TY - CONF A1 - Ulbricht, Alexander T1 - Do Microbes like Additively Manufactured Aluminium? N2 - The use of laser-additively manufactured metallic components in the industrial sector is gaining traction, with the process now entering its application phase. Consequently, the materials are exposed to corrosive microbes, which this study examines in order to determine the implications of this exposure. Specifically, the study examines the exposure of laser powder bed fused AlSi10Mg (PBF-LB/AlSi10Mg) components to sulphate-reducing bacteria in an anaerobic environment. Is the specific PBF-LB microstructure a potential factor in determining or aiding biocorrosion? A prismatic specimen was exposed to sulphate-reducing bacteria (SRB) for two weeks. The sample was scanned by X-ray computed tomography (XCT) before and after SRB exposure. The two data sets were registered to each other (using the internal void distribution as markers, due to the corrosion of the specimen’s surface) to enable the evaluation of the corrosion damage. Virtual cuts of the 3D XCT reconstructions show a loss of volume and localised damage. The damage distribution aligns with the hatching pattern of laser exposure from laser powder bed fusion. T2 - Konferenz iCT 2026 CY - Linz, Austria DA - 10.02.2026 KW - Computed tomography KW - Biokorrosion KW - Additive manufacturing KW - PBF-LB KW - Laser powder bed fusion KW - Sulphate-reducing bacteria PY - 2026 AN - OPUS4-65570 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulbricht, Alexander T1 - Do Microbes like Additively Manufactured Aluminium? First Details of a Corrosion Test using Sulphate-Reducing Bacteria N2 - Additively manufactured metals become relevant for industrial application. Although many studies on wet corrosion of these metals have been conducted, to the authors knowledge no study seems to contain microbiological corrosion (MIC). In the presented study an experiment was conducted on PBF-LB/AlSi10Mg to test this material's susceptibility for MIC. The tested specimen were analysed using Computed Tomography before and after the MIC experiment to enable a detailed characterisation the damage on the specimens' global and local level. A global reduction of material was observed. In addition, localised damage along process inherent features of the materials microstructure was observed. T2 - Beiratssitzung TF Umwelt CY - Berlin, Germany DA - 17.03.2025 KW - Computed Tomography KW - Additive Manufacturing KW - Biocorrosion KW - Sulphate-reducing Bacteria KW - Microbially influenced corrosion PY - 2025 AN - OPUS4-62772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -