TY - CONF A1 - Zencker, Uwe T1 - Fracture Mechanics Analysis of Spent Fuel Claddings during Long-Term Dry Interim Storage N2 - The European Joint Programme on Radioactive Waste Management (EURAD) is working on Spent Fuel Characterization (SFC) in its work package (WP) 8. Inspired by the EURAD activities, the International Atomic Energy Agency (IAEA) established an international Coordinated Research Project (CRP) on SFC. The EURAD WP SFC participants are collaborating as a team on the IAEA CRP on SFC. The EURAD WP SFC project consists of four tasks. Task 3 investigates the behaviour of nuclear fuel and cladding after discharge. The aim of these activities is to understand and describe the evolution of the cladding-pellet system and its ageing under conditions of extended interim storage, transportation and emplacement in a final disposal system. At the Third Research Coordination Meeting on Spent Fuel Characterization, BAM as contributor to Task 3 reported on the activities and status of its research work. T2 - IAEA 3rd Research Coordination Meeting of the Coordinated Research Project on Spent Fuel Characterization CY - Cockermouth, UK DA - 01.07.2024 KW - Nuclear fuel KW - Cladding KW - Discharge PY - 2024 AN - OPUS4-60668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Gaddampally, Mohan Reddy A1 - Völzke, Holger T1 - Failure Analysis on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. The cladding is the first barrier for the spent fuel pellets. An established method for characterising the cladding material is the ring compression test (RCT), in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. Radial hydrides may precipitate in zirconium-based alloys (Zircaloy) under pre-storage drying and during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. The focus of the presented research is on the development of appropriate nu-merical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. A modelling approach based on cohesive zones is ex-plained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zir-conium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hy-drides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. Based on the developed fracture mechanics approach, not only the deformation behaviour but also the fail-ure behaviour of irradiated as well as unirradiated Zircaloy claddings with radial hydrides under RCT loading conditions can be adequately described. T2 - 27th International Conference on Structural Mechanics in Reactor Technology - SMiRT 27 CY - Yokohama, Japan DA - 03.03.2024 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 SP - 1 EP - 8 AN - OPUS4-60671 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Failure Analysis on Irradiated Claddings Subjected to Long-Term Dry Interim Storage N2 - Long-term dry interim storage may adversely affect the mechanical properties of spent fuel rods, possibly resulting in a reduced resilience during handling or transport after storage. The cladding is the first barrier for the spent fuel pellets. An established method for characterising the cladding material is the ring compression test (RCT), in which a small, cylindrical sample of the cladding tube is subjected to a compressive load. Radial hydrides may precipitate in zirconium-based alloys (Zircaloy) under pre-storage drying and during slow cooling, which result in embrittlement of the cladding material and eventually a possible sudden failure of cladding integrity under additional mechanical loads. The focus of the presented research is on the development of appropriate nu-merical methods for predicting the mechanical behaviour and identification of limiting conditions to prevent brittle fracture of Zircaloy claddings. A modelling approach based on cohesive zones is ex-plained which is able to reproduce the propagation of cracks initiated at radial hydrides in the zir-conium matrix. The developed methods are applied to defueled samples of cladding alloy ZIRLO®, which were subjected to a thermo-mechanical treatment to reorient existing circumferential hy-drides to radial hydrides. A selected sample showing sudden load drops during a quasi-static ring compression test is analysed by means of fracture mechanics for illustrative purposes. Based on the developed fracture mechanics approach, not only the deformation behaviour but also the fail-ure behaviour of irradiated as well as unirradiated Zircaloy claddings with radial hydrides under RCT loading conditions can be adequately described. T2 - 27th International Conference on Structural Mechanics in Reactor Technology - SMiRT 27 CY - Yokohama, Japan DA - 03.03.2024 KW - Cladding Embrittlement KW - Cohesive Zone Modelling KW - Ring Compression Test KW - Spent Nuclear Fuel PY - 2024 AN - OPUS4-60672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Weber, Mike A1 - Ballheimer, Viktor A1 - Wille, Frank A1 - Zencker, Uwe T1 - Numerical approach to determine the correct puncture bar length for the IAEA puncture bar drop test N2 - Among other mechanical tests the 1 meter drop onto a steel puncture bar shall be considered for accident safe packages for the transport of radioactive material. According with the IAEA regulations “the bar shall be of solid mild steel of circular section, 15.0 ± 0.5 cm in diameter and 20 cm long, unless a longer bar would cause greater damage…”. The most damaging puncture bar length can be estimated by iterative processes in numerical simulations. On the one hand, a sufficient puncture bar length has to guarantee that shock absorbers or other attachments do not prevent or reduce the local load application to the package, on the other hand, a longer and thus less stiff bar causes a smaller maximum contact force. The contrary influence of increasing puncture bar length and increasing effective drop height shall be taken into account if a shock absorber is directly placed in the target area. The paper presents a numerical approach to identify the bar length that causes maximum damage to the package. Using the example of two typical package masses the sensitivity of contact forces and puncture bar deformations to the initial length are calculated and assessed with regard to the international IAEA package safety requirements. T2 - ASME Pressure Vessels and Piping Conference 2018 CY - Prague, Czech Republic DA - 15.07.2018 KW - Length of puncture bar KW - Mechanical assessment KW - Numerical simulation KW - Puncture bar test KW - Transport of radioactive materials PY - 2018 SP - PVP2018-84614, 1 EP - 7 AN - OPUS4-46538 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Orellana Pérez, Teresa A1 - Völzke, Holger A1 - Wolff, Dietmar A1 - Zencker, Uwe T1 - Relevance of cladding failure mechanisms due to zirconium hydride precipitation under extended dry storage conditions in Germany N2 - The German nuclear waste management strategy consists of dry interim storage of spent fuel inside dual purpose casks and its subsequent direct final disposal in a deep geological repository. Interim storage is limited to 40 years so far, but will have to be extended until repository site selection and operation is concluded, potentially up to 100 years. In this context, research on the long term performance of safety relevant cask components and fuel rod integrity during such extended periods of time is of outmost importance. The barrier function of the fuel cladding depends on its integrity under operational and accidental conditions along with storage and subsequent transportation and is mainly affected over time by altering of the cladding microstructure and by thermo-mechanical conditions during reactor operation and subsequent wet and dry storage. This paper focuses on failure mechanisms regarding cladding embrittlement caused by physical phenomena concerning hydrogen dissolution and precipitation of hydrides in the zirconium matrix. Within this context, potential cladding integrity issues under extended interim storage conditions followed by transportation are emphasized. Delayed hydride cracking (DHC) is a well-known time-dependent temperature-activated phenomenon failure mechanism of the fuel cladding during reactor operation. The phenomenon consists of hydrogen diffusion and hydride precipitation at the tip of an initial crack and the propagation of the crack to an approximate distance equal to the length of the hydride. This failure mechanism is temperature-activated phenomenon and enhances along with thermal cycling of the fuel cladding, e. g. during reactor shutdowns. DHC shows limited relevance under quasi static storage conditions with continuously lowering temperatures. However, the literature points that DHC may occur when the temperature during storage decreases to a certain level after some decades and in combination with stress concentrations in the cladding material. When spent fuel is transferred to dry storage by vacuum drying, the cladding temperature raises up to peak temperatures of ~370°C. Under these conditions, hydrides dissolute into the zirconium matrix up to the solubility limit defined by the peak temperature and this amount of hydrogen can precipitate in a radial re-oriented fashion due to the temperature decrease during storage. Cladding materials with radially precipitated hydrides show significant embrittlement. Radially oriented hydrides are perpendicularly oriented to hoop stresses representing the most critical configuration. Brittle failure of the cladding then occurs by crack propagation through radially oriented hydrides and finally through the zirconium matrix. The susceptibility to radial hydride precipitation depends on cladding material type and microstructure, hydrogen content, pre-drying hydride distribution, irradiation conditions, and temperature and stress histories during drying and storage operations. This paper addresses major considerations concerning spent fuel cladding embrittlement due to hydride precipitation with regard to the boundary conditions of dry spent fuel storage in Germany. Analytical, numerical, and experimental approaches are to be discussed by BAM in order to identify the specific needs for future R&D work in that area with the purpose to provide the necessary data base for proper safety demonstration and evaluation along with future extended storage licensing procedures. T2 - 2017 Water Reactor Fuel Performance Meeting CY - Jeju, Korea DA - 10.09.2017 KW - Cladding KW - Hydride precipitation KW - Spent fuel PY - 2017 SP - 1 EP - 8 AN - OPUS4-44749 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe A1 - Qiao, Linan A1 - Völzke, Holger T1 - Influence of impact angle and real target properties on drop test results of cubic containers N2 - Drop test scenarios with cubic containers without impact limiters at interim storage sites or in a final repository have been investigated by numerical simulations. An ideally flat drop is impossible to conduct as a free fall of a container even under laboratory conditions. Dynamic stresses and strains inside the container structure are sensitive to the impact angle. Even very small impact angles cause remarkable changes in the experimental or numerical results when a flat bottom or wall of a container hits a flat target. For drop tests with transport packages the International Atomic Energy Agency (IAEA) regulations define an essentially unyielding target. In contrast, potential accident scenarios for storage containers are derived from site-specific safety analyses or acceptance criteria in Germany. Each interim storage site or repository has a yielding or so-called real target with individual structural and material properties. The real target acts as a kind of impact limiter. A more conservative container design is required if the impact limiting effect of the target is not considered. T2 - ASME 2017 Pressure Vessels and Piping Conference CY - Waikoloa, Hawaii, USA DA - 16.07.2017 KW - Finite element method KW - Simulation KW - Drop test KW - Impact angle KW - Real target KW - Yielding target PY - 2017 SN - 978-0-7918-5802-8 DO - https://doi.org/10.1115/PVP2017-65731 VL - 7 SP - Article UNSP V007T07A039, 1 EP - 9 AN - OPUS4-43631 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Influence of impact angle and real target properties on drop test results of cubic containers N2 - Drop test scenarios with cubic containers without impact limiters at interim storage sites or in a final repository have been investigated by numerical simulations. An ideally flat drop is impossible to conduct as a free fall of a container even under laboratory conditions. Dynamic stresses and strains inside the container structure are sensitive to the impact angle. Even very small impact angles cause remarkable changes in the experimental or numerical results when a flat bottom or wall of a container hits a flat target. For drop tests with transport packages the International Atomic Energy Agency (IAEA) regulations define an essentially unyielding target. In contrast, potential accident scenarios for storage containers are derived from site-specific safety analyses or acceptance criteria in Germany. Each interim storage site or repository has a yielding or so-called real target with individual structural and material properties. The real target acts as a kind of impact limiter. A more conservative container design is required if the impact limiting effect of the target is not considered. T2 - ASME 2017 Pressure Vessels and Piping Conference CY - Waikoloa, Hawaii, USA DA - 16.07.2017 KW - Finite element method KW - Simulation KW - Drop test KW - Impact angle KW - Real target KW - Yielding target PY - 2017 AN - OPUS4-43632 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Simbruner, Kai A1 - Billone, Michael C. A1 - Zencker, Uwe A1 - Liu, Yung Y. A1 - Völzke, Holger T1 - Brittle failure analysis and modeling of high-burnup PWR fuel cladding alloys N2 - The aim of this research is the development of methods for predicting mechanical behavior and identification of limiting conditions to prevent brittle failure of high-burnup (HBU) pressure water reactor (PWR) fuel cladding alloys. A finite element (FE) model of the ring compression test (RCT) was created to analyze the failure behavior of zirconium-based alloys with radial hydrides during the RCT. An elastic-plastic material model describes the zirconium alloy. The stress-strain curve needed for the elastic-plastic material model was derived by inverse finite element analyses. Cohesive zone modeling is used to reproduce sudden load drops during RCT loading. Based on the failure mechanism in non-irradiated ZIRLO® claddings, a micro-mechanical model was developed that distinguishes between brittle failure along hydrides and ductile failure of the zirconium matrix. Two different cohesive laws representing these types of failure are present in the same cohesive interface. The key differences between these constitutive laws are the cohesive strength, the stress at which damage initiates, and the cohesive energy, which is the damage energy dissipated by the cohesive zone. Statistically generated matrix-hydride distributions were mapped onto the cohesive elements and simulations with focus on the first load drop were performed. Computational results are in good agreement with the RCT results conducted on high-burnup M5® samples. It could be shown that crack initiation and propagation strongly depend on the specific configuration of hydrides and matrix material in the fracture area. KW - Cladding KW - Radial hydrides KW - Ring compression test KW - Cohesive zone model PY - 2024 DO - https://doi.org/10.1515/kern-2024-0109 SN - 2195-8580 SP - 1 EP - 9 PB - Walter de Gruyter GmbH AN - OPUS4-62409 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Structural and Thermal Analyses of Storage Casks T2 - Workshop on Aging Management Issues Related to Long-Term Dry Spent Nuclear Fuel (SNF) Storage CY - Argonne, USA DA - 2014-10-15 PY - 2014 AN - OPUS4-31873 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Numerical Analyses of Crack-like Defects under Impact Loads T2 - Workshop on Aging Management Issues Related to Long-Term Dry Spent Nuclear Fuel (SNF) Storage CY - Argonne USA DA - 2014-10-15 PY - 2014 AN - OPUS4-31875 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Behälterspezifische Sicherheitsbewertung für auslegungsbestimmende Handhabungsstörfälle T2 - 4. RAM-Behältersicherheitstage 2014, BAM CY - Berlin, Germany DA - 2014-03-26 PY - 2014 AN - OPUS4-30711 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Qiao, Linan A1 - Zencker, Uwe A1 - Kasparek, Eva Maria A1 - Völzke, Holger ED - Topping, B.H.V. ED - Iványi, P. T1 - Simulation of damping concrete under severe impact loads using a crushable foam model with damage mechanisms N2 - The deformation and damage behaviour of damping concrete under impact loading conditions is investigated experimentally and numerically. The material model is based on the assumption of crushable foam with volumetric or isotropic hardening combined with ductile and shear damage criteria. Model parameters are determined in static and dynamic compression tests of confined cubic specimens. The derived material model is validated by numerical simulation of penetration tests. The static and dynamic penetration of indenters into uniform as well as assembled bricks made of damping concrete is discussed. Finally, the successful calculation of a large-scale drop test with a heavy cask-like test object onto a realistic damping concrete foundation is demonstrated. T2 - 12th International conference on computational structures technology CY - Naples, Italy DA - 02.09.2014 KW - Damping concrete KW - Impact load KW - Crushable foam material model KW - Damage PY - 2014 SN - 978-1-905088-61-4 DO - https://doi.org/10.4203/ccp.106.233 SN - 1759-3433 SP - Paper 233, 1 EP - 16 PB - Civil Comp Press AN - OPUS4-31480 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Protz, Christian A1 - Zencker, Uwe A1 - Liebich, R. ED - Onate, E. ED - Oliver, J. ED - Huerta, A. T1 - Drop tests and dynamic finite element analyses of steel sheet containers for final disposal of radioactive waste N2 - Within a safety assessment, Containers for radioactive waste have to withstand drop tests at defined conditions. Alternatively to prototype drop tests, numerical methods can be applied, if they are suitable and sufficiently verified. This paper describes the development of a finite element (FE) model of a thin-walled Steel sheet Container used to investigate dynamic load scenarios due to impact events. Experimental and numerical analyses were performed for different drop Orientations. The results are compared to prove the suitability of the FE model. T2 - WCCM XI - 11th World congress on computational mechanics CY - Barcelona, Spain DA - 20.07.2014 KW - Explicit dynamic FEM KW - Impact KW - Drop test KW - Steel sheet container PY - 2014 SP - 1 EP - 12 AN - OPUS4-31137 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Zencker, Uwe T1 - Reliability of Cask Designs under Mechanical Loads in Storage Facilities T2 - 12th International Probabilistic Safety Assessment and Management Conference (PSAM12) CY - Honolulu, HI, USA DA - 2014-06-22 PY - 2014 AN - OPUS4-31108 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -