TY - JOUR A1 - Liu, J.-Y. A1 - Hou, X.-N. A1 - Tian, Y. A1 - Jiang, L. A1 - Deng, S. A1 - Röder, B. A1 - Ermilov, Eugeny T1 - Photoinduced energy and charge transfer in a bis(triphenylamine)-BODIPY-C60 artificial photosynthetic system N2 - Triphenylamines (TPAs), boron dipyrromethenes (BODIPYs) and fullerenes C60 are excellent building blocks for the design of artificial photosynthetic systems. In the present work, we report the synthesis, characterization and detailed photophysical studies of a novel (TPA)2–BODIPY–C60 tetrad in polar and nonpolar solvents. The absorption spectrum of this compound covered virtually the entire visible Region (350–700 nm) and could be interpreted as a superposition of the spectra of individual components. Upon TPA-part excitation, a fast and very efficient excitation energy transfer (EET) delivers the excitation to the BODIPY moiety resulting in complete quenching of the TPA first excited singlet state as well as the appearance of the BODIPY fluorescence. The efficiency of EET process was estimated to be 1. Direct or indirect (via EET) excitation of the BODIPY-part of the tetrad is followed by photoinduced charge transfer to the charge-separated state BODIPY+–C60- irrespective of the solvent used. In polar N,N-dimethylformamide (DMF)charge recombination occurs directly to the ground state with the Charge recombination rate, kCR, slower than 108 s-1, whereas in nonpolar toluene (TOL) a small energy gap between the charge-separated state and first excited singlet state of the BODIPY moiety facilitates the back charge transfer process. The latter results in the appearance of thermally activated delayed fluorescence. The rate of charge separation was found to be ca. 2 times faster in TOL than in DMF. KW - Charge transfer KW - Energy transfer KW - Artificial photosynthesis KW - BODIPY KW - TPA KW - Fullerene C60 PY - 2016 DO - https://doi.org/10.1039/c6ra06841c SN - 2046-2069 VL - 6 IS - 62 SP - 57293 EP - 57305 AN - OPUS4-37080 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Sun, C. A1 - Tian, X. A1 - Wang, L. A1 - Liu, Y. A1 - Wirth, Cynthia A1 - Günster, Jens A1 - Li, D. A1 - Jin, Z. T1 - Effect of particle size gradation on the performance of glass-ceramic 3D printing process N2 - Particle size gradation is regarded as an effective method for overcoming the contradicting requirements in three-dimensional printing (3DP). In present work, particle size gradation was optimized to obtain both acceptable flowability of the powder material and high-strength 3D-printed glass-ceramic products. The effect of gradation on the printing process, sintering process and performance of the 3D-printed glass-ceramic products was investigated comprehensively. The glass-ceramic powders with three size ranges were mixed in certain proportions and applied to print parts. The result showed parts printed with powder mixed by 60 wt% 45–100 µm and 40 wt% 0–25 µm particles had satisfactory density of 1.60 g/cm³ and bending strength of 13.8 MPa. The flowability decreased with an increasing proportion of fine particles. Part density was determined by the powder bulk density in the powder bed as well as the shrinkage during sintering while strength of part was found to be dependent on the sintering degree. KW - Flowability KW - Glass-ceramic KW - Particle size gradation KW - Three-dimensional printing KW - Mechanical properties PY - 2017 DO - https://doi.org/10.1016/j.ceramint.2016.09.197 SN - 0272-8842 VL - 43 IS - 1 SP - 578 EP - 584 PB - Elsevier AN - OPUS4-39783 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -