TY - JOUR A1 - Stark, Wolfgang T1 - Investigation of the curing behaviour of carbon fibre epoxy prepreg by dynamic mechanical analysis DMA JF - Polymer Testing N2 - Carbon fibre prepregs have found widespread application in lightweight constructions. They are based on a carbon fibre fabric impregnated with reactive epoxy resin. Measurements were carried out using commercially available prepreg material. For Dynamic Mechanical Analysis (DMA), a single cantilever measuring device was applied. The DMA results were refined by additional DSC measurements. The measurements were carried out with dynamic heating in the temperature range -90 to 280 °C. The heating rates were 1 and 2 K/min, respectively. A glass transition of the uncured material (Tg0) near 1 °C, and crosslinking-induced vitrification and devitrification at the maximal glass transition temperature of the cured material (Tgmax) in the temperature range 220 to 230 °C were found. The activation energies for the glass transitions were determined using an Arrhenius plot. By detailed consideration of the influence of the frequency on the DMA data, indications for gelation were deduced. KW - CRP KW - Prepreg KW - Carbon fibre KW - Epoxy KW - DMA KW - DSC KW - Glass transition KW - Crosslinking KW - Vitrification KW - Devitrification PY - 2013 DO - https://doi.org/10.1016/j.polymertesting.2012.11.004 SN - 0142-9418 VL - 32 IS - 2 SP - 231 EP - 239 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-27584 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Stark, Wolfgang A1 - Jaunich, Matthias A1 - Mc Hugh, Jarlath T1 - Dynamic mechanical analysis (DMA) of epoxy carbon-fibre prepregs partially cured in a discontinued autoclave analogue process JF - Polymer testing N2 - Epoxy carbon-fibre prepreg, Hexcel Type 6376 HTS, was investigated using Dynamic Mechanical Analysis (DMA). The DMA characteristic parameters are storage modulus E', loss modulus E' and loss factor tanδ. These parameters are ideally suited to observe the vitrification, referred to as glass transition, resulting from the cross-linking reaction. Detection of the cure state may also be achieved by determining the momentary glass transition temperature of partially cured samples. The consequent use of a multi-frequency measuring regime was used to derive the apparent activation energy for the glass transition process. Different temperature programs were also applied to monitor the curing process directly, as well as to investigate the different states of incomplete cure reached in preceding curing steps. The intention was to provide better understanding of the consequences of an interrupted autoclave curing process and to use DMA to detect the cure state achieved. With DMA, the continuation of an incomplete curing process also can be monitored. DMA measurements up to 300 °C showed, furthermore, that the final glass transition temperature was reduced by thermal degradation at high temperatures. KW - Composites KW - Epoxy KW - Cross-linking KW - Prepreg KW - Degree of cure KW - Glass transition PY - 2015 DO - https://doi.org/10.1016/j.polymertesting.2014.11.004 SN - 0142-9418 VL - 41 SP - 140 EP - 148 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-32325 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -