TY - JOUR A1 - Zerbst, Uwe A1 - Beretta, S. A1 - Köhler, G. A1 - Lawton, A. A1 - Vormwald, M. A1 - Beier, H.T. A1 - Klinger, Christian A1 - Cerný, I. A1 - Rudlin, J. A1 - Heckel, Thomas A1 - Klingbeil, Dietmar T1 - Safe life and damage tolerance aspects of railway axles - A review N2 - The paper gives an overview on safe life and damage tolerance methods applied to railway axles. It describes failure scenarios due to fatigue crack initiation and propagation. Besides common aspects of design, specific features such as corrosion and impact damage from flying ballast are discussed which may reduce the fatigue strength of axles during service. Potential effects of non-metallic inclusions from the steel manufacturing process are addressed in the context of the very high number of loading cycles railway axles are designed for. With respect to damage tolerance general lines of fracture mechanics residual lifetime analyses are introduced. More specific discussion is provided on aspects such as the threshold value of fatigue crack propagation and reliability aspects of non-destructive inspection. KW - Railway axle KW - Safe life design KW - Damage tolerance KW - Fatigue strength KW - Fatigue crack propagation KW - Inspection intervals PY - 2013 DO - https://doi.org/10.1016/j.engfracmech.2012.09.029 SN - 0013-7944 SN - 1873-7315 VL - 98 SP - 214 EP - 271 PB - Elsevier Science CY - Kidlington AN - OPUS4-27779 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro ED - Yu, S. ED - Feng, X.-Q. T1 - Fracture mechanics model for predicting fracture strength of metallic alloys containing large second phase particles N2 - An analytical fracture mechanics model for predicting the finite life fatigue strength of components is presented which Combines a number of well established and newly developed approaches such as Murakami’s and McEvily's approach for describing the transient behaviour of crack closure of short cracks, the analytical (long) crack closure function of Newman, the R6 procedure modified by a method for improving the ligament yielding correction proposed by the authors and other elements. Basic assumption is the preexistence of initial flaws such that the crack initiation or nucleation stage is small and can be neglected. The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with artificial initial defects generated by FIB technology, the size of which was fixed on the basis of fractographic investigations on broken, smooth specimens. T2 - ICF13 - 13th International conference on fracture CY - Beijing, China DA - 16.06.2013 KW - Fatigue strength KW - S-N curve KW - Fracture mechanics KW - Crack propagation KW - Short cracks PY - 2013 SN - 978-988-12265-2-5 SP - 1 EP - 12 AN - OPUS4-29537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Hübner, P. T1 - Bruchmechanik an Schweißverbindungen T2 - Gemeinschaftssitzung DVS-AGQ12, DVM AG Bruchmechanik an Schweißverbindungen und IBESS, BAM CY - Berlin, Germany DA - 2013-11-26 PY - 2013 AN - OPUS4-29501 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Klingbeil, Dietmar A1 - Zerbst, Uwe A1 - Klinger, Christian ED - Yu, S. ED - Feng, X.-Q. T1 - Safe life and damage tolerance concepts of railway axles N2 - On July 9, 2008 a high speed train derailed in Cologne main Station, Germany at a low speed because an axle was broken. Fortunately, the derailment happened at a low speed so that nobody was injured. The reason for the broken axle was investigated and it turned out that most likely large inclusions located shortly undemeath the surface in a T-transition were the origin of the final crack. Basing on that result, a systematic investigation on existing safety assessments of railway axles was performed. This results in an analysis of the production process of axles and in a critical review of existing of existing assessments. Improvements and future developments are outlined. T2 - ICF13 - 13th International conference on fracture CY - Beijing, China DA - 16.06.2013 KW - Railway axles KW - Derailment KW - Service loading fatigue KW - Inclusions KW - Safety assessment PY - 2013 SN - 978-988-12265-2-5 SP - 1 EP - 10 AN - OPUS4-29651 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Zerbst, Uwe A1 - Ainsworth, R. A. A1 - Madia, Mauro ED - Klingbeil, D. ED - Vormwald, M. ED - Eulitz, K.-G. T1 - Reference load versus limit load in engineering flaw assessment: A proposal for a hybrid analysis option N2 - The net section limit load FY is a key input parameter for the accuracy of any elastic-plastic flaw assessment procedure of the R6 type. Unfortunately available limit load solutions are of variable quality since they have been obtained over decades by different methods. As a consequence the results of the fracture analyses such as the critical load or crack size are limited in their accuracy and are often significantly conservative. A further problem is that common limit load solutions based on ligament yielding are inadequate in a number of cases even for through crack configurations and should be replaced by some kind of local yielding solutions. In the present paper a simple and straightforward reference load definition is proposed instead of the limit load which strictly corresponds to a ligament yielding parameter Lr = 1 in the R6 Routine and similar approaches such as SINTAP and FITNET. This can be determined by finite element simulation for any geometry. In addition to a previous study on thin wall notched plates the method is applied to plates containing shallow semi-elliptical surface cracks. The results demonstrate that the approach provides a suitable extension and improvement of the existing methods. T2 - 18th European conference on fracture (ECF 18) - Fracture of materials and structures from micro to macro scale CY - Dresden, Germany DA - 2010-08-30 KW - Flaw assessment KW - Reference stress method KW - R6 procedure KW - EPRI method KW - SINTAP KW - FITNET KW - Limit load KW - Reference load PY - 2010 SN - 978-3-00-031802-3 IS - Paper 81 SP - 1 EP - 11 AN - OPUS4-22329 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Ainsworth, R. A. A1 - Madia, Mauro T1 - Reference load versus limit load in engineering flaw assessment. A proposal for a hybride analysis option T2 - 18th European Conference on Fracture CY - Dresden, Germany DA - 2010-08-30 PY - 2010 AN - OPUS4-22287 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro A1 - Riesch-Oppermann, H. A1 - Zerbst, Uwe A1 - Beretta, S. T1 - Ein Konzept für die probabilistische bruchmechanische Bauteilbewertung T2 - 42. Tagung des DVM-Arbeitskreises Bruchvorgänge - Bruchmechanische Werkstoff- und Bauteilbewertung: Beanspruchungsanalyse, Prüfmethoden und Anwendungen CY - Paderborn, Deutschland DA - 2010-02-23 KW - Bruchmechanische Bauteilbewertung KW - SINTAP KW - FITNET KW - Zuverlässigkeit KW - FORM/SORM PY - 2010 SP - 51 EP - 60 AN - OPUS4-22837 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Madia, Mauro A1 - Riesch-Oppermann, H. A1 - Zerbst, Uwe A1 - Beretta, S. ED - Klingbeil, D. ED - Vormwald, M. ED - Eulitz, K.-G. T1 - A new full-probabilistic framework for the structural integrity assessment of structures containing cracks T2 - 18th European conference on fracture (ECF 18) - Fracture of materials and structures from micro to macro scale CY - Dresden, Germany DA - 2010-08-30 KW - Structural integrity KW - SINTAP KW - FITNET KW - Reliability KW - FORM PY - 2010 SN - 978-3-00-031802-3 IS - C.02.1-3 / #306 SP - 1 EP - 10 AN - OPUS4-22843 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Hellmann, D. T1 - Fracture mechanics model for predicting fatigue strength of metallic alloys containing large second phase particles T2 - ECF 19 - 19th European conference on fracture - Fracture mechanics for durability, reliability and safety CY - Kazan, Russia DA - 2012-08-26 KW - Fatigue strength KW - S-N curve KW - Fracture mechanics KW - Crack propagation KW - Short cracks KW - Bruchmechanik KW - Schwingfestigkeit KW - Bauteilbewertung PY - 2012 SN - 978-5-905576-18-8 IS - Proceeding-ID 116 SP - 1 EP - 14 AN - OPUS4-27278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Ainsworth, R. A. A1 - Madia, Mauro T1 - Reference load versus limit load in engineering flaw assessment: A proposal for a hybrid analysis option N2 - The net section limit load FY necessary for assessment at static loading is a key input for the accuracy of any elastic–plastic flaw assessment procedure of the R6 type. Unfortunately available limit load solutions are of variable quality since they have been obtained over decades by different methods. As a consequence the results of the fracture analyses such as the critical load or crack size are limited in their accuracy and are often significantly conservative. Further, common limit load solutions based on ligament yielding are inadequate in a number of cases even for through crack configurations and should be replaced by some kind of local yielding solutions. In the present paper a simple and straightforward reference load definition is proposed instead of the limit load which strictly corresponds to a ligament yielding parameter Lr = 1 in the R6 Routine and similar approaches such as the European SINTAP and FITNET methods. This can be determined by finite element simulation for any geometry. In addition to a previous study on thin wall notched plates the method is applied to plates containing shallow semi-elliptical surface cracks. The results demonstrate that the approach provides a suitable extension and improvement of the existing methods. KW - Flaw assessment KW - Reference stress method KW - R6 procedure KW - SINTAP KW - FITNET KW - Limit load KW - Reference load PY - 2012 DO - https://doi.org/10.1016/j.engfracmech.2011.10.018 SN - 0013-7944 SN - 1873-7315 VL - 91 SP - 62 EP - 72 PB - Elsevier Science CY - Kidlington AN - OPUS4-27279 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Klinger, Christian A1 - Klingbeil, Dietmar T1 - Structural assessment of railway axles - A critical review N2 - The safety assessment of railway axles is based on a two-stage approach: fatigue strength design and regular inspections which, in terms of a general safety philosophy refer to safe-life and damage tolerance concepts. Starting with a recent failure case, a broken axle of a German high speed train, a discussion is presented on issues of both safety levels. These include ideas for finite life design, the treatment of in-service effects on the fatigue strength due to flying ballast damage and corrosion pits, the effect of corrosion on fatigue crack initiation and propagation, potential effects of non-metallic inclusions in steels, the way to detect them by quality control measures and reliability aspects of non-destructive testing with respect to the detection of fatigue cracks. Proposals are made how the safety level could be further improved. KW - Railway axles KW - Safe life design KW - Damage tolerance design KW - Non-destructive testing KW - Flying ballast impact KW - Corrosion KW - Non-metallic inclusions PY - 2013 UR - http://www.sciencedirect.com/science/article/pii/S1350630712002531 SN - 1350-6307 SN - 1873-1961 VL - 35 IS - Special issue on ICEFA V- Part 1 SP - 54 EP - 65 PB - Elsevier Science Publ. CY - Oxford AN - OPUS4-29715 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Arafah, D. T1 - Referenzlastlösungen für die Ermittlung der elastisch-plastischen Rissspritzenbeanspruchung in Platten-Strukturen unter Zug-, Biege-, kombinierter Zug-Biege- und zweiaxialer Zugbelastung T2 - 46. Tagung des DVM-Arbeitskreises Bruchvorgänge CY - Kassel, Germany DA - 2014-02-11 PY - 2014 AN - OPUS4-29738 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Komann, Steffen A1 - Kiyak, Yusuf A1 - Wille, Frank A1 - Zerbst, Uwe A1 - Weber, Mike A1 - Klingbeil, Dietmar T1 - Assessment of ductile cast iron fracture mechanics analysis within licensing of German transport packages N2 - In the design approval of transport packages for radioactive materials, the mechanical and thermal safety assessment is carried out in Germany by competent authority BAM. In recent years BAM was involved in several licensing procedures of new spent fuel and HLW package designs, where the cask body is of Ductile Cast Iron (DCI). According to IAEA regulations package designs have to fulfill requirements for specific conditions of transport. Type B(U) packages must withstand the defined accident conditions of transport. The temperature range from -40°C up to the operational temperature has to be considered. For the cask material DCI, it is necessary to determine safety against brittle fracture. The German guideline BAM-GGR 007 defines requirements for fracture mechanics of packagings made of DCI. Due to complex cask body structure and the dynamic loading a fracture mechanical assessment by analytical approaches is not always possible. Experience of recent design approval procedures show that the application of numerical calculations are applicable to determine the stresses and stress intensity factors in the cask body. At the first step a numerical analysis has to be done to identify the loading state at the whole cask body. Secondly an analysis of a detail of the cask body is made considering the displacement boundary conditions of the global model. An artificial flaw is considered in this detailed model to calculate the fracture mechanical loading state. The finite element mesh was strongly refined in the area of the flaw. The size of the artificial flaw is based on the ultrasonic inspection acceptance criteria applied for cask body manufacture. The applicant (GNS) developed additional analysis tools for calculation of stress intensity factor and/or J-Integral. The assessment approach by BAM led to the decision to develop own tools to the possibility for independent proof of the results. The paper describes the authority assessment approach for DCI fracture mechanics analysis. The validation procedure incl. the development of own tools is explained. BAM developed a postprocessor to determine the fracture mechanical loads. A horizontal 1 m puncture bar drop test is used to give a detailed description of the assessment procedure. T2 - PATRAM 2013 - 17th International symposium on the packaging and transportation of radioactive materials CY - San Francisco, CA, USA DA - 18.08.2013 PY - 2013 SP - 1 EP - 10 PB - Omnipress AN - OPUS4-30175 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Klinger, Christian T1 - Anmerkungen zur Auslegung und zum sicheren Betrieb von Radsatzwellen aus der Sicht von Betriebsfestigkeit und Bruchmechanik N2 - Die Sicherheit von Radsatzwellen beruht gegenwärtig auf zwei Säulen: der Schwingfestigkeitsauslegung und periodischen Inspektionen. Ausgehend von einem Schadensfall, der gebrochenen ICE 3-Welle von Köln, 2008, sollen ausgewählte Aspekte beider Säulen diskutiert und Vorschläge zur weiteren Verbesserung gemacht werden. Diese betreffen u.a. Fragen einer Betriebszeitbegrenzung, Veränderungen der Schwingfestigkeit während des Betriebs infolge von Korrosion und Steinschlag, den Einfluss von Korrosion auf Schwingrissinitiierung und -fortschritt, den potentiellen Einfluss nichtmetallischer Einschlüsse auf die Schwingfestigkeit, die Möglichkeiten sie im Rahmen der Qualitätssicherung zu detektieren sowie Fragen der Bruchmechanik und der Zuverlässigkeit zerstörungsfreier Schwingriss-Prüfverfahren im Rahmen eines Konzepts regelmäßiger Inspektionen. T2 - 40. Tagung des DVM-Arbeitskreises Betriebsfestigkeit CY - Herzogenaurach, Germany DA - 09.10.2013 KW - Radsatzwellen KW - Schwingfestigkeit KW - Sichere Lebensdauer KW - Schadenstoleranz KW - Zerstörungsfreie Inspektion KW - Korrosion KW - Steinschlag KW - Nichtmetallische Einschlüsse KW - Railway axles KW - Fatigue strength KW - Safe life design KW - Damage tolerance design KW - Non-destructive inspection KW - Corrosion KW - Flying ballast impact KW - Non-metallic inclusions PY - 2013 N1 - Serientitel: DVM-Bericht – Series title: DVM-Bericht VL - 140 SP - 69 EP - 80 AN - OPUS4-29458 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schork, B. A1 - Zerbst, Uwe A1 - Kiyak, Yusuf A1 - Kaffenberger, M. A1 - Madia, Mauro A1 - Oechsner, M. T1 - Effect of the parameters of weld toe geometry on the FAT class as obtained by means of fracture mechanics-based simulations N2 - The fracture mechanics-based IBESS approach is applied to the determination of FAT classes of butt welds with crack Initiation along the weld toe. The aim is an investigation of the effect of the geometrical parameters toe radius, flank angle, reinforcement and secondary notches such as roughness or undercuts. The influence of these parameters is discussed both individually and in combination; however, excluding statistical distributions of them and the material data. The results, when compared with conventional FAT classes for butt welds, are encouraging with respect to a potential contribution of IBESS to the discussion of more advanced quality criteria for welds. To that purpose, demands for further research are proposed. KW - Fracture mechanics KW - Weld toe geometry KW - Fatigue crack initiation KW - FAT class approach PY - 2020 DO - https://doi.org/10.1007/s40194-020-00874-7 IS - 64 SP - 925 EP - 936 PB - Springer AN - OPUS4-53079 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bergant, M. A1 - Werner, Tiago A1 - Madia, Mauro A1 - Yawny, A. A1 - Zerbst, Uwe T1 - Short crack propagation analysis and fatigue strength assessment of additively manufactured materials: An application to AISI 316L N2 - This paper presents the application of short crack propagation models based on the cyclic R-curve for assessing the fatigue strength of additively manufactured (AM) materials containing fabrication defects. Chapetti’s and IBESS models were implemented in combination with Murakami’s √area parameter, considering recently published data on laser powder bed fusion processed AISI 316L stainless steels. Estimated S-N curves and Kitagawa-Takahashi diagrams predict fairly well the experimental data, especially the origin of the failure from internal or surface defects. These results provide an indication that the methods based on the cyclic R-curve constitute suitable tools for fatigue behavior assessment of AM materials. KW - AM 316L stainless steel KW - Cyclic R-curve KW - Chapetti’s and IBESS model KW - S-N curve KW - Kitagawa-Takahashi diagram PY - 2021 DO - https://doi.org/10.1016/j.ijfatigue.2021.106396 VL - 151 PB - Elsevier Ltd. AN - OPUS4-53082 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Vojtek, T. A1 - Duarte, Larissa A1 - Zerbst, Uwe A1 - Pokorný, P. A1 - Jambor, M. A1 - Hutař, P. T1 - Determination of fatigue crack propagation thresholds for steel in presence of environmental effects N2 - The experimental determination of the resistance to fatigue crack propagation in steel, particularly in the socalled near-threshold regime, is a crucial issue for safety-relevant components which are designed to operate for a large number of loading cycles before undergoing periodic inspections. This work summarizes the most relevant results of extensive experimental campaigns conducted at BAM and IPM over the last years, which have been devoted to the determination of fatigue crack propagation characteristics on medium and high strength steels. The influence of environment, oxide-induced crack closure and test methodologies in the near-threshold regime are discussed. KW - Steel KW - Fatigue crack propagation threshold KW - Oxide-induced crack closure KW - Environmental effect PY - 2021 DO - https://doi.org/10.1016/j.ijfatigue.2021.106449 SN - 0142-1123 VL - 153 SP - 1 PB - Elsevier Ltd. AN - OPUS4-53525 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Analytical flaw assessment N2 - The paper provides a review on analytical flaw assessment methods with the focus on fracture under monotonic loading and fatigue crack propagation. The first topic comprises linear elastic as well as elastic-plastic fracture mechanics approaches. It essentially follows their historical development. Topics which are separately discussed are reference/Limit loads, the treatment of secondary stresses, strength mismatch, constraint, unstable crack propagation (monotonic R-curve analyses) and statistical aspects. With respect to fatigue crack propagation the analytical treatment of crack closure and constraint and the Determination of the cyclic elastic-plastic crack driving force is discussed. Finally, cyclic Rcurve analyses are briefly addressed. KW - Monotonic and cyclic crack driving force KW - Secondary stresses KW - Strength mismatch KW - Constraint KW - Crack closure KW - R-curve analysis PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.12.002 SN - 0013-7944 SN - 1873-7315 VL - 187 SP - 316 EP - 367 PB - Elsevier AN - OPUS4-44234 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Beier, H. Th. T1 - Fatigue strength and life determination of weldments based on fracture mechanics N2 - The paper provides an overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common ΔK concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit and the finite life branch of the S-N curve are determined. Besides a brief introduction into the approach, validation examples are presented. These comprise different weldment types (butt welds, cross joints and longitudinal stiffened plates), two steels (S355NL and S960QL) of quite different strengths, different weld geometries due to different welding techniques (WIG, MAG), as-welded and stress relieved welds and different stress ratios varying from R = -1 to R = 0.5. T2 - FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Weldments KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-438500 DO - https://doi.org/10.1016/j.prostr.2017.11.106 SN - 2452-3216 VL - 7 SP - 407 EP - 414 PB - ScienceDirect CY - Lecco, Italy AN - OPUS4-43850 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Hensel, Jonas T1 - Application of fracture mechanics to weld fatigue N2 - The application of fracture mechanics to the determination of the fatigue behavior of weldments is discussed with the focus on classic fatigue, i.e., the overall fatigue life and the fatigue strength in terms of an S-N curve and the endurance limit. The following issues are addressed: specific features of short fatigue crack propagation, an adequate initial crack size, multiple crack propagation and its statistical treatment as well as welding residual stresses. As an example, an approach of the authors is applied to the determination of FAT classes for a butt weld with varying weld toe geometry. KW - Weld fatigue KW - Weld toe geometry KW - Short crack propagation KW - FAT class concept PY - 2020 DO - https://doi.org/10.1016/j.ijfatigue.2020.105801 SN - 0142-1123 VL - 139 SP - 105801 PB - Elsevier Ltd. AN - OPUS4-50991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Vormwald, M. A1 - Pippan, R. A1 - Gänser, H.-P. A1 - Sarrazin-Baudoux, C. A1 - Madia, Mauro T1 - About the fatigue crack propagation threshold of metals as a design criterion - A review N2 - The fatigue crack propagation threshold ΔKth is of paramount importance for any kind of damage tolerant design, but in contrast to this importance, the determination and application of the parameter is not on the firm ground as previously assumed. The paper discusses questions of its experimental determination as well as of its application to components. In both fields, new questions have been raised with the potential to challenge or modify long-standing knowledge. Against this background, the paper is an attempt to systematize the established knowledge as well as questions and open issues. KW - Fatigue crack propagation threshold KW - Experimental determination KW - Influencing factors KW - Transferability to components PY - 2016 DO - https://doi.org/10.1016/j.engfracmech.2015.12.002 SN - 0013-7944 SN - 1873-7315 VL - 153 SP - 190 EP - 243 PB - Elsevier Science CY - Kidlington AN - OPUS4-35264 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Beier, T. T1 - IBESS: Integrale Bruchmechanische Ermittlung der Schwingfestigkeit von Schweißverbindungen - eine Einführung T2 - DVS-Congress 2015 CY - Nürnberg DA - 2015-09-14 PY - 2015 AN - OPUS4-33500 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - Application of the cyclic R-curve method in notch fatigue analysis N2 - The paper deals with the prediction of the fatigue Limit of notched specimens. Some authors in the literature have shown that this issue can be solved by employing an approach based on critical distances, others used elastic fracture mechanics. In this paper the fatigue limit of notched specimens is given by the non-propagating condition of mechanically small surface cracks. According to the so-called cyclic R-curve method, the crack driving force of a growing small crack is compared to its resistance force, which incorporates the gradual build-up of crack closure. The fatigue limit is determined by that applied nominal stress, for which the tangency condition of crack driving and resistance force is satisfied. The approach has been modified to incorporate plasticity effects in the mechanically short crack Regime and it has been applied to a mild and a high-strength steel, in case of an infinite plate with circular hole under remote tensile stress. The method has been successfully applied to the evaluation of fatigue notch-sensitivity in case of surface roughness. KW - Notch fatigue KW - Notch sensitivity KW - Cyclic R-curve KW - Non-propagating cracks KW - Critical distance PY - 2016 DO - https://doi.org/10.1016/j.ijfatigue.2015.06.015 SN - 0142-1123 VL - 82 IS - 1 SP - 71 EP - 79 PB - Elsevier Ltd. CY - Oxford, UK AN - OPUS4-35298 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - Bruchmechanische Bestimmung der Schwingfestigkeit basierend auf der zyklischen R-Kurve N2 - Konventionell wird in der Bauteilauslegung zwischen Konzepten der Schwing- und Betriebsfestigkeit auf der einen und der Bruchmechanik auf der anderen Seite unterschieden. Werden in der Schwingfestigkeitsbewertung Gesamtlebensdauern ermittelt, so sind es in der Bruchmechanik Restlebensdauern bei Vorhandensein eines größeren, d.h., bereits zerstörungsfrei auffindbaren Risses. Daneben gibt es seit längerem Bestrebungen, bruchmechanische Ansätze auch für die Ermittlung der Gesamtlebensdauer fruchtbar zu machen. Der besondere Wert einer solchen Kombination besteht darin, dass die Bruchmechanik die explizite theoretische Behandlung von Eingangsparametern (Kerben, Oberflächenrauhigkeit, Mittelspannung, etc.) erlaubt, die in den konventionellen Ansätzen mit vergleichsweise hoher Ungenauigkeit halbempirisch einbezogen werden. Der Beitrag stellt einen von den Autoren entwickelten bruchmechanischen Ansatz zur Ermittlung von Wöhlerkurven vor, der eine Reihe innovativer Merkmale wie die Anwendung der elastischplastischen Bruchmechanik auf kurze Risse, die Ermittlung der Ausgangsrissgröße aus Rissarrestbetrachtungen, die Beschreibung der transienten Entwicklung des Rissschließeffekts mit Hilfe zyklischer R-Kurven (Risslängenabhängigkeit des Schwellenwertes von der Risstiefe), die theoretische Erfassung von Mehrfachrisswachstum bei Lastniveaus oberhalb der Dauerfestigkeit und statistische Aspekte umfasst. Das diskutierte Beispiel ist eine Schweißverbindung (Stumpfnaht) und wurde im Rahmen des laufenden Cluster-Projektes IBESS (Integrale bruchmechanische Ermittlung der Schwingfestigkeit von Schweißverbindungen) generiert. T2 - 42. Tagung des DVM-Arbeitskreises Betriebsfestigkeit CY - Dresden, Germany DA - 07.10.2015 KW - Bruchmechanik KW - Schwingfestigkeit KW - Zyklische R-Kurve PY - 2015 SN - 1616-5144 N1 - Serientitel: DVM-Bericht – Series title: DVM-Bericht IS - 142 SP - 285 EP - 296 CY - Berlin AN - OPUS4-35299 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Klinger, Christian A1 - Clegg, R. T1 - Fracture mechanics as a tool in failure analysis - Prospects and limitations N2 - Although fatigue crack propagation and fracture cause a large part of failure events in industrial practice, fracture mechanics in failure analysis seems to be still a side issue. Starting from an introduction into important basic questions of failure analysis and fracture mechanics, the authors specify what kind of questions in failure analysis can be effectively solved by fracture mechanics (and which can't). They illustrate their discussion with a number of 13 case studies from the literature. Much more pronounced than in the design stage the benefit of fracture mechanics in failure analysis depends on its accuracy. This is limited by both, intrinsic factors of the method and the availability and quality of the input information. The authors discuss the various aspects and provide the reader with some background information which, as they believe, will be helpful for better understanding the prospects and limitations of fracture mechanics in failure analysis and the conditions of its application. KW - Failure analysis KW - Fracture mechanics KW - Fatigue KW - Root cause KW - Accompanying measures PY - 2015 DO - https://doi.org/10.1016/j.engfailanal.2015.07.001 SN - 1350-6307 SN - 1873-1961 VL - 55 SP - 376 EP - 410 PB - Elsevier Science Publ. CY - Oxford AN - OPUS4-33839 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Hübner, P. T1 - Fracture mechanics assessment of welded structures. Method for S-N curve determination T2 - Symposium on recent trends in fracture and damage mechanics CY - Freiberg DA - 2015-09-24 PY - 2015 AN - OPUS4-33848 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Kiyak, Yusuf A1 - Madia, Mauro A1 - Burgold, Andreas A1 - Riedel, Gernot T1 - Reference loads for plates with semi-elliptical surface cracks subjected to tension and bending for application within R6 type flaw assessment N2 - Two of the authors of the present paper proposed a definition of a reference load F0 which can be used as an alternative option to the common limit load for cases where the definition of the latter might be problematic in the frame of flaw assessment procedures such as R6, BS 7910, SINTAP or FITNET. The reference load is defined as that load at which the ligament yielding parameter Lr approaches one. F0, in general, varies along the crack front. It has to be obtained by finite element analyses but the results can be approximated by analytical expressions. In a previous study of the authors such a solution was presented for tension loaded plates with semi-elliptical surface cracks. In the present paper it is extended to pure bending and to combined bending and tension. KW - Flaw assessment KW - R6 procedure KW - BS 7910 KW - SINTAP KW - FITNET KW - Limit load KW - Reference load PY - 2013 DO - https://doi.org/10.1016/j.engfracmech.2012.11.017 SN - 0013-7944 SN - 1873-7315 VL - 99 SP - 132 EP - 140 PB - Elsevier Science CY - Kidlington AN - OPUS4-30416 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Beier, H.T. T1 - A model for the determination of the fatigue life in technical alloys containing large and small defects N2 - The determination of the fatigue life in technical alloys containing large and small defects must rely on a propagation model which accounts for short and long crack growth. Recently an analytical model which incorporates propagation in the short crack regime and plastic correction for the crack driving force has been presented by two of the authors. This work is intended to show further validation of the model, taking into account data sets for different materials with different testing conditions. Despite the assumptions about missing parameters, the value of which had to be taken from the literature, the predictions showed a fairly good approximation of the fatigue lives. A possible interpretation of the results in terms of multiple crack initiation and propagation at higher loads is proposed. T2 - EFC20 - 20th European conference on fracture CY - Trondheim, Norway DA - 30.06.2014 KW - Fatigue strength KW - Crack propagation KW - Short cracks PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-311961 DO - https://doi.org/10.1016/j.mspro.2014.06.082 SN - 2211-8128 VL - 3 SP - 493 EP - 498 PB - Curran CY - Red Hook, NY, USA AN - OPUS4-31196 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Klinger, Christian A1 - Clegg, R. T1 - Fracture mechanics as a tool in failure analysis T2 - ICEFA IV CY - Lisbon, Portugal DA - 2014-07-06 PY - 2014 AN - OPUS4-31122 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Arafah, D. T1 - Reference load solutions for plates with semi-elliptical surface cracks T2 - ECF 20 - European Conference on Fracture CY - Trondheim, Norway DA - 2014-06-30 PY - 2014 AN - OPUS4-31123 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - RPRT A1 - Zerbst, Uwe ED - Zerbst, Uwe T1 - Analytische bruchmechanische Ermittlung der Schwingfestigkeit von Schweißverbindungen (IBESS-A3) N2 - Ziel des DFG-AiF-Forschungsclusters IBESS war die Entwicklung einer Methodik zur bruchmechanischen Ermittlung von Wöhlerkurven in Schweißverbindungen. Dem vorliegenden Teilprojekt A3 kamen dabei zwei Aufgaben zu: die Entwicklung einer analytischen bruchmechanischen Methodik und die Koordinierung des insgesamt acht Partner umfassenden Clusters. Dieser Bericht fasst die Ergebnisse der erstgenannten Aufgabe zusammen. Die bruchmechanische Methode ist durch folgende Aspekte charakterisiert. (a) Sie beschreibt sowohl Kurz- als auch Langrisswachstum. Ersteres umfasst mechanisch und physikalisch kurze Risse. Mechanisch kurze Risse weisen Abmessungen in der Größenordnung der plastischen Zone auf, weshalb sie zwar bruchmechanisch, nicht jedoch auf der Basis des linear-elastischen K-Konzepts charakterisiert werden können. Im Projekt wurde entsprechend eine Methode zur Bestimmung eines „plastizitätskorrigierten“ zyklischen K-Faktors entwickelt, die auf dem zyklischen J-Integral beruht. Physikalisch kurz bedeutet, dass die Rissschließeffekte im Ausgangsstadium der Rissentwicklung zunächst noch nicht vorhanden sind, dann jedoch graduell aufgebaut werden, bis sie mit Erreichen des Langrissstadiums eine risstiefenunabhängig konstante Größe erreichen. Beschrieben wird dieser Effekt durch die Anwendung der sogenannten zyklischen R-Kurve, der Funktion des Schwellenwerts gegen Rissausbreitung von der Risstiefe. Mittels Rissarrestbetrachtungen des kurzen Risses werden (b) die Ausgangsrissgröße für die weitere Bruchmechanikanalyse und (c) die für N = 107 definierte Dauerfestigkeit der Bauteile bestimmt. Die Analyse erfolgt (d) statistisch, Schwankungen der lokalen Nahtgeometrie entlang des Nahtübergangs über ein Modell äquidistanter Abschnitte einbezogen werden. (e) Eigenspannungen werden sowohl im unbehandelten Schweißzustand als auch nach zyklischer Belastung berücksichtigt. Das Modell wird an insgesamt 33 Wöhlerkurven validiert, die an drei Schweißverbindungsformen (Stumpfstoß, Kreuzstoß, Längssteife) mit je zwei unterschiedlichen Ausführungen, zwei Werkstoffen (S355NL und S960QL), sowie im spannungsarmgeglühten und ungeglühten Zustand experimentell ermittelt wurden. KW - Bruchmechanik KW - Schweißverbindungen KW - Schwingfestigkeit PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-359891 SP - Römisch I EP - 182 PB - Bundesanstalt für Materialforschung und -prüfung (BAM) CY - Berlin AN - OPUS4-35989 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Schork, Benjamin T1 - Fracture mechanics based determination of the fatigue strength of weldments N2 - A fracture mechanics model which shall be applied to the fatigue strength determination of weldments has to focus on various aspects such as: (a) the description of mechanical and physical short fatigue crack extension which is characterised by yielding conditions which do not permit the application of the common ΔK concept and by the gradual build-up of the crack closure effect, (b) a consistent methodology for determining the initial crack size, (c) based on this, the determination of a fatigue limit, (d) the treatment of multiple crack propagation at load levels above this limit, (e) the variation of the local geometry along the weld toe, and (f) statistical effects.The paper gives alimited overview of the work the authors did in this field during the last years within the German project cluster IBESS. A model is presented and briefly discussed which covers the questions above. T2 - XV Portugese Conference on Fracture CY - Lissabon, Portugal DA - 10.02.2016 KW - Weldments KW - fatigue strength KW - fracture mechanics KW - fatigue crack propagation PY - 2016 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-361571 UR - http://www.sciencedirect.com/science/article/pii/S2452321616000044 DO - https://doi.org/doi:10.1016/j.prostr.2016.02.003 VL - 2016/1 SP - 10 EP - 17 PB - Elsevier B.V. CY - Amsterdam, Netherlands AN - OPUS4-36157 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Eufinger, J. A1 - Bruder, T. T1 - Bruchmechanisches Modell zur Ermittlung der Schwingfestigkeit von geschweißten und nichtgeschweißten Proben N2 - Ermüdungsrisse gehen in technischen Materialien in der Regel von Werkstoffdefekten auf oder nahe der Oberfläche aus. Bei Schweißverbindungen können Schweißnahtdefekte, z. B. oberflächennahe Schlackeneinschlüsse die Risseinleitungsphase erheblich verkürzen, so dass der Hauptteil der Lebensdauer auf die Phase der Kurzriss- und zu geringerem Anteil auf die Langrissausbreitung entfällt. Bei nichtgeschweißten Bauteilen aus technischen Werkstoffen starten Ermüdungsrisse häufig an Einschlüssen, oberflächennahen Poren oder anderen Ungänzen. Einerseits ermöglicht dies prinzipiell die Anwendung bruchmechanischer Methoden zur Ermittlung der Schwingfestigkeit, andererseits müssen die Methoden in der Lage sein, spezielle Aspekte des Kurzrisswachstums wie den graduellen Aufbau des Rissschließeffekts und die lokale Rissspitzenplastizität zu erfassen. Im Beitrag werden ein geeignetes analytisches Modell sowie erste Validierungen an Proben aus verschiedenen Aluminiumlegierungen vorgestellt. Der abschließende Teil des Beitrags geht auf Besonderheiten von Schweißverbindungen (Schweißnahtdefekte, Eigenspannungen etc.) im Kontext des vorgestellten Modells ein. Eine Erweiterung des Modells für Schweißverbindungen aus Stahl wird im Rahmen eines kürzlich gestarteten DFG-AiF-Clusterprojekts erfolgen. PY - 2013 UR - http://www.hanser-elibrary.com/doi/pdf/10.3139/120.110465 DO - https://doi.org/10.3139/120.110465 SN - 0025-5300 VL - 55 IS - 7-8 SP - 511 EP - 519 PB - Hanser CY - München AN - OPUS4-30323 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe ED - Baumgartner, J. ED - Melz, T. T1 - Assessment of welded joints by fracture mechanics IBESS - the development of a procedure N2 - The idea to determine the fatigue strength of weldments by means fracture mechanics was originally based on the empirical observation that the major portion of the fatigue life in weldments is frequently spent in crack propagation. The present paper gives a brief overview on the basic principles of fracture mechanics-based determination of fatigue strength and on special features which have to be considered for weldments. Based on this information, the ongoing research project IBESS is introduced and briefly reviewed. T2 - SoSDiD - 4th Symposium on structural durability in Darmstadt CY - Darmstadt, Germany DA - 2014-05-14 KW - Fracture mechanics KW - Fatigue strength KW - (Residual) lifetime KW - Weldments PY - 2014 SP - 49 EP - 66 PB - Fraunhofer Verlag AN - OPUS4-31321 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Klinger, Christian T1 - Anmerkungen zur Auslegung und zum sicheren Betrieb von Radsatzwellen aus der Sicht von Betriebsfestigkeit und Bruchmechanik N2 - Die Sicherheit von Radsatzwellen beruht gegenwärtig auf zwei Säulen: der Schwingfestigkeitsauslegung und periodischen Inspektionen. Ausgehend von einem Schadensfall, der gebrochenen ICE 3-Welle von Köln, 2008, werden ausgewählte Aspekte dieser beiden Säulen diskutiert und Vorschläge zur weiteren Verbesserung gemacht. Diese betreffen u. a. Fragen einer Betriebszeitbegrenzung, Veränderungen der Schwingfestigkeit während des Betriebs infolge von Korrosion und Steinschlag, den Einfluss von Korrosion auf Schwingrissinitiierung und -fortschritt, den potenziellen Einfluss nichtmetallischer Einschlüsse auf die Schwingfestigkeit, die Möglichkeiten, sie im Rahmen der Qualitätssicherung zu detektieren, sowie Fragen der Bruchmechanik und der Zuverlässigkeit zerstörungsfreier Schwingriss-Prüfverfahren im Rahmen eines Konzepts regelmäßiger Inspektionen. KW - Radsatzwellen KW - Schwingfestigkeit KW - Sichere Lebensdauer KW - Schadenstoleranz KW - Zerstörungsfreie Inspektion KW - Korrosion KW - Steinschlag KW - Nichtmetallische Einschlüsse PY - 2014 DO - https://doi.org/10.3139/120.110593 SN - 0025-5300 VL - 56 IS - 7-8 SP - 528 EP - 534 PB - Hanser CY - München AN - OPUS4-31355 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Beier, H.T. T1 - A model for fracture mechanics based prediction of the fatigue strength: Further validation and limitations N2 - Recently two of the authors of the present paper proposed a model for a fracture mechanics based prediction of the S–N characteristics of metallic components with large microstructural defects and supported this by a validation exercise on tensile plates made of an aluminium alloy AL5380 H321. Here the authors extend the study using a number of further data sets from the literature for which data were available at different R ratios. These data include two aluminium alloys, Al 2024-T3 and Al 7075-T6, and a ductile cast iron, EN-GJS- 400-18-LT. Despite of necessary assumptions for the compensation of partially missing input information the results were fairly reasonable with the exception of one data set. The authors identify high applied stress levels in combination with potential multiple crack initiation as the probable root of the problem and propose a scheme how the model can be extended for taking into account crack initiation. KW - Fatigue strength KW - S–N curve KW - Fracture mechanics KW - Crack propagation KW - Short cracks PY - 2014 UR - http://ac.els-cdn.com/S0013794413003901/1-s2.0-S0013794413003901-main.pdf?_tid=1403b676-b8a0-11e3-9087-00000aab0f26&acdnat=1396248522_d8c91133aa860e68196d9325c22ce651 DO - https://doi.org/10.1016/j.engfracmech.2013.12.005 SN - 0013-7944 SN - 1873-7315 SP - 1 EP - 17 PB - Elsevier Science CY - Kidlington AN - OPUS4-30452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Arafah, D. A1 - Zerbst, Uwe T1 - Reference load solutions for plates with semi-elliptical surface cracks subjected to biaxial tensile loading N2 - The yield or limit load is a key parameter with respect to the accuracy of flaw assessment based on R6 type procedures such as the R6 routine, the SINTAP and FITNET method, the standard BS 7910 and others. In a number of previous papers two of the present authors proposed the use of a reference load instead of the common limit load, which not only provided more exact fracture mechanics predictions, but showed also a wider and more general application range than the conventional parameter. Here the method has been extended to biaxial tensile loading and it has been successfully validated by a thorough comparison with finite element results and alternative solutions available in the literature. KW - Flaw assessment KW - R6 procedure KW - Limit load KW - Reference load KW - Biaxial tensile loading PY - 2014 DO - https://doi.org/10.1016/j.ijpvp.2014.02.004 SN - 0308-0161 VL - 119 SP - 19 EP - 28 PB - Applied Science Publ. Ltd. CY - Barking AN - OPUS4-31429 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe T1 - The Fatigue Crack Propagation threshold as a design criterion - actual developments and open issues T2 - ESIS TC1/TC3 workshop on "The fatigue crack propagation threshold as a design criterion" CY - Poitiers, France DA - 2014-11-04 PY - 2014 AN - OPUS4-31686 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Schödel, M. A1 - Beier, H.T. T1 - Parameters affecting the damage tolerance behaviour of railway axles N2 - The paper provides a discussion on damage tolerance options applied to railway axles and factors influencing the residual lifetime as well as the required inspection interval. These comprise material properties such as the scatter of the da/dN–ΔK curve, the fatigue crack propagation threshold ΔKth and the toughness of the material. Parameters affecting axle loading such as the press fit, rotating bending, load history and mixed crack opening modes are discussed. Finally the influence of the initial crack geometry on residual lifetime is simulated. KW - Railway axles KW - Damage tolerance KW - Fatigue crack propagation PY - 2011 DO - https://doi.org/10.1016/j.engfracmech.2010.03.013 SN - 0013-7944 SN - 1873-7315 VL - 78 IS - 5 SP - 793 EP - 809 PB - Elsevier Science CY - Kidlington AN - OPUS4-22491 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Ainsworth, R. A. A1 - Madia, Mauro T1 - Grenzlast oder Referenzlast? - Vorschlag für eine hybride Vorgehensweise bei der elastisch-plastischen Bauteilbewertung T2 - 42. Tagung des DVM-Arbeitskreises Bruchvorgänge - Bruchmechanische Werkstoff- und Bauteilbewertung: Beanspruchungsanalyse, Prüfmethoden und Anwendungen CY - Paderborn, Deutschland DA - 2010-02-23 KW - Bruchmechanische Bauteilbewertung KW - EPRI-Methode KW - Referenzspannungsmethode KW - R6-Routine KW - SINTAP KW - FITNET KW - FKM-Richtlinie KW - Grenzlast KW - Referenzlast PY - 2010 SP - 183 EP - 194 AN - OPUS4-22493 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Beretta, S. A1 - Schödel, M. A1 - Zerbst, Uwe A1 - Luke, M. A1 - Varfolomeyev, I. T1 - Stress intensity factor solutions for cracks in railway axles N2 - The aim of this paper is a collection of stress intensity factor solutions for cracks in railway axle geometries which the authors of the present special issue developed and/or used for damage tolerance analyses. These solutions comprise closed form analytical as well as tabled geometry functions and they refer to solid as well as hollow axles and various crack sites such as the T- and V-notch and the axle body. KW - Railway axles KW - Stress intensity factor PY - 2011 DO - https://doi.org/10.1016/j.engfracmech.2010.03.019 SN - 0013-7944 SN - 1873-7315 VL - 78 IS - 5 SP - 764 EP - 792 PB - Elsevier Science CY - Kidlington AN - OPUS4-22495 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Beretta, S. T1 - Failure and damage tolerance aspects of railway components N2 - Railway structures such as rails and axles are safety relevant components since any failure includes the risk of catastrophic derailment. This paper gives a brief overview on the most important potential failure scenarios driven by fatigue crack initiation and propagation and discusses the effects of important influencing factors such as vehicle weight and speed, track quality and environmental conditions. The present paper summarizes earlier work of the authors in this field. KW - Railway rails KW - Railway axles KW - Fatigue crack propagation KW - Damage tolerance KW - Fracture mechanics PY - 2011 DO - https://doi.org/10.1016/j.engfailanal.2010.06.001 SN - 1350-6307 SN - 1873-1961 VL - 18 IS - 2 SP - 534 EP - 542 PB - Elsevier Science Publ. CY - Oxford AN - OPUS4-22639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Kiyak, Yusuf A1 - Zerbst, Uwe T1 - Extended parametric equations for weld toe stress concentration factors and through-thickness stress distributions in butt-welded plates subject to tensile and bending loading N2 - Based on a large set of 2D finite element analyses, parametric equations for weld toe stress concentration factors and through-thickness stress profiles are provided for butt-welded plates. These cover Single-Vand Double-V joints subject to tensile and bending loading. Compared to the most widespread solutions in the literature, which have also been tested against the finite element data in this work, the application range is extended particularly with respect to the weld toe radius(0.1≤ρ≤4 mm)andangle(10 °≤α≤60 °). Furthermore, two values of excess weld metal are considered (h=0.75;2.5mm). The analyses are performed for a plate thickness of 10 mm. Besides the extended validity range, the proposed equations show also an improved accuracy compared to the existing solutions. KW - Butt welds KW - Weld toes KW - Stress analysis KW - Structures PY - 2016 DO - https://doi.org/10.1007/s40194-016-0377-x VL - 60 IS - 6 SP - 1247 EP - 1259 AN - OPUS4-37959 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - S., Romano A1 - D., Manenti A1 - S., Beretta T1 - Semi-probabilistic method for residual lifetime of aluminothermic welded rails with foot cracks N2 - One of the most frequent and dangerous failure modes in continuous welded rails is fatigue crack Propagation terminated by brittle fracture. Due to the brittleness of the weld material and HAZ and the scatter in its mechanical properties, a statistical approach is necessary. The paper deals with surface cracks at the foot base of aluminothermic welded rails, developing a probabilistic methodology for determining the day by day prospective failure probability. The investigations presented here comprise weld material characterization, simulation of fatigue crack propagation and finally the determination of the failure probability using the Monte Carlo method. The effect of various parameters, such as axle weight, Initial crack size, residual stresses, fatigue crack propagation threshold and date of inspection were analyzed. The results show that, independent of the date of the last inspection, almost any failure event happens in wintertime. This is in accordance with practical experience. However, from the proposed analysis it is evident that the main parameter controlling rail fracture is not only the minimum local temperature, but the temperature range over the whole year. Finally, the results are compared to the standard rail classification method. KW - Railway rails KW - Foot crack KW - Fatigue crack KW - Failure probability KW - Residual lifetime PY - 2016 DO - https://doi.org/10.1016/j.tafmec.2016.05.002 SN - 0167-8442 VL - 85 IS - Part B SP - 398 EP - 411 PB - Elsevier AN - OPUS4-38156 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe T1 - Fracture mechanics in failure analysis N2 - Starting from an introduction into important Basic questions of failure analysis and fracture mechanics, the author specifies what kind of questions in failure analysis can be effectively solved by fracture mechanics (and which can't). He illustrates his discussion with a number of case studies. Much more pronounced than in the design stage the benefit of fracture mechanics in failure analysis depends on ist accuracy. This is limited by both, intrinsic factors of the method and the availability and quality of the input information. The author discusses the various aspects and provides the participants with background information helpful for better understanding the prospects and limitations of fracture mechanics in failure analysis and the conditions of its application. T2 - ICEFA VII - International Conference of Engineering Failure Analysis CY - Leipzig, Germany DA - 03.07.2016 KW - Failure analysis PY - 2016 AN - OPUS4-38166 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe T1 - Schadensentwicklung und Schadenstoleranz von SLM-gefertigten Werkstoffen N2 - Unterschiedliche Werkstoffeigenschaften reagieren auf jeweils spezifische Weise auf Gittertyp, Gefüge und Defekte. Für die schadenstolerante Betrachtung von Werkstoff und Bauteil ist das Verständnis dieser Zusammenhange essentiell. Der Beitrag gibt mit Hinblick auf additiv gefertigte metallische Bauteile (Selective Laser Melting) einen kurzen, keineswegs vollständigen Überblick über Faktoren, die die Steifigkeit, Festigkeit, Duktilität, Zähigkeit, Ermüdungsrissausbreitung und Schwingfestigkeit beeinflussen. Es wird aufgezeigt, wie die bruchmechanische Betrachtung zur Quantifizierung der zusammenhänge beitragen kann. T2 - 1. Tagung des Arbeitskreises Additiv gefertigte Bauteile und Strukturen CY - Berlin, Germany DA - 02.11.2016 KW - Selective Laser Melting (SLM) KW - Werkstoffeigenschaften KW - Schadenstoleranz KW - Bruchmechanik PY - 2016 SN - 2509-8772 VL - Bericht 401 SP - 187 EP - 212 AN - OPUS4-38420 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Heckel, Thomas A1 - Carboni, M. T1 - Non-destructive testing and fracture mechanics - A short discussion N2 - A discussion is provided on the relation between non-destructive testing (NDT) and fracture mechanics. The basic tasks behind this are to guarantee the safety of a component at a potential hazard loading event, to specify inspection intervals or, alternatively, of demands on NDT for a fixed inspection regime, to plan accompanying measures for cases of temporary continued operation of structures in which cracks have been detected, and, finally, fatigue strength considerations which take into account initial defects. T2 - 42nd Annual review of progress in quantitative nondestructive evaluation conference CY - Minneapolis, Minnesota, USA DA - 2015-07-26 KW - Zerstörungsfreie Prüfung KW - Schwingfestigkeit KW - Schadenstoleranz KW - Bruchmechanik KW - probability KW - damage tolerance KW - railway axles KW - inspection PY - 2016 SN - 978-0-7354-1353-5 DO - https://doi.org/10.1063/1.4940614 SN - 0094-243X VL - 1706 SP - 150002-1 EP - 150002-5 PB - AIP Publishing CY - Melville, New York, USA AN - OPUS4-33866 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Der Schwellenwert DKth als Auslegekriterium. Aktuelle Entwicklungen und Fragestellungen. T2 - 47. Tagung des DVM-Arbeitskreises Bruchvorgänge CY - Freiberg DA - 2015-02-10 PY - 2015 AN - OPUS4-32351 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Scolavino, L. A1 - Beretta, S. A1 - Madia, Mauro A1 - Zerbst, Uwe T1 - Critical speed of flawed rotors: global vs local approach N2 - The burst of a disc in rotating machinery can cause catastrophic damage of the equipment and, more importantly, it can represent a mortal threat to anyone in the sphere of influence of the event. In order to minimize the danger associated to a rotating component failure, burst testing is required by the authorities in order to set safety margins to the normal operating speeds. Moreover more accurate predicting tools are required for designing the components. This paper presents the results of a numerical and analytical study on the assessment of the crack driving force for discs containing surface flaws. The aim is to provide a simple, though reliable, tool in order to be able to calculate the possible dangerous in-service speed for a rotating component and, therefore, to set burst margins above the normal operating conditions of the equipment. An R6-like flaw assessment procedure is adopted considering different assumptions in the definition of the critical speed and the analytical predictions are compared with the results of elastic-plastic finite element analysis of disc. In particular, the validity and potentiality of the method is proved for surface flaws in different positions in the disc. T2 - ASME Turbo Expo 2014 - GT2014 CY - Düsseldorf, Germany DA - 16.06.2014 KW - Critical speed KW - Flawed rotors KW - Flaw assessment PY - 2014 SN - 978-0-7918-4576-9 DO - https://doi.org/10.1115/GT2014-26881 VL - 7A SP - 26881, 1 EP - 8 AN - OPUS4-32382 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe T1 - Statistische Aspekte der Bauteilbewertung T2 - 47. Tagung des DVM-Arbeitskreises Bruchvorgänge; Weiterbildungsseminar CY - Freiberg, Germany DA - 2015-02-09 PY - 2015 AN - OPUS4-32845 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -