TY - JOUR A1 - Bergant, M. A1 - Werner, Tiago A1 - Madia, Mauro A1 - Yawny, A. A1 - Zerbst, Uwe T1 - Short crack propagation analysis and fatigue strength assessment of additively manufactured materials: An application to AISI 316L N2 - This paper presents the application of short crack propagation models based on the cyclic R-curve for assessing the fatigue strength of additively manufactured (AM) materials containing fabrication defects. Chapetti’s and IBESS models were implemented in combination with Murakami’s √area parameter, considering recently published data on laser powder bed fusion processed AISI 316L stainless steels. Estimated S-N curves and Kitagawa-Takahashi diagrams predict fairly well the experimental data, especially the origin of the failure from internal or surface defects. These results provide an indication that the methods based on the cyclic R-curve constitute suitable tools for fatigue behavior assessment of AM materials. KW - AM 316L stainless steel KW - Cyclic R-curve KW - Chapetti’s and IBESS model KW - S-N curve KW - Kitagawa-Takahashi diagram PY - 2021 DO - https://doi.org/10.1016/j.ijfatigue.2021.106396 VL - 151 PB - Elsevier Ltd. AN - OPUS4-53082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Vojtek, T. A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Pokorný, P. A1 - Jambor, M. A1 - Hutař, P. T1 - Determination of fatigue crack propagation thresholds for steel in presence of environmental effects N2 - The experimental determination of the resistance to fatigue crack propagation in steel, particularly in the socalled near-threshold regime, is a crucial issue for safety-relevant components which are designed to operate for a large number of loading cycles before undergoing periodic inspections. This work summarizes the most relevant results of extensive experimental campaigns conducted at BAM and IPM over the last years, which have been devoted to the determination of fatigue crack propagation characteristics on medium and high strength steels. The influence of environment, oxide-induced crack closure and test methodologies in the near-threshold regime are discussed. KW - Steel KW - Fatigue crack propagation threshold KW - Oxide-induced crack closure KW - Environmental effect PY - 2021 DO - https://doi.org/10.1016/j.ijfatigue.2021.106449 SN - 0142-1123 VL - 153 SP - 1 PB - Elsevier Ltd. AN - OPUS4-53525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Vergleichende Untersuchungen zum intrinsischen Schwellenwert der da/dN-ΔK-Kurve N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung, Δ𝐾𝑡ℎ, und dem sich anschließenden Schwellenwertbereich der 𝑑𝑎𝑑𝑁⁄−Δ𝐾-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - 53. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 18.02.2021 KW - Schadenstolerante Bauteilauslegung, Restlebensdauer, intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung PY - 2021 SN - 2366-4797 SP - 211 EP - 220 PB - Deutscher Verband für Materialforschung und -prüfung e.V. (DVM) CY - Berlin AN - OPUS4-52704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Zerbst, Uwe A1 - Madia, Mauro ED - Yadroitsev, I. ED - Yadroitsava, I. ED - Du Plessies, A. ED - McDonald, E. T1 - Structural integrity II: fatigue properties N2 - If a component is cyclically loaded, its load carrying capacity is considerably lower than in the monotonic loading case. This general observation applies in particular to L-PBF parts. The causes of this are mainly material defects such as pores and unwelded regions (Chapter 8) and a pronounced surface roughness in the as-built condition (Chapter 9). In addition, effects due to the anisotropy of the microstructure (Chapter 6) and a complex residual stress pattern (Chapter 7) play an important role. A consequence is that common strategies of fatigue assessment cannot be transferred to L-PBF applications without modifications. Due to the inhomogeneity of the material, the determination of representative material properties and the transfer to the component is a problem, and this is also the case with regard to the consideration of defects, surface roughness and residual stresses. The chapter gives a brief introduction to these problem areas. KW - Fatigue crack propagation stagesdefects KW - Fatigue strength KW - Fatigue life KW - Fracture mechanics PY - 2021 SN - 978-0-12-824090-8 DO - https://doi.org/10.1016/B978-0-12-824090-8.00015-9 SP - 377 EP - 394 PB - Elsevier Inc. CY - Amsterdam ET - 1 AN - OPUS4-52854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Bruno, Giovanni A1 - Buffière, J.-Y. A1 - Wegener, T. A1 - Niendorf, T. A1 - Wu, T. A1 - Zhang, X. A1 - Kashaev, N. A1 - Meneghetti, G. A1 - Hrabe, Nik A1 - Madia, Mauro A1 - Werner, Tiago A1 - Hilgenberg, Kai A1 - Koukolikova, M. A1 - Prochazka, R. A1 - Dzugan, J. A1 - Möller, B. A1 - Beretta, S. A1 - Evans, Alexander A1 - Wagener, R. A1 - Schnabel, K. T1 - Damage tolerant design of additively manufactured metallic components subjected to cyclic loading: State of the art and challenges N2 - This article is an outcome of a workshop on Fatigue of Additive Manufactured Metallic Components jointly organized by the Federal Institute for Materials Research and Testing (BAM) Berlin, Germany and the National Institute of Standards and Technology (NIST) Boulder, CO, U.S.A. The aim of the workshop was a comprehensive discussion of the specific aspects of additively manufactured (AM) components in regard to failure under cyclic loading. Undoubtedly, a better understanding and the further development of approaches for damage tolerant component design of AM parts are among the most significant challenges currently facing the use of these new technologies. This article presents a thorough overview of the workshop discussions. It aims to provide a review of the parameters affecting the damage tolerance of AM parts with special emphasis on the process parameters intrinsic to the AM technologies, the resulting defects and residual stresses. Based on these aspects, concepts for damage tolerant component design for AM are reviewed and critically discussed. KW - Additive manufacturing KW - Fatigue loading KW - Component assessment KW - Damage tolerance KW - Defects KW - Residual stresses PY - 2021 DO - https://doi.org/10.1016/j.pmatsci.2021.100786 SN - 0079-6425 VL - 121 PB - Elsevier CY - Amsterdam AN - OPUS4-51937 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Bruno, Giovanni A1 - Hilgenberg, Kai T1 - Towards a Methodology for Component Design of Metallic AM Parts Subjected to Cyclic Loading N2 - The safe fatigue design of metallic components fabricated by additive manufacturing (AM) is still a largely unsolved problem. This is primarily due to (a) a significant inhomogeneity of the material properties across the component; (b) defects such as porosity and lack of fusion as well as pronounced surface roughness of the asuilt components; and (c) residual stresses, which are very often present in the as‐built parts and need to be removed by post‐fabrication treatments. Such morphological and microstructural features are very different than in conventionally manufactured parts and play a much bigger role in determining the fatigue life. The above problems require specific solutions with respect to the identification of the critical (failure) sites in AM fabricated components. Moreover, the generation of representative test specimens characterized by similar temperature cycles needs to be guaranteed if one wants to reproducibly identify the critical sites and establish fatigue assessment methods taking into account the effect of defects on crack initiation and early propagation. The latter requires fracture mechanics‐based approaches which, unlike common methodologies, cover the specific characteristics of so‐called short fatigue cracks. This paper provides a discussion of all these aspects with special focus on components manufactured by laser powder bed fusion (L‐PBF). It shows how to adapt existing solutions, identifies fields where there are still gaps, and discusses proposals for potential improvement of the damage tolerance design of L‐PBF components KW - L‐PBF KW - Fatigue KW - Fracture KW - Defects PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-525822 DO - https://doi.org/10.3390/met11050709 VL - 11 IS - 5 SP - 709 PB - MDPI CY - Basel AN - OPUS4-52582 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -