TY - CONF A1 - Blasón Gonzalez, Sergio A1 - Chaudry, M. A1 - Elorriaga, A. A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Llavori, I. A1 - Hilgenberg, Kai T1 - Design methodology of vessel produced by L PBF stainless steel using representative specimens N2 - This work presents the preliminary results of an ongoing project with a double objective: on the one hand, the characterisation of the mechanical properties against fatigue damage of an additively manufactured 316 stainless steel produced by laser powder bed-based (L-PBF) technology; on the other hand, the implementation of numerical simulation techniques able to predict the mechanical behaviour of the material in order to optimise and reduce the design costs of vessels used in the chemical sector. The current state of the work developed in this research framework allows showing the first batch of experimental results of crack propagation rate (FCGR) and high cycle fatigue (HCF) tests. The geometry of the vessels studied presents three clearly differentiated regions, either in terms of thickness (11-15 mm) or concerning the inclination of the walls to the direction of manufacturing (0º - 45º). The experimental campaign carried out so far allows identifying the differences in behaviour when comparing different extraction locations around the vessel. This is due to the variations in thermal cycles that the deposited material undergoes during the manufacturing process. Therefore, this causes variations in the microstructure which lead to changes in the response of the material. In this work, these differences are analysed qualitatively and quantitatively from the results of FCGR and HCF, thus allowing to locate the regions with the highest risk in terms of structural integrity against fatigue. This preliminary phase together with the numerical simulation of the additive manufacturing process are key to achieving a reliable description and modelling of the material. The latter will make it possible to address the priority aim of this project, involving the manufacture of independent samples whose properties are representative of the original material extracted from the reference vessels. It is, therefore, a comprehensive methodology for the design of additively manufactured components based on the localised fatigue mechanical properties of representative specimens. T2 - ECF23, European Conference on Fracture 2022 CY - Funchal, Portugal DA - 27.06.2022 KW - Additive manufacturing KW - Steel 316L KW - Fracture Mechanics PY - 2022 AN - OPUS4-55240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schönherr, J. A. A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Geilen, M. B. A1 - Klein, M. A1 - Oechsner, M. T1 - Robust determination of fatigue crack propagation thresholds from crack growth data JF - Materials N2 - The robust determination of the threshold against fatigue crack propagation DKth is of paramount importance in fracture mechanics based fatigue assessment procedures. The standards ASTM E647 and ISO 12108 introduce operational definitions of DKth based on the crack propagation rate da/dN and suggest linear fits of logarithmic DK– da/dN test data to calculate DKth. Since these fits typically suffer from a poor representation of the actual curvature of the crack propagation curve, a method for evaluating DKth using a nonlinear function is proposed. It is shown that the proposed method reduces the artificial conservativeness induced by the evaluation method as well as the susceptibility to scatter in test data and the influence of test data density. KW - Fatigue crack propagation threshold KW - ISO 12108 KW - ASTM E647 KW - Data evaluation methods KW - Experimental determination PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-552153 DO - https://doi.org/10.3390/ma15144737 SN - 1996-1944 VL - 15 IS - 14 SP - 1 EP - 21 PB - MDPI CY - Basel AN - OPUS4-55215 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Scacco, F. A1 - Zerbst, Uwe A1 - Meneghetti, G. A1 - Madia, Mauro T1 - Comparison between PSM and IBESS approaches for the fatigue life estimation of weldments JF - Welding in the World N2 - In the framework of the fatigue assessment of welded components, several methods are available in design standards such as the nominal stress, hot-spot stress, notch stress and linear elastic fracture mechanics approaches. The present paper aims at comparing two advanced local approaches for the fatigue strength assessment of different welded joints made of steel. The first one is IBESS which is based on short crack fracture mechanics. The second one is the PSM which instead involves the strain energy density approach. Both methods will be briefly presented, and the fatigue life prediction results discussed. The results obtained for the joint geometries considered in this work show advantages and drawbacks of the approaches, which are thoroughly analysed as well. KW - Fatigue KW - Welded joints KW - FAT class KW - IBESS KW - Peak stress method (PSM) KW - Finite element (FE) PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-545139 DO - https://doi.org/10.1007/s40194-022-01284-7 SP - 1 EP - 23 PB - Springer AN - OPUS4-54513 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - The effect of the environmental conditions on the threshold against fatigue crack propagation JF - Procedia Structutal Integrity N2 - The threshold against fatigue crack propagation (ΔKth) is a crucial parameter for the damage tolerance assessment of engineering components subjected to cyclic loading and it is composed by two distinct components, one intrinsic, dependent on the elastic material properties and the lattice type, and one extrinsic, related to the occurrence of crack closure effects. An important issue is that several factors can influence ΔKth and, in general, the fatigue crack propagation behavior. In this work, the influence of the experimental procedure, air humidity, stress ratio and test frequency on da/dN-ΔK data has been investigated. Results are discussed with their potential causes and consequences on the calculations of the residual lifetime. KW - Fatigue crack propagation threshold KW - Crack closure effect KW - Experimental procedure KW - Environmental conditions PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544905 DO - https://doi.org/10.1016/j.prostr.2022.03.030 VL - 38 SP - 292 EP - 299 PB - Elsevier B.V. AN - OPUS4-54490 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Werner, Tiago T1 - Estimation of the Kitagawa-Takahashi diagram by cyclic R curve analysis JF - Procedia Structural Integrity N2 - The Kitagawa-Takahashi (KT) diagram is a proven concept for describing the fatigue limit in presence of a defect or crack. It can be determined empirically with great experimental effort. It can also be estimated by means of the El Haddad relationship if the endurance limit and the long fatigue crack propagation threshold are available in reasonable accuracy. A third option is the determination using the cyclic R-curve, which describes the dependency of the fatigue crack propagation threshold on the crack growth at the short crack propagation stage. This can be experimentally determined using a closure-free initial pre-crack. It can then be applied to the determination of crack arrest for a given applied load and a given defect or crack size. Compared to the other two methods mentioned above, this option has considerable advantages: It can be applied to any component and any stress ratio. It allows the treatment of multiple cracks and provides estimations of the S-N curve in the finite life regime as well as at the endurance limit. Compared to the empirical determination of the KT diagram, the experimental effort is significantly lower and compared to the El Haddad approach it avoids problems such as the use of non-conservative long fatigue crack propagation thresholds (when the conventional load reduction method is applied to materials prone to corrosion) and the mathematical predetermination of the curve shape. The work introduces the method and provides a critical discussion as well as quantitative comparison between the different methods. T2 - FATIGUE DESIGN 2021 CY - Online meeting DA - 17.11.2021 KW - Fatigue life KW - Endurance limit KW - Kitagawa-Takahashi diagram KW - Cyclic R-curve PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544931 DO - https://doi.org/10.1016/j.prostr.2022.03.032 SN - 2452-3216 VL - 38 SP - 309 EP - 316 PB - Elsevier B.V. AN - OPUS4-54493 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Werner, Tiago A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - Comparison of the fatigue behavior of wrought and additively manufactured AISI 316L JF - Procedia Structural Integrity N2 - Additive manufacturing (AM) is becoming increasingly important in engineering applications due to the possibility of producing components with a high geometrical complexity allowing for optimized forms with respect to the in-service functionality. Despite the promising potential, AM components are still far from being used in safety-relevant applications, mainly due to a lack of understanding of the feedstock-process-properties-performance relationship. This work aims at providing a full characterization of the fatigue behavior of the additively manufactured AISI 316L austenitic stainless steel and a direct comparison with the fatigue performance of the wrought steel. To this purpose, a set of specimens has been produced by laser powder bed fusion (L-PBF) and subsequently heat treated at 900 °C for 1 hour for complete stress relief, whereas a second set of specimens has been machined out of hot-rolled plates. Low cycle fatigue (LCF) and high cycle fatigue (HCF) tests have been conducted for characterizing the fatigue behavior. The L-PBF material had a higher fatigue limit and better finite life performance compared to wrought material. Both, LCF and HCF-testing revealed an extensive cyclic softening. T2 - FATIGUE DESIGN 2021 CY - Online meeting DA - 17.11.2021 KW - Additive manufacturing KW - L-PBF KW - 316L KW - Fatigue KW - LCF KW - HCF PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-544952 DO - https://doi.org/10.1016/j.prostr.2022.03.056 SN - 2452-3216 VL - 38 SP - 554 EP - 563 PB - Elsevier B.V. AN - OPUS4-54495 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zhu, Jiangchao A1 - Schurig, M. A1 - Schlums, H. A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - Bruchmechanische Bewertung der Integrität einer Turbinenscheibe bei Überdrehzahl T2 - Bruchmechanische Werkstoff- und Bauteilbewertung: Beanspruchungsanalyse, Prüfmethoden und Anwendungen N2 - Turbinenscheiben sind thermisch und mechanisch hochbeanspruchte, sicherheitsrelevante Komponenten in Gasturbinen. Ihre Integrität wird in Bauteiltests unter Überdrehzahlbedingungen nachgewiesen. Kontext des Aufsatzes ist die Erarbeitung einer zusätzlichen Bewertungsebene auf der Grundlage von Versuchen unter monotoner Beanspruchung, die die Beanspruchung im Bauteil realistisch wiedergeben soll. Betrachtet wird ein halbelliptischer Riss, der bei der weiteren Ausbreitung als Umfangsriss wächst (rim peeling). Die Simulation dieser Stelle im Bauteil schließt die mechanische und thermische Beanspruchung sowie sie Dehnungsbehinderung ein. Letztere wird anhand zweier Parameter, der Spannungsmehrachsigkeit ℎ und des (allerdings modifizierten) Constraint-Parameters nach Newman, der die Spannungen über den plastisch verformten Bereich mittelt, bestimmt. Erwartungsgemäß zeigt sich, dass die höchste Dehnungsbehinderung weder an den Oberflächenpunkten, noch an den tiefsten Punkten, sondern an einer Stelle zwischen beiden auf der Rissfront auftritt. Als Versuchsgeometrie für die monotonen Tests soll eine Kreuzprobe mit wanddurchdringenden Rissen ausgehend von einer Innenbohrung dienen. Durch geeignete Wahl der Risstiefe sowie der in beiden Richtungen angreifenden Kräfte gelingt es, bauteiladäquate Zustände zu erzeugen. T2 - 54. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 22.02.2022 KW - Bruchmechanik KW - Struktur Integrität KW - Turbinenscheibe KW - Constraint PY - 2022 SP - 13 EP - 22 AN - OPUS4-54403 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Baer, Wolfram A1 - Breidung, Marc A1 - Kiyak, Yusuf A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Küppers, M. T1 - Aspekte der analytischen bruchmechanischen Bauteilbewertung T2 - Bruchmechanische Werkstoff- und Bauteilbewertung: Beanspruchungsanalyse, Prüfmethoden und Anwendungen N2 - Am Beispiel eines abgesetzten zylindrischen Bauteils (Achsschenkel) werden Probleme der analytischen bruchmechanischen Bauteilbewertung diskutiert. Als Basis-philosophie wird ein Fail Safe-Kriterium (kontrolliertes Versagen) angesetzt. Die Forderung ist, dass sich der Achsschenkel, bevor er bricht, in einem Ausmaß plastisch verformen kann, bei dem der Fahrer bemerkt, dass mit seinem Fahrzeug etwas nicht in Ordnung ist. Um das zu gewährleisten, muss der Werkstoff einen bestimmten Riss-widerstand aufweisen. Dazu werden im hier vorgestellten ersten Teil des Projektes mittels FEM Rissspitzenbeanspruchungen in Abhängigkeit von der Auslenkung des Zylinders und angenommener Rissgrößen ermittelt. Diese finden als Zielgrößen in der weiteren Analyse Anwendung. Da eine einfach umzusetzende Lösung angestrebt wird, werden zusätzlich analytische Rechnungen an Ersatzgeometrien (halbunendliche Platte und Vollzylinder), aber mit den realen Spannungen am Bauteil durchgeführt. Es zeigt sich, dass die Ergebnisse wegen des Steifigkeitsunterschieds zwischen Bauteil und Ersatzgeometrie unvertretbar konservativ sind. Alternativ wird ein hybrides Konzept vorgestellt, für das die Modellparameter mittels FEM bestimmt werden. Es liefert sehr genaue Ergebnisse. Im Rahmen der analytischen Rechenvorschrift können die Lösungen auf andere Werkstoffe übertragen werden, ohne dass zusätzliche FEM-Analysen notwendig sind. T2 - 54. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 22.02.2022 KW - FEM KW - Bauteilbewertung KW - Fail-safe KW - Analytisches Modell PY - 2022 DO - https://doi.org/10.48447/Br-2022-BB VL - 254 SP - 1 EP - 11 PB - DVM CY - Berlin AN - OPUS4-54406 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schork, B. A1 - Zerbst, Uwe A1 - Kiyak, Yusuf A1 - Kaffenberger, M. A1 - Madia, Mauro A1 - Oechsner, M. T1 - Effect of the parameters of weld toe geometry on the FAT class as obtained by means of fracture mechanics-based simulations JF - Welding in the World N2 - The fracture mechanics-based IBESS approach is applied to the determination of FAT classes of butt welds with crack Initiation along the weld toe. The aim is an investigation of the effect of the geometrical parameters toe radius, flank angle, reinforcement and secondary notches such as roughness or undercuts. The influence of these parameters is discussed both individually and in combination; however, excluding statistical distributions of them and the material data. The results, when compared with conventional FAT classes for butt welds, are encouraging with respect to a potential contribution of IBESS to the discussion of more advanced quality criteria for welds. To that purpose, demands for further research are proposed. KW - Fracture mechanics KW - Weld toe geometry KW - Fatigue crack initiation KW - FAT class approach PY - 2020 DO - https://doi.org/10.1007/s40194-020-00874-7 IS - 64 SP - 925 EP - 936 PB - Springer AN - OPUS4-53079 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bergant, M. A1 - Werner, Tiago A1 - Madia, Mauro A1 - Yawny, A. A1 - Zerbst, Uwe T1 - Short crack propagation analysis and fatigue strength assessment of additively manufactured materials: An application to AISI 316L JF - International Journal of Fatigue N2 - This paper presents the application of short crack propagation models based on the cyclic R-curve for assessing the fatigue strength of additively manufactured (AM) materials containing fabrication defects. Chapetti’s and IBESS models were implemented in combination with Murakami’s √area parameter, considering recently published data on laser powder bed fusion processed AISI 316L stainless steels. Estimated S-N curves and Kitagawa-Takahashi diagrams predict fairly well the experimental data, especially the origin of the failure from internal or surface defects. These results provide an indication that the methods based on the cyclic R-curve constitute suitable tools for fatigue behavior assessment of AM materials. KW - AM 316L stainless steel KW - Cyclic R-curve KW - Chapetti’s and IBESS model KW - S-N curve KW - Kitagawa-Takahashi diagram PY - 2021 DO - https://doi.org/10.1016/j.ijfatigue.2021.106396 VL - 151 PB - Elsevier Ltd. AN - OPUS4-53082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Vojtek, T. A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Pokorný, P. A1 - Jambor, M. A1 - Hutař, P. T1 - Determination of fatigue crack propagation thresholds for steel in presence of environmental effects JF - International Journal of Fatigue N2 - The experimental determination of the resistance to fatigue crack propagation in steel, particularly in the socalled near-threshold regime, is a crucial issue for safety-relevant components which are designed to operate for a large number of loading cycles before undergoing periodic inspections. This work summarizes the most relevant results of extensive experimental campaigns conducted at BAM and IPM over the last years, which have been devoted to the determination of fatigue crack propagation characteristics on medium and high strength steels. The influence of environment, oxide-induced crack closure and test methodologies in the near-threshold regime are discussed. KW - Steel KW - Fatigue crack propagation threshold KW - Oxide-induced crack closure KW - Environmental effect PY - 2021 DO - https://doi.org/10.1016/j.ijfatigue.2021.106449 SN - 0142-1123 VL - 153 SP - 1 PB - Elsevier Ltd. AN - OPUS4-53525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Vergleichende Untersuchungen zum intrinsischen Schwellenwert der da/dN-ΔK-Kurve T2 - Bruchmechanische Werkstoff- und Bauteilbewertung: Beanspruchungsanalyse, Prüfmethoden und Anwendungen N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung, Δ𝐾𝑡ℎ, und dem sich anschließenden Schwellenwertbereich der 𝑑𝑎𝑑𝑁⁄−Δ𝐾-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - 53. Tagung des DVM-Arbeitskreises Bruchmechanik und Bauteilsicherheit CY - Online meeting DA - 18.02.2021 KW - Schadenstolerante Bauteilauslegung, Restlebensdauer, intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung PY - 2021 SN - 2366-4797 SP - 211 EP - 220 PB - Deutscher Verband für Materialforschung und -prüfung e.V. (DVM) CY - Berlin AN - OPUS4-52704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Der Schwellenwert der da/dN-∆K-Kurve als Auslegungskriterium für die Bauteilbewertung T2 - Werkstoffe und Bauteile auf dem Prüfstand. Prüftechnik - Kennwertermittlung - Schadensvermeidung N2 - Für die Bestimmung der Restlebensdauer zyklisch beanspruchter Bauteile kommt dem Schwellenwert für Ermüdungsrissausbreitung ∆Kth und dem sich anschließenden Schwellenwertbereich der da/dN-∆K-Kurve große Bedeutung zu. Dem stehen Unsicherheiten bei der Bestimmung und Analyse gegenüber. Der Aufsatz befasst sich mit der Ermittlung des sogenannten intrinsischen Schwellenwerts, der als robuster Eingangsparameter für eine „rissschließfreie“ Analyse der Restlebensdauer von entscheidender Bedeutung ist. T2 - Tagung Werkstoffprüfung 2020 CY - Online meeting DA - 03.12.2020 KW - Schadenstolerante Bauteilauslegung, KW - Intrinsischer Schwellenwert gegen Ermüdungsrissausbreitung KW - Restlebensdauer PY - 2020 DO - https://doi.org/10.48447/WP-2020-025 SP - 1 EP - 8 AN - OPUS4-52788 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Zerbst, Uwe A1 - Madia, Mauro ED - Yadroitsev, I. ED - Yadroitsava, I. ED - Du Plessies, A. ED - McDonald, E. T1 - Structural integrity II: fatigue properties T2 - Fundamentals of laser powder bed fusion of metals N2 - If a component is cyclically loaded, its load carrying capacity is considerably lower than in the monotonic loading case. This general observation applies in particular to L-PBF parts. The causes of this are mainly material defects such as pores and unwelded regions (Chapter 8) and a pronounced surface roughness in the as-built condition (Chapter 9). In addition, effects due to the anisotropy of the microstructure (Chapter 6) and a complex residual stress pattern (Chapter 7) play an important role. A consequence is that common strategies of fatigue assessment cannot be transferred to L-PBF applications without modifications. Due to the inhomogeneity of the material, the determination of representative material properties and the transfer to the component is a problem, and this is also the case with regard to the consideration of defects, surface roughness and residual stresses. The chapter gives a brief introduction to these problem areas. KW - Fatigue crack propagation stagesdefects KW - Fatigue strength KW - Fatigue life KW - Fracture mechanics PY - 2021 SN - 978-0-12-824090-8 DO - https://doi.org/10.1016/B978-0-12-824090-8.00015-9 SP - 377 EP - 394 PB - Elsevier Inc. CY - Amsterdam ET - 1 AN - OPUS4-52854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Bruno, Giovanni A1 - Hilgenberg, Kai T1 - Towards a Methodology for Component Design of Metallic AM Parts Subjected to Cyclic Loading JF - Metals N2 - The safe fatigue design of metallic components fabricated by additive manufacturing (AM) is still a largely unsolved problem. This is primarily due to (a) a significant inhomogeneity of the material properties across the component; (b) defects such as porosity and lack of fusion as well as pronounced surface roughness of the asuilt components; and (c) residual stresses, which are very often present in the as‐built parts and need to be removed by post‐fabrication treatments. Such morphological and microstructural features are very different than in conventionally manufactured parts and play a much bigger role in determining the fatigue life. The above problems require specific solutions with respect to the identification of the critical (failure) sites in AM fabricated components. Moreover, the generation of representative test specimens characterized by similar temperature cycles needs to be guaranteed if one wants to reproducibly identify the critical sites and establish fatigue assessment methods taking into account the effect of defects on crack initiation and early propagation. The latter requires fracture mechanics‐based approaches which, unlike common methodologies, cover the specific characteristics of so‐called short fatigue cracks. This paper provides a discussion of all these aspects with special focus on components manufactured by laser powder bed fusion (L‐PBF). It shows how to adapt existing solutions, identifies fields where there are still gaps, and discusses proposals for potential improvement of the damage tolerance design of L‐PBF components KW - L‐PBF KW - Fatigue KW - Fracture KW - Defects PY - 2021 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-525822 DO - https://doi.org/10.3390/met11050709 VL - 11 IS - 5 SP - 709 PB - MDPI CY - Basel AN - OPUS4-52582 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zhu, Jiangchao A1 - Madia, Mauro A1 - Schurig, M. A1 - Schlums, H. A1 - Zerbst, Uwe T1 - Fracture mechanics-based structural integrity assessment of aeroengine turbine disks under overspeed conditions T2 - Proceedings of ASME Turbo Expo 2022 N2 - Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on productionsimilar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present part of a fracture mechanics-based procedure under development which aims at replacing the tests on production-similar disks with lab tests on fracture mechanics specimens. In particular, the rimpeeling failure mode is considered as case study. A semi-circular surface crack is modelled at the most stressed region at the diaphragm of a turbine disk, with the crack plane perpendicular to the radial direction. The crack is therefore subjected to a biaxial stress state and grows under increasing rotational speed until it triggers the rim-peeling failure. The finite element simulation of the cracked disk considers the real thermal and mechanical loading conditions. In order to design a lab representative specimen, beside the crack driving force, expressed in terms of � -integral, also the constraint to plastic deformation e.g., stress triaxiality, at the crack-tip must be similar for the same crack in the specimen and in the disk. This has been achieved and as expected, both the highest � -integral and constraint factor are calculated at the same location along the crack front for both disk and specimen. The results of the structural integrity assessment in the form of a Failure Assessment Diagram (FAD) show good agreement between designed specimen and disk both in terms of expected failure mode and value of the critical speed. Probabilistic aspects are also considered in the calculations. T2 - ASME Turbo Expo 2022: Turbomachinery Technical Conference and Exposition (GT2022) CY - Rotterdam, The Netherlands DA - 13.06.2022 KW - Fracture mechanics KW - Burst KW - Turbine disk PY - 2022 SP - 1 EP - 7 PB - ASME AN - OPUS4-55903 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Kiyak, Yusuf A1 - Breidung, Marc A1 - Baer, Wolfram A1 - Küppers, M. ED - Madia, Mauro T1 - Stiffness/constraint effects in analytical flaw assessment - A technical note JF - Engineering Fracture Mechanics N2 - Using the case study of a fail-safe design criterion for a steering knuckle of a commercial vehicle, the effect of stiffness/constraint on the crack driving force in the component is discussed. The problem arises when assessment procedures such as R6, BS 7910 or SINTAP/FITNET are applied in conjunction with substitute geometries for determining the model parameters K-factor and limit load (or a substitute for the latter), as it is common practice. In the example, the conservatism was so pronounced that this procedure was in fact unusable. A way out could be the finite element-based determination of the model parameters and their use in the analytical framework. This procedure is useful and effective if the finite element-based calculations are used in parameter sensitivity analyses. KW - Fail-safe design KW - Fracture resistance KW - Fracture assessment KW - Stiffness KW - Constraint PY - 2022 DO - https://doi.org/10.1016/j.engfracmech.2022.108728 SN - 0013-7944 IS - 273 SP - 1 EP - 15 PB - Elsevier Science CY - Kidlington AN - OPUS4-55544 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - BOOK A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Bruchmechanische Bauteilbewertung N2 - Die sichere Auslegung von Bauteilen kommt an der Anwendung bruchmechanischer Methoden heute nicht mehr vorbei. Das vorliegende Buch bietet eine Einführung in diese Methoden mit besonderen Schwerpunkten auf dem aktuellen Stand der bruchmechanischen Kennwertermittlung und den Methoden der analytischen bruchmechanischen Bauteilbewertung. Es beschreibt die Mechanismen von Risswachstum und Bruch, die grundlegenden Konzepte der Bruchmechanik, die analytische Ermittlung der Rissspitzenbelastung in Bauteilen sowie die Anwendung der Bruchmechanik in unterschiedlichen Kontexten. Der Schwerpunkt liegt dabei auf der praktischen Anwendung u. a. anhand von Demonstrationsbeispielen, die im Detail nachvollzogen werden können. KW - Rissausbreitung KW - Bruch KW - Bruchmechanische Konzepte KW - Bruchmechanische Kennwerte KW - Rissspitzenbelastung KW - Failure Assessment Diagram KW - Rissschließfunktion KW - Kritische Last KW - J-Integral KW - Risswiderstand KW - Stretch-Zone KW - IBESS-Prozedur KW - Constraint faktor KW - Mismatch KW - Ligamentplastifizierung KW - Crack Tip Opening Displacement (CTOD) PY - 2022 SN - 978-3-658-36150-1 SN - 978-3-658-36151-8 DO - https://doi.org/10.1007/978-3-658-36151-8 SP - C1 EP - 372 PB - Springer CY - Heidelberg AN - OPUS4-56004 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Duarte, Larissa A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Schönherr, J. A. A1 - Geilen, M. B. A1 - Klein, M. A1 - Oechsner, M. T1 - Recent developments in the determination of fatigue crack propagation thresholds JF - International Journal of Fatigue N2 - The impact of crack closure and environmental effects on the experimental determination of the fatigue crack propagation threshold is a major problem for the assessment of cyclically loaded components, especially at low stress ratios 𝑅. In this work, the influence of the experimental procedure and air humidity on d𝑎∕d𝑁 − 𝛥𝐾 data at different 𝑅 is discussed. Unlike the results at 𝑅 = −1, the threshold values obtained at 𝑅 ≈ 0.8, i.e. under negligible crack closure levels, show a very small scatter band regardless of the variation of the test parameters and environmental conditions. KW - Fatigue crack propagation threshold KW - Component assessment KW - Crack closure KW - Environmental effects KW - Testing parameters PY - 2022 DO - https://doi.org/10.1016/j.ijfatigue.2022.107131 SN - 0142-1123 VL - 164 SP - 1 EP - 15 PB - Elsevier Ltd. AN - OPUS4-55403 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Analytical flaw assessment JF - Engineering Fracture Mechanics N2 - The paper provides a review on analytical flaw assessment methods with the focus on fracture under monotonic loading and fatigue crack propagation. The first topic comprises linear elastic as well as elastic-plastic fracture mechanics approaches. It essentially follows their historical development. Topics which are separately discussed are reference/Limit loads, the treatment of secondary stresses, strength mismatch, constraint, unstable crack propagation (monotonic R-curve analyses) and statistical aspects. With respect to fatigue crack propagation the analytical treatment of crack closure and constraint and the Determination of the cyclic elastic-plastic crack driving force is discussed. Finally, cyclic Rcurve analyses are briefly addressed. KW - Monotonic and cyclic crack driving force KW - Secondary stresses KW - Strength mismatch KW - Constraint KW - Crack closure KW - R-curve analysis PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.12.002 SN - 0013-7944 SN - 1873-7315 VL - 187 SP - 316 EP - 367 PB - Elsevier AN - OPUS4-44234 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -