TY - CONF A1 - Österle, Werner A1 - Deutsch, Cornelius A1 - Dörfel, Ilona A1 - Gradt, Thomas A1 - Häusler, Ines A1 - Orts-Gil, G. A1 - Prietzel, C. A1 - Schneider, Thomas T1 - Final outcome of a fundamental research project on tribofilms formed during automotive braking, Part 1: Experimental studies N2 - In order to obtain a better understanding of the role of tribofilms during automotive braking, their structures were investigated and the essential features identified. Next, different ingredient combinations were studied by preparing some model materials with simpler compositions than real tribofilms. A test method was developed for verifying the tribological properties of the model materials and for comparison with results obtained with numerical sliding simulations of such structures. Prerequisites of good brake Performance properties were identified. Although the coefficient of friction could be varied in a wide ränge, smooth sliding conditions could only be achieved with values smaller than 0.4. Tests with artificial third body powders turned out to be useful as screening method for the selection of raw materials for brake pad formulations. T2 - EuroBrake 2014 CY - Lille, France DA - 13.05.2014 KW - Tribofilm KW - Third body KW - Pad ingredients KW - Ball milling KW - Pin-on-disc test PY - 2014 SN - 978-0-9572076-4-6 SP - 1 EP - 8 PB - FISITA CY - London AN - OPUS4-35039 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Dmitriev, A.I. A1 - Kloß, Heinz A1 - Österle, Werner T1 - Final outcome of a fundamental research project on tribofilms formed during automotive braking, Part 2: Numerical simulation N2 - In part 1 it was shown that tribofilms usually are 100 nm thick and exhibit a multiphase nanocrystalline structure. The objective of our modelling efforts was to obtain a better understanding of the sliding behaviour and associated friction properties and to study the impact of internal and external parameters on these properties. The method of movable cellular automata (MCA) was used. The third bodies were considered as aggregates of linked nanoparticles which may decompose and form a layer of granulär material, the so-called mechanically mixed layer (MML), if certain fracture criteria are fulfilled. The basic model structure which consists of Fe3Ü4 nanoparticles with 13 % graphite inclusions was used. In order to assess the robustness of the model the following parameter studies were performed. The pressure ränge at an asperity contact was varied between 15 and 50 MPa. The mechanical properties of the oxide were varied between brittle and ductile behaviour corresponding to room temperature and high temperature behaviour. The mechanical properties of the soft ingredient were varied + 50 % of the properties of graphite. The influence T2 - EuroBrake 2014 CY - Lille, France DA - 13.05.2014 KW - Tribofilm KW - Third body KW - Dry friction KW - Modelling KW - Movable cellular automata PY - 2014 SN - 978-0-9572076-4-6 SP - 1 EP - 9 PB - FISITA CY - London AN - OPUS4-35040 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Österle, Werner A1 - Deutsch, Cornelius A1 - Gradt, Thomas A1 - Orts Gil, Guillermo A1 - Schneider, Thomas A1 - Dmitriev, A.I. T1 - Tribological screening tests for the selection of raw materials for automotive brake pad formulations N2 - A modified pin-on-disc test was applied to determine tribological properties of typical brake pad constituents. Ball-milling of these ingredients together with iron oxide and graphite provided model materials displaying the main features of real third bodies. Solid lubricants like graphite affected the friction and wear behaviour of Fe3O4 powders considerably whereas further addition of hard nanoparticles induced only minor effects. This was corroborated by comparison with modelling results. MoS2 played a dual role. Depending on special conditions, this ingredient either reduced or increased friction. The latter could be explained, after nanoscopic characterization, by oxidation and destruction of the wear-protecting tribofilm. KW - Brake pad formulation KW - Raw materials KW - Third body KW - Pin-on-disc test PY - 2014 U6 - https://doi.org/10.1016/j.triboint.2014.01.017 SN - 0301-679X VL - 73 SP - 148 EP - 155 PB - Butterworth-Heinemann CY - Oxford AN - OPUS4-30221 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -