TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Hattendorf, H. T1 - Electrochemical characterization of high alloyed materials in molten salts for solar energy applications N2 - Within the last years the use of feasible alternative energy sources has risen and is going to replace fossil resources more and more. Nevertheless, service conditions in solar facilities are due to the chemical composition of heat transmission media and temperatures, in many cases, extreme in terms of corrosion. Since the construction of power plants shall be economical with maximum life service, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of those facilities. The materials selection depends on the operation temperature of a power plant on the chemical composition of the transmission fluid used. In high corrosive environments Ni-based alloys are often used as an all-round solution for the construction of corrosion resistant parts, because of their good corrosion properties. However, there might be limits for their use regarding their corrosion behavior, with which this contribution deals. Experiences from the electrochemical characterization of materials in aqueous solutions are transferred to molten salts, providing a good addition to common exposure tests at temperatures from 450 0C to 600 0C. By means of electrochemical measurements and exposure tests the suitability of high alloyed materials in molten nitrate salt (60 % NaNO3/40 % KNO3) can be characterized. The method was verified on different Ni-based alloys (UNS N08810, UNS N06600) and Titanium (UNS R50250). T2 - NACE International Corrosion Conference 2015 CY - Dallas, TX, USA DA - 15.03.2015 KW - Localized corrosion KW - Nickel based alloys KW - Solar energy KW - Renewables KW - Electrochemical characterization KW - UNS N08810 KW - UNS N06600 KW - UNS R50250 PY - 2015 SP - paper 5659, S. 1 EP - 9 AN - OPUS4-34748 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yevtushenko, Oleksandra T1 - Corrosion of pipeline steels due tot the condensation effects caused by SO2 and NO2 impurities in CO2 T2 - EUROCORR 2012 CY - Istanbul, Turkey DA - 2012-09-09 PY - 2012 AN - OPUS4-27064 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yevtushenko, Oleksandra T1 - Corrosion stability of piping steels in a circulating supercritical impure CO2 environment T2 - NACE 2013 CY - Orlando, FL, USA DA - 2013-03-17 PY - 2013 AN - OPUS4-27065 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yevtushenko, Oleksandra A1 - Bäßler, Ralph A1 - Bettge, Dirk T1 - Corrosion susceptibility of steels under transport and injection exploitation conditions possible in CCS process chain N2 - Once sequestrated, C02 will be transported and injected in its gaseous, liquid or supercritical state. The presence of impurities significantly influences the corrosion behavior of pipeline steels even with small concentrations of water below its Saturation limit. T2 - EUROCORR 2014 - European corrosion congress CY - Pisa, Italy DA - 08.09.2014 KW - Corrosion KW - Stainless steel KW - CCS KW - COORAL PY - 2014 SN - 978-3-89746-159-8 SP - 1 AN - OPUS4-32745 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yevtushenko, Oleksandra T1 - Corrosion resistance of piping steels in circulating supercritical impure CO2 environment due to moisture, SO2 and NO2 impurities T2 - EUROCORR 2013 CY - Estoril, Portugal DA - 2013-09-01 PY - 2013 AN - OPUS4-28968 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yevtushenko, Oleksandra A1 - Bäßler, Ralph A1 - Carrillo Salgado, I. T1 - Material challenge for carbon capture and storage - Crevice corrosion susceptibility of super austenitic stainless steel UNS NO8031 (alloy 31) and duplex stainless steel S32101 in CO2 saturated saline brine N2 - Corrosion resistance of duplex stainless Steel UNS S32101 and super austenitic stainless Steel UNS NO8031 (alloy 31) was investigated in crevice conditions in a corrosive environment (saline brine, T = 60 °C, C02-flow rate 3-5 L/h, normal pressure) using electrochemical and metallographic techniques. Rectangular rubber was used to form a metal/non-metal-crevice configuration. Potentiodynamic measurements have been carried out in order to determine critical pitting and repassivation potentials. Potentiostatic measurements at different Potentials have been performed and the dependence of pit depth on the potential applied in crevice conditions was investigated. It was shown that the repassivation potential of duplex stainless Steel S32101 coincides with its corrosion potential. Strang pitting corrosion occurred after potentiodynamic measurements with pit depths up to 100 pm. Otherwise, stainless Steel UNS NO8031 shows about 0.5 V difference between the free corrosion potential and the repassivation potential and did not show any signs of pitting corrosion after polarization measurements. Slight rouging effects have been observed. By potentiostatic measurements on duplex stainless Steel S32101 potentials slightly more positive than the corrosion Potentials causing strong pitting corrosion, and pit depths up to 650 pm were measured. Super austenitic stainless Steel UNS NO8031 did not exhibit any signs of pitting corrosion even by applying potentials much more positive than the corrosion potential. T2 - NACE International Corrosion Conference 2013 CY - Orlando, FL, USA DA - 17.03.2013 KW - CO2 KW - Saturated saline brine KW - Crevice corrosion KW - Pitting corrosion KW - Electrochemical measurements PY - 2013 SN - 978-1-627-48145-8 SP - 1 EP - 8 (Paper 2427) PB - Curran CY - Red Hook, NY AN - OPUS4-28964 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bettge, Dirk A1 - Ruhl, Aki Sebastian A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Kranzmann, Axel T1 - Corrosion aspects of materials selection for CO2 transport and storage N2 - The geological storage of carbon dioxide (Carbon Capture and Storage, CCS) in depleted gas reservoirs or in saline aquifers is a widely discussed issue. Carbon dioxide may induce corrosion on the piping steels during compression, transportation and injection. Therefore, selection of appropriate piping steels is a key factor in order to increase the safety and reliability of the CCS technology, and to keep the processes cost-effective. The here described subproject of the COORAL project (German acronym for “C02 purity for capture and storage”) deals with the levels of impurities in the C02 stream that will be acceptable when using specific steels. Material exposure to carbon dioxide (C02) containing specific amounts of water vapor, oxygen (02) sulfur dioxide (S02), nitrogen dioxide (N02), carbon monoxide (CO) can be a challenge to steels. Within this subproject 13 different Steels are tested for suitability as materials used for compression, transportation and injection Units within the CCS chain. T2 - 2nd ICEPE International conference on energy process engineering - Efficient carbon capture for coal power plants CY - Frankfurt/M., Germany DA - 20.06.2011 KW - Carbon capture KW - CCS KW - Corrosion PY - 2011 SP - 76 EP - 78 AN - OPUS4-24250 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Le, Quynh Hoa A1 - Bettge, Dirk T1 - Suitability of Metallic Materials in CC(U)S Applications N2 - Carbon Capture Utilization and Storage (CCUS) is a promising technology to reach the target for reduction of CO2 emissions, e.g. from fossil-fuel operated power plants or cement mills. Crucial points for a sustainable and future-proof CCUS procedure are reliability and cost efficiency of the whole process chain, including separation of CO2 from the source, compression of CO2, its subsequent transportation to the injection site and injection into geological formations, e.g. aquifers. Most components that are in contact with CO2-stream consist of steel. Depending on the operating conditions (e.g. temperature, pressure, and CO2-stream composition) specific suitable steels should be used. The compressed CO2-stream is likely to contain process specific impurities; small amounts of SO2 and NO2 in combination with oxygen and water are most harmful. One approach, as currently preferred by pipeline operators, is to clean the CO2-stream to such levels, acceptable for carbon steel, commonly used as pipeline material. Another consideration would be, to use more corrosion resistant alloys for CO2-streams with higher amounts of impurities. Due to the absence of certified benchmarks for upper limits, systematic experiments with impurities in the CO2-stream were carried out reflecting mainly transport and injection conditions. Within the COORAL project (German acronym for “CO2 purity for capture and storage”) levels of impurities in the CO2-stream, being acceptable when using specific steels, were evaluated. Material exposure to dense or multiphase carbon dioxide (CO2) containing specific amounts of water vapor, oxygen (O2) sulfur dioxide (SO2), nitrogen dioxide (NO2), carbon monoxide (CO) can be a challenge to steels. In some situations, condensation of impurities and reaction products from the CO2 stream can occur. CO2 saturated brine is supposed to rise in the well when the injection process is interrupted. The material selection shall ensure that neither CO2 nor brine or a combination of both will leak out of the inner tubing. This COORAL-work was extended by a follow-up project, called CLUSTER. Here the additional influence of impurities was investigated when merging CO2 streams from different sources, combined within a “so-called” cluster. Results are summarized within the following table regarding suitability for different parts of the process chain. T2 - EUROCORR 2021 CY - Online meeting DA - 20.09.2021 KW - Carbon capture storage KW - Corrosion KW - Steel KW - CCS KW - CCU KW - CO2 PY - 2021 SP - 1 EP - 2 AN - OPUS4-53460 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Bäßler, Ralph A1 - Yevtushenko, Oleksandra A1 - Hattendorf, H. T1 - Suitability of high alloyed materials in molten salts at 600 °C N2 - Within the last years the use of feasible alternative energy sources has risen and is going to replace fossil resources more and more. Nevertheless, service conditions in solar facilities are due to the chemical composition of heat transmission media and temperatures, in many cases, extreme in terms of corrosion. Since the construction of power plants shall be economical with maximum life service, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of those facilities. The materials selection depends on the operation temperature of a power plant on the chemical composition of the transmission fluid used. In high corrosive environments Ni-based alloys are often used as an all-round solution for the construction of corrosion resistant parts, because of their good corrosion properties. However, there might be limits for their use regarding their corrosion behavior, with which this contribution deals. By means of electrochemical measurements and exposure tests the suitability of two high alloyed materials X8NiCrSi38 18 and NiCr25FeAlYB in molten nitrate salt (60 % NaNO3/40 % KNO3) was characterized at 600 °C. T2 - NACE International Corrosion Conference CY - Vancouver, BC, Canada DA - 06.03.2016 KW - Localized corrosion KW - Nickel based alloys KW - Solar energy KW - Renewables KW - Electrochemical characterization KW - X8NiCrSi38-18 KW - NiCr25FeAlYB PY - 2016 SP - 7363-1 EP - 7363-9 CY - Houston, USA AN - OPUS4-36988 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yevtushenko, Oleksandra T1 - Electrochemical studies on pitting corrosion on Cr13 piping steel exposed to CO2 and artifical brine with high chloride concentration T2 - 2. Young Materials Scientist Workshop des World Material Research Institue Forums (WMRIF), BAM CY - Berlin, Germany DA - 2010-08-30 PY - 2010 AN - OPUS4-23077 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yevtushenko, Oleksandra A1 - Bäßler, Ralph A1 - Carrillo-Salgado, I. T1 - Corrosion stability of piping steels in a circulating supercritical impure CO2 environment N2 - Within the project COORAL (German acronym for ''C02 purity for capture and storage") studies on pipeline steels exposed to circulating supercritical impure C02 have been carried out. For this purpose, a loop consisting of compressors, flow meter and two autoclaves was constructed. In order to simulate the real conditions in pipelines, impurities such as H20, CO, S02, N02 and 02 were added to the C02 stream before compression. Exposure experiments were carried out with Steel specimens placed in the autoclaves. Carbon Steel L360NB, pure iron X20Cr13, X46Cr13, X2CrMnNiN22-5-2 and alloy 31 have been exposed to circulating (flow rate 4 L/min) supercritical impure C02 for one week at 60 °C and 10 MPa Surface analysis and weight loss experiments in order to determine the corrosion products and the corrosion rates showed that the impurities cause corrosion problems. Slight general corrosion by L360NB and soft iron was observed. The initiation of pitting corrosion was observed at the surfaces of the materials X20Cr13, X46Cr13, X2CrMnNiN22-5-2. No visible signs of corrosion have been observed on alloy 31. T2 - NACE International Corrosion Conference 2013 CY - Orlando, FL, USA DA - 17.03.2013 KW - Supercritical circulating CO2 KW - Impurities KW - Exposure test KW - Corrosion PY - 2013 SN - 978-1-627-48145-8 SP - 1 EP - 11 (Paper 2372) PB - Curran CY - Red Hook, NY AN - OPUS4-28965 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Yevtushenko, Oleksandra T1 - Corrosion studies on piping steels exposed to CO2 and artifical brines T2 - EUROCORR 2010 CY - Moscow, Russia DA - 2010-09-13 PY - 2010 AN - OPUS4-23076 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Yevtushenko, Oleksandra A1 - Bäßler, Ralph ED - Lexow, J. ED - Kishi, T. ED - Kitagawa, M. ED - Böllinghaus, Thomas T1 - Electrochemical studies on pitting corrosion on Cr13 steel exposed to CO2 and artificial brine with high chloride concentration N2 - Within the project COORAL (German acronym for 'CO2 purity for capture and storage') first studies on piping steels exposed to CO2 and artificial brine with high chloride concentration have been carried out. Corrosion behavior of martensitic Cr13 steel (1.4034) was investigated in a corrosive environment (artificial saline brine, T = 60 °C, CO2-flow rate 3 – 5 L/h, atmospheric pressure, exposure times from 1 h up to 14 days) using electrochemical and metallographic techniques. Different corrosion kinetics were observed as a function of exposure times and chloride concentration in the artificial brine. In CO2-saturated brine pitting corrosion was observed at free corrosion potential, whereas in the brine without addition of NaCl a stable passive layer built up. Predictions about corrosion mechanism are made and verified by means of surface analytical techniques. KW - Stainless steel KW - Pitting corrosion KW - Electrochemistry KW - Carbon dioxide PY - 2012 SN - 978-3-642-23347-0 SN - 978-3-642-23348-7 SP - 45 EP - 53 PB - Springer CY - Berlin Heidelberg AN - OPUS4-27393 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -