TY - JOUR A1 - Braun, Ulrike A1 - Lorenz, Edelgard A1 - Weimann, Christiane A1 - Sturm, Heinz A1 - Karimov, I. A1 - Ettl, J. A1 - Meier, R. A1 - Wohlgemuth, W. A. A1 - Berger, H. A1 - Wildgruber, M. T1 - Mechanic and surface properties of central-venous port catheters after removal: A comparison of polyurethane and Silicon rubber materials N2 - Central venous port devices made of two different polymeric materials, thermoplastic polyurethane (TPU)and silicone rubber (SiR), were compared due their material properties. Both naïve catheters as well as catheters after removal from patients were investigated. In lab experiments the influence of various chemo-therapeutic solutions on material properties was investigated, where as the samples after removal were compared according to the implanted time inpatient. The macroscopic,mechanical performance was assessed with dynamic, specially adapted tests for elasticity. The degradation status of the materials was determined with common tools of polymer characterisation, such as infrared spectroscopy, molecular weight measurements and various methods of thermal analysis. The surface morphology was an alysed using scanning electron microscopy. A correlation between material properties and clinical performance was proposed. The surface morphology and chemical composition of the polyurethane catheter materials can potentially result in increased susceptibility of the catheter to bloodstream infections and thrombotic complications. The higher mechanic failure,especially with increasing implantation time of the silicone catheters is related to the lower mechanical performance compared to the polyurethane material as well as loss of barium sulphate filler particles near the surface of the catheter. This results in preformed microscopic notches, which act as predetermined sites of fracture. KW - Thermoplastic polyurethane (TPU) KW - Silicone rubber (SiR) KW - Catheters KW - Central venous access port KW - Complication KW - Structure propertyrelationship KW - Mechanical testing PY - 2016 DO - https://doi.org/10.1016/j.jmbbm.2016.08.002 SN - 1751-6161 SN - 1878-0180 VL - 64 SP - 281 EP - 291 PB - Elsevier Ltd. AN - OPUS4-37178 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Naumann, Annette A1 - Seefeldt, Henrik A1 - Stephan, Ina A1 - Braun, Ulrike A1 - Noll, Matthias T1 - Material resistance of flame retarded wood-plastic composites against fire and fungal decay N2 - Flame retarded wood-plastic composites (WPCs) should allow safe application in areas of fire risk. Halogen-free flame retardants can contain high amounts of nitrogen, phosphorus or sulphur, which may serve as nutrition source for wood degrading fungi and accelerate wood decay. Therefore, the material resistance of WPCs with each of four flame retardants against both fire or fungal decay was examined in comparison to WPC without flame retardant. Expandable graphite showed the best performance against fire in cone calorimetry and radiant panel testing. Two ammonium polyphosphates and a third nitrogen-containing flame retardant were not as effective. Contrary to the possibility that flame retardants might enhance fungal decay of WPC, the opposite effect occurred in case of the wood-degrading fungi Trametes versicolor and Coniophora puteana according to determination of mass loss and decrease of bending modulus of elasticity. Only the surface mould Alternaria alternata slightly increased the degradation of WPCs with nitrogen-containing flame retardants compared to WPC without flame retardant according to mass loss data and FTIR-ATR analyses. Finally, WPC including expandable graphite as flame retardant was effective against both fire and fungal decay. KW - Wood-plastic composite (WPC) KW - Flame retardants KW - Fire behaviour KW - Fungal decay KW - Fourier transform infrared - attenuated total reflexion (FTIR-ATR) spectroscopy KW - Microscopy PY - 2012 DO - https://doi.org/10.1016/j.polymdegradstab.2012.03.031 SN - 0141-3910 SN - 1873-2321 VL - 97 IS - 7 SP - 1189 EP - 1196 PB - Applied Science Publ. CY - London AN - OPUS4-26058 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Kunststoffe in der Umwelt: Elastomere, Thermoplaste und Duroplaste – worüber sprechen wir eigentlich und was sind die analytischen Herausforderungen? N2 - Übersichtsvortrag zur Thematik Kunststoffe in der Umwelt. Es werden Aspekte zu Definitionen, Eigenschaften und Analytischen Möglichkeiten und Herrausforderungen angesprochen. T2 - Arbeitsgespräch der Ressortforschungseinrichtungen CY - Berlin, Germany DA - 26.11.2018 KW - Mikroplastik KW - Umwelt KW - Polymere Eigenschaften PY - 2018 AN - OPUS4-47183 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Stark, Wolfgang A1 - Teteris, Gundars A1 - Braun, Ulrike A1 - Bohmeyer, W. A1 - Lange, K. T1 - Kontrolle der Vernetzungsreaktion bei reaktiven Harzen - DSC, Rheologie, DMA, FTIR und Online-Ultraschall im Vergleich N2 - Faserverbundbauteile werden durch Tränkung von Fasergewebe mit flüssigem Harz, in der Regel Epoxidharzen, und anschließender Härtung des Harzes gefertigt. Dabei kann man das Gewebe im Vorfeld mit reaktivem Harz tränken und als so genanntes Prepreg verarbeiten oder man injiziert das frisch mit dem Härter gemischte Harz in ein Werkzeug, in dem das Gewebe bereits liegt - z. B. beim RTM-Prozess. Ausgehend von der Aufgabenstellung, eine Prepregherstellung mit hohem Qualitätsstandard zu realisieren und Möglichkeiten der Fertigungskontrolle für den Prepreg-Verarbeiter aufzuzeigen, wurde an einem für die Prepregherstellung vorgesehenen Harzsystem eine weitgehende Charakterisierung des Aushärtungsverlaufs vorgenommen. Wegen der Schwierigkeit, schnell konstante Aushärtungstemperaturen zu erreichen, wurden bei allen Methoden mit einer Heizrate von 1 K/min von RT bis 200 °C aufgeheizt. T2 - Technomer 2011 - 22. Fachtagung über Verarbeitung und Anwendung von Polymeren CY - Chemnitz, Deutschland DA - 10.11.2011 KW - Thermoanalyse KW - Lineare Aufheizung KW - Online Prozesskontrolle KW - Epoxidharz KW - Prepreg PY - 2011 SN - 978-3-939382-10-2 IS - Kap. 1.1 SP - 1 EP - 9 AN - OPUS4-24910 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Lörchner, Dominique A1 - Dittmann, Daniel A1 - Braun, Ulrike A1 - Kroh, L. W. A1 - Köppen, Robert T1 - Investigation of two triazine-based heterocyclic brominated flame retardants by coupled thermogravimetry-Fourier transform infrared spectroscopy N2 - In this study, the thermal decomposition of 1,3,5-tris-(2,3-dibromopropyl)-1,3,5-triazine-2,4,6-trione (TDBPTAZTO) and 2,4,6-tris-(2,4,6-tribromo-phenoxy)-1,3,5-triazine (TTBP-TAZ) were investigated for the first time by thermogravimetric analysis. Both compounds were thermal degraded between 225 and 350 °C (TDBP-TAZTO) as well as 300 and 400 °C (TTBP-TAZ). As a result, mass loss (%) of 98.5% for TTBP-TAZ and 95.4% for TDBP-TAZTO at 600 °C under N2 were observed. The major pyrolytic degradation products of TTBP-TAZ were formed in a single step and identified by FTIR analysis as 2,4,6-tribromophenol and further bromine-substituted aromatic compounds. In comparison, TDBP-TAZTO was pyrolytic degraded in two steps, whereby on the first step the release of hydrogen Bromide and 1,3,5-triallyl-1,3,5-triazine-2,4,6-trione could be detected. In the second minor step, isocyanic acid could be additionally identified. Subsequently, the obtained products of the TGA-FTIR measurements were used for a targeted search for mass fragments in mass spectrometry measurements. For TTBP-TAZ, only the degradation product 1,3,5-tribromobenzene could be detected by MS/MS analyzes. No comparable thermal degradation products, except hydrogen bromide, were observed in the MS/MS spectra of TDBP-TAZTO. Therefore, the search of further mass fragments was not possible compared to the findings of the TGA-FTIR measurements. KW - Pyrolysis KW - Thermal decomposition KW - TGA-FTIR KW - Mass spectrometry PY - 2019 DO - https://doi.org/10.1016/j.jaap.2019.104635 VL - 141 SP - 104635-1 EP - 104635-5 PB - Elsevier B.V. AN - OPUS4-48506 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Lorenz, Edelgard A1 - Maskos, Michael T1 - Investigation of the durability of poly(ether urethane) in water and air N2 - In this study some relevant aspects of the durability of an aromatic poly(ether urethanes) was investigated. Hydrolytic and oxidative treatments at increased temperatures were applied. The induced changes in the materials under investigation were characterised by complementary polymer characterisation methods, such as ATR-FTIR, DSC and mechanical testing. The thermal and hydrolytic treatment did not significantly affect the chemical composition of the materials. Changes can be observed in the microstructure of the materials. PY - 2011 DO - https://doi.org/10.5301/IJAO.2011.6408 SN - 0391-3988 VL - 34 IS - 2 SP - 129 EP - 133 PB - Wichtig Ed. CY - Milano [u.a.] AN - OPUS4-23729 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Jaunich, Matthias A1 - Böhning, Martin A1 - Braun, Ulrike A1 - Teteris, G. A1 - Stark, W. T1 - Investigation of the curing state of ethylene/vinyl acetate copolymer (EVA) for photovoltaic applications by gel content determination, rheology, DSC and FTIR N2 - The cure behaviour of a specific ethylene vinyl acetate material as used for encapsulation of photovoltaic modules was analysed by rheometer, differential scanning calorimetry and Fourier transform infrared spectroscopy to test for a suitable replacement for the laborious determination of gel content. The results show that all applied methods are capable of describing the effects of the cross-linking process. Some provide results very similar to those yielded by analysis of the insoluble content, but the question remains as to whether indirect methods should be preferred over the direct measurement of physical properties, e.g. as performed by the curemeter. A material stored for one year was also tested to demonstrate the effect of extended storage on cure behaviour and how this is detected by different methods. This complements the other methods, which were clearly able to detect the different cure behaviour of the aged EVA, whereas determination of the gel content could not. KW - Photovoltaic cell encapsulation KW - EVA KW - Incoming goods control KW - Insoluble content KW - Rheometer PY - 2016 DO - https://doi.org/10.1016/j.polymertesting.2016.03.013 SN - 0142-9418 VL - 52 IS - 1 SP - 133 EP - 140 PB - Elsevier Ltd. CY - Oxford, UK AN - OPUS4-35918 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Interaction of Red Phosphorus, Melanine Polyphosphate and Magnesium Hydroxide as Fire Retardant in HIPS T2 - 9th European Meeting on Fire Retardancy and Protection of Materials, FRPM '03 CY - Lille, France DA - 2003-09-17 PY - 2003 AN - OPUS4-4028 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Wachtendorf, Volker A1 - Geburtig, Anja A1 - Braun, Ulrike A1 - Schartel, Bernhard A1 - Trubiroha, Peter T1 - Influence of weathering on the stability of flame retardancy in polymeric materials for outdoor use T2 - 4th European weathering symposium - Natural and artificial ageing of polymers CY - Budapest, Hungary DA - 2009-09-16 KW - Flame retardancy KW - Weathering KW - Stability KW - Polymeric material KW - Outdoor PY - 2009 SN - 978-3-9810472-8-8 IS - CEEES Publication No. 11 SP - 313 EP - 326 PB - DWS Werbeagentur und Verlag GmbH CY - Karlsruhe AN - OPUS4-20060 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Balabanovich, Aliaksandr A1 - Schartel, Bernhard A1 - Knoll, Uta A1 - Artner, J. A1 - Ciesielski, M. A1 - Döring, M. A1 - Perez, R. A1 - Sandler, J.K.W. A1 - Altstädt, V. A1 - Hoffmann, T. A1 - Pospiech, D. T1 - Influence of the oxidation state of phosphorus on the decomposition and fire behaviour of flame-retarded epoxy resin composites N2 - A systematic and comparative evaluation of the pyrolysis of halogen-free flame-retarded epoxy resins containing phosphine oxide, phosphinate, phosphonate, and phosphate (phosphorus contents around 2.6 wt.%) and the fire behaviour of their carbon fibre composites is presented. Decomposition pathways are proposed based on the thermal analysis (TG), TG coupled with evolved gas analysis (TG-FTIR), kinetics and analysis of the residue with FTIR and XPS. All organophosphorus-modified hardeners containing phenoxy groups lead to a reduced decomposition temperature and mass loss step for the main decomposition of the cured epoxy resin. With increasing oxidation state of the phosphorus the thermally stable residue increases, whereas the release of phosphorus-containing volatiles decreases. The flammability of the composites was investigated with LOI and UL 94 and the fire behaviour for forced-flaming conditions with cone calorimeter tests performed using different irradiations. The flame retardancy mechanisms are discussed. With increasing oxidation state of the phosphorus additional charring is observed, whereas the flame inhibition, which plays the more important role for the performance of the composites, decreases. The processing and the mechanical performance (delamination resistance, flexural properties and interlaminar bonding strength) of the fibre-reinforced composites containing phosphorus were maintained at a high level and, in some cases, even improved. The potential for optimising flame retardancy while maintaining mechanical properties is highlighted in this study. KW - Fire retardant KW - Composites KW - Organophosphorus-containing epoxy resin PY - 2006 DO - https://doi.org/10.1016/j.polymer.2006.10.022 SN - 0032-3861 SN - 1873-2291 VL - 47 IS - 26 SP - 8495 EP - 8508 PB - Springer CY - Berlin AN - OPUS4-14054 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seefeldt, Henrik A1 - Braun, Ulrike A1 - Hofmann-Böllinghaus, Anja T1 - Influence of structure, wood content, moisture and additives on the burning behaviour of wood plastic composites T2 - Fire and materials 2011 - 12th International conference and exhibiton CY - San Francisco, CA, USA DA - 2011-01-31 PY - 2011 SP - 1 EP - 10 PB - Interscience Communications AN - OPUS4-24650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Identification of tire wear particles based on elemental composition N2 - The identification of tire wear particles by use of ICP-MS is presented. T2 - SETAC CY - Rome, Italy DA - 13.05.2018 KW - Microplastics KW - Tire wear particles KW - ICP-MS PY - 2018 AN - OPUS4-45205 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Paul, Andrea A1 - Wander, Lukas A1 - Becker, Roland A1 - Goedecke, Caroline A1 - Braun, Ulrike T1 - High-throughput NIR spectroscopic (NIRS) detection of microplastics in soil N2 - The increasing pollution of terrestrial and aquatic ecosystems with plastic debris leads to the accumulation of microscopic plastic particles of still unknown amount. To monitor the degree of contamination analytical methods are urgently needed, which help to quantify microplastics (MP). Currently, time-costly purified materials enriched on filters are investigated both by micro-infrared spectroscopy and/or micro-Raman. Although yielding precise results, these techniques are time consuming, and are restricted to the analysis of a small part of the sample in the order of few micrograms. To overcome these problems, here we tested a macroscopic dimensioned NIR process-spectroscopic method in combination with chemometrics. For calibration, artificial MP/soil mixtures containing defined ratios of polyethylene, polyethylene terephthalate, polypropylene, and polystyrene with diameters < 125 µm were prepared and measured by a process FT-NIR spectrometer equipped with a fiber optic reflection probe. The resulting spectra were processed by chemometric models including support vector machine regression (SVR), and partial least squares discriminant analysis (PLS-DA). Validation of models by MP mixtures, MP-free soils and real-world samples, e.g. and fermenter residue, suggest a reliable detection and a possible classification of MP at levels above 0.5 to 1.0 mass% depending on the polymer. The benefit of the combined NIRS chemometric approach lies in the rapid assessment whether soil contains MP, without any chemical pre-treatment. The method can be used with larger sample volumes and even allows for an online prediction and thus meets the demand of a high-throughput method. KW - Microplastics KW - Soil KW - Chemometrics KW - PLS-DA KW - Support vector machines KW - Near Infrared Spectroscopy PY - 2018 DO - https://doi.org/10.1007/s11356-018-2180-2 SN - 1614-7499 SN - 0944-1344 VL - 26 IS - 8 SP - 7364 EP - 7374 PB - Springer AN - OPUS4-45405 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Harmonization in microplastics Analysis N2 - The lecture summarizes the current status of hamonization edr microplastics analytics in Germany. T2 - Symposium on Occurrence and Fate of Microplastics CY - Beijing, China DA - 09.07.2019 KW - Microplastics KW - TED-GC-MS KW - Harmonisation PY - 2019 AN - OPUS4-49063 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Harmonisierung von Untersuchungsverfahren für (Mikro-)Plastik in der Umwelt N2 - Im Rahmen der Thematik "Recycling von Kunststoffen" wird die Thematik "Mikroplastik" vorgestellt T2 - Berliner Recycling- und Rohstoffkonferenz CY - Berlin, Germany DA - 11.03.2019 KW - Mikroplastik KW - Standarisierung KW - Analytik PY - 2019 AN - OPUS4-47582 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gallo, Emanuela A1 - Braun, Ulrike A1 - Schartel, Bernhard A1 - Russo, P. A1 - Acierno, Domenico T1 - Halogen-free flame retarded poly(butylene terephthalate) (PBT) using metal oxides/PBT nanocomposites in combination with aluminium phosphinate N2 - The flame retardancy of poly(butylene terephthalate) (PBT) containing aluminium diethlyphosphinate (AlPi) and/or nanometric metal oxides such as TiO2 or Al2O3 was investigated. In particular the different active flame retardancy mechanisms were discovered. Thermal analysis, evolved gas analysis (TG-FTIR), flammability tests (LOI, UL 94), cone calorimeter measurements and chemical analyses of residues (ATR-FTIR) were used. AlPi acts mainly in the gas phase through the release of diethylphosphic acid, which provides flame inhibition. Part of AlPi remains in the solid phase reacting with the PBT to phosphinate-terephthalate salts that decompose to aluminium phosphate at higher temperatures. The metal oxides interact with the PBT decomposition and promote the formation of additional stable carbonaceous char in the condensed phase. A combination of metal oxides and AlPi gains the better classification in the UL 94 test thanks to the combination of the different mechanisms. KW - Poly(butylene terephthalate) KW - Flammability KW - Metal oxide nanocomposite KW - Metal phosphinate PY - 2009 DO - https://doi.org/10.1016/j.polymdegradstab.2009.04.014 SN - 0141-3910 SN - 1873-2321 VL - 94 IS - 8 SP - 1245 EP - 1253 PB - Applied Science Publ. CY - London AN - OPUS4-19516 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - General aspects of polymers and polymers in environment N2 - The presentation addresses first general aspects of polymers and polymers in environment (definitions, types, phases, morphology, density) and than summarise the possibilities of analysis. T2 - GWRC Workshop on "Microplastics in Water" CY - Nantes, France DA - 22.05.2016 KW - Microplastics KW - Polymers PY - 2016 AN - OPUS4-36901 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - General aspects of polymers and and polymers in environment N2 - The presentation addresses first general aspects of polymers and polymers in environment (definitions, types, phases, morphology, density) and than summarise the possibilities of analysis. T2 - 1. meeting of ISO/TC 61/SC 5/AHG "microplastics" CY - Berlin, Germany DA - 12.04.2016 KW - Microplastics KW - Polymers PY - 2016 AN - OPUS4-36758 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schartel, Bernhard A1 - Weiß, André A1 - Mohr, F. A1 - Kleemeier, M. A1 - Hartwig, A. A1 - Braun, Ulrike T1 - Flame retarded epoxy resins by adding layered silicate in combination with the conventional protection-layer-building flame retardants melamine borate and ammonium polyphosphate N2 - The pyrolysis and flammability of phosphonium-modified layered silicate epoxy resin nanocomposites (EP/LS) were evaluated when LS was combined with two flame retardants, melamine borate (MB) and ammonium polyphosphate (APP), that also act via a surface protection layer. Thermogravimetry (TG), TG coupled with Fourier Transform Spectroscopy (TG-FTIR), oxygen index (LOI), UL 94 burning chamber (UL 94) and cone calorimeter were used. The glassy coating because of 10 wt % MB during combustion showed effects in the cone calorimeter test similar to nanodispersed LS, and somewhat better flame retardancy in flammability tests, such as LOI and UL 94. Adding APP to EP resulted in intumescent systems. The fire retardancy was particularly convincing when 15 wt % APP was used, especially for low external heat flux, and thus, also in flammability tests like LOI and UL 94. V0 classification is achieved when 15 wt % APP is used in EP. The flame retardancy efficiency of the protection layers formed does not increase linearly with the MB and APP concentrations used. The combination of LS with MB or APP shows antagonism; thus the performance of the combination of LS with MB or APP, respectively, was disappointing. No optimization of the carbonaceous-inorganic surface layer occurred for LS-MB. Combining LS with APP inhibited the intumescence, most probably through an increase in viscosity clearly above the value needed for intumescent behavior. KW - Nanocomposites KW - Fire retardance KW - Thermosets KW - Organoclay KW - Ammonium polyphosphate KW - Melamine borate PY - 2010 DO - https://doi.org/10.1002/app.32512 SN - 0021-8995 SN - 1097-4628 VL - 118 IS - 2 SP - 1134 EP - 1143 PB - Wiley InterScience CY - Hoboken, NJ AN - OPUS4-21725 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Schartel, Bernhard T1 - Flame Retardant Mechanisms of Red Phosphorus and Magnesium Hydroxide in High Impact Polystyrene N2 - The flame retardant mechanisms of red phosphorus, magnesium hydroxide and red phosphorus combined with magnesium hydroxide were studied in high impact polystyrene by means of comprehensive decomposition studies and combustion tests. The study is intended to illuminate prerequisites and the potential of red phosphorus as a fire retardant for hydrocarbon polymers in the condensed phase and in the gas phase. Thermal and thermo-oxidative decomposition, decomposition kinetics and the product gases evolved were characterized using thermogravimetry coupled with Fourier transform infrared spectroscopy and mass spectroscopy, respectively. Fire behaviour was investigated with a cone calorimeter using different external heat fluxes, whereas the flammability was determined by limited oxygen indices. The combustion residues were analysed using XPS. Red phosphorus reduced the heat release in HIPS due to radical trapping in the gas phase. Magnesium hydroxide influenced fire behaviour by heat sink mechanisms, release of water and the formation of a magnesia layer acting as a barrier. The combination of both flame retardants in HIPS nearly resulted in a superposition. A slight synergy in barrier characteristics was due to the formation of magnesium phosphate, whereas a slight anti-synergism occurred in flammability and in the gas phase action. The latter effect is controlled by a decreased fuel rate due to the barrier layer rather than by an initiation of red phosphorus oxidation in the condensed phase. KW - Fire retardancy KW - Polystyrene KW - Pyrolysis KW - TG-FTIR KW - Red Phosphorus KW - Mg(OH)2 KW - Cone Calorimeter KW - Additives KW - Thermogravimetric analysis PY - 2004 DO - https://doi.org/10.1002/macp.200400255 SN - 1022-1352 SN - 1521-3935 VL - 205 IS - 16 SP - 2185 EP - 2196 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-4488 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Perez, R.M. A1 - Sandler, J.K.W. A1 - Altstädt, V. A1 - Hoffmann, T. A1 - Pospiech, D. A1 - Artner, J. A1 - Ciesielski, M. A1 - Döring, M. A1 - Braun, Ulrike A1 - Schartel, Bernhard ED - Schartel, Bernhard T1 - Flame retardant epoxy resin system for liquid composite moulding applications KW - Epoxy resin KW - Fire retardancy PY - 2007 SN - 978-3-8334-8873-3 SP - 69 EP - 84 PB - Books on Demand GmbH CY - Norderstedt AN - OPUS4-17627 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seefeldt, Henrik A1 - Dümichen, Erik A1 - Braun, Ulrike T1 - Flame retardancy of glass fiber reinforced high temperature polyamide by use of aluminum diethylphosphinate: thermal and thermo-oxidative effects N2 - Glass fiber reinforced polyamide (PA) 6T/DT flame retarded with aluminum diethylphosphinate (AlPi) was tested to assess its flame retardant properties. Models for the decomposition of PA 6T/DT with and without AlPi are presented. Thermal decomposition was measured by performing TGA with Fourier transform infrared (FTIR) spectroscopy and FTIR spectroscopy in the condensed phase. Fire behavior was studied using a cone calorimeter and flammability was tested with UL 94 and the limiting oxygen index. AlPi works as an effective flame retardant for glass fiber reinforced PA 6T/DT materials, acting in the gas phase. Also observed was condensed-phase action, which occurs especially under oxidative conditions before the samples ignite. KW - Flame retardancy KW - High tmeperature polyamide 6T/DT KW - Aluminum phosphinate KW - Degradation PY - 2013 DO - https://doi.org/10.1002/pi.4497 SN - 0959-8103 SN - 1097-0126 SN - 0007-1641 VL - 62 IS - 11 SP - 1608 EP - 1616 PB - Wiley InterScience CY - Chichester, West Sussex AN - OPUS4-29386 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Flame retardancy mechanisms of phosphorus containing epoxy resins: effects of oxidation state T2 - MODEST CY - San Sebastián, Spain DA - 2006-09-10 PY - 2006 AN - OPUS4-12939 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Bahr, Horst A1 - Sturm, Heinz A1 - Schartel, Bernhard T1 - Flame retardancy mechanisms of metal phosphinates and metal phosphinates in combination with melamine cyanurate in glass-fiber reinforced poly(1,4-butylene terephthalate): the influence of metal cation N2 - The pyrolysis and fire behavior of glass-fiber reinforced poly(butylene terephthalate) (PBT/GF) with two different metal phosphinates as flame retardants in combination with and without melamine cyanurate (MC) were analyzed by means of thermogravimetry, thermogravimetry coupled with infrared spectroscopy, flammability, and cone calorimeter tests as well as scanning electron microscopy/energy dispersive X-ray spectroscopy and X-ray fluorescence spectroscopy. In PBT/GF, dosages of 13-20% of the halogen-free flame retardant aluminum phosphinate or aluminum phosphinate in combination with MC fulfill the requirements for electrical engineering and electronics applications (UL 94 = V-0; LOI > 42%), whereas the use of the same amount of zinc phosphinate or zinc phosphinate in combination with MC does not improve the fire behavior satisfactorily (UL 94 = HB; LOI = 27-28%). The performance under forced flaming conditions (cone calorimeter) is quite similar for both of the metal phosphinates. The use of aluminum and zinc salts results in similar flame inhibition predominantly due to the release of the phosphinate compounds in the gas phase. Both metal phosphinates and MC interact with the polymer changing the decomposition characteristics. However, part of the zinc phosphinate vaporizes as a complete molecule. Because of the different decomposition behavior of the metal salts, only the aluminum phosphinate results in a small amount of thermally stable carbonaceous char. In particular, the aluminum phosphinate-terephthalate formed is more stable than the zinc phosphinate-terephthalate. The small amount of char has a crucial effect on the thermal properties and mechanical stability of the residue and thus the flammability. KW - Flame retardance KW - Polyester KW - Phosphinates KW - Pyrolysis KW - Cone calorimeter PY - 2008 DO - https://doi.org/10.1002/pat.1147 SN - 1042-7147 SN - 1099-1581 VL - 19 IS - 6 SP - 680 EP - 692 PB - John Wiley & Sons, Ltd. CY - Chichester AN - OPUS4-17620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Braun, Ulrike A1 - Sturm, Heinz A1 - Schartel, Bernhard T1 - Flame retardancy mechanisms of aluminium phosphinate in glass-fibre reinforced polyester T2 - Flame Retardants 2008 Conference CY - London, UK DA - 2008-02-12 PY - 2008 SN - 978-0-9556548-1-7 SP - 133 EP - 140 PB - Interscience Communications CY - London, UK AN - OPUS4-17785 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Flame retardancy mechanisms of aluminium phosphinate in glass-fibre reinforced polyester T2 - Flame Retardants 2008 CY - London, England DA - 2008-02-12 PY - 2008 AN - OPUS4-16672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schartel, Bernhard A1 - Braun, Ulrike ED - Menachem Lewin, T1 - Flame retardancy mechanisms of aluminium phosphinate in glass fiber reinforced thermoplastics T2 - 19th Annual BCC Conference - Recent Advances in Flame Retardancy of Polymeric Materials CY - Stamford, Connecticut, USA DA - 2008-06-09 KW - Aluminium phosphinate KW - PA 66 KW - PBT KW - Flame retardancy KW - Cone calorimeter PY - 2008 SN - 1-59623-435-0 IS - CHM007I SP - 36 EP - 47 PB - BCC Research CY - Wellesley, MA, USA AN - OPUS4-19167 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Schartel, Bernhard A1 - Fichera, Mario Augusto A1 - Jäger, Christian T1 - Flame retardancy mechanisms of aluminium phosphinate in combination with melamine polyphosphate and zinc borate in glass-fibre reinforced polyamide 6,6 N2 - The fire retardancy mechanisms of aluminium diethylphosphinate in combination with melamine polyphosphate and zinc borate was analysed in glass-fibre reinforced polyamide 6,6. The influence of phosphorus compounds on the polyamide decomposition pathways was characterized using thermal analysis (TG), evolved gas analysis (TG–FTIR), and FTIR–ATR analysis of the residue. The Lewis acid–base interactions between the flame retardants, the amide unit, and the metal ions control the decomposition. The flammability (LOI, UL 94) and performance under forced-flaming conditions (cone calorimeter using different irradiations) were investigated. Fire residues were analysed with FTIR–ATR, SEM–EDX, and NMR. Aluminium phosphinate in polyamide 6,6 acts mainly by flame inhibition. Melamine polyphosphate shows some fuel dilution and a significant barrier effect. Using a combination of aluminium phosphinate and melamine polyphosphate results in some charring and a dominant barrier effect. These effects are improved in the presence of zinc borate due to the formation of boron–aluminium phosphates instead of aluminium phosphates. KW - Flame retardancy KW - Polyamide 6,6 KW - Metal phosphinate KW - Melamine polyphosphate KW - Zinc borate PY - 2007 SN - 0141-3910 SN - 1873-2321 VL - 92 IS - 8 SP - 1528 EP - 1545 PB - Applied Science Publ. CY - London AN - OPUS4-15707 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Schartel, Bernhard T1 - Flame Retardancy Mechanisms of Aluminium Phosphinate in Combination with Melamine Cyanurate in Glass-Fibre-Reinforced Poly(1,4-butylene terephthalate) N2 - The flame retardancy mechanisms of aluminium diethylphosphinate (AlPi) and its combination with melamine cyanurate (MC) in glass-fibre-reinforced poly(butylene terephthalate) (PBT/GF) were analysed using TGA including evolved gas analysis (TGA-FTIR), cone calorimeter measurements using various irradiations, flammability tests (limited oxygen index, LOI, UL 94) and chemical analyses of residues (FTIR, SEM/EDX). AlPi decomposed mainly through the formation of diethylphosphinic acid and aluminium phosphate and influenced the decomposition of the PBT only slightly. AlPi acted mainly through flame inhibition. A halogen-free V-0 PBT/GF material was achieved with a LOI of 44%. Additional charring influenced the flammability. MC decomposed independently of the polymer and showed some fuel dilution effects. KW - Flame retardance KW - Metal phosphinate KW - Polyester KW - Pyrolysis KW - Thermogravimetric analysis PY - 2008 DO - https://doi.org/10.1002/mame.200700330 SN - 1438-7492 SN - 1439-2054 VL - 293 IS - 3 SP - 206 EP - 217 PB - Wiley-VCH Verl. CY - Weinheim AN - OPUS4-17122 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CHAP A1 - Pikacz, E. A1 - Seefeldt, Henrik A1 - Schartel, Bernhard A1 - Braun, Ulrike A1 - Karrasch, Andrea A1 - Jäger, Christian T1 - Flame retardancy in PC/Silicone rubber blends using BDP and additional additives T2 - 20th Annual conference on recent advances in flame retardancy of polymeric materials CY - Stamford, CT, USA DA - 2009-06-01 KW - Flame retardancy KW - PC blend KW - Aryl phosphate PY - 2009 SN - 1-59623-509-8 VL - 20 IS - Chapter IV-B SP - 236 EP - 246 CY - Wellesley, MA, USA AN - OPUS4-20703 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Braun, Ulrike A1 - Knoll, Uta A1 - Neubert, Dietmar A1 - Schartel, Bernhard ED - Schartel, Bernhard T1 - Fire Retarding Mechanisms of Red Phosphorus in Polybutylenterephthalate (PBT) in Combination with Melamine Cyanurate or Zinc Oxide KW - Fire retardancy KW - Polyester KW - Red phosphorus KW - Thermal analysis KW - Cone calorimeter PY - 2007 SN - 978-3-8334-8873-3 SP - 35 EP - 49 PB - Books on Demand GmbH CY - Norderstedt AN - OPUS4-17662 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Fire Retarding Mechanisms of Red Phosphorus in Polybutylenterephthalate T2 - 10th European Meeting on Fire Retardancy and Protection of Materials (10th European Conference on Fire Retardant Polymers), FRPM '05, BAM, Berlin CY - Berlin, Germany DA - 2005-09-07 PY - 2005 AN - OPUS4-6369 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schartel, Bernhard A1 - Braun, Ulrike A1 - Schwarz, U. A1 - Reinemann, S. ED - Lewin, M. T1 - Fire Retarded Polypropylene/Flax Biocomposites T2 - 14th Conference on Recent Advances in Flame Retardancy of Polymeric Materials ; 14th Annual BCC Conference on Flame Retardancy CY - Stamford, CT, USA DA - 2003-06-02 KW - Fire retardancy KW - PP/Flax Biocomposite KW - Expandable Graphite KW - Ammonium Polyphosphate KW - TG-FTIR KW - Cone Calorimeter PY - 2003 SN - 1-569-65930-3 VL - 14 SP - 219 EP - 228 PB - BCC CY - Norwalk, Conn. AN - OPUS4-2815 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Gallo, Emanuela A1 - Schartel, Bernhard A1 - Braun, Ulrike A1 - Russo, P. A1 - Acierno, Domenico T1 - Fire retardant synergisms between nanometric Fe2O3 and aluminium phosphinate in poly(butylene terephthalate) N2 - The pyrolysis and the flame retardancy of poly(butylene terephthalate) (PBT) containing aluminum diethylphosphinate (AlPi) and nanometric Fe2O3 were investigated using thermal analysis, evolved gas analysis (Thermogravimetry-FTIR), flammability tests (LOI, UL 94), cone calorimeter measurements and chemical analysis of residue (FTIR). AlPi mainly acts as a flame inhibitor in the gas phase, through the release of diethylphosphinic acid. A small amount of Fe2O3 in PBT promotes the formation of a carbonaceous char in the condensed phase. The combination of 5 and 8 wt% AlPi, respectively, with 2 wt% metal oxides achieves V-0 classification in the UL 94 test thanks to complementary action mechanisms. Using PBT/metal oxide nanocomposites shows a significant increase in the flame retardancy efficiency of AlPi in PBT and thus opens the route to surprisingly sufficient additive contents as low as 7 wt%. KW - Poly(butylene terephthalate) (PBT) KW - Flammability KW - Metal oxide KW - Nanocomposite KW - Aluminum diethylphosphinate PY - 2011 DO - https://doi.org/10.1002/pat.1774 SN - 1042-7147 SN - 1099-1581 VL - 22 IS - 12 SP - 2382 EP - 2391 PB - John Wiley & Sons, Ltd. CY - Chichester AN - OPUS4-24915 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Fire Retardant Mechanisms of Phosphinates in Thermoplastics T2 - Fire Retardant Technologies 2009 CY - Preston (Lancashire), England DA - 2009-04-21 PY - 2009 AN - OPUS4-19842 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schartel, Bernhard A1 - Braun, Ulrike A1 - Schwarz, U. A1 - Reinemann, S. T1 - Fire Retardancy of Polypropylene/Flax Blends N2 - A comprehensive characterization of the thermal and the fire behaviour is presented for polypropylene (PP) flax compounds containing ammonium polyphosphate (APP) and expandable graphite as fire retardants. Thermogravimetry coupled with an evolved gas analysis (TG-FTIR) was performed to ensure a significant thermal analysis. The fire response under forced flaming conditions was studied using a cone calorimeter. The external heat flux was varied between 30 and 70 kW m-2 so that the results could be evaluated for different fire scenarios and tests. Different flammability tests (UL 94, limiting oxygen index, glow wire test, GMI 60261) were performed and the results compared with the cone calorimeter data. The different char forming mechanisms are described and the resulting fire retardancy is classified. The successful and ecological friendly fire retardancy is a technological breakthrough for PP/flax biocomposites. KW - Biosomposites KW - Flame retardancy KW - Flax PY - 2003 DO - https://doi.org/10.1016/S0032-3861(03)00692-X SN - 0032-3861 SN - 1873-2291 VL - 44 IS - 20 SP - 6241 EP - 6250 PB - Springer CY - Berlin AN - OPUS4-2640 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike A1 - Schartel, Bernhard T1 - Fire Retardancy Mechanisms of Red Phosphorus in Thermoplastics N2 - The thermal decomposition and the fire behavior of glass fiber reinforced polyamide 66 (PA-66) and high impact polystyrene (HIPS) containing red phosphorus (P4) were investigated. For glass fiber reinforced PA-66, P4 promotes char formation in the condensed phase. Barrier effects and the reduction of combustible volatiles were identified as fire retardancy mechanisms. For HIPS, P4 acts in the gas phase, mainly trapping radicals. The heat release per mass loss polymer is reduced due to an incomplete combustion. T2 - 12th International Conference Additives 2003 CY - San Francisco, CA, USA DA - 2003-04-06 PY - 2003 UR - http://www.executive-conference.com/conferences/archives/abstracts2003/add03_abs5b.html SP - 1(?) EP - 10(?) PB - ECM CY - Plymouth, Mich. AN - OPUS4-2502 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Fire Retardancy Mechanisms of Red Phosphorus in Thermoplastics T2 - Additives 2003 - 12th Annual Conference on Additives and Modifiers CY - San Francisco, CA, USA DA - 2003-04-06 PY - 2003 AN - OPUS4-4010 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schartel, Bernhard A1 - Braun, Ulrike T1 - Fire Retardancy Mechanisms of Phosphorus in Thermoplastics KW - Fire retardancy KW - Red Phosphorus KW - Cone Calorimeter KW - TG-FTIR KW - TG-MS KW - HIPS KW - PBT KW - PA 66 PY - 2004 SN - 0743-0515 VL - 91 SP - 152 EP - 153 PB - Division of Polymeric Materials Science and Engineering, American Chemical Society CY - Washington, DC AN - OPUS4-3971 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Bahr, Horst A1 - Schartel, Bernhard T1 - Fire retardancy effect of aluminium phosphinate and melamine polyphosphate in glass fibre reinforced polyamide 6 N2 - The fire retardancy mechanism of aluminium diethyl phosphinate (AlPi) and AlPi in combination with melamine polyphosphate (MPP) was investigated in glass-fibre reinforced polyamide 6 (PA6/GF) by analysing the pyrolysis, flammability and fire behaviour. AlPi in PA6/GF-AlPi partly vaporises as AlPi and partly decomposes to volatile diethylphosphinic acid (subsequently called phosphinic acid) and aluminium phosphate residue. In fire a predominant gas-phase action was observed, but the material did not reach a V-0 classification for the moderate additive content used. For the combination of both AlPi and MPP in PA6/GF-AlPi-MPP a synergistic effect occurred, because of the reaction of MPP with AlPi. Aluminium phosphate is formed in the residue and melamine and phosphinic acid are released in the gas phase. The aluminium phosphate acts as a barrier for fuel and heat transport, whereas the melamine release results in fuel dilution and the phosphinic acid formation in flame inhibition. The higher amount of aluminium phosphate in PA6/GF-AlPi-MPP stabilised the residue in flammability tests in comparison to PA6/GF-AlPi, so that this material achieved a V-0 classification in the UL 94 test. PY - 2010 DO - https://doi.org/10.1515/epoly.2010.10.1.443 SN - 1618-7229 IS - 041 SP - 1 EP - 14 PB - De Gruyter CY - [S.l.] AN - OPUS4-19821 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Fast identification of microplastics using thermal extraction methods N2 - The presentation presents an overview about existing methods of microplastic detection with a special focus on thermo-analytical methods. T2 - Perkin Elmer Workshop Microplastics CY - Vienna, Austria DA - 11.01.2018 KW - Microplastics KW - TED-GC-MS KW - Analysis PY - 2018 AN - OPUS4-43803 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dümichen, Erik A1 - Eisentraut, Paul A1 - Bannick, Claus Gerhard A1 - Barthel, Anne-Kathrin A1 - Braun, Ulrike A1 - Senz, R. T1 - Fast identification of microplastics in complex environmental samples by a thermal degradation method N2 - n order to determine the relevance of microplastic particles in various environmental media, comprehensive investigations are needed. However, no analytical method exists for fast identification and quantification. At present, optical spectroscopy methods like IR and RAMAN imaging are used. Due to their time consuming procedures and uncertain extrapolation, reliable monitoring is difficult. For analyzing polymers Py-GC-MS is a standard method. However, due to a limited sample amount of about 0.5 mg it is not suited for analysis of complex sample mixtures like environmental samples. Therefore, we developed a new thermoanalytical method as a first step for identifying microplastics in environmental samples. A sample amount of about 20 mg, which assures the homogeneity of the sample, is subjected to complete thermal decomposition. The specific degradation products of the respective polymer are adsorbed on a solid-phase adsorber and subsequently analyzed by thermal desorption gas chromatography mass spectrometry. For certain identification, the specific degradation products for the respective polymer were selected first. Afterwards real environmental samples from the aquatic (three different rivers) and the terrestrial (bio gas plant) systems were screened for microplastics. Mainly polypropylene (PP), polyethylene (PE) and polystyrene (PS) were identified for the samples from the bio gas plant and PE and PS from the rivers. However, this was only the first step and quantification measurements will follow. KW - Thermal Degradation KW - Microplastic PY - 2017 DO - https://doi.org/10.1016/j.chemosphere.2017.02.010 VL - 174 SP - 572 EP - 584 PB - Elsevier Ltd. AN - OPUS4-42143 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dümichen, Erik A1 - Eisentraut, Paul A1 - Bannick, Claus Gerhard A1 - Barthel, Anne-Kathrin A1 - Senz, R. A1 - Braun, Ulrike T1 - Fast identification of microplastics in complex environmental samples by a thermal degradation method N2 - In order to determine the relevance of microplastic particles in various environmental media, comprehensive investigations are needed. However, no analytical method exists for fast identification and quantification. At present, optical spectroscopy methods like IR and RAMAN imaging are used. Due to their time consuming procedures and uncertain extrapolation, reliable monitoring is difficult. For analyzing polymers Py-GC-MS is a standard method. However, due to a limited sample amount of about 0.5 mg it is not suited for analysis of complex sample mixtures like environmental samples. Therefore, we developed a new thermoanalytical method as a first step for identifying microplastics in environmental samples. A sample amount of about 20 mg, which assures the homogeneity of the sample, is subjected to complete thermal decomposition. The specific degradation products of the respective polymer are adsorbed on a solid-Phase adsorber and subsequently analyzed by thermal Desorption gas chromatography mass spectrometry. For certain identification, the specific degradation products for the respective polymer were selected first. Afterwards real environmental samples from the aquatic (three different rivers) and the terrestrial (bio gas plant) systems were screened for microplastics. Mainly polypropylene (PP), polyethylene (PE) and polystyrene (PS) were identified for the samples from the bio gas plant and PE and PS from the rivers. However, this was only the first step and quantification measurements will follow. KW - Microplastics KW - Thermal desorption KW - Gas chromatography PY - 2017 DO - https://doi.org/10.1016/j.chemosphere.2017.02.010 SN - 0045-6535 SN - 1879-1298 IS - 174 SP - 572 EP - 584 PB - Elsevier AN - OPUS4-40235 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wander, Lukas A1 - Vianello, A. A1 - Vollertsen, J. A1 - Westad, F. A1 - Braun, Ulrike A1 - Paul, Andrea T1 - Exploratory analysis of hyperspectral FTIR data obtained from environmental microplastics samples N2 - Hyperspectral imaging of environmental samples with infrared microscopes is one of the preferred methods to find and characterize microplastics. Particles can be quantified in terms of number, size and size distribution. Their shape can be studied and the substances can be identified. Interpretation of the collected spectra is a typical problem encountered during the analysis. The image datasets are large and contain spectra of countless particles of natural and synthetic origin. To supplement existing Analysis pipelines, exploratory multivariate data analysis was tested on two independent datasets. Dimensionality reduction with principal component analysis (PCA) and uniform manifold approximation and projection (UMAP) was used as a core concept. It allowed for improved visual accessibility of the data and created a chemical two-dimensional image of the sample. Spectra belonging to particles could be separated from blank spectra, reducing the amount of data significantly. Selected spectra were further studied, also applying PCA and UMAP. Groups of similar spectra were identified by cluster analysis using k-means, density based, and interactive manual clustering. Most clusters could be assigned to chemical species based on reference spectra. While the results support findings obtained with a ‘targeted analysis’ based on automated library search, exploratory analysis points the attention towards the group of unidientified spectra that remained and are otherwise easily overlooked. KW - Microplastics KW - FTIR KW - Exploratory analysis PY - 2020 DO - https://doi.org/10.1039/c9ay02483b VL - 12 IS - 6 SP - 781 EP - 791 PB - Royal Society of Chemistry AN - OPUS4-50396 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Goedecke, Caroline A1 - Dittmann, Daniel A1 - Eisentraut, Paul A1 - Wiesner, Yosri A1 - Schartel, Bernhard A1 - Klack, Patrick A1 - Braun, Ulrike T1 - Evaluation of thermoanalytical methods equipped with evolved gas analysis for the detection of microplastic in environmental samples N2 - Microplastic particles are currently detected in almost all environmental compartments. The results of detection vary widely, as a multitude of very different methods are used with very different requirements for analytical validity. In this work four thermoanalytical methods are compared and their advantages and limitations are discussed. One of them is thermal extraction-desorption gas chromatography mass spectrometry (TED-GC/MS), an analysis method for microplastic detection that has become established in recent years. In addition, thermogravimetric analysis coupled with Fourier-transform infrared spectroscopy (TGA-FTIR) and mass spectrometry (TGA-MS) were applied, two methods that are less common in this field but are still used in other research areas. Finally, microscale combustion calorimeter (MCC) was applied, a method not yet used for microplastic detection. The presented results are taken from a recently published interlaboratory comparison test by Becker et al. (2020). Here a reference material consisting of suspended matter and specified added polymer masses was examined, and only the results of the recoveries were presented. In the present paper, however, the results for the individual polymers are discussed in detail and individual perspectives for all instruments are shown. It was found that TED-GC/MS is the most suitable method for samples with unknown matrix and unknown, variable kinds and contents of microplastic. TGA-FTIR is a robust method for samples with known matrix and with defined kinds of microplastic. TGA-MS may offer a solution for the detection of PVC particles in the future. MCC can be used as a very fast and simple screening method for the identification of a potential microplastic load of standard polymers in unknown samples. KW - Microplastic KW - TED-GC/MS KW - TGA-MS KW - TGA-FTIR KW - MCC KW - Thermal analysis PY - 2020 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-516687 DO - https://doi.org/10.1016/j.jaap.2020.104961 VL - 152 SP - 104961 PB - Elsevier B.V. AN - OPUS4-51668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Entwicklung einer schnellen und robusten Methode für die Analytik von Mikroplastik in Wasser N2 - Vortrag im Rahmen der Preisverleihung zum Mülheimer Wasser Award 2018, Vorstellung der TED-GC-MS als Methode für Mikroplastik Analyse T2 - 3. Wasseranalytisches Seminar (MWAS 2018) CY - Mülheim a.d. Ruhr, Germany DA - 12.09.2018 KW - Mikroplastik KW - Analytik PY - 2018 AN - OPUS4-46459 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Elastomere und TPE – Gut für die Umwelt? – Kreislaufwirtschaft und Normung vereinen N2 - Der Vortrag fasst Projekte an der BAM mit Hinblick auf Elastomere und Umweltthemen zusammen. T2 - DIN Workshop: Elastomere und TPE – Gut für die Umwelt? – Kreislaufwirtschaft und Normung vereinen CY - Berlin, Germany DA - 08.08.2019 KW - Mikroplastik KW - Reifenabrieb KW - Sportböden PY - 2019 AN - OPUS4-49064 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Einfluss der Feuchtigkeit auf die Schlichte von Glasfasern während der Lagerung T2 - DEWI-OCC CY - Bremen, Germany DA - 2014-05-20 PY - 2014 AN - OPUS4-30704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Müller, Axel A1 - Becker, Roland A1 - Braun, Ulrike A1 - Dorgerloh, Ute T1 - Einfluss der Alterung auf das Sorptionsverhalten von Mikroplastik, eine Laborstudie mit BTEX und Etherverbindungen N2 - Die Präsenz von Mikroplastik in aquatischen Ökosystemen ist ein globales Problem und steht zunehmend im Fokus der Öffentlichkeit. In mehreren Studien konnten Anreicherungen hydrophober, organischer Schadstoffe an MP nachgewiesen werden. Der Einfluss des Alterungszustandes der MP-Partikel auf das Sorptionsverhalten von hydrophoben organischen Substanzen ist nicht hinreichend geklärt. Ziel der vorliegenden Arbeit war die Untersuchung des Sorptionsverhaltens von Schadstoffen mit Bedeutung für limnische Gewässer an künstlich gealterten Partikeln relevanter Polymere. Das Modell verwendete die Aromaten Benzol, Toluol, Ethylbenzol und Xylol (BTEX) sowie Etherverbindungen. Diese Substanzen sind oder waren Bestandteile in unterschiedlichen Kraftstoffen und finden sich daher in vielen aquatischen Ökosystemen weltweit. Als Sorbentien kamen teilkristallines Polypropylen (PP) und amorphes Polystyrol (PS) in Form von Industriepellets zum Einsatz. Die Pellets wurden jeweils sowohl unbehandelt als auch mittels UV-Bestrahlung künstlich gealtert verwendet und mikroskopisch sowie mittels XPS, FTIR und DSC charakterisiert. Die Alterung führte bei PS zu einer verringerten Sorptionskapazität, während bei PP keine Veränderung im Sorptionsverhalten beobachtet wurde. T2 - Wasser 2017 - Jahrestagung der Wasserchemischen Gesellschaft CY - Donaueschingen, Germany DA - 22.05.2017 KW - Mikroplastik KW - Organische Schadstoffe KW - Sorption KW - Polypropylen Polystyrol PY - 2017 SN - 978-3-947197-01-9 SP - 1 EP - 606 PB - Gesellschaft Dt. Chemiker AN - OPUS4-40447 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Perez, R.M. A1 - Sandler, J.K.W. A1 - Altstädt, V. A1 - Hoffmann, T. A1 - Pospiech, D. A1 - Ciesielski, M. A1 - Döring, M. A1 - Braun, Ulrike A1 - Knoll, Uta A1 - Schartel, Bernhard T1 - Effective halogen-free flame retardants for carbon fibre-reinforced epoxy composites N2 - DOPO-based flame retardants with tailored chemical structures are proposed for carbon fibre reinforced epoxy composites. Critical properties related to the fracture toughness are maintained, effectively allowing the use of such compounds in composites for demanding applications. KW - Fire retardancy KW - DOPO KW - Epoxy resin KW - LOI KW - UL94 PY - 2006 DO - https://doi.org/10.1007/s10853-006-0134-4 SN - 0022-2461 SN - 1573-4803 VL - 41 IS - 15 SP - 4981 EP - 4984 PB - Springer Science + Business Media B.V. CY - New York, USA AN - OPUS4-12641 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Schartel, Bernhard T1 - Effect of Red Phosphorus and Melamine Polyphosphate on the Fire Behavior of HIPS N2 - Pyrolysis and fire behavior of high impact polystyrene (HIPS) containing red phosphorus and melamine polyphosphate were investigated. The thermal and thermo-oxidative decomposition were characterized using thermogravimetry coupled with FTIR and MS, respectively. The fire behavior was monitored with a cone calorimeter using different external heat fluxes and determining the LOI. Red phosphorus reduced the heat release in HIPS due to radical trapping in the gas phase. The reduction in effective heat of combustion was accompanied by an increase of incomplete combustion products such as smoke and carbon monoxide. Melamine polyphosphate in HIPS acted in the condensed phase with barrier formation. The heat release rate was reduced, whereas the total heat evolved, smoke and carbon monoxide formation were not influenced significantly. Using both fire retardants, the resulting fire retardancy was characterized mainly by superposition. KW - HIPS KW - Red Phosphorus KW - TG-FTIR KW - TG-MS KW - Cone Calorimeter KW - LOI KW - Fire retardancy KW - Melamine Polyphosphate PY - 2005 DO - https://doi.org/10.1177/0734904105043451 SN - 0734-9041 SN - 1530-8049 VL - 23 IS - 1 SP - 5 EP - 30 PB - Sage CY - London AN - OPUS4-5287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Durability of Thermoplastic Polyurethanes (TPU) T2 - Polydays 2010 CY - Berlin, Germany DA - 2010-10-03 PY - 2010 AN - OPUS4-22107 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kömmling, Anja A1 - Chatzigiannakis, E. A1 - Beckmann, Jörg A1 - Wachtendorf, Volker A1 - von der Ehe, Kerstin A1 - Braun, Ulrike A1 - Jaunich, Matthias A1 - Schade, U. A1 - Wolff, Dietmar T1 - Discoloration Effects of High-Dose gamma-Irradiation and Long-Term Thermal Aging of (U) HMW-PE N2 - Two polyethylene types with ultra-high (UHMWPE) and high molecular weight (HMW-PE) used as neutron radiation shielding materials in casks for radioactive waste were irradiated with doses up to 600 kGy using a 60Co gammasource. Subsequently, thermal aging at 125∘C was applied for up to one year. Degradation effects in the materials were characterized using colorimetry, UV-Visspectroscopy, IR spectroscopy, and DSC. Both materials exhibited a yellowing upon irradiation.The discoloration of UHMW-PE disappeared again after thermal aging.Therefore, the yellowing is assumed to originate fromannealable color centers in the formof free radicals that are trapped in the crystalline regions of the polymer and recombine at elevated temperatures. For the antioxidantcontaining HMWPE, yellowing was observed after both irradiation and thermal aging. The color change was correlated mainly to decomposition products of the antioxidant in addition to trapped radicals as in UHMW-PE. Additionally, black spots appeared after thermal aging of HMW-PE. KW - Irradiation KW - UHMWPE KW - Colour center KW - Yellowness index PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-423992 DO - https://doi.org/10.1155/2017/1362491 SN - 1687-9422 VL - 2017 IS - Article ID 1362491 SP - 1 EP - 10 PB - Hindawi AN - OPUS4-42399 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Bajer, Kamila A1 - Braun, Ulrike T1 - Different aspects of the accelerated oxidation of polypropylene at increased pressure in an autoclave with regard to temperature, pretreatment and exposure media N2 - The aim of this study is to investigate and compare three different factors, temperature, pretreatment and exposure media, on the oxidation and aging behavior of polypropylene (PP) bulk samples in the autoclave test under increased oxygen pressure. The aging of polypropylene, in this case syringe material, was accelerated under different conditions. The samples were aged at 75°, 80° and 85 °C under pure oxygen and at 75 °C under ultrapure water. Further samples treated with 15 kGy (e-beam) were aged at 75 °C under pure oxygen. All experiments were carried out at an oxygen partial pressure of 50 bar. The different courses of aging were evaluated and compared. Color and transparency were used to assess the visual changes; weight, geometry and tensile test for the changes in technical properties; and DSC, FTIR and TDS-GC-MS to improve our physico-chemical understanding of the aging processes. The investigations showed that all factors tested influence oxidation/aging behaviour. Dry or wet exposure has no effect on aging during the induction time. However, after the point of maximum service time the degradation process of polymer changes significantly in the presence of water. The increase of aging temperature decreases the maximum service time; however a temperature higher than 80 °C changes the relative ratio of surface and bulk oxidation. The pretreatment with irradiation decreases the maximum service time further, because the irradiation partly damages the antioxidant, and the mobility of antioxidant fragments inside the polymer changes. These diffusion effects influence the relative ratio of bulk and surface oxidation of the polymer sample. KW - Autoclave test KW - Accelerated aging KW - Polypropylene KW - Electron radiation PY - 2014 DO - https://doi.org/10.1016/j.polymertesting.2014.05.006 SN - 0142-9418 VL - 37 SP - 102 EP - 111 PB - Elsevier Science CY - Amsterdam [u.a.] AN - OPUS4-30867 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wander, Lukas A1 - Lommel, Lukas A1 - Meyer, Klas A1 - Braun, Ulrike A1 - Paul, Andrea T1 - Development of a low-cost method for quantifying microplastics in soils and compost using near-infrared spectroscopy N2 - Near-infrared (NIR) spectroscopy is a promising candidate for low-cost, nondestructive, and high-throughput mass quantification of micro¬plastics in environmental samples. Widespread application of the technique is currently hampered mainly by the low sensitivity of NIR spectroscopy compared to thermo-analytical approaches commonly used for this type of analysis. This study shows how the application of NIR spectroscopy for mass quantification of microplastics can be extended to smaller analyte levels by combining it with a simple and rapid microplastic enrichment protocol. For this purpose, the widely used flotation of microplastics in a NaCl solution, accelerated by centrifugation, was chosen which allowed to remove up to 99 % of the matrix at recovery rates of 83–104 %. The spectroscopic measurements took place directly on the stainless-steel filters used to collect the extracted particles to reduce sample handling to a minimum. Partial least squares regression (PLSR) models were used to identify and quantify the extracted microplastics in the mass range of 1–10 mg. The simple and fast extraction procedure was systematically optimized to meet the requirements for the quantification of microplastics from common PE-, PP-, and PS-based packaging materials with a particle size < 1 mm found in compost or soils with high natural organic matter content (> 10 % determined by loss on ignition). Microplastics could be detected in model samples at a mass fraction of 1 mg g-1. The detectable microplastic mass fraction is about an order of magnitude lower compared to previous studies using NIR spectroscopy without additional enrichment. To emphasize the cost-effectiveness of the method, it was implemented using some of the cheapest and most compact NIR spectrometers available. KW - NIR KW - Soil KW - compost KW - PLSR PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-546405 DO - https://doi.org/10.1088/1361-6501/ac5e5f SN - 0957-0233 VL - 33 IS - 7 SP - 075801 EP - 075814 PB - IOP Publishing Ltd. CY - UK AN - OPUS4-54640 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wander, Lukas A1 - Lommel, Lukas A1 - Braun, Ulrike A1 - Meyer, Klas A1 - Paul, Andrea T1 - Development of a Low-Cost Method for Quantifying Microplastics in Soils and Compost Using Near-Infrared Spectroscopy N2 - Near-infrared (NIR) spectroscopy is a promising candidate for low-cost, nondestructive, and highthroughput mass quantification of microplastics in environmental samples. Widespread application of the technique is currently hampered mainly by the low sensitivity of NIR spectroscopy compared to thermoanalytical approaches commonly used for this type of analysis. This study shows how the application of NIR spectroscopy for mass quantification of microplastics can be extended to smaller analyte levels by combining it with a simple and rapid microplastic enrichment protocol. For this purpose, the widely used flotation of microplastics in a NaCl solution, accelerated by centrifugation, was chosen which allowed to remove up to 99 % of the matrix at recovery rates of 83–104 %. The spectroscopic measurements took place directly on the stainless-steel filters used to collect the extracted particles to reduce sample handling to a minimum. Partial least squares regression (PLSR) models were used to identify and quantify the extracted microplastics in the mass range of 1–10 mg. The simple and fast extraction procedure was systematically optimized to meet the requirements for the quantification of microplastics from common PE-, PP-, and PS-based packaging materials with a particle size < 1 mm found in compost or soils with high natural organic matter content (> 10 % determined by loss on ignition). Microplastics could be detected in model samples at a mass fraction of 1 mg g-1. The detectable microplastic mass fraction is about an order of magnitude lower compared to previous studies using NIR spectroscopy without additional enrichment. To emphasize the cost-effectiveness of the method, it was implemented using some of the cheapest and most compact NIR spectrometers available. KW - Mikroplastik KW - NIR KW - Sensor KW - Kompost KW - Multivariat PY - 2022 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-552605 DO - https://doi.org/10.1088/1361-6501/ac5e5f VL - 33 IS - 7 SP - 1 EP - 13 PB - IOP Publishing Ltd. CY - Bristol AN - OPUS4-55260 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Bannick, C.G. A1 - Szewzyk, R. A1 - Ricking, M. A1 - Schniegler, S. A1 - Obermaier, N. A1 - Barthel, A. K. A1 - Altmann, Korinna A1 - Eisentraut, Paul T1 - Development and testing of a fractionated filtration for sampling of microplastics in water N2 - A harmonization of sampling, sample preparation and detection is pivotal in order to obtain comparable data on microplastics (MP) in the environment. This paper develops and proposes a suitable sampling concept for waterbodies that considers different plastic specific properties and influencing factors in the environment. Both artificial water including defined MP fractions and the discharge of a wastewater treatment plant were used to verify the derived sampling procedure, sample preparation and the subsequent analysis of MP using thermal extraction-desorption gas chromatography - mass spectrometry (TED-GC-MS). A major finding of this paper is that an application of various particle size classes greatly improves the practical handling of the sampling equipment. Size classes also enable the TED-GC-MS to provide any data on the MP size distribution, a substantial sampling property affecting both the necessary sampling volume and the optimal sampling depth. In the artificial water with defined MP fractions, the recovery rates ranged from 80 to 110%, depending on the different MP types and MP size classes. In the treated wastewater, we found both Polyethylene and polystyrene in different size classes and quantities. KW - Microplastics KW - Sampling KW - Sampling techniques KW - Water PY - 2019 DO - https://doi.org/10.1016/j.watres.2018.10.045 SN - 0043-1354 VL - 149 SP - 650 EP - 658 PB - Elsevier AN - OPUS4-47200 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Determination of tire wear particles based on elemental composition N2 - In this presentation the use of ICP-MS for the analysis of tire wear particles in environmental samples is presented. T2 - Wassertagung der GdCh CY - Papenburg, Germany DA - 07.05.2018 KW - ICP-MS KW - Mikroplastik KW - Analytik KW - Reifenabrieb PY - 2018 AN - OPUS4-45201 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Detektion von Mikroplastik in Flaschenwasser mittels thermoanalytischer Verfahren N2 - Im Vortrag wird ein Messfiltertiegel als Zusatztool für die TED-GC/MS vorgestellt, welcher für die Probenaufbereitung von kleinen Partikelfrachten oder kleinen Partikelgrößen genutzt werden kann. Er ist Filtereinheit und Messtiegel in einem, wodurch Verluste bei der Überführung der Probe in das Messgefäß sowie Kontaminationen vermindert werden. Das beispiel ist hier die Filtration von Flaschenwasser mit anschließender Detektion mit der TED-GC/MS. T2 - BVL_Kick-off Meeting "Mikroplastik in Lebensmitteln" CY - Online meeting DA - 03.12.2020 KW - Mikroplastik KW - TED-GC/MS KW - Kleine Partikel KW - Geringe Partikelfrachten KW - Mikroplastik-Massengehalte PY - 2020 AN - OPUS4-51794 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Detection of microplastics using thermoanalytical methods  N2 - The presentation summarized the use of thermal analytic methods for the detection of microplastics. T2 - Workshop State of teh art of anylatical methodes for reliable detection of micro- and nanoplastics CY - Ispra, Italy DA - 13.05.2019 KW - microplastics, sampling, sampling techniques, water PY - 2019 AN - OPUS4-48119 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Deußing, G. A1 - Dümichen, Erik A1 - Braun, Ulrike T1 - Der Fänger im Spülgas N2 - Durch die intelligente Anbindung an eine in der GC/MS gängige Extraktionstechnik (SBSE) lassen sich Zersetzungsprodukte der thermogravimetrischen Analyse (TGA) von Polymeren auf effiziente Weise anreichern, anschließend trennen und sicher identifizieren. KW - Polymeranalytik KW - Thermische Extraktion PY - 2015 UR - http://www.laborpraxis.vogel.de/so-erweitern-sie-die-moeglichkeiten-der-tga-a-490995/index2.html UR - https://files.vogel.de/vogelonline/vogelonline/issues/6773.pdf SN - 0344-1733 VL - 39 IS - 6 SP - 24 EP - 27 PB - Vogel Business Media AN - OPUS4-42149 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Ressnig, A. A1 - Corbiere, T. A1 - Lunkenbein, T. A1 - Braun, Ulrike A1 - Willinger, M. G. A1 - Antonietti, M. T1 - Decomposition synthesis of tuneable, macroporous carbon foams from crystalline precursors via in situ templating N2 - A flexible, sustainable, one-step thermal decomposition route for the synthesis of hierarchical, heteroatom doped carbon foams is presented. Task-specific semi-organic crystals combine functions for three different purposes: the carbon and heteroatom source, a foaming agent (CO2) and an in situ generable template (NaCl). Insights to the decomposition pathway were gained through FTIR/MS coupled TGA and an ultrafast out-of-furnace heating procedure and the products were analysed with (HR)SEM/TEM, EELS, FTIR, and N2 sorption. The resulting macroporous carbon foams are excellent supports for metallic nanoparticles due to their hierarchical structure, high surface area and tuneable heteroatom contents. This was demonstrated for catalytically active copper or the magnetic CoNi alloy for water purification. KW - macroporous carbon KW - thermal decomposition KW - synthesize heteroatom KW - in situ template (NaCl) PY - 2014 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-318641 DO - https://doi.org/10.1039/c4ta03646h SN - 2050-7496 SN - 2050-7488 VL - 2 IS - 42 SP - 18076 EP - 18081 PB - RSC CY - London [u.a.] AN - OPUS4-31864 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Decomposition pathways in the pyrolysis zone: A key to understand fire retardancy mechanisms T2 - FRPM07 CY - Bolton, England DA - 2007-07-04 PY - 2007 AN - OPUS4-15051 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Kittner, Maria A1 - Eisentraut, Paul A1 - Dittmann, Daniel A1 - Braun, Ulrike T1 - Decomposability versus detectability: First validation of TED‐GC/MS for microplastic detection in different environmental matrices N2 - A fast method for microplastic detection is thermal extraction desorption‐gas chromatography/mass spectrometry (TED‐GC/MS), which uses polymer‐specific thermal decomposition products as marker compounds to determine polymer mass contents in environmental samples. So far, matrix impacts of different environmental matrices on TED‐GC/MS performance had not yet been assessed systematically. Therefore, three solid freshwater matrices representing different aquatic bodies with varying organic matter contents were spiked with a total of eight polymers. Additionally, for the first time, the two biodegradable polymers polybutylene adipate terephthalate (PBAT) and polylactide (PLA) were analysed using TED‐GC/MS. The methodological focus of this work was on detectability, quality of signal formation as well as realisation of quantification procedures and determination of the limit of detection (LOD) values. Overall, TED‐GC/MS allowed the unambiguous detection of the environmentally most relevant polymers analysed, even at low mass contents: 0.02 wt% for polystyrene (PS), 0.04 wt% for the tyre component styrene butadiene rubber (SBR) and 0.2 wt% for polypropylene (PP), polyethylene (PE) and PBAT. Further, all obtained LOD values were increased in all matrices compared to the neat polymer without matrix. The LOD of the standard polymers were increased similarly (PS: 0.21–0.34 μg, SBR: 0.27–0.38 μg, PP: 0.32–0.36 μg, PMMA: 0.64–1.30 μg, PET: 0.90–1.37 μg, PE: 3.80–6.99 μg) and their decompositions by radical scission processes were not significantly influenced by the matrices. In contrast, matrixspecific LOD increases of both biodegradable polymers PBAT (LOD: 1.41–7.18 μg) and PLA (0.84–20.46 μg) were observed, probably due to their hetero‐functional character and interactions with the matrices. In conclusion, the TED‐GC/MS performance is not solely determined by the type of the polymers but also by the composition of the matrix. KW - TED-GC/MS KW - Microplastic KW - Freshwater matrices KW - Gas chromatography KW - Mass spectrometry PY - 2023 DO - https://doi.org/10.1002/appl.202200089 SN - 2702-4288 VL - 2 IS - 3 SP - 1 EP - 12 PB - Wiley-VCH CY - Weinheim AN - OPUS4-57419 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Cure Monitoring Using Infrared Spectroscopy T2 - Wissenschaftskolloquium "Nanotechnologie für Kunststoffverbunde CY - Braunschweig, Germany DA - 2014-09-30 PY - 2014 AN - OPUS4-31584 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Brademann-Jock, Kerstin A1 - Stark, Wolfgang T1 - Cure monitoring of epoxy films by heatable in situ FTIR analysis: Correlation to composite parts N2 - The curing mechanism of an epoxy film containing dicyandiamide (DICY) and an epoxy formulation based on diglycidyl ether of Bisphenol A (DGEBA) polymer was studied as a function of various temperature programs. The investigation was performed in situ, using a thin film of the epoxy mixture on a silicon wafer substrate in a heatable transmission tool of a FTIR spectrometer. Based on these model-curing experiments, a major curing mechanism was proposed, taking into account the appearance, the decrease, and the development of characteristic bands at various temperatures. The conclusions of the model curing were correlated to FTIR measurements on a real, 50-mm-thick glass fiber reinforced component composite part from a technical process. It could be shown that characteristic bands that develop at curing temperatures above 150°C appear especially in the center of the thick sample. From the chemical or molecular point of view, this demonstrates the established technician's understanding that temperature control inside a large-scale fiber composite of, for example, aircraft, wind-turbine, automotive applications component is of major importance. KW - Crosslinking KW - Resins KW - Spectroscopy KW - Thermosets KW - Thermal properties PY - 2014 DO - https://doi.org/10.1002/APP.39832 SN - 0021-8995 SN - 1097-4628 VL - 131 IS - 3 SP - 39832, 1 EP - 10 PB - Wiley InterScience CY - Hoboken, NJ AN - OPUS4-30716 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Erdmann, Maren A1 - Trappe, Volker A1 - Sturm, Heinz A1 - Braun, Ulrike A1 - Dümichen, Erik T1 - Cure conversion of structural epoxies by cure state analysis and in situ cure kinetics using nondestructive NIR spectroscopy N2 - Non-isothermal heating rate kinetics was applied to two epoxy resin systems. In situ near-infrared (NIR) measurements were taken with a heatable NIR cell which allowed the cure to be monitored by characteristic absorption bands. An autocatalyzed reaction of the nth order was shown to describe the epoxy conversion curves. Differential Scanning Calorimetry (DSC) was used as a complementary method. The kinetic models developed by both NIR and DSC are in good accordance with experimental epoxy conversion in the in situ NIR setup for single and multiple cure temperature ramps. A linear calibration curve of the characteristic absorption bands of epoxy normalized to aromatic vibrations was introduced. The curing degree of structural epoxies that were cured according to an industrial temperature cure profile was determined by NIR using the calibration curve. The epoxy conversions of the structural components showed good agreement with the experimental in situ NIR. Several degrees of cure for structural specimens were evaluated by NIR and residual reaction enthalpy by DSC. We present the non-destructive NIR spectroscopy as an alternative to determine fast and non-destructive epoxy conversion, particularly suitable for high degrees of cure on structural components. KW - Epoxy resin KW - Curing kinetics KW - In situ near-infrared (NIR) spectroscopy KW - Differential scanning calorimetry (DSC) PY - 2017 UR - http://www.sciencedirect.com/science/article/pii/S0040603117300205 DO - https://doi.org/10.1016/j.tca.2017.01.010 SN - 0040-6031 SN - 1872-762X VL - 650 SP - 8 EP - 17 PB - Elsevier B.V. AN - OPUS4-39123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Schartel, Bernhard A1 - Braun, Ulrike T1 - Comprehensive fire behaviour assessment of polymeric materials based on cone calorimeter investigations N2 - Bench scale performance based cone calorimeter investigations were conducted on glass fibre reinforced polyamide 66 (PA-66) and high impact polystyrene (HIPS) materials. Red phosphorus and magnesium hydroxide were used as fire retardants. Dilution, heat sink, barrier and charring mechanisms are considered to be active in the condensed phase. Dilution, cooling and flame poisoning mechanisms are discussed for the gas phase. Cone calorimeter data are used to give a comprehensive fire behaviour assessment in terms of the propensity to cause a quick growing fire and of the propensity to cause a fire of long duration. The external heat flux is varied between 30 and 75 kW/m2 so that the results for combustion behaviour and flame retardancy, respectively, are valid for different fire scenarios and fire tests. Results on the intrinsic contribution of the steady heat release rate per unit area reveal information about the flammability behaviour. UL 94 results are predicted in close correspondence to UL 94 experiments. PY - 2003 DO - https://doi.org/10.1515/epoly.2003.3.1.177 SN - 1618-7229 IS - 013 SP - 1 EP - 14 PB - De Gruyter CY - [S.l.] AN - OPUS4-15852 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Elert, Anna Maria A1 - Becker, Roland A1 - Dümichen, Erik A1 - Eisentraut, Paul A1 - Falkenhagen, Jana A1 - Sturm, Heinz A1 - Braun, Ulrike T1 - Comparison of different methods for MP detection: What can we learn from them, and why asking the right question before measurments matters? N2 - In recent years, an increasing trend towards investigating and monitoring the contamination of the environment by microplastics (MP) (plastic pieces < 5 mm) has been observed worldwide. Nonetheless, a reliable methodology that would facilitate and automate the monitoring of MP is still lacking. With the goal of selecting practical and standardized methods, and considering the challenges in microplastics detection, we present here a critical evaluation of two vibrational spectroscopies, Raman and Fourier transform infrared (FTIR) spectroscopy, and two extraction methods: thermal extraction desorption gas chromatography mass spectrometry (TED-GC-MS) and liquid extraction with subsequent size exclusion chromatography (SEC) using a soil with known contents of PE, PP, PS and PET as reference material. The obtained results were compared in terms of measurement time, technique handling, detection limits and requirements for sample preparation. The results showed that in designing and selecting the right methodology, the scientific question that determines what needs to be understood is significant, and should be considered carefully prior to analysis. Depending on whether the object of interest is quantification of the MP particles in the sample, or merely a quick estimate of sample contamination with plastics, the appropriate method must be selected. To obtain overall information about MP in environmental samples, the combination of several parallel approaches should be considered. KW - Microplastics KW - FTIR imaging KW - Raman imaging KW - TED-GC-MS KW - SEC KW - Analysis and identification PY - 2017 DO - https://doi.org/10.1016/j.envpol.2017.08.074 SN - 0269-7491 SN - 1873-6424 VL - 231 IS - 2 SP - 1256 EP - 1264 PB - Elsevier AN - OPUS4-42157 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike A1 - Dümichen, Erik A1 - Barthel, Anne-Kathrin A1 - Bannick, Claus Gerhard T1 - Charakterisierung von Mikroplastik Partikeln aus Umweltproben N2 - Durch den stetig steigenden Einsatz von Plastikprodukten sind unerwünschte Kunststofffunde in verschiedenen Umweltmatrices mittlerweile allgegenwärtig. Besonderes Interesse erfahren die Kunststoffpartikel von einer Größe kleiner 5 mm, sogenannte Mikroplastik (MP) Partikel. Es werden aktuell Risiken für Mensch und Umwelt diskutiert, die von diesen Partikeln ausgehen. T2 - Wasser 2016 - Jahrestagung der Wasserchemischen Gesellschaft CY - Bamberg, Deutschland DA - 02.05.2016 KW - Mikroplastik KW - Polymere KW - Polyethylen (PE) KW - Polystyrol (PS) KW - Poly(ethylenterephthalat) (PET) PY - 2016 SN - 978-3-936028-94-2 SP - 74 EP - 76 PB - Wasserchemische Gesellschaft CY - Mülheim an der Ruhr, Germany AN - OPUS4-36782 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Charakterisierung von Mikroplastik Partikeln aus Umweltproben N2 - Durch den stetig steigenden Einsatz von Plastikprodukten sind unerwünschte Kunststofffunde in verschiedenen Umweltmatrices mittlerweile allgegenwärtig. Besonderes Interesse erfahren die Kunststoffpartikel von einer Größe kleiner 5 mm, sogenannte Mikroplastik (MP) Partikel und deren ausgehende Risiken auf Mensch und Umwelt T2 - Wasser 2016 - Jahrestagung der Wasserchemischen Gesellschaft CY - Bamberg, Germany DA - 02.05.2016 KW - Mikroplastik KW - Polymere PY - 2016 AN - OPUS4-36785 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Klöckner, P. A1 - Seiwert, B. A1 - Eisentraut, Paul A1 - Braun, Ulrike A1 - Reemtsma, T. A1 - Wagner, S. T1 - Characterization of tire and road wear particles from road runoffindicates highly dynamic particle properties N2 - Tire and road wear particles (TRWPs) are heteroagglomerates of tire rubber and other particles deposited on the road surface and one of the main contributors to non-exhaust emissions of automobile traffic. In this study, samples from road environments were analyzed for their TRWP contents and concentra- tions of eight organic tire constituents. TRWP concentrations were determined by quantifying Zn in the density fraction < 1.9 g/cm ³and by thermal extraction desorption-gas chromatography-mass spectrometry (TED-GC/MS) and the concentrations ranged from 3.7 to 480 mg TRWP/g. Strong and statistically signif- icant correlations with TRWPs were found for 2-hydroxybenzothiazole and 2-aminobenzothiazole, indi- cating that these substances may be suitable markers of TRWPs. The mass distribution of TRWPs in road dust suggests that the main mass fraction formed on roads consists of coarse particles ( > 100 μm). Data for a sedimentation basin indicate that the fine fraction ( < 50 μm) is preferentially transported by road runoffinto receiving waters. The size distribution and density data of TRWP gathered by three different quantitation approaches also suggest that aging of TRWPs leads to changes in their particle density. An improved understanding of the dynamics of TRWP properties is essential to assess the distribution and dissipation of this contaminant of emerging concern in the environment. KW - Tire Wear KW - Density separation KW - Microplastic KW - Urban PY - 2020 DO - https://doi.org/10.1016/j.watres.2020.116262 VL - 185 SP - 116262 PB - Elsevier Ltd. AN - OPUS4-51256 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Seefeldt, Henrik A1 - Braun, Ulrike T1 - Burning behavior of wood-plastic composite decking boards in end-use conditions: the effects of geometry, material composition, and moisture N2 - In this study, we investigated the basic knowledge necessary to develop flame-retarded wood–plastic composite (WPC) materials by focusing on decking boards. Therefore, the respective effects of geometry, material composition, and moisture were studied by performing cone calorimetric measurements. Using hollow-shaped geometries removes combustible material and reduces the fire load but simultaneously increases fire propagation. The best results were achieved by using high-wood contents. The addition of talc can reduce the intensity of burning. Moisture also has a positive effect on burning behavior. Apart from the well-known mechanism of water, a change was observed in the resultant residue. KW - WPC KW - Wood-plastic composite KW - Cone calorimeter KW - Decking boards PY - 2012 DO - https://doi.org/10.1177/0734904111423488 SN - 0734-9041 SN - 1530-8049 VL - 30 IS - 1 SP - 41 EP - 54 PB - Sage CY - London AN - OPUS4-25357 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Topolniak, Ievgeniia A1 - Hodoroaba, Vasile-Dan A1 - Pfeifer, Dietmar A1 - Braun, Ulrike A1 - Sturm, Heinz T1 - Boehmite Nanofillers in Epoxy Oligosiloxane Resins: Influencing the Curing Process by Complex Physical and Chemical Interactions N2 - In this work, a novel boehmite (BA)-embedded organic/inorganic nanocomposite coating based on cycloaliphatic epoxy oligosiloxane (CEOS) resin was fabricated applying UV-induced cationic polymerization. The main changes of the material behavior caused by the nanofiller were investigated with regard to its photocuring kinetics, thermal stability, and glass transition. The role of the particle surface was of particular interest, thus, unmodified nanoparticles (HP14) and particles modified with p-toluenesulfonic acid (OS1) were incorporated into a CEOS matrix in the concentration range of 1–10 wt.%. Resulting nanocomposites exhibited improved thermal properties, with the glass transition temperature (Tg) being shifted from 30 °C for unfilled CEOS to 54 °C (2 wt.% HP14) and 73 °C (2 wt.% OS1) for filled CEOS. Additionally, TGA analysis showed increased thermal stability of samples filled with nanoparticles. An attractive interaction between boehmite and CEOS matrix influenced the curing. Real-time infrared spectroscopy (RT-IR) experiments demonstrated that the epoxide conversion rate of nanocomposites was slightly increased compared to neat resin. The beneficial role of the BA can be explained by the participation of hydroxyl groups at the particle surface in photopolymerization processes and by the complementary contribution of p-toluenesulfonic acid surface modifier and water molecules introduced into the system with nanoparticles. KW - Real-time infrared spectroscopy KW - Boehmite KW - Nanocomposite KW - Cationic photocuring KW - Cycloaliphatic epoxy oligosiloxane KW - Epoxy conversion degree PY - 2019 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-479628 DO - https://doi.org/10.3390/ma12091513 VL - 12 IS - 9 SP - 1513 PB - MDPI AN - OPUS4-47962 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Beständigkeit von Polymeren: Verständnis molekularer Mechanismen T2 - JKU, Institute of Polymeric Materials and Testing, Seminar lecture CY - Linz, Austria DA - 2013-05-29 PY - 2013 AN - OPUS4-28603 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Beständigkeit von Polymeren: Aushärtungs- und Degradationskontrolle T2 - Workshop am Fraunhofer CSP CY - Halle (Saale), Germany DA - 2012-11-06 PY - 2012 AN - OPUS4-26917 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Beständigkeit von Medizinprodukten T2 - Life Science Day 2012 CY - Berlin, Germany DA - 2012-06-08 PY - 2012 AN - OPUS4-26013 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Schartel, Bernhard A1 - Bartholmai, Matthias A1 - Braun, Ulrike ED - Le Bras, M. T1 - Barrier effects for the fire retardancy of polymers T2 - 9th European Meeting on Fire Retardancy and Protection of Materials CY - Lille, France DA - 2003-09-15 KW - Fire retardancy KW - Nanocomposites KW - Red Phosphorus KW - Mg(OH)2 KW - Cone Calorimeter KW - LOI PY - 2005 SN - 0-85404-582-1 VL - 9 SP - 264 EP - 275 PB - Royal Society of Chemistry CY - Cambridge AN - OPUS4-7377 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dümichen, Erik A1 - Eisentraut, Paul A1 - Celina, M. A1 - Braun, Ulrike T1 - Automated thermal extraction-desorption gas chromatography mass spectrometry: A multifunctional tool for comprehensive characterization of polymers and their degradation products N2 - The TED-GC-MS analysis is a two-step method. A sample is first decomposed in a thermogravimetric analyzer (TGA) and the gaseous decomposition products are then trapped on a solid-phase adsorber. Subsequently, the solid-phase adsorber is analyzed with thermal desorption gas chromatography mass spectrometry (TDU-GC-MS). This method is ideally suited for the analysis of polymers and their degradation processes. Here, a new entirely automated System is introduced which enables high sample throughput and reproducible automated fractioned collection of decomposition products. Strengths and limitations of the system configuration are elaborated via three examples focused on practical challenges in materials analysis and identification: i) separate analysis of the components of a wood-plastic-composite material, ii) quantitative determination of weight concentration of the constituents of a polymer blend and iii) quantitative analysis of model samples of microplastics in suspended particulate matter. KW - Thermal extraction-desorption gas chromatography mass spectrometry KW - Analysis KW - Polymers KW - Microplastics KW - Automation PY - 2019 DO - https://doi.org/10.1016/j.chroma.2019.01.033 VL - 1592 SP - 133 EP - 142 PB - Elsevier CY - Amsterdam AN - OPUS4-48287 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wesch, Ch. A1 - Elert, Anna Maria A1 - Wörner, M. A1 - Braun, Ulrike A1 - Klein, R. A1 - Paulus, M. T1 - Assuring quality in microplastic monitoring: About the value of clean-air devices as essentials for verified data N2 - Avoiding aerial microfibre contamination of environmental samples is essential for reliable analyses when it comes to the detection of ubiquitous microplastics. Almost all laboratories have contamination problems which are largely unavoidable without investments in clean-air devices. Therefore, our study supplies an approach to assess background microfibre contamination of samples in the laboratory under particle-free air conditions. We tested aerial contamination of samples indoor, in a mobile laboratory, within a laboratory fume hood and on a clean bench with particles filtration during the examining process of a fish. The used clean bench reduced aerial microfibre contamination in our laboratory by 96.5%. This highlights the value of suitable clean-air devices for valid microplastic pollution data. Our results indicate, that pollution levels by microfibres have been overestimated and actual pollution levels may be many times lower. Accordingly, such clean-air devices are recommended for microplastic laboratory applications in future research work to significantly lower error rate KW - Microplastics KW - FTIR KW - Quality KW - Environmental Science KW - Biological techniques PY - 2017 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-412402 DO - https://doi.org/10.1038/s41598-017-05838-4 SN - 2045-2322 VL - 7 SP - Article 5424, 1 EP - 8 PB - Nature AN - OPUS4-41240 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dümichen, Erik A1 - Braun, Ulrike A1 - Senz, R. A1 - Fabian, G. A1 - Sturm, Heinz T1 - Assessment of a new method for the analysis of decomposition gases of polymers by a combining thermogravimetric solid-phase extraction and thermal desorption gas chromatography mass spectrometry N2 - For analysis of the gaseous thermal decomposition products of polymers, the common techniques are thermogravimetry, combined with Fourier transformed infrared spectroscopy (TGA–FTIR) and mass spectrometry (TGA–MS). These methods offer a simple approach to the decomposition mechanism, especially for small decomposition molecules. Complex spectra of gaseous mixtures are very often hard to identify because of overlapping signals. In this paper a new method is described to adsorb the decomposition products during controlled conditions in TGA on solid-phase extraction (SPE) material: twisters. Subsequently the twisters were analysed with thermal desorption gas chromatography mass spectrometry (TDS–GC–MS), which allows the decomposition products to be separated and identified using an MS library. The thermoplastics polyamide 66 (PA 66) and polybutylene terephthalate (PBT) were used as example polymers. The influence of the sample mass and of the purge gas flow during the decomposition process was investigated in TGA. The advantages and limitations of the method were presented in comparison to the common analysis techniques, TGA–FTIR and TGA–MS. KW - TDS-GC-MS KW - TGA-FTIR KW - TGA-MS KW - Degradation KW - Polymer KW - Solid-phase extraction PY - 2014 DO - https://doi.org/10.1016/j.chroma.2014.05.057 SN - 0021-9673 VL - 1354 SP - 117 EP - 128 PB - Elsevier B.V. CY - Amsterdam AN - OPUS4-31046 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wawrzyn, Eliza A1 - Schartel, Bernhard A1 - Ciesielski, M. A1 - Kretzschmar, B. A1 - Braun, Ulrike A1 - Döring, M. T1 - Are novel aryl phosphates competitors for bisphenol A bis(diphenyl phosphate) in halogen-free flame-retarded polycarbonate/acrylonitrile-butadiene-styrene blends? N2 - The reactivity of the flame retardant and its decomposition temperature control the condensed-phase action in bisphenol A polycarbonate/acrylonitrile–butadiene–styrene/polytetrafluoroethylene (PC/ABSPTFE) blends. Thus, to increase charring in the condensed phase of PC/ABSPTFE + aryl phosphate, two halogen-free flame retardants were synthesized: 3,3,5-trimethylcyclohexylbisphenol bis(diphenyl phosphate) (TMC-BDP) and bisphenol A bis(diethyl phosphate) (BEP). Their performance is compared to bisphenol A bis(diphenyl phosphate) (BDP) in PC/ABSPTFE blend. The comprehensive study was carried out using thermogravimetry (TG); TG coupled with Fourier transform infrared spectrometer (TG-FTIR); the Underwriters Laboratory burning chamber (UL 94); limiting oxygen index (LOI); cone calorimeter at different irradiations; tensile, bending and heat distortion temperature tests; as well as rheological studies and differential scanning calorimeter (DSC). With respect to pyrolysis, TMC-BDP works as well as BDP in the PC/ABSPTFE blend by enhancing the cross-linking of PC, whereas BEP shows worse performance because it prefers cross-linking with itself rather than with PC. As to its fire behavior, PC/ABSPTFE + TMC-BDP presents results very similar to PC/ABSPTFE + BDP; the blend PC/ABSPTFE + BEP shows lower flame inhibition and higher total heat evolved (THE). The UL 94 for the materials with TMC-BDP and BDP improved from HB to V0 for specimens of 3.2 mm thickness compared to PC/ABSPTFE and PC/ABSPTFE + BEP; the LOI increased from around 24% up to around 28%, respectively. BEP works as the strongest plasticizer in PC/ABSPTFE, whereas the blends with TMC-BDP and BDP present the same rheological properties. PC/ABSPTFE + TMC-BDP exhibits the best mechanical properties among all flame-retarded blends. KW - Polycarbonate (PC) KW - Aryl phosphate KW - Flame retardancy KW - Pyrolysis KW - PC/ABS PY - 2012 DO - https://doi.org/10.1016/j.eurpolymj.2012.06.015 SN - 0014-3057 SN - 1873-1945 VL - 48 IS - 9 SP - 1561 EP - 1574 PB - Elsevier CY - Oxford AN - OPUS4-26292 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dümichen, Erik A1 - Javdanitehran, M. A1 - Erdmann, Maren A1 - Trappe, Volker A1 - Sturm, Heinz A1 - Braun, Ulrike A1 - Ziegmann, G. T1 - Analyzing the network formation and curing kinetics of epoxy resins by in situ near-infrared measurements with variable heating rates N2 - Near-infrared spectroscopy (NIR) turned out to be well suited for analyzing the degree of cure for epoxy systems. In contrast to dynamic scanning calorimetry (DSC), where the released heat of reaction determines the degree of epoxy conversion indirectly, NIR spectroscopy is able to determine the conversion directly by analyzing structural changes. Therefore, a new heatable NIR cell was equipped with an integrated thermocouple, which enables the real sample temperature to be controlled and monitored in situ during epoxy curing. Dynamic scans at different heating rates were used for kinetic modelling, to define kinetic parameters and to predict real curing processes. The kinetic models and their parameters were validated with an isothermal and a more complex multi-step curing scenario. Two available commercial epoxy systems based on DGEBA were used with an anhydride and with an amine hardener. NIR results were compared with DSC data. The simulated conversion predicted with a model fitted on the basis of NIR and DSC dynamic scans showed good agreement with the conversion measured in the isothermal curing validation test. Due to the proven reliability of NIR in measuring the reaction progress of curing, it can be considered a versatile measurement system for in situ monitoring of component production in the automotive, aerospace and wind energy sectors. KW - Epoxy resins KW - Curing kinetics KW - Near-infrared spectroscopy KW - DSC PY - 2015 DO - https://doi.org/10.1016/j.tca.2015.08.008 SN - 0040-6031 SN - 1872-762X VL - 616 SP - 49 EP - 60 PB - Elsevier CY - Amsterdam AN - OPUS4-34187 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Analytik von Mikroplastik mittels Thermoextraktion Desorption Gas Chromatographie Massen Spektrometrie (TED-GC-MS): Nun auch die Luft? N2 - Der Vortrag gibt eine Überblick über die Messung von Mikroplastik mittels TED-GC-MS mit speziellem Fokus auf Luftgetragene Partikel T2 - Odour and Emissions of Plastic Materials CY - Kassel, Germany DA - 19.03.2019 KW - Mikroplastik KW - Standarisierung KW - Analytik PY - 2019 AN - OPUS4-47583 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Analytik von Mikroplastik mittels TED-GC-MS N2 - Der Vortrag stellt spektroskopische und neue thermoanalytische Verfahren zum Nachweis von Mikroplastik dar. Ein spezieller Focus ist auf der Anwendung edr Verfahren für terrestrische Proben. T2 - Fachgespräch Feststoffuntersuchungen 2018 CY - Essen Werden, Germany DA - 05.03.2018 KW - Mikroplastik KW - Analytik KW - GC-MS KW - Thermische Analyse PY - 2018 AN - OPUS4-44525 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Analytik von Mikroplastik mit thermo-analytischen Verfahren N2 - Überblick über laufende Ergebnisse zu der Verwendung von Thermo-analytischen Verfahren zum Nachweis von Mikroplastik in komplexen Umweltproben. T2 - 2. Mülheimer Wasseranalytisches Seminar CY - Mülheim, Germany DA - 14.09.2017 KW - Mikroplastik KW - Polymere KW - Thermische Analyse KW - Biogasanlage KW - Klärschlamm PY - 2016 AN - OPUS4-38931 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Analytik von Mikroplastik in komplexen Umweltproben N2 - Der Sachstand zur Analytik von Mikroplastik in Umweltproben wird dargestellt. T2 - Fachausstellung Kunststoffanalytik CY - Lüdenscheid, Germany DA - 04.12.2019 KW - TED-GC-MS KW - Mikroplastik KW - Analytik PY - 2019 AN - OPUS4-50005 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Analytik von Mikroplastik - Verfahren-Ergebnisse-Harmonisierung N2 - Die zunehmenden Nachweise von Kunststoffen in verschiedenen Umweltmedien erfahren in den letzten Jahren weltweit ein zunehmendes wissenschaftliches, gesellschaftliches und politisches Interesse. Besondere Aufmerksamkeit erfahren Kunststoffpartikel von 1-1.000 µm, sogenanntes Mikroplastik. Es wurde mittlerweile in Wasser, Böden, Luft und Biota nachgewiesen. Obwohl die Wirkungen auf die natürlichen Umweltfunktionen noch unklar sind und kontrovers diskutiert werden, ist allein durch die ubiquitäre Präsenz eine systematische Erfassung von Eintragsquellen und Verbleib der Partikel über alle Umweltmedien notwendig, um Maßnahmen zur Reduktion der Einträge zu veranlassen. Für eine zuverlässige Erfassung sind medienübergreifende Verfahren zu entwickeln, welche die drei analytischen Schritte, Probennahme, Probenaufbereitung und Detektion beinhalten. Die Verfahren adressieren unterschiedliche Zielgruppen, welche verschiedene analytische Informationen fordern. Für die akademische Bewertung werden Verfahren mit hohem analytischen Aufwand favorisiert, welche möglichst detaillierte Information über Partikelsorte, -größe, -zahl und -oberflächenbeschaffenheit geben. Im Gegensatz dazu, fordern Anwender aus der Praxis schnelle und einfache Monitoring Verfahren, welche die Bestimmung eines Massengehaltes, bzw. eines Grenzwertes zulassen. Allen ist gemeinsam, dass ein hoher interdisziplinärer Anspruch besteht, der sowohl technische Voraussetzungen zur repräsentativen Probennahme und die Limitationen von Detektionsverfahren berücksichtigt, als auch die Fachkompetenz von Biologen, Umweltwissenschaften, Analytiker und Polymerwissenschaftler einschließt. Verfahren zum Mikroplastiknachweis müssen auch verschieden Proben mit sehr unterschiedlichen Gehalten an natürlicher Matrix gerecht werden. So müssen allein für Wasser Verfahren entwickelt werden, die Mikroplastik verschiedener Form (sphärische Partikel, komplexe Bruchstücke, Fasern) aus Medien mit sehr variablen Partikelanteil (u.a. Trinkwasser, Oberflächenwasser, Abwasser) repräsentativ erfassen, sowie schnell und kostengünstig sind – einschließlich der notwendigen Probenaufbereitung. Die jeweiligen Detektionsverfahren müssen z.B. einzelne Partikel oder integrale Gehalte über drei Dekadenklassen für thermoplastische und insbesondere auch elastomere Partikelsorten erfassen können. T2 - GDCh Wissenschaftsforum CY - Aachen, Germany DA - 15.09.2019 KW - Mikroplastik KW - Analytik KW - TED-GC-MS PY - 2019 AN - OPUS4-49068 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Analytik von Mikroplastik - Verfahren-Ergebnisse-Harmonisierung N2 - Die zunehmenden Nachweise von Kunststoffen in verschiedenen Umweltmedien erfahren in den letzten Jahren weltweit ein zunehmendes wissenschaftliches, gesellschaftliches und politisches Interesse. Besondere Aufmerksamkeit erfahren Kunststoffpartikel von 1-1.000 µm sogenanntes Mikroplastik. Es wurde mittlerweile in Wasser, Böden, Luft und Biota nachgewiesen. Obwohl die Wirkungen auf die natürlichen Umweltfunktionen noch unklar sind und kontrovers diskutiert werden, ist allein durch die ubiquitäre Präsenz eine systematische Erfassung von Eintragsquellen und Verbleib der Partikel über alle Umweltmedien notwendig, um Maßnahmen zur Reduktion der Einträge zu veranlassen. Für eine zuverlässige Erfassung sind medienübergreifende Verfahren zu entwickeln, welche die drei analytischen Schritte, Probennahme, Probenaufbereitung und Detektion beinhalten. Die Verfahren adressieren unterschiedliche Zielgruppen, welche verschiedene analytische Informationen fordern. Für die akademische Bewertung werden Verfahren mit hohem analytischen Aufwand favorisiert, welche möglichst detaillierte Information über Partikelsorte, -größe, -zahl und -oberflächenbeschaffenheit geben. Im Gegensatz dazu, fordern Anwender aus der Praxis schnelle und einfache Monitoring Verfahren, welche die Bestimmung eines Massengehaltes, bzw. eines Grenzwertes zulassen. Allen ist gemeinsam, dass ein hoher interdisziplinärer Anspruch besteht, der sowohl technische Voraussetzungen zur repräsentativen Probennahme und die Limitationen von Detektionsverfahren berücksichtigt, als auch die Fachkompetenz von Biologen, Umweltwissenschaften, Analytiker und Polymerwissenschaftler einschließt. Verfahren zum Mikroplastiknachweis müssen auch verschieden Proben mit sehr unterschiedlichen Gehalten an natürlicher Matrix gerecht werden. So müssen allein für Wasser Verfahren entwickelt werden, die Mikroplastik verschiedener Form (sphärische Partikel, komplexe Bruchstücke, Fasern) aus Medien mit sehr variablen Partikelanteil (u.a. Trinkwasser, Oberflächenwasser, Abwasser) repräsentativ erfassen sowie schnell und kostengünstig sind – einschließlich der notwendigen Probenaufbereitung. Die jeweiligen Detektionsverfahren müssen z.B. einzelne Partikel oder integrale Gehalte über drei Dekadenklassen für thermoplastische und insbesondere auch elastomere Partikelsorten erfassen können. T2 - GDCh Wissenschaftsforum Chemie CY - Aachen, Germany DA - 15.09.2019 KW - TED-GC-MS KW - Mikroplastik KW - Analytik PY - 2019 AN - OPUS4-49995 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Analytical opportunities & Challenges in (ocean) microplastics N2 - An overview about the analytical opportunities and challenges in microplastic detection is given. T2 - ISO TC61/ Annual bioplastics & ocean microplastics symposium CY - Chengdu, People's Republic of China DA - 29.09.2019 KW - Harmonisation KW - Microplastics KW - TED-GC-MS PY - 2019 AN - OPUS4-50000 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Analytic of microplastics in environmental samples N2 - An overview about the existing possibilities for mircoplastic analysis is given. T2 - 2nd International Symposium on Microplastics CY - Seoul, Korea DA - 02.12.2019 KW - Harmonisation KW - Microplastics KW - TED-GC-MS PY - 2019 AN - OPUS4-50003 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dümichen, Erik A1 - Barthel, Anne-Kathrin A1 - Braun, Ulrike A1 - Bannick, Claus Gerhard A1 - Brand, K. A1 - Jekel, M. A1 - Senz, R. T1 - Analysis of polyethylene microplastics in environmental samples, using a thermal decomposition method N2 - Small polymer particles with a diameter of less than 5 mm called microplastics find their way into the environment from polymer debris and industrial production. Therefore a method is needed to identify and quantify microplastics in various environmental samples to generate reliable concentration values. Such concentration values, i.e. quantitative results, are necessary for an assessment of microplastic in environmental media. This was achieved by thermal extraction in thermogravimetric analysis (TGA), connected to a solid-phase adsorber. These adsorbers were subsequently analysed by thermal desorption gas chromatography mass spectrometry (TDS-GC-MS). In comparison to other chromatographic methods, like pyrolyse gas chromatography mass spectrometry (Py-GC-MS), the relatively high sample masses in TGA (about 200 times higher than used in Py-GC-MS) analysed here enable the measurement of complex matrices that are not homogenous on a small scale. Through the characteristic decomposition products known for every kind of polymer it is possible to identify and even to quantify polymer particles in various matrices. Polyethylene (PE), one of the most important representatives for microplastics, was chosen as an example for identification and quantification. KW - Microplastic KW - Identification and quantification of polymers KW - Thermogravimetric analysis KW - Evolved gas analysis KW - Gas chromatography mass spectroscopy PY - 2015 DO - https://doi.org/10.1016/j.watres.2015.09.002 SN - 0043-1354 VL - 85 SP - 451 EP - 457 PB - Elsevier Ltd. CY - Amsterdam AN - OPUS4-34337 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Analysis of microplastic in environmental samples using thermal analytical methods T2 - ICCE 2015 CY - Leipzig, Germany DA - 2015-09-21 PY - 2015 AN - OPUS4-34528 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - Analysis of microplastic in environmental samples using thermal analytical methods N2 - The presentation addresses first general aspects of polymers and polymers in environment (definitions, types, phases, morphology, density) and than summarise the possibilities of analysis. T2 - Society of Environmental Toxicology and Chemistry Europe CY - Nantes, France DA - 23.05.2016 KW - Microplastics PY - 2016 AN - OPUS4-36900 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Braun, Ulrike A1 - Eisentraut, Paul A1 - Altmann, Korinna A1 - Kittner, Maria A1 - Dümichen, Erik A1 - Thaxton, K. A1 - Kleine-Benne, E. A1 - Anumol, T. T1 - Accelerated Determination of Microplastics in Environmental Samples Using Thermal Extraction Desorption-Gas Chromatography/Mass Spectrometry (TED-GC/MS) N2 - There is growing interest in quantifying microplastics in environmental samples. This application note presents a thermal extraction desorption-gas chromatography/mass spectrometry (TED-GC/MS) method that is well suited to automation and increased sample throughput. The method is also able to detect all particle sizes in the sample as long as the limit of detection (LOD) is reached and allows analysis of larger samples of 15 to 25 mg or more. Samples were decomposed by thermogravimetric analysis (TGA), and the gaseous decomposition products were trapped on a solid-phase sorbent, followed by thermal desorption‑gas chromatography/mass spectrometry (TD-GC/MS) using an Agilent 5977B GC/MSD coupled to an Agilent 7890B GC. Target microplastic particle (MP) polymers were identified in environmental samples including surface water, finished compost, house dust, and drinking water. Quantification of MP polymers in environmental samples provided LODs of 0.06 to 2.2 μg, allowing the detection of MPs in trace amounts with sample weights of up to 1 g. Method repeatability was adequate for reliable quantification with RSDs of approximately 6 to 12%. KW - Environment KW - Microplastic particles KW - TED-GC/MS KW - Mass content KW - Thermoanalytical PY - 2020 VL - 2020 SP - 1 EP - 8 PB - Agilent Technologies Inc. CY - USA AN - OPUS4-51672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Grabmayer, K. A1 - Wallner, G.M. A1 - Beißmann, S. A1 - Braun, Ulrike A1 - Steffen, R. A1 - Nitsche, D. A1 - Röder, B. A1 - Buchberger, W. A1 - Lang, R.W. T1 - Accelerated aging of polyethylene materials at high oxygen pressure characterized by photoluminescence spectroscopy and established aging characterization methods N2 - Two commercial polyethylene grades were exposed to water at elevated temperatures and enhanced oxygen pressure. To characterize their aging behavior laser-induced photoluminescence spectroscopy was applied. Additionally, aging characterization was performed by established methods such as tensile testing, infrared (IR) spectroscopy, high performance liquid chromatography (HPLC), differential scanning calorimetry (DSC) and UV–VIS spectroscopy. During the initial stages of aging, the overall concentration of phenolic antioxidants as well as oxidation onset temperatures decreased exponentially. Simultaneously, significant discoloration due to the formation of conjugated degradation products from phenolic antioxidants (e.g., quinone methides) was detected. After the consumption of antioxidants, photoluminescence started to grow continuously presumably due to the formation of photoluminescent unsaturated carbonyls. In the final stages of aging, embrittlement of the materials as characterized by the degradation of mechanical properties (i.e., loss in ductility) coincided with rising carbonyl index values as well as an increase in crystallinity due to chemicrystallization. Between integrated photoluminescence intensity and carbonyl index, a linear correlation was established. In the induction period, the photoluminescence method exhibited a significantly higher sensitivity to reflect aging induced material changes. KW - Polyethylene KW - PE-RT KW - High oxygen pressure KW - Photoluminescence spectroscopy KW - Aging PY - 2014 DO - https://doi.org/10.1016/j.polymdegradstab.2014.06.021 SN - 0141-3910 SN - 1873-2321 VL - 109 SP - 40 EP - 49 PB - Applied Science Publ. CY - London AN - OPUS4-31349 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike T1 - About Standardization and Analytics of Microplastics N2 - Presentation about national and international standardization of microplastic analysis, as well as the project RUSEKU T2 - Industrievereinigung Chemiefaser e.V. CY - Frankfurt, Germany DA - 26.02.2019 KW - Standardisation KW - Microplastic KW - Analysis PY - 2019 AN - OPUS4-47577 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Paul, Andrea A1 - Breitfeld, S. A1 - Sauer, Andreas A1 - Becker, Roland A1 - Kalbe, Ute A1 - Bremser, Wolfram A1 - Braun, Ulrike T1 - A Raman spectroscopic method for the monitoring of microplastics in soil N2 - Due to the increasing presence of microplastic particles (MP) in the Environment and the unknown risks arising from them, there is an urgent need for analytical methods that allow for an efficient identification and quantification of microplastics (MP), i.e. particles < 5 mm, in environmental samples. So far, mostly timeconsuming (micro) infrared or micro-Raman spectroscopic methods are applied. Here an faster alternative Approach is presented based on a Raman processspectrometer with fiber-optical probes in combination with multivariate data analysis. T2 - 12. Kolloquium Prozessanalytik CY - Berlin, Germany DA - 28.11.2016 KW - Raman spectroscopy KW - Microplastics KW - Soil KW - Chemometrics KW - PLS-DA PY - 2016 SP - P10, 59 EP - 60 AN - OPUS4-38392 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Wiesner, Yosri A1 - Bednarz, Marius A1 - Braun, Ulrike A1 - Bannick, Claus Gerhard A1 - Ricking, Mathias A1 - Altmann, Korinna T1 - A promising approach to monitor microplastic masses in composts N2 - Inputs of plastic impurities into the environment via the application of fertilizers are regulated in Germany and the EU by means of ordinances. Robust and fast analytical methods are the basis of legal regulations. Currently, only macro- and large microplastic contents (>1 mm) are measured. Microplastics (1–1,000 µm), are not yet monitored. Thermal analytical methods are suitable for this purpose, which can determine the mass content and can also be operated fully automatically in routine mode. Thermal extraction desorption-gas chromatography/mass spectrometry (TED-GC/MS) allows the identification of polymers and the determination of mass contents in solid samples from natural environments. In accordance with the German or European Commission (EC) Fertiliser Ordinance, composting plants should be monitored for microplastic particles with this method in the future. In this context a compost plant was sampled. At the end of the rotting process, the compost was sieved and separated in a coarse (>1 mm) and a fine fraction (<1 mm). The fine fraction was processed using density separation comparing NaCl and NaI as possible salt alternative and screened for microplastic masses by TED-GC/MS with additional validation and quality assurance experiments. With TED-GC/MS total microplastics mass contents of 1.1–3.0 μg/mg in finished compost could be detected with polyethylene mainly. What differs much to the total mass of plastics in the coarse fraction with up to 60 μg/mg, which were visually searched, identified via ATR-FTIR and gravimetrically weighted. KW - Microplastics KW - TED-GC/MS KW - Compost KW - Monitoring KW - Soil PY - 2023 UR - https://nbn-resolving.org/urn:nbn:de:kobv:b43-586688 DO - https://doi.org/10.3389/fenvc.2023.1281558 SN - 2673-4486 VL - 4 SP - 1 EP - 12 PB - Frontiers Media CY - Lausanne AN - OPUS4-58668 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Dümichen, Erik A1 - Braun, Ulrike A1 - Sturm, Heinz A1 - Kraemer, R. A1 - Deglmann, P. A1 - Gaan, S. A1 - Senz, R. T1 - A new molecular understanding of the thermal degradation of PA 66 doped with metal oxides: Experiment and computation N2 - The thermal molecular degradation of polyamide 66 (PA 66) doped with (partially supported) metal oxide particles (Fe2O3, ZnO, Al2O3) was investigated qualitatively and quantitatively using common analysis techniques like thermogravimetry coupled with IR-spectroscopic evolved gas analysis (TGA-FTIR). Using pyrolysis coupled with gas chromatography mass spectrometry (Py-GC-MS), qualitative conclusions were drawn about the complex hydrocarbon products. However, the combination of TGA with solid-phase extraction, followed by thermal desorption gas chromatography mass spectrometry (TED-GC-MS), allows qualitative and even semi-quantitative conclusions about the decomposition pathway of PA 66 in the presence of various metal oxide particles. The investigations under inert conditions showed that the presence of metal particles increases the rate of decarboxylation and deamination reactions, as well as the formation rate of cyclopentanone and pyridine derivatives. These species are a consequence of various condensation reactions. The condensation reactions release a large amount of water, thus triggering the hydrolysis of PA 66. Molecular thermal degradation mechanisms were developed for the main decomposition as well as for the condensation reactions and supported by quantum chemical calculations. The catalytic effect of the metal oxides in PA 66 increases in the following order: PA 66 = PA 66 – Al2O3 < PA 66 – Fe2O3 < PA 66 – ZnO. KW - PA 66 KW - Metal oxide particles KW - Thermal degradation KW - Solid-phase extraction KW - Molecular modeling PY - 2015 DO - https://doi.org/10.1016/j.polymdegradstab.2015.07.011 SN - 0141-3910 SN - 1873-2321 VL - 120 SP - 340 EP - 356 PB - Elsevier Ltd. CY - London AN - OPUS4-33806 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -