TY - JOUR A1 - Weimann, Karin A1 - Adam, Christian A1 - Buchert, M. A1 - Sutter, J. T1 - Environmental Evaluation of Gypsum Plasterboard Recycling N2 - Gypsum is widely used in the construction sector and its worldwide consumption has been increasing for several decades. Depending on the life-time of the used gypsum products, an increase of gypsum in construction and demolition waste follows. Especially against the background of a circular economy, the recycling of waste gypsum is of growing importance. However, the use of recycled gypsum makes only sense if it is environmentally friendly. Therefore, an evaluation of the environmental impacts of an industrial-scale processing for the recycling of post-consumer gypsum waste was conducted. The evaluation was performed with an established life cycle assessment software. Original data provided by industry and complementary data from a database for life cycle assessments were used for the calculations. Two scenarios for recycled gypsum with different transportation distances were calculated. These results are compared with results of the environmental evaluation of gypsum derived from coal-fired power plants (FGD gypsum) and natural gypsum. The results show that utilization of recycled gypsum can be environmentally advantageous compared to the use of natural gypsum or FGD gypsum, especially in the impact categories land transformation and resource consumption (abiotic depletion potential). For most environmental impact categories the specific transportation distances have a strong influence. KW - Gypsum plasterboards KW - Gypsum waste KW - Recycled gypsum KW - Environmental evaluation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522321 DO - https://doi.org/10.3390/min11020101 SN - 2075-163X VL - 11 IS - 2 SP - 101 PB - MDPI CY - Basel, Schweiz AN - OPUS4-52232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vogel, Christian A1 - Helfenstein, J. A1 - Massey, M. A1 - Sekine, R. A1 - Kretzschmar, R. A1 - Beiping, L. A1 - Peter, T. A1 - Chadwick, O. A1 - Tamburini, F. A1 - Rivard, C. A1 - Herzel, Hannes A1 - Adam, Christian A1 - Pradas del Real, A. A1 - Castillo-Michel, H. A1 - Zuin, L. A1 - Wang, D. A1 - Félix, R. A1 - Lassalle-Kaiser, B. A1 - Frossard, E. T1 - Microspectroscopy reveals dust-derived apatite grains in acidic, highly-weathered Hawaiian soils N2 - Dust deposition is an important source of phosphorus (P) to many ecosystems. However, there is little evidence of dust-derived P-containing minerals in soils. Here we studied P forms along a well-described climatic Gradient on Hawaii, which is also a dust deposition gradient. Soil mineralogy and soil P forms from six sites along the climatic gradient were analyzed with bulk (X-ray diffraction and P K-edge X-ray absorption near edge structure) and microscale (X-ray fluorescence, P K-edge X-ray absorption near edge structure, and Raman) analysis methods. In the wettest soils, apatite grains ranging from 5 to 30 μm in size were co-located at the micro-scale with quartz, a known continental dust indicator suggesting recent atmospheric deposition. In addition to co-location with quartz, further evidence of dust-derived P included backward trajectory modeling indicating that dust particles could be brought to Hawaii from the major global dust-loading areas in central Asia and northern Africa. Although it is not certain whether the individual observed apatite grains were derived from long-distance transport of dust, or from local dust sources such as volcanic ash or windblown fertilizer, these observations offer direct evidence that P-containing minerals have reached surface layers of highly-weathered grassland soils through atmospheric deposition. KW - Phosphorus KW - soil KW - microspectroscopy KW - Raman spectroscopy KW - XANES spectroscopy KW - x-ray diffraction PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-511522 DO - https://doi.org/10.1016/j.geoderma.2020.114681 SN - 0166-0918 SN - 1872-6259 VL - 381 SP - 114681-1 EP - 114681-11 PB - Elsevier CY - Amsterdam AN - OPUS4-51152 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vogel, Christian A1 - Huang, L. T1 - Ammonium and nitrate in agricultural soils analyzed with the Diffusive Gradients in Thin-films technique N2 - The aim of this study was to investigate the passive sampler method Diffusive Gradients in Thin-films (DGT) for ammonium and nitrate in amended soils. Therefore, we used soils from a pot experiment with maize where nitrogen (N) was supplied as ammonium sulfate nitrate (ASN), without and with a nitrification inhibitor (NI). The additional use of a NI can delay the nitrification in the soil and making the ammonium available for a longer period in the soil solution after its application. Homogenized soil samples were collected directly from each pot after one week of incubation before sowing and after harvesting the maize. Nitrate and ammonium in these soil samples were extracted using DGT devices equipped with a Putolite A520E (for nitrate) and Microlite PrCH (for ammonium) binding layer. Ammonium DGT which determined the mobile and labile ammonium forms based on diffusion and the resupplies from the solid soil phase, only showed a significantly higher amount of extractable ammonium with NI compared to that without NI for some samples. However, significantly lower values were found for nitrate of treatments with NI compared to without NI after harvest. Thus, the lower nitrate amounts for treatments with NI compared to the treatments without NI after harvest indicated the delay of the nitrification process by the NI. Furthermore, we compared also the ammonium and nitrate DGT results to chemical extraction with KCl solutions. The results demonstrated that the trends of DGT results and chemical extraction were complimentary through all the treatments. T2 - International Passive Sampling Workshop (IPSW) 2021 virtual CY - Online meeting DA - 04.11.2021 KW - Phosphorus KW - Diffusive gradients in thin-films (DGT) KW - Ammonium KW - Nitrate PY - 2021 AN - OPUS4-53698 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Vogel, Christian A1 - Krüger, O. A1 - Gentzmann, Marie A1 - Adam, Christian T1 - Can we use passive samplers for the determination of chromium(VI) in phosphorus fertilizers? N2 - Phosphorus (P) fertilizers from secondary resources became increasingly important in the last years. However, these novel P-fertilizers can also contain toxic pollutants. Chromium in its hexavalent state (Cr(VI)) is regulated with low limit values for agricultural products due to its high toxicity, but the determination of Cr(VI) in these novel fertilizer matrices can be hampered by redox processes that lead to false results. Thus, we applied the passive sampler technique Diffusive Gradients in Thin-films (DGT) for the determination of Cr(VI) in fertilizers and compared the results with the standard wet chemical extraction method (German norm DIN EN 15192) and Cr K-edge X-ray absorption near-edge structure (XANES) spectroscopy. We determined an overall good correlation between the wet chemical extraction and the DGT method. DGT was very sensitive and in most cases selective for the analysis of Cr(VI) in P-fertilizers. However, hardly soluble Cr(VI) compounds cannot be detected with the DGT method since only mobile Cr(VI) is analyzed. Furthermore, Cr K-edge XANES spectroscopy showed that the DGT binding layer also adsorbs small amounts of mobile Cr(III) compounds which leads to overestimated Cr(VI) values. The results of certain types of P-fertilizers containing mobile Cr(III) or partly immobile Cr(VI), showed that optimization of the DGT method is required to avoid over- or underestimation of Cr(VI). T2 - International Passive Sampling Workshop (IPSW) 2021 virtual CY - Online meeting DA - 04.11.2021 KW - Phosphorus KW - Sewage sludge KW - Chromium KW - Fertilizer PY - 2021 AN - OPUS4-53699 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Steckenmesser, D. A1 - Vogel, Christian A1 - Herzel, Hannes A1 - Félix, R. A1 - Adam, Christian A1 - Steffens, D. T1 - Thermal treatment of sewage sludge for phosphorus fertilizer production: a model experiment N2 - Phosphorus (P) resource availability and quality is declining and recycling P-fertilizers from waste materials are becoming increasingly important. One important secondary P resource is sewage sludge (SSL) where P is often bound as aluminum phosphate (Al-P), iron phosphate (Fe-P) and polyphosphate (poly-P), respectively. Thermal treatment in different ways is a promising way in P recycling to produce highly plant-available P-fertilizers. To investigate mechanisms behind transformation of hardly available P-species toward plant-available P forms we treated a model SSL containing different kinds of defined P sources by low-temperature conversion (LTC) at 500 °C and subsequent thermochemical treatment of the LTC product with Na additives (TCT) at 950 °C, respectively. Pot experiments with ryegrass were carried out to determine the plant availability of P of the different treatments. The poly-P (here pyrophosphates) based fertilizers had a very high plant availability after both thermal treatments. During LTC treatment the plant availability of the Fe-P and Al-P variants increased because of the Formation of Fe(II) phosphates and/or pyro-/polyphosphates. Especially the formation of Al-polyphosphate shows a high plant availability. The subsequent TCT further increased strongly the plant availability of the Fe-P variants because of the formation of highly plant-available CaNaPO4. Thus, a direct TCT without prior LTC probably also produce CaNaPO4 and is recommended for Fe-P based SSL. However, a molar Ca/P ratio of � 1 in the fertilizer is favorable for CaNaPO4 formation. Thus, the knowledge on the source of primary P in SSL is essential for choosing the accurate thermal treatment method to produce highly plant-available P-fertilizers from SSL. KW - Phosphorus KW - Sewage sludge KW - X-ray diffraction KW - X-ray absorption near-edge structure (XANES) spectroscopy KW - Fertilizer PY - 2021 DO - https://doi.org/10.1080/01904167.2021.1994595 SN - 0190-4167 VL - 45 IS - 8 SP - 1123 EP - 1133 PB - Taylor & Francis Online AN - OPUS4-53755 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schraut, Katharina A1 - Kargl, F. A1 - Adam, Christian A1 - Ivashko, O. T1 - In situ synchrotron XRD measurements during solidification of a melt in the CaO–SiO2 system using an aerodynamic levitation system N2 - Phase formation and evolution was investigated in the CaO–SiO2 system in the range of 70–80 mol% CaO. The samples were container-less processed in an aerodynamic levitation system and crystallization was followed in situ by synchrotron x-ray diffraction at the beamline P21.1 at the German electron synchrotron (DESY). Modification changes of di- and tricalcium silicate were observed and occurred at lower temperatures than under equilibrium conditions. Despite deep sample undercooling, no metastable phase formation was observed within the measurement timescale of 1 s. For the given cooling rates ranging from 300 K s−1 to about 1 K s−1, no decomposition of tricalcium silicate was observed. No differences in phase evolution were observed between reducing and oxidizing conditions imposed by the levitation gas (Ar and Ar + O2). We demonstrate that this setup has great potential to follow crystallization in refractory oxide liquids in situ. For sub-second primary phase formation faster detection and for polymorph detection adjustments in resolution have to be implemented. KW - Aerodynamic levitation KW - Calcium silicate KW - Phase formation KW - Oxide melts KW - In situ synchrotron x-ray diffraction PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-526952 DO - https://doi.org/10.1088/1361-648X/abf7e1 VL - 33 IS - 26 SP - 264003 (12pp) PB - IOP Publishing AN - OPUS4-52695 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian A1 - Stephan, D. A1 - Meng, Birgit A1 - Simon, Sebastian A1 - von Werder, Julia T1 - Synthesis and characterisation of alites from reduced basic oxygen furnace slags N2 - Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment. In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC. If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases. KW - BOFS KW - Hydration products KW - Thermal analysis KW - X-ray diffraction PY - 2021 DO - https://doi.org/10.1016/j.cemconres.2021.106518 SN - 0008-8846 VL - 147 SP - 6518 PB - Elsevier Ltd. AN - OPUS4-52939 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian T1 - Reductive treatment of steel making slags to produce a hydraulic binder and crude iron N2 - Steelmaking slags are a by-product of steel production, that are currently used primarily in road construction, earthwork, and hydraulic engineering. In this use, the iron bound in the steelmaking slags (< 30 wt.%) is lost. Recovery of iron from steelmaking slags is possible by thermochemical reductive treatment. The reductive treatment of liquid steelmaking slags causes iron oxides to be reduced to metallic iron, which separates from the mineral phase due to its higher density. The chemical composition of the mineral phase is thus adapted to that of the Portland cement clinker and the mineral alite, the most important component of Portland cement, is formed. This way, crude iron can be recovered, and at the same time a hydraulic binder can be produced. This process, however, is uneconomical due to the high temperatures required (~1800 °C). In the current project, the process is to be adapted so that the reduction of liquid steelmaking slag can be carried out at ~1600 °C. The chemical composition is to be modified in such a way that the melting temperature of the slags as well as their viscosity are in a technically suitable range and still a product with good cementitious properties is obtained. T2 - LithiumDays CY - Online meeting DA - 06.12.2021 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2021 AN - OPUS4-56081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar A1 - Adam, Christian T1 - Hydraulic reactivity of alite rich material from post-treated basic oxygen furnace slags N2 - Basic oxygen furnace slags (BOFS) are a by-product of steel production. In 2016, 10.4 Mt of BOFS were produced in the European Union (EU). The main part of BOFS is used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. However, it is also possible to produce higher value products from BOFS. For example, many researchers have investigated the possibility of producing Portland cement clinker and crude iron from BOFS by a carbothermal post-treatment. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The carbothermal treatment reduces the iron oxides in the BOFS to metallic iron, which accumulates at the bottom of the furnace by density separation. In addition to metallic iron, the process generates a mineral product rich in the tricalcium silicate solid solution alite. As the main constituent of Portland cement clinker, the hydraulic reactive mineral alite is of high economic importance. In previous studies, the hydraulic reactivity of the mineral product was investigated by testing the compressive strength of blends with 70 wt.% ordinary Portland cement (OPC). Recent investigations focused on the hydraulic properties of the pure mineral product from the reduced BOFS. The heat of hydration of the mineral product was measured by isothermal calorimetry and compared with the heat of hydration of a synthetic low-iron slag and OPC. In addition, the formation of hydration products was investigated with differential scanning calorimetry (DSC) and x-ray diffraction analysis (XRD) on freeze-dried samples after defined curing times. The results of the calorimetric measurements indicate that the mineral product produced less heat of hydration and its reaction was delayed compared to the synthetic low-iron slag and OPC. Hydration products such as portlandite and calcium silicate hydrates (C-S-H) formed later and in lower amounts. The production of a hydraulic material from BOFS by reductive treatment is of great interest to both the cement and steel industries. The substitution of cement clinker in OPC with a hydraulic material such as reduced BOFS leads to a reduction in greenhouse gas emissions from cement production. The steel industry benefits from an application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. Furthermore, it may be possible to return the recovered crude iron to production. T2 - 3rd European Mineralogical Conference CY - Cracow, Poland DA - 30.08.2021 KW - BOFS KW - Calcium silicate KW - Hydraulic reactivity PY - 2021 AN - OPUS4-53473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar A1 - Adam, Christian T1 - Portland cement clinker from reduced basic oxygen furnace slag N2 - Basic oxygen furnace slag (BOFS) is a by-product of the steelmaking process, of which about 10.4 Mt are produced annually in the European Union. Besides its predominant use in road construction, earthwork, and hydraulic engineering, it is also possible to use BOFS as a source material for Portland cement clinker. The main difference in the chemical composition of BOFS from the chemical composition of Portland cement clinker is its high content of iron oxides (7-50 wt.%). In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via thermochemical reductive treatment. Carbothermal treatment of liquid BOFS causes reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The produced low-iron mineral product was chemically similar to Portland cement clinker and contained the most important Portland cement mineral alite (Ca3SiO5) as main component. Besides alite, the mineral product contained other Portland cement clinker constituents such as belite (β-Ca2SiO4) and tricalcium aluminate (Ca3Al2O6). The production of Portland cement clinker and crude iron from BOFS has economic and ecological benefits for both the cement and steel industry. Cement clinker from reduced BOFS may be used as a substitute for cement clinker from conventional cement production, thereby CO2 emissions will be reduced. The steel industry benefits from a high-value application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. However, reductive treatment requires high temperatures and, for economic reasons, has to be carried out immediately after casting of the liquid BOFS, which is a logistical challenge for most steel plants. A cost-benefit analysis is therefore essential. T2 - European Congress and Exhibition on Advanced Materials and Processes CY - Online meeting DA - 13.09.2021 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2021 AN - OPUS4-53475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -