TY - JOUR A1 - Weimann, Karin A1 - Adam, Christian A1 - Buchert, M. A1 - Sutter, J. T1 - Environmental Evaluation of Gypsum Plasterboard Recycling N2 - Gypsum is widely used in the construction sector and its worldwide consumption has been increasing for several decades. Depending on the life-time of the used gypsum products, an increase of gypsum in construction and demolition waste follows. Especially against the background of a circular economy, the recycling of waste gypsum is of growing importance. However, the use of recycled gypsum makes only sense if it is environmentally friendly. Therefore, an evaluation of the environmental impacts of an industrial-scale processing for the recycling of post-consumer gypsum waste was conducted. The evaluation was performed with an established life cycle assessment software. Original data provided by industry and complementary data from a database for life cycle assessments were used for the calculations. Two scenarios for recycled gypsum with different transportation distances were calculated. These results are compared with results of the environmental evaluation of gypsum derived from coal-fired power plants (FGD gypsum) and natural gypsum. The results show that utilization of recycled gypsum can be environmentally advantageous compared to the use of natural gypsum or FGD gypsum, especially in the impact categories land transformation and resource consumption (abiotic depletion potential). For most environmental impact categories the specific transportation distances have a strong influence. KW - Gypsum plasterboards KW - Gypsum waste KW - Recycled gypsum KW - Environmental evaluation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522321 DO - https://doi.org/10.3390/min11020101 SN - 2075-163X VL - 11 IS - 2 SP - 101 PB - MDPI CY - Basel, Schweiz AN - OPUS4-52232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vogel, Christian A1 - Helfenstein, J. A1 - Massey, M. A1 - Sekine, R. A1 - Kretzschmar, R. A1 - Beiping, L. A1 - Peter, T. A1 - Chadwick, O. A1 - Tamburini, F. A1 - Rivard, C. A1 - Herzel, Hannes A1 - Adam, Christian A1 - Pradas del Real, A. A1 - Castillo-Michel, H. A1 - Zuin, L. A1 - Wang, D. A1 - Félix, R. A1 - Lassalle-Kaiser, B. A1 - Frossard, E. T1 - Microspectroscopy reveals dust-derived apatite grains in acidic, highly-weathered Hawaiian soils N2 - Dust deposition is an important source of phosphorus (P) to many ecosystems. However, there is little evidence of dust-derived P-containing minerals in soils. Here we studied P forms along a well-described climatic Gradient on Hawaii, which is also a dust deposition gradient. Soil mineralogy and soil P forms from six sites along the climatic gradient were analyzed with bulk (X-ray diffraction and P K-edge X-ray absorption near edge structure) and microscale (X-ray fluorescence, P K-edge X-ray absorption near edge structure, and Raman) analysis methods. In the wettest soils, apatite grains ranging from 5 to 30 μm in size were co-located at the micro-scale with quartz, a known continental dust indicator suggesting recent atmospheric deposition. In addition to co-location with quartz, further evidence of dust-derived P included backward trajectory modeling indicating that dust particles could be brought to Hawaii from the major global dust-loading areas in central Asia and northern Africa. Although it is not certain whether the individual observed apatite grains were derived from long-distance transport of dust, or from local dust sources such as volcanic ash or windblown fertilizer, these observations offer direct evidence that P-containing minerals have reached surface layers of highly-weathered grassland soils through atmospheric deposition. KW - Phosphorus KW - soil KW - microspectroscopy KW - Raman spectroscopy KW - XANES spectroscopy KW - x-ray diffraction PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-511522 DO - https://doi.org/10.1016/j.geoderma.2020.114681 SN - 0166-0918 SN - 1872-6259 VL - 381 SP - 114681-1 EP - 114681-11 PB - Elsevier CY - Amsterdam AN - OPUS4-51152 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vogel, Christian T1 - Application of Diffusive Gradients in Thin-films (DGT) and spectroscopic techniques to analyze phosphorus in soils N2 - A wide range of analytical methods are used to estimate the plant-availability of soil phosphorus (P). Previous investigations showed that analytical methods based on the Diffusive Gradients in Thin films (DGT) technique provide a very good correlations to the amount of bioavailable nutrients and pollutants in environmental samples (Davison 2016, Vogel et al. 2017). However, the DGT results do not identify which P compound of the soil has the high bioavailability. But there are various spectroscopic techniques (infrared, Raman, P K-edge and L-edge XANES and P NMR spectroscopy) available to characterize P species in soils. Therefore, spectroscopic investigation of DGT binding layers after deployment allow us to determine the specific compounds. Nutrients such as phosphorus and nitrogen are often, together with other elements, present as molecules in the environment. These ions are detectable and distinguishable by infrared, P K- and L-edge X-ray absorption near-edge structure (XANES) and NMR spectroscopy, respectively. Additionally, microspectroscopic techniques make it also possible to analyze P compounds on the DGT binding layer with a lateral resolution down to 1 μm2. Therefore, species of elements and compounds of e.g. a spatial soil segment (e.g. rhizosphere) can be mapped and analyzed, providing valuable insight to understand the dynamics of nutrients in the environment. T2 - SPP1685 Closing Conference: New Approaches to Ecosystem Nutrition - Phosphorus and Beyond CY - Freiburg, Germany DA - 25.10.2021 KW - Phosphorus KW - Diffusive gradients in thin-films (DGT) KW - Passive sampling PY - 2021 AN - OPUS4-53641 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vogel, Christian T1 - Ammonium and nitrate in agricultural soils analyzed with the Diffusive Gradients in Thin-films technique N2 - The aim of this study was to investigate the passive sampler method Diffusive Gradients in Thin-films (DGT) for ammonium and nitrate in amended soils. Therefore, we used soils from a pot experiment with maize where nitrogen (N) was supplied as ammonium sulfate nitrate (ASN), without and with a nitrification inhibitor (NI). The additional use of a NI can delay the nitrification in the soil and making the ammonium available for a longer period in the soil solution after its application. Homogenized soil samples were collected directly from each pot after one week of incubation before sowing and after harvesting the maize. Nitrate and ammonium in these soil samples were extracted using DGT devices equipped with a Putolite A520E (for nitrate) and Microlite PrCH (for ammonium) binding layer. Ammonium DGT which determined the mobile and labile ammonium forms based on diffusion and the resupplies from the solid soil phase, only showed a significantly higher amount of extractable ammonium with NI compared to that without NI for some samples. However, significantly lower values were found for nitrate of treatments with NI compared to without NI after harvest. Thus, the lower nitrate amounts for treatments with NI compared to the treatments without NI after harvest indicated the delay of the nitrification process by the NI. Furthermore, we compared also the ammonium and nitrate DGT results to chemical extraction with KCl solutions. The results demonstrated that the trends of DGT results and chemical extraction were complimentary through all the treatments. T2 - International Passive Sampling Workshop (IPSW) 2021 virtual CY - Online meeting DA - 04.11.2021 KW - Phosphorus KW - Diffusive gradients in thin-films (DGT) KW - Ammonium KW - Nitrate PY - 2021 AN - OPUS4-53698 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vogel, Christian T1 - Fluorine K-edge X-ray absorption near-edge structure (XANES) spectroscopy as a novel tool for the characterization of per- and polyfluoroalkyl substances (PFAS) in soils and sludges N2 - Per- and polyfluoroalkyl substances (PFAS) have been used extensively in the past because of their inert chemical character and resistance to degradation by environmental influences. Since the beginning of their commercial use, PFAS have been widely exposed to the environment by application of PFAS in consumer products or as foaming agent in firefighting foams, thus several cases of contaminated soils sites have been reported. Since the number of known PFAS already exceeds 4700, their characterization and direct analysis is challenging given the current available techniques. Here, we introduce the novel fluorine (F) K-edge X-ray absorption near-edge structure (XANES) spectroscopy as a tool to analyze PFAS and inorganic fluorine compounds in contaminated soils and sewage sludges. While F K-edge bulk-XANES spectroscopy provide us information on the overall fluorine bonding in a sample micro X-ray fluorescence (XRF) in combination with F K-edge micro-XANES spectroscopy can also detect minor fluorine compounds and PFAS hotspots in investigated soils and sludges. Additionally, we used the combustion ion chromatography (CIC) to analyze the total amount of all PFAS as a sum parameter (extractable organic fluoride: EOF) in soils and sewage sludges. During combustion in the CIC, the PFAS in the sample get destroyed at temperatures of approx. 1000 °C and converted in inorganic fluorides that subsequently gets quantified by ion chromatography. Thus, for the first time we successfully combined F K-edge XANES spectroscopy and CIC as analytical tools to detect and quantify PFAS contaminants in soils and sewage sludges. T2 - SETAC Europe CY - Online meeting DA - 03.05.2021 KW - Sewage sludge KW - Combustion ion chromatography KW - Soil KW - X-ray absorption near-edge structure (XANES) spectroscopy PY - 2021 AN - OPUS4-52563 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vogel, Christian T1 - Can we use passive samplers for the determination of chromium(VI) in phosphorus fertilizers? N2 - Phosphorus (P) fertilizers from secondary resources became increasingly important in the last years. However, these novel P-fertilizers can also contain toxic pollutants. Chromium in its hexavalent state (Cr(VI)) is regulated with low limit values for agricultural products due to its high toxicity, but the determination of Cr(VI) in these novel fertilizer matrices can be hampered by redox processes that lead to false results. Thus, we applied the passive sampler technique Diffusive Gradients in Thin-films (DGT) for the determination of Cr(VI) in fertilizers and compared the results with the standard wet chemical extraction method (German norm DIN EN 15192) and Cr K-edge X-ray absorption near-edge structure (XANES) spectroscopy. We determined an overall good correlation between the wet chemical extraction and the DGT method. DGT was very sensitive and in most cases selective for the analysis of Cr(VI) in P-fertilizers. However, hardly soluble Cr(VI) compounds cannot be detected with the DGT method since only mobile Cr(VI) is analyzed. Furthermore, Cr K-edge XANES spectroscopy showed that the DGT binding layer also adsorbs small amounts of mobile Cr(III) compounds which leads to overestimated Cr(VI) values. The results of certain types of P-fertilizers containing mobile Cr(III) or partly immobile Cr(VI), showed that optimization of the DGT method is required to avoid over- or underestimation of Cr(VI). T2 - International Passive Sampling Workshop (IPSW) 2021 virtual CY - Online meeting DA - 04.11.2021 KW - Phosphorus KW - Sewage sludge KW - Chromium KW - Fertilizer PY - 2021 AN - OPUS4-53699 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Steckenmesser, D. A1 - Vogel, Christian A1 - Herzel, Hannes A1 - Félix, R. A1 - Adam, Christian A1 - Steffens, D. T1 - Thermal treatment of sewage sludge for phosphorus fertilizer production: a model experiment N2 - Phosphorus (P) resource availability and quality is declining and recycling P-fertilizers from waste materials are becoming increasingly important. One important secondary P resource is sewage sludge (SSL) where P is often bound as aluminum phosphate (Al-P), iron phosphate (Fe-P) and polyphosphate (poly-P), respectively. Thermal treatment in different ways is a promising way in P recycling to produce highly plant-available P-fertilizers. To investigate mechanisms behind transformation of hardly available P-species toward plant-available P forms we treated a model SSL containing different kinds of defined P sources by low-temperature conversion (LTC) at 500 °C and subsequent thermochemical treatment of the LTC product with Na additives (TCT) at 950 °C, respectively. Pot experiments with ryegrass were carried out to determine the plant availability of P of the different treatments. The poly-P (here pyrophosphates) based fertilizers had a very high plant availability after both thermal treatments. During LTC treatment the plant availability of the Fe-P and Al-P variants increased because of the Formation of Fe(II) phosphates and/or pyro-/polyphosphates. Especially the formation of Al-polyphosphate shows a high plant availability. The subsequent TCT further increased strongly the plant availability of the Fe-P variants because of the formation of highly plant-available CaNaPO4. Thus, a direct TCT without prior LTC probably also produce CaNaPO4 and is recommended for Fe-P based SSL. However, a molar Ca/P ratio of � 1 in the fertilizer is favorable for CaNaPO4 formation. Thus, the knowledge on the source of primary P in SSL is essential for choosing the accurate thermal treatment method to produce highly plant-available P-fertilizers from SSL. KW - Phosphorus KW - Sewage sludge KW - X-ray diffraction KW - X-ray absorption near-edge structure (XANES) spectroscopy KW - Fertilizer PY - 2021 DO - https://doi.org/10.1080/01904167.2021.1994595 SN - 0190-4167 VL - 45 IS - 8 SP - 1123 EP - 1133 PB - Taylor & Francis Online AN - OPUS4-53755 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simon, Franz-Georg A1 - Vogel, Christian A1 - Kalbe, Ute T1 - Antimony and vanadium in incineration bottom ash – leaching behavior and conclusions for treatment processes N2 - Due to its large mineral fraction, incineration bottom ash (IBA) from municipal solid waste incineration is an interesting raw material that can be used for road construction or to produce secondary building materials. However, leaching chloride, sulfate, and potentially harmful heavy metals may cause problems in using IBA in civil engineering. Investigating leaching behavior is crucial for the assessment of the environmental compatibility of IBA applications. Various test procedures are available for that purpose. In the present study, a long-term leaching test of a wet-mechanically treated IBA was performed in a lysimeter for almost six years. While concentrations of chloride, sulfate and the majority of the heavy metals started to decrease rapidly with progressive liquid-to-solid ratio (L/S), antimony (Sb) and vanadium (V) behaved differently. At the beginning of the lysimeter test, the Sb and V concentrations were low, but after approximately one year of operation at an L/S ratio of around 0.8 L/kg, a steady increase was observed. It was shown that this increase is the result of low Ca concentrations due to the formation of CaCO3. With the data, the solubility products from Ca-antimonate and Ca-vanadate were calculated. The unusual leaching behavior of Sb and V should be kept in mind when considering field scenarios and evaluating the impact on the environment. KW - Bottom ash KW - Lysimeter KW - Leaching of waste materials KW - Secondary building materials PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-534317 DO - https://doi.org/10.31025/2611-4135/2021.15115 SN - 2611-4135 VL - 16 SP - 75 EP - 81 PB - CISA CY - Padua AN - OPUS4-53431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Franz-Georg T1 - EI-GEO (S&T CALL 2017), Environmental impact of geosynthetics in aquatic systems N2 - 2021 marks the 10th anniversary of the first ERA.Net RUS joint call for European-Russian STI cooperation projects. Pooling the resources of more than 20 European and Russian funding agencies, more than 150 projects were funded with an estimated budget of about € 60 million. Being even larger than many thematic ERA.NETs, the ERA.Net RUS Plus has been the biggest and most successful regional ERA.NET so far. Indicating a strong demand for scientific cooperation, the smaller-scale projects funded within the ERA.Net RUS (Plus) calls perfectly complement Russian participation in the EU Framework Programmes. Not least of all, the ERA-Net RUS calls are examples of successful collaboration at a time when cooperation in other fields is complicated by the politically challenging situation. These calls contributed to keeping the communication channels open. Against this background a dedicated event in late 2021 highlighted what has been achieved within the first decade of the initiative. The project EI-GEO coordinated by BAM was selected as best practice project. The presentation displays the main results of the project and discusses the key success factors. T2 - ERA.Net RUS: Celebrating ten years of multilateral European-Russian Research and Innovation cooperation CY - Online meeting DA - 09.12.2021 KW - Geosynthetics KW - Coastal protection KW - European research area PY - 2021 AN - OPUS4-53965 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Simon, Fabian T1 - A fast and simple extraction method for the determination of PFASs in soil samples - HR-CS-GFMAS a new screening tool N2 - Here, we describe a fast and simple extraction method for the determination of per- and polyfluorinated alkyl substances (PFASs) utilizing extractable organic fluorine (EOF) sum parameter analysis and high resolution-continuum source-graphite furnace molecular absorption spectrometry (HR-CS-GFMAS) in soil samples. After extraction and separation of inorganic and organic fluorinated compounds, organically bound fluorinated compounds were indirectly determined via the molecular absorption of gallium mono-fluoride at 211.248 nm. The implementation of the decisions of the “Stockholm Convention on persistent organic pollutants” as well as the “Protocol on Persistent Organic Pollutants of the Convention on Long-Range Transboundary Air Pollution” of the UNECE include the reduction respectively the elimination of PFASs in the environment. Currently, regulations aim to target single compounds (mostly C8-PFAS). But the PFAS group includes over 4700 substances, which are potentially persistent and toxic, thus target analytical approaches are not suitable for a holistic approach investigating the PFAS pollutant situation. Furthermore, forbidden PFASs are substituted by short-chain PFASs, thus the number of unknow substances is steadily increasing. For this reason, sum parameter approaches are more suitable to investigate and assess the pollution situation as well as derive exposure limits. Our developed analytical method was successfully applied to determine PFASs in soil samples from a polluted site. In view of steadily increasing numbers of PFAS substances, our method will make an important contribution in assessing the pollution situation as well as support policy makers in deriving exposure limits for PFAS in the future. T2 - ENSOr - International Workshop on Emerging policy challenges on new soil contaminants CY - Online Meeting DA - 06.05.2021 KW - PFAS KW - HR-CS-GFMAS KW - Soil KW - Sediment PY - 2021 AN - OPUS4-52608 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schraut, Katharina A1 - Kargl, F. A1 - Adam, Christian A1 - Ivashko, O. T1 - In situ synchrotron XRD measurements during solidification of a melt in the CaO–SiO2 system using an aerodynamic levitation system N2 - Phase formation and evolution was investigated in the CaO–SiO2 system in the range of 70–80 mol% CaO. The samples were container-less processed in an aerodynamic levitation system and crystallization was followed in situ by synchrotron x-ray diffraction at the beamline P21.1 at the German electron synchrotron (DESY). Modification changes of di- and tricalcium silicate were observed and occurred at lower temperatures than under equilibrium conditions. Despite deep sample undercooling, no metastable phase formation was observed within the measurement timescale of 1 s. For the given cooling rates ranging from 300 K s−1 to about 1 K s−1, no decomposition of tricalcium silicate was observed. No differences in phase evolution were observed between reducing and oxidizing conditions imposed by the levitation gas (Ar and Ar + O2). We demonstrate that this setup has great potential to follow crystallization in refractory oxide liquids in situ. For sub-second primary phase formation faster detection and for polymorph detection adjustments in resolution have to be implemented. KW - Aerodynamic levitation KW - Calcium silicate KW - Phase formation KW - Oxide melts KW - In situ synchrotron x-ray diffraction PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-526952 DO - https://doi.org/10.1088/1361-648X/abf7e1 VL - 33 IS - 26 SP - 264003 (12pp) PB - IOP Publishing AN - OPUS4-52695 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian A1 - Stephan, D. A1 - Meng, Birgit A1 - Simon, Sebastian A1 - von Werder, Julia T1 - Synthesis and characterisation of alites from reduced basic oxygen furnace slags N2 - Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment. In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC. If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases. KW - BOFS KW - Hydration products KW - Thermal analysis KW - X-ray diffraction PY - 2021 DO - https://doi.org/10.1016/j.cemconres.2021.106518 SN - 0008-8846 VL - 147 SP - 6518 PB - Elsevier Ltd. AN - OPUS4-52939 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina T1 - Reductive treatment of steel making slags to produce a hydraulic binder and crude iron N2 - Steelmaking slags are a by-product of steel production, that are currently used primarily in road construction, earthwork, and hydraulic engineering. In this use, the iron bound in the steelmaking slags (< 30 wt.%) is lost. Recovery of iron from steelmaking slags is possible by thermochemical reductive treatment. The reductive treatment of liquid steelmaking slags causes iron oxides to be reduced to metallic iron, which separates from the mineral phase due to its higher density. The chemical composition of the mineral phase is thus adapted to that of the Portland cement clinker and the mineral alite, the most important component of Portland cement, is formed. This way, crude iron can be recovered, and at the same time a hydraulic binder can be produced. This process, however, is uneconomical due to the high temperatures required (~1800 °C). In the current project, the process is to be adapted so that the reduction of liquid steelmaking slag can be carried out at ~1600 °C. The chemical composition is to be modified in such a way that the melting temperature of the slags as well as their viscosity are in a technically suitable range and still a product with good cementitious properties is obtained. T2 - LithiumDays CY - Online meeting DA - 06.12.2021 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2021 AN - OPUS4-56081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina T1 - Portland cement clinker from reduced basic oxygen furnace slag N2 - Basic oxygen furnace slag (BOFS) is a by-product of the steelmaking process, of which about 10.4 Mt are produced annually in the European Union. Besides its predominant use in road construction, earthwork, and hydraulic engineering, it is also possible to use BOFS as a source material for Portland cement clinker. The main difference in the chemical composition of BOFS from the chemical composition of Portland cement clinker is its high content of iron oxides (7-50 wt.%). In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via thermochemical reductive treatment. Carbothermal treatment of liquid BOFS causes reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The produced low-iron mineral product was chemically similar to Portland cement clinker and contained the most important Portland cement mineral alite (Ca3SiO5) as main component. Besides alite, the mineral product contained other Portland cement clinker constituents such as belite (β-Ca2SiO4) and tricalcium aluminate (Ca3Al2O6). The production of Portland cement clinker and crude iron from BOFS has economic and ecological benefits for both the cement and steel industry. Cement clinker from reduced BOFS may be used as a substitute for cement clinker from conventional cement production, thereby CO2 emissions will be reduced. The steel industry benefits from a high-value application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. However, reductive treatment requires high temperatures and, for economic reasons, has to be carried out immediately after casting of the liquid BOFS, which is a logistical challenge for most steel plants. A cost-benefit analysis is therefore essential. T2 - European Congress and Exhibition on Advanced Materials and Processes CY - Online meeting DA - 13.09.2021 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2021 AN - OPUS4-53475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina T1 - Hydraulic reactivity of alite rich material from post-treated basic oxygen furnace slags N2 - Basic oxygen furnace slags (BOFS) are a by-product of steel production. In 2016, 10.4 Mt of BOFS were produced in the European Union (EU). The main part of BOFS is used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. However, it is also possible to produce higher value products from BOFS. For example, many researchers have investigated the possibility of producing Portland cement clinker and crude iron from BOFS by a carbothermal post-treatment. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The carbothermal treatment reduces the iron oxides in the BOFS to metallic iron, which accumulates at the bottom of the furnace by density separation. In addition to metallic iron, the process generates a mineral product rich in the tricalcium silicate solid solution alite. As the main constituent of Portland cement clinker, the hydraulic reactive mineral alite is of high economic importance. In previous studies, the hydraulic reactivity of the mineral product was investigated by testing the compressive strength of blends with 70 wt.% ordinary Portland cement (OPC). Recent investigations focused on the hydraulic properties of the pure mineral product from the reduced BOFS. The heat of hydration of the mineral product was measured by isothermal calorimetry and compared with the heat of hydration of a synthetic low-iron slag and OPC. In addition, the formation of hydration products was investigated with differential scanning calorimetry (DSC) and x-ray diffraction analysis (XRD) on freeze-dried samples after defined curing times. The results of the calorimetric measurements indicate that the mineral product produced less heat of hydration and its reaction was delayed compared to the synthetic low-iron slag and OPC. Hydration products such as portlandite and calcium silicate hydrates (C-S-H) formed later and in lower amounts. The production of a hydraulic material from BOFS by reductive treatment is of great interest to both the cement and steel industries. The substitution of cement clinker in OPC with a hydraulic material such as reduced BOFS leads to a reduction in greenhouse gas emissions from cement production. The steel industry benefits from an application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. Furthermore, it may be possible to return the recovered crude iron to production. T2 - 3rd European Mineralogical Conference CY - Cracow, Poland DA - 30.08.2021 KW - BOFS KW - Calcium silicate KW - Hydraulic reactivity PY - 2021 AN - OPUS4-53473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scholz, Philipp A1 - Putna-Nimane, I. A1 - Barda, I. A1 - Liepina-Leimane, I. A1 - Strode, E. A1 - Kileso, A. A1 - Esiukova, E. A1 - Chubarenko, B. A1 - Purina, I. A1 - Simon, Franz-Georg T1 - Environmental impact of geosynthetics in coastal protection N2 - Geosynthetic materials are applied in measures for coastal protection. Weathering or any damage of constructions, as shown by a field study in Kaliningrad Oblast (Russia), could lead to the littering of the beach or the sea (marine littering) and the discharge of possibly harmful additives into the marine environment. The ageing behavior of a widely used geotextile made of polypropylene was studied by artificial accelerated ageing in water-filled autoclaves at temperatures of 30 to 80 °C and pressures of 10 to 50 bar. Tensile strength tests were used to evaluate the progress of ageing, concluding that temperature rather than pressure was the main factor influencing the ageing of geotextiles. Using a modified Arrhenius equation, it was possible to calculate the half-life for the loss of 50% of the strain, which corresponds to approximately 330 years. Dynamic surface leaching and ecotoxicological tests were performed to determine the possible release of contaminants. No harmful effects on the test organisms were observed. KW - Geosynthetics KW - Geotextiles KW - Dynamic surface leaching test KW - Artificial ageing KW - Marine littering PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520576 DO - https://doi.org/10.3390/ma14030634 SN - 1996-1944 VL - 14 IS - 3 (Special issue: Measurement of the environmental impact of materials) SP - 634-1 EP - 634-13 PB - MDPI CY - Basel AN - OPUS4-52057 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schoknecht, Ute A1 - Mathies, Helena A1 - Lisec, Jan T1 - Leaching and transformation of film preservatives in paints induced by combined exposure to ultraviolet radiation and water contact under controlled laboratory conditions N2 - Stormwater from urban areas can transport biocidally active substances and related transformation products from buildings into the environment. The occurrence of these substances in urban runoff depends on the availability of water, and on ultraviolet radiation exposure that causes photolytic reactions. In a systematic laboratory study, painted test specimens were exposed to either ultraviolet radiation, water contact, or a combination of both. Leaching of the biocidally active substances carbendazim, diuron, octylisothiazolinone, terbutryn, and selected transformation products of terbutryn and diuron were observed under various exposure conditions. Remaining concentrations of these substances in the paint were quantified. It was demonstrated that the distribution of active substances and transformation products in eluates and in the coatings themselves differs with exposure conditions. Strategies for environmental monitoring of biocide emissions need to consider the most relevant transformation products. However, environmental concentrations of biocidally active substances and transformation products depend on earlier exposure conditions. As a consequence, monitoring data cannot describe emission processes and predict expected leaching of biocidally active substances from buildings if the data are collected only occasionally. KW - Substance release KW - Construction products KW - Biocides KW - Transformation KW - UV radiation KW - Water contact PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-532114 DO - https://doi.org/10.3390/w13172390 SN - 2073-4441 VL - 13 IS - 17 SP - 1 EP - 16 PB - MDPI CY - Basel AN - OPUS4-53211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlögel, Kai A1 - Loose, Florian T1 - Enhancing the Sustainability of Carbon Fibre Reinforced Polymers (CFRP Strategies for Effective Feedstock Recycling as Reducing Agents in Pyrometallurgy N2 - Despite its contribution to tackling climate change by lightweight design, growing CFRP production also results in a global waste generation of 62 kt/a. Accordingly, the energy-intensive production process of carbon fibers (CF) necessitates sustainable recycling solutions. Herein we will give an overview of current recycling processes, discuss their limitations and present a novel approach for safe treatment of CF unsuitable for material recovery . Our project CF Pyro examines feedstock recycling in pyrometallurgical processes, focusing on reactivity of CF, process stability and prevention of hazardous WHO fiber release. Besides fundamental experimental breakthroughs, their broader impact on circular economy will be presented. T2 - CU Online Forum „Composites and Sustainability“ CY - Online meeting DA - 29.06.2021 KW - Carbon Fibers KW - Recycling KW - Electric Arc Furnace KW - CFRP KW - Pyrometallurgy KW - Steelmaking PY - 2021 AN - OPUS4-52920 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Roesch, Philipp A1 - Vogel, Christian A1 - Huthwelker, T. A1 - Wittwer, Philipp A1 - Simon, Franz-Georg T1 - Investigation of per‑ and polyfluoroalkyl substances (PFAS) in soils and sewage sludges by fluorine K‑edge XANES spectroscopy and combustion ion chromatography N2 - For the first time, fluorine K-edge X-ray absorption near-edge structure (XANES) spectroscopy was applied to detect per- and polyfluoroalkyl substances (PFAS) in various soil and sewage sludge samples. The method can be used to determine the speciation of inorganic and organic fluorides, without pre-treatment of solid samples. Therefore, XANES spectra of several inorganic fluorides as well as selected fluorinated organic compounds were recorded. While inorganic fluorides partially exhibit a variety of sharp spectral features in the XANES spectrum, almost all inspected organofluorine compounds show two distinct broad features at 688.5 and 692.0 eV. Moreover, the peak intensity ratio 688.5 eV/692.0 eV in the PFAS XANES spectrum can be inversely correlated to the chain length of the perfluoro sulfonic acid group. The detection of targeted PFAS by bulk-XANES spectroscopy in combination with linear combination fitting in soils and sewage sludges was not applicable due to the low organic fluorine to total fluorine ratio of the samples (0.01–1.84%). Nonetheless, direct analysis of pure PFAS revealed that analysis of organofluorine species might be achieved in higher concentrated samples. Furthermore, quantitative measurements by combustion ion chromatography (CIC) evaluated as sum parameters extractable organically bound fluorine (EOF) and total fluorine (TF) emphasize that besides soils, sewage sludges are a significant source of organic fluorine in agriculture (154–7209 μg/kg). KW - Sewage sludge KW - Combustion ion chromatography KW - Oil KW - X-ray absorption near-edge structure (XANES) spectroscopy KW - Per- and polyfluoroalkyl substances (PFAS) PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-538953 DO - https://doi.org/10.1007/s11356-021-17838-z VL - 29 IS - 18 SP - 26889 EP - 26899 PB - Springer AN - OPUS4-53895 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Roesch, Philipp T1 - Investigation of PFAS Contaminated Solid Matrices by Combustion Ion Chromatography (CIC) - Development of EOF and AOF as Sum Parameters in Environmental Analysis N2 - Per- and polyfluoralkyl surfactants (PFAS) are industrially produced surface chemicals used in daily applications that have gained public and political attention due their unnaturally high appearance in drinking water, nourishments and soils.[1] Their chemical structures exhibit both lipophilic and hydrophilic properties, leading to a highly inert and persistent character.[2] Various PFAS have shown to be bioaccumulative in plants and animals, and some have been characterized as highly toxic when ingested.[3] When exposed to the environment, PFAS slowly get mobilized by natural water resources, leading to contamination of large areas of soil and natural water sources.[4] While PFAS contamination of drinking water has been investigated intensively, perfluoralkyl contamination of soils has been rarely examined as of yet. At the same time, an increasing amount of PFAS contamination sites are being discovered worldwide, calling for a sophisticated strategy towards analytical characterization.[5] Since the number of known PFAS already exceeds 4700, the established sum parameters like extractable organic fluorine (EOF) and adsorbable organic fluorine (AOF) are key elements to fully survey the impact of exposure.[6] Simultaneously, innovative soil remediation strategies are required to contain environmental destruction and to minimize further spreading of contaminants.[7] Addressing these challenges requires suitable analytical devices that are capable of mobilizing PFAS in the solid as well as in the liquid phase. The use of combustion ion chromatography (CIC) enables analysis of both immobile and volatile PFAS and allows the detection of both total fluorine (TF) and EOF or AOF of a given soil or aqueous sample. Based on preliminary results, the clean-up of a PFAS contaminated matrix is monitored via EOF detection over time. Additionally, we tested the effectiveness of urea (CH₄N₂O) as fluoride scavenger with the aim to improve the separation of inorganic and organic fluorine and therefore, to improve AOF accuracy. The presented findings can be contributive with regard to future AOF/EOF sum parameter development and application. T2 - Eurosoil 2021 CY - Online meeting DA - 23.08.2021 KW - PFAS KW - Sum parameter analyis KW - Combustion ion chromatography PY - 2021 AN - OPUS4-53195 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -