TY - JOUR A1 - Yu, D. A1 - Kleemeier, M. A1 - Wu, Guang Mei A1 - Schartel, Bernhard A1 - Liu, W.Q. A1 - Hartwig, A. T1 - The absence of size- dependency in flame retarded composites containing low-melting organic-inorganic glass and clay: Comparison between micro- and nanocomposites N2 - Due to optimised processing of epoxy based composite materials containing a low-melting organic–inorganic glass together with an organo clay, the size of the glass particles could be successfully reduced. Thus truly nano-dispersed composites were obtained, with glass particles in the range of 10 nm to 200 nm. The small particle size allowed efficient interaction of glass particles and organo clay layers. The flame retardancy as well as the thermo-mechanical properties were tested, and the results showed that the low-melting glass led to a remarkable reduction of peak heat release rate by forming an enhanced barrier layer. Nevertheless no further improvement could be achieved by lowering the particle size to the nanometre region. For good flame retardancy a microdispersion of the low-melting glass was already sufficient. KW - Epoxy resin KW - Nanocomposites KW - Low-melting glass KW - Clay KW - Flame retardancy PY - 2011 DO - https://doi.org/10.1016/j.polymdegradstab.2011.06.003 SN - 0141-3910 SN - 1873-2321 VL - 96 IS - 9 SP - 1616 EP - 1624 PB - Elsevier Ltd. CY - London AN - OPUS4-24211 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yu, D. T1 - Improvement in Flame Retardancy of Epoxy/Clay Composites by Using Low Melting Organic-Inorganic Glasses T2 - 2nd International Conference on Flame Retardants: Chinese and International Markets Requirements, Challenges and Innovations CY - Guangzhou, China DA - 2011-05-15 PY - 2011 AN - OPUS4-24676 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yu, D. A1 - Kleemeier, M. A1 - Wu, Guang Mei A1 - Schartel, Bernhard A1 - Liu, W.Q. A1 - Hartwig, A. T1 - Phosphorus and silicon containing low-melting organic-inorganic glasses improve flame retardancy of epoxy/clay composites N2 - New low-melting organic–inorganic glassy polymers containing phosphorus and silicon are synthesized by the reaction between phenylphosphonic acid and methyltrichlorosilane or methyltriethoxysilane. They possess both low-softening points and high onset decomposition temperatures, which are favorable for preparing flame retardant composites. Although the glass by itself is sensitive to water, the composites are not significantly affected in that way. For glass/clay/epoxy composites glass transition temperature (Tg) as well as storage modulus increase with the glass amount. The glasses improve flame retardancy significantly due to flame inhibition and the formation of fire residue working as protection layer during burning. The total heat evolved is reduced by 23–28% for using 5–15 wt.% glass and the maximum HRR even by 58–48%. The latter effect decreases with increasing glass amount due to an adulterate residue deformation. The combination of glass and clay is proposed as a possible route to enhance flame retardancy. KW - Clay KW - Epoxy resin KW - Flame retardancy KW - Organic-inorganic polymer KW - Low-melting glass PY - 2011 DO - https://doi.org/10.1002/mame.201100014 SN - 1438-7492 SN - 1439-2054 VL - 296 IS - 10 SP - 952 EP - 964 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-24516 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Yu, D. A1 - Kleemeier, M. A1 - Wu, Guang Mei A1 - Schartel, Bernhard A1 - Liu, W.Q. A1 - Hartwig, A. T1 - A low melting organic-inorganic glass and its effect on flame retardancy of clay/epoxy composites N2 - A low-melting organic-inorganic glass with a high molecular weight soluble in solvents was synthesized by hydrolytic polycondensation of phenyltriethoxysilane followed by a subsequent heat treatment. Softening point and thermostability were strongly increased after heat treatment. The composites of glass/epoxy and glass/clay/epoxy were studied with respect to their thermal properties, fire behavior and mechanical properties. Heat release rate as measured by cone calorimetry was remarkably reduced in the presence of glass, relative to neat epoxy resin and polymer/clay composites. The combination of glass and clay is a promising approach. It showed mainly superposition and even synergistic effects in some fire properties for higher filler concentrations due to the formation of an enhanced barrier. The structure of residue was investigated by transmission electron microscopy (TEM). KW - Low-melting glass KW - Clay KW - Epoxy resin PY - 2011 DO - https://doi.org/10.1016/j.polymer.2011.03.033 SN - 0032-3861 SN - 1873-2291 VL - 52 IS - 10 SP - 2120 EP - 2131 PB - Elsevier Ltd. AN - OPUS4-23858 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -