TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Beier, H.T. T1 - A model for fracture mechanics based prediction of the fatigue strength: Further validation and limitations N2 - Recently two of the authors of the present paper proposed a model for a fracture mechanics based prediction of the S–N characteristics of metallic components with large microstructural defects and supported this by a validation exercise on tensile plates made of an aluminium alloy AL5380 H321. Here the authors extend the study using a number of further data sets from the literature for which data were available at different R ratios. These data include two aluminium alloys, Al 2024-T3 and Al 7075-T6, and a ductile cast iron, EN-GJS- 400-18-LT. Despite of necessary assumptions for the compensation of partially missing input information the results were fairly reasonable with the exception of one data set. The authors identify high applied stress levels in combination with potential multiple crack initiation as the probable root of the problem and propose a scheme how the model can be extended for taking into account crack initiation. KW - Fatigue strength KW - S–N curve KW - Fracture mechanics KW - Crack propagation KW - Short cracks PY - 2014 UR - http://ac.els-cdn.com/S0013794413003901/1-s2.0-S0013794413003901-main.pdf?_tid=1403b676-b8a0-11e3-9087-00000aab0f26&acdnat=1396248522_d8c91133aa860e68196d9325c22ce651 DO - https://doi.org/10.1016/j.engfracmech.2013.12.005 SN - 0013-7944 SN - 1873-7315 SP - 1 EP - 17 PB - Elsevier Science CY - Kidlington AN - OPUS4-30452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Ainsworth, R. A. A1 - Beier, H.T. A1 - Pisarski, H. A1 - Zhang, Z. L. A1 - Nikbin, K. A1 - Nitschke-Pagel, T. A1 - Münstermann, S. A1 - Kucharczyk, P. A1 - Klingbeil, Dietmar T1 - Review on fracture and crack propagation in weldments - A fracture mechanics perspective N2 - Welding is one of the most common methods in industrial practice for joining components. Its main advantages are high speed in manufacturing combined with low costs and, usually, a high degree of flexibility, integrity and reliability. Nevertheless, welding is a highly complex metallurgical process and, therefore, weldments are susceptible to material discontinuities, flaws and residual stresses which may lead to structural failure and life time reduction. As a consequence weldments are an important field of fracture mechanics methods although its application is more complex than for homogeneous or non-welded structures. The aim of the paper is to provide an overview on the current state of fracture mechanics application to weldments. It starts by discussing the specific features which any fracture mechanics analysis of weldments has to take into account. Then, the experimental determination of fracture toughness, fatigue crack propagation and tensile properties of weldments is addressed. Finally, the analytical determination of the crack driving force in components and structural integrity assessment approaches for weldments are presented. KW - Weldments KW - Fracture mechanics KW - Fracture toughness KW - Fatigue crack propagation KW - Residual stresses KW - Strength mismatch PY - 2014 DO - https://doi.org/10.1016/j.engfracmech.2014.05.012 SN - 0013-7944 SN - 1873-7315 VL - 132 SP - 200 EP - 276 PB - Elsevier Science CY - Kidlington AN - OPUS4-32819 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro ED - Yu, S. ED - Feng, X.-Q. T1 - Fracture mechanics model for predicting fracture strength of metallic alloys containing large second phase particles N2 - An analytical fracture mechanics model for predicting the finite life fatigue strength of components is presented which Combines a number of well established and newly developed approaches such as Murakami’s and McEvily's approach for describing the transient behaviour of crack closure of short cracks, the analytical (long) crack closure function of Newman, the R6 procedure modified by a method for improving the ligament yielding correction proposed by the authors and other elements. Basic assumption is the preexistence of initial flaws such that the crack initiation or nucleation stage is small and can be neglected. The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with artificial initial defects generated by FIB technology, the size of which was fixed on the basis of fractographic investigations on broken, smooth specimens. T2 - ICF13 - 13th International conference on fracture CY - Beijing, China DA - 16.06.2013 KW - Fatigue strength KW - S-N curve KW - Fracture mechanics KW - Crack propagation KW - Short cracks PY - 2013 SN - 978-988-12265-2-5 SP - 1 EP - 12 AN - OPUS4-29537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Hellmann, D. T1 - Fracture mechanics model for predicting fatigue strength of metallic alloys containing large second phase particles T2 - ECF 19 - 19th European conference on fracture - Fracture mechanics for durability, reliability and safety CY - Kazan, Russia DA - 2012-08-26 KW - Fatigue strength KW - S-N curve KW - Fracture mechanics KW - Crack propagation KW - Short cracks KW - Bruchmechanik KW - Schwingfestigkeit KW - Bauteilbewertung PY - 2012 SN - 978-5-905576-18-8 IS - Proceeding-ID 116 SP - 1 EP - 14 AN - OPUS4-27278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Beretta, S. T1 - Failure and damage tolerance aspects of railway components N2 - Railway structures such as rails and axles are safety relevant components since any failure includes the risk of catastrophic derailment. This paper gives a brief overview on the most important potential failure scenarios driven by fatigue crack initiation and propagation and discusses the effects of important influencing factors such as vehicle weight and speed, track quality and environmental conditions. The present paper summarizes earlier work of the authors in this field. KW - Railway rails KW - Railway axles KW - Fatigue crack propagation KW - Damage tolerance KW - Fracture mechanics PY - 2011 DO - https://doi.org/10.1016/j.engfailanal.2010.06.001 SN - 1350-6307 SN - 1873-1961 VL - 18 IS - 2 SP - 534 EP - 542 PB - Elsevier Science Publ. CY - Oxford AN - OPUS4-22639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -