TY - JOUR A1 - Schartel, Bernhard A1 - Braun, Ulrike A1 - Balabanovich, Aliaksandr A1 - Artner, J. A1 - Ciesielski, M. A1 - Döring, M. A1 - Perez, R.M. A1 - Sandler, J.K.W. A1 - Altstädt, V. T1 - Pyrolysis and fire behaviour of epoxy systems containing a novel 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide-(DOPO)-based diamino hardener N2 - Highly soluble 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide-(DOPO)-based diamino hardener (2), bearing its amino groups directly on the DOPO framework, is investigated with respect to its use as a reactive flame retardant in thermosets. A mechanism for decomposition of the corresponding phosphorus-modified epoxy resin system based on a diglycidylether of bisphenol A DGEBA and 2 (DGEBA/2) is proposed and compared to the systems using DGEBA and 4,4'-diaminodiphenylsulfon (DGEBA/DDS) and to a similar system based on the structurally comparable non-reactive DOPO-based compound (DGEBA/DDS/1). Additive 1 changed the decomposition characteristics of the epoxy resin only slightly and phosphorus was released. Incorporating 2 induces two-step decomposition and most of the phosphorus remains in the residue. Furthermore, the fire behaviour of neat epoxy resin systems and a representative carbon fibre-reinforced composite based on DGEBA, DDS and 2 (DGEBA/DDS/2) were examined and compared to that of the analogous composite systems based on DGEBA/DDS and DGEBA/DDS/1. Based on different flame retardancy mechanisms both the reactive compound 2 and the additive compound 1 improve flammability (increase in LOI >13% and achieving V-1 behaviour) of the epoxy resin and composites. Under forced flaming only the flame inhibition of the additive compound 1 acts sufficiently. Lastly, the superior key mechanical properties of the epoxy resin and composite based on 2 are sketched. KW - Decomposition KW - DOPO KW - Flame retardancy KW - Composites KW - Thermosets PY - 2008 DO - https://doi.org/10.1016/j.eurpolymj.2008.01.017 SN - 0014-3057 SN - 1873-1945 VL - 44 IS - 3 SP - 704 EP - 715 PB - Elsevier CY - Oxford AN - OPUS4-16708 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Perez, R.M. A1 - Sandler, J.K.W. A1 - Altstädt, V. A1 - Hoffmann, T. A1 - Pospiech, D. A1 - Ciesielski, M. A1 - Döring, M. A1 - Braun, Ulrike A1 - Balabanovich, Aliaksandr A1 - Schartel, Bernhard T1 - Novel phosphorus-modified polysulfone as a combined flame retardant and toughness modifier for epoxy resins N2 - A novel phosphorus-modified polysulfone (P-PSu) was employed as a combined toughness modifier and a source of flame retardancy for a DGEBA/DDS thermosetting system. In comparison to the results of a commercially available polysulfone (PSu), commonly used as a toughness modifier, the chemorheological changes during curing measured by means of temperature-modulated DSC revealed an earlier occurrence of mobility restrictions in the P-PSu-modified epoxy. A higher viscosity and secondary epoxy-modifier reactions induced a sooner vitrification of the reacting mixture; effects that effectively prevented any phase separation and morphology development in the resulting material during cure. Thus, only about a 20% increase in fracture toughness was observed in the epoxy modified with 20 wt.% of P-PSu, cured under standard conditions at 180 °C for 2 h. Blends of the phosphorus-modified and the standard polysulfone (PSu) were also prepared in various mixing ratios and were used to modify the same thermosetting system. Again, no evidence for phase separation of the P-PSu was found in the epoxy modified with the P-PSu/PSu blends cured under the selected experimental conditions. The particular microstructures formed upon curing these novel materials are attributed to a separation of PSu from a miscible P-PSu–epoxy mixture. Nevertheless, the blends of P-PSu/PSu were found to be effective toughness/flame retardancy enhancers owing to the simultaneous microstructure development and polymer interpenetration. KW - Flame retardants KW - Phosphorus-modified polysulfone KW - Fracture toughness PY - 2007 SN - 0032-3861 SN - 1873-2291 VL - 48 IS - 3 SP - 778 EP - 790 PB - Springer CY - Berlin AN - OPUS4-14515 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Seefeldt, Henrik A1 - Braun, Ulrike A1 - Hofmann-Böllinghaus, Anja T1 - Influence of structure, wood content, moisture and additives on the burning behaviour of wood plastic composites T2 - Fire and materials 2011 - 12th International conference and exhibiton CY - San Francisco, CA, USA DA - 2011-01-31 PY - 2011 SP - 1 EP - 10 PB - Interscience Communications AN - OPUS4-24650 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike A1 - Selinka, Hans-Christoph A1 - Bannick, Claus Gerhard A1 - Fretschner, Till A1 - Kerndorff, Alexander A1 - Marquar, Natalie A1 - Obermaier, Nathan A1 - Schneider, Beater A1 - Schneider, Rudolf A1 - Konthur, Zoltán T1 - Von der Kläranlage in das Labor N2 - Im Vorhaben „MARKERIA - Bestimmung von anthropogenen Markerkonzentrationen für die SARS-CoV-2 Quantifizierung mittels eines Hochdurchsatzverfahrens (ELISA)“ geht es um die Bestimmung von Carbamazepin, Diclofenac, Koffein und einer endogenen Gallensäure als potentielle Marker für die Kalibrierung der SARS-CoV-2 Quantifizierung im Abwasser. Es ist ein Teilvorhaben des übergeordneten Projektes ESI-CorA und wird von der BAM im Auftrag des Umweltbundesamtes durchgeführt. Der Vortrag wurde gehalten im Rahmen der Abschlussveranstaltung des Projektes ESI-CorA. Er gab den Projektstand wieder, den UBA und BAM bis dahin erzielt hatten, das SARS-CoV-2 Virus und die anthropogenen Marker in 20 Kläranlagenzuläufen zu bestimmen und miteinander zu korrelieren. T2 - Abschlussveranstaltung des EU-Projekts ESI-CorA CY - Karlsruhe, Germany DA - 22.03.2023 KW - Wastewater-based epidemiology KW - Abwasser KW - ELISA KW - Coronavirus KW - COVID-19 PY - 2023 AN - OPUS4-59204 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Erdmann, Maren A1 - Trappe, Volker A1 - Sturm, Heinz A1 - Braun, Ulrike A1 - Dümichen, Erik T1 - Cure conversion of structural epoxies by cure state analysis and in situ cure kinetics using nondestructive NIR spectroscopy N2 - Non-isothermal heating rate kinetics was applied to two epoxy resin systems. In situ near-infrared (NIR) measurements were taken with a heatable NIR cell which allowed the cure to be monitored by characteristic absorption bands. An autocatalyzed reaction of the nth order was shown to describe the epoxy conversion curves. Differential Scanning Calorimetry (DSC) was used as a complementary method. The kinetic models developed by both NIR and DSC are in good accordance with experimental epoxy conversion in the in situ NIR setup for single and multiple cure temperature ramps. A linear calibration curve of the characteristic absorption bands of epoxy normalized to aromatic vibrations was introduced. The curing degree of structural epoxies that were cured according to an industrial temperature cure profile was determined by NIR using the calibration curve. The epoxy conversions of the structural components showed good agreement with the experimental in situ NIR. Several degrees of cure for structural specimens were evaluated by NIR and residual reaction enthalpy by DSC. We present the non-destructive NIR spectroscopy as an alternative to determine fast and non-destructive epoxy conversion, particularly suitable for high degrees of cure on structural components. KW - Epoxy resin KW - Curing kinetics KW - In situ near-infrared (NIR) spectroscopy KW - Differential scanning calorimetry (DSC) PY - 2017 UR - http://www.sciencedirect.com/science/article/pii/S0040603117300205 DO - https://doi.org/10.1016/j.tca.2017.01.010 SN - 0040-6031 SN - 1872-762X VL - 650 SP - 8 EP - 17 PB - Elsevier B.V. AN - OPUS4-39123 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike A1 - Trappe, Volker A1 - Sturm, Heinz T1 - Einfluss der Feuchtigkeit auf die Schlichte von Glasfasern während der Lagerung T2 - DEWI-OCC CY - Bremen, Germany DA - 2014-05-20 PY - 2014 AN - OPUS4-30704 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike A1 - Dümichen, Erik A1 - Sturm, Heinz T1 - Cure Monitoring Using Infrared Spectroscopy T2 - Wissenschaftskolloquium "Nanotechnologie für Kunststoffverbunde CY - Braunschweig, Germany DA - 2014-09-30 PY - 2014 AN - OPUS4-31584 LA - deu AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - JOUR A1 - Braun, Ulrike A1 - Bahr, Horst A1 - Sturm, Heinz A1 - Schartel, Bernhard T1 - Flame retardancy mechanisms of metal phosphinates and metal phosphinates in combination with melamine cyanurate in glass-fiber reinforced poly(1,4-butylene terephthalate): the influence of metal cation N2 - The pyrolysis and fire behavior of glass-fiber reinforced poly(butylene terephthalate) (PBT/GF) with two different metal phosphinates as flame retardants in combination with and without melamine cyanurate (MC) were analyzed by means of thermogravimetry, thermogravimetry coupled with infrared spectroscopy, flammability, and cone calorimeter tests as well as scanning electron microscopy/energy dispersive X-ray spectroscopy and X-ray fluorescence spectroscopy. In PBT/GF, dosages of 13-20% of the halogen-free flame retardant aluminum phosphinate or aluminum phosphinate in combination with MC fulfill the requirements for electrical engineering and electronics applications (UL 94 = V-0; LOI > 42%), whereas the use of the same amount of zinc phosphinate or zinc phosphinate in combination with MC does not improve the fire behavior satisfactorily (UL 94 = HB; LOI = 27-28%). The performance under forced flaming conditions (cone calorimeter) is quite similar for both of the metal phosphinates. The use of aluminum and zinc salts results in similar flame inhibition predominantly due to the release of the phosphinate compounds in the gas phase. Both metal phosphinates and MC interact with the polymer changing the decomposition characteristics. However, part of the zinc phosphinate vaporizes as a complete molecule. Because of the different decomposition behavior of the metal salts, only the aluminum phosphinate results in a small amount of thermally stable carbonaceous char. In particular, the aluminum phosphinate-terephthalate formed is more stable than the zinc phosphinate-terephthalate. The small amount of char has a crucial effect on the thermal properties and mechanical stability of the residue and thus the flammability. KW - Flame retardance KW - Polyester KW - Phosphinates KW - Pyrolysis KW - Cone calorimeter PY - 2008 DO - https://doi.org/10.1002/pat.1147 SN - 1042-7147 SN - 1099-1581 VL - 19 IS - 6 SP - 680 EP - 692 PB - John Wiley & Sons, Ltd. CY - Chichester AN - OPUS4-17620 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - GEN A1 - Braun, Ulrike A1 - Sturm, Heinz A1 - Schartel, Bernhard T1 - Flame retardancy mechanisms of aluminium phosphinate in glass-fibre reinforced polyester T2 - Flame Retardants 2008 Conference CY - London, UK DA - 2008-02-12 PY - 2008 SN - 978-0-9556548-1-7 SP - 133 EP - 140 PB - Interscience Communications CY - London, UK AN - OPUS4-17785 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER - TY - CONF A1 - Braun, Ulrike A1 - Sturm, Heinz A1 - Schartel, Bernhard T1 - Flame retardancy mechanisms of aluminium phosphinate in glass-fibre reinforced polyester T2 - Flame Retardants 2008 CY - London, England DA - 2008-02-12 PY - 2008 AN - OPUS4-16672 LA - eng AD - Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin, Germany ER -