TY - JOUR A1 - Österle, Werner A1 - Krause, S. A1 - Moelders, Theodor A1 - Neidel, A. A1 - Oder, Gabriele A1 - Völker, J. T1 - Influence of heat treatment on microstructure and hot crack susceptibility of laser-drilled turbine blades made from René 80 N2 - Turbine components from conventionally cast nickel-base alloy René 80 show different hot cracking susceptibilities depending on their heat treatment conditions leading to slightly different microstructures. Electron probe micro-analysis, focused ion beam technique and analytical transmission electron microscopy were applied to reveal and identify grain boundary precipitates and the γ–γ'-microstructure. The distribution of borides along grain boundaries was evaluated statistically by quantitative metallography. The following features could be correlated with an increase of cracking susceptibility: i) Increasing grain size, ii) increasing fraction of grain boundaries with densely spaced borides, iii) lack of secondary γ'-particles in matrix channels between the coarse cuboidal γ'-precipitates. The latter feature seems to be responsible for linking-up of cracked grain boundary precipitates which occurred as an additional cracking mechanism after one heat treatment, whereas decohesion at the boride-matrix-interface in the heat affected zone of laser-drilled holes was observed for both heat treatments. KW - Turbine blades KW - Nickel-base superalloy KW - Laser drilling KW - Hotcrack susceptibility KW - Grain boundary precipitates PY - 2008 DO - https://doi.org/10.1016/j.matchar.2008.01.021 SN - 1044-5803 SN - 1873-4189 VL - 59 IS - 11 SP - 1564 EP - 1571 PB - Elsevier CY - New York, NY AN - OPUS4-17932 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schempp, Philipp A1 - Cross, C.E. A1 - Pittner, Andreas A1 - Oder, Gabriele A1 - Neumann, R. S. A1 - Rooch, Heidemarie A1 - Dörfel, Ilona A1 - Österle, Werner A1 - Rethmeier, Michael T1 - Solidification of GTA aluminium weld metal: Part I - Grain morphology dependent upon alloy composition and grain refiner content N2 - The solidification conditions during welding strongly influence the weid metal microstructure and mechanical properties of a weid. In the first part of this study, the grain morphology of gas tungsten arc (GTA) bead-on-plate welds was investigated for the aluminum Alloys 1050A (Al 99.5), 6082 (Al SifMgMn), and 5083 (AI Mg4.5Mn0.7). The experiments revealed that increasing welding speed and alloy content allow the growth of small, equiaxed grains, particularly in the weid center. Furthermore, increasing grain refiner additions led to a Strong reduction of the weid metal mean grain size and hence facilitated the columnar to equiaxed transition (CET). In addition, wavelength dispersive X-ray spectroscopy (WDS) and transmission electron microscopy (TEM) analysis revealed in the weid metal TiB2 particles that were surrounded by Al3Ti. This suggests the duplex nucleation theory for nucleation of aluminum grains in GTA weid metal. KW - Aluminium KW - Gas tungsten arc welding (GTAW) KW - Grain refinement KW - Columnar to equiaxed transition (CET) KW - Epitaxial nucleation KW - Duplex nucleation theory PY - 2014 SN - 0043-2296 SN - 0096-7629 VL - 93 SP - 53-s EP - 59-s PB - American Welding Society CY - New York, NY AN - OPUS4-30413 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -