TY - JOUR A1 - Schartel, Bernhard A1 - Frasca, Daniele A1 - Schulze, Dietmar A1 - Wachtendorf, Volker A1 - Krafft, Bernd A1 - Morys, Michael A1 - Böhning, Martin A1 - Rybak, Thomas T1 - Multilayer graphene rubber nanocomposites N2 - Multilayer Graphene (MLG), a nanoparticle with a specific surface of BET = 250 m²/g and thus made of only approximately 10 graphene sheets, is proposed as a nanofiller for rubbers. When homogenously dispersed, it works at low loadings enabling the replacement of carbon black (CB), increase in efficiency, or reduction in filler concentration. Actually the appropriate preparation yielded nanocomposites in which just 3 phr are sufficient to significantly improve the rheological, curing and mechanical properties of different rubbers, as shown for Chlorine-Isobutylene-Isoprene Rubber (CIIR), Nitrile-Butadiene Rubber (NBR), Natural Rubber (NR), and Styrene-Butadiene Rubber (SBR). A mere 3 phr of MLG tripled the Young’s modulus of CIIR, an effect equivalent to 20 phr of carbon black. Similar equivalents are observed for MLG/CB mixtures. MLG reduces gas permeability, increases thermal and electrical conductivities, and retards fire behavior. The later shown by the reduction in heat release rate in the cone calorimeter. The higher the nanofiller concentration is (3 phr, 5 phr, and 10 phr was investigated), the greater the improvement in the properties of the nanocomposites. Moreover, the MLG nanocomposites improve stability of mechanical properties against weathering. An increase in UV-absorption as well as a pronounced radical scavenging are proposed and were proved experimentally. To sum up, MLG is interesting as a multifunctional nanofiller and seems to be quite ready for rubber development. T2 - TOP 2016, VIII International Conference on “Times of Polymers and Composites” CY - Naples, Italy DA - 19.06.2016 KW - Graphene KW - Nanocomposite KW - Rubber PY - 2016 SN - 978-0-7354-1390-0 DO - https://doi.org/10.1063/1.4949621 SN - 0094-243X SN - 1551-7616 VL - 1736 SP - 020046, 1 EP - 4 PB - AIP AN - OPUS4-36864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Niebergall, Ute A1 - Zanotto, M. A1 - Wachtendorf, Volker A1 - Böhning, Martin T1 - Impact of biodiesel sorption on tensile properties of PE-HD for container applications N2 - In previous papers, we investigated the influence of biodiesel or diesel on mechanical properties of a high-density polyethylene (PE-HD) for tank applications using Charpy impact tests and dynamicmechanical analysis (DMA). In this work, covering two more PE-HD materials, we extend our study to addressing the tensile properties, especially changes of Young's modulus, after immersion in biodiesel or diesel at 60 °C. As we cover sorption and desorption behavior, during desorption, i.e. storage at 60 °C in a circulating air oven, ageing or degradation phenomena were also observed and characterized in some detail using spectral reflectance measurements and FT-IR spectroscopy. The results obtained here support the concept of co-oxidation, i.e. the faster oxidation of the PE-HD matrix if the samples were previously saturated with biodiesel, itself easily oxidizable. KW - polyethylene KW - biodiesel KW - biofuels KW - sorption KW - plasticization KW - degradation PY - 2016 DO - https://doi.org/10.1016/j.polymertesting.2016.01.025 SN - 0142-9418 VL - 50 SP - 315 EP - 324 PB - Elsevier AN - OPUS4-35369 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kalbe, Ute A1 - Krüger, Oliver A1 - Wachtendorf, Volker A1 - Berger, Wolfgang A1 - Hally, S. T1 - Development of leaching procedures for synthetic turf systems containing scrap tyre granules N2 - Scrap tyres are widely reused in the form of granules as infill materials or component of sub-base layers in construction of sporting grounds such as synthetic turf areas and athletic track surfaces. The recycled rubber may contain organic and inorganic pollutants due to the presence of vulcanisation catalysts, stabilisers and other additives which can be released into soil and groundwater in the case of outdoor sports facilities. In order to evaluate the amount of potentially mobile pollutants, leaching tests can be employed. This study aimed particularly at the investigation of the feasibility of column tests using complete synthetic surface flooring or turf system assemblies. The release of zinc and polycyclic aromatic hydrocarbons (PAH) leached from components of sports surfaces containing recycled rubber granules was considered. Additionally, batch tests on coated and uncoated styrene butadiene rubber (SBR) granules aged by artificial weathering were performed to indicate its possible influence on the leaching behaviour of zinc and PAH. The chosen approach of column tests simulating typical complete synthetic sports surface installations has been proven to be feasible and robust. The time-dependent leaching behaviour and interactions between single components can be evaluated by column tests. Zinc was the most relevant contaminant in the eluates and its leachability was enhanced after accelerated ageing by artificial weathering. Leachable PAH were found in relatively low but well detectable amounts which increase by ageing as well. KW - Waste rubber KW - SBR KW - Artificial turf KW - Leaching KW - behaviour KW - Column test KW - Batch test KW - Weathering PY - 2013 DO - https://doi.org/10.1007/s12649-013-9248-5 SN - 1877-2641 SN - 1877-265X VL - 4 IS - 4 SP - 745 EP - 757 PB - Springer Science + Business Media CY - Dordrecht AN - OPUS4-29454 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wachtendorf, Volker A1 - Kalbe, Ute A1 - Krüger, O. A1 - Bandow, Nicole ED - Brown, R. ED - Gedde, U.W. ED - Hedenqvist, M.S. T1 - Influence of weathering on the leaching behaviour of zinc and PAH from synthetic sports surfaces N2 - Synthetic materials used for outdoor sports grounds consist of a mix of inorganic, organic and polymeric compounds that show ageing due to weathering and a complex leaching behaviour by percolation of rainwater, which can limit its lifetime. Additionally, weathering exposure induces degradation processes in the polymers, which leads to the formation of new surfaces allowing water to access additional reservoirs of leachable compounds. A laboratory test comprising artificial weathering, ozonisation and subsequent leaching was developed to investigate this behaviour in a reproducible and controllable way. The experiments showed a general decline of Zn, polycyclic aromatic hydrocarbons (PAH) and total organic carbon (TOC) concentrations after an initial increase. Within this general trend, the course of concentration over exposure duration is very specific for individual sample materials and the analyte under investigation. The results indicate that weathering and degradation behaviour cannot be predicted from initial material conditions. Thus, weathering experiments are recommended to fill this gap of knowledge. KW - Athletic tracks KW - Artificial turf KW - Ageing KW - Artificial weathering KW - Polymer degradation KW - Rubber granules KW - Leaching KW - Contamination PY - 2017 DO - https://doi.org/10.1016/j.polymertesting.2017.09.021 SN - 0142-9418 SN - 1873-2348 VL - 63 IS - October SP - 621 EP - 631 PB - Elsevier Ltd. CY - Amsterdam, The Netherlands AN - OPUS4-42205 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Erdmann, Maren A1 - Kleinbub, Sherin A1 - Wachtendorf, Volker A1 - Schütter, Jan David A1 - Niebergall, Ute A1 - Böhning, Martin A1 - Koerdt, Andrea T1 - Photo-oxidation of PE-HD affecting polymer/fuel interaction and bacterial attachment N2 - In the present study, a simple approach was used to investigate the effect of UV-exposure on two high density Polyethylene materials (PE-HD), commonly used for storage tanks, on fuel sorption behavior and colonization by microorganisms. The aim was to investigate whether the sorption behavior of the fuels (diesel/biodiesel) and the colonization by microorganisms, frequently occurring in the fuel, is affected and may lead to undesirable or safety-relevant material changes. We showed that the UV-irradiation leads to significant changes of the sorption behavior due to chemi-crystallization and crosslinking. The fuel Sorption is affected by the UV-induced formation of polar carbonyl and hydroxyl groups predominantly occurring at the surface. With respect to microbial colonization behavior for Bacillus subtilis and Pseudomonas aeruginosa, isolated from a contaminated diesel sample, differences of the initial adhesion could be shown depending on the initial type of polyethylene as well as on the degree of UV-induced degradation. KW - High density polyethylene KW - Bacterial attachment KW - UV-irradiation KW - Fuel sorption PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-510001 DO - https://doi.org/10.1038/s41529-020-0122-1 VL - 4 IS - 1 SP - Article number: 18 PB - Nature Partner Journals AN - OPUS4-51000 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Frasca, Daniele A1 - Schulze, Dietmar A1 - Wachtendorf, Volker A1 - Krafft, Bernd A1 - Rybak, Thomas A1 - Schartel, Bernhard T1 - Multilayer Graphene/Carbon Black/Chlorine Isobutyl Isoprene Rubber Nanocomposites N2 - High loadings of carbon black (CB) are usually used to achieve the properties demanded of rubber compounds. In recent years, distinct nanoparticles have been investigated to replace CB in whole or in part, in order to reduce the necessary filler content or to improve performance. Multilayer graphene (MLG) is a nanoparticle made of just 10 graphene sheets and has recently become commercially available for mass-product nanocomposites. Three phr (part for hundred rubbers) of MLG are added to chlorine isobutyl isoprene rubber (CIIR)/CB composites in order to replace part of the CB. The incorporation of just 3 phr MLG triples the Young’s modulus of CIIR; the same effect is obtained with 20 phr CB. The simultaneous presence of three MLG and CB also delivers remarkable properties, e.g. adding three MLG and 20 phr CB increased the hardness as much as adding 40 phr CB. A comprehensive study is presented, showing the influence on a variety of mechanical properties. The potential of the MLG/CB combination is illustrated to reduce the filler content or to boost performance, respectively. Apart from the remarkable mechanical properties, the CIIR/CB/MLG nanocomposites showed an increase in weathering resistance. KW - nanocomposites KW - rubber KW - multilayer graphene KW - carbon black PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-358569 DO - https://doi.org/10.3390/polym8030095 SN - 2073-4360 VL - 8 SP - 95 PB - MDPI CY - Basel, Switzerland AN - OPUS4-35856 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker T1 - Wirkung simulierter Sonnenstrahlung auf Kohlenstoffnanoröhren gefüllte Polymerkomposite T2 - 43. Jahrestag der GUS 2014 - Umwelteinflüsse erfassen, simulieren, bewerten CY - Stutensee, Germany DA - 2014-03-26 PY - 2014 AN - OPUS4-30647 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barthel, Anne-Kathrin A1 - Wachtendorf, Volker A1 - Sturm, Heinz A1 - Meyer-Plath, Asmus ED - Reichert, T. T1 - Irradiation-induced surface changes on CNT-filled polymeric materials N2 - The present study examines weathering-related degradation mechanisms of CNT-containing polymers and discusses whether and under what conditions degradation might lead to the release of nanoscale components. For this purpose, the study used accelerated artificial aging. The photodegradation of composites based polycarbonate containing multi-walled CNTs of type "Baytubes C150P" was studied under irradiation with a Xenon-arc irradiation device (λ-cut-off at 290 nm). Resulting surface modifications were evaluated with complementary chemical and microscopic characterization techniques. At sufficiently high radiation dose, a significant degradation of the matrix was observed for some of the polymers under examination which led to entangled networks of uncovered CNT at the composite surface. By investigation of potential exposure mechanisms of CNTs in polymer composites, the present work contributes to the risk assessment of CNT-containing products. T2 - 6th European weathering symposium Natural and artificial ageing of polymers CY - Bratislava, Slovak Republic DA - 11.09.2013 PY - 2013 SN - 978-3-9813136-8-0 N1 - Serientitel: CEEES Publication – Series title: CEEES Publication IS - 16 SP - 295 EP - 308 AN - OPUS4-31161 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Barthel, Anne-Kathrin A1 - Wachtendorf, Volker A1 - Sturm, Heinz A1 - Meyer-Plath, A. ED - Ziegahn, K.-F. T1 - Wirkung simulierter Sonnenstrahlung auf Kohlenstoffnanoröhren gefüllte Polymerkomposite N2 - Durch das Füllen von Polymeren mit Nanopartikeln oder Nanoröhren werden verbesserte Materialeigenschaften z.B. bezüglich mechanischer Stabilität, Witterungsbeständigkeit, elektrischer Leitfähigkeit und Flammschutz angestrebt. Mit dem vermehrten Einsatz derartiger Nanokomposite gewinnen aber auch Fragen des Umwelt- und Gesundheitsschutzes an Bedeutung. Es gilt zu klären, ob durch Herstellung, Benutzung und Witterungsbeanspruchung möglichweise nanoskalige Partikel freigesetzt werden können. Zu diesem Zweck wurden mit Kohlenstoffnanoröhren, Carbon Nanotubes (CNT), gefüllte Polymerkomposite spektral breitbandig wie auch quasimonochromatisch unter variierter klimatischer Beanspruchung bestrahlt. Die sich vor allem an der Oberfläche mit der Alterung abzeichnenden Veränderungen wurden mikroskopisch und spektroskopisch charakterisiert. T2 - 43. Jahrestagung der GUS 2014 CY - Stutensee-Blankenloch, Germany DA - 26.03.2014 KW - Nanokomposit KW - Nanopartikel KW - CNT KW - Bewitterung KW - Bestrahlung KW - Simulierte Sonnenstrahlung KW - Alterung PY - 2014 SN - 978-3-9816286-0-9 SP - 65 EP - 74 AN - OPUS4-31160 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wachtendorf, Volker T1 - Maßgeschneiderte künstliche Bewitterungstests zur Untersuchung der alterungsbedingten Freisetzung von Produkten in die Umwelt N2 - Genormte künstliche Bewitterungstests sind häufig nicht spezifisch für die Anwendungssituation oder das Material. Das macht die Entwicklung spezifischer Tests erforderlich. Für deren Entwicklung müssen Maximalparameter der Anwendungssituation bekannt sein, womit dann der künstliche Test formuliert wird und dessen Bedingungen werden dann solange optimiert, bis die Korrelation der Effekte von natürlichem und künstlichem Test ausreichend ist. Für Untersuchungen der Freisetzung kann der verbleibende Rest in der Probe und/oder die freigesetzte Menge in Luft, Boden, Wasser bestimmt werden. Im ersten Beispiel der Witterungswirkung wurde die Freisetzung von Kohlenstoff-Nanoröhrchen (CNT) aus Polymer-Kompositen untersucht (unter Verwendung von empfindlich-nachweisbarer radioaktiver 14C-Markierung für einzelne CNT-Partikel), in einem zweiten die Freisetzung von anorganischen und organischen Bestandteilen aus elastomeren Bestandteilen von Sportböden (Bahnen und Kunstrasen) in Wasser. T2 - SKZ-Tagung: Bewitterung van Kunststoffen CY - Würzburg, Germany DA - 06.07.2022 KW - Künstliche Bewitterung KW - UV KW - Degradation KW - Freisetzung KW - CNT KW - Carbo-Nanotubes KW - Composite KW - Nano-Partikel KW - 14C-Markierung KW - Sportböden KW - Kunstrasen KW - Grundwasser PY - 2022 AN - OPUS4-55219 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Rhiem, S. A1 - Barthel, Anne-Kathrin A1 - Meyer-Plath, A. A1 - Hennig, M. P. A1 - Wachtendorf, Volker A1 - Sturm, Heinz A1 - Schäffer, A. A1 - Maes, H. M. T1 - Release of 14C-labelled carbon nanotubes from polycarbonate composites N2 - Waste disposal of carbon nanotube (CNT) containing products is expected to be the most important pathway for release of CNTs into the environment. In the present work, the use of radiolabelled CNTs (14C-CNT) for polycarbonate polymer nanocomposites with 1 wt% 14C-CNT content allowed for the first time to quantify and differentiate the CNT release according to the type of impact along the materials' ageing history. After an initial exposure of the nanocomposite by solar-like irradiation, further environmental impacts were applied to composite material. They aimed at mimicking disposal site conditions that may induce further ageing effects and CNT release. This study included shaking in water, rapid temperature changes, soaking in humic acid solution as well as waste water effluent, and, finally, gentle mechanical abrasion. All ageing impacts were applied sequentially, both on pristine (control) and on solar-irradiated nanocomposites. All experiments were accompanied by absolute quantification of radioactive release as well as chemical and morphological analyses of the nanocomposite surfaces using infra-red (IR) spectroscopy, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM). The morphological analysis showed that spectral irradiation can uncover CNT networks on the outer nanocomposite surface layers by polymer degradation. After having subjected the solar-irradiated nanocomposite to all studied disposal site effect, the total radioactive release was quantified to amount to 64 mg CNT/m2, whereas only 0.8 mg CNT/m2 were found for the un-irradiated control sample. Solar degradation of polymers was thus found to significantly increase the propensity of the studied polymer nanocomposites to release CNTs during ageing effects at the product's end-of-life typical for disposal sites. KW - Weathering KW - Carbon nanotubes KW - Nanocomposites KW - Release KW - Quantification PY - 2016 UR - http://www.sciencedirect.com/science/article/pii/S0269749116303748 DO - https://doi.org/10.1016/j.envpol.2016.04.098 SN - 0269-7491 VL - 215 IS - August SP - 356 EP - 365 PB - Elsevier Ltd. CY - Paris AN - OPUS4-36899 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wachtendorf, Volker A1 - Stephan, Ina A1 - Schulz, Ulrich A1 - Petzold, I. T1 - Die komplexe Wirkung von Schimmelpilz und Klima auf Polymeroberflächen und ihre Simulation im Labor T2 - 33. Jahrestagung der GUS, "Umwelteinflüsse erfassen, simulieren, bewerten" CY - Pfinztal, Deutschland DA - 2004-03-17 PY - 2004 SN - 3-9808382-4-2 SP - 69 EP - 84 PB - GUS CY - Pfinztal AN - OPUS4-4880 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kömmling, Anja A1 - Chatzigiannakis, E. A1 - Beckmann, Jörg A1 - Wachtendorf, Volker A1 - von der Ehe, Kerstin A1 - Braun, Ulrike A1 - Jaunich, Matthias A1 - Schade, U. A1 - Wolff, Dietmar T1 - Discoloration Effects of High-Dose gamma-Irradiation and Long-Term Thermal Aging of (U) HMW-PE N2 - Two polyethylene types with ultra-high (UHMWPE) and high molecular weight (HMW-PE) used as neutron radiation shielding materials in casks for radioactive waste were irradiated with doses up to 600 kGy using a 60Co gammasource. Subsequently, thermal aging at 125∘C was applied for up to one year. Degradation effects in the materials were characterized using colorimetry, UV-Visspectroscopy, IR spectroscopy, and DSC. Both materials exhibited a yellowing upon irradiation.The discoloration of UHMW-PE disappeared again after thermal aging.Therefore, the yellowing is assumed to originate fromannealable color centers in the formof free radicals that are trapped in the crystalline regions of the polymer and recombine at elevated temperatures. For the antioxidantcontaining HMWPE, yellowing was observed after both irradiation and thermal aging. The color change was correlated mainly to decomposition products of the antioxidant in addition to trapped radicals as in UHMW-PE. Additionally, black spots appeared after thermal aging of HMW-PE. KW - Irradiation KW - UHMWPE KW - Colour center KW - Yellowness index PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-423992 DO - https://doi.org/10.1155/2017/1362491 SN - 1687-9422 VL - 2017 IS - Article ID 1362491 SP - 1 EP - 10 PB - Hindawi AN - OPUS4-42399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Metz, Christian A1 - Franz, Philipp A1 - Fischer, C. A1 - Wachtendorf, Volker A1 - Maierhofer, Christiane T1 - Zerstörungsfreie Charakterisierung der Alterung additiv gefertigter Kunststoffbauteile N2 - Das vorgestellte Projekt beschäftigt sich mit den optischen, thermophysikalischen und mechanischen Materialeigenschaften von additiv gefertigten Kunststoffteilen und deren Alterung. Dazu wurden mittels Fused Layer Modeling (FLM) Probekörper aus ABS hergestellt, die anschließend für drei Monate einer künstlichen Bewitterung unterzogen wurden. Die dabei erzeugte definierte Alterung wurde nach drei Zeitabschnitten jeweils mit zerstörungsfreien Methoden charakterisiert. Dabei wurde neben den spektroskopischen Standardmethoden auch die aktive Thermografie eingesetzt. Die Ergebnisse zeigen, dass sich mittels der Thermografie sowohl chemische Veränderungen als auch mechanische Schädigungen (Fehlstellen) darstellen lassen. Die Bewitterung beeinflusst die Teiltransparenz der Proben zumindest im sichtbaren Spektralbereich, was bei der Charakterisierung der Fehlstellen, die mittels optisch angeregter aktiver Thermografie detektiert wurden, berücksichtigt werden muss. T2 - DGZfP-Jahrestagung 2019 CY - Friedrichshafen, Germany DA - 27.05.2019 KW - 3D Druck KW - Additive Fertigung KW - Thermografie KW - Polymere KW - Künstliche Bewitterung PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-491561 UR - https://jt2019.dgzfp.de/Portals/jt2019/bb/Di.3.B.1.pdf SN - 978-3-947971-02-2 VL - 171 SP - 1 EP - 8 PB - Deutsche Gesellschaft für Zerstörungsfreie Prüfung (DGZfP) CY - Berlin AN - OPUS4-49156 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Metz, Christian A1 - Franz, Philipp A1 - Maierhofer, Christiane A1 - Wachtendorf, Volker A1 - Fischer, C. ED - Ziegahn, K.-F. T1 - Untersuchung der Beständigkeit additiv gefertigter Bauteile durch Thermografie nach künstlicher Bewitterung N2 - Additiv gefertigte Prüfkörper aus Polyamid 12 (Laser Sinter Verfahren) und Acrylnitril-Butadien-Styrol (Fused Layer Modeling Verfahren) wurden über 2000 Stunden künstlich bewittert und ihr Alterungsverhalten untersucht. Die Ergebnisse wurden anschließend mit denen von Prüfkörpern verglichen, welche auf dieselbe Weise künstlich bewittert, aber mittels konventionellem KunststoffSpritzguss hergestellt wurden. T2 - 48. Jahrestagung der GUS 2019 CY - Stutensee, Germany DA - 27.03.2019 KW - Polymere KW - Additive Fertigung KW - 3D Druck KW - Künstliche Bewitterung KW - Thermografie PY - 2019 SN - 978-3-9818507-3-4 VL - 48 SP - 207 EP - 216 CY - Pfinztal (Berghausen) AN - OPUS4-48502 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Metz, Christian A1 - Franz, Philipp A1 - Fischer, C. A1 - Wachtendorf, Volker A1 - Maierhofer, Christiane T1 - Active thermography for quality assurance of 3D-printed polymer structures N2 - Additively manufactured test specimens made of polyamide 12 (PA 12) by Laser Sintering as well as of acrylonitrile butadiene styrene (ABS) by Fused Layer Modelling, were characterised with active thermography directly after manufacturing and after artificial weathering. For this, two different excitation methods (flash and pulse heating) were used and compared, regarding their suitability for the detection of constructed and imprinted defects inside the test specimens. To increase the quality of the thermograms, data processing methods like thermal signal reconstruction (TSR) and Fourier Transformation after TSR were applied. To further investigate the long-term stability of the additively manufactured test specimens towards environmental stress, like UV radiation, heat, humidity, water contact and frost with active thermography, an artificial weathering test over 2000 hours (~3 months) was applied to the specimens. The monitoring of the changes in the optical properties of the weathered plastics was supplemented by spectral reflectance and UV/VIS spectroscopy. KW - Additive manufacturing KW - Polymers KW - Artificial weathering KW - Active thermography KW - UV/VIS spectroscopy PY - 2019 DO - https://doi.org/10.1080/17686733.2019.1686896 SN - 1768-6733 (Print) 2116-7176 (Online) VL - 18 IS - 1 SP - 50 EP - 72 PB - Taylor & Francis AN - OPUS4-49817 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Vega Puga, E. A1 - Wachtendorf, Volker A1 - Kömmling, Anja A1 - Brendelberger, S. A1 - Jaunich, Matthias A1 - Sattler, C. T1 - Lifetime prediction and degradation assessment of FKM and FFKM O-rings under high temperature thermo-oxidative ageing N2 - To support the development of solar reactor technologies for hydrogen production, this study investigates the thermo-oxidative degradation mechanisms of fluorinated elastomers and predicts their lifetimes at high temperatures (200–300 ◦C) consistent with the application requirements. An accelerated ageing programme is conducted with FKM and FFKM O-rings and flat samples for up to 21 days. Optical microscopy is used to analyse the exposed seals’ morphological changes, while IR microscopy is utilised to investigate the underlying chemical degradation mechanisms of both elastomers. Findings suggest that FKM’s degradation arises from dehydrofluorination of the polymer, followed by chain scission and backbone cleavage as a result of the oxidation of newly formed C=C double bonds. FFKM’s degradation is primarily associated with chain scission, but there is also indication that post-curing processes may occur during material ageing. Furthermore, hardness, equilibrium compression set (CS), continuous compression stress relaxation (CSR) and leakage rate tests are used to evaluate changes in the mechanical properties and sealing performance of the elastomers. Equilibrium CS data is extrapolated using time-temperature shifts (TTS) and used to derive an end-of-life criterion of 75 % equilibrium CS, which correlates to leakage rates higher than a predetermined threshold. Service lifetime predictions of FKM and FFKM O-rings at several temperatures are performed and a seal operating temperature of 200 ◦C is suggested, which ensures reasonable O-ring replacement intervals of more than half a year in the solar reactor for both considered materials. KW - Fluoroelastomer KW - Perfluoroelastomer KW - Thermo-oxidative ageing KW - Lifetime prediction KW - Compression set PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-630112 DO - https://doi.org/10.1016/j.polymertesting.2025.108820 SN - 1873-2348 VL - 147 SP - 1 EP - 17 PB - Elsevier BV CY - Amsterdam AN - OPUS4-63011 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Tang, S. A1 - Wachtendorf, Volker A1 - Klack, Patrick A1 - Qian, Lijun A1 - Dong, Y. A1 - Schartel, Bernhard T1 - Enhanced flame-retardant effect of montmorillonite/phosphaphenanthrene compound in an epoxy thermoset N2 - A phosphaphenanthrene and triazinetrione group containing flame retardant (TAD) is combined with organically modified montmorillonite (OMMT) in epoxy resin thermosets (EP) to improve the performance of the flame-retardant system. When only 1 wt% OMMT/4 wt% TAD is introduced into the EP, the limited oxygen index (LOI) rises from 26% to 36.9% and a V-0 rating is achieved in a UL 94 test. The decomposition and pyrolysis products in the gas phase and condensed phase were characterized using thermogravimetry-Fourier transform infrared spectroscopy (TG-FTIR). The influence on the decomposition of EP, such as the increase in char yield, is limited with the incorporation of OMMT; a large amount of the phosphorus is released into the gas phase. The flame-retardant effect evaluation based on cone calorimeter data testified that OMMT improves the protective-barrier effect of the fire residue of OMMT/TAD/EP on the macroscopic scale, while TAD mainly causes flame inhibition. The fire residues showed a corresponding macroscopic appearance (digital photo) and microstructure (scanning electron microscope [SEM] results). The protective barrier effect of OMMT and the flame-inhibition effect of TAD combined to exert a superior flame-retardant effect, resulting in sufficient flame-retardant performance of OMMT/TAD/EP KW - Flame retardant KW - Nanocomposite KW - DOPO KW - Thermoset KW - Epoxy resin KW - TG-FTIR PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-388865 DO - https://doi.org/10.1039/c6ra25070j SN - 2046-2069 VL - 7 IS - 2 SP - 720 EP - 728 AN - OPUS4-38886 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schilling, Markus A1 - Marschall, Niklas A1 - Niebergall, Ute A1 - Wachtendorf, Volker A1 - Böhning, Martin T1 - Unveiling Effects of Biodiesel and Diesel on Environmental Stress Cracking of PE-HD N2 - The behavior of high‐density polyethylene with respect to resistance against environmental stress cracking (ESC) is usually regarded as an inherent material property being specific for respective types of PE‐HD and tested using standardized methods, conditions, and also standard testing liquids (usually aqueous surfactant solutions). On the other hand, for practical applications the ESC behavior of those polymeric materials, commonly used for pipes or containers, in contact with other liquids (e.g., fuels) is often of relevant interest, but for a reasonable assessment, where consistent benchmark data for a direct comparison are often missing, it is essential to determine the actually prevailing failure mode and classify it related to crack propagation or other mechanisms. Using the well‐established Full Notch Creep Test, which favorably allows for a detailed microscopic fracture surface analysis after failure, the behavior of two typical PE‐HD types for container applications is investigated in biodiesel and diesel and compared to a standard surfactant solution. This enables a clear identification of characteristic features of the interaction of biodiesel and diesel as sorptive fuels in contact with the polymer, revealing the complex interplay of sorption and plasticization as well as ESC inducing effects on PE‐HD, which could be clearly shown for both fuels. KW - Biodiesel KW - Confocal laser scanning microscopy (LSM) KW - Diesel KW - Full notch creep test (FNCT) KW - Plasticization PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-650525 DO - https://doi.org/10.1002/pen.70239 SN - 0032-3888 SP - 1 EP - 16 PB - Wiley CY - Hoboken (NJ) AN - OPUS4-65052 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ramanujam, Maalolan A1 - Wachtendorf, Volker A1 - Purohit, Purv A1 - Mix, Renate A1 - Schönhals, Andreas A1 - Friedrich, Jörg Florian T1 - A detailed dielectric relaxation spectroscopy study of artificial UV weathered low density polyethylene N2 - Artificial weathering of LDPE under dry conditions (<10% of relative humidity) by UV radiation was monitored by dielectric spectroscopy. For an apolar polymer like LDPE, dielectric study yields Information about the change in structure and dynamics of the system. The fluctuations of the polar groups which are generated as a result of photooxidation such as carbonyl groups can be monitored as characteristic relaxation processes like the αc or β mode. The dielectric loss characterized by typical dielectric parameters like the activation energy and dielectric strength are strongly dependent upon changes induced by photooxidation in the amorphous and crystalline domains. This paper discusses in detail how the foil reached its mechanical disintegration. It was found that initial stages of weathering induce chain scission and/or crosslinking in the amorphous domains of the polymer and the motional processes in the crystalline regions are not affected. After this induction period, an increase in the degree of crystallization was observed by employing differential calorimetry. The increasing crystallinity is considered as one of the reasons for embrittlement which finally leads to the complete loss of the structural integrity. KW - Artificial weathering KW - UV radiation KW - Dielectric relaxation KW - LDPE PY - 2012 DO - https://doi.org/10.1016/j.tca.2011.12.003 SN - 0040-6031 SN - 1872-762X VL - 530 SP - 73 EP - 78 PB - Elsevier CY - Amsterdam AN - OPUS4-25547 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -