TY - JOUR A1 - Zerbst, Uwe A1 - Beretta, S. A1 - Köhler, G. A1 - Lawton, A. A1 - Vormwald, M. A1 - Beier, H.T. A1 - Klinger, Christian A1 - Cerný, I. A1 - Rudlin, J. A1 - Heckel, Thomas A1 - Klingbeil, Dietmar T1 - Safe life and damage tolerance aspects of railway axles - A review JF - Engineering fracture mechanics N2 - The paper gives an overview on safe life and damage tolerance methods applied to railway axles. It describes failure scenarios due to fatigue crack initiation and propagation. Besides common aspects of design, specific features such as corrosion and impact damage from flying ballast are discussed which may reduce the fatigue strength of axles during service. Potential effects of non-metallic inclusions from the steel manufacturing process are addressed in the context of the very high number of loading cycles railway axles are designed for. With respect to damage tolerance general lines of fracture mechanics residual lifetime analyses are introduced. More specific discussion is provided on aspects such as the threshold value of fatigue crack propagation and reliability aspects of non-destructive inspection. KW - Railway axle KW - Safe life design KW - Damage tolerance KW - Fatigue strength KW - Fatigue crack propagation KW - Inspection intervals PY - 2013 DO - https://doi.org/10.1016/j.engfracmech.2012.09.029 SN - 0013-7944 SN - 1873-7315 VL - 98 SP - 214 EP - 271 PB - Elsevier Science CY - Kidlington AN - OPUS4-27779 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro ED - Yu, S. ED - Feng, X.-Q. T1 - Fracture mechanics model for predicting fracture strength of metallic alloys containing large second phase particles T2 - ICF13 - 13th International conference on fracture (Proceedings) N2 - An analytical fracture mechanics model for predicting the finite life fatigue strength of components is presented which Combines a number of well established and newly developed approaches such as Murakami’s and McEvily's approach for describing the transient behaviour of crack closure of short cracks, the analytical (long) crack closure function of Newman, the R6 procedure modified by a method for improving the ligament yielding correction proposed by the authors and other elements. Basic assumption is the preexistence of initial flaws such that the crack initiation or nucleation stage is small and can be neglected. The application of the model is demonstrated for small tension plates of aluminium Al 5380 H321 with artificial initial defects generated by FIB technology, the size of which was fixed on the basis of fractographic investigations on broken, smooth specimens. T2 - ICF13 - 13th International conference on fracture CY - Beijing, China DA - 16.06.2013 KW - Fatigue strength KW - S-N curve KW - Fracture mechanics KW - Crack propagation KW - Short cracks PY - 2013 SN - 978-988-12265-2-5 SP - 1 EP - 12 AN - OPUS4-29537 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Hellmann, D. T1 - Fracture mechanics model for predicting fatigue strength of metallic alloys containing large second phase particles T2 - ECF 19 - 19th European conference on fracture - Fracture mechanics for durability, reliability and safety T2 - ECF 19 - 19th European conference on fracture - Fracture mechanics for durability, reliability and safety CY - Kazan, Russia DA - 2012-08-26 KW - Fatigue strength KW - S-N curve KW - Fracture mechanics KW - Crack propagation KW - Short cracks KW - Bruchmechanik KW - Schwingfestigkeit KW - Bauteilbewertung PY - 2012 SN - 978-5-905576-18-8 IS - Proceeding-ID 116 SP - 1 EP - 14 AN - OPUS4-27278 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Zerbst, Uwe A1 - Madia, Mauro ED - Yadroitsev, I. ED - Yadroitsava, I. ED - Du Plessies, A. ED - McDonald, E. T1 - Structural integrity II: fatigue properties T2 - Fundamentals of laser powder bed fusion of metals N2 - If a component is cyclically loaded, its load carrying capacity is considerably lower than in the monotonic loading case. This general observation applies in particular to L-PBF parts. The causes of this are mainly material defects such as pores and unwelded regions (Chapter 8) and a pronounced surface roughness in the as-built condition (Chapter 9). In addition, effects due to the anisotropy of the microstructure (Chapter 6) and a complex residual stress pattern (Chapter 7) play an important role. A consequence is that common strategies of fatigue assessment cannot be transferred to L-PBF applications without modifications. Due to the inhomogeneity of the material, the determination of representative material properties and the transfer to the component is a problem, and this is also the case with regard to the consideration of defects, surface roughness and residual stresses. The chapter gives a brief introduction to these problem areas. KW - Fatigue crack propagation stagesdefects KW - Fatigue strength KW - Fatigue life KW - Fracture mechanics PY - 2021 SN - 978-0-12-824090-8 DO - https://doi.org/10.1016/B978-0-12-824090-8.00015-9 SP - 377 EP - 394 PB - Elsevier Inc. CY - Amsterdam ET - 1 AN - OPUS4-52854 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe ED - Baumgartner, J. ED - Melz, T. T1 - Assessment of welded joints by fracture mechanics IBESS - the development of a procedure T2 - SoSDiD - 4th Symposium on structural durability in Darmstadt (Proceedings) N2 - The idea to determine the fatigue strength of weldments by means fracture mechanics was originally based on the empirical observation that the major portion of the fatigue life in weldments is frequently spent in crack propagation. The present paper gives a brief overview on the basic principles of fracture mechanics-based determination of fatigue strength and on special features which have to be considered for weldments. Based on this information, the ongoing research project IBESS is introduced and briefly reviewed. T2 - SoSDiD - 4th Symposium on structural durability in Darmstadt CY - Darmstadt, Germany DA - 2014-05-14 KW - Fracture mechanics KW - Fatigue strength KW - (Residual) lifetime KW - Weldments PY - 2014 SP - 49 EP - 66 PB - Fraunhofer Verlag AN - OPUS4-31321 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Beier, H.T. T1 - A model for fracture mechanics based prediction of the fatigue strength: Further validation and limitations JF - Engineering fracture mechanics N2 - Recently two of the authors of the present paper proposed a model for a fracture mechanics based prediction of the S–N characteristics of metallic components with large microstructural defects and supported this by a validation exercise on tensile plates made of an aluminium alloy AL5380 H321. Here the authors extend the study using a number of further data sets from the literature for which data were available at different R ratios. These data include two aluminium alloys, Al 2024-T3 and Al 7075-T6, and a ductile cast iron, EN-GJS- 400-18-LT. Despite of necessary assumptions for the compensation of partially missing input information the results were fairly reasonable with the exception of one data set. The authors identify high applied stress levels in combination with potential multiple crack initiation as the probable root of the problem and propose a scheme how the model can be extended for taking into account crack initiation. KW - Fatigue strength KW - S–N curve KW - Fracture mechanics KW - Crack propagation KW - Short cracks PY - 2014 UR - http://ac.els-cdn.com/S0013794413003901/1-s2.0-S0013794413003901-main.pdf?_tid=1403b676-b8a0-11e3-9087-00000aab0f26&acdnat=1396248522_d8c91133aa860e68196d9325c22ce651 DO - https://doi.org/10.1016/j.engfracmech.2013.12.005 SN - 0013-7944 SN - 1873-7315 SP - 1 EP - 17 PB - Elsevier Science CY - Kidlington AN - OPUS4-30452 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro T1 - Fracture mechanics based assessment of the fatigue strength: approach for the determination of the initial crack size JF - Fatigue & fracture of engineering materials & structures N2 - In a number of previous papers, the authors have proposed a model for fracture mechanics based prediction of the S-N characteristics of metallic components with large microstructural defects. Here, an extension to materials that do not show large defects onto the fracture surfaces is provided. In such cases, an approach based on a so-called cyclic R-curve analysis is proposed for the determination of the initial flaw size, which has to be used in the calculation of fatigue crack propagation. The principle is explained and demonstrated by a first application to a welded joint. KW - Fatigue strength KW - Weldments KW - Short cracks KW - Initial flaw size KW - Cyclic R-curve PY - 2015 DO - https://doi.org/10.1111/ffe.12288 SN - 1460-2695 SN - 0160-4112 SN - 8756-758X VL - 38 IS - 9 SP - 1066 EP - 1075 PB - Blackwell CY - Oxford AN - OPUS4-33838 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Madia, Mauro A1 - Beier, H. Th. T1 - Fatigue strength and life determination of weldments based on fracture mechanics JF - 3rd international Symposium on fatigue design and material defects (FDMD 2017) N2 - The paper provides an overview on the results of a German cluster project on the use of fracture mechanics to the determination of the fatigue strength of weldments with fatigue cracks originating at the weld toes. The approach includes (a) a concept for short crack propagation for which the common ΔK concept is not applicable and the crack closure effects are still being gradually build-up, (b) a method for determining fatigue life relevant initial crack sizes as they are needed in any fracture mechanics analysis and (c) multiple cracking and crack coalescence at load levels higher than the endurance limit. The analyses are stochastically performed. Both, the endurance limit and the finite life branch of the S-N curve are determined. Besides a brief introduction into the approach, validation examples are presented. These comprise different weldment types (butt welds, cross joints and longitudinal stiffened plates), two steels (S355NL and S960QL) of quite different strengths, different weld geometries due to different welding techniques (WIG, MAG), as-welded and stress relieved welds and different stress ratios varying from R = -1 to R = 0.5. T2 - FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Weldments KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-438500 DO - https://doi.org/10.1016/j.prostr.2017.11.106 SN - 2452-3216 VL - 7 SP - 407 EP - 414 PB - ScienceDirect CY - Lecco, Italy AN - OPUS4-43850 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Zerbst, Uwe A1 - Hilgenberg, Kai T1 - Damage development and damage tolerance of structures manufactured by selective laser melting - a review JF - 3rd International symposium on fatigue design and material defects (FDMD 2017) N2 - The additive manufacturing technology of Selective Laser Melting (SLM) experiences a rapid development within an increasing marked of quite different application fields. The properties of SLM materials and structures are influenced by a number of tech-nological parameters such as the metal powder (particle size, homogeneity, cleanliness), the laser tool (power, beam diameter, pulse lengths), the scanning operation (speed, sequence and orientation of melting paths), parameters of the over-all equipment (design and preheating of the base plate, currents and turbulence in the protective gas atmosphere) and, last not least, the hatching strategy including the build-up direction of the structure with respect to the loading direction of the component. For the perspective use of SLM structures as load carrying, safety-relevant components the knowledge of their mechanical properties is necessary. It is essential to understand these in the context of the manufacturing-related features and at the back-ground of the basic characteristics of metallic materials: crystal lattice, microstructure and material defects. The paper provides an overview on factors which affect the mechanical parameters stiffness, strength, ductility, toughness, fatigue crack propagation and fatigue strength in the context of selective laser melting. T2 - FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-438511 DO - https://doi.org/10.1016/j.prostr.2017.11.071 SN - 2452-3216 VL - 7 SP - 141 EP - 148 PB - ScienceDirect CY - Lecco, Italy AN - OPUS4-43851 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zerbst, Uwe A1 - Hilgenberg, Kai T1 - Damage development and damage tolerance of structures manufactured by selective laser melting N2 - The additive manufacturing technology of Selective Laser Melting (SLM) experiences a rapid development within an increasing marked of quite different application fields. The properties of SLM materials and structures are influenced by a number of tech-nological parameters such as the metal powder (particle size, homogeneity, cleanliness), the laser tool (power, beam diameter, pulse lengths), the scanning operation (speed, sequence and orientation of melting paths), parameters of the over-all equipment (design and preheating of the base plate, currents and turbulence in the protective gas atmosphere) and, last not least, the hatching strategy including the build-up direction of the structure with respect to the loading direction of the component. For the perspective use of SLM structures as load carrying, safety-relevant components the knowledge of their mechanical properties is necessary. It is essential to understand these in the context of the manufacturing-related features and at the back-ground of the basic characteristics of metallic materials: crystal lattice, microstructure and material defects. The paper provides an overview on factors which affect the mechanical parameters stiffness, strength, ductility, toughness, fatigue crack propagation and fatigue strength in the context of selective laser melting. T2 - 3rd International Symposium on Fatigue Design an Material Defects, FDMD 2017 CY - Lecco, Italy DA - 19.09.2017 KW - Fatigue strength KW - Fracture mechanics KW - Initial crack size KW - Short crack propagation KW - Multiple crack propagation PY - 2017 AN - OPUS4-43853 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -