TY - CONF A1 - Jaunich, Matthias A1 - Kömmling, Anja A1 - Böhning, Martin A1 - Silbernagl, Dorothee T1 - Comparison of ageing behavior of O-ring seals under hydrogen and air N2 - Elastomeric seals are essential components in the infrastructure which prevent leakage of gas and ensure proper function of technical devices and are therefore highly safety relevant. For proper function a remaining resilience and tolerance to pressure changes is required. The ageing of elastomers is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurrence of critical failure is desired. Hydrogen is a key element for the energy turnaround and therefore the compatibility of seals with hydrogen is essential. In addition to the effect of hydrogen uptake and release, which might also cause destructive effects such as rapid gas decompression, ageing at high temperature under hydrogen atmosphere is of interest too. Most of the existing work is addressing the performance of new materials and comprises only very limited investigations concerning long-term use and the behaviour of aged materials in contact with hydrogen. As ageing can lead to substantial changes of material properties, it must be evaluated whether these changes are beneficial or deteriorating for the component function. In this work we present and compare results of the characterization of three sealing materials (EPDM, HNBR, FKM) after ageing at high temperature under hydrogen and air. Despite the common assumption that ageing under hydrogen atmosphere should be less severe for the material in comparison to air ageing, this is not the case for every material. T2 - ASME PVP2025, Pressure Vessels & Piping Conference CY - Montreal, Quebec, Canada DA - 20.07.2025 KW - Aging KW - Seal KW - Compression set KW - Atomic force microscopy PY - 2025 SP - 1 EP - 7 AN - OPUS4-63889 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zaghdoudi, M. A1 - Kömmling, Anja A1 - Böhning, Martin A1 - Jaunich, Matthias T1 - Ageing of elastomers in air and in hydrogen environment - A comparative study N2 - EPDM, HNBR and FKM materials were exposed at 150 ◦C to air under atmospheric pressure and to hydrogen at 50 bar for different ageing times. All measurements after hydrogen exposure were conducted on samples in degassed condition to assess irreversible effects resulting from that exposure and to compare them to those after ageing in air. Density, hardness, tensile properties, compression set, and hydrogen permeability of all samples were analysed. In both ageing environments, HNBR exhibited the most significant changes of material properties. However, for both EPDM and HNBR, considerably less severe ageing effects were observed under hydrogen in comparison to ageing in air. On the other hand, FKM showed about the same low level of deterioration in both ageing environments but exhibited poor resistance against damage due to rapid gas decompression in hydrogen environment that can lead to seal failure. The obtained results may serve as a guidance toward a better understanding for design and utilisation of elastomeric materials in future hydrogen infrastructure components. KW - Rapid gas decompression KW - Condensed matter physics KW - Hydrogen KW - Sustainability and the environment KW - Rubber sealing KW - Renewable energy PY - 2024 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-597417 DO - https://doi.org/10.1016/j.ijhydene.2024.03.053 SN - 0360-3199 SN - 1879-3487 VL - 63 SP - 207 EP - 216 PB - Elsevier CY - Oxford AN - OPUS4-59741 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vega Puga, E. A1 - Wachtendorf, Volker A1 - Kömmling, Anja A1 - Brendelberger, S. A1 - Jaunich, Matthias A1 - Sattler, C. T1 - Lifetime prediction and degradation assessment of FKM and FFKM O-rings under high temperature thermo-oxidative ageing N2 - To support the development of solar reactor technologies for hydrogen production, this study investigates the thermo-oxidative degradation mechanisms of fluorinated elastomers and predicts their lifetimes at high temperatures (200–300 ◦C) consistent with the application requirements. An accelerated ageing programme is conducted with FKM and FFKM O-rings and flat samples for up to 21 days. Optical microscopy is used to analyse the exposed seals’ morphological changes, while IR microscopy is utilised to investigate the underlying chemical degradation mechanisms of both elastomers. Findings suggest that FKM’s degradation arises from dehydrofluorination of the polymer, followed by chain scission and backbone cleavage as a result of the oxidation of newly formed C=C double bonds. FFKM’s degradation is primarily associated with chain scission, but there is also indication that post-curing processes may occur during material ageing. Furthermore, hardness, equilibrium compression set (CS), continuous compression stress relaxation (CSR) and leakage rate tests are used to evaluate changes in the mechanical properties and sealing performance of the elastomers. Equilibrium CS data is extrapolated using time-temperature shifts (TTS) and used to derive an end-of-life criterion of 75 % equilibrium CS, which correlates to leakage rates higher than a predetermined threshold. Service lifetime predictions of FKM and FFKM O-rings at several temperatures are performed and a seal operating temperature of 200 ◦C is suggested, which ensures reasonable O-ring replacement intervals of more than half a year in the solar reactor for both considered materials. KW - Fluoroelastomer KW - Perfluoroelastomer KW - Thermo-oxidative ageing KW - Lifetime prediction KW - Compression set PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630112 DO - https://doi.org/10.1016/j.polymertesting.2025.108820 SN - 1873-2348 VL - 147 SP - 1 EP - 17 PB - Elsevier BV CY - Amsterdam AN - OPUS4-63011 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Comparison of Ageing Behavior of O-Ring Seals Under Hydrogen and Air N2 - Elastomeric seals are essential components in the infrastructure which prevent leakage of gas and ensure proper function of technical devices and are therefore highly safety relevant. For proper function a remaining resilience and tolerance to pressure changes is required. The ageing of elastomers is an undesirable but inevitable process leading to a limited lifetime of rubber products such as seals. Independent of the application, as e.g. automotive, piping or container applications, a long lifetime or at least a timely exchange of a seal before occurrence of critical failure is desired. Hydrogen is a key element for the energy turnaround and therefore the compatibility of seals with hydrogen is essential. In addition to the effect of hydrogen uptake and release, which might also cause destructive effects such as rapid gas decompression, ageing at high temperature under hydrogen atmosphere is of interest too. Most of the existing work is addressing the performance of new materials and comprises only very limited investigations concerning long-term use and the behaviour of aged materials in contact with hydrogen. As ageing can lead to substantial changes of material properties, it must be evaluated whether these changes are beneficial or deteriorating for the component function. In this work we present and compare results of the characterization of three sealing materials (EPDM, HNBR, FKM) after ageing at high temperature under hydrogen and air. Despite the common assumption that ageing under hydrogen atmosphere should be less severe for the material in comparison to air ageing, this is not the case for every material. T2 - ASME PVP2025, Pressure Vessels & Piping Conference CY - Montreal, Canada DA - 20.07.2025 KW - Aging KW - Seal KW - Compression set KW - Atomic force microscopy PY - 2025 AN - OPUS4-63888 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaunich, Matthias T1 - Elastomerdichtungen für Wasserstoffanwendungen - Vergleich des Alterungsverhaltens in Luft und Wasserstoff N2 - In diesem Beitrag soll ein Fokus auf das Alterungsverhalten von Elastomerdichtungen unter Wasserstoff gelegt werden. Hierfür wurden Untersuchungen bei einem mittleren Wasserstoffdruck über Alterungszeiten von bis zu 100 Tagen durchgeführt. Das Alterungsverhalten wird im Vergleich der Alterungseffekte unter thermooxidativen Bedingungen betrachtet und bewertet. Die Annahme, dass der Alterungseffekt unter Wasserstoff stets weniger ausgeprägt ist als an Luft bestätigt sich nicht durch die Ergebnisse. T2 - 4. O-Ring-Forum der Firma ISGATEC CY - Bad Schönborn, Germany DA - 15.05.2025 KW - Wasserstoff KW - Dichtung KW - Thermische Alterung KW - Elastomer PY - 2025 AN - OPUS4-63135 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -