TY - JOUR A1 - Duan, K. A1 - Zhu, L. A1 - Li, M. A1 - Xiao, L. A1 - Bevilacqua, N. A1 - Eifert, L. A1 - Manke, I. A1 - Markötter, Henning A1 - Zhang, R. A1 - Zeis, R. A1 - Sui, P. -C. T1 - Multiphase and Pore Scale Modeling on Catalyst Layer of High-Temperature Polymer Electrolyte Membrane Fuel Cell N2 - Phosphoric acid as the electrolyte in high-temperature polymer electrolyte membrane fuel cell plays an essential role in ist performance and lifetime. Maldistribution of phosphoric acid in the catalyst layer (CL) may result in performance degradation. In the present study, pore-scale simulations were carried out to investigate phosphoric acid’s multiphase flow in a cathode CL. A reconstructed CL model was built using focused ion beam-SEM images, where distributions of pore, carbon support, binder, and catalyst particles can be identified. The multi-relaxation time lattice Boltzmann method was employed to simulate phosphoric Acid invading and leaching from the membrane into the CL during the membrane electrode assembly fabrication process. The predicted redistribution of phosphoric acid indicates that phosphoric acid of low viscosity or low wettability is prone to leaching into the CL. The effective transport properties and the active electrochemical active surface area (ECSA) were computed using a pore-scale model. They were subsequently used in a macroscopic model to evaluate the cell performance. A parametric study shows that cell performance first increases with increasing phosphoric acid content due to the increase of ECSA. However, further increasing phosphoric acid content results in performance degradation due to mass transfer limitation caused by acid flooding. KW - Gas diffusion layers KW - Lattice Boltzmann simulation KW - Electrochemical impedance spectra KW - Phosphoric acid KW - HT-PEFC PY - 2021 DO - https://doi.org/10.1149/1945-7111/abff03 VL - 168 IS - 5 SP - 054521 PB - IOP Science AN - OPUS4-53836 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bevilacqua, N. A1 - Asset, T. A1 - Schmid, M. A. A1 - Markötter, Henning A1 - Manke, I. A1 - Atanassov, P. A1 - Zeis, R. T1 - Impact of catalyst layer morphology on the operation of high temperature PEM fuel cells N2 - Electrochemical impedance spectroscopy (EIS) is a well-established method to analyze a polymer electrolyte membrane fuel cell (PEMFC). However, without further data processing, the impedance spectrum yields only qualitative insight into the mechanism and individual contribution of transport, kinetics, and ohmic losses to the overall fuel cell limitations. The distribution of relaxation times (DRT) method allows quantifying each of these polarization losses and evaluates their contribution to a given electrocatalyst's depreciated performances. We coupled this method with a detailed morphology study to investigate the impact of the 3D-structure on the processes occurring inside a high-temperature polymer electrolyte membrane fuel cell (HT-PEMFC). We tested a platinum catalyst (Pt/C), a platinum-cobalt alloy catalyst (Pt3Co/C), and a platinum group metal-free iron-nitrogen-carbon (Fe–N–C) catalyst. We found that the hampered mass transport in the latter is mainly responsible for its low performance in the MEA (along with its decreased intrinsic performances for the ORR reaction). The better performance of the alloy catalyst can be explained by both improved mass transport and a lower ORR resistance. Furthermore, single-cell tests show that the catalyst layer morphology influences the distribution of phosphoric acid during conditioning. KW - High-temperature polymer electrolyte membrane fuel cell KW - Platinum-free catalyst KW - Mass transport KW - Oxygen reduction reaction KW - Distribution of relaxation times analysis PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-520917 DO - https://doi.org/10.1016/j.powera.2020.100042 VL - 7 SP - 100042 PB - Elsevier Ltd. AN - OPUS4-52091 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -