TY - JOUR A1 - Menrad, Andreas A1 - Goedecke, Thomas A1 - Gründer, Klaus-Peter A1 - Wagner, M.H. T1 - The internal pressure test in experiment and simulation - Influence of the wall thickness variation and the change of the packaging behavior after the impact of standard liquids N2 - The effect of the wall thickness variation of blow-moulded bodies made of high-density polyethylene on an internal pressure test after prestoring the packaging with standard liquids was evaluated in experiments and simulations. The objects of the investigation were jerrycans used for the transportation and storage of dangerous goods. The wall thickness was determined using two alternative methods to the magnetostatic measurement. These alternative methods are used for research purpose to get a volumetric model of the jerrycan wall as a geometric model for the simulation. The comparison of the experiments and the simulations of the internal pressure test were performed using the digital image correlation method. The integral strain and deformation of the whole jerrycan was detected by measuring the total mass of the jerrycan being filled with water during the internal pressure test. This is a suitable alternative to the optical measurements of local deformation by the digital image correlation method. Prestorage at 40°C without the influence of chemicals strengthens the jerrycan, whereas the swelling effect of butyl acetate and hydrocarbon mixture softens the jerrycan. The comparison with the experiment is necessary to verify the accuracy of the simulation. It shows that the deformation can be simulated more precisely by using the actual measured geometry. The weakening of the high-density polyethylene caused by a hydrocarbon mixture can be simulated using the Arrhenius equation. The aim of the simulation was to discover whether it is possible to use specimens to predict the behaviour of a packaging both after the influence of standard liquids. T2 - 18th IAPRI World packaging conference CY - San Luis Obispo, CA, USA DA - 17.06.2012 KW - Wall thickness KW - Internal pressure test KW - Finite element KW - Simulation KW - Jerrycan PY - 2013 DO - https://doi.org/10.1002/pts.1983 SN - 0894-3214 VL - 26 IS - 6 SP - 311 EP - 326 PB - Wiley CY - Chichester, UK AN - OPUS4-29282 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Joshi, Ranjit A1 - Schulze, Rolf-Dieter A1 - Meyer-Plath, Asmus A1 - Wagner, M.H. A1 - Friedrich, Jörg Florian T1 - Selective surface modification of polypropylene using underwater plasma technique or underwater capillary discharge N2 - Among new types of plasma processes, the underwater plasma is one of the most attractive methods for functionalization of polymer surfaces. The interesting features of plasma solution system are that the material surfaces to be modified remain in contact with the plasma-moderated solution. The role of plasma-moderated liquids, allows the reach of the reactive species through solution onto the geometrically hindered sites. The UV radiation produced in plasma formation helps in generating additional excited, ionized, and dissociated molecules and species in the reaction solution. An interesting feature of the technique is its flexibility to use a wide variety of additives as or in solution system. This allows us to create a selective or monotype functionalization of material surfaces. Such system was studied for the selective hydroxyl functionalization of polypropylene surface. The oxidation of polymer surfaces and the introduction of O-containing functional groups by underwater plasma was found to exceed concentrations typically achieved in oxygen low-pressure gas discharge plasmas up-to two-folds (maximal 56 O/100 C). The fraction of OH groups among all O-containing moieties amounts from 25 to 40% in comparison to that in the gas plasma of about 10% OH groups. Addition of hydrogen peroxide into this same system increases the fraction of C—O bonds up to 75% (27-OH/100 O). A study was focused to optimize the role of hydrogen peroxide on the efficiency of oxidation and selectivity with chemical derivatization with respect to the formation of mono-sort hydroxyl functionalities, calculated using a chemical derivatization technique. KW - Capillary discharge KW - Functionalization of polymer KW - Modification surfaces KW - Underwater plasma KW - Surface modification KW - Polymer functionalization PY - 2009 DO - https://doi.org/10.1002/ppap.200930601 SN - 1612-8850 SN - 1612-8869 VL - 6 IS - Suppl. 1 SP - 5218 EP - 5222 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-22772 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Joshi, Ranjit A1 - Friedrich, Jörg Florian A1 - Wagner, M.H. T1 - Study of carboxylic functionalization of polypropylene surface using the underwater plasma technique N2 - Non-equilibrium solution plasma treatment of polymer surfaces in water offers the possibility of more dense and selective polymer surface functionalization in comparison to the well-known and frequently used low-pressure oxygen plasma. Functional groups are introduced when the polymer surface contacts the plasma moderated solution especially water solutions. The emission of ions, electrons, energy-rich neutrals and complexes, produced by the ion avalanche are limited by quenching, with the aid of the ambient water phase. The UV-radiation produced in plasma formation also helps to moderate the reaction solution further by producing additional excited, ionized/dissociated molecules. Thus, monotype functional groups equipped polymer surfaces, preferably OH groups, originating from the dissociated water molecules, could be produced more selectively. An interesting feature of the technique is its flexibility to use a wide variety of additives in the water phase. Another way to modify polymer surfaces is the deposition of plasma polymers carrying functional groups as carboxylic groups used in this work. Acetic acid, acrylic acid, maleic and itaconic acid were used as additive monomers. Acetic acid is not a chemically polymerizing monomer but it could polymerize by monomer/molecular fragmentation and recombination to a cross linked layer. The other monomers form preferably water-soluble polymers on a chemical way. Only the fragmented fraction of these monomers could form an insoluble coating by cross linking to substrate. The XPS analysis was used to track the alterations in -O-CO- bond percentage on the PP surface. To identify the -COOH groups on substrate surface unambiguously, which have survived the plasma polymerization process, the derivatization with trifluoroethanol was performed. KW - Polymeroberflächen KW - Funktionelle Gruppen PY - 2009 DO - https://doi.org/10.1140/epjd/e2009-00088-6 SN - 1434-6060 VL - 54 IS - 2 SP - 249 EP - 258 PB - Springer CY - Berlin AN - OPUS4-19607 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Menrad, Andreas A1 - Goedecke, Thomas A1 - Wagner, M.H. T1 - Drop test of plastic packagings - Correlation with material parameters and change of packaging behaviour after impact of standard liquids N2 - A guided drop test was performed to achieve a defined and reproducible impact orientation of jerrycans. The drop heights where 50% of the jerrycans experienced a failure from a crack where fluid can escape (50% failure drop height) were compared among jerrycans made of four different materials, in their original state and preconditioned with standard liquids. To analyse the impact of only elevated temperatures, the packages were preconditioned for 21?days at 40°C without the use of chemicals. The 50% failure drop height was compared by using Young's modulus; the notched impact strength (NIS) of specimen cut from plates which were manufactured by compression moulding and the notched tensile impact strength of specimen cut-outs of the jerrycans' side walls. The NIS depends highly on the thermal preconditioning of the plates being manufactured by compression moulding. A trend can be seen that a higher Young's modulus, a higher NIS and a higher notched tensile impact strength result in a higher 50% failure drop height, but the values are spread. The influence of the wall thickness cannot be neglected. The change of the 50% failure drop height in regard to the preconditioning at 40°C with and without nitric acid was compared in terms of their resistance to molecular degradation, density and degree of crystallinity. The conditioning at elevated temperature causes post-crystallization. It was shown that the resistance to molecular degradation determined on pressed plates correlates with the change of the 50% failure drop height after pre-storage with nitric acid. KW - HDPE KW - Drop test KW - Notched impact strength KW - Tensile impact strength KW - Molecular degradation PY - 2014 DO - https://doi.org/10.1002/pts.2042 SN - 0894-3214 VL - 27 IS - 6 SP - 479 EP - 493 PB - Wiley CY - Chichester, UK AN - OPUS4-32640 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -