TY - CONF A1 - Geburtig, Anja T1 - Combined impact of UV radiation and nitric acid (HNO3) on HDPE jerrycans – comparison of outdoor and lab test N2 - A damaging action of HNO3-55% only occurs in combination with its decomposition into nitrous gases, which can be caused by UV radiation. In a laboratory test, transparent HDPE jerrycans have been exposed to both UV radiation and 55 wt-% nitric acid solution at (41 ± 2)°C, for up to 20 days. For comparison, UV radiant exposure (21 days) and nitric acid exposure (up to 6 weeks) were performed separately, at nearly equal temperatures. The respective damages are compared with FTIR spectroscopy in ATR and HT-gel permeation chromatography (GPC) on a molecular level and with hydraulic internal pressure testing as a component test. For the used jerrycans, relevant oxidation can only be found after the combined exposure. The gradual increase in oxidative damage shows the good reproducibility of the lab exposure. The decomposition of nitric acid into nitrous gases by UV radiation – as well as the jerrycan oxidation – is also observed at lower HNO3 concentration (28 wt- %). Similar results are obtained after outdoor tests. Again, the damage occurs only after combined exposure, in contrast to the exposures to UV only and to HNO3 only, which were conducted in parallel. Outdoor exposures are most readily accepted as they represent possible end-use conditions. However, the reproducibility of these exposures is poor due to the large temporal variations in weather. There are also several safety risks, which is why the number of replicates remains limited. Since the outdoor and lab exposure tests show the same qualitative results, it is appropriate to conduct systematic studies in the laboratory. After 6 days of lab exposure, the oxidation damage is rated as critical, which corresponds to about 1/10 year in Central Europe, according to the UV radiant exposure. It should be noted that this amount can also occur in two sunny weeks. T2 - 24th iapri World Packaging Conference CY - Valencia, Spain DA - 17.06.2024 KW - UV exposure KW - Nitric acid KW - Polyethylene KW - Oxidation PY - 2024 AN - OPUS4-60416 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Altmann, Korinna T1 - PE-Rezyklat Einsatz in Gefahrgutbehältern? N2 - In diesem Vortrag geht es darum zu beschreiben, ob Rezyklat für PE Behälter gefüllt mit Gefahrgut Anwendung finden darf. Kanister aus Neuware und Rezyklat wurden verschiedenen Untersuchungen unterzogen. Es wurde der Feststoff und Leachable getestet. Methoden sind TED-GC/MS und GC-HRMS. Proben der Leachable wurden nach 1 und 4 Wochen genommen und die Peakanzahl vergleichen dargestellt. Als Lösemittel wurden Wasser, Ethanol, EtOAc, Ammoniak und HNO3 verwendet. T2 - Fachaustausch Projekt GeSKAR CY - Dessau, Germany DA - 10.01.2025 KW - Gefahrgutbehälter KW - Rezyklat PY - 2025 AN - OPUS4-62396 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Wägner, Yannick A1 - Geburtig, Anja T1 - Gedanken, Tipps & Tricks zu künstlichen Bewitterungsprüfungen N2 - Die Fragestellung kann nur exemplarisch dargestellt werden, aber ist hoffentlich auch für langjährige Praktiker in den ausgewählten Punkten interessant. Es sollen für folgende Bereiche Beispiele gegeben werden: Probenvorbereitung, Testvorbereitung, Testdurchführung und Auswertung. T2 - 53. Jahrestagung der GUS 2025 CY - Stutensee-Blankenloch bei Karlsruhe, Germany DA - 26.03.2025 KW - Wechseltemperaturen KW - Künstliche Bewitterung KW - Prüfung KW - UV KW - Feuchte KW - Beregnung PY - 2025 SN - 978-3-9826129-2-8 VL - 53 SP - 253 EP - 257 PB - Gesellschaft für Umweltsimulation e.V. CY - 76327 Pfinztal (Berghausen) AN - OPUS4-62861 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bandow, N. A1 - Aitken, M. D. A1 - Geburtig, Anja A1 - Kalbe, Ute A1 - Piechotta, Christian A1 - Schoknecht, Ute A1 - Simon, Franz-Georg A1 - Stephan, Ina T1 - Using Environmental Simulations to Test the Release of Hazardous Substances from Polymer-Based Products: Are Realism and Pragmatism Mutually Exclusive Objectives? N2 - The potential release of hazardous substances from polymer-based products is currently in the focus of environmental policy. Environmental simulations are applied to expose such products to selected aging conditions and to investigate release processes. Commonly applied aging exposure types such as solar and UV radiation in combination with water contact, corrosive gases, and soil contact as well as expected general effects on polymers and additional ingredients of polymer-based products are described. The release of substances is based on mass-transfer processes to the material surfaces. Experimental approaches to investigate transport processes that are caused by water contact are presented. For tailoring the tests, relevant aging exposure types and release quantification methods must be combined appropriately. Several studies on the release of hazardous substances such as metals, polyaromatic hydrocarbons, flame retardants, antioxidants, and carbon nanotubes from polymers are summarized exemplarily. Differences between natural and artificial exposure tests are discussed and demonstrated for the release of flame retardants from several polymers and for biocides from paints. Requirements and limitations to apply results from short-term artificial environmental exposure tests to predict long-term environmental behavior of polymers are presented. KW - Environmental simulations KW - Polymer-based products KW - Artificial weathering KW - Degradation KW - Leaching KW - Soil contact PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-509310 DO - https://doi.org/10.3390/ma13122709 SN - 1996-1944 VL - 13 IS - 12 SP - Paper 2709, 22 PB - MDPI CY - Basel, Switzerland AN - OPUS4-50931 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Gorbushina, Anna A1 - Plarre, Rüdiger A1 - Stephan, Ina T1 - Umweltsimulation an der BAM – Grundlegende Ansätze mit Beispielen aus der natürlichen Umwelt N2 - Drei grundlegend verschiedene Ansätze für Umweltsimulation werden an Beispielen illustriert: (i) Ganzheitlicher Ansatz - Nachstellen von Umweltmilieus im Labor Ziel ist hier das Nachstellen von (kombinierten) Umweltbedingungen im Labor; die Umweltparameter werden mit all ihren Wechselwirkungen aufgebracht. Hauptnutzen ist eine gegenüber der natürlichen Beanspruchung erhöhte Reproduzierbarkeit der Umweltbedingungen. Hat man sein Laborsetup entwickelt, ist es auf verschiedene Materialien anwendbar. Unter solchen Laborbedingungen ermittelte Lebensdauern sind dabei nicht auf die typischerweise sehr variablen Real-Umweltbedingungen übertragbar. (ii) Parametrisierter Ansatz - Ermittlung einzelner Materialempfindlichkeiten Hierbei werden im Labor die Wirkungen separater Umweltparameter auf Materialien nachgestellt. Für eine solche Separation der Einflussfaktoren ist insbesondere die Aufschlüsselung möglicher Wechselwirkungen der Umwelt-parameter (z.B. Mikroklima an bestrahlten Oberflächen) erforderlich. Einzelne (meist Alterungs-) Empfindlichkeiten können qualitativ nachgewiesen werden oder sogar – als Beanspruchungs-Wirkungs-Funktionen – quantifiziert werden, was einen wesentlichen Schritt in Richtung der Digitalisierung der Material¬prüfung darstellt. Insbesondere ist dann auch eine Lebensdauer-vorhersage für vorgegebene Zeitreihen der Beanspruchungs¬parameter umsetzbar. (iii) Rückwirkungen auf die Umwelt Umweltbeanspruchungen können zur Freisetzung von Schadstoffen in die Umwelt führen. Durch die Nachstellung kritischer, aber realitätsnaher Einsatzszenarien kann die Menge an freigesetzten Substanzen abgeschätzt werden. Egal, welcher Ansatz verfolgt wird – ein Vergleich mit der oder einer Real-beanspruchung ist unerlässlich, ebenso wie die Messdatenaufzeichnung (data logging) aller potenziell relevanten Beanspruchungsparameter während dieser Realbeanspruchung. Obwohl die naturnahe Umwelt – sowohl in der BAM als auch bei der GUS – gegenüber der technischen Umwelt eher untergeordnet auftritt, werden zur Illustration Beispiele aus der naturnahen Umwelt verwendet. T2 - 50. Jahrestagung der GUS CY - Online meeting DA - 23.03.2022 KW - Umweltsimulation PY - 2022 SN - 978-3-9818507-7-2 SP - 79 EP - 89 AN - OPUS4-55015 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker A1 - Geburtig, Anja T1 - Digitale Umweltsimulation am Beispiel der Photooxidation von Polymeren N2 - Die Umweltwirkungen auf ein Material werden als Überlapp der Funktionskurven von Materialempfindlichkeit und einwirkenden Umweltparametern betrachtet. Wenn entweder die Empfindlichkeit oder die Beanspruchungen Null sind, ergibt sich auch keine Umweltwirkung und bei beidseitig Werten größer Null das jeweilige Produkt der beiden. Die Akkumulation der nicht-reversiblen Effekte über die Zeit und allen Eigenschaftsänderungen entspricht der Alterung des Materials für den jeweiligen Expositionszeitraum. Die digitale Umweltsimulation gliedert sich hier in drei Teilaspekte. Ein erster, rein materialwissenschaftlicher Teil hat die Aufgabe, alle relevanten Materialempfindlichkeiten experimentell zu quantifizieren. Ein zweiter – unter Umständen numerischer Teil – hat die Aufgabe, das Bauteil und seine Einbaulage zu digitalisieren und aus den makroskopischen Umgebungsbedingungen die relevanten mikroklimatischen Umweltparameter für alle Oberflächen- oder Volumenelemente zu bestimmen. In einem dritten Teil werden die Einwirkungen über den betrachteten Zeitraum berechnet und kumuliert. Dieses Konzept, das auf den so genannten Expositions-Reaktions-Funktionen (ERF) basiert, wird an Beispielen der Photoxidation erläutert. Dieses Vorgehen wurde schon beim ViPQuali-Projekt als Numerische Umweltsimulation umgesetzt. Überprüft werden muss das Modell unbedingt an einer realitätsnahen Validierungsbeanspruchung. Hier werden die ermittelten ERFs mit über den kompletten Beanspruchungszeitraum geloggten Umweltparametern gekoppelt, um die berechnete mit der experimentell erfahrenen Alterungswirkung zu vergleichen. Nur so kann sichergestellt sein, dass alle für die Anwendungsumgebung relevanten Materialempfindlichkeiten einbezogen wurden. T2 - 52. Jahrestagung der GUS CY - Stutensee-Blankenloch, Germany DA - 26.03.2024 KW - UV KW - Polymer 3R KW - Bewitterung KW - Bestrahlung PY - 2024 SN - 978-3-9826129-0-4 SP - 31 EP - 40 PB - Gesellschaft für Umweltsimulation e.V. CY - Pfinztal (Berghausen) AN - OPUS4-59830 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Meurer, Maren T1 - Is olypropylene relevant for microplastic analytics? N2 - Nowadays, in every terrestrial and aquatic ecosystem, even in the remotest areas, small residues of plastics, the so called microplastic (MP) can be found. MPs are particles with a size of 1-1000 µm (ISO/TR 21960:2020), mainly containing synthetic polymers like polyethylene (PE), polypropylene (PP), polystyrene (PS) or polyethylene terephthalate (PET). Even styrene-butadiene rubber (SBR) as an indication for tire wear is included due to similar particle formation. To understand the MPs consequences to the environment, it is of high priority to capture its extent of contamination. It is surprising that in the analysis of polymer masses in environmental samples, PE, PS and SBR are often detected, but only small amounts of PP, although this is the second most commonly produced standard plastic and many MP particles originate from carelessly disposed packaging materials. This presentation provides hypotheses about the reasons of rare PP identification and mass quantification in environmental samples. Different investigations of pristine PP and representative environmental samples, including the pre-treatment by Accelerated Solvent Extraction (ASE) or with density separation followed by the thermal extraction / desorption gas chromatography-mass spectrometry (TED-GC/MS) are presented. The results are discussed according to the material properties and a possible degradation mechanism under different weathering conditions which indicate less stability under relevant storage conditions. T2 - Society of Environmental Toxicology and Chemistry CY - Dublin, Ireland DA - 30.04.2023 KW - Sample preparation KW - Polypropylene KW - Microplastic KW - Degradation PY - 2023 AN - OPUS4-57474 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Falkenhagen, Jana T1 - Combined impact of UV radiation and nitric acid (HNO3) on HDPE jerrycans – comparison of outdoor and lab test N2 - A damaging action of HNO3-55% only occurs in combination with its decomposition into nitrous gases, which can be caused by UV radiation. In a laboratory test, transparent HDPE jerrycans have been exposed to both UV radiation and 55 wt-% nitric acid solution at (41 ± 2)°C, for up to 20 days. For comparison, UV radiant exposure (21 days) and nitric acid exposure (up to 6 weeks) were performed separately, at nearly equal temperatures. The respective damages are compared with FTIR spectroscopy in ATR and HT-gel permeation chromatography (GPC) on a molecular level and with hydraulic internal pressure testing as a component test. For the used jerrycans, relevant oxidation can only be found after the combined exposure. The gradual increase in oxidative damage shows the good reproducibility of the lab exposure. The decomposition of nitric acid into nitrous gases by UV radiation – as well as the jerrycan oxidation – is also observed at lower HNO3 concentration (28 wt- %). Similar results are obtained after outdoor tests. Again, the damage occurs only after combined exposure, in contrast to the exposures to UV only and to HNO3 only, which were conducted in parallel. Outdoor exposures are most readily accepted as they represent possible end-use conditions. However, the reproducibility of these exposures is poor due to the large temporal variations in weather. There are also several safety risks, which is why the number of replicates remains limited. Since the outdoor and lab exposure tests show the same qualitative results, it is appropriate to conduct systematic studies in the laboratory. After 6 days of lab exposure, the oxidation damage is rated as critical, which corresponds to about 1/10 year in Central Europe, according to the UV radiant exposure. It should be noted that this amount can also occur in two sunny weeks. T2 - 24th iapri World Packaging Conference CY - Valencia, Spain DA - 17.06.2024 KW - Ppolyethylene KW - UV exposure KW - Nitric acid KW - Oxidation PY - 2024 VL - 2 SP - 30 EP - 37 PB - ITENE AN - OPUS4-60414 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scholl, Juliane A1 - Scharpmann, Philippa A1 - Bagheri, Abbas A1 - Lisec, Jan A1 - Meiers, Emelie A1 - Jaeger, Carsten A1 - Leonhardt, Robert A1 - Haase, Hajo A1 - Koch, Matthias T1 - Beyond the lab: Real-world composition of commercial Li-ion battery electrolytes N2 - This study presents a systematic, characterization of electrolytes from commercial lithium-ion batteries (LIB), encompassing 90 batteries from leading global manufacturers across diverse formats and application sectors. An integrated, complementary mass spectrometric workflow combining LC–MS/MS, GC–MS, and high-resolution MS was employed. To ensure robust structural annotation, molecular identifications were assigned confidence levels following Schymanski et al. (2014). Across all formats, PF6− was confirmed as the dominant Li+ counterion, frequently coexisting with BF4−, PO2F2−, and bis(fluorosulfonyl)imide (FSI−), forming binary and ternary salt systems optimized for both conductivity and safety. Solvent systems revealed the widespread use of propylene carbonate (PC) combined with diverse carbonate mixtures, demonstrating trends in performance optimization specific to cell format. A variety of additives were identified, reflecting a clear shift towards multifunctional, synergistic additive packages and the gradual replacement of fluorinated species with environmentally safer alternatives. Cycling studies demonstrated that electrolyte degradation mechanisms are strongly influenced by electrode composition and additive chemistry, with oxidative degradation pathways dominating. Together, these findings provide rare empirical insight into the evolving formulation strategies of electrolytes in commercial LIB, still employing classic carbonates and LiPF6, but highlighting a trend toward safer, more robust, and sustainable electrolyte architectures by using synergistic multifunctional systems. KW - Mass Spectrometry KW - Lithium-ion batteries KW - Electrolyte degradation PY - 2026 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-656254 DO - https://doi.org/10.1016/j.jpowsour.2026.239739 SN - 0378-7753 VL - 673 SP - 1 EP - 13 PB - Elsevier B.V. AN - OPUS4-65625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Böttcher, Nils T1 - Kick-off LiBaTra - WP4: Safety Tests N2 - Die BAM ist Projektpartner im vom BMWE geförderten Verbundvorhaben LiBaTra („Lithium-Ionen-Batterie Transport und sichere Deaktivierung für das Recycling“). Weitere Projektpartner neben der BAM sind die Universität Braunschweig mit dem iPAT (Institut für Partikeltechnik) sowie die Firmen Siemens Energy SE sowie No Canary. Die BAM bearbeitet das Teilvorhaben „Risikobestimmung tiefenentladener Energiespeicher“ (FKZ: 03EI6145A-D). Die Präsentation gibt die wesentlichen Arbeitsinhalte des Teilvorhabens der BAM wieder. T2 - Kick-off Meeting des Verbundvorhabens LiBaTra CY - Online meeting DA - 17.02.2026 KW - Auswirkungsbetrachtungen KW - Elektrische Energiespeicher KW - Lithium-Ionen-Batterie KW - Stationäre Energiespeicher KW - Thermisches Durchgehen PY - 2026 AN - OPUS4-65657 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Geburtig, Anja A1 - Wachtendorf, Volker A1 - Falkenhagen, Jana T1 - Combined impact of UV radiation and nitric acid on high‐density polyethylene containers as a laboratory test N2 - In a laboratory test, transparent high‐density polyethylene (HDPE) jerrycans have been exposed to both UV radiation and 55 wt‐% nitric acid solution at (41 ± 2)°C, for up to 20 days. For comparison, UV radiant exposure (21 days) and nitric acid exposure (up to 6 weeks) were performed separately, at nearly equal temperatures. The damages are compared with FTIR spectroscopy in ATR and HT‐gel permeation chromatography(GPC) on a molecular level and with hydraulic internal pressure testing as a component test. For the used jerrycans, relevant oxidation can only be found after the combined exposure. This is caused by the decomposition of nitric acid into nitrous gases by UV radiation, which is also observed at lower concentrations (28 wt‐%). After 6 days of laboratory exposure, this is rated as critical, which corresponds to about 1/10 year in Central Europe, according to the UV radiant exposure. The gradual increase in oxidative damage shows the reproducibility of the test. KW - Molecular mass distribution KW - High-density polyethylene KW - Nitric acid KW - UV radiation PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-550141 DO - https://doi.org/10.1002/pts.2673 SN - 0894-3214 VL - 35 IS - 10 SP - 729 EP - 735 PB - Wiley CY - New York, NY AN - OPUS4-55014 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Jaeger, Carsten T1 - Untargeted Analysis of Leachables Released from Recycled Polyethylene Canisters N2 - Recycling existing materials and products as far as possible is an integral part of the circular economy. Plastic-based packaging, including containers for food and beverages but also for storing and transporting chemicals and dangerous goods, are presently made to a wide range from fossil resources. However, even for these “contact sensitive” products, there is still the aim of sustainability using recycled materials. For packings for the transport of dangerous goods, safety characteristics of the containments made from the “virgin” materials including polyethylene (PE) are well known and tested within the frame of their design type approval. Much less, however, is known about their counterparts made from recycled materials. Apart from material weaking, incorporation of residues into recycled plastics can cause contamination of the goods inside the packaging. To fill this gap, we have evaluated high-density PE (HDPE) canisters made from post-consumer waste towards release of plastic additives and contaminants such as residues from former contents. Using a comprehensive untargeted high-resolution mass spectrometry (HRMS) approach as well as thermal extraction-desorption gas chromatography-mass spectrometry (TED-GC/MS), we detected up to 870 distinct components depending on the type of stored chemical and storage duration. Most of the components were unique to or released in significantly higher amounts from recycled HDPE compared to conventional HDPE. 129 of the components could be identified and analyzed for functional use. The analysis revealed “cosmetics”, “fragrance” and “flavoring” as major associations next to known and expected uses in the field of “plastics”, indicating significant introduction of foreign contaminants into the product. We present details on the compound classes involved and discuss consequences for political targets on increasing recycling rates in this product segment. T2 - International Conference on Non-Target Screening CY - Erding, Germany DA - 13.10.2025 KW - Extractables KW - Leachables KW - Untargeted analysis KW - Recycling KW - Polyethylene PY - 2025 AN - OPUS4-65742 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -