TY - JOUR A1 - Coniglio, N. A1 - Cross, Carl Edward A1 - Dörfel, Ilona A1 - Österle, Werner T1 - Phase formation in 6060/4043 aluminium weld solidification N2 - Weld metal microstructure for alloy 6060 aluminum welds, made using the gas-tungsten arc process and alloy 4043 filler metal, has been characterized using optical metallography, EPMA microprobe analysis, SEM/EBSD and STEM/EDX electron microscopy, and single-sensor differential thermal analysis (SS-DTA). In addition, alloy 6060 castings were solidified at variable cooling rates approaching that of welding, to provide a reference for comparison with weld microstructure. It was found that a major change in cast microstructure occurs at cooling rates higher than 27 K/s resulting in a structure similar to that observed in weld metal. Rapid cooling is believed to favor low temperature solidification reactions that normally would be achieved only at higher silicon content. Accordingly, additions of 4043 filler metal that increase the weld metal silicon content have only limited affect on weld solidification range and microstructure. This has direct implications regarding how 4043 filler additions improve weldability and weld quality. KW - 6060 aluminium KW - GTA weld KW - Weld metal microstructure KW - Cooling rate KW - Scanning TEM KW - Thermal analysis PY - 2009 U6 - https://doi.org/10.1016/j.msea.2009.03.087 SN - 0921-5093 SN - 1873-4936 VL - 517 IS - 1-2 SP - 321 EP - 327 PB - Elsevier CY - Amsterdam AN - OPUS4-20625 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -