TY - JOUR A1 - Naghib Zadeh, Hamid A1 - Glitzky, Carsten A1 - Österle, Werner A1 - Rabe, Torsten T1 - Low temperature sintering of barium titanate based ceramics with high dielectric constant for LTCC applications N2 - The sintering temperature of BaTiO3 powder was reduced to 900 °C due to the ZnO-B2O3-Li2O-Nb2O5-Co2O3 addition. Excellent densification was achieved after sintering at 900 °C for 2 h. The low sintering temperature of newly developed capacitor materials allows a co-firing with pure silver electrodes. The dielectric constant and the temperature stability of the dielectric constant are strongly correlated with the composition of the ZnO-B2O3-Li2O additives. A high dielectric constant up to 3000 and a dielectric loss less than 0.024 were measured on multilayer capacitors sintered at 900 °C with silver inner electrodes. KW - BaTiO3 and titanates KW - Capacitors KW - Dielectric properties KW - LTCC PY - 2011 U6 - https://doi.org/10.1016/j.jeurceramsoc.2010.10.003 SN - 0955-2219 SN - 1873-619X VL - 31 IS - 4 SP - 589 EP - 596 PB - Elsevier Ltd. CY - Oxford AN - OPUS4-22886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -