TY - JOUR A1 - Mishra, Biswajit A1 - Kumar Singh, Amit A1 - Shankar Mahobia, Girija T1 - Hydrogen reduction studies of low-grade multimetallic magnetite ore pellets N2 - The hydrogen reducibility of pellets made from a low-grade multimetallic magnetite ore (Fe content ∼ 45 %) was investigated in the present study. Pellets were reduced in a horizontal tube furnace at temperatures ranging from 973 K to 1173 K for 1 to 60 min. Pure Hydrogen (H2) gas (99.9 %) at three flow rates of 0.25 L/min, 0.5 L/min, and 1 L/min were blown during the reduction process. A maximum reduction degree of 94.07 %, metallization ratio of 0.925, and H2 gas utilization of 9.01 % were obtained at a temperature and a reduction time of 1173 K and 60 min, respectively. In order to optimize the hydrogen utilization, a reduction temperature of 1173 K, a reduction time of 45 min, and a gas flow rate of 0.25 L/min were selected, resulting in a reduction degree and metallization ratio of 90 % and 0.89, respectively. The cold crushing strength (CCS) of the reduced pellets initially decreased and then increased slightly, exhibiting behavior similar to high-grade ores. Imputities like SiO2, Al2O3, and MgO, present in the low grade ores are found to control the porosity of the pellets, directly affecting the CCS and reducibility of the pellets. KW - Cold Crushing Strength KW - Low-grade iron ores KW - Hydrogen Reduction KW - Metallization ratio KW - Gangue elements PY - 2024 DO - https://doi.org/10.1016/j.mineng.2024.108823 SN - 0892-6875 VL - 215 SP - 1 EP - 14 PB - Elsevier B.V. AN - OPUS4-62539 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - da Silva, Luiza Helena Bueno A1 - Goes, Aryel C. A1 - Rodrigues, Andre A1 - Fourcassié, Vincent A1 - McMahon, Dino Peter A1 - Haifig, Ives T1 - Social immune response reflects infection progression in a soldierless termite N2 - Social interactions represent a double-edged sword. On one hand, sociality can facilitate sanitary collective behaviours; on the other hand, it creates opportunities for pathogen transmission. In termites, sanitary behaviours can entail a rescuing strategy at early stages of infection, followed by the elimination at later stages. We explored whether the neotropical soldierless species Anoplotermes pacificus employs a progressive approach towards infected nestmates, with different behavioural displays depending on the infection stage. We infected A. pacificus workers with the fungus Metarhizium anisopliae and incubated them for 2, 12, 15 and 20 h, corresponding to infection progression and, therefore, severity. Infected termites were placed with naïve nestmates and their behaviours were recorded for 3 h. Fungus-infected termites triggered up to fourfold higher levels of sanitary behaviour than in non-infected termites. Antennation behaviour decreased during the observation period, whereas sanitary behaviour, which we defined as directed behaviour towards the focal termite involving mouthparts, increased in frequency as incubation duration increased. Sanitary behaviour therefore appears to be a strategy for colony disinfection, which varies in intensity according to infection status, ultimately resulting in the immobilisation of infected individuals at later stages of infection. Alarm responses were also up to three times more frequent in treatment than in control groups and did not vary with incubation duration. A. pacificus workers therefore identify, communicate and respond to pathogen-treated individuals in a progressive manner, indicating that collective responses in this species are also significantly shaped by the stage of infection. By progressively modulating their social immune responses, termites may be able to optimize resource allocation within the colony by balancing the risk of individual infection versus protection of the group. KW - Anoplotermes pacificus KW - Isoptera KW - Infection KW - Metarhizium KW - Social immunity PY - 2024 DO - https://doi.org/10.1007/s00265-024-03556-2 VL - 79 IS - 1 SP - 1 PB - Springer Science and Business Media LLC AN - OPUS4-62397 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vogel, Christian A1 - Roesch, Philipp A1 - Wittwer, Philipp A1 - Sommerfeld, Thomas A1 - Riedel, Maren A1 - Leube, Peter A1 - Kalbe, Ute A1 - Schoknecht, Ute A1 - Simon, Franz-Georg T1 - Per- and Polyfluoroalkyl Substances (PFAS) in Ski Waxes and Snow from Cross-Country Skiing in Germany - Comparative study of Sum Parameter and Target Analysis N2 - Per- and polyfluoroalkyl substances (PFAS) are often environmentally exposed via discharge through human consumer products, such as ski waxes. In our study we analyzed various ski waxes from the 1980s and 2020s, to determine both the sum parameter values total fluorine (TF), extractable organically bound fluorine (EOF), hydrolysable organically bound fluorine (HOF) as well as targeted PFAS analysis. This showed that modern high-performance waxes contain up to 6 % TF, but also PFAS-free labelled ski waxes contain traces of PFAS with EOF/HOF values in the low mg kg-1 range. With the ban of all fluorine-based waxes with the start of the 2023/2024 winter season this will probably change soon. Moreover, we applied our analysis methods to snow samples from a frequently used cross country ski trail (Kammloipe) in the Ore Mountain region in Germany, assessing the potential PFAS entry/discharge through ski waxes. Melted snow samples from different spots were analyzed by the adsorbable organically bound fluorine (AOF) sum parameter and PFAS target analysis and confirmed the abrasion of the ski waxes into the snow. Moreover, on a PFAS hotspot also soil samples were analyzed, which indicate that PFAS from the ski waxes adsorb after snow melting into the soil. KW - Combustion Ion Chromatography KW - Per- and Polyfluoroalkyl substances (PFAS) KW - Consumer Products PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-612760 DO - https://doi.org/10.1016/j.hazadv.2024.100484 VL - 16 SP - 1 EP - 5 PB - Elsevier B.V. AN - OPUS4-61276 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Roesch, Philipp A1 - Schinnen, Andrea A1 - Riedel, Maren A1 - Sommerfeld, Thomas A1 - Sawal, G. A1 - Bandow, N. A1 - Vogel, Christian A1 - Kalbe, Ute A1 - Simon, Franz-Georg T1 - Investigation of pH-dependent extraction methods for PFAS in (fluoropolymer-based) consumer products: A comparative study between targeted and sum parameter analysis N2 - Here, we report a comparative study of different sum parameter analysis methods for the extraction of per- and polyfluoroalkyl substances (PFAS) from manufactured consumer products, which can be measured by combustion ion chromatography (CIC). Therefore, a hydrolysis-based extraction method was further developed, which accounts for the addition of hydrolyzable covalently bound polyfluoroalkylated side-chain polymers (SFPs) to the extractable organic fluorine portion of the mass balance proposed as "hydrolyzable organically bound fluorine" (HOF). To test this hypothesis, the method was applied to 39 different consumer products containing fluoropolymers or monomeric PFAS taken from four different categories: outdoor textiles, paper packaging, carpeting, and permanent baking sheets. We also evaluated the method's efficiency by extracting four synthesized fluorotelomer polyacrylate reference compounds. The total fluorine (TF) and extractable organically bound fluorine (EOF) values were measured through CIC using established protocols. The TF values ranged from sub-ppb to %-levels, depending on the compound class. All samples showed results for hydrolyzed organofluorine (HOF) between 0.03 and 76.3 μg/g, while most EOF values were lower (0.9 and <0.4 mmol/g for both types of chitosan and activated carbon, respectively). Milled activated carbon proved to be the better adsorption material, considering the fixed volume of the adsorber (>99.9% PFOS adsorbed). Overall, the cross-linking agent concentration in chitosan is a crucial factor influencing its PFOS absorption potential. Our results feature cross-linked chitosan as an effective economic and ecologic alternative for PFOS adsorption in aqueous solutions. KW - Combustion Ion Chromatography KW - Per- and Polyfluoroalkyl substances (PFAS) KW - Remediation PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-618406 DO - https://doi.org/10.3390/app142311145 VL - 14 IS - 23 SP - 1 EP - 13 PB - MDPI AN - OPUS4-61840 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wen, Keqing A1 - Gorbushina, Anna A1 - Schwibbert, Karin A1 - Bell, Jérémy T1 - Microfluidic platform with precisely controlled hydrodynamic parameters and integrated features for generation of microvortices to accurately form and monitor biofilms in flow N2 - Microorganisms often live in habitats characterized by fluid flow, and their adhesion to surfaces in industrial systems or clinical settings may lead to pipe clogging, microbially influenced corrosion, material deterioration, food spoilage, infections, and human illness. Here, a novel microfluidic platform was developed to investigate biofilm formation under precisely controlled (i) cell concentration, (ii) temperature, and (iii) flow conditions. The developed platform central unit is a single-channel microfluidic flow cell designed to ensure ultrahomogeneous flow and condition in its central area, where features, e.g., with trapping properties, can be incorporated. In comparison to static and macroflow chamber assays for biofilm studies, microfluidic chips allow in situ monitoring of biofilm formation under various flow regimes and have better environment control and smaller sample requirements. Flow simulations and experiments with fluorescent particles were used to simulate bacteria flow in the platform cell for calculating flow velocity and direction at the microscale level. The combination of flow analysis and fluorescent strain injection in the cell showed that microtraps placed at the center of the channel were efficient in capturing bacteria at determined positions and to study how flow conditions, especially microvortices, can affect biofilm formation. The microfluidic platform exhibited improved performances in terms of homogeneity and robustness for in vitro biofilm formation. We anticipate the presented platform to be suitable for broad, versatile, and high-throughput biofilm studies at the microscale level. KW - Topographical pattern KW - E. coli KW - Fluorescence KW - Bacteria trapping KW - Particle velocimetry PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-610450 DO - https://doi.org/10.1021/acsbiomaterials.4c00101 SN - 2373-9878 VL - 10 IS - 7 SP - 4626 EP - 4634 PB - ACS Publ. CY - Washington, DC AN - OPUS4-61045 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Catanzaro, Ilaria A1 - Gorbushina, Anna A1 - Onofri, Silvano A1 - Schumacher, Julia T1 - 1,8‐Dihydroxynaphthalene (DHN) melanin provides unequal protection to black fungi Knufia petricola and Cryomyces antarcticus from UV‐B radiation N2 - Black fungi on rock surfaces endure a spectrum of abiotic stresses, including UV radiation. Their ability to tolerate extreme conditions is attributed to the convergent evolution of adaptive traits, primarily highly melanized cell walls. However, studies on fungal melanins have not provided univocal results on their photoprotective functions. Here, we investigated whether the black fungi Knufia petricola and Cryomyces antarcticus only use DHN melanin or may employ alternative mechanisms to counteract UV‐induced damage. For this, melanized wild types and non‐melanized Δpks1 mutants were exposed to different doses of UV‐B (312 nm) followed by incubation in constant darkness or in light–dark cycles to allow light‐dependent DNA repair by photolyases (photoreactivation). C. antarcticus could tolerate higher UV‐B doses but was sensitive to white light, whereas K. petricola showed the opposite trend. DHN melanin provided UV‐B protection in C. antarcticus, whereas the same pigment or even carotenoids proved ineffective in K. petricola. Both fungi demonstrated functional photoreactivation in agreement with the presence of photolyase‐encoding genes. Our findings reveal that although the adaptive trait of DHN melanization commonly occurs across black fungi, it is not equally functional and that there are species‐specific adaptations towards either UV‐induced lesion avoidance or repair strategies. KW - Rock-inhabiting Ascomycetes KW - Pigment KW - Photoprotection KW - Photolyase KW - Disinfection PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-616859 DO - https://doi.org/10.1111/1758-2229.70043 VL - 16 IS - 6 SP - 1 EP - 13 PB - Wiley AN - OPUS4-61685 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sathiyamani, S. A1 - Ngiam, S. A1 - Bonnerot, O. A1 - Jaengsawang, S. A1 - Panarut, P. A1 - Helman-Wazny, Agnieszka A1 - Colini, C. T1 - Material Characterisation of 19–20th Century Manuscripts from Northern Thailand N2 - Material analysis was carried out on four manuscripts from Northern Thailand, which included two palm-leaf manuscripts and two paper manuscripts. The two palm-leaf manuscripts MS 6 and MS 7 were found to have been written in the traditional method, wherein text was incised on the surface of the leaves, and then soot applied to the surfaces, confirmed by the identification of carbon ink. MS 7 additionally showed the presence of trace levels of iron in the ink, either from soot paste or from the stylus used for inscribing. The paper manuscript MS 3 was written in iron-gall ink, with sections written using a methyl-violet based ink while MS 4 was written in carbon ink. The paper used in the case of MS 3 was found to be machine made, while khoi fibres (Streblus asper) were used for making the paper used for MS 4. A combination of traditional and modern pigments, like molybdenum orange, was used for decorating the edges and cover. The results improved our understanding of these manuscripts in particular, and also provided us with insights about the rapid adoption of modern materials and their incorporation into the production of written artefacts from Northern Thailand in the late 19th and early 20th centuries. KW - Materials analysis KW - Paper manuscript KW - Palm-leaf manuscript KW - Writing inks PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-652586 DO - https://doi.org/10.1515/res-2023-0028 SN - 0034-5806 VL - 45 IS - 2-3 SP - 117 EP - 140 PB - Walter de Gruyter GmbH AN - OPUS4-65258 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian A1 - Stephan, Dietmar A1 - Meng, Birgit A1 - Simon, Sebastian A1 - von Werder, Julia A1 - Hirsch, Tamino A1 - Manninger, Tanja T1 - Effect of gypsum on the hydration of fused cement clinker from basic oxygen furnace slag N2 - Fused cement clinker can be produced from molten basic oxygen furnace slag (BOFS) by way of a reductive thermochemical treatment. During the thermochemical treatment, oxidic iron is reduced to metallic iron and separated. The resulting low-iron slag has a chemical and mineralogical composition similar to ordinary Portland cement (OPC) clinker. In this study, the hydraulic reactivity of the fused clinker from BOFS with and without gypsum was investigated using isothermal calorimetry, differential scanning calorimetry, in situ X-ray diffraction and powder X-ray diffraction. Furthermore, a synthetic fused clinker without foreign ions and fused clinker produced by a mixture of both materials was studied. The hydraulic reaction of the fused clinker from BOFS was considerably slower than that of OPC. However, the reaction can be accelerated by adding gypsum as a sulfate carrier. Furthermore, the results showed an increased reaction rate with decreasing content of foreign ions such as Fe, P or Mn. KW - General Materials Science KW - Building and Construction PY - 2024 DO - https://doi.org/10.1680/jadcr.23.00070 SN - 0951-7197 SP - 1 EP - 19 PB - Telford AN - OPUS4-59391 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hamann, Christopher A1 - Piehl, Patrick A1 - Weingart, Eric A1 - Stolle, Dirk A1 - Al-Sabbagh, Dominik A1 - Ostermann, Markus A1 - Auer, Gerhard A1 - Adam, Christian T1 - Selective removal of zinc and lead from electric arc furnace dust by chlorination–evaporation reactions N2 - Re-melting of scrap in an electric arc furnace (EAF) results in the accumulation of filter dust from off-gas treatment that predominantly consists of iron and zinc oxides. Filter dust is classified as hazardous waste due to its high contents of potentially toxic or ecotoxic elements such as Pb, Cr, Cd, and As. A promising processing route for this waste is selective chlorination, in which the non-ferrous metal oxides are chlorinated and selectively evaporated in form of their respective chlorides from the remaining solids via the process gas flow. Here, we investigate stepwise thermochemical treatment of EAF dust with either waste iron(II) chloride solution or hydrochloric acid at 650, 800, and 1100 ◦C. The Zn and Pb contents of the thermochemically processed EAF dust could be lowered from 29.9% and 1.63% to 0.09% and 0.004%, respectively. Stepwise heating allowed high separation between zinc chloride at the 650 ◦C step and sodium-, potassium-, and lead-containing chlorides at higher temperatures. Furthermore, the lab-scale results were transferred to the use of an experimental rotary kiln highlighting the possibilities of upscaling the presented process. Selective chlorination of EAF dust with liquid chlorine donors is, therefore, suggested as a potential recycling method for Zn-enriched steelworks dusts. KW - Electric arc furnace dust KW - Zinc KW - Selective Chlorination KW - Hazardous waste KW - Resource Recovery PY - 2024 DO - https://doi.org/10.1016/j.jhazmat.2023.133421 SN - 0304-3894 VL - 465 SP - 1 EP - 13 PB - Elsevier AN - OPUS4-59345 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Barkeshli, Mandana A1 - Stephan, Ina A1 - Shevchuk, Ivan A1 - Soltani, Mojtaba T1 - Characteristics of Sizing Materials Used in Persian Medieval Manuscripts: Physical, Optical, Spectral Imaging, and Fungicidal Properties N2 - In this study, we investigated the diverse range of materials used for sizing in Iranian paper manuscripts during the Timurid (fifteenth century) to Safavid (sixteenth century) and Qajar (nineteenth century) periods. Our approach combined historical analysis with scientific examination of reconstructed sizings. We reconstructed 15 sizing materials based on identified Persian historical recipes and analysed their physical, optical, and spectral characteristics. Additionally, we assessed their behaviour against the mould fungus Aspergillus flavus. The results revealed distinctive properties for each sizing material, shedding light on their potential applications in paper preservation. Furthermore, our investigation demonstrated variations in hygroscopicity, thickness, grammage, and ash content post-sizing. The sizing materials also exhibited different effects on paper reflectance properties. Additionally, our study revealed insights into the impact of sizing on burnished papers, indicating that the mechanical process of burnishing did not significantly alter the chemical composition or spectral properties of the paper, with only minor changes in brightness observed in specific cases. All tested sizing materials supported varying levels of mould growth, indicating potential implications for paper conservation. Our findings provide valuable insights into the historical practices of Iranian paper sizing and offer practical considerations for the preservation of paper manuscripts. KW - Paper sizings KW - Persian historical recipes KW - Physical and optical characteristics KW - Fungicidal property KW - Spectral imaging PY - 2024 DO - https://doi.org/10.1080/00393630.2024.2342647 VL - 69 SP - 519 EP - 536 PB - Informa UK Limited AN - OPUS4-60159 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -