TY - JOUR A1 - Zhu, Jiangchao A1 - Madia, Mauro A1 - Schurig, Michael A1 - Kruse, Julius A1 - Conrad, Fabian A1 - Schlums, Hartmut A1 - Kontermann, Christian A1 - Zerbst, Uwe T1 - On the use of representative specimens for the structural integrity assessment of safety-relevant rotating components N2 - Safety-relevant components, for which a failure in service could have catastrophic consequences, are usually designed for extremely low probability of failure and they are subjected to stringent part qualification procedures according to guidelines set by regulatory agencies. Manufacturers are often forced to perform tests on full scale or scaled components to ensure the structural integrity under defined loading conditions, which usually implies a huge experimental and financial effort. Therefore, companies try to develop new strategies such as digital twins, which allow to massively reduce costs, without compromising safety. This work presents a new quasi-static testing and assessment concept, the main idea of which is to replace, or at least reduce, the experimental testing on components by testing specimens representative of the component. Fracture mechanics specimens have been designed iteratively by numerical simulations to match the stress state at the crack-tip of the maximum permissible defect defined by regulatory agencies for the component. Potentially, the major benefit of the proposed approach is that the tests can be performed on conventional laboratory testing machines. The effectiveness of the methodology is demonstrated in case of the structural integrity assessment of a Ni-base superalloy aero-engine turbine disk at overspeed conditions. KW - Structural integrity KW - Turbine disk KW - Burst KW - Fracture mechanics KW - Representative specimens KW - Quasi-static testing PY - 2025 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-624208 DO - https://doi.org/10.1016/j.engfracmech.2024.110710 SN - 0013-7944 VL - 314 SP - 1 EP - 23 PB - Elsevier Ltd. AN - OPUS4-62420 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Ainsworth, R. A. A1 - Beier, H.T. A1 - Pisarski, H. A1 - Zhang, Z. L. A1 - Nikbin, K. A1 - Nitschke-Pagel, T. A1 - Münstermann, S. A1 - Kucharczyk, P. A1 - Klingbeil, Dietmar T1 - Review on fracture and crack propagation in weldments - A fracture mechanics perspective N2 - Welding is one of the most common methods in industrial practice for joining components. Its main advantages are high speed in manufacturing combined with low costs and, usually, a high degree of flexibility, integrity and reliability. Nevertheless, welding is a highly complex metallurgical process and, therefore, weldments are susceptible to material discontinuities, flaws and residual stresses which may lead to structural failure and life time reduction. As a consequence weldments are an important field of fracture mechanics methods although its application is more complex than for homogeneous or non-welded structures. The aim of the paper is to provide an overview on the current state of fracture mechanics application to weldments. It starts by discussing the specific features which any fracture mechanics analysis of weldments has to take into account. Then, the experimental determination of fracture toughness, fatigue crack propagation and tensile properties of weldments is addressed. Finally, the analytical determination of the crack driving force in components and structural integrity assessment approaches for weldments are presented. KW - Weldments KW - Fracture mechanics KW - Fracture toughness KW - Fatigue crack propagation KW - Residual stresses KW - Strength mismatch PY - 2014 DO - https://doi.org/10.1016/j.engfracmech.2014.05.012 SN - 0013-7944 SN - 1873-7315 VL - 132 SP - 200 EP - 276 PB - Elsevier Science CY - Kidlington AN - OPUS4-32819 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Beretta, S. T1 - Failure and damage tolerance aspects of railway components N2 - Railway structures such as rails and axles are safety relevant components since any failure includes the risk of catastrophic derailment. This paper gives a brief overview on the most important potential failure scenarios driven by fatigue crack initiation and propagation and discusses the effects of important influencing factors such as vehicle weight and speed, track quality and environmental conditions. The present paper summarizes earlier work of the authors in this field. KW - Railway rails KW - Railway axles KW - Fatigue crack propagation KW - Damage tolerance KW - Fracture mechanics PY - 2011 DO - https://doi.org/10.1016/j.engfailanal.2010.06.001 SN - 1350-6307 SN - 1873-1961 VL - 18 IS - 2 SP - 534 EP - 542 PB - Elsevier Science Publ. CY - Oxford AN - OPUS4-22639 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schork, B. A1 - Zerbst, Uwe A1 - Kiyak, Yusuf A1 - Kaffenberger, M. A1 - Madia, Mauro A1 - Oechsner, M. T1 - Effect of the parameters of weld toe geometry on the FAT class as obtained by means of fracture mechanics-based simulations N2 - The fracture mechanics-based IBESS approach is applied to the determination of FAT classes of butt welds with crack Initiation along the weld toe. The aim is an investigation of the effect of the geometrical parameters toe radius, flank angle, reinforcement and secondary notches such as roughness or undercuts. The influence of these parameters is discussed both individually and in combination; however, excluding statistical distributions of them and the material data. The results, when compared with conventional FAT classes for butt welds, are encouraging with respect to a potential contribution of IBESS to the discussion of more advanced quality criteria for welds. To that purpose, demands for further research are proposed. KW - Fracture mechanics KW - Weld toe geometry KW - Fatigue crack initiation KW - FAT class approach PY - 2020 DO - https://doi.org/10.1007/s40194-020-00874-7 IS - 64 SP - 925 EP - 936 PB - Springer AN - OPUS4-53079 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Vormwald, M. T1 - Applying fracture mechanics to fatigue strength determination - some basic considerations N2 - A discussion is provided on demands that must be met in order to apply fracture mechanics to the determination of overall fatigue lifetime and strength, i.e., S-N curves and fatigue limits. These comprise the determination of the cyclic crack driving force for all stages of fatigue crack propagation, in particular for the short crack stage where the crack driving force has to be determined for elastic-plastic deformation and the gradual build-up of the crack closure phenomenon. Special emphasis is put on a fatigue damage relevant specification of the initial crack size. Different approaches in the literature are discussed. Another important aspect is the adequate treatment of multiple crack propagation. Finally, the discussion is illustrated by an example of a butt weld made of a medium strength steel. KW - Multiple cracks KW - Fatigue strength KW - Fracture mechanics KW - Fatigue crack propagation KW - Initial crack size PY - 2019 DO - https://doi.org/10.1016/j.ijfatigue.2019.05.009 SN - 0142-1123 VL - 126 SP - 188 EP - 201 PB - Elsevier Ltd. AN - OPUS4-48091 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zhu, Jiangchao A1 - Madia, Mauro A1 - Schurig, Michael A1 - Fedelich, Bernard A1 - Schlums, Hartmut A1 - Zerbst, Uwe T1 - Burst speed assessment of aero-engine turbine disk based on failure assessment diagram and global stability criterion N2 - Aero-engine turbine disks are safety-relevant components which are operated under high thermal and mechanical stress conditions. The actual part qualification and certification procedures make use of spin-tests conducted on production-similar disks. While these tests provide, on the one hand, a reliable definition of the critical conditions for real components, on the other hand they represent a relevant cost item for engine manufacturers. The aim of this work is to present two alternative burst speed assessment methods under development based on the Failure Assessment Diagram (FAD) and a global stability criterion, respectively. In the scope of the fracture mechanics assessment, the failure modes hoop-burst and rim-peeling are investigated with semicircular surface cracks modelled at the critical regions on the turbine disk. The comparison of the predicted critical rotational speed shows good agreement between the assessment methods. KW - Global stability criterion KW - Fracture mechanics KW - Burst KW - Turbine disk PY - 2023 DO - https://doi.org/10.1016/j.engfracmech.2022.109005 SN - 0013-7944 VL - 277 SP - 1 EP - 15 PB - Elsevier Ltd. AN - OPUS4-56736 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -