TY - CONF A1 - Weimann, Karin A1 - Adam, Christian ED - Martins, I. M. ED - Ulsen, C. ED - Villagran, Y. T1 - Advantages of recycling gypsum plasterboards N2 - Advantages of recycling gypsum plaster boards During the last decades the material composition of buildings has become increasingly diverse. However, largely sorted material flows are needed for generating high quality secondary building materials. The use of secondary building materials can meet the requirements of sustainability in several ways: the extended time availability of primary raw materials and, thereby, the preservation of natural resources as well as the conservation of landfill sites. Recycling of gypsum (calcium sulfate) can be a good example for the environmental benefits of closed-loop recycling. The content of sulfates in other secondary building materials, in particular in recycled concrete aggregates, should be minimized for quality reasons. In contrast, separated gypsum can also be used in gypsum production if the high quality requirements for the recycled gypsum are met. Since almost all processing steps in the recycling process are associated with environmental impacts, an environmental evaluation of the use of recycled gypsum as a substitute in gypsum production has to be carefully conducted. This paper focusses on the techniques for generating recycled gypsum from gypsum plasterboards, the related quality requirements and a comprehensive environmental evaluation of the complete process. T2 - IV International Conference Progress of Recycling in the Built Environment CY - Lisbon, Portugal DA - 11.10.2018 KW - Environmental evaluation KW - Gypsum KW - CDW processing PY - 2018 SN - 978-2-35158-208-4 VL - PRO 124 SP - 243 EP - 250 PB - Rilem publications S.A.R.L. CY - Paris AN - OPUS4-48078 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weimann, Karin A1 - Adam, Christian T1 - Advantages of recycling gypsum plasterboards N2 - During the last decades the material composition of buildings has become increasingly diverse. However, largely sorted material flows are needed for generating high quality secondary building materials. The use of secondary building materials can meet the requirements of sustainability in several ways: the extended time availability of primary raw materials and, thereby, the preservation of natural resources as well as the conservation of landfill sites. Recycling of gypsum (calcium sulfate) can be a good example for the environmental benefits of closed-loop recycling. The content of sulfates in other secondary building materials, in particular in recycled concrete aggregates, should be minimized for quality reasons. In contrast, separated gypsum can also be used in gypsum production if the high quality requirements for the recycled gypsum are met. Since almost all processing steps in the recycling process are associated with environmental impacts, an environmental evaluation of the use of recycled gypsum as a substitute in gypsum production has to be carefully conducted. This paper focusses on the techniques for generating recycled gypsum from gypsum plasterboards, the related quality requirements and a comprehensive environmental evaluation of the complete process. T2 - IV International Conference Progress of Recycling in the Built Environment CY - Lisbon, Portugal DA - 11.10.2018 KW - Environmental evaluation KW - CDW processing KW - Gypsum PY - 2018 AN - OPUS4-48079 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weimann, Karin T1 - Gypsum plasterboard recycling N2 - The use of secondary building materials can meet the requirements of sustainability in several ways: the extended time availability of primary raw materials and, thereby, the protection of natural ressources as well as the conservation of landfill sites. Regarding the predicted decrease of gypsum supply in Germany, particularly the recycling of gypsum (calcium sulfate) is of growing importance. Currently, the gypsum demand is fulfilled (at least 60%) by gypsum as side product from coal-fired power plants (FGD Gypsum). Germany’s natural gypsum deposits fulfil the remaining gypsum demand. Due to national climate protection goals the gypsum supply from coal power plants will decrease significantly in the future. In addition, the content of sulfates in other secondary building materials, in particular in recycled concrete aggregates, should be minimized for quality reasons. Separated gypsum can be used in gypsum production if the high quality requirements for recycled gypsum are met. Accordingly, there have been significant advancements in the processing of gypsum residues in the last years. Since almost all processing steps in the recycling process are associated with environmental impacts, an evironmental evaluation of the use of recycled gypsum as a substitute in gypsum production has to be carefully conducted. The presentation focusses on the techniques for generating recycled gypsum from gypsum plaster boards, the related quality requirements and a comprehensive environmental evaluation of the complete process. T2 - MINEA Workshop: Recovery Potential of Construction and Demolition Waste CY - Brussels, Belgium DA - 21.03.2019 KW - Gypsum KW - CDW processing KW - Environmental evaluation PY - 2019 AN - OPUS4-48220 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stawski, Tomasz A1 - Karafiludis, Stephanos A1 - Pimentel, C. A1 - Montes Hernandez, G A1 - Kochovski, Z A1 - Bienert, Ralf A1 - Weimann, Karin A1 - Emmerling, Franziska A1 - Scoppola, E A1 - Van Driessche, A T1 - Solution-driven processing of calcium sulfate: the mechanism of the reversible transformation of gypsum to bassanite in brines N2 - Calcium sulfate hemihydrate (CaSO4ᐧ0.5H2O), also known as bassanite, has been used as a precursor to produce gypsum (dihydrate, CaSO4ᐧ2H2O) for various construction and decorative purposes since prehistoric times. The main route to obtain hemihydrate is a thermal treatment of gypsum at temperatures typically between 150 °C and 200 °C to remove some of the structural water. In this contribution, we introduce (Fig. 1) a more efficient and sustainable method (T < 100 °C) that enables the direct, rapid, and reversibly conversion of gypsum to bassanite using reusable high salinity aqueous solutions (brines with c[NaCl] > 4 M). The optimum conditions for the efficientproduction of bassanite in a short time (< 5 min) involve the use of brines with c(NaCl) > 4 M and maintaining a temperature, T > 80 °C. When the solution containing bassanite crystals is cooled down to around room temperature, eventually gypsum is formed. When the temperature is raised again to T > 80 °C, bassanite is rapidly re-precipitated. This contrasts with the typical behaviour of the bassanite phase in low salt environments. Traditionally, hemihydrate is obtained through a solid state thermal treatment because bassanite is considered to be metastable with respect to gypsum and anhydrite in aqueous solutions, and therefore gypsum-to-bassanite conversion should not occur in water. Its very occurrence actually contradicts numerical thermodynamic predictions regarding solubility of calcium sulfate phases. By following the evolution of crystalline phases with in situ and time-resolved X-ray diffraction/scattering and Raman spectroscopy, we demonstrated that the phase stability in brines at elevated temperatures is inaccurately represented in the thermodynamic databases. Most notably for c(NaCl) > 4 M, and T > 80 °C gypsum becomes readily more soluble than bassanite, which induces the direct precipitation of the latter from gypsum. The fact that these transformations are controlled by the solution provides extensive opportunities for precise manipulation of crystal formation. Our experiments confirmed that bassanite remained the sole crystalline structure for many hours before reverting into gypsum. This property is extremely advantageous for practical processing and efficient crystal extraction in industrial scenarios. T2 - Granada Münster Discussion Meeting GMDM 10 CY - Münster, Germany DA - 29.11.2023 KW - Gypsum KW - Bassanite KW - Calcium sulfate KW - Recycling KW - Scattering PY - 2024 AN - OPUS4-59162 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -