TY - JOUR A1 - Dmitriev, A. I. A1 - Häusler, Ines A1 - Wetzel, B. A1 - Zhang, G. A1 - Österle, Werner T1 - Modeling of the stress-strain behavior of an epoxy-based nanocomposite filled with silica nanoparticles N2 - The method of movable cellular automata (MCA) was applied to simulate the stress-strain behavior of a nano composite consisting of an epoxy matrix and 6 vol. % silica nano particles. The size of the elements used for modelling was fixed at 10 nm, corresponding approximately to the diameter of the filler particles. Since not only the stress-strain response of the two constituents but also debonding of neighboring particles and granular flow was taken into account, plastic deformation as well as crack initiation and propagation could be simulated with the model. Modelling results were compared with tensile test results of both, pure epoxy as well as the epoxy-6 vol. % SiO2 composite. Since assuming bulk properties of the two constituents did not yield satisfactory results, slight modifications of the nanoparticle response functions and nanostructures were tested numerically. Finally, it was observed that only the assumption of slightly increased strength properties of the epoxy yielded good correlation between experimental and modelling results. This was attributed to an increased cross linking of the epoxy caused by the presence of silica nano particles. KW - Nanocomposite KW - Polymer matrix composite KW - Stress-strain behavior KW - Modeling KW - Computational mechanics PY - 2016 DO - https://doi.org/http://dx.doi.org/10.1016/j.matdes.2015.10.038 SN - 0264-1275 VL - 89 SP - 950 EP - 956 PB - Elsevier AN - OPUS4-35596 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Dmitriev, A. I. A1 - Wetzel, B. A1 - Zhang, G. A1 - Häusler, Ines A1 - Jim, B.C. T1 - The role of carbon fibers and silica nanoparticles on friction and wear reduction of an advanced polymer matrix composite N2 - Excellent tribological properties of an advanced polymer matrix composite were obtained by a combination of micro- and nano-sized fillers. Surface features and the nanostructure of tribofilms were characterized by advanced microscopic techniques, and correlated with the macroscopic behavior in terms of wear rate and friction evolution. A model based on movable cellular automata was applied for obtaining a better understanding of the sliding behavior of the nanostructured tribofilms. The failure of the conventional composite without silica nanoparticles could be attributed to severe oxidational wear after degradation of an initially formed polymer transfer film. The hybrid composite preserves its antiwear and antifriction properties because flash temperatures at micron-sized carbon fibers, lead to polymer degradation and subsequent release of nanoparticles. It has been shown that the released particles are mixed with other wear products and form stable films at the disc surface thus preventing further severe oxidational wear. Furthermore, the released wear product also is embedding carbon fibers at the composite surface thus preventing fiber fragmentation and subsequent third body abrasion. With nanoscale modelling we were able to show that low friction and wear can be expected if the nanostructured silica films contain at least 10 vol.% of a soft ingredient. KW - Carbon fibers KW - Silica nanoparticles KW - Hybrid composite KW - Tribological properties KW - Tribofilm KW - Sliding simulation PY - 2016 DO - https://doi.org/10.1016/j.matdes.2015.12.175 SN - 0264-1275 VL - 93 SP - 474 EP - 484 PB - Elsevier AN - OPUS4-35598 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, G. A1 - Wetzel, B. A1 - Jim, B. A1 - Österle, Werner T1 - Impact of counterface topography on the formation mechanisms of nanostructured tribofilm of PEEK hybrid nanocomposites N2 - The effect of steel counterface topography on the formation mechanisms of nanostructured tribofilms of polyetheretherketone (PEEK) hybrid nanocomposites was studied. Three types of surface finishes with mean roughness Ra ranging from nano- to micro-scale were investigated. Tribo-sintering of nanopartides, oxidation of counterface steel and compaction of wear debris are identified to be competing factors dominating the formation and function of the tribofilms. Counterface topography played an important role on the competing factors, and thereby influenced significantly the final structure, the load-carrying capability and the lubrication performance of the tribofilms. It was disclosed that a thin tribofilm, which mainly consists of silica nanoparticles and which forms on the counterface with a submicron roughness, benefits best the tribological performance of the composites KW - Surface topography KW - Nanocomposite KW - Tribology KW - Tribofilm PY - 2015 DO - https://doi.org/10.1016/j.triboint.2014.11.015 SN - 0301-679X VL - 83 SP - 156 EP - 165 PB - Butterworth-Heinemann CY - Oxford AN - OPUS4-34612 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bosch, R.-W. A1 - Cottis, R.A. A1 - Csecs, K. A1 - Dorsch, T. A1 - Dunbar, L. A1 - Heyn, Andreas A1 - Huet, F. A1 - Hyökyvirta, O. A1 - Kerner, Z. A1 - Kobzova, A. A1 - Macak, J. A1 - Novotny, R. A1 - Öijerholm, J. A1 - Piippo, J. A1 - Richner, R. A1 - Ritter, S. A1 - Sánchez-Amaya, J.M. A1 - Somogyi, A. A1 - Väisänen, S. A1 - Zhang, W. T1 - Reliability of electrochemical noise measurements: Results of round-robin testing on electrochemical noise N2 - Sixteen laboratories have performed electrochemical noise (EN) measurements based on two systems. The first uses a series of dummy cells consisting of a 'star' arrangement of resistors in order to validate the EN measurement equipment and determine its baseline noise performance, while the second system, based on a previous round-robin in the literature, examines the corrosion of aluminium in three environments. All participants used the same measurement protocol and the data reporting and analysis were performed with automatic procedures to avoid errors. The measurement instruments used in the various laboratories include commercial general-purpose potentiostats and custom-built EN systems. The measurements on dummy cells have demonstrated that few systems are capable of achieving instrument noise levels comparable to the thermal noise of the resistors, because of its low level. However, it is of greater concern that some of the instruments exhibited significant artefacts in the measured data, mostly because of the absence of anti-aliasing filters in the equipment or because the way it is used. The measurements on the aluminium samples involve a much higher source noise level during pitting corrosion, and most (though not all) instruments were able to make reliable measurements. However, during passivation, the low level of noise could be measured by very few systems. The round-robin testing has clearly shown that improvements are necessary in the choice of EN measurement equipment and settings and in the way to validate EN data measured. The results emphasise the need to validate measurement systems by using dummy cells and the need to check systematically that the noise of the electrochemical cell to be measured is significantly higher than the instrument noise measured with dummy cells of similar impedance. KW - Electrochemical noise KW - Round-robin KW - Corrosion PY - 2014 DO - https://doi.org/10.1016/j.electacta.2013.12.093 SN - 0013-4686 SN - 1873-3859 VL - 120 SP - 379 EP - 389 PB - Elsevier Science CY - Kidlington AN - OPUS4-30284 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Giovannozzi, A. A1 - Gradt, Thomas A1 - Häusler, Ines A1 - Rossi, A. A1 - Wetzel, B. A1 - Zhang, G. A1 - Dmitriev, A.I. T1 - Exploring the potential of Raman spectroscopy for the identification of silicone oil residue and wear scar characterization for the assessment of tribofilm functionality N2 - We applied a combination of Raman spectroscopy (RS) and cross-sectional transmission electron microscopy (X-TEM) to identify silicone oil residues and tribofilms at steel disc surfaces after tribological testing. Neither chemical cleaning nor mechanical removal of a 50 µm thick surface layer produced a surface without any silicone residue. Nevertheless, long-term tribological properties are not affected due to silicone degradation which has been proved by Raman spectroscopy. Excellent anti-wear and anti-friction properties of a nanocomposite at severe stressing conditions correlated with the formation of a silica-based tribofilm containing amorphous and graphite-like carbon nanoparticles. Since reliable carbon quantification by analytical TEM is difficult, RS is a useful complementary method for carbon identification at wear scars. KW - Raman spectroscopy KW - Cross-sectional TEM KW - Silicone oil residue KW - Tribofilm PY - 2015 DO - https://doi.org/10.1016/j.triboint.2015.04.046 SN - 0301-679X VL - 90 SP - 481 EP - 490 PB - Butterworth-Heinemann CY - Oxford AN - OPUS4-33421 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Qiu, Yan A1 - Yu, H. A1 - Gornushkin, Igor B. A1 - Li, J. A1 - Wu, Q. A1 - Zhang, Z. A1 - Li, X. T1 - Measurement of trace chromium on structural steel surface from a nuclear power plant using dual-pulse fiber-optic laser-induced breakdown spectroscopy N2 - Remote and on-line measurement of chromium on structural steel surface in nuclear power plants is critical for protection against fluid accelerated corrosion. To improve the insufficient sensitivity of fiber-optic laser-induced breakdown spectroscopy toward trace element detection, a dual-pulse spectral enhancement system is set up. In an iron matrix, for the purpose of improving sensitivity of trace chromium analysis and reducing the self-absorption of iron, the effects of key parameters are investigated. The optimal values of the parameters are found to be: 450 ns inter-pulse delay, 700 ns gate delay, 30 mJ/6 mJ pulse energy ratio, and 19.8 mm lens-to-sample distance (corresponding to a 799 μm laser focused spot size). Compared to the single-pulse system, the shot number of dual-pulse ablation is limited for reducing surface damage. After the optimization of the dual-pulse system, the signal-to-noise ratio of the trace chromium emission line has been improved by 3.5 times in comparison with the single-pulse system, and the self-absorption coefficient of matrix iron has been significantly reduced with self-reversal eliminated. The number of detectable lines for trace elements has more than doubled thus increasing the input for spectral calibration without significantly increasing the ablation mass. Three calibration methods including internal standardization, partial least squares regression and random forest regression are employed to determine the chromium and manganese concentrations in standard samples of low alloy steel, and the limit of detection is respectively calculated as 36 and 515 ppm. The leave-one-out cross validation method is utilized to evaluate the accuracy of chromium quantification, and the concentration mapping of chromium is performed on the surface of a steel sample (16MND5) with a relative error of 0.02 wt.% KW - Fiber-optic laser-induced breakdown spectroscopy (FO-LIBS) KW - Dual-pulse KW - Parameter optimization KW - Spectral enhancement KW - Self-absorption coefficient KW - Concentration mapping PY - 2020 DO - https://doi.org/10.1016/j.apsusc.2020.147497 SN - 0169-4332 VL - 533 IS - 147497 SP - 1 EP - 29 PB - Elsevier CY - Amsterdam AN - OPUS4-51143 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, Zhiyang A1 - Kneipp, Janina T1 - Surface Molecular Patterning by Plasmon-Catalyzed Reactions N2 - Self-assembled monolayers (SAMs) on plasmonic substrates play a significant role applications of surface-enhanced Raman scattering (SERS). At the same time, localized surface plasmon resonances (LSPRs) can be employed for a broad range of plasmon-supported chemical modifications. Here, micropatterning using the derivatization of SAMs on gold nanosubstrates for rewritable SERS-based security labels or as the basis for sensing arrays functionalized with biomolecules is demonstrated using different plasmon-catalyzed reactions. The formation of 4,4′-dimercaptoazobenzene (DMAB) from p-aminothiophenol (PATP) as well as from p-nitrothiophenol (PNTP) and the reduction of PNTP to PATP are used to change the functionality of the substrate in specified positions. Employing LSPR, the reactions are started by illumination using visible laser light at a high intensity in a focal spot of a microscope objective and yield microscopic patterns of the reaction product. The obtained molecular patterns can be erased by other reactions, enabling different strategies for rewriting, encryption, or stepwise functionalization. KW - 4,4′-dimercaptoazobenzene KW - Surface molecular patterning KW - Plasmon-catalyzed reactions KW - p-aminothiophenol KW - p-nitrothiophenol PY - 2021 DO - https://doi.org/10.1021/acsami.1c12410 SN - 1944-8252 VL - 13 IS - 36 SP - 43708 EP - 43714 PB - ACS Publications AN - OPUS4-53341 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wu, Z. A1 - Guo, X. A1 - Xie, G. A1 - Yan, T. A1 - Wu, Dejian A1 - Zhang, F. A1 - Ang, R. T1 - Heat and electric flux coupling of closed-loop thermoelectric generator N2 - Thermoelectric generator (TEG) has been proved as a promising technology for directly converting heat into electricity based on Seebeck effect. On the contrary, this electricity can trigger a solid-state cooling based on conventional Peltier effect. However, these two effects induce a coupling between heat and electric flux, especially for the quantitative relationship still remaining a mystery. Here, we show experimental evidence and theoretical calculation for the coupling by monitoring transient response of fluid temperature and output power. The experimental maximum heat flow in open circuit is 1162 W at cold fluid flow rate = 0.3 m3/h and fluid temperature difference ΔTf = 70 °C, enhanced by 13% owing to heat compensation from intrinsic coupling in closed-loop circuit. Meanwhile, the measured maximum output power of TEG is 18.2 W, and subsequently decreases to 15.4 W due to the objective existence of coupling. This double-edged sword in coupling vigorously inspires the potential applications in heat-dissipation situation such as spacecraft, electronic components, photovoltaic, refrigerator and etc. Present findings open a novel avenue for manipulating heat-electricity conversion in practical engineering. KW - Thermoelectric generator PY - 2021 DO - https://doi.org/10.1016/j.enconman.2021.114529 SN - 0196-8904 VL - 244 SP - 1 EP - 13 PB - Elsevier Ltd. AN - OPUS4-53661 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhang, Z. A1 - Kneipp, Janina T1 - Ligand-Supported Hot Electron Harvesting: Revisiting the pHResponsive Surface-Enhanced Raman Scattering Spectrum of p‑Aminothiophenol N2 - The discussion of the surface-enhanced Raman scattering (SERS) spectra of p-aminothiophenol (PATP) and of ist photocatalytic reaction product 4,4′-dimercaptoazobenzene (DMAB) is important for understanding plasmon-supported spectroscopy and catalysis. Here, SERS spectra indicate that DMAB forms also in a nonphotocatalytic reaction on silver nanoparticles. Spectra measured at low pH, in the presence of the acids HCl, H2SO4, HNO3, and H3PO4, show that DMAB is reduced to PATP when both protons and chloride ions are present. Moreover, the successful reduction of DMAB in the presence of other, halide and nonhalide, ligands suggests a central role of these species in the reduction. As discussed, the ligands increase the efficiency of hot-electron harvesting. The pH-associated reversibility of the SERS spectrum of PATP is established as an Observation of the DMAB dimer at high pH and of PATP as a product of its hot-electron reduction at low pH, in the presence of the appropriate ligand. KW - Redox reactions KW - Metal nanoparticles KW - Ligands KW - Raman spectroscopy KW - Nanoparticle formation PY - 2021 DO - https://doi.org/10.1021/acs.jpclett.0c03732 SN - 1948-7185 VL - 12 IS - 5 SP - 1542 EP - 1547 PB - ACS Publications AN - OPUS4-52140 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schutjajew, K. A1 - Pampel, Jonas A1 - Zhang, W. A1 - Antonietti, M. A1 - Oschatz, M. T1 - Influence of pore architecture and chemical structure on the sodium storage in nitrogen‐doped hard carbons N2 - Hard carbon is the material of choice for sodium ion battery anodes. Capacities comparable to those of lithium/graphite can be reached, but the understanding of the underlying sodium storage mechanisms remains fragmentary. A two‐step process is commonly observed, where sodium first adsorbs to polar sites of the carbon (“sloping region”) and subsequently fills small voids in the material (“plateau region”). To study the impact of nitrogen functionalities and pore geometry on sodium storage, a systematic series of nitrogen‐doped hard carbons is synthesized. The nitrogen content is found to contribute to sloping capacity by binding sodium ions at edges and defects, whereas higher plateau capacities are found for materials with less nitrogen content and more extensive graphene layers, suggesting the formation of 2D sodium structures stabilized by graphene‐like pore walls. In fact, up to 84% of the plateau capacity is measured at potentials less than 0 V versus metallic Na, that is, quasimetallic sodium can be stabilized in such structure motifs. Finally, gas physisorption measurements are related to charge discharge data to identify the energy storage relevant pore architectures. Interestingly, these are pores inaccessible to probe gases and electrolytes, suggesting a new view on such “closed pores” required for efficient sodium storage. KW - Sodium Ion Batteries KW - Hard Carbon KW - Storage Mechanism KW - Anode PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-522529 DO - https://doi.org/10.1002/smll.202006767 VL - 17 IS - 48 SP - 2006767 PB - Wiley Online Library AN - OPUS4-52252 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhou, F. A1 - Ma, C. A1 - Zhang, K. A1 - Chan, Yin Yam A1 - Xiao, Y. A1 - Schartel, Bernhard A1 - Döring, M. A1 - Wang, B. A1 - Hu, W. A1 - Hu, Y. T1 - Synthesis of Ethyl (Diethoxymethyl)phosphinate Derivatives and Their Flame Retardancy in Flexible Polyurethane Foam: Structure-flame Retardancy Relationships N2 - Three novel liquid ethyl (diethoxymethyl)phosphinate derivatives (EDPs) were synthesized and incorporated into flexible polyurethane foams (FPUFs). The flame retardancy of FPUFs were evaluated by limiting oxygen index (LOI), vertical burning and cone calorimetry tests, and the results indicated the structure-flame retardancy relationship of EDPs. Among these EDPs, P-(diethoxymethyl)-N-phenylphosphonamidate (EDPPA) exhibited the best flame retardant effect, methyl 3-((diethoxymethyl)(ethoxy)phosphoryl)propanoate (EDPMA) the second, and ethyl phenyl (di-ethoxymethyl)phosphonate (EDPPO) the worst. When the incorporation of EDPPA was 10 wt%, the FPUFs could self-extinguish and pass the vertical burning test. Meanwhile, the LOI value of FPUF-PA increased to 23.6% with 20 wt% loading of flame retardant. According to the investigation of volatiles during the thermal degradation of FPUFs and the morphologies of char residues after cone test, we inferred the pos- sible flame retardant mechanism. The results indicated that EDPs could release phosphorus-containing compounds in the gas phase, which would generate phosphorus-containing radicals and play the role of radical scavenger. In the condensed phase, EDPs can promote the formation of dense, intact and thermal stably char layer on the surface of FPUFs. Moreover, we found that the structure influence on flame retardancy was attributed to the atoms linked to the central phosphorus. Our results indicate that these EDPs are promising flame retardants in FPUFs that can be applied to improve the flame retardancy of FPUFs in various practical applications. KW - Ethyl (diethoxymethyl)phosphinate derivatives KW - Flame retardant KW - Flexible polyurethane foam KW - Structure-flame retardancy relationship PY - 2021 DO - https://doi.org/10.1016/j.polymdegradstab.2021.109557 SN - 0141-3910 VL - 188 SP - 109557 PB - Elsevier Ltd. AN - OPUS4-53085 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -