TY - CONF A1 - Stawski, Tomasz T1 - Solution-driven processing of calcium sulfate: the mechanism of the reversible transformation of gypsum to bassanite in brines N2 - Calcium sulfate hemihydrate (CaSO4ᐧ0.5H2O), also known as bassanite, has been used as a precursor to produce gypsum (dihydrate, CaSO4ᐧ2H2O) for various construction and decorative purposes since prehistoric times. The main route to obtain hemihydrate is a thermal treatment of gypsum at temperatures typically between 150 °C and 200 °C to remove some of the structural water. In this contribution, we introduce (Fig. 1) a more efficient and sustainable method (T < 100 °C) that enables the direct, rapid, and reversibly conversion of gypsum to bassanite using reusable high salinity aqueous solutions (brines with c[NaCl] > 4 M). The optimum conditions for the efficientproduction of bassanite in a short time (< 5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the typical behaviour of the bassanite phase in low salt environments. Traditionally, hemihydrate is obtained through a solid state thermal treatment because bassanite is considered to be metastable with respect to gypsum and anhydrite in aqueous solutions, and therefore gypsum-to-bassanite conversion should not occur in water. Its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures is inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline structure for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios. T2 - Granada Münster Discussion Meeting GMDM 10 CY - Münster, Germany DA - 29.11.2023 KW - Gypsum KW - Bassanite KW - Calcium sulfate KW - Recycling KW - Scattering PY - 2024 AN - OPUS4-59162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herzel, Hannes T1 - Rückholbarkeit Klärschlammaschen aus Langzeitlagern N2 - Das Institut für Siedlungswasserwirtschaft (ISA) der RWTH Aachen University sowie die Bundesanstalt für Materialforschung und -prüfung (BAM) untersuchen gemeinsam fünf deponierte KSA, die von drei Deponiebetreibern ausgebaut und zur Verfügung gestellt wurden sind. Im Fokus der Untersuchungen stehen die physikalische und chemische Charakterisierung der deponierten KSA sowie deren P-Rückgewinnungspotenzial bei der Behandlung in thermochemischen sowie nasschemischen Verfahren. Diese Ergebnisse werden im Vergleich mit „frischen“, also nicht deponierten KSA-Proben vergleichbarer Herkunft bewertet, um so den Einfluss der Lagerung auf die KSA zu erfassen. T2 - 4. Sitzung der LAGA AG Sicherstellung der Phosphorrückgewinnung bis 2029 CY - Berlin, Germany DA - 17.07.2025 KW - Deponie KW - Recycling KW - langzeitlagerung KW - Phosphor PY - 2025 AN - OPUS4-64795 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Taube, Mareike Carolin A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Beckmann, T. A1 - Reuter, M. A1 - Stelter, M. ED - Reiser, B. T1 - Recycling von metallurgischen Rückständen - Schmelzversuche zeigen, wie die Tantalrückgewinnung aus Zinnschlacken und weiteren Reststoffen optimiert werden kann N2 - Since the recycling of tantalum bearing post-consumer waste is practically not existent, metallurgical residues are the most important feed for the tantalum recycling. Most tin ores naturally contain significant quantities of refractory metals. During the smelting process in primary tin production these elements are enriched in the slag phase. This slag is a highly valuable raw material for tantalum production due to its considerable concentration of tantalum and its functioning as an additional slag former in further pyrometallurgical treatment. In this paper the first process stage of an existing pyrometallurgical process for tantalum recovery, mainly from low grade pyrometallurgical residues, is discussed. Smelting trials were carried out in a pilot-scale electric arc furnace to analyse the effect of feeding on the activity of carbon as a reducing agent. Therefore, blowing petroleum coke through an iron lance and the manual adding of coke into the melting bath were tested. During the pyrometallurgical treatment elements with a high affinity to carbon were reduced to their carbide form and enriched in the molten iron-based metal phase. The objective of the process was to reduce the oxidic tantalum completely and to enrich it into the metal phase. Furthermore, the transfer of unwanted elements such as titanium into the metal phase was aimed to be avoided. Spoon test specimens were taken from the liquid mineral melt to follow the evolution of the reduction process. The cooled down solidified melting bath was investigated by using the XRD and EDX method to characterise the slag system and to identify relevant mineral phases. N2 - Da das Recycling von tantalhaltigen Post-Consumer-Abfällen praktisch nicht existiert, stellen metallurgische Reststoffe eine äußerst wichtige Rohstoffquelle für das Tantalrecycling dar. Die meisten Zinnerze enthalten von Natur aus erhebliche Mengen an Refraktärmetallen. Diese Elemente werden in den Schlacken der pyrometallurgischen Primärzinngewinnung angereichert. Aufgrund ihrer vergleichsweise hohen Wertstoffkonzentration und ihrer Funktion als zusätzlicher Schlackenbildner stellen diese Schlacken einen wertvollen Rohstoff für die Verhüttung tantalhaltiger Reststoffe dar. In der vorliegenden Arbeit wird ein existierendes Verfahren zur Tantalrückgewinnung diskutiert, dem hauptsächlich pyrometallurgische Rückstände geringer Wertstoffkonzentration als Einsatzstoff dienen. Mit Hilfe des Verfahrens sollte dasoxidisch vorliegende Tantal vollständig reduziert und in der Metallphase angereichert werden. Weiterhin sollte vermieden werden, dass unerwünschte Elemente wie Titan in die Metallphase überführt werden. Ziel der Untersuchung war es, die ablaufenden Reduktionsprozesse besser zu verstehen, um so Ansätze für die Prozessoptimierung identifizieren zu können. KW - Lichtbogenofen KW - Pyrometallurgie KW - Recycling KW - Tantal KW - Zinnschlacke PY - 2020 SN - 0934-3482 VL - 33 SP - 10 EP - 17 PB - Rhombos-Verlag CY - Berlin AN - OPUS4-50656 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Kalinka, Gerhard T1 - Recycling von Faserverbundwerkstoffen N2 - Der Vortrag beschreibt Aktivitäten der BAM zum Recycling von carbonfaser-verstärkten Verbundwerkstoffen. T2 - Fachdialog Recycling von Windenergieanlagen CY - Berlin, Germany DA - 23.09.2024 KW - Polymer Matrix Composite KW - Carbon Fibres KW - Recycling KW - Pyrolysis KW - Recycling by Design PY - 2024 AN - OPUS4-61536 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Piehl, Patrick T1 - Recovery of zinc from steel mill dusts in the rotary kiln by joint treatment with chloride-containing residues N2 - During iron and steel production, several by-products such as slags, dusts and sludges are generated in addition to pig iron and steel as primary products. While established recycling routes exist for slags, there are still considerable recycling problems for other residual materials, especially for filter dusts and sludges containing zinc and lead from waste gas purification. However, the high heavy metal contents make landfilling these dusts and sludges cost-intensive and ecologically problematic. In addition, the relatively high zinc and iron loads represent a valuable material potential, which can make reprocessing of the material with recovery of the zinc and iron loads as secondary raw materials ecologically as well as economically attractive. Against this background, a process is being developed in a cooperative project between Ferro Duo GmbH and the Federal Institute for Materials Research and Testing (BAM), in which the heavy metals (zinc, lead, cadmium, etc.) contained in the filter dusts and sludges are selectively converted into chlorides in a thermochemical process after the addition of a chlorine donor and evaporated at temperatures between 650 and 1100 °C. This process can be used to recover zinc and iron as secondary raw materials. Experiments to date in a batch reactor show that >99% of the zinc and lead can be removed from the treated material. However, a continuous process is necessary for an economical process, which is why this process is transferred to a rotary kiln and relevant process parameters are identified and optimized. The results of these investigations will be presented here. T2 - European Congress and Exhibition on Advanced Materials and Processes 2021 CY - Online meeting DA - 13.09.2021 KW - Elektroofenstaub KW - Gichtgasschlamm KW - Recycling KW - Ressourcenrückgewinnung KW - Zink PY - 2021 AN - OPUS4-53290 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herzel, Hannes T1 - R-Rhenania – Modifiziertes Rhenania Phosphat aus der Klärschlammverbrennung mit thermochemischen Aufschluss N2 - Der Betreiber der Klärschlammverbrennungsanlage Altenstadt (Emter GmbH) integriert einen thermochemischen Prozessschritt in die vorhandene Monoverbrennung und erweitert die Anlage entsprechend, um einen Ausgangsstoff für die Düngemittelproduktion zu erzeugen und damit zur Phosphatrückgewinnung gemäß Klärschlammverordnung (AbfKlärV) beizutragen. Die Umrüstung der Anlage fand im ersten Halbjahr 2024 statt und seit Sommer 2024 steht eine Kapazität für die jährliche Produktion von 15.000 Tonnen schadstoffarmen R-Rhenania Phosphat mit hochwirksamen Phosphatverbindungen zur Verfügung. Diese Demonstrationsanlage wird durch ein wissenschaftliches Monitoring im vom BMFTR geförderte Projekt R-Rhenania (2020-2026) mit u.a. Ökobilanzierungen, Gefäß- und Feldversuche begleitet. Der Projektpartner sePura plant den produzierten Dünger vollständig regional in Bayern zu verwerten T2 - DPP Forum CY - Frankfurt am Main, Germany DA - 08.10.2025 KW - Phosphor KW - Recycling KW - CaNaPO4 KW - Pflanzenversuche KW - Klärschlamm KW - Additiv PY - 2025 AN - OPUS4-64711 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adam, Christian A1 - Herzel, Hannes T1 - R-Rhenania - Modifiziertes Rhenania Phosphat aus Klärschlammasche für Bayern N2 - Im Verbundprojekt R-Rhenania wird eine industrielle Demonstrationsanlage am Standort der Monoverbrennungsanlage Altenstadt der Firma Emter errichtet und im Jahr 2024 den Betrieb aufnehmen. Die vorhandene Rostfeuerung-Monoverbrennung wird so umgebaut, dass ein neues thermochemisches Verfahren integriert werden kann, welches hochwirksame und schadstoffarme Dünger produziert (bis zu 17.000 t/a). Die thermochemischen Produkte werden in Gefäß- und Feldversuchen im ökologischen Landbau auf ihre Düngewirkung getestet. Die Umweltverträglichkeit der Demonstrationsanlage wird untersucht, wie auch die Übertragbarkeit des Verfahrens auf weitere Regionen. T2 - Statusseminar RePhoR CY - Frankfurt am Main, Germany DA - 03.05.2023 KW - Phosphor KW - Monoverbrennung KW - Recycling KW - Nährstoffe KW - Dünger PY - 2023 AN - OPUS4-59486 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herzel, Hannes T1 - Phosphorrückgewinnung in Deutschland: Thermochemisches Verfahren in Altenstadt N2 - Die Firma Emter GmbH betreibt die Klärschlammverbrennungsanlage Altenstadt und hat in die bestehende Monoverbrennung einen thermochemischen Prozess integriert, um hochwirksame und schadstoffarme Düngemittel aus Klärschlamm herzustellen. Die Anlage ist aktuell die größte Phosphor-recyclinganlage in Deutschland mit der die Vorgaben der AbfKlärV bereits frühzeitig umgesetzt werden. Im Prozess wird schwerlösliches Phosphat in pflanzen-verfügbares Phosphat umgewandelt und gleichzeitig werden Schadstoffe thermisch zerstört oder entfernt. Seit Mitte 2024 steht eine Kapazität für die jährliche Produktion von 15.000 Tonnen des sogenannten R-Rhenania- Phosphats bereit. Dieser Recyclingdünger wird nach REACH registriert, erfüllt alle Vorgaben der Düngemittelverordnung und kann in der Landwirtschaft breit eingesetzt werden. Die Eigenschaften des Phosphats, wie etwa dessen Unlöslichkeit in Wasser, entsprechen den Anforderungen des ökologischen Landbaus. Aufgrund dieser Passfähigkeit finden im Rahmen von R-Rhenania seit 2001 bis heute umfangreiche Feldversuche im ökologischen Landbau statt. Das Projekt R-Rhenania begleitet die Phosphorrecyclinganlage mit Untersuchungen zur Produktqualität, mit Gefäßversuchen und Feldversuchen im ökologischen Landbau, mit Ökobilanzierung und der Konfektionierung verschiedener Düngemittelprodukte. T2 - Eröffnungsfeier Altenstadt CY - Altenstadt, Germany DA - 16.10.2026 KW - Phosphor KW - Recycling KW - Großtechnik KW - Dünger KW - Thermochemisch PY - 2025 AN - OPUS4-64824 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Herzel, Hannes T1 - Modifiziertes Rhenania Phosphat aus der Klärschlammverbrennung mit thermochemischem Aufschluss N2 - Der Betreiber der Klärschlammverbrennungsanlage Altenstadt (Emter GmbH) integriert einen thermochemischen Prozessschritt in die vorhandene Monoverbrennung und erweitert die Anlage entsprechend, um einen Ausgangsstoff für die Düngemittelproduktion zu erzeugen und damit zur Phosphatrückgewinnung gemäß Klärschlammverordnung (AbfKlärV) beizutragen. Die Umrüstung der Anlage fand im ersten Halbjahr 2024 statt und seit Sommer 2024 steht eine Kapazität für die jährliche Produktion von 15.000 Tonnen schadstoffarmen R-Rhenania Phosphat mit hochwirksamen Phosphatverbindungen zur Verfügung. Diese Demonstrationsanlage wird durch ein wissenschaftliches Monitoring im vom BMFTR geförderte Projekt R-Rhenania (2020-2026) mit u.a. Ökobilanzierungen, Gefäß- und Feldversuche begleitet. Der Projektpartner sePura plant den produzierten Dünger vollständig regional in Bayern zu verwerten. T2 - P-RÜCK – 11. Phosphor Kongress CY - Stuttgart, Germany DA - 19.11.2025 KW - Phosphor KW - Recycling KW - Thermochemisch KW - Großtechnik KW - Klärschlamm PY - 2025 AN - OPUS4-65018 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Franz-Georg A1 - Kalbe, Ute T1 - Measurement of the Environmental Impact of Materials N2 - This Special Issue, ‘Measurement of the Environmental Impact of Materials’, is focused on the impact that materials have on the environmental compartments of soil, water and air. Leaching and emission processes, including underlying mechanisms, are a recurring topic in most published articles in the present Special Issue. Contributions have come from three continents and numerous countries (USA, Germany, France, Latvia, Poland, Russia, Japan, Korea and Thailand) indicating the global dimension of the subject. KW - Leaching KW - Recycling KW - Nano-materials PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545099 DO - https://doi.org/10.3390/ma15062208 SN - 1996-1944 VL - 15 IS - 6 SP - 1 EP - 3 PB - MDPI CY - Basel AN - OPUS4-54509 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -