TY - CONF A1 - Ulbricht, Alexander T1 - Do Microbes like Additively Manufactured Aluminium? N2 - The use of laser-additively manufactured metallic components in the industrial sector is gaining traction, with the process now entering its application phase. Consequently, the materials are exposed to corrosive microbes, which this study examines in order to determine the implications of this exposure. Specifically, the study examines the exposure of laser powder bed fused AlSi10Mg (PBF-LB/AlSi10Mg) components to sulphate-reducing bacteria in an anaerobic environment. Is the specific PBF-LB microstructure a potential factor in determining or aiding biocorrosion? A prismatic specimen was exposed to sulphate-reducing bacteria (SRB) for two weeks. The sample was scanned by X-ray computed tomography (XCT) before and after SRB exposure. The two data sets were registered to each other (using the internal void distribution as markers, due to the corrosion of the specimen’s surface) to enable the evaluation of the corrosion damage. Virtual cuts of the 3D XCT reconstructions show a loss of volume and localised damage. The damage distribution aligns with the hatching pattern of laser exposure from laser powder bed fusion. T2 - Konferenz iCT 2026 CY - Linz, Austria DA - 10.02.2026 KW - Computed tomography KW - Biokorrosion KW - Additive manufacturing KW - PBF-LB KW - Laser powder bed fusion KW - Sulphate-reducing bacteria PY - 2026 AN - OPUS4-65570 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulbricht, Alexander T1 - Do Microbes like Additively Manufactured Aluminium? First Details of a Corrosion Test using Sulphate-Reducing Bacteria N2 - Additively manufactured metals become relevant for industrial application. Although many studies on wet corrosion of these metals have been conducted, to the authors knowledge no study seems to contain microbiological corrosion (MIC). In the presented study an experiment was conducted on PBF-LB/AlSi10Mg to test this material's susceptibility for MIC. The tested specimen were analysed using Computed Tomography before and after the MIC experiment to enable a detailed characterisation the damage on the specimens' global and local level. A global reduction of material was observed. In addition, localised damage along process inherent features of the materials microstructure was observed. T2 - Beiratssitzung TF Umwelt CY - Berlin, Germany DA - 17.03.2025 KW - Computed Tomography KW - Additive Manufacturing KW - Biocorrosion KW - Sulphate-reducing Bacteria KW - Microbially influenced corrosion PY - 2025 AN - OPUS4-62772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea T1 - The Power of networks – COST Action CA20130 N2 - For optimal research on microbiologically influenced corrosion (MIC), balanced and interdisciplinary cooperation is extremely important. However, differing perspectives, thought processes, and even variations in nomenclature/terminology often hinder the establishment of effective collaborations. Over the past four years, COST Action Euro-MIC (CA20130) has effectively addressed these discrepancies. Through regular meetings, conferences, and scientific exchanges, a large international network has been established. Many scientific findings and results have been achieved through scientific, interdisciplinary exchange within the international network. The upcoming presentation will highlight three examples (among many others) that have resulted in successful collaborations, third-party funding applications, publications, or outstanding results and emphasize that successful results in MIC research, facilitated by an interdisciplinary network, can lead more quickly to meaningful and application-oriented findings. Project 1&2 describe two different kinds of Projects related to the use of Nanoparticles; one is about the efficacy testing of novel Nanoparticles. Project 2 deals about how to apply already working and tested nanoparticles to different materials and conditions. Project 3a is related to the energy sector; a crucial part of our society, and currently undergoing significant changes. Climate change, rising temperatures, increased use of fertilizers and other environmental pollutants have led to an increasing occurrence of microorganisms and contamination in some sectors. But how we deal with “baggage” from the past and store nuclear waste without harm or risk for human and environment, but also how to transfer the gained knowledge to areas like safe Hydrogen storage in geological underground formation. T2 - ISMOS10 CY - Nashville, TN, USA DA - 11.08.2025 KW - COST Action CA20130 KW - MIC KW - STSM Grants KW - Networking PY - 2025 AN - OPUS4-64295 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea T1 - Euro-MIC COST Action CA20130 Closing Workshop & Conference N2 - Ensuring the safety of offshore wind structures (OWS) is critical to guaranteeing their long-term performance and supporting reliable green energy supply. Microbiologically influenced corrosion (MIC) presents a significant challenge, particularly for monopiles in seabed environments. This study investigates the behavior of microorganisms and their impact on the corrosion process of carbon steel within monopiles. To simulate MIC at the sediment/water interface, an in-house experimental column was developed and inoculated with sediment and water samples from the North Sea. The system was operated under varying flow rates to replicate seabed movement conditions. Multiple molecular microbiological methods, surface analysis techniques, and other approaches were employed to assess the effects of different treatments. This study provides insights into MIC mechanisms in offshore environments and supports the development of strategies to monitor MIC in OWS infrastructure T2 - Final COST Action Conference - Horsens CY - Horsens, Denmark DA - 17.09.2025 KW - MIC KW - COST Action Euro-MIC KW - Interdisciplinarity PY - 2025 AN - OPUS4-64299 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea T1 - Euro-MIC 2021-2025, our journey, and paths forward N2 - Microbiologically Influenced Corrosion (MIC) refers to the detrimental effects on materials caused by microorganisms, and it is becoming an increasingly significant issue for society. Unlike the USA, Canada, and Australia, Europe has less developed cooperation on MIC. Although several research groups and industrial stakeholders are addressing MIC, discussions remain fragmented, and information exchange is limited. A truly transdisciplinary approach is rarely seen. As a result, Europe often relies on methods, preventive measures, and standards from other regions, as there are no equivalent European standards. This situation makes Europe a) highly dependent, and b) in some cases, unable to use certain measures or standards due to European legal restrictions (e.g., the use of biocides). In 2021, researchers established the “Euro-MIC” network, financially supported by the EU project “COST-Action,” to tackle these issues. Through COST-Action, Euro-MIC aims to facilitate necessary interactions, communication, knowledge sharing, and training for personnel and researchers across various disciplines. COST-Action supports network activities, workshops, training schools, conferences, and more. Euro-MIC aspires to position Europe as a leader in MIC, promoting ideas on par with other nations while upholding European values and ensuring greater protection for people, property, and the environment. In this presentation, I will briefly introduce the principles of COST Action and highlight the significant opportunities provided by this EU-funded project. COST Action fosters interdisciplinarity, networking, training, scientific exchange, and the promotion of young scientists. By showcasing some examples of CA20130 COST ACTION Euro-MIC, I hope to demonstrate that COST Action is not only relevant for addressing MIC but can also be applied to other important topics and sectors. T2 - Unseen Corrosion: Unveiling Hidden Threats and Innovating Monitoring Solutions CY - Bergen, Norway DA - 15.05.2025 KW - COST Action CA20130 KW - MIC KW - Network KW - Corrosion KW - Microorganisms PY - 2025 UR - https://www.norceresearch.no/en/events/unseen-corrosion AN - OPUS4-63726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea T1 - Simulating Microbiologically Influenced Corrosion (MIC) at Seabed Environment in Monopile N2 - Ensuring the safety of offshore wind structures (OWS) is critical to guaranteeing their long-term performance and supporting reliable green energy supply. Microbiologically influenced corrosion (MIC) presents a significant challenge, particularly for monopiles in seabed environments. This study investigates the behavior of microorganisms and their impact on the corrosion process of carbon steel within monopiles. To simulate MIC at the sediment/water interface, an in-house experimental column was developed and inoculated with sediment and water samples from the North Sea. The system was operated under varying flow rates to replicate seabed movement conditions. Multiple molecular microbiological methods, surface analysis techniques, and other approaches were employed to assess the effects of different treatments. This study provides insights into MIC mechanisms in offshore environments and supports the development of strategies to monitor MIC in OWS infrastructure T2 - ISMOS10 CY - Nashville, TN, USA DA - 11.08.2025 KW - MIC KW - Environmental Simulation KW - Field testing KW - Marine Environment PY - 2025 AN - OPUS4-64298 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea T1 - Technical challenges for the investigation of Microbiologically influenced corrosion under laboratory conditions across several sectors N2 - Microbiologically influenced corrosion MIC occurs in different sectors, under various conditions and can significantly contribute to material degradation. The most convincing effect can be observed with sulphate-reducing bacteria (SRB). There are many stakeholders who do not need to be convinced of this as there is ample scientific evidence clearly showing that SRBs corrode metal. However, many believe this is solely due to the produced H2S. Fewer people are aware that SRBs also have other mechanisms that can lead to corrosion, such as electrical MIC on metal (direct electron uptake from the metal used as electron donor). Despite this, many sectors or industries remain skeptical in several areas. When considering other classes or species, the skepticism increases even more. The reason is simple: microbiologist cannot consistently prove MIC on laboratory scale for all corrosive microorganisms. In contrast to materials sciences, where experiments can be narrowed down to a limited number of parameters, microbiology is too complex to simulate simply in the lab. Several factors are mandatory for the growth of microorganisms, consequently increasing the number of parameters. Even when making the system more complex, there are still unknown species in the field, whose growth conditions are not yet understood. We know via 16S rRNA analysis that the species is present, but that is all we know. If these samples are enriched in the lab, many species will not survive and their impact on the whole community cannot be investigated. Therefore, lab tests related to MIC works only for a certain number of microorganisms. This means the key-result for other disciplines are missing, and important numbers for calculating the lifespan of a material can only be provided with limited accuracy. This is neither satisfying nor useful for engineers, material scientist or similar professionals, and it is understandable. However, MIC occurs, and we need to address it in our infrastructure or other important areas. With this presentation, I aim to show the currently available techniques for testing on a laboratory scale. I will use SRBs and methanogenic archaea as examples to highlight the advantages and disadvantages of each method and point out where improvements are needed. The examples will be cross-sectoral and applicable to other sectors as well. This talk will highlight the currently existing challenges of testing MIC in the laboratory and may help generate creative solutions. T2 - MICxUS 2025 CY - Nicosia, Cyprus DA - 21.01.2025 KW - MIC KW - Biocorrosion KW - Laboratory testing KW - Interdisziplinarity KW - Microorganisms PY - 2025 UR - https://www.unic.ac.cy/ehresearch/micxus2025/#tab-98dc74f32bf3b8f95bd AN - OPUS4-63725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea T1 - Mikrobielle Einflüsse auf Wasserstoffspeicherung: Materialien, Abbauprozesse und Teststrategien N2 - Wasserstoff gilt als Schlüsseltechnologie für die Energiewende – doch seine sichere Anwendung stellt neue Anforderungen an Technik, Infrastruktur und Personal. Die Veranstaltung „H₂ Sicherheit“ bietet eine umfassende Plattform, um sich über die sicherheitsrelevanten Aspekte von Wasserstoff zu informieren und praxisnahe Lösungen kennenzulernen. Expert:innen aus Forschung, Industrie und Netzbetrieb geben Einblicke in aktuelle Entwicklungen, Herausforderungen und Best Practices. Fokus dieser Präsentation war der Mikrobielle Einfluss bei der unterirdischen Speicherung von Wasserstoff und das neuartige Testsystem (MISTRAL) T2 - DVGW- H₂ Sicherheit | 26. – 27. November 2025 CY - Online meeting DA - 26.11.2025 KW - MIC KW - MISTRAL KW - Hochdruckbehälter KW - Wasserstoff KW - Unterirdische geologische Formationen PY - 2025 AN - OPUS4-64890 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nordholt, Niclas T1 - Bacterial resistance evolution on antimicrobial surfaces: Mechanistic insights from a standardizable method N2 - Introduction: Antimicrobial surfaces and coatings (AMCs) are important to prevent the spread of pathogens, especially in hygiene-sensitive areas. However, the evolution and selection of bacterial resistance to AMCs may threaten their efficacy in the long term. In addition, resistance evolution to AMCs may pose the risk for the development of cross-resistance to antibiotics. The assessment of unacceptable resistance risks during the authorization of AMCs is hampered by the lack of standardized test methods that quantify the adaptability of exposed bacteria to AMCs. Objectives: • To develop a standardizable method to determine resistance evolution of bacteria on AMCs (ALEE-AMC) • To assess performance and robustness of ALEE-AMC in a ring trial • To uncover the mechanisms underlying evolution of resistance to a metallic copper AMC • To use ALEE-AMC to assess the evolution of resistance on a novel, nano-particle-based AMC Methods: ALEE-AMC was developed based on an international standard to determine the efficacy of antimicrobial surfaces (ISO 22196). In the ALEE-AMC test, adaptive laboratory evolution is conducted by repeated cycles of AMC exposure and re-growth of surviving cells, selecting for increased survival, followed by isolation of evolved clones. Metallic copper was used as a reference AMC and Escherichia coli as a model microorganism in the ring trial. Evolved E. coli populations from the ring trial partners were subjected to phenotypic (antimicrobial susceptibility testing, ISO 22196) and genotypic (whole genome sequencing) characterization. ALEE-AMC will be used to assess the evolution of resistance on a novel, nano-particle-based AMC currently under development. Findings: The results of the ALEE-AMC ring trial show that repeated exposure to a metallic copper AMC can reproducibly select for reduced copper susceptibility in individual evolutionary lineages across ring trial participants. However, failure to adapt in individual lineages was also observed in all trials. Isolated evolved E. coli clones exhibited increased survival upon exposure to copper surfaces. Adaptation to copper did not induce cross-resistance to antibiotics because the antibiotic susceptibility of copper-adapted clones did not increase above the clinical breakpoint. Whole genome sequencing of the evolved E. coli revealed a high diversity of mutations, including mutations in genes involved in survival to antibiotics. These results indicate the existence of multiple, underexplored evolutionary pathways towards increased survival of antimicrobial copper surfaces. Conclusion: ALEE-AMC offers a standardizable platform to assess the risk of resistance development towards novel and existing AMCs, including nano-particle-based and metallic copper AMCs. Specifically, using ALEE-AMC provided insights into evolvable survival mechanisms to copper AMCs and its consequences for antimicrobial resistance. T2 - FEMS MICRO 2025 CY - Mailand, Italy DA - 14.07.2025 KW - Biocides KW - Antimicrobial surfaces KW - Biocide resistance KW - Standardization KW - ISO 22196 KW - Evolution PY - 2025 AN - OPUS4-63837 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn T1 - Bacterial adhesion on ultrashort pulse laser processed surfaces ― more than size matters! N2 - Bacterial biofilms are aggregates of bacterial cells, often attached to a surface and enclosed by a self-produced extracellular matrix which confers increased stress tolerance and resistance to cleaning. Biofilm formation leads to biofouling which gives rise to high costs in numerous technical settings due to biocorrosion and biodegradation. However, biofilms can also be attractive for industrial settings such as wastewater treatment systems or for soil bioremediation processes. Hence, the control of bacterial adhesion to a surface is of major concern. Surface topography strongly influences bacterial adhesion. Therefore, one promising way to achieve bacteria-guiding surfaces lies in the contactless and aseptic large-area laser processing of technical surfaces. We used short and ultrashort pulsed laser systems to generate different surface textures, mainly high-spatial-frequency and low-spatial-frequency laser-induced periodic surface structures, LIPSS (HFSL and LFSL), on Ti, Ti-alloy, steel, and polymers (PET and PE). Pristine (polished) and laser processed samples were subjected to bacterial adhesion experiments with two different Escherichia coli strains and Staphylococcus aureus as test organisms. The bacterial strains differed in their cell wall structure (grampositive vs. gramnegative strains), in size, shape, the occurrence of cell appendages, and in their biofilm forming capabilities. Adhesion patterns were analyzed microscopically and compared regarding the respective test strain and surface topography. Our results revealed that adhesion behavior strongly depends not only on the material’s topography and chemistry, but also on the specific bacterial strain, the presence of cell appendages, and ambient growth conditions. T2 - 13th International Conference on Photoexcited Processes and Applications, ICPEPA-13 CY - Lecce, Italy DA - 14.09.2025 KW - Biofilm KW - Bacterial adhesion KW - Laser-induced periodic surface structures (LIPSS) KW - Ultrashort laser pulses PY - 2025 AN - OPUS4-64166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -