TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar A1 - Adam, Christian T1 - Formation and hydraulic reactivity of an alite rich material from post treated basic oxygen furnace slag N2 - Basic oxygen furnace slag (BOFS) is a by-product of steelmaking of which about 10.4 Mt are produced annually in the EU. BOFS is mostly used in road construction, earthwork and hydraulic engineering. However, in this use, the iron bound in BOFS is lost and the opportunity to produce higher value products from BOFS is forgone. In recent decades, many researchers have investigated a thermochemical process to reduce iron oxides to metallic iron in molten BOFS. The metallic iron formed separates from the reduced slag due to its higher density and can be recovered. An advantage of this process is that simultaneously the chemical composition of the reduced slag is adapted to that of the Portland cement clinker and the hydraulic reactive mineral alite is formed. In this study, BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent, and the hydraulic properties of the reduced, low-iron BOFS were investigated. Despite a chemical and mineralogical composition similar to that of Portland cement clinker, the reduced BOFS produced less heat of hydration, and its reaction was delayed compared to Portland cement. However, the addition of gypsum, as is also done in cement production from Portland cement clinker, has been found to accelerate the hydration rate of reduced BOFS. Further research to improve the hydraulic properties of the reduced slag is essential. If successful, the production of a hydraulic binder and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry. T2 - GeoMin Köln 2022 CY - Cologne, Germany DA - 11.09.2022 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2022 AN - OPUS4-56080 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian T1 - Reductive treatment of steel making slags to produce a hydraulic binder and crude iron N2 - Steelmaking slags are a by-product of steel production, that are currently used primarily in road construction, earthwork, and hydraulic engineering. In this use, the iron bound in the steelmaking slags (< 30 wt.%) is lost. Recovery of iron from steelmaking slags is possible by thermochemical reductive treatment. The reductive treatment of liquid steelmaking slags causes iron oxides to be reduced to metallic iron, which separates from the mineral phase due to its higher density. The chemical composition of the mineral phase is thus adapted to that of the Portland cement clinker and the mineral alite, the most important component of Portland cement, is formed. This way, crude iron can be recovered, and at the same time a hydraulic binder can be produced. This process, however, is uneconomical due to the high temperatures required (~1800 °C). In the current project, the process is to be adapted so that the reduction of liquid steelmaking slag can be carried out at ~1600 °C. The chemical composition is to be modified in such a way that the melting temperature of the slags as well as their viscosity are in a technically suitable range and still a product with good cementitious properties is obtained. T2 - LithiumDays CY - Online meeting DA - 06.12.2021 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2021 AN - OPUS4-56081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar A1 - Adam, Christian T1 - Hydraulic reactivity of alite rich material from post-treated basic oxygen furnace slags N2 - Basic oxygen furnace slags (BOFS) are a by-product of steel production. In 2016, 10.4 Mt of BOFS were produced in the European Union (EU). The main part of BOFS is used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. However, it is also possible to produce higher value products from BOFS. For example, many researchers have investigated the possibility of producing Portland cement clinker and crude iron from BOFS by a carbothermal post-treatment. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The carbothermal treatment reduces the iron oxides in the BOFS to metallic iron, which accumulates at the bottom of the furnace by density separation. In addition to metallic iron, the process generates a mineral product rich in the tricalcium silicate solid solution alite. As the main constituent of Portland cement clinker, the hydraulic reactive mineral alite is of high economic importance. In previous studies, the hydraulic reactivity of the mineral product was investigated by testing the compressive strength of blends with 70 wt.% ordinary Portland cement (OPC). Recent investigations focused on the hydraulic properties of the pure mineral product from the reduced BOFS. The heat of hydration of the mineral product was measured by isothermal calorimetry and compared with the heat of hydration of a synthetic low-iron slag and OPC. In addition, the formation of hydration products was investigated with differential scanning calorimetry (DSC) and x-ray diffraction analysis (XRD) on freeze-dried samples after defined curing times. The results of the calorimetric measurements indicate that the mineral product produced less heat of hydration and its reaction was delayed compared to the synthetic low-iron slag and OPC. Hydration products such as portlandite and calcium silicate hydrates (C-S-H) formed later and in lower amounts. The production of a hydraulic material from BOFS by reductive treatment is of great interest to both the cement and steel industries. The substitution of cement clinker in OPC with a hydraulic material such as reduced BOFS leads to a reduction in greenhouse gas emissions from cement production. The steel industry benefits from an application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. Furthermore, it may be possible to return the recovered crude iron to production. T2 - 3rd European Mineralogical Conference CY - Cracow, Poland DA - 30.08.2021 KW - BOFS KW - Calcium silicate KW - Hydraulic reactivity PY - 2021 AN - OPUS4-53473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar A1 - Adam, Christian T1 - Portland cement clinker from reduced basic oxygen furnace slag N2 - Basic oxygen furnace slag (BOFS) is a by-product of the steelmaking process, of which about 10.4 Mt are produced annually in the European Union. Besides its predominant use in road construction, earthwork, and hydraulic engineering, it is also possible to use BOFS as a source material for Portland cement clinker. The main difference in the chemical composition of BOFS from the chemical composition of Portland cement clinker is its high content of iron oxides (7-50 wt.%). In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via thermochemical reductive treatment. Carbothermal treatment of liquid BOFS causes reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The produced low-iron mineral product was chemically similar to Portland cement clinker and contained the most important Portland cement mineral alite (Ca3SiO5) as main component. Besides alite, the mineral product contained other Portland cement clinker constituents such as belite (β-Ca2SiO4) and tricalcium aluminate (Ca3Al2O6). The production of Portland cement clinker and crude iron from BOFS has economic and ecological benefits for both the cement and steel industry. Cement clinker from reduced BOFS may be used as a substitute for cement clinker from conventional cement production, thereby CO2 emissions will be reduced. The steel industry benefits from a high-value application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. However, reductive treatment requires high temperatures and, for economic reasons, has to be carried out immediately after casting of the liquid BOFS, which is a logistical challenge for most steel plants. A cost-benefit analysis is therefore essential. T2 - European Congress and Exhibition on Advanced Materials and Processes CY - Online meeting DA - 13.09.2021 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2021 AN - OPUS4-53475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar Aloys A1 - Adam, Christian T1 - Zementklinker durch Nachbehandlung von Stahlwerksschlacken N2 - Die Klinkerphasenbildung durch Sinterung in Drehrohröfen bei der Herstellung von Portlandzementklinker (PZK) ist gründlich erforscht und optimiert. Im Hinblick auf mög-liche ökonomische und ökologische Vorteile befassen sich aktuelle Forschungsvorha-ben darüber hinaus mit der Herstellung von Klinkermineralen aus Stahlwerksschla-cken, die eine vergleichbare chemische Zusammensetzung aufweisen. Neuste Untersuchungen zeigen, dass nach der reduzierenden Behandlung schmelz-flüssiger Linz-Donawitz-(LD)-Schlacken und Abscheidung des gebildeten metallischen Eisens eine mineralische Schlacke entsteht, die unabhängig von ihren Abkühlbedin-gungen ca. 50–60 Gew.% des wichtigsten Klinkerminerals Alit (C3S) enthält und eine hohe hydraulische Reaktivität aufweist. Die Stabilität des Alits auch nach langsamer Abkühlung deutet auf eine Stabilisierung des Minerals durch Nebenelemente aus den LD-Schlacken hin. Ein sinkender Anteil an LD-Schlacke durch Zusatz synthetischer Schlackemischung, die sich hinsichtlich ihrer Hauptkomponenten wie eine ausreduzierte LD-Schlacke zusammensetzt, führt zu einem Rückgang des Alitgehaltes und dem Zerfall der Schlacke beim Erstarren. T2 - 5. Schlacken-Symposium CY - Meitingen, Germany DA - 25.10.2018 KW - Zement KW - LD-Schlacke KW - Tricalciumsilikat PY - 2018 AN - OPUS4-46409 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian A1 - Stephan, D. A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit T1 - Production of a hydraulic material from post-treated steelmaking slags N2 - Steelmaking slag is a by-product of steel production of which 4.5 Mt were produced in 2020 in Germany alone. It is mainly used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. With this use, iron oxides still contained in steelmaking slag are lost. In addition, the possibility of producing higher-grade products from steelmaking slag is foregone. In recent decades, many researchers have investigated the production of Portland cement clinker and crude iron from basic oxygen furnace slags (BOFS) via a reductive treatment. Carbothermal treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. Simultaneously, the chemical composition of the reduced slag is adapted to that of the Portland cement clinker. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as a reducing agent. The resulting low-iron mineral product had a similar chemical composition to Portland cement clinker and was rich in the tricalcium silicate solid solution alite (Ca3SiO5). Based on its chemical and mineralogical composition, similar to that of Portland cement clinker, the reduced BOFS has the potential to react comparably. In our study, the reduced BOFS produced less heat of hydration compared to OPC and its hydraulic reaction was delayed. However, adding gypsum has been shown to accelerate the hydration rate of the reduced BOFS compared to that known from the calcium silicates of Portland cement clinker. Further research to improve the hydraulic properties of the reduced slag is essential. If successful, producing a hydraulic binder and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry. T2 - 16th International Congress on the Chemistry of Cement ICCC 2023 CY - Bangkok, Thailand DA - 18.09.2023 KW - Steelmaking slag KW - Alite hydraulic reactivity KW - Clinker substitute PY - 2023 AN - OPUS4-58522 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar T1 - Production of an alite-rich material from reduced basic oxygen furnace slags N2 - Basic oxygen furnace slag (BOFS) is a by-product of steelmaking of which about 10.4 Mt are produced annually in the EU. BOFS is mostly used in road construction, earthwork and hydraulic engineering. However, in this use, the iron bound in BOFS is lost and the opportunity to produce higher value products from BOFS is forgone. In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via a thermochemical reductive treatment. The reductive treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density and can be recovered. An advantage of this process is that simultaneously the chemical composition of the reduced BOFS is adapted to that of Portland cement clinker and the hydraulic reactive mineral alite (Ca3SiO5) is formed. In this study, German BOFS was reduced in a small-scale electric arc furnace and a low-iron mineral product rich in alite was produced. Despite a chemical and mineralogical composition similar to that of Portland cement clinker, the reduced BOFS produced less heat of hydration, and its reaction was delayed compared to Portland cement. However, adding gypsum accelerated the hydration rate of the reduced BOFS. Further research to improve the hydraulic properties of the reduced BOFS is essential. If successful, the production of a hydraulic material and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry. T2 - GeoBerlin 2023 CY - Berlin, Germany DA - 04.09.2023 KW - BOFS KW - Alite KW - Hydraulic reactivity PY - 2023 AN - OPUS4-58206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute A1 - Kalbe, Ute A1 - Happel, O. T1 - Combination of leaching tests with ecotoxicity and chemical analysis – lessons learnt N2 - The presentation describes analytical methods to characterize eluates from leaching tests and identify organic substances in leachates. Chances to obtain complementary information from ecotoxtests and chemical analysis are discussed. T2 - Workshop: Ecotoxicological evaluation of construction products – test results, implementation in Guidance, Technical Standards and Ecolabelling CY - Online meeting DA - 21.03.2022 KW - Leaching KW - Ecotoxicity KW - Construction products PY - 2022 AN - OPUS4-55276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute T1 - Leaching und Transformation von Bioziden aus Fassadenfarben N2 - Anhand von Beobachtungen aus Labor- und Freilandversuchen wurde dargestellt, wie Wasserkontakt und Strahlung die Auslaugung und Transformation der Wirkstoffe Diuron und Terbutryn beeinflussen. Auf Optionen zur modellhaften Darstellung dieser Prozesse wurde kurz eingegangen. T2 - Optimierung und Minimierung des Biozideinsatzes in Baustoffen CY - Online meeting DA - 09.02.2022 KW - Leaching KW - Transformation KW - Biozid KW - Fassadenfarbe PY - 2022 AN - OPUS4-55273 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute T1 - The Impact of Weather Conditions on Biocides in Paints N2 - Aim. The European biocidal products regulation requires environmental risk assessments for biocidal products under service conditions. This is only possible, if processes that lead to biocide emissions into the environment are understood and can be reasonably predicted. Actual emissions due to leaching result from different processes that are affected by material properties and environmental conditions. Transformation of biocides can affect emissions considerably. Leaching and possible transformation of the film preservatives carbendazim, diuron, OIT and terbutryn in paints was observed under laboratory and field conditons in order to investigate the influence of different factors, e.g. water contact and radiation on biocide emissions. The paints contained either white titanium dioxide or a red iron oxide pigment to check whether pigments affect leaching processes. Methods. Test specimens of a water-based styrene acrylic dispersion paint on glass were exposed to UVA-radiation in a UV weathering device and/or exposed to water contact by immersion events on the basis of the European standard EN 16105. Plywood panels were coated and exposed to natural weather conditions in a semi-field experiment. Concentrations of biocides and transformation products were analysed in leachates from laboratory tests, runoff samples and remaining coatings. Results. The impact of weathering conditions on transformation processes differs for the investigated active substances. Water contact, radiation as well as pigments in the paints determine the pattern and amount of transformation products on coatings, leachates and runoff water. Observations from laboratory and field experiments were compared. It proved that results from laboratory tests support understanding of data from field experiments. Detailed knowledge on the fate of active substances under environmental conditions supports manufacturers to develop safe applications of film preservatives and authorities to evaluate its environmental impact. T2 - European Technical Coatings Congress 2022 CY - Kraków, Poland DA - 12.07.2022 KW - Paints KW - Biocides KW - Transformation KW - Emission PY - 2022 AN - OPUS4-55274 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute T1 - Leaching und Transformation von Bioziden aus Fassadenfarben N2 - Anhand von Beobachtungen aus Labor- und Freilandversuchen wird dargestellt, wie Wasserkontakt und Strahlung die Auslaugung und Transformation der Wirkstoffe Diuron und Terbutryn beeinflussen. Auf Optionen zur modellhaften Darstellung dieser Prozesse wird kurz eingegangen. T2 - OMiBiB - Optimierung und Minimierung des Biozideinsatzes in Baustoffen CY - Online meeting DA - 09.02.2022 KW - Leaching KW - Transformation KW - Biozide KW - Fassadenfarben PY - 2022 AN - OPUS4-54318 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute A1 - Bandow, Nicole T1 - Auswaschversuche zur Charakterisierung der Umweltverträglichkeit von Bauprodukten N2 - Im Vortrag werden Auswaschversuche mit Bauprodukten vorgestellt, die dazu dienen sollen, Bauprodukte mit geringer Auswaschung zu erkennen. Zu verschiedenen Bauprodukten (Lacke für Außenanwendungen, Wärmedämmverbundsystemen, Dachziegel und Dachfolien) werden ausgewählte Ergebnisse vorgestellt. Die Eignung der Auswaschverfahren und die Testergebnisse werden bewertet. T2 - Umwelteigenschaften von Bauprodukten: Schnellbewitterung, Leaching, Modellierung CY - Holzkirchen, Germany DA - 17.04.2018 KW - Testverfahren KW - Auswaschversuche KW - Bauprodukte PY - 2018 AN - OPUS4-44734 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schoknecht, Ute A1 - Mathies, Helena T1 - Transformation of biocides in organic coatings due to UV radiation and water contact N2 - Transformation of carbendazim, diuron, octylisothiazolinone and terbutryn was investigated in two paints containing either white titanium dioxide or a red iron oxide pigment. Test specimens of these coatings on glass were exposed to water contact and UVA-radiation under laboratory conditions. Panels of birch plywood were coated and exposed to natural weather conditions in a field experiment. Concentrations of biocides and transformation products were analysed in leachates from laboratory tests, runoff samples and remaining coatings. Water contact, UVA radiation as well as pigments in the paints affected the pattern and amount of transformation products. T2 - Advanced Coationgs Technology '18 CY - Sosnowiec, Poland DA - 13.11.2018 KW - Biocide KW - Transformation KW - Weathering KW - UV radiation PY - 2018 AN - OPUS4-46648 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Selina A1 - Schreiber, Frank T1 - Effect of biocides on the evolution and spread of resistance N2 - Biocides used as material preservatives are in contact with various environments during direct application or passive leaching from protected materials. Antimicrobial resistance (AMR) is a global health problem and the environment is an important compartment for the evolution and transmission of AMR. Soil is an environment with a large reservoir of natural microbial communities and antimicrobial resistance (AMR) genes. Those natural microbial communities are frequently exposed to biocides used as material preservatives. Previous studies have shown that antibiotics, metals and pesticides affect the underlying processes of resistance evolution and spread; namely de novo mutagenesis and horizontal gene transfer by conjugation and transformation in microbial communities. However, it is unknown if active substances used in material preservatives are involved in these processes. We show that biocides used as material preservatives affect rates of mutation and conjugation in microorganism in a species- and substance-dependent manner, while rates of transformation are not directly affected. Our data highlights the importance of assessing the contribution of material preservatives on AMR evolution and spread in the environment. T2 - Microbiome Network Meeting CY - Berlin, Germany DA - 20.07.2022 KW - Biocides KW - Antimicrobial resistance KW - Horizontal gene transfer KW - Mutation rate PY - 2022 AN - OPUS4-56426 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Selina A1 - Schreiber, Frank T1 - Antimicrobial resistance in soil microbes mediated by resistance evolution and horizontal gene transfer (HGT) N2 - Biocides are in contact with soils through direct application and passive leaching from protected materials. Consequently, soil microorganisms are exposed to biocides even though they are not their primary targets. Soil is a large reservoir of microbial diversity and has been hypothesized to be a crucial factor for the evolution and spread of antimicrobial resistance. Currently, there is little knowledge on how biocides used to protect materials affect the evolution and spread of resistance. Thus, our aim is to investigate the risk for the evolution of biocide resistance and cross-resistance to antibiotics. In addition, we aim to elucidate the affect of biocides on the spread of resistance via horizontal gene transfer (HGT). In adaptive laboratory evolution experiments we cultured selected model soil microorganism with representative biocides under selection regimes with increasing and stable biocide concentrations followed by antibiotic and biocide cross-resistance determination. Moreover, we investigate if the selected biocides affect the rates of de novo mutations and HGT of plasmids that carry resistance genes among soil microorganism. Our results show only small increases of biocide resistance during serial transfers under increasing biocide concentrations. One reason for this might be the narrow selective window for biocide resistance due to steep dose-response relationships. Furthermore, our results indicate that a stable low-level biocide regime did not select for high level cross-resistance to antibiotics and other biocides. Moreover, material preservatives affected the rates of HGT via conjugation and the mutation rates at sub-inhibitory concentrations. The results will enable future risk assessment regarding resistance evolution for biocides used as material preservatives. T2 - 4th Evo Eco PhD Meeting CY - Lutherstadt Wittenberg DA - 04.03.2020 KW - Microbiology KW - Biocides KW - Horizontal gene transfer HGT KW - Resistance evolution KW - Antimicrobial resistance PY - 2020 AN - OPUS4-51313 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Selina A1 - Kanaris, Orestis A1 - Nordholt, Niclas A1 - Schreiber, Frank T1 - Effect of biocides on the evolution and spread of resistance N2 - Biocides used as material preservatives are in contact with various environments during direct application or passive leaching from protected materials [1]. Antimicrobial resistance (AMR) is a global health problem and the environment is an important compartment for the evolution and transmission of AMR [2,3]. Soil is an environment with a large reservoir of natural microbial communities and antimicrobial resistance (AMR) genes. Those natural microbial communities are frequently exposed to biocides used as material preservatives. Previous studies have shown that antibiotics, metals and pesticides affect the underlying processes of resistance evolution and spread; namely de novo mutagenesis and horizontal gene transfer by conjugation and transformation in microbial communities. However, it is unknown if active substances used in material preservatives are involved in these processes. We show that biocides used as material preservatives affect rates of mutation and conjugation in microorganism in a species- and substance-dependent manner, while rates of transformation are not directly affected. Our data highlights the importance of assessing the contribution of material preservatives on AMR evolution and spread in the environment. T2 - RokoCon2022 CY - Berlin, Germany DA - 29.09.2022 KW - Biocide KW - Antimicrobial resistance KW - Tolerance KW - Horizontal gene transfer KW - Mutation rate PY - 2022 AN - OPUS4-56431 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schmidt, Alexandra A1 - Bresch, Harald T1 - OECD test guideline on particle size and size distribution: Comparability of measurement results N2 - OECD-Prüfrichtlinien werden weltweit für regulatorische Zwecke angewandt, da sie eine harmonisierte und über internationale Ringversuche validierte Vorschrift zur Analyse vorgeben. Die bestehende Prüfrichtlinie TG 110 zur Größencharakterisierung von Partikeln und Fasern ist für viele Methoden und Materialklassen nicht geeignet, weswegen es Bedarf an einer Neuentwicklung gibt. Im Fokus der neuen TG steht die reproduzierbare und vergleichbare Anwendung von Methoden zur Bestimmung von Partikelgröße sowie Größenverteilung annährend sphärischer und faserförmiger Nanomaterialien im Bereich 1-1000 nm. Berücksichtigt werden die häufig angewandten Methoden zur Größencharakterisierung mit ihren unterschiedlichen physikalisch-technischen Limitierungen und die Bestimmung unterschiedlicher Durchmesser (hydrodynamischer, Feret…). Weiterhin sind materialspezifische Einflüsse durch die Partikel sowie das Messmedium zu berücksichtigen. Jede der Methoden soll unter Berücksichtigung von ISO-Standards und den materialspezifischen Limitierungen in der neuen Prüfrichtlinie beschrieben und über einen Ringversuch validiert werden. T2 - BAM BfR Workshop CY - Berlin, Germany DA - 21.03.2019 KW - OECD KW - Nanoparticle KW - Particle Size KW - Nano KW - Characterization PY - 2019 AN - OPUS4-47633 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlögel, Kai A1 - Loose, Florian A1 - Hee, Johann A1 - Quicker, Peter A1 - Adam, Christian T1 - Enhancing the Sustainability of Carbon Fibre Reinforced Polymers (CFRP Strategies for Effective Feedstock Recycling as Reducing Agents in Pyrometallurgy N2 - Despite its contribution to tackling climate change by lightweight design, growing CFRP production also results in a global waste generation of 62 kt/a. Accordingly, the energy-intensive production process of carbon fibers (CF) necessitates sustainable recycling solutions. Herein we will give an overview of current recycling processes, discuss their limitations and present a novel approach for safe treatment of CF unsuitable for material recovery . Our project CF Pyro examines feedstock recycling in pyrometallurgical processes, focusing on reactivity of CF, process stability and prevention of hazardous WHO fiber release. Besides fundamental experimental breakthroughs, their broader impact on circular economy will be presented. T2 - CU Online Forum „Composites and Sustainability“ CY - Online meeting DA - 29.06.2021 KW - Carbon Fibers KW - Recycling KW - Electric Arc Furnace KW - CFRP KW - Pyrometallurgy KW - Steelmaking PY - 2021 AN - OPUS4-52920 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schliephake, H. A1 - Adam, Christian T1 - CFK-Abfälle als Primärkohleersatz Im Lichtbogenofen bei der Stahlerzeugung N2 - CFK-Abfälle werden trotz der bestehenden Verfahren zur Rückgewinnung der Carbonfasern zukünftig vermehrt anfallen. Für diese Abfälle wird nach technischen Lösungen der energetischen oder stofflichen Verwertung gesucht. Eine Möglichkeit ist die Nutzung der CFK-Abfälle als Primärkohleersatz im Lichtbogenofen bei der Stahlherstellung. T2 - 3. Fachtagung Composite Recycling & LCA CY - Stuttgart, Germany DA - 20.02.2019 KW - Carbonfaser KW - CFK PY - 2019 AN - OPUS4-47438 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Rühle, Bastian A1 - Bresch, Harald A1 - Resch-Genger, Ute A1 - Hodoroaba, Vasile-Dan A1 - Radnick, Jörg T1 - Perspektive der BAM auf neuartige Materialien N2 - Neuartige Materialien, die bekannte (Werk-)Stoffe mit neuen Funktionalitäten ausstatten, spielen eine zunehmend wichtige Rolle im Bereich der Materialforschung und -prüfung. Das Spektrum neuartiger Materialien reicht von der gezielten Oberflächenfunktionalisierung und -strukturierung makroskopischer Materialien, dünnen Beschichtungen bis hin zu mikro- und nanoskaligen Kompositmaterialien und funktionalen Materialien an der Schnittstelle zur Biologie, Biotechnologie, nachhaltige Energiespeicherung und Sensorik. Dabei bieten neuartige Materialien die Chance, Werkstoffe und Produkte mit erweiterter oder verbesserter Funktionalität zu erhalten und Sicherheit bereits im Designprozess zu berücksichtigen. Durch dieses breite Anwendungsspektrum und die Herausforderungen, die solche Materialien für die Sicherheit in Chemie und Technik mit sich bringen, sind diese in allen Themenfeldern der BAM repräsentiert (Material, Analytical Sciences, Energie, Infrastruktur und Umwelt). Die Aufgaben der BAM erstrecken sich dabei von der Herstellung von Referenzmaterialien für Industrie, Forschung und Regulation, über die Erstellung von standardisierten Referenzverfahren für nachhaltige Messungen im Umwelt- und Lebenswissenschaftsbereich bis hin zur Bereitstellung von belastbaren und zitierbaren Referenzdaten. Durch die genaue Charakterisierung neuartiger Materialien können potentiell problematische Substanzen identifiziert und deren Risiken besser abgeschätzt werden. In diesem Beitrag werden einige aktuelle Beispiele aus diesen Bereichen vorgestellt. T2 - NanoDialog der Bundesregierung - Chancen und Risiken von Neuartigen Materialien CY - Berlin, Germany DA - 22.05.2019 KW - Advanced Materials KW - Nanomaterialien KW - Neuartige Materialien PY - 2019 AN - OPUS4-49594 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -