TY - CONF A1 - Piehl, Patrick A1 - Weingart, E. A1 - Adam, Christian T1 - Recovery of zinc from steel mill dusts in the rotary kiln by joint treatment with chloride-containing residues N2 - During iron and steel production, several by-products such as slags, dusts and sludges are generated in addition to pig iron and steel as primary products. While established recycling routes exist for slags, there are still considerable recycling problems for other residual materials, especially for filter dusts and sludges containing zinc and lead from waste gas purification. However, the high heavy metal contents make landfilling these dusts and sludges cost-intensive and ecologically problematic. In addition, the relatively high zinc and iron loads represent a valuable material potential, which can make reprocessing of the material with recovery of the zinc and iron loads as secondary raw materials ecologically as well as economically attractive. Against this background, a process is being developed in a cooperative project between Ferro Duo GmbH and the Federal Institute for Materials Research and Testing (BAM), in which the heavy metals (zinc, lead, cadmium, etc.) contained in the filter dusts and sludges are selectively converted into chlorides in a thermochemical process after the addition of a chlorine donor and evaporated at temperatures between 650 and 1100 °C. This process can be used to recover zinc and iron as secondary raw materials. Experiments to date in a batch reactor show that >99% of the zinc and lead can be removed from the treated material. However, a continuous process is necessary for an economical process, which is why this process is transferred to a rotary kiln and relevant process parameters are identified and optimized. The results of these investigations will be presented here. T2 - European Congress and Exhibition on Advanced Materials and Processes 2021 CY - Online meeting DA - 13.09.2021 KW - Elektroofenstaub KW - Gichtgasschlamm KW - Recycling KW - Ressourcenrückgewinnung KW - Zink PY - 2021 AN - OPUS4-53290 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Piehl, Patrick A1 - Auer, G. A1 - Kehrmann, A. A1 - Adam, Christian T1 - Thermochemical treatment of steel work dusts and sludges for the recovery of zinc and iron N2 - During iron and steel production, several by-products such as slags, dusts, and sludges are generated in addition to pig iron and steel as primary products. Especially for filter dusts and sludges containing zinc and lead from gas purification, there are still considerable recycling problems. However, the high heavy metal contents make landfilling of these dusts and sludges cost-intensive and ecologically problematic. In addition, the relatively high zinc and iron loads represent a valuable resource, which can make reprocessing of the material with recovery of the zinc and iron loads as secondary raw materials ecologically as well as economically attractive. Nevertheless, established recycling methods like the Waelz process fall short in regaining more than one valuable metal from the dusts and operate only under narrow ranges of material compositions, which makes it problematic to adapt these processes to new dust compositions as are to be formed in future steel work operations. To tackle these problems, the German Federal Institute for Materials Research and Testing (BAM) and Ferro Duo GmbH investigate innovative recycling methods for steelwork dusts and sludges in a joint project. This mainly focusses on regaining valuable metals such as iron as well as zinc from blast furnace sludge (BFS) and electric arc furnace dust (EAFD) by thermochemical treatment. Therefore, mixtures of these materials are heated under inert atmosphere employing the carbon present in BFS as internal reducing agent. During the process, metallic iron is formed in the solid reaction product while zinc and other volatile heavy metals are evaporated. This paves the way for the generation of zinc as well as sponge iron as two separate products valuable for metallurgical processes. The process basically consists of heating a mixture of BFS and EAFD to temperatures between 700 and 1100 °C under inert (e.g., nitrogen) or reducing (e.g., CO) gas flow. When a suitable mixing ratio is applied, the carbon present in the BFS can be effectively used as reducing agent for iron and zinc present in both starting materials generating a solid residue with high metallic iron and low carbon content as well as a gas stream laden with zinc and other volatile heavy metals, that can be regained by off-gas treatment. The project aims at testing this concept as a continuous process in a pilot plant established by Ferro Duo GmbH with BAM supplying comprehensive scientific support by lab- and small scale-experiments. Additionally, considering the necessity to mitigate CO2 emissions and the resulting shift in compositions of steel work dusts and sludges, our research also investigates replacement of carbon present in the sludges by hydrogen as potentially carbon-neutral reducing agent. Here, the use of non-explosive forming gas as reducing agent for EAFD shows potential to give a product high in metallic iron while zinc and other heavy metals are effectively evaporated from the solid material making it possible to regain them from the exhaust gas stream. T2 - 11th European Slag Conference CY - Cologne, Germany DA - 04.10.2022 KW - Elektroofenstaub KW - Gichtgasschlamm KW - Recycling KW - Ressourcenrückgewinnung KW - Zink PY - 2022 AN - OPUS4-55950 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Piehl, Patrick T1 - Thermochemische Aufarbeitung von Stahlwerksstäuben und -schlämmen zur Zink- und Eisenrückgewinnung N2 - Stahlwerksstäube und -schlämme enthalten in der Regel Schwermetalle wie Zink, Blei und Cadmium, die ein direktes Recycling verhindern und diese Stoffe potenziell umweltgefährdend machen. Um diese Schwermetalle aus den Materialien zu entfernen, werden drei thermochemische Verfahren zur Aufarbeitung von Gichtgasschlamm, Elektroofenstaub und ähnlichen Stahlwerksstäuben vorgestellt. Zum einen kann die Mischung von Elektroofenstaub mit chloridhaltigen Lösungen, wie sie z. B. in der Titandioxidproduktion anfallen, gemischt werden, um bei der thermischen Behandlung Schwermetallchloride zu effektiv verdampfen. Weiterhin kann der im Gichtgasschlamm enthaltene Kohlenstoff genutzt werden, um in Mischungen aus Gichtgasschlamm und Elektroofenstaub bei der thermischen Behandlung als Reduktionsmittel zu wirken. Dieses Verfahren führt zur Rückgewinnung von Zink und metallischem Eisen und wird im Technikums- und Pilotmaßstab erprobt. Abschließend wird die Nutzung von Wasserstoff als Reduktionsmittel für Elektroofenstaub vorgestellt. Hierbei lässt sich der Reststoff potenziell klimaneutral in Eisenschwamm umwandeln, wobei die chemischen Grundlagen anhand von DTA-Experimenten und thermodynamischen Simulationen ergründet werden. T2 - Berliner Konferenz Metallkreisläufe CY - Berlin, Germany DA - 13.04.2024 KW - Elektroofenstaub KW - Gichtgasschlamm KW - Recycling KW - Ressourcenrückgewinnung KW - Zink PY - 2024 AN - OPUS4-59726 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schliephake, H. A1 - Adam, Christian T1 - CFK-Abfälle als Primärkohleersatz Im Lichtbogenofen bei der Stahlerzeugung N2 - CFK-Abfälle werden trotz der bestehenden Verfahren zur Rückgewinnung der Carbonfasern zukünftig vermehrt anfallen. Für diese Abfälle wird nach technischen Lösungen der energetischen oder stofflichen Verwertung gesucht. Eine Möglichkeit ist die Nutzung der CFK-Abfälle als Primärkohleersatz im Lichtbogenofen bei der Stahlherstellung. T2 - 3. Fachtagung Composite Recycling & LCA CY - Stuttgart, Germany DA - 20.02.2019 KW - Carbonfaser KW - CFK PY - 2019 AN - OPUS4-47438 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schlögel, Kai A1 - Loose, Florian A1 - Hee, Johann A1 - Quicker, Peter A1 - Adam, Christian T1 - Enhancing the Sustainability of Carbon Fibre Reinforced Polymers (CFRP Strategies for Effective Feedstock Recycling as Reducing Agents in Pyrometallurgy N2 - Despite its contribution to tackling climate change by lightweight design, growing CFRP production also results in a global waste generation of 62 kt/a. Accordingly, the energy-intensive production process of carbon fibers (CF) necessitates sustainable recycling solutions. Herein we will give an overview of current recycling processes, discuss their limitations and present a novel approach for safe treatment of CF unsuitable for material recovery . Our project CF Pyro examines feedstock recycling in pyrometallurgical processes, focusing on reactivity of CF, process stability and prevention of hazardous WHO fiber release. Besides fundamental experimental breakthroughs, their broader impact on circular economy will be presented. T2 - CU Online Forum „Composites and Sustainability“ CY - Online meeting DA - 29.06.2021 KW - Carbon Fibers KW - Recycling KW - Electric Arc Furnace KW - CFRP KW - Pyrometallurgy KW - Steelmaking PY - 2021 AN - OPUS4-52920 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar A1 - Adam, Christian T1 - Formation and hydraulic reactivity of an alite rich material from post treated basic oxygen furnace slag N2 - Basic oxygen furnace slag (BOFS) is a by-product of steelmaking of which about 10.4 Mt are produced annually in the EU. BOFS is mostly used in road construction, earthwork and hydraulic engineering. However, in this use, the iron bound in BOFS is lost and the opportunity to produce higher value products from BOFS is forgone. In recent decades, many researchers have investigated a thermochemical process to reduce iron oxides to metallic iron in molten BOFS. The metallic iron formed separates from the reduced slag due to its higher density and can be recovered. An advantage of this process is that simultaneously the chemical composition of the reduced slag is adapted to that of the Portland cement clinker and the hydraulic reactive mineral alite is formed. In this study, BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent, and the hydraulic properties of the reduced, low-iron BOFS were investigated. Despite a chemical and mineralogical composition similar to that of Portland cement clinker, the reduced BOFS produced less heat of hydration, and its reaction was delayed compared to Portland cement. However, the addition of gypsum, as is also done in cement production from Portland cement clinker, has been found to accelerate the hydration rate of reduced BOFS. Further research to improve the hydraulic properties of the reduced slag is essential. If successful, the production of a hydraulic binder and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry. T2 - GeoMin Köln 2022 CY - Cologne, Germany DA - 11.09.2022 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2022 AN - OPUS4-56080 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian T1 - Reductive treatment of steel making slags to produce a hydraulic binder and crude iron N2 - Steelmaking slags are a by-product of steel production, that are currently used primarily in road construction, earthwork, and hydraulic engineering. In this use, the iron bound in the steelmaking slags (< 30 wt.%) is lost. Recovery of iron from steelmaking slags is possible by thermochemical reductive treatment. The reductive treatment of liquid steelmaking slags causes iron oxides to be reduced to metallic iron, which separates from the mineral phase due to its higher density. The chemical composition of the mineral phase is thus adapted to that of the Portland cement clinker and the mineral alite, the most important component of Portland cement, is formed. This way, crude iron can be recovered, and at the same time a hydraulic binder can be produced. This process, however, is uneconomical due to the high temperatures required (~1800 °C). In the current project, the process is to be adapted so that the reduction of liquid steelmaking slag can be carried out at ~1600 °C. The chemical composition is to be modified in such a way that the melting temperature of the slags as well as their viscosity are in a technically suitable range and still a product with good cementitious properties is obtained. T2 - LithiumDays CY - Online meeting DA - 06.12.2021 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2021 AN - OPUS4-56081 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar A1 - Adam, Christian T1 - Hydraulic reactivity of alite rich material from post-treated basic oxygen furnace slags N2 - Basic oxygen furnace slags (BOFS) are a by-product of steel production. In 2016, 10.4 Mt of BOFS were produced in the European Union (EU). The main part of BOFS is used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. However, it is also possible to produce higher value products from BOFS. For example, many researchers have investigated the possibility of producing Portland cement clinker and crude iron from BOFS by a carbothermal post-treatment. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The carbothermal treatment reduces the iron oxides in the BOFS to metallic iron, which accumulates at the bottom of the furnace by density separation. In addition to metallic iron, the process generates a mineral product rich in the tricalcium silicate solid solution alite. As the main constituent of Portland cement clinker, the hydraulic reactive mineral alite is of high economic importance. In previous studies, the hydraulic reactivity of the mineral product was investigated by testing the compressive strength of blends with 70 wt.% ordinary Portland cement (OPC). Recent investigations focused on the hydraulic properties of the pure mineral product from the reduced BOFS. The heat of hydration of the mineral product was measured by isothermal calorimetry and compared with the heat of hydration of a synthetic low-iron slag and OPC. In addition, the formation of hydration products was investigated with differential scanning calorimetry (DSC) and x-ray diffraction analysis (XRD) on freeze-dried samples after defined curing times. The results of the calorimetric measurements indicate that the mineral product produced less heat of hydration and its reaction was delayed compared to the synthetic low-iron slag and OPC. Hydration products such as portlandite and calcium silicate hydrates (C-S-H) formed later and in lower amounts. The production of a hydraulic material from BOFS by reductive treatment is of great interest to both the cement and steel industries. The substitution of cement clinker in OPC with a hydraulic material such as reduced BOFS leads to a reduction in greenhouse gas emissions from cement production. The steel industry benefits from an application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. Furthermore, it may be possible to return the recovered crude iron to production. T2 - 3rd European Mineralogical Conference CY - Cracow, Poland DA - 30.08.2021 KW - BOFS KW - Calcium silicate KW - Hydraulic reactivity PY - 2021 AN - OPUS4-53473 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar A1 - Adam, Christian T1 - Portland cement clinker from reduced basic oxygen furnace slag N2 - Basic oxygen furnace slag (BOFS) is a by-product of the steelmaking process, of which about 10.4 Mt are produced annually in the European Union. Besides its predominant use in road construction, earthwork, and hydraulic engineering, it is also possible to use BOFS as a source material for Portland cement clinker. The main difference in the chemical composition of BOFS from the chemical composition of Portland cement clinker is its high content of iron oxides (7-50 wt.%). In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via thermochemical reductive treatment. Carbothermal treatment of liquid BOFS causes reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as reducing agent. The produced low-iron mineral product was chemically similar to Portland cement clinker and contained the most important Portland cement mineral alite (Ca3SiO5) as main component. Besides alite, the mineral product contained other Portland cement clinker constituents such as belite (β-Ca2SiO4) and tricalcium aluminate (Ca3Al2O6). The production of Portland cement clinker and crude iron from BOFS has economic and ecological benefits for both the cement and steel industry. Cement clinker from reduced BOFS may be used as a substitute for cement clinker from conventional cement production, thereby CO2 emissions will be reduced. The steel industry benefits from a high-value application for its by-products that avoids cost expensive landfilling and may even bring economic advantages. However, reductive treatment requires high temperatures and, for economic reasons, has to be carried out immediately after casting of the liquid BOFS, which is a logistical challenge for most steel plants. A cost-benefit analysis is therefore essential. T2 - European Congress and Exhibition on Advanced Materials and Processes CY - Online meeting DA - 13.09.2021 KW - BOFS KW - Portland Cement KW - Hydraulic reactivity PY - 2021 AN - OPUS4-53475 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar Aloys A1 - Adam, Christian T1 - Zementklinker durch Nachbehandlung von Stahlwerksschlacken N2 - Die Klinkerphasenbildung durch Sinterung in Drehrohröfen bei der Herstellung von Portlandzementklinker (PZK) ist gründlich erforscht und optimiert. Im Hinblick auf mög-liche ökonomische und ökologische Vorteile befassen sich aktuelle Forschungsvorha-ben darüber hinaus mit der Herstellung von Klinkermineralen aus Stahlwerksschla-cken, die eine vergleichbare chemische Zusammensetzung aufweisen. Neuste Untersuchungen zeigen, dass nach der reduzierenden Behandlung schmelz-flüssiger Linz-Donawitz-(LD)-Schlacken und Abscheidung des gebildeten metallischen Eisens eine mineralische Schlacke entsteht, die unabhängig von ihren Abkühlbedin-gungen ca. 50–60 Gew.% des wichtigsten Klinkerminerals Alit (C3S) enthält und eine hohe hydraulische Reaktivität aufweist. Die Stabilität des Alits auch nach langsamer Abkühlung deutet auf eine Stabilisierung des Minerals durch Nebenelemente aus den LD-Schlacken hin. Ein sinkender Anteil an LD-Schlacke durch Zusatz synthetischer Schlackemischung, die sich hinsichtlich ihrer Hauptkomponenten wie eine ausreduzierte LD-Schlacke zusammensetzt, führt zu einem Rückgang des Alitgehaltes und dem Zerfall der Schlacke beim Erstarren. T2 - 5. Schlacken-Symposium CY - Meitingen, Germany DA - 25.10.2018 KW - Zement KW - LD-Schlacke KW - Tricalciumsilikat PY - 2018 AN - OPUS4-46409 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian A1 - Stephan, D. A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit T1 - Production of a hydraulic material from post-treated steelmaking slags N2 - Steelmaking slag is a by-product of steel production of which 4.5 Mt were produced in 2020 in Germany alone. It is mainly used in road construction, earthwork and hydraulic engineering. A smaller part is returned to the metallurgical circle, used as fertilizer or landfilled. With this use, iron oxides still contained in steelmaking slag are lost. In addition, the possibility of producing higher-grade products from steelmaking slag is foregone. In recent decades, many researchers have investigated the production of Portland cement clinker and crude iron from basic oxygen furnace slags (BOFS) via a reductive treatment. Carbothermal treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density. Simultaneously, the chemical composition of the reduced slag is adapted to that of the Portland cement clinker. In this study, German BOFS was reduced in a small-scale electric arc furnace using petrol coke as a reducing agent. The resulting low-iron mineral product had a similar chemical composition to Portland cement clinker and was rich in the tricalcium silicate solid solution alite (Ca3SiO5). Based on its chemical and mineralogical composition, similar to that of Portland cement clinker, the reduced BOFS has the potential to react comparably. In our study, the reduced BOFS produced less heat of hydration compared to OPC and its hydraulic reaction was delayed. However, adding gypsum has been shown to accelerate the hydration rate of the reduced BOFS compared to that known from the calcium silicates of Portland cement clinker. Further research to improve the hydraulic properties of the reduced slag is essential. If successful, producing a hydraulic binder and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry. T2 - 16th International Congress on the Chemistry of Cement ICCC 2023 CY - Bangkok, Thailand DA - 18.09.2023 KW - Steelmaking slag KW - Alite hydraulic reactivity KW - Clinker substitute PY - 2023 AN - OPUS4-58522 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schraut, Katharina A1 - Adam, Christian A1 - Adamczyk, Burkart A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Meng, Birgit A1 - Stephan, Dietmar T1 - Production of an alite-rich material from reduced basic oxygen furnace slags N2 - Basic oxygen furnace slag (BOFS) is a by-product of steelmaking of which about 10.4 Mt are produced annually in the EU. BOFS is mostly used in road construction, earthwork and hydraulic engineering. However, in this use, the iron bound in BOFS is lost and the opportunity to produce higher value products from BOFS is forgone. In recent decades, many researchers have investigated the production of both Portland cement clinker and crude iron from BOFS via a thermochemical reductive treatment. The reductive treatment of liquid BOFS causes a reduction of iron oxides to metallic iron, which separates from the mineral phase due to its higher density and can be recovered. An advantage of this process is that simultaneously the chemical composition of the reduced BOFS is adapted to that of Portland cement clinker and the hydraulic reactive mineral alite (Ca3SiO5) is formed. In this study, German BOFS was reduced in a small-scale electric arc furnace and a low-iron mineral product rich in alite was produced. Despite a chemical and mineralogical composition similar to that of Portland cement clinker, the reduced BOFS produced less heat of hydration, and its reaction was delayed compared to Portland cement. However, adding gypsum accelerated the hydration rate of the reduced BOFS. Further research to improve the hydraulic properties of the reduced BOFS is essential. If successful, the production of a hydraulic material and crude iron from BOFS could have economic and ecological benefits for both the cement and steel industry. T2 - GeoBerlin 2023 CY - Berlin, Germany DA - 04.09.2023 KW - BOFS KW - Alite KW - Hydraulic reactivity PY - 2023 AN - OPUS4-58206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sichler, Theresa A1 - Herzel, Hannes A1 - Adam, Christian T1 - European Sewage Sludge Ash Monitoring N2 - For the European sewage sludge ash monitoring ash samples from sewage sludge incineration plants were requested from all over Europe. First results of the received samples regarding main and trace element contents were presented at ESPC4. Moreover, a list of all known European facilities for sewage sludge monoincineration was presented. T2 - European Sustainable Phosphorus Conference 4 CY - Vienna, Austria DA - 20.06.2022 KW - Sewage sludge ash KW - Sewage sludge incineration KW - Phosphorus recovery PY - 2022 AN - OPUS4-55145 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sichler, Theresa T1 - Analyseverfahren und Messhäufigkeit zur Bestimmung des Phosphorgehalts im Klärschlamm nach AbfKlärV N2 - Auf dem Betreiberforum der DWA-Plattform P-Rück wurden die Empfehlungen für den Vollzug der Phosphorrückgewinnungspflicht aus Klärschlamm vorgestellt. Diese Empfehlungen behandeln die Häufigkeit der Phosphoruntersuchungen im Klärschlamm, wo ein Jahresgang empfohlen wird und eine Empfehlung der Phosphorbestimmung über Aufschluss der Probe in der Mikrowelle und Messung mit ICP-OES. Untermauert wurden die Empfehlungen mit den Ergebnissen von Klärschlamm-Monitoring, Ringversuch und Analytikvergleich aus dem Vorhaben extraWERT. T2 - Betreiberforum der DWA-Plattform P-Rück CY - Stuttgart, Germany DA - 23.06.2022 KW - Klärschlamm KW - Ringversuch KW - Reproduzierbarkeit KW - Phosphorrückgewinnung PY - 2022 AN - OPUS4-55146 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sichler, Theresa A1 - Roskosch, A. A1 - Adam, Christian T1 - Ergebnisse des Vorhabens extraWERT N2 - Der Vortrag liefert eine Zusammenfassung der wichtigsten Ergebnisse des extraWERT-Vorhabens mit Schwerpunkt auf den Umsetzungsfragen zur Klärschlammverordnung. Bei diesen Punkten handelt es sich um die Untersuchung von monatlichen Phosphorschwankungen in kommunalem Klärschlamm und die Gleichwertigkeit verschiedener Verfahren zur Phosphorbestimmung in Klärschlamm. T2 - vgbe-Fachtagung Thermische Abfall-, Klärschlammbehandlung und Wirbelschichtfeuerungen 2022 CY - Hamburg, Germany DA - 09.05.2022 KW - Klärschlammverordnung KW - Phosphorrückgewinnung KW - Ringversuch PY - 2022 AN - OPUS4-54843 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sichler, Theresa T1 - BAM-Projekt „extraWERT“: Gleichwertigkeit der nach AbfKlärV zulässigen Verfahren zur Phosphorbestimmung in Klärschlamm N2 - In Deutschland ist ab 2029 eine Phosphorrückgewinnung aus Klärschlamm verpflichtend. Ausgenommen sind Klärschlämme mit weniger als 20 g P/kg TM. Für die Phosphorbestimmung sind verschiedene Methoden nach Klärschlammverordnung als gleichwertig zugelassen: Der Königswasseraufschluss in der Mikrowelle und am Rückfluss sowie die Messung an ICP-OES, ICP-MS und die photometrische Bestimmung mittels Ammoniummolybdaten. An der BAM wurden die unterschiedlichen Methodenkombinationen aus Aufschluss- und Messmethode an 15 Klärschlämmen überprüft und in einem Ringversuch mit einem Klärschlamm getestet. Die Ergebnisse werden in diesem Vortrag zusammengefasst. Als Folge der Untersuchungen wird für die Phosphorbestimmung in Klärschlamm die ICP-OES-Messung nach Königswasseraufschluss in der Mikrowelle empfohlen. T2 - VDLUFA Frühjahrssitzung 2022 der Fachgruppe III Düngemittel CY - Vienna, Austria DA - 18.05.2022 KW - Ringversuch KW - Reproduzierbarkeit KW - Wiederholbarkeit KW - Phosphorrückgewinnung KW - Gleichwertigkeit Messverfahren PY - 2022 AN - OPUS4-54852 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sichler, Theresa A1 - Adam, Christian T1 - Nährstoffrückgewinnung aus Klärschlamm: Eine Betrachtung zukünftiger Verwertungsszenarien für Deutschland N2 - Agricultural sewage sludge utilization becomes less important in Germany. In 2017, new fertilizer and waste laws caused the agricultural sewage sludge utilization to collapse by more than a quarter. From 2029, in German wastewater treatment plants (WWTPs) phosphorus (P) must be recovered from sewage sludge ifit contains more than 2 wt % P. Agricultural utilization will be prohibited for large WWTPs > 100,000 population equivalents (pe) from 2029 and > 50,000 pe from 2032. In Germany, each federal state must annually report amounts and quality of agriculturally utilized sewage sludge which was 17 % of the total disposal in 2019. The reports of 10 States were evaluated for 2016 and 2017 representing approx. 60 % ofthe total agriculturallyused sludge volume. Whereas phosphorus recovery is mandatory this does not apply to other nutrients. However, many P recovery processes recover other nutrients, too. Considering three differentscenariosfor future German sewage sludge disposal shows that 70 - 77 % ofthe P load in sewage sludge will probably be recovered in the future. At the same time, this applies for about 0 - 16 % of nitrogen, 36 - 52 % of calcium, 31-53 % of potassium, and 40 - 52 % of magnesium. However, these recovered nut rient loads can substitute only 1 % or less ofthe commercial fertilizer demand except from phosphorus which is about 45 % ofthe demand. T2 - Berliner Klärschlammkonferenz CY - Berlin, Germany DA - 15.11.2021 KW - Phosphor KW - Klärschlammverordnung KW - Phosphorrückgewinnung PY - 2021 AN - OPUS4-54118 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sichler, Theresa T1 - Ergebnisse des Vorhabens extraWERT - Gleichwertigkeit zugelassener Methoden zur Phosphoruntersuchung des Klärschlamms N2 - Die Ergebnisse des extraWERT-Vorhabens wurden Vertreter*innen des Umweltministeriums von Bund und Ländern vorgestellt und im Zusammenhang mit dem Vollzug der AbfKlärV diskutiert. Es ging um die Phosphorschwankungen in kommunalem Klärschlamm und eine Empfehlung der Untersuchungshäufigkeit, um den Phosphorgehalt rechtssicher festzustellen. Des weiteren wurde die Performance verschiedener nach Verordnung gleichwertiger Analyseverfahren für Phosphor in Klärschlamm diskutiert anhand von Ringversuchsergebnissen und Eigenuntersuchungen an 15 Klärschlammproben. T2 - Bund-Länder-Gespräch zum Vollzug der AbfKlärV CY - Online meeting DA - 16.12.2021 KW - Klärschlammverordnung KW - Phosphorrückgewinnung KW - Analytik KW - Ringversuch PY - 2021 AN - OPUS4-54119 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sichler, Theresa T1 - Gleichwertigkeit der nach AbfKlärV zulässigen Verfahren zur Phosphorbestimmung in Klärschlamm N2 - In dem Meeting wurde den Notifizierern und Ausrichtern des jährlichen länderübergreifenden Ringversuchs Klärschlamm die Ergebnisse zu Untersuchungen hinsichtlich der Gleichwertigkeit verschiedener nach AbfKlärV zulässiger Verfahren zur Phosphorbestimmung in Klärschlamm vorgestellt. Die Untersuchungen an 15 Klärschlammproben ergaben die höchsten Ergebnisse für das Messverfahren ICP-OES und das Aufschlussverfahren in der Mikrowelle. Diese Ergebnisse wurden im Ringversuch bestätigt. T2 - Meeting der Notifizierer und Ausrichter des länderübergreifenden Ringversuchs (LÜRV) CY - Online meeting DA - 08.12.2021 KW - Klärschlammverordnung KW - Analytik KW - Ringversuch KW - Phosphorbestimmung PY - 2021 AN - OPUS4-54121 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Sichler, Theresa T1 - Schwankungen der P-Gehalte in Klärschlämmen im Kontext der Klärschlammverordnung N2 - Es wurden die Schwankungen der Phosphorgehalte in kommunalem Klärschlamm vorgestellt. Dazu wurden von 9 Kläranlagen monatlich Klärschlammproben genommen und auf P untersucht. T2 - KlärschlammTage CY - Online Meeting DA - 09.06.2021 KW - Phosphor KW - Klärschlamm KW - Phosphorrückgewinnung KW - Abwasserbehandlung KW - Klärschlammverordnung PY - 2021 AN - OPUS4-52840 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -