TY - CONF A1 - Wilke, Olaf A1 - Jann, Oliver T1 - Comparison of Formaldehyde Concentrations in Emission Test Chambers Using EN 717-1 and EN 16516 N2 - For many years EN 717-1 (Wood-based panels - Determination of formaldehyde release - Part 1: Formaldehyde emission by the chamber method) is the standard for formaldehyde emission testing of wooden boards. In 2017 EN 16516 (Construction products - Assessment of release of dangerous substances - Determination of emissions into indoor air) was published as a new harmonised standard for the emission testing of construction products. Because test chamber conditions are different, both standards give different concentrations for formaldehyde. For the determination of a conversion factor four test series were set up with different wooden boards. T2 - Conference on Indoor Air CY - Philadelphia, PA, USA DA - 22.07.2018 KW - Loading factor KW - Construction products KW - European standard KW - Air exchange rate PY - 2018 AN - OPUS4-45631 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wilke, Olaf A1 - Seeger, Stefan A1 - Brödner, Doris A1 - Erdmann, Kerstin A1 - Rasch, Fabian T1 - Chemical characterization of ultra-fine particles released from laser printers N2 - 11 laser printers from 5 manufacturers were purchased in 2017 and tested for their UFP emissions. Size resolved sampling of the emitted particles was done with a 13 stage (30 nm to 10 µm) low pressure cascade impactor. The sampled particles were analysed for their chemical composition by thermal extraction (vaporization at 290°C) followed by GC-MS analysis. High boiling cyclic siloxanes (D10 to D16) were detected as constituents of UFP from laser printers. In comparison to measurements in 2008, aliphatic long-chain alkanes (C22 to C34) were detected additionally as chemical constituents of UFP from most of the tested printers and their amounts were higher than for cyclic siloxanes. Printers of one manufacturer showed very low UPF emissions compared to the other manufacturers. T2 - Indoor Air Conference 2022 CY - Kuopio, Finland DA - 12.06.2022 KW - UFP KW - Thermal extraction KW - Cascade impactor PY - 2022 AN - OPUS4-55107 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Völzke, Jule L. A1 - Hodjat Shamami, Parya A1 - Gawlitza, Kornelia A1 - Feldmann, Ines A1 - Zimathies, Annett A1 - Meyer, Klas A1 - Weller, Michael G. T1 - Corundum as a novel affinity platform for the isolation of human IgG from plasma N2 - Nonporous corundum powder was functionalized covalently with protein binders to isolate and enrich specific proteins from complex matrices.The common crosslinker glutaraldehyde was compared with a hyperbranched polyglycerol (PG) of around 10 kDa. The latter was oxidized with periodate to generate aldehyde groups that can covalently react with the amines of the surface and the amino groups from the protein via a reductive amination process. The amount of bound protein was quantified via aromatic amino acid analysis (AAAA). As a proof of concept, IgG was extracted with protein A from crude human plasma. The advantages of corundum include the very low price, extremely high physical and chemical stability, pressure resistance, favorable binding kinetics, convenient handling, and flexible application. T2 - Adlershofer Forschungsforum 2022 CY - Berlin, Germany DA - 11.11.2022 KW - Affinity support KW - Affinity chromatography KW - Affinity extraction KW - Phosphonic acids KW - Polyglycerol KW - Reductive amination KW - Amino acid analysis KW - Tyrosine KW - Protein quantification KW - SDS-PAGE KW - Antibodies KW - Antibody purification KW - Downstream processing KW - Bovine serum albumin KW - BSA KW - Protein a KW - TEM KW - ESEM KW - Aluminum oxide KW - Sapphire KW - Human plasma KW - Protein immobilization KW - Protein hydrolysis KW - Glutaraldehyde KW - Aromatic amino acid analysis AAAA PY - 2022 AN - OPUS4-56154 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Torge, Manfred A1 - Feldmann, Ines A1 - Günther, Tobias A1 - Wilsch, Gerd T1 - Analytische Untersuchungen an Glasmalfarben mittels EDX und LIBS N2 - Nach 1850 wurde zur weiteren Herabsetzung der Einbrenntemperatur von Glasmalfarben Borax (Na2B4O7 · 10 H2O) zugesetzt. Das Verhältnis war nun 1 Teil SiO2, 3 Teile PbO und 0,5 Teile Borax. Der analytische Nachweis von Bor in eingebrannten Malschichten war bisher jedoch nicht möglich. In Laborversuchen wurden Glasmalfarben mit unterschiedlichem Gehalt an Borax auf Modellgläser aufgetragen, eingebrannt und anschließend unter simulierten Umweltbedingungen zeitraffend im Klimaschrank bewittert. Mit Hilfe von elektronenmikroskopischen Untersuchungen können Malschichten charakterisiert werden und somit Hinweise auf mögliche Schadensursachen liefern. Der Nachweis von Bor erfolgte mit Hilfe von LIBS-Messungen (Laser Induced Breakdown Spectroscopy) an im Labor hergestellten Glasmalfarben mit unterschiedlichem Boraxgehalt. T2 - Archäometrie und Denkmalpflege 2018 CY - Hamburg, Germany DA - 20.04.2018 KW - Glasmalfarben KW - Umweltsimulation KW - Analytik PY - 2018 AN - OPUS4-45069 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Torge, Manfred A1 - Seneschal-Merz, Karine A1 - Feldmann, Ines A1 - Bücker, Michael A1 - Oleszczuk, S. T1 - EDX-Analysis on medieval glasses and innovative protection of stained glass panels N2 - The church of Koszewko (Poland) is a brick building edified in the 15th century built on cobblestone foundations. There are five windows in the sanctuary. Three of them enclose heraldic panels from the Küssow’s family from the 15th century which are surrounded with Goethe glass from the 18th century to complete the windows. The colored heraldic panels are strongly damaged and corroded with massive paint layer losses, glass- and leadbreakages. Those medieval glass fragments have been shortly discovered and are of particular interest for Poland since only few medieval glazing have been conserved. The damages as well as the glass compositions have been investigated with ESEM/EDX. Two categories of medieval glass compositions have been identified. The blue glass is particularly sensible to corrosion because of his high content in K2O. The colorless and the red glass samples belong to a stable glass type. Due to the thickness of the gel layer, it is easy to see that the degradation is strongly proceeded. The protection of those medieval stained-glass panels is absolute necessary. The medieval panels have been restored and surrounded from a copper frame. Then they have been fixed on the wood frame in the church. The exterior glazing has been closed with a panel of Goethe glass. The gap between the Goethe- and the medieval glass is about 3 cm. The Goethe glass panel has been stabilized with a film based on polyester to protect the medieval glasses against any damages. In this way, a low cost protective glazing has been installed for a long-term conservation of each medieval stained-glass panels. The climate measurements over the period of one year on the restored windows are in process. The temperature and the relative humidity are recorded in the church interior, in the gap between the original and the Goethe glass and outdoors. T2 - 93rd Annual Meeting of DGG and Annual Meeting of USTV CY - Nuremberg, Germany DA - 13.05.2019 KW - Medieval glasses KW - Stained glasses KW - EDX Analysis KW - Corrosion PY - 2019 AN - OPUS4-48025 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Torge, Manfred A1 - Feldmann, Ines A1 - Seneschal-Merz, Karine A1 - Bücker, Michael A1 - Oleszczuk, O. T1 - EDX-Untersuchungen an mittelaltelichen Gläsern und innovativer Schutz der Glasmalereien N2 - In Vorbereitung einer Restaurierung erfolgten naturwissenschaftliche Untersuchungen zu Schadensphänomenen und Glaszusammensetzungen an mittelalterlichen Gläsern aus der Dorfkirche in Koszewko (Polen)im Environmental Scanning Electron Microscope (ESEM) mit EDX. Die Ergebnisse zeigen, dass die Glasverwitterung schon sehr stark vorangeschritten ist und ein zukünftiger Schutz der mittelalterlichen Glasmalereifelder vor Umwelteinflüssen unbedingt notwendig ist. Es wurde ein Schutzverglasungsystem entwickelt, das speziell auf den langfristigen Erhalt der einzelnen mittelalterlichen Glasmalereifelder ausgelegt ist. T2 - 21th Congress of Association Internationale pour l´Histoire du Verre CY - Istanbul, Turkey DA - 03.09.2018 KW - Glasanalyse KW - ESEM KW - Schutzverglasung PY - 2018 AN - OPUS4-45947 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seeger, Stefan A1 - Pollakowski-Herrmann, Beatrix A1 - Osan, J. A1 - Gross, A. A1 - Stosnach, H. A1 - Kayser, Y. A1 - Beckhoff, B. T1 - Quantification of element mass concentrations in aerosols by combination of cascade impactor sampling and in-situ TXRF Spectroscopy N2 - A mobile Bruker S2 Picofox TXRF spectrometer has been used in two field campaigns within the EMPIR env07 AEROMET project for the on-site analysis of cascade impactor aerosol samples.The results show that even at moderate air pollution levels – i.e.PM10 fairly below 20 μg/m³ - element mass concentrations in air in the range of 100 pg/m³could be measured in up to 13 size bins after sampling times of less than only 0.5 days. T2 - UFP 2019 Ultrafeinstaub in der Atmosphäre und in Innenräumen, 3. Symposium CY - Technische Universität Berlin, Germany DA - 19.09.2019 KW - TXRF ambient air aerosol chemical analysis aerosol element composition KW - Aerosol KW - TXRF KW - Cascade impactor KW - Aerosol element alanysis KW - Aerosol element mass concentration PY - 2019 AN - OPUS4-49580 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Schwirn, K. A1 - Völker, D. A1 - Ahtiainen, J. A1 - Schmidt, Alexandra A1 - Bresch, Harald A1 - Kämpf, K. A1 - Bachmann, V. A1 - Kuhlbusch, T. T1 - OECD Test Guidelines development for chemicals safety assessment of nanomaterials N2 - The OECD test guidelines (TGs) for testing chemicals have been widely used for regulatory purposes all over the world since the establishment of the Mutual Acceptance of Data (MAD) principle in 1984. This MAD principle ensures that, if a chemical is tested under the Good Laboratory Practice (GLP) conditions accordingly to an OECD TG, the data should be accepted in all OECD countries. The TGs have been developed, harmonized, internationally validated (round robin tests) and adopted by OECD countries to be used for the physical-chemical characterisation, fate estimation, and hazard identification for risk assessment of various chemicals. In addition to the TGs, OECD Guidance Documents (GDs) usually provide guidance on how to use TGs and how to interpret the results. These GDs do not have to be fully experimentally validated, and hence they are not under MAD, but they are based on relevant published scientific research. But are the existing TGs and the related GDs applicable and adequate for the regulatory testing of nanomaterials? In general, it is accepted that most of the "endpoints" or more precisely measurement variables are applicable also for nanomaterials. However, for some endpoints new or amended TGs are needed. In addition, several GDs are needed to give more precise advice on the test performance in order to gain regulatory relevant data on nanomaterials. The poster will present the status quo on recent TGs and GDs development for nanomaterials at OECD level with relevance for physical-chemical characterisation. Emphasis will be given to the proposed OECD TG on particle size and size distribution for manufactured nanomaterials. The development of such a TG is of special importance as particle size and size distribution is considered as major information for nanomaterial identification and characterization. A reliable and reproducible characterisation of particle size and size distribution is also needed for chemicals risk assessment of nanomaterials, for instance to interpret and compare test results and - in future – to forecast interaction and effects of nanomaterials. The presented poster will illustrate the way from the idea for a new TG and new GD to an accepted OECD TG/GD. T2 - BAM-PTB Workshop 2018 CY - Berlin, Germany DA - 14.05.2018 KW - Nano KW - OECD KW - Nanomaterials KW - Test Guideline KW - Prüfrichtlinie PY - 2018 AN - OPUS4-45108 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina A1 - Bücker, Michael A1 - Feldmann, Ines A1 - Reimann, Mandy T1 - Mobile anodization for the conservation of damaged architectural aluminium elements N2 - Initial situation: Aluminum is an often-used building material in modern architecture, not only for construction but as well for facades and decorative elements. In the 1950th and 1960th, after World War II, many buildings in Germany were constructed with aluminum or contain elements of colored anodized aluminum. In the last years a larger number of these buildings are increasingly in the sight of conservation works including the aluminum parts such as window frames or facade coverings. Damaged Aluminum Surfaces: Common damages are a change of color or gloss changes through weathering processes, drill holes or marks due to later modifications, scratches in the anodized layer due to extensive wear e.g. at handrails or door handles. To repair damaged aluminum surfaces, there are usually two options: smaller damaged areas are repaired by using a touch-up pen. In case of larger damages, the complete re-anodization is necessary. This includes to de-anodize the surface with cleaning and grinding the whole aluminum object. Both possibilities are disadvantageous for the objects. The touch-up pen often does not match the color of the original surface together with an insufficient corrosion protection for outdoors. While the newly anodized surface differs in color and gloss from the originally applied color. Research Approach: The whole procedure contrasts with the principal approach in conservation which aims to intervene as less as possible, in case of the conservation of an object. To fulfill this approach in a more appropriate way the research project focuses on a mobile and partial application for colored, anodized aluminum parts. To anodize aluminum the application of an electrolyte onto the surface together with sufficient voltage and current is necessary. Generally diluted sulfuric acid is used as electrolyte. Different possibilities are examined to enable the mobile application of the electrolyte, e. g. the application by producing a gel matrix or like in electroplating by pen or brush wrapped with a fleece fabric. Experimental part: First experiments are conducted to examine the structure of the anodized layer in relation with proper cleaning, anodization time with applied voltage and current and the coloring process. The aim was to reduce the preparation procedure and the anodization time as much as possible to facilitate the mobile application. Examinations with Keyence microscope, Eddy current testing and REM are performed to characterize the layers. The results are shown in table 1. A clear connection between proper cleaning, anodization time, voltage and amperage and the achieved thickness of the anodized layer is significant. Cracks in the layer show that raising the voltage and amperage results in thicker layers but as well in a crumbled and less stable anodized surface. Gel preparation: In addition to the anodization process with a liquid e.g. sulfuric acid a gel application is tested to prevent the electrolyte from rinsing down during the mobile application. For this purpose, several gel-forming agents are tested together with their stability in acid systems. It was observed, that the consistency of the gels varies dependent of the time. Conductivity: The conductivity of sulfuric acid combined with different gel-systems was measured and compared in order to predict the possible growth of layers during anodic oxidation process. Further steps: Determination and optimization of application parameters like voltage, amperage and anodization-time to build up a preferably stable and sufficient thick anodized layer. Examination of gel preparation to guarantee a stable product, enforcing with textile tape for easy application. T2 - Architectural Aluminum in the 21st Century CY - Boston, MA, USA DA - 24.03.2018 KW - Aluminum KW - Anodization KW - Historic buildings KW - Mobile application PY - 2018 AN - OPUS4-45018 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Raedel, Martina A1 - Bücker, Michael A1 - Feldmann, Ines A1 - Reimann, M. T1 - Conservation of damaged architectural aluminum elements N2 - Aluminum is an often-used building material in modern architecture. In recent years buildings from the 1950th and 1960th are increasingly subject of conservation works including the aluminum parts. Typical surface damages are signs of corrosion caused by weathering processes or scratches in the anodized layer due to extensive wear. To repair damaged aluminum surfaces, there are usually two options: smaller areas are repaired by using a touch-up pen, for larger damages it is necessary to remove the anodized layer completely. Both possibilities are disadvantageous for the objects; the touch-up pen often does not match the color together with an insufficient corrosion protection, while newly anodized layers often differ in color and gloss from the original surface. For this reason, a research project was initiated to develop a mobile method to repair anodized aluminum parts. The first step focusses on the mobile anodization process by using the electrolyte with a gel substrate. Different cathodic materials are to be tested together with appropriate cooling material. The anodized area should be isolated to protect undamaged areas. Examinations of the produced layers are conducted by using Keyence microscope, eddy current testing and ESEM analysis. Further steps are to transform the coloring and sealing process for mobile application. Color could be applied by using a brush or by spray while the sealing process could be performed with water vapor. An heatable putty knife could be used, if heating up the area will be necessary. Once the application process is developed, the anodization will be tested on samples with artificial damages, fixed in horizontal and vertical positions. The stability of the anodized surface will be examined by accelerated ageing in a climate chamber and outdoor weathering. The electrolyte (diluted sulfuric acid) was combined with a gel binder to enable a mobile application. Several thickening agents were tested concerning their conductivity and stability in acid systems. Anodization tests with different cathodic material and shapes were conducted. The temperature during anodization was controlled and adjusted if necessary. The anodized area was restricted by using either a lacquer, an adhesive or a removable silicon barrier. The fist results show the feasibility of the method on enclosed areas. The achieved thickness was measured by eddy current testing and the structure was controlled by ESEM analysis. The examinations show a connection between thickness and porosity of the anodized layers and the temperature during the application process. Next steps are testing mobile coloring and sealing methods followed by mobile anodization on artificial damaged areas. T2 - Metal 2019 CY - Neuchâtel, Switzerland DA - 02.09.2019 KW - Mobile anodisation KW - Aluminium KW - Conservation KW - Damage repair PY - 2020 UR - https://www.lulu.com/shop/claudia-chemello-and-laura-brambilla-and-edith-joseph/metal-2019-proceedings-of-the-interim-meeting-of-the-icom-cc-metals-working-group-september-2-6-2019-neuch%C3%A2tel-switzerland-ebook/ebook/product-24517161.html AN - OPUS4-51479 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -