TY - JOUR A1 - Zerbst, Uwe T1 - Application of Fracture Mechanics to welds with crack origin at the weld toe - a Review - Part 1: Consequences of inhomogeneous microstructure for materials testing and failure assessment N2 - The two-part paper provides an overview on the state-of-the-art in the application of engineering fracture mechanics to weldments. This, of course, cannot be exhaustive but is limited to butt and fillet welds with crack initiation at weld toes. In the present first pari, the authors briefly focus on the susceptibility of welds to cracks and other defects. Following this, they discuss in more detail the consequences of material inhomogeneity across the weld for fracture mechanics. Inhomogeneity causes scatter in fracture toughness and strength mis-match effects which both have to be considered in fracture toughness testing, crack driving force determination and fracture assessment of welded components. Part 2 of the paper series will add a discussion of welding residual stresses and questions of applying fracture mechanics to residual as well as total lifetime estimation of welds under cyclic loading. KW - Fracture toughness KW - Crack driving force KW - Material inhomogeneity KW - Strength mis-match PY - 2019 DO - https://doi.org/10.1007/s40194-019-00801-5 SN - 0043-2288 VL - 63 IS - 6 SP - 1715 EP - 1732 PB - Springer AN - OPUS4-48755 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Hildenberg, Kai A1 - Hrabe, N. T1 - Thoughts on damage tolerance and safe life design in metallic AM structures N2 - Der Vortrag bietet eine Diskussion zur Abschätzung des Schadenstoleranzverhaltens metallischer AM - Komponenten. Im Fokus stehen Probleme bei der Ermittlung repräsentativer Materialdaten, der Einfluss von Materialdefekten und Eigenspannungen. Ausgehend von derzeitigem Stand auf dem Gebiet werden Möglichkeiten der Schadenstoleranten Bauteileauslegung von AM diskutiert. N2 - The presentation provides a discussion and damage tolerant assessment of metallic AM components. In the focus are problems of the determination of representative material data, the effect of material defects and residual stresses. Starting with the actual state-of-the-art in the field, options and possibilities of a damage tolerant design for AM are discussed. T2 - BAM/NIST-Workshop on Fatigue of Additive Manufactured Metallic Components CY - Berlin, Germany DA - 16.05.2019 KW - Schadenstolerante Bauteilauslegung KW - Repräsentative Werkstoffeigenschaften KW - Defekte Eigenspannung KW - Damage tolerant component design KW - Representative material properties KW - Residual stresses PY - 2019 AN - OPUS4-48810 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Vormwald, M. T1 - Applying fracture mechanics to fatigue strength determination - some basic considerations N2 - A discussion is provided on demands that must be met in order to apply fracture mechanics to the determination of overall fatigue lifetime and strength, i.e., S-N curves and fatigue limits. These comprise the determination of the cyclic crack driving force for all stages of fatigue crack propagation, in particular for the short crack stage where the crack driving force has to be determined for elastic-plastic deformation and the gradual build-up of the crack closure phenomenon. Special emphasis is put on a fatigue damage relevant specification of the initial crack size. Different approaches in the literature are discussed. Another important aspect is the adequate treatment of multiple crack propagation. Finally, the discussion is illustrated by an example of a butt weld made of a medium strength steel. KW - Multiple cracks KW - Fatigue strength KW - Fracture mechanics KW - Fatigue crack propagation KW - Initial crack size PY - 2019 DO - https://doi.org/10.1016/j.ijfatigue.2019.05.009 SN - 0142-1123 VL - 126 SP - 188 EP - 201 PB - Elsevier Ltd. AN - OPUS4-48091 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Hensel, J. A1 - Nitschke-Pagel, T. T1 - Schweißeigenspannungen und Bauteilintegrität aus bruchmechanischer Sicht N2 - Der Vortrag thematisiert die Behandlung von Schweißeigenspannungen bei der Auslegung geschweißter Bauteile. Ausgehend von Fragen der Klassifizierung unterschiedlicher Typen von Eigenspannungen wird auf Fragen der Behandlung von Primär- und Sekundärspannungen, der Ermittlung und Aussagefähigkeit von Eigenspannungs-Tiefen-Profilen und der Stabilität der Eigenspannungen bei zyklischer Beanspruchung eingegangen. Neben der Auslegung auf Bruch wird die Beschreibung der Ermüdungsrissausbreitung bei Vorhandensein von Eigenspannungen diskutiert, wobei neben der klassischen Langrissbruchmechanik auch Besonderheiten der Kurzrissbruchmechanik angesprochen werden. T2 - DVM - Workshop "Eigenspannungen in der industriellen Praxis" CY - Berlin, Germany DA - 05.11.2019 KW - Schweißeigenspannungen KW - Primär- und Sekundärspannungen KW - Schweißeigenspannungs-Tiefen-Profile KW - Stabilität von Eigenspannungen KW - Kurz- und Langriss-Ermüdungsbruchmechanik PY - 2019 AN - OPUS4-49498 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - BOOK A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Schork, B. A1 - Hensel, J. A1 - Kucharczyk, P. A1 - Tchoffo Ngoula, D. A1 - Tchuindjang, D. A1 - Bernhard, J. A1 - Beckmann, C. T1 - Fatigue and fracture of weldments - The IBESS approach for the determination of the fatigue life and strength of weldments by fracture mechanics analysis N2 - The acronym IBESS stands for "Integrale Bruchmechanische Ermittlung der Schwingfestigkeit von Schweißverbindungen" which, translated from German, means "integral fracture mechanics determination of the fatigue strength of welds". the method introduced in this study is the outcome of a German Research cluster in which eight partners were involved. A list of them is found at the end this study. The IBESS method is characterized by a number of partially novel aspects and elements of fracture mechanics applied to the evaluation of fatigue stength of welds. The most important ones are: (a) Determination of fatigue crack propagation for mechanically/physically short and long cracks. (b) Determination of an elastic-plastic crack driving force for the treatment of mechanically short cracks. To that purpose an analytical expression for the cyclic J-integral was developed and validated against finite element results. (c) The gradual build-up of the crack closure phenomenon is determined by using cyclic R-curves which describe the crack size dependency of the fatigue crack propagation threshold in the physically short crack growth regime. (d) A physically meaningful initial crack size is defined for total life consideration. It is based on a two-criteria approach. Based on a cyclic R-curve analysis, the crack size at crack arrest is determined as a lower bound. If, however, a pre-existing crack-like defect is larger than this, its dimensions define the initial crack size. (e) Multiple crack propagation at the weld toe is considered. (f) In conjunction with this, the variation of the weld toe geometry is considered in a stochastic model. (g) As a result, both the fatigue limit (defined for 107 loading cycles) and the finite life (high cycle) fatigue S-N curve are obtained statistically. (h) At various analysis steps, parametric equations have been developed which allow for analytical calculations instead of complete stochastic analyses based on finite elements which are unrealistic even at present. (i) The method has been validated with a large number of S-N curves including two materials, three weldment types with two geometries, each referring to differnt manufacturing technologies and the as-welded and stressrelieved state. (j) Althrough not finally solved, an extended discussion is provided on the issue of welding residual stresses including their redistribution under cyclic loading. (k) A number of simplifications is proposed at lower analyses levels which, however, partly lack complete validation by now. KW - Crack initation KW - Short crack KW - Fracture of weldments KW - IBESS PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-468853 UR - https://www.kriso.ee/db/9783030040727.html SN - 978-3-03004-072-7 SP - 1 EP - 189 PB - Springer-Verlag CY - Berlin AN - OPUS4-46885 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - BOOK A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Schork, B. A1 - Hensel, J. A1 - Kucharczyk, P. A1 - Ngoula, D. A1 - Tchuindjang, D. A1 - Bernhard, J. A1 - Beckmann, C. T1 - The IBESS approach for the determination of the fatigue life and strength of weldments by fracture mechanics analysis N2 - This book provides a comprehensive and thorough guide to those readers who are lost in the often-confusing context of weld fatigue. It presents straightforward information on the fracture mechanics and material background of weld fatigue, starting with fatigue crack initiation and short cracks, before moving on to long cracks, crack closure, crack growth and threshold, residual stress, stress concentration, the stress intensity factor, J-integral, multiple cracks, weld geometries and defects, microstructural parameters including HAZ, and cyclic stress-strain behavior. The book treats all of these essential and mutually interacting parameters using a unique form of analysis. KW - Fatigue crack propagation KW - Cyclic J-integral KW - Cyclic R-curve analysis KW - Fatigue S-N curve KW - HAZ PY - 2019 SN - 978-3-030-04072-7 SN - 978-3-030-04073-4 DO - https://doi.org/10.1007/978-3-030-04073-4 SP - 1 EP - 130 PB - Springer CY - Cham AN - OPUS4-47576 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Klinger, Christian A1 - Bettge, Dirk A1 - Murakami, Y. T1 - Defects as a root cause of fatigue failure of metallic components. III: Cavities, dents, corrosion pits, scratches N2 - This third part of the review on defects as root cause of fatigue failure addresses cavities (pores, micro-shrinkages, unmelted regions), defective microstructures and microcracks as material defects and defects due to local damage during manufacturing, service and maintenance such as dents, scratches and localized corrosion. In addition, damage due to contact fatigue and the effect of surface roughness are discussed in the context of fatigue failure. Also addressed is the competition between different kinds of defects in controlling the initiation and early growth of fatigue cracks. KW - Pores KW - Micro-shrinkages KW - Impact damage KW - Contact fatigue KW - Corrosion pits KW - Scratches PY - 2019 DO - https://doi.org/10.1016/j.engfailanal.2019.01.034 SN - 1350-6307 VL - 97 SP - 759 EP - 776 PB - Pergamon-Elsevier Science Ltd CY - Oxford, England AN - OPUS4-47373 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Klinger, Christian A1 - Bettge, Dirk A1 - Murakami, Y. T1 - Defects as a root cause of fatigue failure of metallic components. I: Basic aspects N2 - According to the definition of the ASM handbook [1,3], a defect is "an imperfection. that can be shown to cause failure by a quantitative analysis and that would not have occurred in the absence of the imperfection". The topic of the present three-part review is a discussion of defects which can cause failure in cyclically loaded structures. The features discussed comprise material defects such as non-metallic inclusions, pores or micro-shrinkages, etc. and geometric defects such as surface roughness and secondary notches which have their origin in manufacturing, and defects such as surface damage due to scratches, impact events or contact fatigue as well as corrosion pits which arise in service. In this first part, the discussion is prefaced by an introduction to basic aspects which are essential for a deeper understanding of the characteristics and mechanisms how the defects influence fatigue crack initiation and propagation. These include the life cycle of a fatigue crack from initiation up to fracture, crack arrest, multiple crack initiation and coalescence, and the material and geometrical properties affecting these. KW - Defects KW - Fatigue crack propagation stages KW - Crack arrest KW - Multiple cracks PY - 2019 DO - https://doi.org/10.1016/j.engfailanal.2019.01.055 SN - 1350-6307 VL - 97 SP - 777 EP - 792 PB - Pergamon-Elsevier Science Ltd CY - Oxford, England AN - OPUS4-47372 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Klinger, Christian A1 - Bettge, Dirk A1 - Murakami, Y. T1 - Defects as a root cause of fatigue failure of metallic components. II: Non-metallic inclusions N2 - This second part of the review on defects as root cause of fatigue failure comprises the origin, the nature and the effects of non-metallic inclusions. Topics addressed are the different kinds of inclusions formed during the manufacturing process, various types of mis-match causing local stresses and, as a consequence, fatigue crack initiation, and effects of characteristics such as size, morphology, localization, spatial distribution and orientation of the defects on the fatigue behavior. Methods for inclusion counting and sizing are discussed along with statistical aspects necessary to be considered when evaluating structural components. KW - Non-metallic inclusions KW - Mis-match KW - Inclusion size KW - Inclusion cluster KW - Statistics PY - 2019 DO - https://doi.org/10.1016/j.engfailanal.2019.01.054 SN - 1350-6307 VL - 98 SP - 228 EP - 239 PB - Elsevier Ltd. AN - OPUS4-47459 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Hilgenberg, Kai A1 - Daum, Werner A1 - Maierhofer, Christiane A1 - Altenburg, Simon A1 - Bruno, Giovanni A1 - Heckel, Thomas A1 - Skrotzki, Birgit A1 - Zerbst, Uwe A1 - Kranzmann, Axel A1 - Bettge, Dirk A1 - Sommer, Konstantin A1 - Seeger, Stefan A1 - Nitsche, Michael A1 - Günster, Jens A1 - Evans, Alexander T1 - Additive manufacturing at the BAM: We focus on Safety N2 - In Germany, the Federal Institute for Materials Research and Testing (BAM) is addressing challenges in the implementation of additive manufacturing on the industrial landscape for safety-critical applications. KW - Process development KW - Additive Manufacturing KW - In-situ Process Monitoring KW - Non-destructive Materials KW - Characterisation KW - Safety KW - Fatigue KW - Environment KW - Standardisation PY - 2019 UR - https://static.asminternational.org/amp/201910/22/ SN - 0882-7958 VL - 177 IS - 7 SP - 22 EP - 26 PB - ASM International CY - Materials Park, OH, USA AN - OPUS4-49780 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Analytical flaw assessment N2 - The paper provides a review on analytical flaw assessment methods with the focus on fracture under monotonic loading and fatigue crack propagation. The first topic comprises linear elastic as well as elastic-plastic fracture mechanics approaches. It essentially follows their historical development. Topics which are separately discussed are reference/Limit loads, the treatment of secondary stresses, strength mismatch, constraint, unstable crack propagation (monotonic R-curve analyses) and statistical aspects. With respect to fatigue crack propagation the analytical treatment of crack closure and constraint and the Determination of the cyclic elastic-plastic crack driving force is discussed. Finally, cyclic Rcurve analyses are briefly addressed. KW - Monotonic and cyclic crack driving force KW - Secondary stresses KW - Strength mismatch KW - Constraint KW - Crack closure KW - R-curve analysis PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.12.002 SN - 0013-7944 SN - 1873-7315 VL - 187 SP - 316 EP - 367 PB - Elsevier AN - OPUS4-44234 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe T1 - Foreword N2 - The subject of this Special Issue is the fracture mechanics-based determination of the fatigue strength of weldments. Except for one, all papers were written in closer or wider relation to a methodology developed within the framework of the German Project cluster IBESS. Some of them provide background or supplementary information needed in that context but which is also relevant in a wider frame of research activities. The acronym IBESS stands for the topic of this Special Issue (in German: „Integrale Methode zu Bruchmechanischen Ermittlung der Schwingfestigkeit von Schweißverbindungen). Eight partners were involved. The cluster was cooperatively founded by the German Research Foundation (Deutsche Forschungsgemeinschaft) and by the German AiF Network (Arbeitsgemeinschaft industrieller Forschungsvereinigungen) for industrial research. KW - Fracture mechanics PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2018.05.046 SN - 0013-7944 VL - 198 IS - SI SP - 1 EP - 1 PB - Elsevier Ltd. AN - OPUS4-48696 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Madia, Mauro A1 - Zerbst, Uwe A1 - Beier, T. A1 - Schork, B. T1 - The IBESS model – Elements, realisation and validation N2 - The work presents the procedure developed within the German research project IBESS, which allows for the fracture mechanics-based prediction of the fatigue strength of welded joints under constant amplitude loading. Based on the experimental observations of the crucial failure mechanisms, the approach focuses on the short crack propagation, where elastic-plastic fracture mechanics and the build-up of closure effects must be considered as well as the variability of the local geometry at the weld toe and the modelling of multiple crack interaction. Analytical solutions are provided for the approximation of the through-thickness stress profiles at the weld toe and for the determination of the crack driving force in the form of a plasticity-corrected stress intensity factor range ∆K_p. Proposals for the determination of the initial crack size and the crack closure factor are also included. The approach is validated against a large number of experimental data, which comprises fatigue tests on individual cracks monitored by heat tinting and beach-marking techniques, as well as stress life curves. Three kinds of welded joints, two steels of significant different strengths and three stress ratios are considered. The results show that the procedure provides good estimations of the statistical distribution of the fatigue strength of welded joints both for the finite and infinite life regime. Furthermore, the predictions are compared with available benchmark data for structural steels. KW - Welded joints KW - Life prediction KW - Fatigue crack growth KW - Short cracks KW - Crack closure PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.08.033 SN - 0013-7944 SN - 1873-7315 VL - 198 SP - 171 EP - 208 PB - Elsevier AN - OPUS4-46852 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Gerwien, Peter A1 - Kucharczyk, P. A1 - Münstermann, S. A1 - Schork, B. T1 - Fracture-mechanics-based prediction of the fatigue strength of weldments. Material aspects N2 - Any fracture mechanics based determination of the fatigue strength of weldments requires different input information such as the local weld geometry and material data of the areas the crack is passing through during its propagation. The latter is so far not a trivial task as the fatigue crack is usually initiated at the weld toe at the transition from the weld metal to the heat affected zone and it subsequently propagates through the different microstructures of the latter to eventually grow into the base material and to cause final fracture. This paper describes how the material input information has gained particularly for heat affected zone material by thermo-mechanically simulated material specimens for two steels of quite different static strength. The data comprise the cyclic stress-strain curve, the crack closure effect-corrected crack growth characteristics, long crack fatigue crack propagation thresholds, the dependency of the parameter on the crack length and monotonic fracture resistance. The substantial experimental effort was necessary for the validation exercises of the IBESS approach, however, within the scope of practical application more easily applicable estimating methods are required. For that purpose the paper provides a number of appropriate proposals in line with its check against the reference data from the elaborate analyses. KW - Heat affected zone KW - Cyclic stress-strain curve KW - Fatigue crack propagation KW - Fatigue crack propagation threshold KW - Fracture resistance PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.09.010 SN - 0013-7944 SN - 1873-7315 VL - 198 SP - 79 EP - 102 PB - Elsevier AN - OPUS4-46854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Maierhofer, J. A1 - Kolitsch, S. A1 - Gänser, H.-P. A1 - Pippan, R. T1 - The cyclic R-curve – Determination, problems, limitations and application N2 - The so-called cyclic R curve, i.e. the crack size dependence of the fatigue crack propagation threshold in the physically short crack regime, is a key parameter for bringing together fatigue strength and fracture mechanics concepts. Its adequate determination is of paramount importance. However, notwithstanding this relevance, no test guideline is available by now and only very few institutions have spent research effort on cyclic R curves so far. The aim of the present paper is to give an overview on the state-of-the-art. Besides an introduction into the basic principles, the discussion will concentrate on the experimental determination on the one hand and questions of its application on the other hand. KW - Cyclic R-curve KW - Fatigue crack propagation threshold KW - Crack closure mechanisms KW - Cyclic R-curve analysis KW - Kitagawa-Takahashi diagram PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.09.032 SN - 0013-7944 SN - 1873-7315 VL - 198 SP - 45 EP - 64 PB - Elsevier AN - OPUS4-46855 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Tchoffo Ngoula, D. A1 - Beier, T. A1 - Vormwald, M. T1 - Cyclic J-integral: Numerical and analytical investigations for surface cracks in weldments N2 - The cyclic J-integral (∆J-integral) is a crack tip parameter of elastic-plastic fracture mechanics which can be used as governing parameter for the description of fatigue crack growth (FCG) in metallic structures. In this contribution, it is applied for modelling FCG in weldments. The ∆J-integral is determined by means of analytical approximation formulas as well as numerical methods. An analytical solution, which takes into account effects of the local ligament plasticity, was derived. This solution is based on well established methods such as R6, BS7910 and SINTAP which were modified for cyclic loading. It incorporates methods for the description of short crack closure behaviour as well as the well known analytical (long) crack closure function of Newman. A specific code was written to evaluate the ∆J-integral numerically in the course of finite element based crack growth simulations. The code was first validated for an infinite plate with centre crack by applying elastic and elastic-plastic material behaviour. Next, the ∆J-integral was calculated for cracks in various butt and cruciform welded joints. The results were compared with the results of the derived analytical approximation formula. A good accordance was achieved between the results. KW - Cyclic J-integral KW - Elastic-plastic fracture mechanics KW - Fatigue crack growth KW - Short cracks KW - Weldments PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.06.023 SN - 0013-7944 VL - 198 SP - 22 EP - 44 PB - Elsevier AN - OPUS4-46857 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Schork, B. A1 - Kaffenberger, M. A1 - Oechsner, M. A1 - Kucharzcyk, P. A1 - Hensel, J. A1 - Bernhard, J. A1 - Tchuindjang, D. T1 - The effect of the local and global weld geometry as well as material defects on crack initiation and fatigue strength N2 - The paper provides an application of the IBESS approach to the investigation of the influence of various parameters of the global and local weld geometry as well as material defects on the fatigue strength of weldments. For this purpose, the global weld parameters, such as the weld toe radius, the flank angle, the excess weld metal, local secondary notches (in the present study as a measure of surface imperfections) and inclusions sizes have been determined as statistical distributions for different joint types and geometries and two steels of different strengths. The results are in line with literature data and reveal the potential of the theoretical approach to predict the correct trends. The combination with an advanced weld quality system has been demonstrated to be possible. KW - Weldments KW - Fatigue strength KW - Fracture mechanics KW - Weld geometry KW - Inclusions KW - Multiple crack initiation PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.07.001 SN - 0013-7944 SN - 1873-7315 VL - 198 SP - 103 EP - 122 PB - Elsevier AN - OPUS4-46858 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Klinger, Christian A1 - Madia, Mauro T1 - Defekte als Ursache für das Versagen metallischer Komponenten N2 - Ein Defekt ist „eine Imperfektion …, für die in einer quantitativen Analyse gezeigt werden kann, dass sie Versagen verursacht hat, welches ohne die Imperfektion nicht aufgetreten wäre“. Defekte in diesem Sinn können einerseits Werkstoffimperfektionen wie nichtmetallische Einschlüsse, Poren und Porennester, Nichtdurchschweißungen oder Bereiche defekter Mikrostruktur, andererseits unbeabsichtige geometrische Imperfektionen wie Kratzer, Eindrücke, Korrosionsgrübchen, Einbrandkerben, zu große Oberflächenrauheit u.a. sein. Sie können in der Fertigung, im Betrieb oder auch bei der Wartung entstehen. Nicht jede Imperfektion ist ein Defekt im oben genannten Sinn. Entscheidend ist zumeist nicht, dass an ihr ein oder mehrere Risse initiiert werden, sondern dass wenigstens ein Riss wachstumsfähig bleibt und so innerhalb der projektierten Lebensdauer zum Bruch oder anderweitigem Versagen führt. Aufgrund des begrenzten Umfangs bleibt die vorliegen-de Übersicht beschränkt. T2 - Sitzung des DVK AK Betriebsfestigkeit CY - Stuttgart/Renningen, Germany DA - 26.09.2018 KW - Werstoff- und geometrische Imperfektion KW - Rissausbreitungsstadien KW - Rissarrest KW - Einschlüsse KW - Poren KW - Oberflächenschädigung KW - Rauheit PY - 2018 AN - OPUS4-46883 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Hensel, J. A1 - Nitschke-Pagel, T. A1 - Tchoffo Ngoula, D. A1 - Beier, T. T1 - Welding residual stresses as needed for the prediction of fatigue crack propagation and fatigue strength N2 - Welding residual stresses have an impact on the performance of welded structures, on their fracture resistance, their resistance against fatigue crack propagation and, most important, their fatigue strength and fatigue lifetime. The present paper provides an overview on the issue mainly from the point of view of the application of fracture mechanics to the determination of the fatigue strength as the topic of this Special issue. Besides own experimental and theoretical data a comprehensive discussion is provided in that context which includes the definition and interaction of short- and long-range (or reaction) residual stresses, the effect of cyclic mechanical loading and its treatment in fracture and fatigue analyses. KW - Welding residual stresses KW - Fracture KW - Fatigue crack propagation KW - Elastic follow-up PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.10.024 SN - 0013-7944 VL - 198 SP - 123 EP - 141 PB - Elsevier AN - OPUS4-46860 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Vormwald, M. A1 - Beier, T. T1 - Fatigue strength and fracture mechanics - A general perspective N2 - Common fracture mechanics based fatigue considerations are usually limited to the residual lifetime determination of so-called long cracks. The extension of this concept to the total lifetime, as in the S-N curve approach, requires an adequate description of short crack propagation which cannot be based on the Delta K concept, and it must consider the crack closure phenomenon as well as its gradual build-up at the short crack stage. Further, it has to provide a meaningful definition of initial crack dimensions and a solution for the multiple crack problem at stress levels higher than the fatigue limit as it is specific for some configurations such as weldments. This paper aims at a discussion of all these points and offers possible solutions which are illustrated by examples taken from the German IBESS project on fracture mechanics based determination of the fatigue strength of weldments, the results of which will be discussed in more detail in this Special issue. KW - Fatigue strength KW - Endurance limit KW - Fracture mechanics KW - Short crack propagation KW - Multiple cracking KW - Weldments PY - 2018 DO - https://doi.org/10.1016/j.engfracmech.2017.04.030 SN - 0013-7944 SN - 1873-7315 VL - 198 SP - 2 EP - 23 PB - Elsevier AN - OPUS4-46862 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -