TY - JOUR A1 - Richter, Matthias A1 - Horn, Wolfgang A1 - Juritsch, Elevtheria A1 - Klinge, A. A1 - Radeljic, L. A1 - Jann, Oliver T1 - Natural building materials for interior fitting and refurbishment - What about indoor emissions? N2 - Indoor air quality can be adversely affected by emissions from building materials, consequently having a negative impact on human health and well-being. In this study, more than 30 natural building materials (earth dry boards and plasters, bio-based insulation materials, and boards made of wood, flax, reed, straw, etc.) used for interior works were investigated as to their emissions of (semi-) volatile organic compounds ((S)VOC), formaldehyde, and radon. The study focused on the emissions from complete wall build-ups as they can be used for internal Partition walls and the internal insulation of external walls. Test chambers were designed, allowing the compounds to release only from the surface of the material facing indoors under testing Parameters that were chosen to simulate model room conditions. The emission test results were evaluated using the AgBB evaluation scheme, a procedure for the health-related evaluation of construction products and currently applied for the approval of specific groups of building materials in Germany. Seventeen out of 19 sample build-ups tested in this study would have passed this scheme since they generally proved to be low-emitting and although the combined emissions of multiple materials were tested, 50% of the measurements could be terminated before half of the total testing time. KW - Bio-based insulation KW - Earthen building materials KW - Volatile organic compounds KW - Semivolatile organic compounds KW - Radon PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-519634 DO - https://doi.org/10.3390/ma14010234 VL - 14 IS - 1 (Special issue: Measurement of the environmental impact of materials) SP - 234-1 EP - 234-14 PB - MDPI CY - Basel AN - OPUS4-51963 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wilke, Olaf A1 - Horn, Wolfgang A1 - Richter, Matthias A1 - Jann, Oliver T1 - Volatile organic compounds from building products - Results from six round robin tests with emission test chambers conducted between 2008 and 2018 N2 - Emission testing of volatile organic compounds (VOC) from materials and products is commonly based on emission test chamber measurements. To ensure the comparability of results from different testing laboratories, their measurement performance must be verified. For this purpose, Bundesanstalt für Materialforschung und -prüfung (BAM) organizes an international proficiency test (round robin test, RRT) every two years using well-characterized test materials (one sealant, one furniture board, and four times a lacquer) with defined VOC emissions. The materials fulfilled the requirements of homogeneity, reproducibility, and stability. Altogether, 36 VOCs were included of which 33 gave test chamber air concentrations between 13 and 83 µg/m3. This is the typical concentration range to be expected and to be quantified when performing chamber tests. Three compounds had higher concentrations between 326 and 1105 µg/m3. In this paper, the relative standard deviations (RSD) of BAM round robin tests since 2008 are compared and the improvement of the comparability of the emission chamber testing is shown by the decrease of the mean RSD down to 28 % in 2018. In contrast, the first large European interlaboratory comparison in 1999 showed a mean RSD of 51 %. KW - Construction product KW - Emission test chamber KW - Interlaboratory comparison KW - Proficiency testing KW - Rround robin test KW - VOC emission PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-526139 DO - https://doi.org/10.1111/ina.12848 VL - 31 IS - 6 SP - 2049 EP - 2057 PB - Wiley AN - OPUS4-52613 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Brandt, S. A1 - Müller, B. A1 - Brozowski, F. A1 - Plehn, W. A1 - Horn, Wolfgang T1 - Weiterentwicklung des Geruchsmessverfahrens für Bauprodukte T1 - Further development of the odour measurement method for building products N2 - Bauprodukte und Einrichtungsgegenstände für Innenräume, wie Bodenbeläge und Wandpaneele, sollen das Wohlbefinden und die Gesundheit der Raumnutzerinnen und -nutzer nicht durch das Ausdünsten von Geruchsstoffen stören. Mit der Geruchsprüfung nach ISO 16000-28 „Innenraumluft - Bestimmung der Geruchsstoffemissionen aus Bauprodukten mit einer Emissionsprüfkammer“ wird der Produktgeruch zu einer messbaren Größe. So kann z. B. die empfundene Intensität, also die Stärke eines Geruchseindruckes, mit Hilfe eines Vergleichsmaßstabes von Probandinnen und Probanden ermittelt werden. Im hier vorgestellten Projekt werden Vorschläge zur Weiterentwicklung der Methode vorgestellt, um im Ergebnis die Reproduzierbarkeit der Messergebnisse weiter zu verbessern. Dabei werden vor allem das Probenpräsentationssystem und die Bewertungsmethodik für die empfundene Intensität bei der Bewertung von Bauprodukten gemäß AgBB-Schema betrachtet, da diese einen wesentlichen Einfluss haben. N2 - Emissions or odours occurring from building products and furnishings for interiors, like floor coverings or wall panels, should not have a negative impact on well-being or health. Odours can be measured applying the standard ISO 16000-28 „Indoor air - Determination of odour emissions from building products using test chambers” It describes among other procedures the assessment of perceived intensi-ty with comparative scale by a group of panellists. In the study presented here, proposals for further technical development of the methodology are discussed to increase the reproducibility of measurement results. The sampling procedure and evaluation method of perceived intensity are investigated in particular because they have a major influence at the assessment of construction products applying the procedure of the Committee for Health Evaluation of Building Products. KW - Geruchsmessung KW - Emissionen KW - Bauprodukte KW - VOC PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527458 UR - http://www.gefahrstoffe.de SN - 0949-8036 SN - 1436-4891 VL - 81 IS - 3-4 SP - 151 EP - 155 PB - VDI Fachmedien CY - Düsseldorf AN - OPUS4-52745 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Plarre, Rüdiger A1 - Zocca, Andrea A1 - Spitzer, Andrea A1 - Benemann, Sigrid A1 - Gorbushina, Anna A1 - Li, Y. A1 - Waske, Anja A1 - Funk, Alexander A1 - Wilgig, Janka A1 - Günster, Jens T1 - Searching for biological feedstock material: 3D printing of wood particles from house borer and drywood termite frass N2 - Frass (fine powdery refuse or fragile perforated wood produced by the activity of boring insects) of larvae of the European house borer (EHB) and of drywood termites was tested as a natural and novel feedstock for 3D-printing of wood-based materials. Small particles produced by the drywood termite Incisitermes marginipennis and the EHB Hylotrupes bajulus during feeding in construction timber, were used. Frass is a powdery material of particularly consistent quality that is essentially biologically processed wood mixed with debris of wood and faeces. The filigree-like particles flow easily permitting the build-up of woodbased structures in a layer wise fashion using the Binder Jetting printing process. The Quality of powders produced by different insect species was compared along with the processing steps and properties of the printed parts. Drywood termite frass with a Hausner Ratio HR = 1.1 with ρBulk = 0.67 g/cm3 and ρTap = 0.74 g/cm3 was perfectly suited to deposition of uniformly packed layers in 3D printing. We suggest that a variety of naturally available feedstocks could be used in environmentally responsible approaches to scientific material sciences/additive manufacturing. KW - 3D printing KW - X-ray tomographic KW - SEM micrography KW - Drywood termite PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-521517 DO - https://doi.org/10.1371/journal.pone.0246511 VL - 16 IS - 2 SP - e0246511 AN - OPUS4-52151 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stock, S. C. A1 - Koester, M. A1 - Boy, J. A1 - Godoy, R. A1 - Nájera, F. A1 - Matus, F.J. A1 - Merino, C. A1 - Abdallah, Khaled A1 - Leuschner, C. A1 - Spielvogel, S. A1 - Gorbushina, Anna A1 - Kuzyakov, Y. A1 - Dippold, M. A. T1 - Plant carbon investment infine roots and arbuscular mycorrhizal fungi: Across-biome study on nutrient acquisition strategies N2 - Plant resource acquisition strategies were ecosystem-specific with distinct mutualism with arbuscular mycorrhizal (AM) fungi. Root traits indicated conservative resource economics in the arid shrubland, but an acquisitive and self-sufficient (“do-it-yourself”) acquisition strategy in the semiarid coastal matorral, resulting in large carbon (C) investments (green). Forest plants with conservative root traits seem to intensively outsource their acquisition to AM fungi, compensating for lower uptake capacities of conservative roots (red line). High allocations of freshly assimilated C into AM fungal storage compounds illustrated the relevance of AM fungi as C sink, especially in the semiarid matorral. KW - Natural ecosystems KW - Temperate rain forest KW - Arbuscular mycorrhiza KW - Plant economic spectrum KW - Root economics space KW - 13CO2 pulse labeling PY - 2021 DO - https://doi.org/10.1016/j.scitotenv.2021.146748 VL - 781 SP - 146748 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-52804 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Steckenmesser, D. A1 - Vogel, Christian A1 - Herzel, Hannes A1 - Félix, R. A1 - Adam, Christian A1 - Steffens, D. T1 - Thermal treatment of sewage sludge for phosphorus fertilizer production: a model experiment N2 - Phosphorus (P) resource availability and quality is declining and recycling P-fertilizers from waste materials are becoming increasingly important. One important secondary P resource is sewage sludge (SSL) where P is often bound as aluminum phosphate (Al-P), iron phosphate (Fe-P) and polyphosphate (poly-P), respectively. Thermal treatment in different ways is a promising way in P recycling to produce highly plant-available P-fertilizers. To investigate mechanisms behind transformation of hardly available P-species toward plant-available P forms we treated a model SSL containing different kinds of defined P sources by low-temperature conversion (LTC) at 500 °C and subsequent thermochemical treatment of the LTC product with Na additives (TCT) at 950 °C, respectively. Pot experiments with ryegrass were carried out to determine the plant availability of P of the different treatments. The poly-P (here pyrophosphates) based fertilizers had a very high plant availability after both thermal treatments. During LTC treatment the plant availability of the Fe-P and Al-P variants increased because of the Formation of Fe(II) phosphates and/or pyro-/polyphosphates. Especially the formation of Al-polyphosphate shows a high plant availability. The subsequent TCT further increased strongly the plant availability of the Fe-P variants because of the formation of highly plant-available CaNaPO4. Thus, a direct TCT without prior LTC probably also produce CaNaPO4 and is recommended for Fe-P based SSL. However, a molar Ca/P ratio of � 1 in the fertilizer is favorable for CaNaPO4 formation. Thus, the knowledge on the source of primary P in SSL is essential for choosing the accurate thermal treatment method to produce highly plant-available P-fertilizers from SSL. KW - Phosphorus KW - Sewage sludge KW - X-ray diffraction KW - X-ray absorption near-edge structure (XANES) spectroscopy KW - Fertilizer PY - 2021 DO - https://doi.org/10.1080/01904167.2021.1994595 SN - 0190-4167 VL - 45 IS - 8 SP - 1123 EP - 1133 PB - Taylor & Francis Online AN - OPUS4-53755 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gerrits, Ruben A1 - Wirth, R. A1 - Schreiber, A. A1 - Feldmann, Ines A1 - Knabe, Nicole A1 - Schott, J, A1 - Benning, L.G. A1 - Gorbushina, Anna T1 - High-resolution imaging of fungal biofilm-induced olivine weathering N2 - Many microorganisms including free-living and symbiotic fungi weather minerals through the formation of biofilms on their surface. Weathering thus proceeds not only according to the mineral’s chemistry and the environmental conditions but also according to the local biofilm chemistry. These processes can be dissected in experiments with defined environmental settings and by employing genetic tools to modify traits of the fungal biofilm. Biofilms of the rock-inhabiting fungus Knufia petricola strain A95 (wild-type, WT) and its melanin-deficient mutant (ΔKppks) were grown on polished olivine sections in subaerial (air-exposed) and subaquatic (submerged) conditions. After seven months of interaction at pH 6 and 25°C, the fungus-mineral interface and abiotic olivine surface were compared using high resolution transmission electron microscopy (HRTEM). The abiotic, subaquatic olivine section showed a 25 nm thick, continuous amorphous layer, enriched in Fe and depleted in Si compared to the underlying crystalline olivine. This amorphous layer formed either through a coupled interfacial dissolution reprecipitation mechanism or through the adsorption of silicic acid on precipitated ferric hydroxides. Its thickness was likely enhanced by mechanical stresses of polishing. Directly underneath a fungal biofilm (WT and mutant alike), the surface remained mostly crystalline and was strongly etched and weathered, indicating enhanced olivine dissolution. The correlation between enhanced olivine dissolution and the absence of a continuous amorphous layer is a strong indication of the dissolution-inhibiting qualities of the latter. We propose that the fungal biofilm sequesters significant amounts of Fe, preventing formation of the amorphous layer and driving olivine dissolution onwards. The seemingly similar olivine surface underneath both WT and mutant biofilms illustrates the comparably insignificant role of specific biofilm traits in the weathering of olivine once biofilm attachment is imposed. Under subaerial conditions, the absence of water on the abiotic surface prohibited olivine dissolution. This was overcome by the water retention capacities of both the WT and mutant biofilm: the olivine surface underneath subaerial fungal biofilms was as weathered as the corresponding subaquatic olivine surface. Under the studied environmental settings, the effect of fungal biofilms on olivine weathering seems to be universal, independent of the production of melanin, the composition of extracellular polymeric substances (EPS) or air-exposure. KW - Bio-weathering KW - Forsterite KW - Extracellular polymeric substances KW - Melanin KW - Black fungi PY - 2021 DO - https://doi.org/10.1016/j.chemgeo.2020.119902 VL - 559 SP - 119902 PB - Elsevier B.V. AN - OPUS4-51403 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hamann, Christopher A1 - Spanka, M. A1 - Stolle, Dirk A1 - Auer, G. A1 - Weingart, Eric A1 - Al-Sabbagh, Dominik A1 - Ostermann, Markus A1 - Adam, Christian T1 - Recycling of blast-furnace sludge by thermochemical treatment with spent iron(II) chloride solution from steel pickling N2 - One of the typical wastes produced in blast-furnace (BF) ironmaking is BF sludge, which mostly consists of carbon and iron oxides, but also contains toxic trace metals such as Zn, Pb, Cd, As, and Hg that render the material hazardous. Due to the lack of an established recycling process, BF sludges are landfilled, which is ecologically questionable and costly. Here, we investigate selective removal of Zn, Pb, and Cd from BF sludge by chlorination–evaporation reactions using thermodynamic modelling and laboratory-scale experiments. Specifically, BF sludge was thermochemically treated at 650–1000 °C with a spent iron(II) chloride solution from steel pickling and the effects of process temperature and retention time on removal of Zn, Pb, and Cd were investigated. Zinc and Pb were quantitatively removed from BF sludge thermochemically treated at 900–1000 °C, whereas Fe and C as well as other major elements were mostly retained. The Zn, Pb, and Cd contents in the thermochemically treated BF sludge could be lowered from ∼56 g/kg, ∼4 g/kg, and ∼0.02 g/kg to ≤0.7 g/kg, ≤0.02 g/kg, and ≤0.008 g/kg, respectively, thus rendering the processed mineral residue a non-hazardous raw material that may be re-utilized in the blast furnace or on the sinter band. KW - Blast-furnace sludge KW - Selective chlorination KW - Zinc chloride PY - 2021 DO - https://doi.org/https://doi.org/10.1016/j.jhazmat.2020.123511 SN - 0304-3894 VL - 402 IS - 123511 SP - 1 EP - 12 PB - Elsevier CY - Amsterdam AN - OPUS4-51141 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gentzmann, Marie A1 - Schraut, Katharina A1 - Vogel, Christian A1 - Gäbler, H.-E. A1 - Huthwelker, T. A1 - Adam, Christian T1 - Investigation of scandium in bauxite residues of different origin N2 - This paper focuses on the scandium speciation in bauxite residues of different origin. Insights into mineralchemical similarities and differences of these materials will be presented and links to their natural geological background discussed. The presented research should provide fundamental knowledge for the future development of efficient and viable technologies for Sc-recovery from bauxite residues derived from different bauxites and accumulating at different localities. In total, five bauxite residues were investigated which originated from Greece, Germany, Hungary and Russia (North Ural & North Timan) using a combination of different analytical tools. Those included: laser ablation inductively coupled plasma mass spectrometry, X-ray absorption near Edge structure (XANES) spectroscopy, μ-Raman spectroscopy as well as scanning electron microscopy and electron microprobe analyses. X-ray fluorescence and inductively coupled plasma mass spectrometry were used to determine the overall chemical composition. The investigated samples were found to exhibit a relatively homogenous distribution of Sc between the larger mineral particles and the fine-grained matrix except for Al-phases like diaspore, boehmite and gibbsite. These phases were found to be particularly low in Sc. The only sample where Sc mass fractions in Al-phases exceeded 50 mg/kg was the Russian sample from North Ural. Fe-phases such as goethite, hematite and chamosite (for Russian samples) were more enriched in Sc than the Al-phases. In fact, in Greek samples goethite showed a higher capacity to incorporate or adsorb Sc than hematite. Accessory minerals like zircon, rutile/anatase and ilmenite were found to incorporate higher mass fractions of Sc (>150 mg/kg), however, those minerals are only present in small amounts and do not represent major host phases for Sc. In Russian samples from North Ural an additional Ca–Mg rich phase was found to contain significant mass fractions of Sc (>500 mg/kg). μ-XANES spectroscopy was able to show that Sc in bauxite residue occurs adsorbed onto mineral surfaces as well as incorporated into the crystal lattice of certain Fe-phases. According to our observations the bauxite type, i.e. karstic or lateritic, the atmospheric conditions during bauxitization, i.e. oxidizing or reducing, and consequently the dominant Sc-bearing species in the primary Bauxite influence the occurrence of Sc in bauxite residues. In karstic bauxites, underlying carbonate rocks can work as a pH-barrier and stabilize Sc. This prevents the Sc from being mobilized and removed during bauxitization. Hence, karstic bauxites are more prone to show a Sc enrichment than lateritic bauxites. Reducing conditions during bauxitization support the incorporation of Sc into clay minerals such as chamosite, which can dissolve and reprecipitate during Bayer processing causing Sc to be redistributed and primarily adsorb onto mineral surfaces in the bauxite residue. Oxidizing conditions support the incorporation of Sc into the crystal lattice of Fe-oxides and hydroxides, which are not affected in the Bayer process. The genetic history of the bauxite is therefore the major influential factor for the Sc occurrence in bauxite residues. KW - Sc recovery KW - Scandium KW - Bauxite Residue KW - Red Mud KW - XANES PY - 2021 DO - https://doi.org/10.1016/j.apgeochem.2021.104898 SN - 0883-2927 VL - 126 SP - 104898 PB - Elsevier Ltd. AN - OPUS4-52123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schraut, Katharina A1 - Adamczyk, Burkart A1 - Adam, Christian A1 - Stephan, D. A1 - Meng, Birgit A1 - Simon, Sebastian A1 - von Werder, Julia T1 - Synthesis and characterisation of alites from reduced basic oxygen furnace slags N2 - Basic oxygen furnace slags (BOFS) are by-products of the steelmaking process. Several researchers have studied the production of Portland cement clinker and metallic iron from BOFS via a reductive treatment. In this study, we applied a carbothermal reduction of BOFS in a technical-scale electric arc furnace and characterised the clinker-like products. Those clinker-like non-metallic products (NMPs) had a chemical and mineralogical composition comparable to clinker for ordinary Portland cement (OPC) and contained large elongated alite crystals as major component. The pure NMPs reacted more slowly and achieved a lower degree of hydration compared with commercial OPC. If the reactivity of the products can be further increased by employing specific adaptations, it can be used as a full clinker substitute for OPC. Nevertheless, it is also an option to use the material without further modifications as a cement component or concrete addition, which contributes to the strength development in both cases. KW - BOFS KW - Hydration products KW - Thermal analysis KW - X-ray diffraction PY - 2021 DO - https://doi.org/10.1016/j.cemconres.2021.106518 SN - 0008-8846 VL - 147 SP - 6518 PB - Elsevier Ltd. AN - OPUS4-52939 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vogel, Christian A1 - Helfenstein, J. A1 - Massey, M. A1 - Sekine, R. A1 - Kretzschmar, R. A1 - Beiping, L. A1 - Peter, T. A1 - Chadwick, O. A1 - Tamburini, F. A1 - Rivard, C. A1 - Herzel, Hannes A1 - Adam, Christian A1 - Pradas del Real, A. A1 - Castillo-Michel, H. A1 - Zuin, L. A1 - Wang, D. A1 - Félix, R. A1 - Lassalle-Kaiser, B. A1 - Frossard, E. T1 - Microspectroscopy reveals dust-derived apatite grains in acidic, highly-weathered Hawaiian soils N2 - Dust deposition is an important source of phosphorus (P) to many ecosystems. However, there is little evidence of dust-derived P-containing minerals in soils. Here we studied P forms along a well-described climatic Gradient on Hawaii, which is also a dust deposition gradient. Soil mineralogy and soil P forms from six sites along the climatic gradient were analyzed with bulk (X-ray diffraction and P K-edge X-ray absorption near edge structure) and microscale (X-ray fluorescence, P K-edge X-ray absorption near edge structure, and Raman) analysis methods. In the wettest soils, apatite grains ranging from 5 to 30 μm in size were co-located at the micro-scale with quartz, a known continental dust indicator suggesting recent atmospheric deposition. In addition to co-location with quartz, further evidence of dust-derived P included backward trajectory modeling indicating that dust particles could be brought to Hawaii from the major global dust-loading areas in central Asia and northern Africa. Although it is not certain whether the individual observed apatite grains were derived from long-distance transport of dust, or from local dust sources such as volcanic ash or windblown fertilizer, these observations offer direct evidence that P-containing minerals have reached surface layers of highly-weathered grassland soils through atmospheric deposition. KW - Phosphorus KW - soil KW - microspectroscopy KW - Raman spectroscopy KW - XANES spectroscopy KW - x-ray diffraction PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-511522 DO - https://doi.org/10.1016/j.geoderma.2020.114681 SN - 0166-0918 SN - 1872-6259 VL - 381 SP - 114681-1 EP - 114681-11 PB - Elsevier CY - Amsterdam AN - OPUS4-51152 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Herzel, Hannes A1 - Stemann, J. A1 - Simon, Sebastian A1 - Adam, Christian T1 - Comparison of thermochemical treatment of sewage sludge ash with sodium sulphate in laboratory-scale and pilot-scale experiments N2 - There is an ongoing debate on European scale concerning the criticality of phosphorus. In Switzerland and Germany, phosphorus recovery from phosphorus-rich waste streams will become obligatory. Sewage sludge ash is rich in phosphorus and may become an important secondary feedstock. Thermochemical treatment of sewage sludge ash with sodium sulphate under reducing conditions was shown to remove heavy metals from the solid product and produce the fully plant available crystalline phase CaNaPO4. Pilot-scale experiments in a rotary kiln were carried out at temperatures between 750 and 1000 °C and were compared to laboratory-scale experiments with crucibles. Process upscaling was successfully demonstrated but a series of differences were noticed: In comparison to laboratory-scale, solubility of phosphorus in samples from pilot-scale experiments was lower at all chosen treatment temperatures because of shorter retention time and incomplete decomposition of sodium sulphate. X-ray diffraction analysis revealed remaining phase fractions of whitlockite (Ca3-x(Mg,Fe)x(PO4)2) and sodium sulphate from the starting materials in products and thus indicated incomplete reaction. In contrast to the results of laboratory-scale experiments, the crystalline phase CaNaPO4 was clearly absent in the products from the rotary kiln but instead a Mg-bearing phase (Ca,Mg)NaPO4 was formed. Laboratory-scale experiments confirmed (Ca,Mg)NaPO4 is an intermediate phase between whitlockite and CaNaPO4. However, both crystalline phases are characterized by high plant availability. It was shown that heavy metal removal increased at higher temperatures whereas solubility and thus plant availability of phosphorus already reached its maxima at temperatures of 950 °C in pilot-scale and 875 °C in laboratory-scale experiments. KW - Crystalline phase identification KW - Heavy metal removal KW - Phosphorus availability KW - Process upscaling KW - Recovery KW - Rhenanite PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-524084 DO - https://doi.org/10.1007/s13762-021-03252-y VL - 19 IS - 3 SP - 1997 EP - 2006 PB - Springer AN - OPUS4-52408 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Weimann, Karin A1 - Adam, Christian A1 - Buchert, M. A1 - Sutter, J. T1 - Environmental Evaluation of Gypsum Plasterboard Recycling N2 - Gypsum is widely used in the construction sector and its worldwide consumption has been increasing for several decades. Depending on the life-time of the used gypsum products, an increase of gypsum in construction and demolition waste follows. Especially against the background of a circular economy, the recycling of waste gypsum is of growing importance. However, the use of recycled gypsum makes only sense if it is environmentally friendly. Therefore, an evaluation of the environmental impacts of an industrial-scale processing for the recycling of post-consumer gypsum waste was conducted. The evaluation was performed with an established life cycle assessment software. Original data provided by industry and complementary data from a database for life cycle assessments were used for the calculations. Two scenarios for recycled gypsum with different transportation distances were calculated. These results are compared with results of the environmental evaluation of gypsum derived from coal-fired power plants (FGD gypsum) and natural gypsum. The results show that utilization of recycled gypsum can be environmentally advantageous compared to the use of natural gypsum or FGD gypsum, especially in the impact categories land transformation and resource consumption (abiotic depletion potential). For most environmental impact categories the specific transportation distances have a strong influence. KW - Gypsum plasterboards KW - Gypsum waste KW - Recycled gypsum KW - Environmental evaluation PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522321 DO - https://doi.org/10.3390/min11020101 SN - 2075-163X VL - 11 IS - 2 SP - 101 PB - MDPI CY - Basel, Schweiz AN - OPUS4-52232 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Cunliffe, A. J. A1 - Askew, P. D. A1 - Stephan, Ina A1 - Iredale, G. A1 - Cosemans, P. A1 - Simmons, L. M. A1 - Verran, J. A1 - Redfern, J. T1 - How do we determine the efficacy of an antibacterial surface? A review of standardised antibacterial material testing methods N2 - Materials that confer antimicrobial activity, be that by innate property, leaching of biocides or design features (e.g., non-adhesive materials) continue to gain popularity to combat the increasing and varied threats from microorganisms, e.g., replacing inert surfaces in hospitals with copper. To understand how efficacious these materials are at controlling microorganisms, data is usually collected via a standardised test method. However, standardised test methods vary, and often the characteristics and methodological choices can make it difficult to infer that any perceived antimicrobial activity demonstrated in the laboratory can be confidently assumed to an end-use setting. This review provides a critical analysis of standardised methodology used in academia and industry, and demonstrates how many key methodological choices (e.g., temperature, humidity/moisture, airflow, surface topography) may impact efficacy assessment, highlighting the need to carefully consider intended antimicrobial end-use of any product. KW - Antimicrobial materials KW - Antimicrobial testing KW - ISO 22196 KW - Antimicrobial surfaces KW - Antibacterial coatings PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-532138 DO - https://doi.org/10.3390/antibiotics10091069 SN - 2079-6382 VL - 10 IS - 9 SP - 1 EP - 14 PB - MDPI CY - Basel AN - OPUS4-53213 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Herzel, Hannes A1 - Aydin, Zeynep A1 - Adam, Christian T1 - Crystalline phase analysis and phosphorus availability after thermochemical treatment of sewage sludge ash with sodium and potassium sulfates for fertilizer production N2 - Phosphorus rich sewage sludge ash is a promising source to produce phosphorus recycling fertilizer. However, the low plant availability of phosphorus in these ashes makes a treatment necessary. A thermochemical treatment (800–1000 °C) with alkali additives transforms poorly plant available phosphorus phases to highly plant available calcium alkali Phosphates (Ca,Mg)(Na,K)PO4. In this study, we investigate the use of K2SO4 as additive to produce a phosphorus potassium fertilizer in laboratory-scale experiments (crucible). Pure K2SO4 is not suitable as high reaction temperatures are required due to the high melting point of K2SO4. To overcome this barrier, we carried out series of experiments with mixtures of K2SO4 and Na2SO4 resulting in a lower economically feasible reaction temperature (900–1000 °C). In this way, the produced phosphorus potassium fertilizers (8.4 wt.% K, 7.6 wt.% P) was highly plant available for phosphorus indicated by complete extractable phosphorus in neutral ammonium citrate solution. The added potassium is, in contrast to sodium, preferably incorporated into silicates instead of phosphorus phases. Thus, the highly extractable phase (Ca,Mg)(Na,K)PO4 in the thermochemical products contain less potassium than expected. This preferred incorporation is confirmed by a pilot-scale trial (rotary kiln) and thermodynamic calculation. KW - Phosphorus recovery KW - Recycling fertilizer KW - Calcium alkali phosphate KW - Silicate PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-536276 DO - https://doi.org/10.1007/s10163-021-01288-3 SN - 1611-8227 IS - 23 SP - 2242 EP - 2254 PB - Springer AN - OPUS4-53627 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schraut, Katharina A1 - Kargl, F. A1 - Adam, Christian A1 - Ivashko, O. T1 - In situ synchrotron XRD measurements during solidification of a melt in the CaO–SiO2 system using an aerodynamic levitation system N2 - Phase formation and evolution was investigated in the CaO–SiO2 system in the range of 70–80 mol% CaO. The samples were container-less processed in an aerodynamic levitation system and crystallization was followed in situ by synchrotron x-ray diffraction at the beamline P21.1 at the German electron synchrotron (DESY). Modification changes of di- and tricalcium silicate were observed and occurred at lower temperatures than under equilibrium conditions. Despite deep sample undercooling, no metastable phase formation was observed within the measurement timescale of 1 s. For the given cooling rates ranging from 300 K s−1 to about 1 K s−1, no decomposition of tricalcium silicate was observed. No differences in phase evolution were observed between reducing and oxidizing conditions imposed by the levitation gas (Ar and Ar + O2). We demonstrate that this setup has great potential to follow crystallization in refractory oxide liquids in situ. For sub-second primary phase formation faster detection and for polymorph detection adjustments in resolution have to be implemented. KW - Aerodynamic levitation KW - Calcium silicate KW - Phase formation KW - Oxide melts KW - In situ synchrotron x-ray diffraction PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-526952 DO - https://doi.org/10.1088/1361-648X/abf7e1 VL - 33 IS - 26 SP - 264003 (12pp) PB - IOP Publishing AN - OPUS4-52695 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Keshmiri, Hamid A1 - Armin, F. A1 - Elsayad, K. A1 - Schreiber, Frank A1 - Moreno, M. T1 - Leaky and waveguide modes in biperiodic holograms N2 - This study details a theoretical analysis of leaky and waveguide modes in biperiodic all-dielectric holograms. By tuning diffraction orders and subsequently confining local density of optical states at two distinct resonance wavelengths, we present a new class of highly sensitive refractive index biosensing platforms that are capable of resolving 35.5 to 41.3 nm/RIU of spectral shift for two separate biological analytes. KW - Antimicrobial resistance KW - Bacteria KW - Photonics KW - Diffractive gratings PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-527632 DO - https://doi.org/10.1038/s41598-021-89971-1 SN - 2045-2322 (online) VL - 11 IS - 1 SP - 10991 PB - Springer Nature AN - OPUS4-52763 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nordholt, Niclas A1 - Kanaris, Orestis A1 - Schmidt, Selina A1 - Schreiber, Frank T1 - Persistence against benzalkonium chloride promotes rapid evolution of tolerance during periodic disinfection N2 - Biocides used as disinfectants are important to prevent the transmission of pathogens, especially during the current antibiotic resistance crisis. This crisis is exacerbated by phenotypically tolerant persister subpopulations that can survive transient antibiotic Treatment and facilitate resistance evolution. Here, we show that E. coli displays persistence against a widely used disinfectant, benzalkonium chloride (BAC). Periodic, persister-mediated failure of disinfection rapidly selects for BAC tolerance, which is associated with reduced cell Surface charge and mutations in the lpxM locus, encoding an enzyme for lipid A biosynthesis. Moreover, the fitness cost incurred by BAC tolerance turns into a fitness benefit in the presence of antibiotics, suggesting a selective advantage of BAC-tolerant mutants in antibiotic environments. Our findings highlight the links between persistence to disinfectants and resistance evolution to antimicrobials. KW - Persistence KW - Biocides KW - Evolution KW - Cross-resistance KW - Biocide tolerance KW - Disinfection PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-538532 DO - https://doi.org/10.1038/s41467-021-27019-8 SN - 2041-1723 VL - 12 IS - 1 SP - 6792 PB - Springer AN - OPUS4-53853 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Valentin, J. A1 - Straub, H. A1 - Pietsch, Franziska A1 - Lemare, M. A1 - Ahrens, C. A1 - Schreiber, Frank A1 - Webb, J. A1 - van der Mei, H. A1 - Ren, Q. T1 - Role of the flagellar hook in the structural development and antibiotic tolerance of Pseudomonas aeruginosa biofilms N2 - Pseudomonas aeruginosa biofilms exhibit an intrinsic resistance to antibiotics and constitute a considerable clinical threat. In cystic fibrosis, a common feature of biofilms formed by P. aeruginosa in the airway is the occurrence of mutants deficient in flagellar motility. This study investigates the impact of flagellum deletion on the structure and antibiotic tolerance of P. aeruginosa biofilms, and highlights a role for the flagellum in adaptation and cell survival during biofilm development. Mutations in the flagellar hook protein FlgE influence greatly P. aeruginosa biofilm structuring and antibiotic tolerance. Phenotypic analysis of the flgE knockout mutant compared to the wild type (WT) reveal increased fitness under planktonic conditions, reduced initial adhesion but enhanced formation of microcolony aggregates in a microfluidic environment, and decreased expression of genes involved in exopolysaccharide formation. Biofilm cells of the flgE knock-out mutant display enhanced tolerance towards multiple antibiotics, whereas its planktonic cells show similar resistance to the WT. Confocal microscopy of biofilms demonstrates that gentamicin does not affect the viability of cells located in the inner part of the flgE knock-out mutant biofilms due to reduced penetration. These findings suggest that deficiency in flagellar proteins like FlgE in biofilms and in cystic fibrosis infections represent phenotypic and evolutionary adaptations that alter the structure of P. aeruginosa biofilms conferring increased antibiotic tolerance. KW - Antimicrobial resistance KW - Bacteria KW - Biofilms KW - Biocides PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-541113 DO - https://doi.org/10.1038/s41396-021-01157-9 SN - 1751-7370 VL - 16 IS - 4 SP - 1176 EP - 1186 PB - Springer Nature AN - OPUS4-54111 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Franziska, Pietsch A1 - Nordholt, Niclas A1 - Heidrich, Gabriele A1 - Schreiber, Frank T1 - Prevalent Synergy and Antagonism Among Antibiotics and Biocides in Pseudomonas aeruginosa N2 - Antimicrobials can exert specific physiological effects when used in combination that are different from those when applied alone. While combination effects have been extensively mapped for antibiotic-antibiotic combinations, the combination effects of antibiotics with antimicrobials used as biocides or antiseptics have not been systematically investigated. Here, we investigated the effects of combinations of antibiotics (meropenem, gentamicin, and ciprofloxacin) and substances used as biocides or antiseptics [octenidine, benzalkonium chloride, cetrimonium bromide, chlorhexidine, Povidone-iodine, silver nitrate (AgNO3), and Ag-nanoparticles] on the planktonic growth rate of Pseudomonas aeruginosa. Combination effects were investigated in growth experiments in microtiter plates at different concentrations and the Bliss interaction scores were calculated. Among the 21 screened combinations, we find prevalent combination effects with synergy occurring six times and antagonism occurring 10 times. The effects are specific to the antibiotic-biocide combination with meropenem showing a tendency for antagonism with biocides (6 of 7), while gentamicin has a tendency for synergy (5 of 7). In conclusion, antibiotics and biocides or antiseptics exert physiological combination effects on the pathogen P. aeruginosa. These effects have consequences for the efficacy of both types of substances and potentially for the selection of antimicrobial resistant strains in clinical applications with combined exposure (e.g., wound care and coated biomaterials). KW - Synergy KW - Antagonism KW - Suppression KW - Biocides KW - Antibiotics KW - Pseudomonas aeruginosa PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520845 DO - https://doi.org/10.3389/fmicb.2020.615618 VL - 11 SP - Article 615618 PB - Frontiers CY - Lausanne AN - OPUS4-52084 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Li, M. A1 - Schlaich, C. A1 - Zhang, J. A1 - Donskyi, Ievgen A1 - Schwibbert, Karin A1 - Schreiber, Frank A1 - Xia, Y. A1 - Radnik, Jörg A1 - Schwerdtle, T. A1 - Haag, R. T1 - Mussel-inspired multifunctional coating for bacterial infection prevention and osteogenic induction N2 - Bacterial infection and osteogenic integration are the two main problems that cause severe complications after surgeries. In this study, the antibacterial and osteogenic properties were simultaneously introduced in biomaterials, where copper nanoparticles (CuNPs) were generated by in situ reductions of Cu ions into a mussel-inspired hyperbranched polyglycerol (MI-hPG) coating via a simple dip-coating method. This hyperbranched polyglycerol with 10 % catechol groups’ modification presents excellent antifouling property, which could effectively reduce bacteria adhesion on the surface. In this work, polycaprolactone (PCL) electrospun fiber membrane was selected as the substrate, which is commonly used in biomedical implants in bone regeneration and cardiovascular stents because of its good biocompatibility and easy post-modification. The as-fabricated CuNPs-incorporated PCL membrane [PCL-(MI-hPG)-CuNPs] was confirmed with effective antibacterial performance via in vitro antibacterial tests against Staphylococcus aureus (S. aureus), Escherichia coli (E. coli), and multi-resistant E. coli. In addition, the in vitro results demonstrated that osteogenic property of PCL-(MI-hPG)-CuNPs was realized by upregulating the osteoblast-related gene expressions and protein activity. This study shows that antibacterial and osteogenic properties can be balanced in a surface coating by introducing CuNPs. KW - Mussel-inspired coating KW - CuNPs KW - Multi-resistant bacteria KW - Antibacterial KW - Antifouling KW - Osteogenesis PY - 2021 DO - https://doi.org/10.1016/j.jmst.2020.08.011 SN - 1005-0302 VL - 68 SP - 160 EP - 171 PB - Elsevier Ltd. AN - OPUS4-51519 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -