TY - JOUR A1 - Kranzmann, Axel A1 - Neddemeyer, Torsten A1 - Ruhl, Aki Sebastian A1 - Hünert, Daniela A1 - Bettge, Dirk A1 - Oder, Gabriele A1 - Saliwan Neumann, Romeo T1 - The challenge in understanding the corrosion mechanisms under oxyfuel combustion conditions N2 - Basic research on the corrosive effect of flue gases has been performed at the BAM Federal Institute for Materials Research and Testing (Germany). Conditions at both high and low temperatures were simulated in specially designed experiments. Carburization occured in flue gases with high CO2 content and temperatures higher than 500 °C. In SO2 containing flue gases sulphur was detected in the oxide scale. At lower temperatures no corrosion was observed when gases with low humidity were investigated. Humidity higher than 1500 ppm was corrosive and all steels with Cr contents lower than 12% revealed corroded surfaces. At low temperatures below 10 °C a mixture of sulphuric and nitric acid condensed on metal surfaces. Acid condensation caused severe corrosion. Humidity, CO2, O2, and SO2 contents are the important factors determining corrosion. Below 300 °C acid condensation is the primary reason for corrosion. Low humidity and low temperatures are conditions which can be expected in the CO2 separation and treatment process. This work includes major conditions of the flue gas and CO2 stream in CCS plants and CCS technology. KW - Coal KW - Oxyfuel power plant KW - Corrosion KW - Carburization KW - Sulphur KW - Sulphuric acid PY - 2011 DO - https://doi.org/10.1016/j.ijggc.2011.05.029 SN - 1750-5836 VL - 5 IS - Supplement 1 SP - S168 EP - S178 PB - Elsevier CY - New York, NY [u.a.] AN - OPUS4-24705 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Dreßler, Martin A1 - Dörfel, Ilona A1 - Reinsch, Stefan A1 - Saliwan Neumann, Romeo T1 - Korundhaltige Aluminiumoxidschichten T2 - 15. Symposium: Verbundwerkstoffe und Werkstoffverbunde CY - Kassel, Germany DA - 2005-04-06 PY - 2005 UR - http://www.dgm.de/download/tg/706/706_85.pdf SP - 5 Seiten PB - DGM CY - Kassel AN - OPUS4-7522 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Davydenko, L. A1 - Nazarchuk, M. A1 - Nasiedkin, D. A1 - Plyuto, Y. A1 - Mosquera Feijoo, Maria A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Dörfel, Ilona A1 - Saliwan Neumann, Romeo A1 - Kranzmann, Axel A1 - Pérez, F.J. T1 - Anticorrosion hybrid AlPO4/Al2O3 coatings on the surface of P92 steel for oxy-fuel power plant application T2 - XtremeCOAT 2014 - Surface engineering for functional applications under extreme conditions CY - Madrid, Spain DA - 2014-10-20 KW - Corrosion protection KW - Hybrid coatings KW - Boehmite KW - AlPO4 PY - 2014 SP - P 5, 1 EP - 2 AN - OPUS4-31453 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schulz, Wencke A1 - Nofz, Marianne A1 - Dörfel, Ilona A1 - Saliwan Neumann, Romeo A1 - Kranzmann, Axel T1 - Aluminiumoxid als Schutzschicht für kommerzielle Kraftwerksstähle (Teil 1) N2 - In Kohlekraftwerken mit Oxyfuel-Technologie erfolgt die Verbrennung unter Zufuhr von reinem Sauerstoff. Damit steht für die Abscheidung und Speicherung von CO2 ein Rauchgas mit hohem CO2-Anteil zur Verfügung (CCS-Technologie). Aufgrund dieses Verbrennungsprozesses ändert sich im Wesentlichen die Rauchgaszusammensetzung hin zu hohem H2O- und SO2 -Anteil. Deshalb wurden in verschiedenen Laboratorien kommerzielle Kraftwerksstähle unter den entsprechenden korrosiven Bedingungen getestet. Im Vergleich zur herkömmlichen Verbrennungsmethode zeigten die ferritisch-martensitischen Stähle schon nach 1000 h Auslagerungszeit unter Oxyfuel-Bedingungen eine durch einen deutlich erhöhten Materialverlust gekennzeichnete Korrosion. Eine Möglichkeit um dennoch die Lebensdauer dieser Stähle zu gewährleisten, besteht im Aufbringen geeigneter Schutzschichten auf die Stahloberfläche. Die vorliegende Arbeit befasst sich mit der Herstellung und Bewertung von Sol-Gel-Aluminiumoxidschichten als Schutz vor Korrosion in Oxyfuel-Rauchgas-Atmosphäre. Diese wurden auf den warmfesten Stahl X20CrMoV12-1 (X20) mittels der Tauchmethode aufgebracht. Anschließend erfolgte eine Auslagerung der beschichteten Proben für 1000 h bei 600 °C in einer H2O-CO2-O2-SO2 -Atmosphäre. Im Vergleich zum unbeschichteten Stahl X20 war der Materialverlust des beschichteten Stahls deutlich geringer. Insbesondere konnte durch die Aluminiumoxidschicht der Transport von CO2 und SO2 zur Stahloberfläche verhindert werden. KW - Stahl KW - Korrosion KW - Aluminiumoxid KW - Sol-Gel PY - 2016 SN - 0016-4232 VL - 107 IS - 9 SP - 1900 EP - 1903 PB - Leuze Verlag CY - Bad Saulgau AN - OPUS4-38148 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Blank, Robin A1 - Nitschke, Heike A1 - Saliwan Neumann, Romeo A1 - Kranzmann, Axel T1 - Materialographic Preparation of Salt N2 - Molten salt containing systems gain in importance for sustainable energy use and production. For research and development, interactions of molten salts with potential container materials are of major interest. This article introduces preparation procedures to display an intact metal and salt microstructure and their interface using light optical microscopy and scanning electron microscopy. The exemplary material combination is the ternary salt mixture NaCl-KCl-MgCl2 and the low alloyed steel 1.4901 (T92) with a maximum service temperature of 550 °C. These are potential elements/materials for use in latent heat thermal energy storages. KW - Molten salt KW - Corrosion KW - Steel KW - Aging KW - Dry preparation PY - 2021 DO - https://doi.org/10.1515/pm-2022-0058 VL - 59 IS - 10 SP - 628 EP - 640 PB - De Gruyter AN - OPUS4-56048 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dreßler, Martin A1 - Nofz, Marianne A1 - Saliwan Neumann, Romeo A1 - Dörfel, Ilona A1 - Griepentrog, Michael T1 - Sol-gel derived alumina layers on nickel-base superalloy Inconel-718 (IN-718) N2 - Modified Yoldas sols can be used to prepare crack-free well adherent layers on different substrate materials such as soda–lime glass, corundum and metal (IN-718). These layers having thicknesses of 0.6 µm are strain tolerant and withstand thermal cycling between 810 °C and room temperature. Introducing alpha-Al2O3 filler particles into modified Yoldas sols allows the preparation of thicker layers of 1.6 µm, which as well can be thermally cycled without noticeable delaminations. Chemical bonding seems to be the predominant layer bonding mechanism. KW - Sol-gel KW - Alumosol KW - Filler particles KW - Inconel-718 KW - Scanning electron microscopy PY - 2008 DO - https://doi.org/10.1016/j.tsf.2008.08.124 SN - 0040-6090 VL - 517 IS - 2 SP - 786 EP - 792 PB - Elsevier CY - Amsterdam AN - OPUS4-18263 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Nolze, Gert A1 - Saliwan Neumann, Romeo A1 - Buchheim, Michaela T1 - Microstructure investigations of iron meteorites by EBSD and EDS analyses T2 - EMC 2012 - 15th European Microscopy Congress CY - Manchester, UK DA - 2012-09-16 KW - Orientation relationship KW - Weathering KW - Hibbingite PY - 2012 UR - http://www.emc2012.org.uk//documents/Abstracts/Abstracts/EMC2012_0090.pdf SP - 1 EP - 2(?) AN - OPUS4-27922 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nofz, Marianne A1 - Sojref, Regine A1 - Dreßler, Martin A1 - Hünert, Daniela A1 - Dörfel, Ilona A1 - Saliwan Neumann, Romeo T1 - Sol-gel alumina coatings for high-temperature corrosion protection of Ni-base alloy SC16 in water vapour containing atmosphere N2 - Alumosols in combination with well dispersed corundum were successfully used to form up to 2.5 ìm thick coatings on the Ni-base alloy SC16. These coatings withstood heat treatments at 700 °C in a water vapour containing atmosphere. The heat treatment caused formation of delta-alumina in the coating and diffusion of chromium and titanium into the coating. KW - Alumina KW - Coating KW - Sol-gel KW - Corrosion KW - Protection PY - 2009 SN - 0020-5214 VL - 58 IS - 4 SP - 192 EP - 195 PB - DVS-Verl. CY - Düsseldorf AN - OPUS4-19726 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Richter, Tim A1 - Schröpfer, Dirk A1 - Rhode, Michael A1 - Boerner, Andreas A1 - Saliwan Neumann, Romeo A1 - Schneider, M. A1 - Laplanche, G. T1 - Influence of machining on the surface integrity of high- and medium-entropy alloys N2 - High- and medium-entropy alloys (HEAs) are a quite new class of materials. They have a high potential for applications from low to high temperatures due to the excellent combination of their structural properties. Concerning their application as components; processing properties, such as machinability, have hardly been investigated so far. Hence, machinability analyses with a focus on the influence of the milling process and its basic parameters (cutting speed, feed per cutting edge) on the resulting surface integrity of specimens from an equiatomic high- (CoCrFeMnNi) and a medium- (CoCrNi) entropy alloy have been carried out. A highly innovative milling process with ultrasonic assistance (USAM) was compared to conventional milling processes. Recent studies have shown that USAM has a high potential to significantly reduce the mechanical load on the tool and workpiece surface during milling. In this study, the basic machining and ultrasonic parameters were systematically varied. After machining, the surface integrity of the alloys was analyzed in terms of topography, defects, subsurface damage, and residual stresses. It was observed that USAM reduces the cutting forces and increases the surface integrity in terms of lower tensile residual stresses and defect density near the surfaces for the CoCrFeMnNi alloy. It was shown that the cutting forces and the metallurgical influence in the sub surface region are reduced by increasing the cutting speed and reducing the feed rate per cutting edge. With the CoCrNi alloy, the tool revealed severe wear. As a result, for this alloy no influence of the parameters on the machinability could be determined. KW - High Entropy Alloy KW - Medium Entropy Alloys KW - Ultrasonic assited machining PY - 2022 DO - https://doi.org/10.1016/j.matchemphys.2021.125271 SN - 0254-0584 VL - 275 SP - 125271 PB - Elsevier B.V. AN - OPUS4-53606 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Nadammal, Naresh A1 - Kromm, Arne A1 - Saliwan Neumann, Romeo A1 - Farahbod, Lena A1 - Haberland, Christoph A1 - Portella, Pedro Dolabella T1 - Influence of support configurations on the characteristics of selective laser-melted Inconel 718 N2 - Samples fabricated using two different support configurations by following identical scan strategies during selective laser melting of superalloy Inconel 718 were characterized in this study. Characterization methods included optical microscopy, electron back-scattered diffraction and x-ray diffraction residual stress measurement. For the scan strategy considered, microstructure and residual stress development in the samples were influenced by the support structures. However, crystallographic texture intensity and the texture components formed within the core part of the samples were almost independent of the support. The formation of finer grains closer to the support as well as within the columnar grain boundaries resulted in randomization and texture intensity reduction by nearly half for the sample built on a lattice support. Heat transfer rates dictated by the support configurations in addition to the scan strategy influenced the microstructure and residual stress development in selective laser-melted Inconel 718 samples. KW - Additive manufacturing KW - Selective laser melting KW - Support configurations KW - Microstructure and texture KW - Residual stress PY - 2018 DO - https://doi.org/10.1007/s11837-017-2703-1 SN - 1047-4838 SN - 1543-1851 VL - 70 IS - 3 SP - 343 EP - 348 PB - Springer CY - USA AN - OPUS4-44175 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -