TY - THES A1 - Ecker, Melanie T1 - Development, Characterization and Durability of Switchable Information Carriers based on Shape Memory Polymers N2 - The aim of this thesis was the development of switchable information carriers based on shape memory polymers (SMPs) and the investigation of their durability. Deployed as a new kind of security label, such technology may be an effective tool to prevent counterfeiting and product piracy. Thermoplastic as well as thermoset SMPs turned out to be applicable as a specific substrate for the fabrication of switchable information carriers. In particular, a physically cross-linked and semi-crystalline poly(ester urethane) (PEU), and a chemically cross-linked epoxy-based polymer were investigated. Both SMPs were able to undergo distinct changes in shape upon triggering, which is commonly known as the shape memory effect (SME). A key step for the fabrication of switchable information carriers was the development of a suitable technique for a surface-specific coloring of the polymeric base material. In particular, it was necessary to have a thin coat of paint in order to assure sufficient surface contrasts within the subsequently laser-engraved barcodes (e.g. quick response (QR) codes). In detail, coloring was conducted by diffusion of staining solutions, based on organic dyes, into the polymeric matrix. As a result of properly selected exposure times, homogenous layers of paint having thicknesses of about 100 μm, could be produced. In order to obtain room temperature stable, temporary shapes with non-decipherable code information, various programming procedures were applied to the information carriers. These were either based on tensile or on compressive deformation. For instance, when using plane steel plates in the course of compressive deformation, code areas were randomly distorted. By contrast, selective distortions could be achieved using a steel ball type indenter. However, the triggering of the SME resulted in almost complete shape recoveries. As a result, the information carriers could reliably be switched back to readable states. Before the developed information carriers can be brought onto the market, it is important to evaluate their durability against various environmental impacts. Artificial weathering was conducted exemplarily on blue and black colored QR code carriers based on PEU. Various scenarios were selected: exposure to UVA irradiation and aging in aqueous solution. In both cases, the durability was investigated at temperatures below and above the switching temperature of the employed SMP. It turned out, that the limiting factor for the usage of switchable information carriers was a lack of contrast and thus was dye-related. In the case of UV irradiation, the color of the dyes started fading, culminating in unreadable QR codes. For hydrolytic degradation, the non-colored code regions were stained in the course of aging. This originates from the fact that the organic dyes used for coloring were soluble in water. As a consequence, they were able to diffuse easily in and out of the swollen polymeric matrix. For both scenarios, aging at elevated temperature caused acceleration of the observed effects. However, the shape memory properties of the PEU were only slightly influenced by the applied aging scenarios. Next, an additional thermo-responsive security feature was added to the information carriers. Therefore, thermochromic pigments (T-PIGs) were embedded into a PEU matrix. However, in contrast to the organic dyes, the size of the thermochromics microcapsules was too large to diffuse into the polymeric matrix. Thus, another procedure for a surface-specific coloring of the PEU was developed. This mainly included the preparation of a PEU-paste doped with T-PIG by solution mixing. The thermochromic paste was deposited by means of a solvent casting technique as thin layer atop the PEU plaque. After solvent evaporation, tightly connected PEU/PEU-T-PIG laminates were obtained. Beyond that, the layer thickness was adjustable by using a doctor blade for the paste deposition. Subsequent laser ablation finalized the QR code carriers. These were readable at room temperature, but unreadable above the color switching temperature of the employed T-PIGs due to a lack of contrast. Hence, the obtained multifunctional information carriers were characterized by distinct shape memory properties and tunable color switching performances. Furthermore, the combination of several T-PIGs having different colors and switching temperatures resulted in surfaces with multiple and unique temperature-dependent changes in color. Besides that, information carriers with temporarily concealed information could be obtained by covering the QR code with an additional layer doped with T-PIG. N2 - Ziel der Arbeit war es, schaltbare Informationsträger aus Formgedächtnispolymer (FGP) zu entwickeln, und diese auf ihre Beständigkeit gegenüber unterschiedlichen Umwelteinflüssen zu untersuchen. Eingesetzt als neuartige Etiketten könnten diese zur fälschungssicheren Kennzeichnung von Waren verwendet werden. Sowohl thermoplastische als auch duroplastische FGPs waren geeignete Ausgangsmaterialien für solche Informationsträger. Im Speziellen wurde sowohl ein physikalisch quervernetztes, semikristallines Poly(ester urethan) (PEU), als auch ein chemisch quervernetztes, amorphes FGP auf Epoxidbasis näher untersucht. Ein wichtiger Schritt für die Entwicklung von schaltbaren Informationsträgern aus FGP war die Entwicklung eines Färberverfahrens, bei dem das Polymer nur oberflächennah eingefärbt wird. So konnten ausreichend hohe Kontraste in den anschließend mittels Lasergravur eingebrachten Barcodes (z.B. QR engl. quick response Codes) erreicht werden. Die Färbung der Polymeroberflächen durch Diffusion von organischen Färbelösungen in die Polymermatrix stellte sich als probate Methode heraus. Dabei konnte die Eindringtiefe der Farbstoffe durch die Einwirkzeit auf etwa 100 μm eingestellt werden. Um die Informationsträger in stabile, temporäre Formen mit unlesbarer Information zu überführen, wurden unterschiedliche thermomechanische Programmierungsmethoden angewendet. Sowohl Druck- als auch Zugverformung stellten sich hierfür als geeignet heraus. In beiden Fällen waren die Informationen im programmierten Zustand aufgrund zu großer Verzerrungen der QR Codes unlesbar. Durch den Einsatz von konfigurierbaren Stempelwerkzeugen während der Druckverformung war es darüber hinaus möglich, selektive Verformung der Oberfläche zu erreichen. Nach dem Auslösen des Formgedächtniseffektes kehrten die Etiketten nahezu in ihre ursprüngliche Form zurück, sodass die Information dann in jedem Fall wieder lesbar war. Um die Haltbarkeit der neu entwickelten Informationsträger gegenüber Umwelteinflüssen besser beurteilen zu können, wurden gefärbte Etiketten aus PEU künstlich bewittert. Hierfür wurden zwei Alterungsszenarien gewählt: die Degradation durch UVA-Strahlung und die Beständigkeit in wässrigem Medium. In beiden Fällen wurde die Bewitterung unterhalb und oberhalb der Schalttemperatur des Polymers durchgeführt. Die UV-Alterung führte zum Ausbleichen der Farben und somit zum Verlust der Lesbarkeit durch die Abnahme des QR Code Kontrastes. Während der Alterung in Wasser wurden die anfangs ungefärbten Domänen innerhalb des QR Codes nach und nach gefärbt, was ebenfalls zu einem Kontrastverlust führte. Das rührte daher, dass die organischen Farbstoffe wasserlöslich waren und somit in das gequollene Polymer hinein- und hinausdiffundieren konnten. Lagerung bei erhöhter Temperatur führte in beiden Fällen zu einer Beschleunigung der beobachteten Phänomene. Im Gegensatz dazu wurde während der untersuchten Alterungszenarien die Formgedächtnis-Funktionalität des Polymers kaum beeinflusst. Anschließend wurden die Informationsträger mit einem weiteren thermoresponsiven Sicherheitsmerkmal kombiniert. Die hierfür verwendeten thermochromen Pigmente (T-PIGs) waren im Vergleich zu den vorher verwendeten Farbstoffen jedoch zu groß, um in die Polymermatrix hineinzudiffundieren. Daher wurde eine weitere Methode zur oberflächenspezifischen Einfärbung von Polymeren entwickelt. Hierzu wurde zunächst eine viskose PEU-Lösung hergestellt, die im Anschluss mit den T-PIGs vermengt wurde. Die so erhaltene Paste wurde mittels der sogenannten „solvent cast“ Technik als dünner Film auf die Polymeroberfläche aufgebracht. Dabei konnte die Schichtdicke durch den Einsatz eines „doctor blades“ eingestellt werden. Nach dem vollständigen Abdampfen des Lösungsmittels wurden fest verbundene PEU/PEU-T-PIG Laminate erhalten. Die anschließende Lasergravur führte zu Informationsträgern, die bei Raumtemperatur lesbar waren. Oberhalb der Farbumschlagstemperatur der eingesetzten T-PIGs wurden diese jedoch aufgrund von Kontrastverlusten unlesbar. Die so erhaltenen multifunktionalen Informationsträger waren demzufolge neben ihren Formgedächtniseigenschaften durch einstellbare, temperaturabhängige Farbänderungen charakterisiert. Darüber hinaus war es möglich, Informationsträger mit mehreren Farbumschlägen zu erhalten, indem T-PIGs mit unterschiedlichen Farben und Farbumschlagstemperaturen während der Herstellung eingesetzt wurden. In einem weiteren Szenario wurden Informationsträger mit einer Schicht aus thermochromer Paste überdeckt. Als Folge war der Barcode bei Raumtemperatur unter dieser Schicht verborgen und wurde erst beim Erwärmen oberhalb der Schalttemperatur sichtbar und lesbar. T3 - BAM Dissertationsreihe - 132 KW - durability KW - smart materials KW - Shape memory polymers KW - QR codes KW - thermochromism PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-5086 VL - 132 SP - 1 EP - 202 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-508 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Bleul, Regina T1 - Herstellung, Charakterisierung und Funktionalisierung polymerer Nanopartikel und Untersuchung der Wechselwirkungen mit biologischen Systemen N2 - Die Nanomedizin beschäftigt sich unter anderen mit der Frage, wie sich die Behandlung gefährlicher Krankheiten effizienter und sicherer gestalten lässt, deren konventionelle Therapie oftmals mit schweren Nebenwirkungen einhergeht. Die Vision ist, ein theranostisches Wirkstoffträgersystem zu schaffen, das seinen therapeutischen Cargo sicher an den Wirkort transportiert, dort freisetzt und gleichzeitig in Echtzeit verfolgt werden kann, um die Therapie individuell anzupassen. Die Grundlage für die erfolgreiche Entwicklung eines Wirkstoffträgersystems bilden Untersuchungen zum Verhalten von nanopartikulären Substanzen in physiologischer Umgebung. Im Rahmen der vorliegenden Arbeit wurden polymere Nanopartikel unterschiedlicher Morphologie durch die kontrollierte Selbstorganisation amphiphiler Blockcopolymere hergestellt, charakterisiert und auf ihre Wechselwirkungen mit menschlichen Zellen und Serumproteinen untersucht. Dazu wurde eine Studie zur Geometrie- und Größenabhängigkeit der Zytoxizität von nanoskaligen Kugel- und Zylindermizellen sowie Vesikelstrukturen durchgeführt. Des Weiteren wurde das Agglomerationsverhalten von verschiedenen polymeren Nanopartikeln in Anwesenheit von Serumproteinen untersucht. Mit Hilfe eines Mikromischer-basierenden Verfahrens gelang es, kontinuierlich sehr einheitliche Polymervesikel herzustellen und diese in situ mit unterschiedlichen Komponenten zu beladen - unter anderem mit dem Wirkstoff Camptothecin sowie einer hohen Dichte an hydrophoben Eisenoxid-Nanopartikeln. Diese wirkstoffbeladenen Hybridvesikel zeigten in vitro im Vergleich zum freien Wirkstoff eine erhöhte zytotoxische Wirksamkeit gegen die Krebszelllinie PC-3. Nach einer Funktionalisierung mit einem krebszellspezifischen Targeting-Peptid und einer zusätzlichen Fluoreszenzmarkierung wurde mit Hilfe der Durchflusszytometrie und konfokalen Laser-Scanning-Mikroskopie eine rezeptor-spezifische Zellaufnahme in PC-3-Krebszellen demonstriert. Messungen zur magnetischen Charakterisierung bestätigten zudem die potenzielle Anwendung magnetischer Polymervesikel als MRT-Kontrastmittel wie auch als Tracer für das Magnetic Particle Imaging (MPI). Kontinuierlich hergestellte, wirkstoffbeladene, magnetische Polymervesikel erfüllen somit viele Grundvoraussetzungen für ein theranostisches Wirkstoffträgersystem und bieten weitere Entwicklungsmöglichkeiten im Hinblick auf Magnetfluid-Hyperthermie, magnetisches Targeting oder eine durch ein Magnetfeld induzierte Wirkstofffreisetzung. N2 - One of the main goals of nanomedicine is to improve the treatment of hazardous diseases whose conventional therapy often has serious side effects. The vision is to create a theranostic drug delivery system which is capable of safely transporting therapeutic cargo through the body to a targeted site of disease at which point the drug is released. Furthermore, it is desirable to track the carrier in real time which would allow for a personal adjustment of the therapy. Studies on the behavior of nanoparticulate substances in a physiological environment form the basis for the possibility to successfully develop a drug carrier system. In the present work, polymeric nanoparticles with different morphologies were prepared by the controlled self-assembly of amphiphilic block copolymers. The nanoparticles were subsequently characterized and their interactions with human cells and serum proteins investigated. A cytotoxicity study with spherical and cylindrical micelles as well as vesicular structures was carried out and showed a dependency of cytotoxic effects on the geometry and size of the nanoparticles. The agglomeration behavior of various polymeric nanoparticles in the presence of serum proteins was also studied. Highly uniform polymeric vesicles were continuously manufactured in a micromixer based device and in situ loading with different components was performed. In this way, dual loaded vesicles with the anticancer drug camptothecin and a high amount of hydrophobic iron oxide nanoparticles were produced. When tested in vitro, these drug-loaded vesicles showed an increased cytotoxic activity against the cancer cell line PC-3 when compared to the free drug. Specific cellular uptake in PC-3 cancer cells was demonstrated with flow cytometry and confocal laser scanning microscopy after functionalization with a cancer cell specific targeting peptide and an additional fluorescent label. Magnetic characterization of the iron oxide-loaded vesicles also confirmed the potential application as MRI contrast agents and as tracers for magnetic particle imaging (MPI). Continuously manufactured, drug-loaded, magnetic polymeric vesicles thus fulfill many prerequisites for a theranostic drug carrier system and provide opportunities for further developments in the field of magnetic fluid hyperthermia, magnetic targeting or magnetic drug release. T3 - BAM Dissertationsreihe - 133 KW - Selbstorganisation KW - Nanomedizin KW - Wirkstoffträgersystem KW - Krebstherapie KW - Theranostik PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-5134 VL - 133 SP - 1 EP - 238 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-513 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Wettmarshausen, Sascha T1 - Hoch selektive Polyolefin-Oberflächenfunktionalisierung in bromenthaltenden Niederdruckplasmen: Untersuchungen zur Pfropfung, Umfunktionalisierung und Verbesserung der Hafteigenschaften in Metall-Polymer-Verbunden N2 - Selektiv funktionalisierte Oberflächen von Polyolefinen sind für verschiedenste Einsatzgebiete wie Adhäsions-, Chemie-, Medizin- und Biotechnik von großem Interesse. Eine Möglichkeit Polymeroberflächen effizient zu funktionalisieren ist, diese durch eine plasmaphysikalisch angeregte Gasphase unter Einsatz geeigneter Präkursoren chemisch zu modifizieren. Im Rahmen der vorliegenden Arbeit wurde die Wirkung bromhaltiger Gasphasenplasmen, die Bromoform, Allybromid oder tert-Butylbromid enthielten, auf Polyethylen (PE) und Polypropylen (PP) untersucht. Überraschenderweise wurde hierbei eine hochselektive und hochdichte monosortige Br-Funktionalisierung beobachtet. Um die für diese hohe Selektivität verantwortlichen Prozesse zu untersuchen, wurden analoge halogenhaltige Plasmen, die Tetrafluormethan, Fluoroform, Chloroform, Bromoform und Diiodmethan enthielten, auf ihre chemische Selektivität, ihre Funktionalisierungseffizienz und ihr Ionisationspotential und Elektronentemperatur charakterisiert. Es wurde untersucht, ob die Halogenidfunktionalität als CX oder als C-CXn-Gruppe an der Oberfläche gebildet wird. Für die Bewertung der Langzeitstabilität der Funktionalisierung wurde die Nachoxidation der plasmamodifizierten Polymeroberflächen kontrolliert. Im Anschluss wurde die Umsetzbarkeit mit systematisch variierten organischen Verbindungen bestimmt. Ziel hierbei war zu untersuchen, wie gut sich die Bromidfunktionalität als universelle Abgangsgruppe zur Kopplung flexibilisierender Spacer- Moleküle in der Metall-Polymer-Grenzfläche eignet. Es wurden dazu Kopplungsreaktionen mit unterschiedlich langen und steifen endständigen Alkohol-, Amin- und Glykol- Verbindungen durchgeführt. Darüber hinaus wurden Umfunktionalisierungsreaktionen an bromierten Oberflachen durchgeführt. Auf diese Weise konnte gezeigt werden, dass es möglich ist, die C-Br- Funktionalität gegen eine andere auszutauschen. Spezielles Augenmerk wurde auf die Umfunktionalisierung zu primären Aminogruppen gelegt. Diese wurden über einfache Substitutionsreaktionen mit konzentriertem oder verflüssigtem Ammoniak erzeugt. Auch oberflachengebundene Hydroxylgruppen konnten erzeugt werden. Dazu wurden Bromidfunktionen durch Substitution mit Kalium- und Natriumhydroxid in geeigneten Lösungsmitteln umgesetzt. Polypropylenoberflächen, die mit verschiedenen Spacern ausgerüstet worden waren, wurden im Vakuum mit dünnen Filmen aus Aluminium und Kupfer bedampft. Die Haftfestigkeit dieser Beschichtung wurde anschließend durch Schalfestigkeitsmessungen untersucht. N2 - Selectively functionalized polyolefine surfaces are essential for many applications in adhesion, chemistry, medicine and biotechnology. To provide polymer surfaces with special functionalities it is necessary to treat them with according precursors in plasma. In this work polypropylene (PP) and polyethylene (PE) were exposed to bromine containing (bromoform, allylbromide, tert-butylbromide) plasmas. Surpisingly, the bromination appeared as high selective and formed high dense C-Br groups at the polyolefin surface. Halogen containing plasmas like tetrafluormethane, fluoroform, chloroform, bromoform and diiodinemethane were compared with regard to their selectivity, yield as well as ionisation potential and electron temperature of the corresponding plasma. It was also analysed if the halogens are bonded as C-X or C-CXn-fragments onto the surface. Moreover, the post-plasma oxidation stability was also investigated. Subsequently the brominated polyolefine surfaces were allowed to react with different organic compounds. The aim was to demonstrate the universality of the C-Br group for attaching of any OH and NH2 functional group containing molecule. Terminal alcohol, glycols and amines are used. Especially, flexibilizing spacers within the metal-polymer interface of different length, stiffness and functionality were introduced. Besides grafting of spacers it was also shown that it is possible to change the functionality of the surface. Concentrated or liquid ammonia should produce primary amino groups through a simple substitution. Hydroxyl groups were formed by hydrolysis using potassium hydroxide and sodium hydroxide in different solvents. The different grafted polypropylene surfaces were brought into vacuum and were metalized with copper or aluminium. The thus produced metal-polymer composite was then tested on the peel strengths of the evaporated metal film. T3 - BAM Dissertationsreihe - 48 KW - Plasma KW - Pfropfung KW - Funktionalisierung KW - Bromierung KW - Polymere PY - 2009 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-1100 SN - 978-3-9812910-4-9 SN - 1613-4249 VL - 48 SP - 1 EP - 139 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-110 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Jagst, Eda T1 - Surface Functional Group Characterization Using Chemical Derivatization X-ray Photoelectron Spectroscopy (CD-XPS) N2 - Ziel dieser Arbeit war die Charakterisierung und Quantifizierung von Aminofunktionalitäten auf Oberflächen mittels der Analyseverfahren Röntgen-Photoelektronenspektrometrie (XPS) und Röntgen-Absorptionsspektrometrie (Analyse der Feinstruktur an der Absorptionskante, NEXAFS). Die Oberflächen wurden durch Spincoating, Selbstassemblierung oder Plasmapolymerisation hergestellt und die primären Aminogruppen mit den dafür oft genutzten Markern PFB und TFBA derivatisiert. Die Gasphasenderivatisierungen mittels PFB und TFBA wurden auch genutzt, um Reaktionsverhalten, Reaktionszeit und die resultierenden spektroskopischen Unterschiede genauer zu ermitteln. In nasschemischen Untersuchungen reagierten abgeschirmte Amine mit PFB und TFBA unterschiedlich stark mit Ausbeuten von 78- 89%, was als maximale Ausbeute der Oberflächenderivatisierung in der Gasphase angesehen wird. Die Dünnschichtfilme wurden mittels Spin coating von 4,4’-Methylen-bis(2,6-diethylanilin) auf Si-Wafern hergestellt und reagierten bei 50 ºC mit den Markern. Die Sättigungszeit betrug in beiden Fällen 15 min. Die XPS Messungen zeigten die erfolgreiche Umsetzungen durch das Auftreten eines neuen CF3- bzw. C-F-Signals und einen BE-Verschiebung der entsprechenden C=N-Gruppe. In Übereinstimmung mit den XPS-Daten, zeigen die NEXAFS-Spektren eine Scharfe π*(C=N) Resonanz und die CF3 bzw. C-F Resonanz in der σ*-Region. Die Ausbeuten der Reaktionen wurden aus den Komponenten-Flächen der hochaufgelösten XP N1s Spektren und aus den [F]/[N]-Verhältnissen berechnet. Stöchiometrie und XP-Übersichtsspektren dienten zur Bestimmung der Aminofunktionalitäten an den Oberflächen. Die Resultate waren konsistent und zeigten eine Ausbeute von 80- 90% für PFB und 60-70% für TFBA. Für die Untersuchung von selbstorganisierenden Monoschichten (SAMs) mit unterschiedlichen Funktionalitäten wurden spektroskopische Daten von aliphatischen und aromatischen SAMs mit denen von Si-Wafern, welche mit Polyallylamin und 4,4’-Methylenbis(2,6-diethylanilin) beschichtet wurden, verglichen. Die Orientierung der Monoschichten wurde mittels der winkelaufgelösten NEXAFS an der C K-Kante bestimmt. Die scharfen Signale im Differenzspektrum zeigen eine erfolgreiche Orientierung der Bindungen bzw. funktionellen Gruppen und resultieren aus der Polarisationsabhängigkeit der NEXAFS-Resonanzen an relevanten Molekülorbitalen. Die Gasphasen-Oberflächenderivatisierungen von zwei SAMs mit Aminofunktionalitäten (4-Aminophenylbutan-1- thiolat und 11-Amino-1-undecanthiol) wurden untersucht. Für eine Zeit von 90 min. wurde 4-Aminophenylbutan-1- thiolat mit TFBA bzw. 11-Amino-1-undecanthiol mit PFB bei RT umgesetzt. Die stöchiometrischen Daten der Umsetzungen waren in Übereinstimmung mit den Elementkonzentrationen, welche sich aus den XPS-Daten ableiten ließen. Die Ausbeuten wurden mit Hilfe der N1s-Spektren berechnet und betrugen 60-80%. Da für eine aussagekräftige NEXAFS-Messung eine gewisse Anzahl von Spektren aufgenommen werden muss, steigt die Gefahr der Schädigung der Probe durch Strahlung. Aus diesem Grund wurde ein 11-Amino-1-undecanthiol-Film auf Au für 1 h mit weichem Röntgenlicht bestrahlt und die spektroskopischen Unterschiede an der C und N K- Kante untersucht. Es zeigte sich kein signifikanter Unterschied für die N K-Kante, allerdings erhöhten sich die Intensitäten der C=C und C=N-Spezies im C K-Kanten-Spektrum, was für einen Strahlenschaden spricht. Mittels Allylamin als Plasmagas und Si-Wafern wurden plasma-chemisch abgeschiedene Allylaminfilm Oberflächen hergestellt und untersucht. Der Einfluss der externen Plasmaparameter (Duty Cycle, Plasmaleistung und Druck des gasförmigen Monomers im Reaktor) auf den chemischen Charakter des abgeschiedenen Films wurde im Detail analysiert. Die anschließenden Gasphasen-Oberflächenderivatisierungen mit TFBA und PFB zeigten Nebenreaktionen. C-F- Bindungsbruch und HF-Abspaltung führten zu einem zusätzlichen Signal im XP F1s Spektrum. Oberflächen, welche mit PFB derivatisiert wurden, zeigten einen höheren Anteil von C-F-Bindungsbrüchen, da an fluorierten aromatischen Molekülen leicht nukleophile aromatische Substitutionen stattfinden. Potentielle Schäden durch Röntgenstrahlung wurden mittels TFBA derivatisierter Proben, welche für 10 h der Strahlung ausgesetzt wurden, studiert. Es zeigte sich eine Abnahme der Fluorgehalte an der Oberfläche, allerdings hat dieser Effekt aufgrund der kurzen Messzeiten praktische keine Auswirkung bei der Datenerfassung. Da die HF-Abspaltung auf TFBA- Oberflächen prozentual geringer ist, wurde es als Marker für alle weiteren Kupplungsreaktionen genutzt. Eine Serie von Proben, welche bei einer Plasmaleistung von 20W, 0,5 Duty Cycle und einem Druck von 15 Pa derivatisiert wurden, zeigten eine Sättigungszeit von 90 min. Bei variierenden Plasmabedingungen wurden die unterschiedlichen [CF3]-Flächenprozent in den hochaufgelösten XP C1s Spektren miteinander verglichen. Duty Cycle, Plasmaleistung und Druck zeigten identische Trends in der Retention der Aminogruppen. Grundsätzlich führt die Anwendung von harten Plasmabedingungen, d .h bei hoher effektiver Plasmaleistung, zu Filmen mit einer vergleichsweisen geringen Retention der Aminofunktionalitäten. Darüber hinaus sind diese Filme stark vernetzt bzw. verzweigt. Eine hohe Anzahl ungesättigter Kohlenstoffspezies ist ebenfalls typisch. In Abhängigkeit von den XPS-Daten wurden für die Quantifizierung der Aminogruppen an der Oberfläche die Methoden QEA (Quantitative Elementar-Analyse) und PFA (Peak Fit Analyse) genutzt. Die Berechnungen wurden mittels Youden-Plot verglichen und zeigten keine Abweichung voneinander. NEXAFS wurde zusätzlich genutzt, um den Einfluss der Plasmaparameter auf die Aminogruppen zu studieren, da die Methode empfindlich gegenüber ungesättigten Spezies ist. Eine Zunahme der Fragmentationsraten bei Veränderungen in den Plasmaparametern konnten aus Intensitätsveränderungen in den NEXAFS C K-Kanten Spektren abgeleitet werden. Ein Ringversuch für die Bestimmung von Hydroxylgruppen auf mit Plasma behandelten Oberflächen wurde ebenfalls durchgeführt. Dafür wurde eine Polypropylenfolie, welche Sauerstoffplasma bei 100 W für 90 s ausgesetzt wurde, mit TFAA derivatisiert. Die Oberfläche wurde mittels XPS untersucht und der [OH]-Gehalt mittels QEA und PFA bestimmt. Die Methoden zeigten eine Abweichung von 33% voneinander. CD-XPS wurde erfolgreich zur Bestimmung unterschiedlicher Funktionalitäten auf Dünnschichtfilmen eingesetzt. Allerdings bedarf es für den Erhalt von in sich konsistenten Datensätzen einer validierten Derivatisationsprozedur, die in jedem Labor angewendet werden muss. Die verwendete Hardware und die Peak-Fitting-Prozeduren bei XPSUntersuchungen müssen ebenfalls im Detail beschrieben werden. Die Inhomogenitäten und eventuelle Strahlungsschäden führen zu Abweichungen in den erhaltenen Resultaten. Die gemessene Schichtdicke muss auch für konsistente Ergebnisse optimiert werden. Dünnere Schichten führen zu weniger Hintergrundrauschen. Die erfolgreich durchgeführten Derivatisierungsreaktionen zeigten die Verfügbarkeit der Aminogruppen an der Oberfläche. In einem nächsten Schritt können an diese Funktionalitäten z.B. Stammzellen oder DNA gekoppelt werden, was hochinteressant in Hinblick auf potentielle biologische Anwendungen ist. N2 - Different amino group carrying surfaces, prepared by spin coating, self-assembly and plasma polymerization, were successfully investigated by XPS and NEXAFS. Amino groups were derivatized with the widely used primary amino group tags, PFB and TFBA, prior to analysis. Primary amino group quantification was then carried out according to the spectroscopic data. The gas-phase derivatization reactions of PFB and TFBA were also studied in order to understand their reaction behaviour, the spectral differences they cause and the time required for reaction completion. For the determination of maximum reaction yields of gas-phase surface derivatizations, a set of liquid-phase derivatization reactions was carried out. The selected amino compounds with a different degree of steric hindrance were reacted with PFB and TFBA. The yields (78-89%) were accepted as the upper limit of the gas- phase surface derivatizations. Thin films were prepared by spin coating of 4,4’-methylenebis(2,6-diethylaniline) on Si wafers and were reacted with the markers at 50ºC. The saturation time was found to be 15 min. for both reactions. XPS measurements showed the formation of a CF3 or C-F peak and a BE shift of the corresponding C=N group indicating a successful reaction. The NEXAFS results supported the XPS data by showing a sharp π*(C=N) resonance. The CF3 and C-F resonances were observed in the σ* region. The yields of the reactions were calculated from the component areas of the high resolution XP N1s spectra and from the [F]/[N] ratios. The surface amino groups were calculated from the stoichiometry and from the XP survey scans. The results were consistent with each other and showed a yield of 80-90% for PFB and 60-70% for TFBA. Self-assembled monolayers (SAMs) of different terminal groups were prepared and investigated with XPS and NEXAFS. The spectral properties of aliphatic and aromatic SAMs were compared to the reference surfaces of poly(allylamine) and 4,4’-methylenebis(2,6-diethylaniline) spin coated on Si wafers. NEXAFS was used to determine the orientation of SAMs. An angle resolved NEXAFS was applied at the C K-edge in order to prove a successful SAM deposition on Au. The intense peaks in the difference spectra are due to the polarization dependence in the orbital responsible for the NEXAFS resonance showing a successful bond/functional group orientation. The gas-phase surface derivatization of two amino terminated SAMs, 4-aminophenylbutane-1-thiolate and 11- amino-1-undecanethiol, were studied. 4-aminophenylbutane-1-thiolate was derivatized with TFBA whereas 11- amino-1-undecanethiol with PFB at room temperature for 90 min. The stoichiometrical data were compared to the atomic percentages obtained from the XPS spectra and the results were consistent with each other. The yields of the reactions (60-80%) were obtained from the high resolution N1s spectra. Since a certain number of spectra had to be acquired to reach reasonable S/N ratios, a considerable danger of beam damage in the NEXAFS measurements occurs. The potential radiation damage effects on the C and N K- edge of 11-amino-1-undecanethiol film on Au was studied. The spectral differences before and after 1 h radiation exposure were investigated. The intensities of resonances related to unsaturated species such as C=C and C=N were increased for the C K-edge spectra. The NEXAFS N K-edge spectra of 11-amino-1-undecanethiol film showed no significant irradiation effect. Plasma deposited allylamine samples were successfully investigated by XPS and NEXAFS. Primary amino group quantification on plasma deposited allylamine surfaces was carried out by derivatization after plasma deposition. TFBA and PFB showed side reactions when plasma polymerization was used. Due to the radical mechanisms, C- F bond cleavages followed by HF releases occurred resulting in a second peak formation in XP F1s spectra. PFB derivatized surfaces suffer more from the C-F bond cleavage since fluorinated aromatic molecules are highly susceptible to nucleophilic aromatic substitution. Potential X-ray beam damage of TFBA was studied by a 10 h XPS measurement and showed a fluorine degradation. Due to the short measurement times, X-ray beam damage can be neglected. Since HF release on the TFBA surfaces are lower in percentage, it was used as the marker reagent for the coupling reactions. A series of samples deposited at 20W, 0.5 duty cycle and 15 Pa were derivatized to determine the time required for saturation (90 min.). Plasma polymerized allylamine samples with different duty cycle, power and pressure values were prepared in order to study the effects of external plasma parameters on the primary amino group retention. The [CF3] area percentages, obtained from the high resolution XP C1s spectra, vs. plasma parameter variations were compared. Duty cycle, power and pressure variation experiments showed the same trend on amino group retention. The more the plasma conditions move from mild to hard, the more rearrangements occur on the surface. Milder plasma conditions promote the retention of amino groups originating from the allylamine monomer. QEA (Quantitative Elemental Analysis) and PFA (Peak Fit Analysis) methods were used for the quantification of surface amino groups, depending on the XPS data. The results of two data evaluation methods were compared by using a Youden plot showing no deviation. NEXAFS was used along with XPS in order to study plasma parameter effects on amino groups. As being sensitive against unsaturated moieties, NEXAFS was successfully applied to plasma deposited allylamine surfaces. An increase in fragmentation rate due to a variation in plasma parameters was followed by intensity changes in NEXAFS C K-edge spectra. An inter-laboratory comparison of hydroxyl group determination on plasma surfaces was carried out. Hydroxyl groups on polypropylene foil, treated with oxygen plasma at 100 W for 90 s, were coupled with TFAA. The surfaces were investigated with XPS and the [OH] amount on the surfaces was calculated by QEA and PFA methods showing a 33% deviation between the two methods. CD-XPS is applied successfully in order to determine different functional groups on the thin film surfaces. However, a validated derivatization procedure, which can be easily applied in each lab, should be established. The used hardware and the peak fitting procedures of XPS should be defined in detail for the validation. The sample inhomogeneity and the effects of beam damage play a role on the deviations of the results. The surface thickness should be optimized for consistency. By the derivatization reactions, the surface amino groups are successfully quantified. As the next step, the studied surfaces can be used for potential biological applications, such as coupling the available amino groups with DNA or stem cells. T3 - BAM Dissertationsreihe - 69 KW - functional group KW - photoelectron spectroscopy KW - surface analysis KW - Organic surface KW - plasma modification PY - 2011 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-893 SN - 978-3-9813853-4-1 SN - 1613-4249 VL - 69 SP - 1 EP - 129 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-89 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Pawlowski, Kristin Helga T1 - Wirkungsmechanismen von Bisphenol-A-bis(diphenylphosphat) als Flammschutzmittel in Polycarbonat / Acrylnitril-Butadien-Styrol-Copolymerisat N2 - Die Suche nach halogenfreien Flammschutzmitteln für Polycarbonat / Acrylnitril- Butadien-Styrol-Copolymerisat (PC/ABS) führte zur Entwicklung von Triphenylphosphat (TPP), Resorcinol-bis(diphenylphosphat) (RDP) und Bisphenol-A- bis(diphenylphosphat) (BDP). Das unvollständige Wissen über die genauen Wirkungsmechanismen dieser Arylphosphate erschwert jedoch eine gezielte Optimierung der Systeme. In der vorliegenden Arbeit wurden die verschiedenen Flammschutzmechanismen von BDP in PC/ABS aufgeklärt. Ein Vergleich zwischen BDP mit RDP und TPP wurde gezogen und der Einfluss weiterer Additive wie Polytetrafluorethylen (PTFE), Böhmit, Zinkborat und Talk auf das Flammschutzverhalten von BDP herausgearbeitet. Dazu wurde das thermische Abbauverhalten mittels TG und TG-FTIR aufgeklärt. Die Entflammbarkeit wurde mit LOI- und UL 94-Tests bestimmt und das Brandverhalten anhand von Messungen im Cone Calorimeter bei unterschiedlichen Bestrahlungsstärken bewertet. Die Verbrennungsrückstände wurden mittels Festkörper-FTIR und Festkörper-NMR-Messungen charakterisiert. BDP wirkt in PC/ABS in der Gasphase durch Flammenvergiftung und in der festen Phase als Vernetzungsinitiator von PC. PTFE beeinflusst das Fließverhalten der Polymerschmelze und ermöglicht so die beste Klassifizierung im UL 94-Test von PC/ABS mit BDP. BDP ist thermisch stabiler als RDP und TPP und deshalb am aktivsten mit PC in der festen Phase. Böhmit verursacht durch eine H2O-Freisetzung Hydrolysereaktionen und wirkt somit leicht antagonistisch bezüglich der Festphasenaktivität von BDP. Zinkborat reagiert mit BDP zu alpha-Zinkphosphat und Borphosphat und unterdrückt so die Wirkung von BDP als Flammenvergifter und Vernetzungsinitiator. Die Zugabe von Talk bewirkt eine Verstärkung des Rückstandes, hat aber einen antagonistischen Effekt bezüglich der Gasphasenaktivität von BDP. Die Ergebnisse dieser Arbeit liefern ein detailliertes Verständnis der Flammschutzmechanismen von BDP und deren Abhängigkeit von der physikalischen und chemischen Umgebung. Mit diesem Wissen kann die Weiterentwicklung von BDP und anderen Arylphosphaten als Flammschutzmittel in PC/ABS gezielt optimiert werden. N2 - The search for halogen-free flame retardants for polycarbonate/acrylonitrile-butadiene- styrene (PC/ABS) has led to the development of triphenylphosphate (TPP), resorcinol bis(diphenyl phosphate) (RDP) and bisphenol A bis(diphenyl phosphate) (BDP).The lack of knowledge about the detailed flame retardant mechanisms of those arylphosphates makes it difficult to optimize those systems. In this thesis, the various flame retardancy mechanisms of BDP in PC/ABS have been clarified. BDP was compared to RDP and TPP and the influence of further additives (Polytetrafluoroethylene (PTFE), boehmite, zinc borate and talc) on the mechanisms of BDP were revealed. The thermal decomposition behaviour was clarified by means of TG and TG-FTIR. The flammability was determined by LOI and UL 94. The fire behaviour was evaluated by cone calorimeter measurements with different irradiations. Combustion residues were characterized by means of solid-state-FTIR and solid-state-NMR. BDP acts in PC/ABS as a flame inhibitor in the gas phase and as an initiator of cross linking in the condensed phase. PTFE influences the dripping behaviour of the polymer melt and enables PC/ABS + BDP to achieve the best classification in UL 94. BDP is thermally more stable than RDP and TPP and hence the most active flame retardant in the condensed phase. Boehmite releases water, which causes hydrolysis. This has an antagonistic effect concerning the condensed phase action of BDP. Zinc borate reacts with BDP to form alpha-zinc phosphate and borophosphate and suppresses the mechanisms of BDP as flame inhibitor and cross linking initiator. Talc stabilizes the char, but has an antagonistic effect on the gas phase action of BDP. The results gained from this thesis give a detailed understanding about the flame retardancy mechanisms of BDP and their dependence on the physical and chemical environment. They are fundamentals for a continuing development and improvement of aryl phosphates as flame retardants in PC/ABS. T3 - BAM Dissertationsreihe - 33 KW - PC/ABS KW - Entflammbarkeit KW - Pyrolyse KW - Acrylphosphate KW - Flammschutzmittel PY - 2008 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-1250 SN - 978-3-9812072-3-1 SN - 1613-4249 VL - 33 SP - 1 EP - 117 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-125 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Perret, Birgit T1 - Neuartige halogenfreie Flammschutzmittel für schnell härtende Epoxidharzsysteme und deren kohlefaserverstärkte Komposite in Automobilbau und Luftfahrt N2 - Phosphorhaltiger Flammschutz als effektive halogenfreie Alternative in Epoxidharzen rückt immer mehr in den Blickpunkt des Interesses. Oft werden kommerzielle additive Flammschutzmittel verwendet, die zu Einbußen vor allem in der Mechanik führen. Zusätze, wie Kohlefasern beeinflussen die Wirkungsmechanismen und Effektivitäten der Flammschutzmittel zusätzlich. Der Anteil an optimal an die Epoxidharzmatrix angepassten additiven Flammschutzmitteln ist bisher gering, da ein tieferes Verständnis von Struktur-Eigenschaftsbeziehungen und den daraus resultierenden vorherrschenden Flammschutzmechanismen und Einflüssen von Additiven fehlt. In der vorliegenden Arbeit wurden Flammschutzmechanismen von systematisch varrierten neuartigen oligomeren Flammschutzmitteladditiven auf Phosphorbasis in zwei in der Industrie gebräuchlichen Epoxidharzen, DGEBA/DMC und RTM6, aufgeklärt und ein Vergleich der Wirkungsweisen der Flammschutzmittel in beiden Harzen gezogen. Das Brandverhalten wurde charakterisiert und die Effizienz der Flammschutzmittel bewertet. Der Einfluss von Kohlefasern auf die Wirkungsmechanismen und das Brandverhalten wurde untersucht und die Effizienz der Flammschutzmittel in den Kompositen mit den Reinharzen verglichen. Das thermische Zersetzungsverhalten wurde mittels TG ermittelt. Produkte aus der Gasphase wurden mit TG- FTIR identifiziert und Wechselwirkungen in der kondensierten Phase online in einer mit FTIR gekoppelten hot- stage Zelle charakterisiert. Intrinsische Brandeigenschaften wurden mit dem Bombenkalorimeter und dem PCFC, die Entflammbarkeit mit LOI und UL 94 bestimmt. Das Brandverhalten wurde anhand von Cone Calorimeter Messungen unter Berücksichtigung verschiedener Brandzenarien beurteilt und die Brandrückstände mittels Elementaranalyse, REM und μ-CT untersucht. Durch die sternförmige Struktur sind die untersuchten Flammschutzmittel gut mit der Harzmatrix mischbar, ihr Einfluss auf die Mechanik ist gering und auf die Glasübergangstemperaturen moderat. In DGEBA/DMC wirken alle Flammschutzmittel hauptsächlich in der Gasphase, in RTM6 sowohl in der Gas- als auch kondensierten Phase. Die Wirkungsweise hängt maßgeblich von vier Faktoren ab: in den Harzen von der strukturellen Beschaffenheit, sowie den Abbautemperaturen, in den Flammschutzmitteln von der hydrolytischen Stabilität, sowie der chemischen Umgebung der Phosphorgruppen. Diese vier Faktoren steuern die Bildung reaktiver Gruppen von Harz und Flammschutzmittel in der kondensierten Phase, die zu Vernetzungsreaktionen führen. Unabhängig von der Wirkung in der Gas- oder kondensierten Phase oder in beiden, reduzieren alle untersuchten Flammschutzmittel das Brandrisiko drastisch, wobei die Kombination aus Gas- und Festphasenaktivität in RTM6 zu einer etwas besseren Effektivität führt. Die Performance in der Entflammbarkeit wird mit Zugabe der Flammschutzmittel in beiden Harzen hinsichtlich des LOI verbessert. Im UL 94 bewirkt die alleinige Gasphasenaktivität der untersuchten Flammschutzmittel in DGEBA/DMC keine Verbesserung, während das Zusammenspiel von Gas- und Festphasenaktivität in RTM6 zur besten Klassifizierung im UL 94 führt. Der Einsatz von Kohlefasern mindert zwar die Wirkung in der kondensierten Phase, die Effizienz der Flammschutzmittel wird auf Grund der weiterhin vorherrschenden Gasphasenaktivität jedoch nur geringfügig beeinflusst. Im LOI führt die Kombination aus X Kohlefasern und Flammschutzmitteln zu teilweise drastischen Steigerungen auf Grund von synergistischen Effekten insbesondere in RTM6. Die Ergebnisse liefern ein umfassendes Verständnis über Struktur-Eigenschaftsbeziehungen phosphorhaltiger Flammschutzmittel und Additive in Epoxidharzen. Die aufgeklärten Wirkungsmechanismen bilden wesentliche Grundlagen für die Weiterentwicklung und Optimierung des Flammschutzes in Epoxidharzen. Unter Berücksichtigung mechanischer Eigenschaften, thermischer Stabilitäten und Flammschutzeffizienz wurden mehrere optimale Flammschutzlösungen gefunden N2 - Phosphorous-containing flame retardants as an effective alternative to halogen-containing ones are attracting growing interest for the use in epoxy resins. Commercially available additive flame retardants often lead to the deterioration of certain material properties, particularly in the mechanical properties. Additives like carbon fibres further influence the mechanisms of action and the effectiveness of flame retardants. The percentage of flame retardants that are adapted perfectly to the epoxy matrix is negligible so far, since deeper understanding is lacking of the structure-property relationships and the flame-retarding mechanisms they entail, not to mention the influence of additives. The present study elucidates the flame-retarding mechanisms of different novel oligomeric flame retardant additives based on phosphorous, which are added to two industrially used epoxy matrices, DGEBA/DMC and RTM6. The mechanisms of action of These systematically varied flame retardants were compared in both epoxy resins. The burning behaviour was characterised and the efficiency of the flame retardants was estimated. The influence of carbon fibres on the flame-retarding mechanisms and burning behaviour was investigated, and the efficiency of the flame retardants in the composites was compared with that of the bulk materials. The thermal decomposition behaviour was investigated using a TG. Volatile products in the gas phase were identified using a TG-FTIR. Interactions in the condensed phase were characterised online using an FTIR coupled with a hot-stage cell. Intrinsic fire properties were examined with a bomb calorimeter and PCFC, and flammability with LOI and UL 94. The burning behaviour was evaluated via a cone calorimeter under consideration of different fire scenarios. The fire residues were investigated using elemental analysis, REM and μ-CT. All investigated flame retardants are well miscible due to their star-shaped structure, and they have a minor influence on the mechanical properties and a moderate one on the glasstransition temperature. In DGEBA/DMC all flame retardants work mainly in the gas phase. In RTM6 they work in the gas phase as well as in the condensed phase. The mechanism of action is strongly dependent on four parameters: in the epoxy resins, on their structure and the decomposition temperatures resulting from their structure; in the flame retardants, on the hydrolytical stability and chemical environment of the phosphorous. These four parameters control the formation of reactive groups from the epoxy resins and the flame retardants in the condensed phase, which lead to cross-linking reactions. Independent of the action in the gas and/or condensed phase, all flame retardants drastically reduce the fire risk, whereas the combination of gas-phase and condensed-phase action in RTM6 yields slightly better efficiency. The flammability performance with regard to the LOI increases with addition of the flame retardants. In the UL 94, for the investigated flame retardants in DGEBA/DMC, the gas-phase action alone does not improve performance, while the interplay of gas-phase and condensed-phase action in RTM6 leads to the best classification in UL 94. Indeed, the use of carbon fibres decreases the action in the condensed phase, while the efficiency of the flame retardants with respect to the gas-Phase action is influenced only slightly. In the LOI the combination of carbon fibres and flame retardants leads to some drastic increases due to synergistic effects, particularly in RTM6. T3 - BAM Dissertationsreihe - 92 KW - Flammschutzmittel KW - carbon fibre composites KW - burning behavior KW - decomposition mechanisms KW - Epoxidharze KW - Abbaumechanismen KW - Brandverhalten KW - Kohlefaserkomposite KW - Flame retardants KW - epoxy resins PY - 2012 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-660 SN - 978-3-9815134-7-9 SN - 1613-4249 VL - 92 SP - 1 EP - 178 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-66 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Natte, Kishore T1 - Synthesis of novel polymeric hybrid nanoparticles with enhanced interfacial and colloidal properties for biomedical studies N2 - Die geringe Größe von Nanopartikeln (Durchmesser < 100 nm) gewährleistet sowohl eine hohe spezifische Oberfläche sowie Permeabilität durch eine Vielzahl biologischer Systeme. Als Folge weisen Nanopartikel (NP) eine starke Wechselwirkung mit biologischen Systemen auf, wodurch diese in den letzten Jahren zunehmend in der biomedizinischen Forschung Anwendung fanden. Aufgrund der relativ geringen Toxizität sowie der Möglichkeit zur Einführung unterschiedlicher funktioneller Gruppen eignen sich besonders auf Siliziumdioxid (Silica)basierende Nanopartikel für biomedizinische Studien. Der Schwerpunkt dieser Doktorarbeit lag in der Synthese und Charakterisierung von neuartigen Hybrid-NP mit verbesserten Eigenschaften für biologische Studien. Insbesondere soll eine Unterdrückung der Proteinadsorption erlangt werden sowie stark fluoreszierende NP in Gegenwart serumreicher Medien erhalten werden. Zu Beginn wird der Syntheseweg zur Darstellung hoch fluoreszierender Silica-Nanopartikel präsentiert, durch kovalente Anbindung des Alexa Farbstoffs und nachfolgender Ummantelung durch eine zusätzliche Silicahülle. Diese Nanopartikel wurden mittels dynamischen Lichtstreuung (DLS), Transmissionselektronenmikroskopie (TEM) und Fluoreszenzspektroskopie untersucht. Letztgenannte Methode beinhaltet die Bestimmung der absoluten Quantenausbeute solcher streuenden Suspensionen mit einer integrierenden Kugelkonfiguration sowie die Zuordnung von Helligkeitswerten. Bei geringer Ausdehnung der Hülle zeigen Silica NP mit Kern-Schale Architektur eine glatte Oberfläche und hohe Quantenausbeuten, in Größenordnung der freien Farbstoffe. Eine Erhöhung der Menge an Hüllen-Precusor führt zu einer himbeerartigen Morphologie der Oberfläche und einer Verminderung der Quantenausbeute. Es folgt die Darstellung zweier unterschiedlicher Typen neuartiger Silica- Polyethylenglykolhybride NP (H-SiO2-PEG und G-SiO2@PEG) unter Verwendung desselben polymerprecursors oder desselben polymerprecursors: Der Einfluss der Konzentration des polymerpreursors Poly(ethylen glykol) methylether-3-(triethoxysilyl) propylurethan (mPEG- IPTES) auf die Partikeleigenschaften wurde ausführlich untersucht. Bei polymergepfropften NP bestimmt die Konzentration des polymer precursors die Dichte des angekoppelten PEGs und folglich die Hydrophobieder NP Oberfläche. Dagegen beeinflusst bei kondensierten NP der precursor die Partikelgröße, aber nicht die Dichte der Polymerketten auf der Oberfläche. Abschließend wird der Einfluss der Polymerlänge auf die Verminderung der BSA Adsorption beschrieben. SNPs@PEG mit verschiedenen Molekulargewichten des mPEG (Mw = 350, 2000 und 5000 g/mol) wurden an die NP Oberfläche durch nucleophile Substitution von tosyliertem mPEG an aminierte Silica NP kovalent angebunden (hemisches Pfropfen). Die resultierenden Hybrid-NP wurden einheitlich mittels DLS, TEM, Fourier- Transformations-Infrarotspektroskopie (FTIR), thermogravimetrischer Analyse (TGA)und Photoelektronenspektroskopie (PES) charakterisiert. Bovine Serum Albumin (BSA) wurde in verschiedenen Konzentrationen als Modellprotein verwendet, um die Ausbildung der protein corona durch Adsorption an ursprünglichen sowie an modifizierten NP oder modifizierten NPs(SNPs@PEG) zu untersuchen. Das Zeta-Potenzial der ursprünglichen Silica NP sowie SNPs@PEG (Mw = 350 g/mol) zeigen eine dynamische Entwicklung der Nanopartikel- protein coronain Abhängigkeit von der Inkubationsdauer (0, 24, 48 h). Im Gegensatz hierzu konnte bei SNPs@PEG mit Mw 2000 g/mol eine signifikante Minderung der Ausbildung der protein corona sowie der zeitlichen Entwicklung beobachtet werden. Insgesamt wird die protein corona stark von den adsorptionshindernden Eigenschaften des PEGs beeinflusst. N2 - The reduced size of nanoparticles (diameter < 100 nm) confers them high specific surface areas and permeability through many biological pathways resulting in high interaction with biological systems. Therefore, in the recent years, nanoparticles (NPs) have increasingly found many applications in biomedical research. Herein, silica-based NPs are among the most promising candidates for biomedical studies due to their relative low toxicity and the possibility of functional variability. The main focus of this thesis work has been the synthesis and characterisation of novel hybrid NPs with enhanced properties for biomedical studies. More specifically, suppression of protein adsorption and achievement of highly fluorescent NPs in serum-rich media are well focused. First, a chemical strategy for the preparation of highly fluorescent silica nanoparticles by covalent attachment of Alexa dyes and subsequent shielding by an additional pure silica shell is well presented. These nanoparticles were investigated by Dynamic light scattering (DLS), Transmission electron microscopy (TEM) and fluorescence spectroscopy, the latter includes determination of absolute fluorescence quantum yields of such scattering suspensions with an integrating sphere setup and the assignment of fluorescence intensity values. At low shelling extension core-shell fluorescent silica nanoparticles show smooth surfaces and high quantum yields, even comparable to those for free dyes. However, by increasing the amount of shell precursor, nanoparticle surfaces show raspberry morphologies and decay of the quantum yields. Secondly, two different types of novel silica-poly(ethylene glycol) hybrid nanoparticles (H- SiO2-PEG and G- SiO2@PEG) have been synthesized by use of the same polymer precursor: Here the influence of concentration of the polymer precursor poly(ethylene glycol) methyl ether-3-(triethoxysilyl) propyl urethane (mPEG-IPTES) on the particle properties was scrutinised. For polymer grafted NPs, the concentration of polymer precursor increases the PEG density and the hydrophobicity of the NPs surface. On the other hand, for condensated NPs, the polymer precursor influences the size, but not the density of polymer chains on the NPs surface, which indicates that PEG on the surface of the NPs effectively reduces the adsorption of Bovine serum albumin (BSA). Finally, the influence of polymer length on the ability to repel BSA adsorption onto nanoparticles is reported. SNPs@PEG with different molecular weights (mPEG: 350, 2000 and 5000 g/mol) were synthesized by nucleophilic substitution of tosylated mPEG to aminated silica nanoparticles (chemical grafting). The resulted hybrid nanoparticles were consistently characterized by DLS, TEM, Fourier transform infrared spectroscopy (FTIR), Thermogravimetric analysis (TGA) and X-ray photoelectron spectroscopy (XPS). BSA at different concentrations were used as a model protein to study the protein-corona formation after adsorption onto the pristine and modified nanoparticles (SNPs@PEG). For pristine SNPs and SNPs@PEG (MW = 350 g/mol), zeta potential at different incubation times (0, 24 and 48 h) show a dynamic evolution of the nanoparticle-protein corona. Conversely, for SNPs@PEG with MW ≥ 2000 g/mol, a significant suppression of corona formation and time evolution was observed. In resume, protein corona is strongly influenced by the adsorption inhibition of PEG surfaces. T3 - BAM Dissertationsreihe - 99 KW - Silica KW - PEG KW - Fluoreszierende Nanopartikel KW - Hybridnanopartikel KW - Hybrid nanoparticles KW - Corona KW - Fluorescent particles PY - 2013 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-596 SN - 978-3-9815360-7-2 SN - 1613-4249 VL - 99 SP - 1 EP - 115 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-59 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Traulsen, Christoph T1 - Programmierbare supramolekulare (Komposit-)Multischichten auf Gold- und Siliziumoberflächen N2 - The present doctoral thesis focuses on the deposition of programmable supramolecular multilayers and composite-multilayers on gold and silicon substrates using a layer-by-layer selfassembly approach which is based on coordination chemistry. For this purpose, a variety of pyridine- and terpyridine-terminated self-assembled monolayers has been developed and deposited on gold and silicon substrates. Multitechnique analysis was carried out using X-ray photoelectron spectroscopy (XPS), (angle-dependent) near-edge Xray-absorption fine-structure spectroscopy (NEXAFS spectroscopy), time-of-flight secondaryion mass spectrometry (ToF-SIMS), transmissions UV/Vis spectroscopy as well as atomic force microscopy (AFM). By optimization of the deposition procedure, highly-ordered monomolecular and binary monolayers were deposited. As a proof of principle, transition metal-ions and appropriately labeled test-ligands were deposited on top of the functional monolayers. Furthermore, monolayers of terpyridine-terminated tetralactam macrocycles and the corresponding ether rotaxanes have been immobilized using coordination chemistry. In order to enhance the macrocycle surface coverage, the deposition procedure has been optimized as well. Multilayers consisting of diterpyridine-terminated tetralactam macrocycles have been deposited using either Fe(II) or alternatingly Fe(II) and Ni(II) metal-ions. The surface analysis proved a regular layer growth and a remarkable orientation of the macrocycles within the layer stacks. The applicability of the deposition procedure was expanded to a programmable layer stack by implementing pyridine-terminated macrocycles. The monodentate ligands led to an additional coordination sphere and thus to the application of a different transition metal-ion. The macrocycles and metal-ions were programmed according to the deposition sequence applied. The corresponding layer stack exhibited a linear dichroism of the π*-resonance corresponding to a preferential orientation of the macrocycles. Furthermore, the concept was extended to the deposition of composite multilayers consisting of pyridine-functionalized macrocycles and gold-nanoparticles which were synthesized during this thesis as well. Finally, reversible on-surface host-guest complex formation N2 - Die vorliegende Dissertation befasst sich mit der Herstellung von programmierbaren, supramolekularen Multischichten und Komposit-Multischichten auf Gold- und Siliziumoberflächen durch Anwendung eines koordinationschemischen Schicht-auf-Schicht-Selbstorganisationsverfahrens und den damit verbundenen Synthesen, Beschichtungen und Analysen. Um dieses Ziel zu erreichen, wurde zunächst eine Vielzahl von pyridin- und terpyridinterminierten selbstorganisierten Monoschichten (SAM) hergestellt und auf Gold- und Siliziumoberflächen abgeschieden. Die Abscheideprozedur wurde optimiert wobei zur Analytik der Oberflächen Röntgenphotoelektronenspektroskopie (XPS), winkelabhängiger kantennaher Röntgenabsorptionsfeinstrukturspektroskopie (NEXAFS-Spektroskopie), Flugzeit-Sekundärionen-Massenspektrometrie (ToF-SIMS), Transmissions-UV/Vis-Spektroskopie sowie Rasterkraftmikroskopie (AFM) eingesetzt wurde. Es konnte gezeigt werden, dass sich hochgeordnete monomolekulare und gemischte Monoschichten erzeugen lassen. Die terminalen funktionellen Gruppen dieser SAMs konnten als Ligand zur Komplexbildung mit Übergangsmetallionen verwendet werden. Diese koordinative Haftschicht wurde zur Verknüpfung zunächst von Testliganden und später von terpyridin-terminierten Tetralactam-Makrozyklen (TLM) und darauf basierenden Etherrotaxanen verwendet. Hierbei wurden ebenfalls die Beschichtungsbedingungen optimiert, um einen vollständigen Bedeckungsgrad zu erreichen. Unter Verwendung dieser Bedingungen wurden anschließend Multischichten aus TLMs und Fe(II)-Ionen sowie alternierend Fe(II) und Ni(II) abgeschieden. Die Analyse der hergestellten Multischichten zeigte reproduzierbar ein regelmäßiges, kontrollierbares Wachstum und eine Vorzugsorientierung. Durch den Einsatz von pyridin- und terpyridin-terminierten TLMs mit variierenden Metallionen konnte gezeigt werden, dass es möglich ist, die Abfolge verschiedener Schichten der Multischicht gezielt festzulegen. Im weiteren Verlauf der Arbeit wurden pyridin-terminierte Goldnanopartikel hergestellt und in die Multischichten integriert, um so Komposit-Multischichten herzustellen. Letztlich konnte gezeigt werden, dass die erzeugten Multischichten genutzt werden können, um über nicht-kovalente Wechselwirkungen reversibel Gastmoleküle zu binden und freizusetzten. KW - Layer-by-layer deposition KW - XPS KW - NEXAFS KW - ToF SIMS KW - Progammable rotaxane stacks PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000096664-6 SP - 1 EP - 141 PB - Freie Universität CY - Berlin AN - OPUS4-39615 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Heinrich, Thomas T1 - Switchable Surfaces: Mono- and Multilayers of Stimuli-Responsive Supramolecules on Solid Supports N2 - Rotaxanes are mechanically interlocked molecules (MIMs) that are considered to be excellent prototypes for the development of molecular machines. They comprise a discrete number of molecules that are bound to each other via non-covalent interactions. Mechanically interlocked means that a covalent bond must be broken in order to separate the molecules from another. If the rotaxanes are furthermore provided with different binding sites, they can perform a con-formational change and thus a nanoscopic movement by the application of an external stimu-lus. However, this movement is not directed in solution and a macroscopic effect is therefore, if at all, very difficult to realize. The integration of rotaxanes into a reference system by, for example, the immobilization on a surface is regarded as a promising approach to convert the generated nanoscopic motion into a macroscopic effect. The present work describes the immobilization of chloride-switchable rotaxanes onto surfaces using a variety of methods. In detail, the applied methods are the metal-mediated layer-by-layer (LbL) self-assembly and the covalent deposition using click chemistry, which can be con-sidered as separate approaches. Before the rotaxanes were immobilized, the deposition meth-ods were first established and gradually improved on the basis of earlier results by using dif-ferent macrocycle and guest molecules. Various template layers – so-called self-assembled monolayers (SAMs) – were used. These are terminated with pyridine or terpyridine for the metal-induced LbL deposition. Azide-terminated SAMs are used for the covalent deposition. In the course of that, the following objectives were achieved: The deposition of diterpyridin functionalized macrocycles in multilayers with a preferential orientation was investigated and verified by transmission-UV/Vis, X-ray photoelectron spectroscopy (XPS) as well as near edge X-ray absorption fine structure (NEXAFS). In order to produce the multilayer, metal-ions and macrocycles were alternately deposited onto various SAMs. To enable further process control for the LbL deposition, Time-of-Flight Secondary Ion Mass Spectrometry (ToF-SIMS) has been extended by use of Principal Component Analysis (PCA) which is capable of analyzing even very small changes in the deposition procedure. By using two different macrocycles and four metals, a mixed multilayer was fabricated that can be programmed by its deposition sequence. The treatment of the multilayers with appropriate guest molecules showed that they are on one hand addressable to the lowest layer by an external stimulus and that they are on the other hand able to incorporate a relatively large amount of the guest. Additionally, the covalently deposited supramolecules are also able to bind guests and to adapt to their structures. In both cases, the reversibility could be shown by appropriate experiments. Finally, the introduction of pyridine-functionalized nanoparticles into the multilayers led to a higher guest uptake, which can be explained by the reduction of the macrocycle-order due to the uneven surface of the nanoparticles. KW - Layer-by-layer deposition KW - XPS KW - NEXAFS KW - ToF SIMS KW - Switchable rotaxane PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000103658-0 SP - 1 EP - 139 PB - Freie Unversität CY - Berlin AN - OPUS4-39614 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Altmann, Korinna T1 - Abscheidung ultradünner funktionalgruppentragender Polymerschichten auf Metalloberflächen mittels Elektrospray Ionisation N2 - Funktionalisierte Oberflächen sind in vielen Bereichen, z. B. als Haftvermittler in Polymerkompositen, für katalytische Anwendungen oder als Sensoren von Interesse. Für viele solcher Anwendungen ist es ausreichend, den verwendeten Werkstoff mit einem ultradünnen Polymerfilm zu überziehen. Dazu gibt es bislang einige Verfahren, wie z. B. Chemical Vapour Deposition, Layer-by-Layer-Technik, Langmuir-Blodgett-Technik oder Spin-Coating, die alle bestimmte Nachteile haben. In der vorliegenden Arbeit wurden wenige Nanometer dicke Polymerschichten auf metallischen und nicht-metallischen Substraten mittels Elektrospray Ionisation abgeschieden. So wurden typischerweise etwa 10 nm dicke Schichten von Polyacrylsäure (PAA) hergestellt. Die analytische Charakterisierung der produzierten Schichten erfolgte mit der Röntgen-Photoelektronenspektroskopie. Die Atomkraft- bzw. Rasterelektronenmikroskopie gaben Auskunft über den Bedeckungsgrad und die Schichtmorphologie. Die Infrarot-Reflexions-Absorptions-Spektroskopie wurde zur Bestimmung des Restlösemittelgehaltes verwendet. Zur Optimierung der Schichtabscheidung und -struktur wurden verschiedene Parameter variiert, wie z. B. der Kapillaren-Proben-Abstand, die Beschichtungszeit oder die Beschichtungstemperatur, wobei sich herausstellte, dass die Schichtbildungsparameter für jedes Polymer individuell angepasst werden müssen. Es konnte gezeigt werden, dass Beschichtungen, bei denen sich das Substrat senkrecht zur Kapillare befindet, bei Raumtemperatur mit einem Kapillaren-Proben-Abstand von mindestens 100 mm zu lösemittelfreien PAA-Schichten führen. Dabei war die Ausbildung der Filmtopographie unabhängig sowohl von der Konzentration der Lösung als auch von der Oberflächenenergie des Substrates. N2 - Functionalized surfaces are of interest in plenty of technical fields, e.g. used as adhesion promoter for polymer composites, in catalytic applications or as sensors. For lots of these applications it is sufficient to cover the used materials with an ultra thin polymer film. All existing methods, e. g. chemical vapour pressure, layer-by-layer-technique, Langmuir-Blodgett technique or spin coating have disadvantages. The following work presents the deposition of few nanometer scale polymer layers on metallic and non-metal substrates by electrospray ionization. Most experiments were performed with poly(acrylic acid) (PAA). Layers of about 10 nm were deposited. The coverage and the morphology of the produced layers were analyzed by X-ray photoelectron spectroscopy, atomic force spectroscopy and scanning electron microscopy. The residual amount of solvent within the deposited layers was identified by infrared reflection absorption spectroscopy. Optimisation of the layer deposition was performed by varying the process parameters, e. g. distance to the sample, deposition time or deposition temperature. Based on the knowledge acquired in the experiments it was realized that the deposition parameters have to be found individually for each single polymer. It could be shown that depositions at room temperature with capillary-sample-distances higher than 100 mm, where the sample is placed vertical to the capillary, produce solvent free PAA layers. The film topography was independent of the concentration of the polymer solution and of the substrate surface energy. T3 - BAM Dissertationsreihe - 137 KW - Kapillaren-Proben-Abstand KW - Elektrospray Ionisation KW - Elektrospray Abscheidung KW - Ultradünne Schichtabscheidung KW - Polyacrylsäure KW - deposition KW - surface functionalization KW - electrospray ionisation PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-5142 VL - 137 SP - 1 EP - 132 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-514 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Dittrich, Bettina T1 - Graphen als Flammschutzmittel in Thermoplast-Kompositen N2 - Seit der erstmaligen erfolgreichen Isolierung von Graphen gilt das zweidimensionale Kohlenstoff Nanomaterial mit der Dicke eines Atoms als vielversprechender Füllstoff für multifunktionale Polymerwerkstoffe. Die Multifunktionalität beinhaltet auch die erwartete Flammschutzwirkung von Graphen Nanopartikeln. In der vorliegenden Arbeit wurde Graphen hinsichtlich seiner Flammschutzwirkung und seines Einflusses auf Werkstoffeigenschaften wie die elektrische Leitfähigkeit in Polymer Nanokompositen charakterisiert. Durch den Vergleich mit anderen, kommerziell erhältlichen, Kohlenstoffmaterialien mit unterschiedlicher Morphologie (sphärisch, Röhren, dicke Plättchen aus 50 bis 100 Graphen Lagen und dünne Schichten aus 10 Graphen Lagen) wurde die Effektivität von Graphen eingeordnet und Rückschlüsse über die Struktur-Eigenschafts-Beziehungen zwischen Partikelmorphologie und Nanokomposit Merkmalen gezogen. Graphen wurde mit halogenfreien Flammschutzmitteln, die Vertreter der unterschiedlichen Flammschutzmechanismen (chemische und physikalische Wirkungsweise, Gas- und Festphasenaktivität) sind, kombiniert. Dabei wurde die Einsatzmöglichkeit von Graphen als Hilfsstoff zur Verbesserung der Flammschutzwirkung der verwendeten halogenfreien Systeme untersucht. Die Untersuchungen umfassten den thermischen Abbau, die Entflammbarkeit und das Verhalten während einer erzwungenen Verbrennung, aber auch Schlüsselexperimente. Die Schlüsselexperimente führten zum tieferen Verständnis der beobachteten Brandeigenschaften durch die Aufklärung von Wirkmechanismen und Struktur-Eigenschafts-Beziehungen. Die teilweise selbstkonzipierten und –entwickelten Schlüsselexperimente umfassten das rheologische Verhalten, die Partikelverteilung, die Wärmeabsorption und –leitfähigkeit, die strukturelle Qualität des Brandrückstandes und den Temperaturverlauf innerhalb und an der Rückseite einer brennenden Probe. Der dünne Schichtpartikel Graphen war besser in der Polymermatrix dispergiert als die zu vergleichenden Kohlenstoffmaterialien. Graphen bildete bei vergleichsweise niedrigeren Konzentrationen ein zusammenhängendes Partikelnetzwerk aus, das für die elektrische Leitfähigkeit der Komposite verantwortlich ist und die Viskosität der Polymerschmelze erhöhte. Durch das Zusammenwirken von erhöhter Schmelzviskosität und dem Labyrinth Effekt des Partikelnetzwerkes verschob Graphen den Beginn des Polymerabbaus am deutlichsten zu höheren Temperaturen. In den Entflammbarkeitstests Sauerstoffindex und UL 94 führte die erhöhte Schmelzviskosität aufgrund fehlenden Abfließens und Abtropfens zur vermehrten Bereitstellung von Brennstoff und abhängig vom Matrixpolymer teilweise zu einer Verschlechterung der Einstufung. Die ausschließlich festphasenaktive Flammschutzwirkung von Graphen beruhte auf der Bildung einer Rückstandschicht, die aus den jeweiligen Kohlenstoffpartikeln bestand und als Hitzeschild wirkte. Im Vergleich zu den anderen Kohlenstoffmaterialien hatte die Rückstandsstruktur der Graphen Komposite eindeutig die höchste Qualität und reduzierte die (maximale) Wärmeabgaberate am stärksten. In Kombination mit den halogenfreien Flammschutzsystemen bestimmte das Wirkprinzip der einzelnen Systeme die Verwendbarkeit von Graphen als Hilfsmittel. Ein kommerzielles, intumeszentes Flammschutzmittelsystem reagierte sehr empfindlich auf die durch Graphen erhöhte Viskosität der kondensierten Phase und tolerierte nur sehr geringe Graphenmengen ohne Verschlechterung der Intumeszenz. In einem gasphasenaktiven Flammschutzmittel fügte Graphen durch Rückstandsbildung einen Festphasenmechanismus hinzu und senkte die Brandausbreitung und somit das Brandrisiko noch einmal deutlich. Graphen und ein rückstandsbildendes Metallhydroxid verstärkten sich synergistisch hinsichtlich der Rückstandsqualität und der Entflammbarkeitstests. Mit den erhaltenen Ergebnissen ist eine umfassende Charakterisierung der Struktur-Eigenschafts- Beziehungen zwischen Partikelmorphologie und Kompositeigenschaften und die Einordnung von Graphen in die Reihe der Kohlenstoff-Nanopartikel möglich. Die aufgeklärten Wirkprinzipien von Graphen in Nanokompositen, wie auch in Kombination mit unterschiedlichen Flammschutzsystemen, bilden die Grundlage für eine weitere Optimierung des zweidimensionalen Kohlenstoff-Nanomaterials Graphen als Flammschutzmittel. N2 - Since the first successful isolation of graphene, the two dimensional, one atom thick carbon nanomaterial is considered as promising filler for multifunctional plastic materials. This includes an expected flame retardancy effect in graphene nanocomposites caused by the nanoparticle. In this study, the flame retardancy effect of graphene was characterized as well as its influence on polymer nanocomposite properties like electrical conductivity. By comparing with other carbon nanomaterials of varying morphology (spherical, tubular, platelets of 50 to 100 single graphene layers and layers of ten single graphene layers), the efficiency of graphene was ranked and the structure-property-relationship between particle morphology and material property was revealed. Graphene was investigated as adjuvant for three halogen-free flame retardants representing different flame retardancy mechanisms (chemical and physical action, gas and condensed phase activity). The materials were investigated according to its pyrolysis behavior, reaction to small flame and burning behavior under forced flaming conditions. Additionally, partly self designed key experiments were performed like the investigation of the rheological behavior, particle dispersion, heat absorption, thermal conductivity, structural quality of residue and temperature development inside and on the backside of a burning sample. Due to the key experiments, a deeper understanding of the nanoparticles’ modes of action was obtained and the structure-property-relationships were explained. The thinly layered graphene particles showed the best particle dispersion within the group of carbon materials. An interconnected particle network of graphene was established throughout the polymer matrix at comparatively low concentrations. By overcoming the percolation threshold, electrical conductivity occurred for the nanocomposites. The particle network caused an increase in melt viscosity that hindered the diffusion of the pyrolysis gases and delayed the release. The shift of mass loss onset to higher temperatures was intensified by the labyrinth effect of the nanoparticle network. The increased viscosity provided the flame zones of oxygen index and UL 94 test with additional fuel as flowing and dripping off of the polymer melt stopped and the material was kept in the pyrolysis zone. The flame retardancy mechanism of graphene took place exclusively in the condensed phase by the formation of a residual protection layer consisting of the nanoparticles and heat shielding. Compared to the other carbon materials, the highest quality of residue structure was observed in case of the graphene nanocomposites. Consequently, graphene was the most effective flame retardant in changing the burning behavior and reducing the (peak) heat release rate the increase of condensed phase viscosity due to graphene. Only very low amounts of graphene were tolerated without inhibiting the intumescence. In an exclusively gas phase active flame retardancy system, graphene was able to add condensed phase activity by residue formation and so to reduce flame spread and fire risk. By strongly enhancing the residual structure, synergistic effects occurred between graphene and a residue forming metal hydroxide in terms of reaction to small flame. The obtained results allow characterizing the structure-property-relationship between particle morphology and composite properties comprehensively. By comparing with commercially used carbon materials, graphene was ranked according to its flame retardant and filler efficiency. Understanding of the nanoparticles’ modes of action - in nanocomposites as well as in combination with different flame retardants – gives an hint how to further optimize the use of the two dimensional carbon nanomaterial graphene as polymer filler. T3 - BAM Dissertationsreihe - 118 KW - Graphen KW - Kohlenstoffpartikel KW - Flammschutz KW - Nanokomposite KW - halogenfrei PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-406 SN - 978-3-9816380-6-6 SN - 1613-4249 VL - 118 SP - 1 EP - 137 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-40 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Wawrzyn, Eliza T1 - Novel routes in flame retardancy of bisphenol A polycarbonate/impact modifier/aryl phosphate blends N2 - Die hohe Nutzung elektronischer Geräte und die damit verbundenen Ansprüche an den Brandschutz verstärken das Interesse an umweltfreundlich flammgeschützten Bisphenol A Polycarbonat (PC) basierten Materialien. Diese Arbeit befasst sich mit der Entwicklung neuer und verbesserter Flammschutzsysteme für schlagzähmodifizierte PC/Aryl phosphate. Durchgeführte Untersuchungen umfassen Pyrolyse (TG, TG-FTIR, ATR-FTIR, NMR), Entflammbarkeit (LOI und UL94) sowie Brandverhalten (Cone Calorimeter bei verschiedenen Bestrahlungsstärken) der Materialien. Ein Ansatz zur Verbesserung der Rückstandsbildung von PC/ABSPTFE+Aryl phosphate ist der Austausch von Bisphenol A Diphenylphosphat (BDP) gegen neue Aryl phosphate. Zwei neue Flammschutzmittel wurden synthetisiert: 3,3,5-Trimethylcyclohexylbisphenolbis(diphenylphosphat) (TMC-BDP) und Bisphenol A-bis(diethylphosphat) (BEP). TMC-BDP ist thermisch beständiger als BDP, es werden daher verstärkt chemische Reaktionen zwischen den Komponenten von PC/ABSPTFE+Aryl phosphate erwartet. BEP hingegen sollte die Vernetzung des Rückstands durch Einbringen von Phosphatgruppen erhöhen. Es konnte jedoch bei keiner der neuen Verbindungen eine Verbesserung des Flammschutzes im Vergleich zu PC/ABSPTFE+BDP festgestellt werden. BEP vernetzt sich in PC/ABSPTFE vorzugsweise mit sich selbst anstatt mit PC und für TMC-BDP waren die Ergebnisse ebenso gut wie für BDP. BDP ist bereits ein hoch optimiertes Flammschutzmittel für PC/ABSPTFE Systeme. Zur Etablierung eines neuen Schlagzähmodifizierers, der neben den mechanischen auch die Flammschutzeigenschaften des Materials verbessert, wurde das bisher in PC/ABSPTFE/BDP verwendete ABS durch einen Silikon-Acrylat-Kautschuk (SiR) mit hohem Polydimethylsiloxan (PDMS)- Anteil ersetzt. PDMS verschlechtert die von BDP hervorgerufenen Gas- und Festphasenmechanismen und reagiert zudem während der Verbrennung mit PC. Durch die Reaktionen von PDMS-PC und PDMS-BDP in PC/SiRPTFE/BDP wird anorganischer Siliziumdioxid-Rückstand gebildet, der sich zum kohlenstoffhaltigen Rückstand addiert und den LOI um 10% im Vergleich zum PC/ABSPTFE/BDP System verbessert. SiR mit hohem PDMS-Anteil wird daher als Ersatz für ABS in schlagzähmodifizierten PC/BDP Blends vorgeschlagen. Zur Erhöhung des Flammschutzes wurden verschiedene Additive zu PC/SiRPTFE/BDP hinzugefügt: (i) Schichtsilikate: Talk und organisch modifizierte Schichtsilikate (LS), (ii) Metallhydroxide: Magnesiumhydroxid (Mg(OH)2) und Böhmit (AlO(OH)), (iii) Metalloxide und –carbonate: Magnesiumoxid (MgO), Siliziumdioxid (SiO2) und Kalziumcarbonat (CaCO3) sowie (iiii) hydrierte Metallborate: Zinkborat (ZnB), Kalziumborat (CaB) und Magnesiumborat (MgB). Es konnte gezeigt werden, dass die PC/SiRPTFE/BDP+Additiv Blends sehr empfindlich auf chemische (z.B. Hydrolyse) und physikalische (z.B. Viskosität) Effekte reagieren. Die starke Deformation von PC/SiRPTFE/BDP Materialen macht es schwierig den Rückstand zu optimieren. Zusammenfassend werden ZnB, MgB und CaB zur Verbesserung des Flammschutzes von PC/SiRPTFE/BDP empfohlen. Der Flammschutz verbessert sich dabei in Bezug auf Entflammbarkeit, Brandlast sowie maximale Wärmabgaberate des Materials. Die Ergebnisse der Arbeit ermöglichen die Auswahl des besten Flammschutzmittels, Schlagzähmodifizierers und anorganischen Füllstoffs zur Herstellung von flammgeschützen PC basierten Werkstoffen. N2 - The massive use of electronic engineering products accompanied by high demands on fire safety has led to increasing interest in environmentally friendly flame retardancy of bisphenol A polycarbonate (PC) based materials. In this work, novel routes for enhancing the flame retardancy of PC/Impact Modifier/Aryl phosphate were studied with respect to pyrolysis (TG, TG-FTIR, ATR-FTIR, NMR), flammability (LOI and UL 94) and fire behavior (cone calorimeter at different irradiations). To improve charring of PC/ABSPTFE+Aryl phosphate, the exchange of bisphenol A bis(diphenyl phosphate) (BDP) with novel aryl phosphates was proposed. Two novel flame retardants were synthesized: 3,3,5-trimethylcyclohexylbisphenol-bis(diphenyl phosphate) (TMC-BDP) and bisphenol A- bis(diethylphosphate) (BEP). TMC-BDP was more stable than BDP, thus gave a potential to increase the chemical reactions between the components of the PC/ABSPTFE+Aryl phosphate, whereas more reactive BEP was expected to increase the cross linking activity with the polymer matrix. Nevertheless, the corresponding blends did not enhance the flame retardancy compared to PC/ABSPTFE+BDP. BEP in PC/ABSPTFE preferred to cross-link with itself instead of with PC, thus it showed poor fire protection performance. TMC-BDP gave as good results as BDP in PC/ABSPTFE material. The results delivered evidence that BDP possesses a high degree of optimization in PC/ABSPTFE system. To provide a novel impact modifier improving not only mechanical properties but also the fire retardancy of PC/BDP material, the replacement of highly flammable acrylonitrilebutadiene- styrene (ABS) with silicon acrylate rubber (SiR) with high content of polydimethylsiloxane (PDMS) was studied. In PC/SiRPTFE/BDP the replacement of ABS is beneficial, but PDMS worsened the BDP gas phase and condensed phase action. PDMS reacted also with PC during combustion. PDMS-PC and PDMS-BDP interactions led to silicon dioxide. In fact, the inorganic residue of PC/SiRPTFE/BDP contributed to fire residue and greatly improved the LOI of about 10 % in comparison to PC/ABSPTFE+BDP system. Thus, the use of SiR with high PDMS content is proposed as replacement of ABS in PC/Impact Modifier/BDP blend. To enhance the fire protection, the PC/SiRPTFE/BDP was combined with several adjuvants: (i) layered fillers: talc and organically modified layered silicate (LS), (ii) metal hydroxides: magnesium hydroxide (Mg(OH)2) and boehmite (AlO(OH)), (iii) metal oxides and carbonate: magnesium oxide (MgO) and silicium dioxide (SiO2) and calcium carbonate (CaCO3) as well as (iiii) hydrated metal borates: zinc borate (ZnB), calcium borate (CaB) and magnesium borate (MgB). It was demonstrated that the blend PC/SiRPTFE/BDP+filler is very sensitive to chemical (e.g. hydrolysis) and physical (e.g. viscosity) effects. Additionally,the large deformations of PC/SiRPTFE/BDP materials make difficult to optimize the char. Overall, the ZnB, MgB and CaB are proposed for enhancing the flame retardancy of PC/SiR/BDP with respect to flammability results, reduction of fire hazard and maximum of heat release rate. The results of this work enable the understanding of various mechanisms controlling the fire behavior and thus effective selection of the most appropriate flame retardant, impact modifier and inorganic fillers for producing fire resistant PC based polymers. T3 - BAM Dissertationsreihe - 102 KW - flame retardancy KW - pyrolysis KW - decomposition KW - bisphenol A polycarbonate KW - flammbility PY - 2013 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-565 SN - 978-3-9815748-2-1 SN - 1613-4249 VL - 102 SP - 1 EP - 126 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-56 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Brehme, Sven T1 - Neue phosphorhaltige Polyester für den halogenfreien Flammschutz von kompaktem, glasfaserverstärktem und geschäumtem Polybutylenterephthalat N2 - Phosphorhaltige Alternativen haben halogenhaltige Flammschutzmittel für PBT zunehmend verdrängt. Die meisten der verwendeten Flammschutzmittel verschlechtern jedoch die mechanischen Eigenschaften des PBT oder neigen zum Ausblühen. Trotz ihrer gängigen Verwendung fehlt ein grundlegendes Verständnis für den Einfluss der chemischen Struktur der Flammschutzmittel auf das Brandverhalten und die Eigenschaften des Werkstoffs. Ebenso lückenhaft ist das Wissen über den Einfluss der Makrostruktur des Werkstoffs auf dessen Brandverhalten und die Flammschutzanforderungen. Als Alternative zu den gängigen niedermolekularen Flammschutzadditiven werden in dieser Arbeit phosphorhaltige Polyester als Flammschutzmittel für kompaktes, glasfaserverstärktes und geschäumtes PBT vorgestellt und ihr Pyrolyse- und Brandverhalten analysiert. Nicht nur die Makrostruktur des PBT, sondern auch die chemische Struktur der phosphorhaltigen Polyester wurde gezielt variiert, um entsprechende Struktur-Eigenschaftsbeziehungen ableiten zu können. Das glasfaserverstärkte PBT zeigt eine höhere Entflammbarkeit, der PBT Integralschaum ein höheres Risiko durch Flammenausbreitung als kompaktes PBT. Das Vorhandensein von Verbrückungen und P-O-Carom.-Bindungen im Phosphorsubstituenten der phosphorhaltigen Polyester erhöht deren Rückstandsbildung bzw. Aktivität in der kondensierten Phasen. Die Art der aktiven Flammschutzmechanismen entscheidet darüber, welche Brandrisiken reduziert werden. Als einer der phosphorhaltigen Polyester bildet PET-P-DOPO einen nicht mischbaren Blend mit PBT. Es hat eine gute Flammschutzwirkung und verschlechtert die mechanischen Eigenschaften nicht so stark wie gängige Flammschutzmittel. PET-P-DOPO birgt dabei das Potential, die mechanischen Eigenschaften und die Flammschutzwirkung durch eine Verbesserung der Mischbarkeit und eine Erhöhung des Phosphorgehaltes noch weiter zu optimieren. Für PBT Integralschaum ist PET-P-DOPO weniger geeignet. In glasfaserverstärktem PBT übertrifft PET-P-DOPO die gängigen Flammschutzmittel, selbst wenn diese mit höherem Phosphorgehalt eingesetzt werden. Die Ergebnisse tragen wesentlich zum Verständnis der grundlegenden Struktur- Eigenschaftsbeziehungen im Flammschutz von Polymeren bei. Sie ermöglichen die Vorhersage spezieller Anforderungen an die Flammschutzmittel aus der Makrostruktur des Werkstoffs. Weiterhin erlauben sie eine gezieltere Auswahl und Optimierung bestehender Flammschutzmittel durch die Anpassung ihrer chemischen Struktur sowie das gezielte Design neuer Flammschutzmittel für bestimmte Anwendungen bzw. Schutzziele. Mit PET-P-DOPO wurde außerdem eine vielversprechende Alternative zu gängigen Additiven im Flammschutz von PBT gefunden. N2 - Phosphorus-containing alternatives have increasingly substituted halogen-containing flame retardants in the flame retardancy of PBT. Unfortunately, most of the flame retardants deteriorate the mechanical properties of PBT or tend to bloom. Despite their common usage, a detailed understanding of how burning behaviour and material properties are influenced by the chemical structure of the flame retardants is still missing. The knowledge about the influence of the material's macrostructure on burning behaviour and flame retardancy demands is incomplete, too. In this study, phosphorus polyesters are presented as an alternative to commonly used low-molecular additives for the flame retardancy of compact, glass fibre reinforced and foamed PBT. The pyrolysis and burning behaviour of these polyesters is discussed. The macrostructure of PBT as well as the chemical structure of the phosphorus polyesters was systematically varied to deduce the corresponding structure-property relationships. Glass fibre reinforced PBT has a higher flammability than compact PBT, while PBT integral foam has a higher risk of flame spread. The presence of bridging groups and P-O-Carom.-bonds in the phosphorus substituent of the phosphorus polyesters increases their charforming ability and their condensed-phase activity, respectively. The nature of the active flame-retardancy mechanisms determines the fire risks, which are reduced. One of the phosphorus polyesters, PET-P-DOPO, forms an immiscible blend with PBT. PET-P-DOPO has a good flame-retardancy performance and deteriorates the mechanical properties less than common flame retardants. Additionally, it still has the potential for further optimisation. An improved miscibility and a higher phosphorus Content would improve the mechanical properties and the flame-retardancy performance, respectively. PET-P-DOPO is less suited to flame retard PBT integral foam. In glass fibre reinforced PBT, however, PET-P-DOPO outperforms common flame-retardant additives even if they are used with a higher phosphorus content than PET-P-DOPO. The results essentially contribute to the understanding of fundamental structure-property relationships in flame retardancy of polymers. They permit to predict specific flameretardancy demands from the material's macrostructure. Furthermore, the results allow a more specific selection and optimisation of existing flame retardants through the modification of their chemical structure and a targeted design of new flame retardants for specific applications or protection goals, respectively. A promising alternative to common additives for the flame retardancy of PBT was found with PET-P-DOPO. T3 - BAM Dissertationsreihe - 127 KW - Struktur-Eigenschaftsbeziehung KW - Flammschutz KW - phosphorhaltige Polyester KW - Polybutylenterephthalat KW - halogenfrei PY - 2015 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-4892 SN - 978-3-9816668-7-8 VL - 127 SP - 1 EP - 160 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-489 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - THES A1 - Dümichen, Erik T1 - Einsatz neuer thermoanalytischer Verfahren zur Untersuchung thermischer und thermo-oxidativer Degradationsmechanismen sowie dem Netzwerkaufbau von Polymeren N2 - Die Anwendung thermoanalytischer Methoden für die Polymercharakterisierung hat aufgrund der makromolekularen Struktur von Polymere Vorteile. Es wurden zwei neue thermoanalyti-sche Verfahren entwickelt und deren Einsatz anhand von Anendungsbeispielen demons-triert, sowie mit etablierten, thermoanalytischen Methoden verglichen. Für die thermische- und thermo-oxidative Zersetzungsgasanalytik wurde die Thermogravi-metrie (TGA) gekoppelt mit der Thermodesoptions-Gaschromatographie-Massenspektrometrie (TDS-GC-MS). Die Zersetzungsgase der TGA wurden dafür über ei-nen Festphasenadsorber geleitet, auf dem eine repräsentative Auswahl von polymerspezifi-schen Analyten adsorbiert wurde. Die thermische Extraktion der Analyten erfolgte in der TDS-GC-MS. Dies ermöglichte die Trennung der Analyten sowie die eindeutige Identifizie-rung mittels charakteristischer Massenfragmentmuster. Sie wurde als TED-GC-MS bezeichnet. Es stellte sich heraus, dass sie sich besonders für die Analyse von komplexen Kohlen-wasserstoffgemischen mit Molmassen von mehr als 100 g/mol eignet. In Kombination mit anderen Kopplungstechniken wie beispielsweise die TGA-FTIR/MS, die speziell für die Ana-lyse von kleineren Molekülen verwendet wurde, konnten neue grundlegende Zersetzungs-mechanismen entwickelt werden. Es wurde beispielsweise sichtbar, dass sowohl bei der thermischen als auch bei der thermo-oxidativen Degradation von Polyamid 66 (PA 66) Kon-densationsreaktionen eine wichtige Rolle spielen. Die Methode erwies sich darüber hinaus als besonders geeignet für die Identifizierung und Quantifizierung von Polymeren in Umweltproben. Es entstand dazu eine erste grundlegende Arbeit für die quantitative Bestimmung von Polyethylen (PE) Mikroplastik in Umweltproben. Im zweiten Teil der Arbeit wurde eine steuerbare beheizbare Zelle eingeführt. Mit ihr war es möglich, mit Hilfe der Nahinfrarotspektroskopie (NIR), sich verändernde Netzwerkstrukturen während der Härtung sichtbar zu machen. Vergleichend dazu wurden etablierte, kalorische Messungen durchgeführt. Somit konnten für verschiedene Epoxidsysteme die Aushärtegrade während der Härtung mit variablen Heizraten bestimmt werden. Dadurch konnten Aushär-tungskinetiken erstellt werden, die durch isotherme und komplexe Aushärtungsszenarien validiert wurden. KW - Thermische Methoden KW - Polymer KW - Analytik PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:188-fudissthesis000000100982-9 UR - http://www.diss.fu-berlin.de/diss/receive/FUDISS_thesis_000000100982 SP - 1 EP - 65 PB - FU Berlin CY - Berlin AN - OPUS4-42171 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -