EP - 239 PB - Walter de Gruyter GmbH AN - OPUS4-62585 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Arai, Marylyn Setsuko A1 - Ravaro, Leandro Piaggi A1 - Brambilla, Gabriel A1 - Maia, Lauro June Queiroz A1 - Reza Dousti, Mohammad A1 - de Camargo, Andrea Simone Stucchi T1 - Upconverting Nanoparticles and Cu(I) Complex-Based Platform for Oxygen Sensing, Thermometry, and Emission Color Tuning N2 - Multifunctional nanoplatforms combine different material properties to meet a wide range of applications, allowing highly customizable systems. In this rapidly advancing research field, we introduce a multifunctional nanomaterial based on the synergy between Tm3+-doped upconverting nanoparticles (UCNPs) and a Cu(I) complex (CuCom). This material is designed for oxygen sensing, optical thermometry, and emission color tuning. In various concentrations, the CuCom complex was electrostatically integrated into a mesoporous silica shell surrounding the core UCNPs (UCNP@mSiO2). The optimized system, UCNP@mSiO2@CuCom-10, was evaluated for different applications. Due to the spectral overlap between the CuCom absorption and the nanoparticles emission, excitation at 980 nm allows most of the UV-blue emission output from the UCNPs to be transferred to the CuCom via luminescent resonance energy transfer (LRET), producing red emission from the molecule. The remaining Tm3+ emission enables optical thermometry, while CuCom’s sensitivity to molecular oxygen supports its application in gas sensing. In upconversion mode, the nanoplatform achieved a Stern−Volmer constant for O2 sensing of 1.64 and demonstrated thermometric relative sensitivities of 0.9% and 1% K−1 at room temperature, with a linear response from 193 to 373 K. Additionally, the emission color of UCNP@mSiO2@CuCom-10 can be tuned from blue to white and yellow, by varying the excitation and temperature, adding further functionality to the system. This multifunctional platform suggests promising applications in biology, medicine, and environmental monitoring. KW - M KW - O2 sensing KW - Upconversion KW - Luminescence resonance energy transfer (LRET) KW - Optical thermometry KW - Mesoporous silica shell PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-625869 SN - 2574-0970 DO - https://doi.org/10.1021/acsanm.4c06351 VL - 8 SP - 854 EP - 862 PB - American Chemical Society (ACS) AN - OPUS4-62586 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Paskin, Alice A1 - Couasnon, Thaïs A1 - Blukis, Roberts A1 - Perez, Jeffrey Paulo H. A1 - Reinsch, Stefan A1 - Roddatis, Vladimir A1 - Syczewski, Marcin A1 - Benning, Liane G. T1 - Temperature-Induced Phase Transitions of Vivianite: In Situ Analysis of a Redox-Driven Crystallization N2 - We document a solid-state, temperature-dependent (25−700 °C), multistage redox transformation of crystalline ferrous iron phosphate, vivianite (Fe3(PO4)2·8H2O). Under anoxic conditions, vivianite breaks down at T > 250 °C into an anhydrous, amorphous intermediate Fe3(PO4)2 phase, yet the bulk shape and morphology of the starting vivianite crystals were retained. This amorphous intermediate phase remained stable until T > 500 °C, after which a redox-dependent crystallization into two different minerals was observed. Under anoxic conditions, the amorphous ferrous intermediate (Fe3(PO4)2) transformed into the crystalline ferrous phosphate (graftonite, (Fe2+)3(PO4)2), while under oxic conditions it crystallized into a ferric phosphate (rodolicoite, Fe3+PO4). Graftonite formation occurs via an exothermic molar enthalpy (ΔHcryst) of −16.7 ± 0.2 kJ mol−1. Rietveld refinements of the two crystalline endmembers (vivianite and graftonite) revealed a unit cell volume decrease of ∼3.1% during the transformation, which was observed by in situ electron microscopic observations as an overall shrinking of the initial vivianite crystals. Despite volume loss and bubble-like features, the original vivianite shape was preserved, indicating a solid-state pseudomorphic transformation. Ex situ XRD and TEM-EELS analyses confirmed the ferrous-to-ferric oxidation, forming rodolicoite, through changes in the Fe geometry and oxidation state. KW - Vivianite KW - Graftonite KW - Crystallization enthalpy KW - Ferrous phosphates PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-640782 DO - https://doi.org/10.1021/acs.inorgchem.5c02399 SN - 0020-1669 VL - 46 IS - 36 SP - 18227 EP - 18236 PB - American Chemical Society (ACS) AN - OPUS4-64078 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rosenbusch, Ivo A1 - Arai, Marylyn Setsuko A1 - Rizzo, Fabio A1 - de Camargo, Andrea S. S. A1 - Ravoo, Bart Jan T1 - A host–guest approach to ratiometric pH sensing using upconversion nanoparticles N2 - A new pH nanosensor based on β-NaYF4:Yb3+/Tm3+ upconversion nanoparticles functionalized with cyclodextrin and a pH-sensitive adamantane-modified nitrobenzoxadiazole dye (NBD-Ad). KW - Host-guest materials KW - Upconversion nanoparticles KW - Ratiometric optical sensors KW - pH sensing PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-637722 DO - https://doi.org/10.1039/d5na00145e SN - 2516-0230 VL - 7 IS - 13 SP - 4142 EP - 4151 PB - Royal Society of Chemistry (RSC) AN - OPUS4-63772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Xie, Zhuocheng A1 - Atila, Achraf A1 - Guénolé, Julien A1 - Korte-Kerzel, Sandra A1 - Al-Samman, Talal A1 - Kerzel, Ulrich T1 - Predicting grain boundary segregation in magnesium alloys: An atomistically informed machine learning approach N2 - Grain boundary (GB) segregation substantially influences the mechanical properties and performance of magnesium (Mg). Atomic-scale modeling, typically using ab-initio or semi-empirical approaches, has mainly focused on GB segregation at highly symmetric GBs in Mg alloys, often failing to capture the diversity of local atomic environments and segregation energies, resulting in inaccurate structure-property predictions. This study employs atomistic simulations and machine learning models to systematically investigate the segregation behavior of common solute elements in polycrystalline Mg at both 0 K and finite temperatures. The machine learning models accurately predict segregation thermodynamics by incorporating energetic and structural descriptors. We found that segregation energy and vibrational free energy follow skew-normal distributions, with hydrostatic stress, an indicator of excess free volume, emerging as an important factor influencing segregation tendency. The local atomic environment’s flexibility, quantified by flexibility volume, is also crucial in predicting GB segregation. Comparing the grain boundary solute concentrations calculated via the Langmuir-McLean isotherm with experimental data, we identified a pronounced segregation tendency for Nd, highlighting its potential for GB engineering in Mg alloys. This work demonstrates the powerful synergy of atomistic simulations and machine learning, paving the way for designing advanced lightweight Mg alloys with tailored properties. KW - Machine learning KW - Grain boundary segregation KW - Magnesium alloys KW - Atomistic simulation PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-638499 DO - https://doi.org/10.1016/j.jma.2025.03.021 SN - 2213-9567 VL - 13 IS - 6 SP - 2636 EP - 2650 PB - Elsevier B.V. AN - OPUS4-63849 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blaeß, Carsten A1 - Boccaccini, A. R. A1 - Müller, Ralf T1 - Sintering and Crystallization of Fluoride-Containing Bioactive Glass F3 N2 - The fluoride-containing bioactive glass F3 with nominal composition (mol%) 44.8 SiO2 - 2.5 P2O3 - 36.5 CaO - 6.6 Na2O - 6.6 K2O - 3.0 CaF2 is a highly promising candidate for bone replacement applications. Its strong crystallization tendency, however, requires a thorough understanding of the interplay between glass powder particle size, surface crystallization, and sintering. Therefore, this study characterizes the sintering and crystallization of bulk specimens and various particle size fractions by differential thermal-analysis, laser scanning, electron microscopy, X-ray diffraction, and Infrared spectroscopy. Particle size fractions < 56 µm were found to fully densify, while crystals growing from the glass particle surface retard sintering of coarser fractions. Small amounts of a non-stoichiometrically calcium phosphosilicate (Ca14.92(PO4)2.35(SiO4)5.65) occurs as the primary crystal phase followed by combeite (Na4Ca4[Si6O18]) as a temporarily dominating phase. The surface crystallization of both pha­ses was found to be mainly responsible for sinter retardation. During later stages of crystallization, additional phases such as cuspidine (Ca4F2Si2O7) and silicorhenanite (Na2Ca4(PO4)2SiO4) occur, but finally monoclinic wollastonite (CaSiO3) forms as the dominant phase. KW - Bioactive Glass KW - Sintering KW - Crystallization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-632482 DO - https://doi.org/10.52825/glass-europe.v3i.2564 SN - 2940-8830 VL - 3 SP - 105 EP - 124 AN - OPUS4-63248 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Waurischk, Tina A1 - Deubener, J. A1 - Müller, Ralf T1 - Internal friction and energy dissipation during fracture in silicate glasses N2 - To obtain a deeper insight into the nature of energy dissipation during fracture, the internal friction of 13 borosilicate, aluminosilicate, soda-lime, and lead-containing glasses, for which inert crack growth data are known, was measured using dynamic mechanical thermal analysis. For asymmetrically bent glass beams, the loss tangent, tan δ, was determined between 0.2 and 50 Hz at temperatures between 273 K and the glass transition temperature, Tg. It was found that the area under the tan δ vs T·Tg−1 curve correlates with the crack growth exponent, n, in the empirical v = v0·KIn relation between crack growth velocity, v, and stress intensity, KI, which indicates that n correlates with the degree of energy dissipation of sub-Tg relaxation phenomena. KW - Glass KW - Internal friction KW - Crack growth PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-631582 DO - https://doi.org/10.1063/5.0255432 SN - 0021-9606 VL - 162 IS - 19 SP - 1 EP - 9 PB - AIP Publishing AN - OPUS4-63158 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Pan, Z. A1 - Waurischk, Tina A1 - Duval, A. A1 - Müller, Ralf A1 - Deubener, J. A1 - Krishnan, N. M. A. A1 - Wondraczek, K. A1 - Wondraczek, L. T1 - Precise Real‐Time Measurement of Liquid Viscosity Using Digital Video Data N2 - Quantitative knowledge of liquid viscosity is of fundamental importance in many areas of materials synthesis and processing. However, the determination of viscosity often relies on specialized experimental equipment, offline experimentation, or invasive procedures, in particular when required in extreme conditions such as at high temperature, high pressure, and in confined or corrosive environments. Here, this study proposes and validates a fast and simple method that mimics the intuitive perception of liquid flow within a quantitative framework. For this, this study employs digital video observation to derive quantitative values of the shear viscosity of liquids, with high precision and rapid acquisition rates. The technique involves capturing liquid dynamics after minor mechanical stimulation. Processed imaging data are indexed by similarity and referenced to a digital database generated with a finite element model, from which values of viscosity are obtained in line. The approach is tested on water at room temperature and on a high‐temperature glass melt. Covering a viscosity range of four orders of magnitude, both yield convincing agreement with tabulated reference data at low computational cost. KW - Image analyses KW - Liquids KW - Materials discovery KW - Similarity analyses KW - Viscosities PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-634606 DO - https://doi.org/10.1002/aisy.202500297 SN - 2640-4567 SP - 1 EP - 12 PB - Wiley AN - OPUS4-63460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -