TY - JOUR A1 - Wäsche, Rolf A1 - Klaffke, Dieter T1 - Wear of multiphase SiC based ceramic composites containing free carbon N2 - Ceramics are of increasing interest for application in many branches of technique. In order to improve the tribological performance of ceramic materials, composites on the basis of silicon carbide with different amounts of titanium carbide, boron carbide, titanium diboride and free carbon in the form of graphite were manufactured by a reaction sintering process. The friction and wear behaviour of these composites was investigated with oscillating sliding motion in unlubricated tests at room temperature on different levels of relative humidity. Additional tests were performed under water lubrication, revealing the superior behaviour of composites for special test conditions. A major influence of the free carbon on friction or wear behaviour was not observed. The tribological behaviour in air as well as under water is mainly dependant on the amount of titanium phases. KW - Siliziumkarbid KW - Verbundwerkstoffe KW - Tribooxidation KW - Silicon carbide KW - Ceramic composites KW - Humidity water KW - Lubrication PY - 2001 DO - https://doi.org/10.1016/S0043-1648(01)00566-X SN - 0043-1648 VL - 249 SP - 220 EP - 228 PB - Elsevier CY - Amsterdam AN - OPUS4-900 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wäsche, Rolf A1 - Habig, Karl-Heinz T1 - Physikalisch-chemische Grundlagen der Feststoffschmierung - Literaturübersicht - N2 - Die für einen erfolgreichen Einsatz von Festschmierstoffen zur Minderung von Reibung und Verschleiß systembestimmender Parameter wie Last, Geschwindigkeit, Temperatur, umgebende Atmosphäre, Filmbildung und -haltung sowie die Anwendungstechnologien werden dargestellt, ferner Modellvorstellungen zum Verschleißverhalten von Festschmierstoffen im Hinblick auf konkrete Anwendungsfälle diskutiert. T3 - BAM Forschungsberichtreihe - 158 KW - Festschmierstoff KW - Transferschmierung KW - Hohe Temperaturen KW - Graphit KW - Reibung KW - Verschleißmodelle KW - gebundene Filme KW - Synergieeffekte PY - 1989 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-2921 SN - 978-3-88314-889-X SN - 0938-5533 VL - 158 SP - 1 EP - 112 PB - Wirtschaftsverlag NW CY - Bremerhaven AN - OPUS4-292 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Wäsche, Rolf A1 - Köse, Fatma T1 - Einfluß der Verfahrensparameter beim Gelcasting auf die Entstehung bruchauslösender Gefügefehler in hochreinen Aluminiumoxidkeramiken N2 - Es wird die Untersuchung des Entlüftungsvorgangs in Keramikschlickern beschrieben, die Teil des Gelcastingprozesses zur Herstellung hochfester Aluminiumoxidkeramiken sind. Ziel der Untersuchung war es, den Einfluss von Viskosität und Entlüftungszeit als prozessvariablen auf die Entstehung von bruchauslösenden Fehlern im Gefüge zu verdeutlichen. T3 - BAM Forschungsberichtreihe - 221 PY - 1997 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-2294 SN - 978-3-89429-036-4 SN - 0938-5533 VL - 221 SP - 1 EP - 54 PB - Wirtschaftsverlag NW CY - Bremerhaven AN - OPUS4-229 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dörfel, Ilona A1 - Wäsche, Rolf A1 - Rabe, Torsten A1 - Steinborn, Gabriele T1 - Tribological Induced Microstructural Changes in Subsurface Layers of Si3N4-Based Materials KW - Tribologie PY - 1994 SN - 1013-9826 VL - 89-91 SP - 763 EP - 767 PB - Trans Tech Publ. CY - Aedermannsdorf AN - OPUS4-577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klaffke, Dieter A1 - Hartelt, Manfred A1 - Wäsche, Rolf ED - Bartz, Wilfried J. T1 - Non-Oxide Ceramics as Tribo Materials - Analysis of Wear Mechanisms under Oscillating Sliding Conditions in Various Atmospheres T2 - 12th International Colloquium Tribology CY - Esslingen, Germany DA - 2000-01-11 KW - Tribologie PY - 2000 SN - 3-924813-44-2 VL - 3 SP - 1755 EP - 1763 PB - Techn. Akad. Esslingen CY - Ostfildern AN - OPUS4-848 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wäsche, Rolf T1 - Characterisation of tribological interface in low wear magneli type ceramics T2 - International Conference on Characterisation and Control of Interfaces (ICCC 2009) CY - Kurashiki, Japan DA - 2009-09-06 PY - 2009 AN - OPUS4-22871 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wäsche, Rolf A1 - Woydt, Mathias A1 - Rehmer, Birgit ED - Ewsuk, K. ED - Naito, M. ED - Kakeshita, T. ED - Kirihara, S. ED - Uematsu, K. ED - Abe, H. T1 - Characterization of the tribological interface in low wear Magneli type ceramics N2 - The tribological behaviour under dry sliding conditions of Magneli phase Ti4O7 and e-phase Ti2Cr2O7 with α-alumina as a sliding partner has been characterised at room temperature by oscillating sliding. The mechanical properties as well as Vickers hardness measurements do not reveal big differences between the materials, and 4-point bending strengths are around 200 MPa for both materials. Although the friction coefficients are in the medium range of 0.6 and do not differ much between the materials, the wear behaviour is very different. At room temperature, the wear coefficient of Ti2O7 is strongly dependent on relative humidity, and wear is highest under dry conditions when relative humidity is low as it is typically found for many ceramic materials. Ti2Cr2O7 shows remarkably different wear behaviour with the lowest wear in dry conditions. The measured coefficients of wear at low relative humidity of 4% are more than 2 orders of magnitude lower than those for Ti2O7. T2 - 3rd International conference on characterization and control of interfaces for high quality advanced materials CY - Kurashiki, Japan DA - 2009-09-06 PY - 2009 SN - 978-0-470-90917-1 VL - 219 SP - 111 EP - 116 PB - John Wiley & Sons CY - Hoboken, New Jersey, USA AN - OPUS4-21842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Salge, T. A1 - Wäsche, Rolf A1 - Hodoroaba, Vasile-Dan T1 - Advanced light element and low energy X-ray analysis of a TiB2 – TiC – SiC ceramic material using EDS spectrum imaging N2 - The accurate EDS microanalysis of light elements such as boron and carbon by spectrum imaging will be demonstrated using a sintered hard ceramic material composed of the three major phases titanium boride (TiB2), titanium carbide (TiC), silicon carbide (SiC) and minor phases, sub-μm in size. The combination of these three materials leads to improved mechanical and tribological properties. Silicon carbide is a material used for mechanical seals. It has the disadvantage of reduced failsafe running functions, causing increased wear when running dry. The added titanium components (TiC and TiB2) improve the failsafe running functions. This technology has already been transferred to industrial applications. KW - EDS KW - Spectrum imaging KW - Ceramic KW - Phase analysis KW - Light elements PY - 2018 UR - https://www.bruker.com/fileadmin/user_upload/8-PDF-Docs/X-rayDiffraction_ElementalAnalysis/Microanalysis_EBSD/LabReports/App_eds_10_LE_keramik_Rev1_1_lores.pdf SP - 1 EP - 5 CY - Berlin AN - OPUS4-44622 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Wäsche, Rolf T1 - A study on wear particle analysis in lubricated steel-steel contacts T2 - International Tribology Congress/ITC 2015 CY - Tokyo, Japan DA - 2015-09-15 PY - 2015 AN - OPUS4-34324 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Hartelt, Manfred A1 - Wäsche, Rolf A1 - Hodoroaba, Vasile-Dan T1 - Verschleißpartikel-Analyse mit Rasterelektronenmikroskopie und energiedispersiver Röntgenspektrometrie im Transmissionsmodus (TSEM/EDX) N2 - Untersucht wurden Verschleißpartikel als elektronen-transparente Proben auf dünnen Trägerfolien mit einem hochauflösendem Rasterelektronenmikroskop und energiedispersiver Röntgenspektrometrie im Transmissionsmodus. Die hohe laterale Auflösung dieser modernen Methoden ermöglicht eine morphologische Charakterisierung der Verschleißpartikel bis in den nm-Bereich. Die hochauflösende Elementanalyse erlaubt eine Interpretation der Zusammensetzung und damit Rückschlüsse auf die Verschleißpartikelbildung. Die tribologischen Untersuchungen sind an einem Modell-Verschleißtribometer nach DIN 51834-2 geschmiert, aber ohne Ölkreislauf, durchgeführt worden. Die Präparation der Verschleißpartikel über eine Entnahme und Übertragung einer geringen Schmierstoffmenge mit einer Mikropipette auf eine TEM-Trägerfolie ist mit einem geringen Aufwand möglich. Der präparative Aufwand ist relativ gering. Das benötigte Schmierstoffvolumen beträgt wenige Mikroliter (0,001ml). Die Untersuchung zeigt die geringe geometrische Größe der Verschleißpartikel und bestätigt indirekt die These der Reaktionsschichtbildung mit einer geringen Schichtdicke, die ständig verschleißt und sich stetig neu bildet. Die beschriebenen Verschleißprozesse sind in der Modell-Verschleiß-Prüfung mit sehr hohen Pressungen am Versuchsbeginn nachweisbar. T2 - 55. Tribologie-Fachtagung - Reibung, Schmierung und Verschleiß - Forschung und praktische Anwendungen CY - Göttingen, Germany DA - 22.09.2014 PY - 2014 SN - 978-3-00-046545-1 VL - I SP - 05/1 EP - 05/10 AN - OPUS4-31528 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -