TY - CONF A1 - Taghavi Kalajahi, Sara T1 - The effectiveness of cathodic protection (CP) on microbiologically influenced corrosion (MIC) control N2 - Cathodic protection (CP) is an electrochemical method, to manage corrosion in different industries, especially in buried and sub-merged environments. In those environments microorganisms are present and can affect the corrosion process and cause microbiologically influenced corrosion (MIC). Most of the industry standards recommend performing CP using -800 mV (Ag/AgCl), however, if microorganisms capable of initiating MIC are present, for instance sulfate reducing bacteria (SRB), it is recommended to use even more negative potentials. It is assumed that this will provide adequate protection of the metal. Currently there is no information or valid data in the context of CP, on the level of MIC threat and the extent to which more negative potentials can be used to provide adequate protection and not over-protection (due to hydrogen embrittlement threat). Conflicting statements can be found in the literature regarding the effectiveness of CP on MIC, from reducing biofilm attachment to increasing bacterial activity and biofilm attachment. Recently, the development and lower price of molecular microbiological methods (MMM) have opened the door for more effective studies of MIC mechanisms along with other electrochemical methods and surface analysis. In this work, the genetic functionality of biofilms formed in the laboratory under CP conditions is investigated using transcriptomics. Gene expression of SRB biofilms under different CP potentials (-800, -850 and -900 mV) will be studied; comparison with control will allow us to distinguish the specific genes that are differentially expressed, leading to a better understanding of the mechanism of CP to affect bacterial activity and diversity. Keywords - cathodic protection, microbiologically influenced corrosion, molecular microbial methods. T2 - IBBS CY - Berlin, Germany DA - 09.09.2024 KW - Microbiologically influenced corrosion PY - 2024 AN - OPUS4-61981 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Mezera, Marek T1 - Bacterial adhesion on femtosecond laser-induced periodic surface structures N2 - Biofilm formation in industrial or medical settings is usually unwanted and leads to serious health problems and high costs. Inhibition of initial bacterial adhesion prevents biofilm formation and is, therefore, a major mechanism of antimicrobial action of surfaces. Surface topography largely influences the interaction between bacteria and surfaces which makes topography an ideal base for antifouling strategies and eco-friendly alternatives to chemical surface modifications. Femtosecond laser-processing was used to fabricate sub-micrometric surface structures on silicon and stainless steel for the development of antifouling topographies on technical materials. T2 - Future Tech Week 2020 CY - Online meeting DA - 21.09.2020 KW - Laser-induced periodic surface structures (LIPSS) KW - Bacterial adhesion KW - Biofilm growth KW - Structural color KW - Femtosecond laser processing PY - 2020 UR - http://futuretechweek.fetfx.eu/wp-content/uploads/gravity_forms/2-5432af7ecff9e0243d7383ab3f931ed3/2020/09/BioCombs4Nanofibers_Poster-for-Future_Tech_Week_2020_08-09-2020_with_Reprint-permission_for_upload.pdf AN - OPUS4-51233 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Richter, Anja T1 - Bacterial adhesion on ultrashort laser processed surfaces N2 - Bacterial biofilms are multicellular communities adhering to surfaces and embedded in a self-produced extracellular matrix. Due to physiological adaptations and the protective biofilm matrix itself, biofilm cells show enhanced resistance towards antimicrobial treatment. In medical and industrial settings, biofilms on e.g. for implants or for surfaces in food-processing industry can be a fertile source of bacterial pathogens and are repeatedly associated with persisting, nosocomial and foodborne infections. As extensive usage of antibiotics and biocides can lead to the emergence of resistances, various strategies are currently developed, tested and improved to realize anti-bacterial surface properties through surface functionalization steps avoiding antibiotics. In this study, contact-less and aseptic large-area ultrashort laser scan processing is employed to generate different surface structures in the nanometer- to micrometer-scale on technical materials, i.e. titanium-alloy, steel, and polymer. The processed surfaces were characterized by optical and scanning electron microscopy and subjected to bacterial colonization studies with Escherichia coli test strains. For each material, biofilm results of the fs-laser treated surfaces are compared to that obtained on polished (non-irradiated) surfaces as a reference. Depending on the investigated surfaces, different bacterial adhesion patterns were found, suggesting an influence of geometrical size, shape and cell appendages of the bacteria and – above all – the laser-processed nanostructure of the surface itself. T2 - European Materials Research Society Spring Meeting 2021 CY - Online Meeting DA - 31.05.2021 KW - Bacterial adhesion KW - Biofilm formation KW - Ultrashort laser processing KW - Laser-induced periodic surface structures (LIPSS) PY - 2021 UR - https://www.european-mrs.com/laser-material-processing-fundamental-interactions-innovative-applications-emrs AN - OPUS4-52765 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Razkin Bartolomé, Malen T1 - Bacterial adhesion on fs-laser processed laser-induced periodic surface structures N2 - Bacteria are ubiquitous and colonize all types of surfaces, including those in close proximity to humans, such as skin, food, and everyday objects. This raises the question of whether their presence represents a problem to be mitigated or a potential source of benefit to be harnessed, thereby stimulating scientific inquiry into the role of surface-associated bacteria in diverse domains ranging fromhuman health to industrial biotechnology. Aim: The objective of this project is to explore the impact of modifying surface topography on bacterial adhesion behavior. By manipulating the physical characteristics of the substrate, the attachment and detachment dynamics of bacteria can potentially be modified, leading to novel strategies for controlling bacterial colonization in various applications, such as medical devices. Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus) were tested on LIPSS-covered Fused Silica samples. T2 - 2023 Spring Meeting · , 2023 · Strasbourg CY - Strasbourg, France DA - 29.05.2023 KW - LIPSS KW - Biofilm KW - fs-laser processing PY - 2023 AN - OPUS4-58456 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bonse, Jörn T1 - Impact of laser-induced periodic surface structures on the bactericidal properties of copper and brass N2 - Surfaces of metallic copper and copper alloys effectively inactivate microorganisms and viruses. However, the exact inactivation mode is still under debate. Main factors are assumed to include direct contact with the metallic surface, influx of Cu(I)/Cu(II) ions and the generation of reactive oxygen species (ROS). Laser-induced periodic surface structures (LIPSS) are frequently reported to act antibacterial, mainly by prevention of bacterial adhesion due to a limited number of possible adhesion points or by increasing the overall surface of intrinsically antibacterial materials. In time-kill experiments with E. coli and S. aureus we analyzed the impact of LIPSS on the toxicity of metallic copper and brass. We also conducted ROS accumulation assays and conclude that the application of LIPSS is not generally straight forward to obtain or improve antibacterial surfaces. Thus, the antibacterial effects of LIPPS. T2 - 2023 Spring Meeting CY - Strasbourg, France DA - 29.05.2023 KW - LIPSS KW - Antimicrobial KW - Reactive oxygen species PY - 2023 AN - OPUS4-58465 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Ulbricht, Alexander T1 - Do Microbes like Additively Manufactured Aluminium? First Details of a Corrosion Test using Sulphate-Reducing Bacteria N2 - Additively manufactured metals become relevant for industrial application. Although many studies on wet corrosion of these metals have been conducted, to the authors knowledge no study seems to contain microbiological corrosion (MIC). In the presented study an experiment was conducted on PBF-LB/AlSi10Mg to test this material's susceptibility for MIC. The tested specimen were analysed using Computed Tomography before and after the MIC experiment to enable a detailed characterisation the damage on the specimens' global and local level. A global reduction of material was observed. In addition, localised damage along process inherent features of the materials microstructure was observed. T2 - Beiratssitzung TF Umwelt CY - Berlin, Germany DA - 17.03.2025 KW - Computed Tomography KW - Additive Manufacturing KW - Biocorrosion KW - Sulphate-reducing Bacteria KW - Microbially influenced corrosion PY - 2025 AN - OPUS4-62772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Abilio, André T1 - Expert System for Screening Microbiologically Influenced Corrosion (MIC) as Internal Failure Cause in Oil and Gas Upstream Pipelines N2 - The analysis of pipeline failures due to Microbiologically Influenced Corrosion (MIC) is challenging due to the complex interaction of many influencing parameters including pipeline operation conditions, fluid chemistry and microbiology, as well as the analysis of corrosion features and products. To help address this challenge, an expert system was developed to assist non-specialists in screening internal pipeline corrosion failures due to MIC related threats. To accomplish this, 15 MIC subject matter experts (with a total of 355 man-years of accumulated MIC based experience) were recruited to evaluate a total of 65 MIC failure cases based on real-life scenarios. These case study parameters and the expert elicited results were input into an Artificial Neural Network (ANN) model to create a model system which can screen whether a given failure scenario is one of three outcomes: a) failure is likely due to MIC, b) failure is likely not due to MIC, or c) the conclusion is inconclusive (analysis needs more data/information). The model system had an overall accuracy of 74.8% and it showcases that knowledge from subject matter experts can be captured in a reasonably effective way to screen for possible MIC failures. Based on that, this presentation will provide details of the model development process and key results to date. Important considerations regarding the level of confidence of the diagnoses and variation between expert opinion will also be discussed alongside with ideas on how to improve the model for field applicability. T2 - ISMOS 9 CY - Edinburgh, United Kingdom DA - 27.06.2023 KW - Expert System KW - Microbiologically Influenced Corrosion (MIC) KW - Oil and Gas Upstream KW - Failure Investigation KW - Artificial neural networks (ANN) PY - 2023 AN - OPUS4-64603 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braymer, Joseph T1 - Methanobacterium IM1 as a model organism to study MIC N2 - Microbiologically influenced corrosion (MIC), also known as biocorrosion, is a process where microbes corrode metal surfaces causing detrimental damage to manmade infrastructure. Several studies, mainly under anaerobic conditions, have identified sulfate-reducing bacteria and methanogens as key players in biocorrosion. However, an important issue is that most MIC-related microbes at the moment are non-culturable. In addition, improved technologies (i.e., omics, biochemical, and microscopy methods) are needed to study, detect, simulate, and modulate MIC-related cases. Therefore, the selection of strains that can cause MIC, are culturable, and are genetically accessible, are of high importance for establishing new methods to study MIC on the molecular level. For example, the archaeal strain Methanobacterium IM1 has caught great attention due to its involvement in biocorrosion processes. Genes encoding for a novel enzyme (MIC NiFe-hydrogenase) have been proposed in this methanogen to be directly related to the e T2 - International Biodeterioration and Biodegradation Symposium 19 CY - Berlin, Germany DA - 11.09.2024 KW - Biocorrosion KW - Methanogen KW - Iron KW - Hydrogenase KW - Mechanism PY - 2024 AN - OPUS4-61508 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea T1 - Simulating Microbiologically Influenced Corrosion (MIC) at Seabed Environment in Monopile N2 - Ensuring the safety of offshore wind structures (OWS) is critical to guaranteeing their long-term performance and supporting reliable green energy supply. Microbiologically influenced corrosion (MIC) presents a significant challenge, particularly for monopiles in seabed environments. This study investigates the behavior of microorganisms and their impact on the corrosion process of carbon steel within monopiles. To simulate MIC at the sediment/water interface, an in-house experimental column was developed and inoculated with sediment and water samples from the North Sea. The system was operated under varying flow rates to replicate seabed movement conditions. Multiple molecular microbiological methods, surface analysis techniques, and other approaches were employed to assess the effects of different treatments. This study provides insights into MIC mechanisms in offshore environments and supports the development of strategies to monitor MIC in OWS infrastructure T2 - ISMOS10 CY - Nashville, TN, USA DA - 11.08.2025 KW - MIC KW - Environmental Simulation KW - Field testing KW - Marine Environment PY - 2025 AN - OPUS4-64298 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Koerdt, Andrea T1 - Technical challenges for the investigation of Microbiologically influenced corrosion under laboratory conditions across several sectors N2 - Microbiologically influenced corrosion MIC occurs in different sectors, under various conditions and can significantly contribute to material degradation. The most convincing effect can be observed with sulphate-reducing bacteria (SRB). There are many stakeholders who do not need to be convinced of this as there is ample scientific evidence clearly showing that SRBs corrode metal. However, many believe this is solely due to the produced H2S. Fewer people are aware that SRBs also have other mechanisms that can lead to corrosion, such as electrical MIC on metal (direct electron uptake from the metal used as electron donor). Despite this, many sectors or industries remain skeptical in several areas. When considering other classes or species, the skepticism increases even more. The reason is simple: microbiologist cannot consistently prove MIC on laboratory scale for all corrosive microorganisms. In contrast to materials sciences, where experiments can be narrowed down to a limited number of parameters, microbiology is too complex to simulate simply in the lab. Several factors are mandatory for the growth of microorganisms, consequently increasing the number of parameters. Even when making the system more complex, there are still unknown species in the field, whose growth conditions are not yet understood. We know via 16S rRNA analysis that the species is present, but that is all we know. If these samples are enriched in the lab, many species will not survive and their impact on the whole community cannot be investigated. Therefore, lab tests related to MIC works only for a certain number of microorganisms. This means the key-result for other disciplines are missing, and important numbers for calculating the lifespan of a material can only be provided with limited accuracy. This is neither satisfying nor useful for engineers, material scientist or similar professionals, and it is understandable. However, MIC occurs, and we need to address it in our infrastructure or other important areas. With this presentation, I aim to show the currently available techniques for testing on a laboratory scale. I will use SRBs and methanogenic archaea as examples to highlight the advantages and disadvantages of each method and point out where improvements are needed. The examples will be cross-sectoral and applicable to other sectors as well. This talk will highlight the currently existing challenges of testing MIC in the laboratory and may help generate creative solutions. T2 - MICxUS 2025 CY - Nicosia, Cyprus DA - 21.01.2025 KW - MIC KW - Biocorrosion KW - Laboratory testing KW - Interdisziplinarity KW - Microorganisms PY - 2025 UR - https://www.unic.ac.cy/ehresearch/micxus2025/#tab-98dc74f32bf3b8f95bd AN - OPUS4-63725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -