TY - JOUR A1 - Stark, Wolfgang T1 - Investigation of curing behaviour of melamine/phenolic (MP) thermosets N2 - Commercially available melamine/phenolic (MP) moulding compounds used for manufacturing electro installation parts were investigated by laboratory thermal analysis methods: Dynamic Mechanical Analysis (DMA), Differential Scanning Calorimetry (DSC) and Dielectric Analysis (DEA). The results were compared with on-line measurements in a compression mould using incorporated dielectric and ultrasound sensors. Softening and cross-linking behaviour were analyzed. For on-line process monitoring, only the ultrasound method worked well. The dielectric method was distorted by water formed as a by-product from the poly-condensation reaction. KW - Thermoset KW - Melamine KW - Phenol KW - Moulding compound KW - Cross-linking KW - DSC PY - 2010 U6 - https://doi.org/10.1016/j.polymertesting.2010.05.008 SN - 0142-9418 VL - 29 IS - 6 SP - 723 EP - 728 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-20982 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stark, Wolfgang A1 - Jaunich, Matthias T1 - Investigation of ethylene/vinyl acetate copolymer (EVA) by thermal analysis DSC and DMA N2 - Two types of commercially applied Ethylene/Vinyl Acetate Copolymers (EVA) for encapsulation of photovoltaic modules were investigated by the thermal analysis methods of Differential Scanning Calorimetry (DSC) and Dynamic Mechanical Analysis (DMA) in the temperature range from -150 °C to 200 °C. Glass transition, crystal melting and cross-linking were analyzed. The aims of the investigations were to gain more information for incoming goods control and to get information about the whole temperature dependent material properties in the investigated temperature range, starting at very low temperatures up to the crosslinking temperature region. KW - EVA KW - Thermal analysis KW - DSC KW - DMA KW - Glass transition KW - Crystal melting KW - Cross-linking PY - 2011 U6 - https://doi.org/10.1016/j.polymertesting.2010.12.003 SN - 0142-9418 VL - 30 IS - 2 SP - 236 EP - 242 PB - Elsevier Ltd. CY - Amsterdam [u.a.] AN - OPUS4-23206 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stark, Wolfgang A1 - Jaunich, Matthias A1 - Mc Hugh, Jarlath T1 - Dynamic mechanical analysis (DMA) of epoxy carbon-fibre prepregs partially cured in a discontinued autoclave analogue process N2 - Epoxy carbon-fibre prepreg, Hexcel Type 6376 HTS, was investigated using Dynamic Mechanical Analysis (DMA). The DMA characteristic parameters are storage modulus E', loss modulus E' and loss factor tanδ. These parameters are ideally suited to observe the vitrification, referred to as glass transition, resulting from the cross-linking reaction. Detection of the cure state may also be achieved by determining the momentary glass transition temperature of partially cured samples. The consequent use of a multi-frequency measuring regime was used to derive the apparent activation energy for the glass transition process. Different temperature programs were also applied to monitor the curing process directly, as well as to investigate the different states of incomplete cure reached in preceding curing steps. The intention was to provide better understanding of the consequences of an interrupted autoclave curing process and to use DMA to detect the cure state achieved. With DMA, the continuation of an incomplete curing process also can be monitored. DMA measurements up to 300 °C showed, furthermore, that the final glass transition temperature was reduced by thermal degradation at high temperatures. KW - Composites KW - Epoxy KW - Cross-linking KW - Prepreg KW - Degree of cure KW - Glass transition PY - 2015 U6 - https://doi.org/10.1016/j.polymertesting.2014.11.004 SN - 0142-9418 VL - 41 SP - 140 EP - 148 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-32325 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -