TY - CONF A1 - Beygi Nasrabadi, Hossein T1 - Platform MaterialDigital (PMD) approach for the integration and management of FAIR low cycle fatigue (LCF) testing data N2 - This study represents the generation and storage of findable, accessible, interoperable, and reusable (FAIR) fatigue testing data by utilizing the Platform MaterialDigital (PMD) core ontology (PMDco) as well as some containerized PMD-server applications. Based on the specifications of the ISO 12106:2017-03 standard [1] and the acquired test reports of the mechanical testing facility, a highly comprehensive process graph of the fatigue testing procedure was created. Consequently, the PROV Ontology (PROVO) and PMDco [2] were used as upper-level ontologies to model the fatigue testing ontology (FTO). A part of the FTO classes hierarchy is shown in Fig. 1, where all the concepts of test procedure, test apparatus, test piece, and test properties were respectively located in the appropriate hierarchies of pmd:Process (prov:Activity), pmd:ProcessingNode (prov:Agent), pmd:Object (prov:Entity), and pmd:ValueObject (prov:Entity) classes. FTO is publicly available via the GitLab repository [3]. Reusing these upper-level ontologies and materials testing standards not only improves FTO's compatibility with other ontologies but also ensures its acceptance and deployment in industry [4]. The fatigue testing process graph has also been designed in such a manner that it allows for the entire mapping of testing metadata. In this respect, low-cycle fatigue (LCF) experiments were carried out on several cast copper alloys at various strain ratios, and the resulting CSV test report files were stored in a public repository [5]. Eventually, the processes of mapping the experimental test data into the fatigue process graph, converting the RDF data, storage of the triples in a triple store, and SPARQL query from the obtained triples are evaluated by different PMD-based tools like PMD OntoDocker [6]. T2 - MSE2024 CY - Darmstadt, Germany DA - 24.09.2024 KW - Digitalization KW - FAIR KW - Low cycle fatigue PY - 2024 AN - OPUS4-61151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ávila Calderón, Luis T1 - Assessing the low cycle fatigue behaviour of additively manufactured Ti-6Al-4V: Challenges and first results N2 - The understanding of process-microstructure-property-performance (PMPP) relationships in additive manufacturing (AM) of metals is highly necessary to achieve wide-spread industrial application and replace conventionally manufactured parts, especially regarding safety-relevant applications. To achieve this understanding, reliable data and knowledge regarding material’s microstructure-property relationships (e.g. the role of defects) is needed, since it represents the base for future more targeted process optimizations and more reliable calculations of performance. However, producing reliable material data and assessing the AM material behaviour is not an easy task: big challenges are e.g. the actual lack of standard testing methods for AM materials and the occasional difficulties in finding one-to-one comparable material data for the conventional counterpart. This work aims to contribute to end this lack of reliable material data and knowledge for the low cycle fatigue behaviour of the most used titanium alloy in aerospace applications (Ti-6Al-4V). For this purpose, two sets of test specimens were investigated. The first set was manufactured from cylindrical rods produced by an optimized DED-L process and the second was manufactured from a hot formed round bar. The test specimens were cyclically loaded until failure in the low-cycle-fatigue (LCF) regime. The tests were carried out according to ISO 12106 between 0.3 to 1.0 % axial strain amplitude from room temperature up to 400°C. The LCF behaviour is described and compared between materials and with literature values based on cyclic deformation curves and strain-based fatigue life curves. Besides, the parameters of Manson-Coffin-Basquin relationship were calculated. The microstructures (initial and after failure) and fracture surfaces were comparative characterized. Thereby, the focus lied on understanding the role of grain morphology and defects on the failure mechanisms and fatigue lifetimes. For this latter characterization, optical microscopy (OM), scanning electron microscopy (SEM) and micro computed tomography (µCT) were used. T2 - 4th International Symposium on Fatigue Design and Material Defects CY - Online meeting DA - 26.05.2020 KW - Ti-6Al-4V KW - Additive manufacturing KW - Low cycle fatigue KW - Micro computed tomography KW - Microstructure PY - 2020 AN - OPUS4-50893 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -