TY - JOUR A1 - Taube, Mareike Carolin A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Beckmann, T. A1 - Reuter, M. A1 - Stelter, M. ED - Reiser, B. T1 - Recycling von metallurgischen Rückständen - Schmelzversuche zeigen, wie die Tantalrückgewinnung aus Zinnschlacken und weiteren Reststoffen optimiert werden kann N2 - Since the recycling of tantalum bearing post-consumer waste is practically not existent, metallurgical residues are the most important feed for the tantalum recycling. Most tin ores naturally contain significant quantities of refractory metals. During the smelting process in primary tin production these elements are enriched in the slag phase. This slag is a highly valuable raw material for tantalum production due to its considerable concentration of tantalum and its functioning as an additional slag former in further pyrometallurgical treatment. In this paper the first process stage of an existing pyrometallurgical process for tantalum recovery, mainly from low grade pyrometallurgical residues, is discussed. Smelting trials were carried out in a pilot-scale electric arc furnace to analyse the effect of feeding on the activity of carbon as a reducing agent. Therefore, blowing petroleum coke through an iron lance and the manual adding of coke into the melting bath were tested. During the pyrometallurgical treatment elements with a high affinity to carbon were reduced to their carbide form and enriched in the molten iron-based metal phase. The objective of the process was to reduce the oxidic tantalum completely and to enrich it into the metal phase. Furthermore, the transfer of unwanted elements such as titanium into the metal phase was aimed to be avoided. Spoon test specimens were taken from the liquid mineral melt to follow the evolution of the reduction process. The cooled down solidified melting bath was investigated by using the XRD and EDX method to characterise the slag system and to identify relevant mineral phases. N2 - Da das Recycling von tantalhaltigen Post-Consumer-Abfällen praktisch nicht existiert, stellen metallurgische Reststoffe eine äußerst wichtige Rohstoffquelle für das Tantalrecycling dar. Die meisten Zinnerze enthalten von Natur aus erhebliche Mengen an Refraktärmetallen. Diese Elemente werden in den Schlacken der pyrometallurgischen Primärzinngewinnung angereichert. Aufgrund ihrer vergleichsweise hohen Wertstoffkonzentration und ihrer Funktion als zusätzlicher Schlackenbildner stellen diese Schlacken einen wertvollen Rohstoff für die Verhüttung tantalhaltiger Reststoffe dar. In der vorliegenden Arbeit wird ein existierendes Verfahren zur Tantalrückgewinnung diskutiert, dem hauptsächlich pyrometallurgische Rückstände geringer Wertstoffkonzentration als Einsatzstoff dienen. Mit Hilfe des Verfahrens sollte dasoxidisch vorliegende Tantal vollständig reduziert und in der Metallphase angereichert werden. Weiterhin sollte vermieden werden, dass unerwünschte Elemente wie Titan in die Metallphase überführt werden. Ziel der Untersuchung war es, die ablaufenden Reduktionsprozesse besser zu verstehen, um so Ansätze für die Prozessoptimierung identifizieren zu können. KW - Lichtbogenofen KW - Pyrometallurgie KW - Recycling KW - Tantal KW - Zinnschlacke PY - 2020 SN - 0934-3482 VL - 33 SP - 10 EP - 17 PB - Rhombos-Verlag CY - Berlin AN - OPUS4-50656 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taube, Mareike Carolin A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Beckmann, T. A1 - Reuter, M. A1 - Stelter, M. ED - Thiel, S. ED - Thomé-Kozmiensky, E. ED - Pretz, T. ED - Senk, D. G. ED - Wotruba, H. T1 - Tantal-Rückgewinnung aus Zinnschlacken und weiteren Reststoffen N2 - Since the recycling of tantalum bearing post-consumer waste is practically not existent, metallurgical residues are the most important feed for the tantalum recycling. Most tin ores naturally contain significant quantities of refractory metals. During the smelting process in primary tin production these elements are enriched in the slag phase. This slag is a highly valuable raw material for tantalum production due to its considerable concentration of tantalum and its functioning as an additional slag former in further pyrometallurgical treatment. In this paper the first process stage of an existing pyrometallurgical process for tantalum recovery, mainly from low grade pyrometallurgical residues, is discussed. Smelting trials were carried out in a pilot-scale electric arc furnace to analyse the effect of feeding on the activity of carbon as a reducing agent. Therefore, blowing petroleum coke through an iron lance and the manual adding of coke into the melting bath were tested. During the pyrometallurgical treatment elements with a high affinity to carbon were reduced to their carbide form and enriched in the molten iron-based metal phase. The objective of the process was to reduce the oxidic tantalum completely and to enrich it into the metal phase. Furthermore, the transfer of unwanted elements such as titanium into the metal phase was aimed to be avoided. Spoon test specimens were taken from the liquid mineral melt to follow the evolution of the reduction process. The cooled down solidified melting bath was investigated by using the XRD and EDX method to characterise the slag system and to identify relevant mineral phases. T2 - Berliner Konferenz Mineralische Nebenprodukte und Abfälle CY - Berlin, Germany DA - 13.05.2019 KW - Zinnschlacke KW - Tantal KW - Recycling KW - Pyrometallurgie KW - Lichtbogenofen PY - 2019 SN - 978-3-944310-47-3 VL - 6 SP - 378 EP - 393 PB - Thomé-Kozmiensky Verlag GmbH CY - Neuruppin AN - OPUS4-48357 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Taube, Mareike Carolin A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Beckmann, T. A1 - Reuter, M. A1 - Stelter, M. T1 - Tantal-Rückgewinnung aus Zinnschlacken und weiteren Reststoffen N2 - Since the recycling of tantalum bearing post-consumer waste is practically not existent, metallurgical residues are the most important feed for the tantalum recycling. Most tin ores naturally contain significant quantities of refractory metals. During the smelting process in primary tin production these elements are enriched in the slag phase. This slag is a highly valuable raw material for tantalum production due to its considerable concentration of tantalum and its functioning as an additional slag former in further pyrometallurgical treatment. In this paper the first process stage of an existing pyrometallurgical process for tantalum recovery, mainly from low grade pyrometallurgical residues, is discussed. Smelting trials were carried out in a pilot-scale electric arc furnace to analyse the effect of feeding on the activity of carbon as a reducing agent. Therefore, blowing petroleum coke through an iron lance and the manual adding of coke into the melting bath were tested. During the pyrometallurgical treatment elements with a high affinity to carbon were reduced to their carbide form and enriched in the molten iron-based metal phase. The objective of the process was to reduce the oxidic tantalum completely and to enrich it into the metal phase. Furthermore, the transfer of unwanted elements such as titanium into the metal phase was aimed to be avoided. Spoon test specimens were taken from the liquid mineral melt to follow the evolution of the reduction process. The cooled down solidified melting bath was investigated by using the XRD and EDX method to characterise the slag system and to identify relevant mineral phases. T2 - Berliner Konferenz mineralische Nebenprodukte und Abfälle 2019 CY - Berlin, Germany DA - 13.05.2019 KW - Zinnschlacken KW - Tantal KW - Recycling KW - Pyrometallurgie KW - Lichtbogenofen PY - 2019 AN - OPUS4-48352 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adamczyk, Burkart A1 - Schraut, Katharina A1 - Adam, Christian ED - Thiel, S. ED - Thomé-Kozmiensky, E. ED - Friedrich, B. ED - Pretz, T. ED - Quicker, P. ED - Senk, D. G. ED - Wortruba, H. T1 - Nachbehandlung von Stahlwerksschlacken und deren Verwertung als Klinkermaterial T1 - Post-treatment of steelmaking slags and their utilisation as cement clinker N2 - Steelmaking slags produced using the Linz-Donawitz method (LD slags) are widely used as building and construction materials in road, earth and water works. Because the legal conditions become more and more re-strictive , this application is uncertain in the future. LD slags contain high amounts of mineral bound iron (in form of Fe2O3), which must be considered as a waste of resources. Except for the Iron the chemical composition is quite similar to that of Portland cement clinker. However, due to the high content of Fe2O3 the mineralogical composition differs significantly, resulting in a low hydraulic reactivity. A post-treatment of the liquid LD slag in an electric arc furnace under reducing conditions enables the reduction of the iron compounds to metallic iron, which separates from the mineral phase due to its higher density. The remaining solidified mineral fraction mainly contains typical crystalline phases of cement clinker in similar ratios: Alite (Ca3SiO5; > 60%) as main phase, Belite (Ca2SiO4, 10%), Tricalciumaluminate (Ca3Al2O6; 5%) and Brownmillerite (Ca2(Al,Fe)2O5, 1%) as secondary phases. Alite, which usually decomposes to Belite and free lime under slow cooling conditions, is stabilized in the Fe-reduced slag probably by integration of foreign ions into the lattice and is stable even if the slag is cooled down very slowly. Furthermore, the particularly large Alite crystals do not exhibit the typical decomposition edge of Belite and lime, found in Alite from ordinary ce-ment clinker. Technological tests for building materials show a high hydraulic reactivity and a compressive strength after 28 days comparable or even slightly higher to reference cement. Nevertheless, because of the increasing viscosity with decreasing Fe2O3 content, the treatment requires a temperature higher than the slag decanted from the LD converter. Furthermore, during the reduction of the bound Iron huge amounts of carbon monoxide are released, resulting in foaming of the slag. Both aspects make it difficult to manage the process. In addition, for economic reasons the treatment has to be carried out immediately after casting the slag from the LD converter to avoid the solidification, which is a logistical challenge for most steel plants. Otherwise the separation of the mineral bound iron as metallic phase and the utilisation of the mineral fraction as cement clinker will both save resources and lower the global CO2-output. For these reasons further initiatives should be considered in the medium term. N2 - LD-Schlacken weisen eine große chemische Ähnlichkeit zu Protlandzementklinker auf. Sie enthalten jedoch noch bis zu 30% Eisen, das mineralisch in oxidischer Form gebunden vorliegt. Dadurch kann sich bei der Erstarrung die wichtigste Klinkerphase "Alit" nicht ausbilden. Durch eine reduzierende Schmelzbehandlung der Schlacke kann des mineralisch gebundene Eisen als Metall separiert werden. Dadurch wird auch die Mineralogie der Schlacke so verändert, dass auch sie nun praktisch einem Portlandzementklinker entspricht. Entsprechende Versuche wurden am kleintechnischen Lichtbogenofen der BAM durchgeführt. Es werden Ergebnisse vorgestellt und auf Grenzen und Möglichkeiten eines derartigen Prozesses im Hinblick auf eine industrielle Umsetzung eingegangen. T2 - Berliner Konferenz Mineralische Nebenprodukte und Abfälle CY - Berlin, Germany DA - 11.06.2018 KW - Zementklinker KW - Stahlwerksschlacke KW - LD-Schlacke KW - Lichtbogenofen KW - Alit PY - 2018 SN - 978-3-944310-41-1 VL - 5 SP - 282 EP - 296 PB - Thomé-Kozmiensky Verlag GmbH CY - Neuruppin AN - OPUS4-45199 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Adamczyk, Burkart A1 - Schraut, Katharina A1 - Adam, Christian T1 - Nachbehandlung von Stahlwerksschlacke und deren Verwertung als Klinkermaterial N2 - LD-Schlacken weisen eine große chemische Ähnlichkeit zu Protlandzementklinker auf. Sie enthalten jedoch noch bis zu 30% Eisen, das mineralisch in oxidischer Form gebunden vorliegt. Dadurch kann sich bei der Erstarrung die wichtigste Klinkerphase "Alit" nicht ausbilden. Durch eine reduzierende Schmelzbehandlung der Schlacke kann des mineralisch gebundene Eisen als Metall separiert werden. Dadurch wird auch die Mineralogie der Schlacke so verändert, dass auch sie nun praktisch einem Portlandzementklinker entspricht. Entsprechende Versuche wurden am kleintechnischen Lichtbogenofen der BAM durchgeführt. Es werden Ergebnisse vorgestellt und auf Grenzen und Möglichkeiten eines derartigen Prozesses im Hinblick auf eine industrielle Umsetzung eingegangen. T2 - Berliner Konferenz "Mineralische Nebenprodukte und Abfälle" CY - Berlin, Germany DA - 11.06.2018 KW - LD-Schlacke KW - Lichtbogenofen KW - Zementklinker PY - 2018 AN - OPUS4-45221 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -