TY - JOUR A1 - Rieger, J. A1 - Colla, V. A1 - Matino, I. A1 - Branca, T. A. A1 - Stubbe, G. A1 - Panizza, A. A1 - Brondi, C. A1 - Falsafi, M. A1 - Hage, J. A1 - Wang, X. A1 - Voraberger, B. A1 - Fenzl, T. A1 - Masaguer, V. A1 - Faraci, E. L. A1 - di Sante, L. A1 - Cirilli, F. A1 - Loose, Florian A1 - Thaler, C. A1 - Soto, A. A1 - Frittella, P. A1 - Foglio, G. A1 - di Cecca, C. A1 - Tellaroli, M. A1 - Corbella, M. A1 - Guzzon, M. A1 - Malfa, E. A1 - Morillon, A. A1 - Algermissen, D. A1 - Peters, K. A1 - Snaet, D. T1 - Residue Valorization in the Iron and Steel Industries: Sustainable Solutions for a Cleaner and More Competitive Future Europe N2 - The steel industry is an important engine for sustainable growth, added value, and high-quality employment within the European Union. It is committed to reducing its CO2 emissions due to production by up to 50% by 2030 compared to 1990′s level by developing and upscaling the technologies required to contribute to European initiatives, such as the Circular Economy Action Plan (CEAP) and the European Green Deal (EGD). The Clean Steel Partnership (CSP, a public–private partnership), which is led by the European Steel Association (EUROFER) and the European Steel Technology Platform (ESTEP), defined technological CO2 mitigation pathways comprising carbon direct avoidance (CDA), smart carbon usage SCU), and a circular economy (CE). CE ap-proaches ensure competitiveness through increased resource efficiency and sustainability and consist of different issues, such as the valorization of steelmaking residues (dusts, slags, sludge) for internal recycling in the steelmaking process, enhanced steel recycling (scrap use), the use of secondary carbon carriers from non-steel sectors as a reducing agent and energy source in the steelmaking process chain, and CE business models (supply chain analyses). The current paper gives an overview of different technological CE approaches as obtained in a dedicated workshop called “Resi4Future—Residue valorization in iron and steel industry: sustainable solutions for a cleaner and more competitive future Europe” that was organized by ESTEP to focus on future challenges toward the final goal of industrial deployment. KW - Circular economy KW - Steelmaking residues KW - Clean steel PY - 2021 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-530350 VL - 11 IS - 8 SP - 1202 PB - MDPI AN - OPUS4-53035 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Neuhold, S. A1 - Algermissen, D. A1 - Drissen, P. A1 - Adamczyk, Burkart A1 - Presoly, P. A1 - Sedlazeck, K. P. A1 - Schenk, J. A1 - Raith, J. G. A1 - Pomberger, R. A1 - Vollprecht, D. T1 - Tailoring the FeO/SiO2 Ratio in Electric Arc Furnace Slags to Minimize the Leaching of Vanadium and Chromium N2 - Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior. KW - Electric arc furnace (EAF) slags KW - FactSageTM calculations KW - Leaching control mechanisms KW - Melting experiments PY - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-571517 VL - 10 IS - 7 SP - 1 EP - 18 PB - MDPI AN - OPUS4-57151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Adamczyk, Burkart A1 - Neuhold, S. A1 - Drissen, P. A1 - Algermissen, D. A1 - Presoly, P. A1 - Sedlazeck, K. P. A1 - Schenk, J. A1 - Raith, J. G. A1 - Pomberger, R. A1 - Vollprecht, D. T1 - Tailoring the FeO/SiO2 ratio in electric arc furnace slags to minimize the leaching of Vanadium and Chromium N2 - Based on recently published research on leaching control mechanisms in electric arc furnace (EAF) slags, it is assumed that a FeO/SiO2 ratio of around one leads to low leached V and Cr concentrations. This ratio influences the mineral phase composition of the slag toward higher amounts of spinel and a lower solubility of calcium silicate phases by suppressing the formation of magnesiowuestite and highly soluble calcium silicate phases. To evaluate this hypothesis, laboratory and scaled up tests in an EAF pilot plant were performed on slag samples characterized by elevated V and Cr leaching and a high FeO/SiO2 ratio. Prior to the melting experiments, the optimum FeO/SiO2 ratio was calculated via FactSageTM. In the melting experiments, the ratio was adjusted by adding quartz sand, which also decreased the basicity (CaO/SiO2) of the slag. As a reference, remelting experiments without quartz sand addition were conducted and additionally, the influence of the cooling rate of the slag was examined. The remelted (without quartz sand) and the remelted modified slags (with quartz sand) were analyzed chemically and mineralogically and the leaching behavior was investigated. The modification of the slags yielded a minimized release of V and Cr, supporting the hypothesis that the FeO/SiO2 ratio influences the mineralogy and the leaching behavior. KW - Electric arc furnace slags KW - FactSage calculations KW - EAF slags KW - Leaching control mechanisms KW - Melting experiments PY - 2020 U6 - http://nbn-resolving.de/urn/resolver.pl?urn:nbn:de:kobv:b43-507748 VL - 10 IS - 7 SP - 2549 EP - 2565 AN - OPUS4-50774 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -