TY - JOUR A1 - Zerbst, Uwe A1 - Hensel, Jonas T1 - Application of fracture mechanics to weld fatigue JF - International Journal of Fatigue N2 - The application of fracture mechanics to the determination of the fatigue behavior of weldments is discussed with the focus on classic fatigue, i.e., the overall fatigue life and the fatigue strength in terms of an S-N curve and the endurance limit. The following issues are addressed: specific features of short fatigue crack propagation, an adequate initial crack size, multiple crack propagation and its statistical treatment as well as welding residual stresses. As an example, an approach of the authors is applied to the determination of FAT classes for a butt weld with varying weld toe geometry. KW - Weld fatigue KW - Weld toe geometry KW - Short crack propagation KW - FAT class concept PY - 2020 DO - https://doi.org/10.1016/j.ijfatigue.2020.105801 SN - 0142-1123 VL - 139 SP - 105801 PB - Elsevier Ltd. AN - OPUS4-50991 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Vormwald, M. A1 - Beier, T. T1 - Fatigue strength and fracture mechanics - A general perspective JF - Engineering fracture mechanics N2 - Common fracture mechanics based fatigue considerations are usually limited to the residual lifetime determination of so-called long cracks. The extension of this concept to the total lifetime, as in the S-N curve approach, requires an adequate description of short crack propagation which cannot be based on the Delta K concept, and it must consider the crack closure phenomenon as well as its gradual build-up at the short crack stage. Further, it has to provide a meaningful definition of initial crack dimensions and a solution for the multiple crack problem at stress levels higher than the fatigue limit as it is specific for some configurations such as weldments. This paper aims at a discussion of all these points and offers possible solutions which are illustrated by examples taken from the German IBESS project on fracture mechanics based determination of the fatigue strength of weldments, the results of which will be discussed in more detail in this Special issue. KW - Fatigue strength KW - Endurance limit KW - Fracture mechanics KW - Short crack propagation KW - Multiple cracking KW - Weldments PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.04.030 SN - 0013-7944 SN - 1873-7315 VL - 198 SP - 2 EP - 23 PB - Elsevier AN - OPUS4-46862 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Beier, H. Th. T1 - Fatigue strength and life determination of weldments based on fracture mechanics JF - 3rd international Symposium on fatigue design and material defects (FDMD 2017) N2 - The paper provides an overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common ΔK concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit and the finite life branch of the S-N curve are determined. Besides a brief introduction into the approach, validation examples are presented. These comprise different weldment types (butt welds, cross joints and longitudinal stiffened plates), two steels (S355NL and S960QL) of quite different strengths, different weld geometries due to different welding techniques (WIG, MAG), as-welded and stress relieved welds and different stress ratios varying from R = -1 to R = 0.5. T2 - FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Weldments KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-438500 DO - https://doi.org/10.1016/j.prostr.2017.11.106 SN - 2452-3216 VL - 7 SP - 407 EP - 414 PB - ScienceDirect CY - Lecco, Italy AN - OPUS4-43850 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Hilgenberg, Kai T1 - Damage development and damage tolerance of structures manufactured by selective laser melting - a review JF - 3rd International symposium on fatigue design and material defects (FDMD 2017) N2 - The additive manufacturing technology of Selective Laser Melting (SLM) experiences a rapid development within an increasing marked of quite different application fields. The properties of SLM materials and structures are influenced by a number of tech-nological parameters such as the metal powder (particle size, homogeneity, cleanliness), the laser tool (power, beam diameter, pulse lengths), the scanning operation (speed, sequence and orientation of melting paths), parameters of the over-all equipment (design and preheating of the base plate, currents and turbulence in the protective gas atmosphere) and, last not least, the hatching strategy including the build-up direction of the structure with respect to the loading direction of the component. For the perspective use of SLM structures as load carrying, safety-relevant components the knowledge of their mechanical properties is necessary. It is essential to understand these in the context of the manufacturing-related features and at the back-ground of the basic characteristics of metallic materials: crystal lattice, microstructure and material defects. The paper provides an overview on factors which affect the mechanical parameters stiffness, strength, ductility, toughness, fatigue crack propagation and fatigue strength in the context of selective laser melting. T2 - FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-438511 DO - https://doi.org/10.1016/j.prostr.2017.11.071 SN - 2452-3216 VL - 7 SP - 141 EP - 148 PB - ScienceDirect CY - Lecco, Italy AN - OPUS4-43851 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Hilgenberg, Kai T1 - Damage development and damage tolerance of structures manufactured by selective laser melting N2 - The additive manufacturing technology of Selective Laser Melting (SLM) experiences a rapid development within an increasing marked of quite different application fields. The properties of SLM materials and structures are influenced by a number of tech-nological parameters such as the metal powder (particle size, homogeneity, cleanliness), the laser tool (power, beam diameter, pulse lengths), the scanning operation (speed, sequence and orientation of melting paths), parameters of the over-all equipment (design and preheating of the base plate, currents and turbulence in the protective gas atmosphere) and, last not least, the hatching strategy including the build-up direction of the structure with respect to the loading direction of the component. For the perspective use of SLM structures as load carrying, safety-relevant components the knowledge of their mechanical properties is necessary. It is essential to understand these in the context of the manufacturing-related features and at the back-ground of the basic characteristics of metallic materials: crystal lattice, microstructure and material defects. The paper provides an overview on factors which affect the mechanical parameters stiffness, strength, ductility, toughness, fatigue crack propagation and fatigue strength in the context of selective laser melting. T2 - 3rd International Symposium on Fatigue Design an Material Defects, FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 AN - OPUS4-43853 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Vormwald, M. T1 - Fatigue strength and fracture mechanics JF - Procedia Structural Integrity N2 - If fracture mechanics shall be applied to the total lifetime respectively the fatigue limit of components (within the meaning of the S-N curve approach) it has to address four challenges: (a) It has to adequately describe so-called short crack propagation, which cannot be based on the common long crack concepts for principle reasons. Since the crack size is in the order of the plastic zone size, the modelling of short crack propagation cannot be based on the common linear elastic Delta K concept. Instead, an elastic-plastic parameter such as the cyclic J integral has to be applied. A second point is that the crack closure concept has to be modified in that the crack opening stress is not a constant, crack size- independent parameter but shows a transient behaviour with increasing short crack size. (b) It has to provide a meaningful definition of the initial crack dimensions as the starting point for an S-N curve relevant (residual) lifetime analysis. This can be based either on the (statistical) size of material defects which can be treated as cracks or by the size of the crack which would arrest subsequent to early crack propagation, whatever is larger. (c) It has to cope with the problem of multiple cracks for load levels higher than the fatigue limit such as it occurs in many applications in the absence of very large initial defects. (d) This requires consequent statistical treatment taking into account variations in the local geometry of the area where crack initiation has to be expected as well as the scatter in the initial crack size and in the material data used for the analyses. T2 - 2nd International Conference on Structural Integrity CY - Funchal, Madeira, Portugal DA - 04.09.2017 KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 DO - https://doi.org/10.1016/j.prostr.2017.07.065 SN - 2452-3216 VL - 5 SP - 745 EP - 752 AN - OPUS4-42545 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Vormwald, M. T1 - Fatigue strength and fracture mechanics N2 - If fracture mechanics shall be applied to the total lifetime respectively the fatigue limit of components (within the meaning of the S-N curve approach) it has to address four challenges: (a) It has to adequately describe so-called short crack propagation, which cannot be based on the common long crack concepts for principle reasons. Since the crack size is in the order of the plastic zone size, the modelling of short crack propagation cannot be based on the common linear elastic Delta K concept. Instead, an elastic-plastic parameter such as the cyclic J integral has to be applied. A second point is that the crack closure concept has to be modified in that the crack opening stress is not a constant, crack size- independent parameter but shows a transient behaviour with increasing short crack size. (b) It has to provide a meaningful definition of the initial crack dimensions as the starting point for an S-N curve relevant (residual) lifetime analysis. This can be based either on the (statistical) size of material defects which can be treated as cracks or by the size of the crack which would arrest subsequent to early crack propagation, whatever is larger. (c) It has to cope with the problem of multiple cracks for load levels higher than the fatigue limit such as it occurs in many applications in the absence of very large initial defects. (d) This requires consequent statistical treatment taking into account variations in the local geometry of the area where crack initiation has to be expected as well as the scatter in the initial crack size and in the material data used for the analyses. T2 - 2nd International Conference on Structural Integrity CY - Funchal, Madeira, Portugal DA - 04.09.2017 KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 AN - OPUS4-42546 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -